WO2002010298A1 - Compositions de revetement comprenant des constituants, des revetements, des substrats revetus a blocage silyle, et procedes afferents a ces compositions - Google Patents

Compositions de revetement comprenant des constituants, des revetements, des substrats revetus a blocage silyle, et procedes afferents a ces compositions Download PDF

Info

Publication number
WO2002010298A1
WO2002010298A1 PCT/US2000/020837 US0020837W WO0210298A1 WO 2002010298 A1 WO2002010298 A1 WO 2002010298A1 US 0020837 W US0020837 W US 0020837W WO 0210298 A1 WO0210298 A1 WO 0210298A1
Authority
WO
WIPO (PCT)
Prior art keywords
coating composition
group
composition according
components
hydroxyl
Prior art date
Application number
PCT/US2000/020837
Other languages
English (en)
Inventor
Steven V. Barancyk
John W. Burgman
James B. O'dywer
Laura A. Kiefer-Liptak
Michael Allen Mayo
Gregory J. Mccollum
Shiryn Tyebjee
Original Assignee
Ppg Industries Ohio, Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ppg Industries Ohio, Inc. filed Critical Ppg Industries Ohio, Inc.
Priority to PCT/US2000/020837 priority Critical patent/WO2002010298A1/fr
Priority to AU2000263928A priority patent/AU2000263928A1/en
Publication of WO2002010298A1 publication Critical patent/WO2002010298A1/fr

Abstract

L'invention concerne des compositions de revêtement formées à partir d'au moins une matière à fonctionnalité non-vinylique hydroxyle comprenant au moins un groupe hydroxyle alcoolique bloquée par un groupe silyle hydrolysable, et au moins un agent de durcissement. Selon l'invention, un autre mode de réalisation concerne une composition de revêtement formée à partir de constituants comprenant au moins une matière à fonctionnalité de carbamate bloquée par un groupe silyle hydrolysable, et au moins un agent de durcissement. Selon l'invention, un autre mode de réalisation a trait à une composition de revêtement formée à partir de constituants comprenant au moins une matière à fonctionnalité de carboxyle comprenant au moins un groupe carboxylique bloqué par un groupe silyle hydrolysable, et au moins un agent de durcissement. Selon l'invention, un autre mode de réalisation concerne une composition de revêtement formée à partir de constituants comprenant au moins une matière d'amide à fonctionnalité comprenant au moins un amide bloqué par un groupe silyle hydrolysable, et au moins un agent de durcissement. Selon l'invention, d'autres modes de réalisation concernent des substrats revêtus de compositions durcies citées ci-dessus. L'invention concerne également des revêtements composites à multi-constituants comprenant un revêtement de base durci déposé provenant d'une composition de revêtement pigmentée et un revêtement supérieur durci déposé provenant d'une composition de revêtement supérieure. Selon l'invention, les revêtements composites à multi-constituants permettent d'obtenir une couleur plus des revêtements transparents et à résistance élevée aux rayures. Selon l'invention, des modes de réalisation supplémentaires concernent des procédés d'amélioration de la résistance aux rayures d'un substrat.
PCT/US2000/020837 2000-07-31 2000-07-31 Compositions de revetement comprenant des constituants, des revetements, des substrats revetus a blocage silyle, et procedes afferents a ces compositions WO2002010298A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
PCT/US2000/020837 WO2002010298A1 (fr) 2000-07-31 2000-07-31 Compositions de revetement comprenant des constituants, des revetements, des substrats revetus a blocage silyle, et procedes afferents a ces compositions
AU2000263928A AU2000263928A1 (en) 2000-07-31 2000-07-31 Coating compositions comprising silyl blocked components, coatings, coated substrates and methods related thereto

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/US2000/020837 WO2002010298A1 (fr) 2000-07-31 2000-07-31 Compositions de revetement comprenant des constituants, des revetements, des substrats revetus a blocage silyle, et procedes afferents a ces compositions

Publications (1)

Publication Number Publication Date
WO2002010298A1 true WO2002010298A1 (fr) 2002-02-07

Family

ID=21741638

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2000/020837 WO2002010298A1 (fr) 2000-07-31 2000-07-31 Compositions de revetement comprenant des constituants, des revetements, des substrats revetus a blocage silyle, et procedes afferents a ces compositions

Country Status (2)

Country Link
AU (1) AU2000263928A1 (fr)
WO (1) WO2002010298A1 (fr)

Cited By (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2003070837A2 (fr) * 2002-02-20 2003-08-28 Ppg Industries Ohio, Inc. Composition filmogene durcissable en poudre presentant des proprietes de fluidite et d'etalement ameliorees
WO2007067523A1 (fr) * 2005-12-09 2007-06-14 Ppg Industries Ohio, Inc. Méthode de réduction de la durée nécessaire pour appliquer un revêtement résistant aux rayures
US7476344B2 (en) 2005-02-25 2009-01-13 E.I. Du Pont De Nemours Electrical apparatuses containing polytrimethylene homo- or copolyether glycol based electrical insulation fluids
US7544746B2 (en) 2002-05-29 2009-06-09 Tate & Lyle Public Limited Company Hyperbranched polymers
US7629396B2 (en) 2005-02-23 2009-12-08 E.I. Du Pont De Nemours And Company Silicon-containing polytrimethylene homo- for copolyether composition
CN105131656A (zh) * 2015-10-13 2015-12-09 中国石油化工股份有限公司 纳米二氧化钛改性方法
CN110325607A (zh) * 2017-03-16 2019-10-11 美国陶氏有机硅公司 有机硅防粘涂料组合物
CN111489720A (zh) * 2020-05-08 2020-08-04 雅歌乐器(漳州)有限公司 一种吉他的生产工艺
CN112424287A (zh) * 2018-08-14 2021-02-26 帝斯曼知识产权资产管理有限公司 用于具有硬度和光泽度的出色平衡的涂料的氧化型、离子型和短油型醇酸树脂

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0584978A1 (fr) * 1992-08-04 1994-03-02 Shin-Etsu Chemical Co., Ltd. Composition de polymère reticulable à température ambiante
US5359005A (en) * 1991-04-29 1994-10-25 Ppg Industries, Inc. Stable, one-package, non-gelled coating composition curable under ambient conditions
DE19612746A1 (de) * 1995-03-31 1996-10-02 Mazda Motor Einkomponenten-Überzugszusammensetzung bzw. -Beschichtungsmasse und Beschichtungsverfahren unter Verwendung derselben
US5786435A (en) * 1993-03-19 1998-07-28 Mazda Motor Corporation Low solvent composition of alicyclic epoxy oligomer
EP0900832A2 (fr) * 1997-09-03 1999-03-10 Kansai Paint Co., Ltd. Composition de revêtement à haute teneur en matières solides et procédé de formation d'un revêtement de finissage

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5359005A (en) * 1991-04-29 1994-10-25 Ppg Industries, Inc. Stable, one-package, non-gelled coating composition curable under ambient conditions
EP0584978A1 (fr) * 1992-08-04 1994-03-02 Shin-Etsu Chemical Co., Ltd. Composition de polymère reticulable à température ambiante
US5786435A (en) * 1993-03-19 1998-07-28 Mazda Motor Corporation Low solvent composition of alicyclic epoxy oligomer
DE19612746A1 (de) * 1995-03-31 1996-10-02 Mazda Motor Einkomponenten-Überzugszusammensetzung bzw. -Beschichtungsmasse und Beschichtungsverfahren unter Verwendung derselben
EP0900832A2 (fr) * 1997-09-03 1999-03-10 Kansai Paint Co., Ltd. Composition de revêtement à haute teneur en matières solides et procédé de formation d'un revêtement de finissage

Cited By (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2003070837A3 (fr) * 2002-02-20 2004-12-02 Ppg Ind Ohio Inc Composition filmogene durcissable en poudre presentant des proprietes de fluidite et d'etalement ameliorees
WO2003070837A2 (fr) * 2002-02-20 2003-08-28 Ppg Industries Ohio, Inc. Composition filmogene durcissable en poudre presentant des proprietes de fluidite et d'etalement ameliorees
US7544746B2 (en) 2002-05-29 2009-06-09 Tate & Lyle Public Limited Company Hyperbranched polymers
US7629396B2 (en) 2005-02-23 2009-12-08 E.I. Du Pont De Nemours And Company Silicon-containing polytrimethylene homo- for copolyether composition
US7696264B2 (en) 2005-02-23 2010-04-13 E. I. Du Pont De Nemours And Company Silicon-containing polytrimethylene homo- or copolyether composition
US7476344B2 (en) 2005-02-25 2009-01-13 E.I. Du Pont De Nemours Electrical apparatuses containing polytrimethylene homo- or copolyether glycol based electrical insulation fluids
WO2007067523A1 (fr) * 2005-12-09 2007-06-14 Ppg Industries Ohio, Inc. Méthode de réduction de la durée nécessaire pour appliquer un revêtement résistant aux rayures
CN105131656A (zh) * 2015-10-13 2015-12-09 中国石油化工股份有限公司 纳米二氧化钛改性方法
CN110325607A (zh) * 2017-03-16 2019-10-11 美国陶氏有机硅公司 有机硅防粘涂料组合物
CN110325607B (zh) * 2017-03-16 2021-08-10 美国陶氏有机硅公司 有机硅防粘涂料组合物
US11453805B2 (en) 2017-03-16 2022-09-27 Dow Silicones Corporation Silicone release coating compositions
CN112424287A (zh) * 2018-08-14 2021-02-26 帝斯曼知识产权资产管理有限公司 用于具有硬度和光泽度的出色平衡的涂料的氧化型、离子型和短油型醇酸树脂
CN112424287B (zh) * 2018-08-14 2023-03-28 科思创(荷兰)有限公司 用于具有硬度和光泽度的出色平衡的涂料的氧化型、离子型和短油型醇酸树脂
CN111489720A (zh) * 2020-05-08 2020-08-04 雅歌乐器(漳州)有限公司 一种吉他的生产工艺
CN111489720B (zh) * 2020-05-08 2024-02-27 雅歌乐器(漳州)有限公司 一种吉他的生产工艺

Also Published As

Publication number Publication date
AU2000263928A1 (en) 2002-02-13

Similar Documents

Publication Publication Date Title
US6635341B1 (en) Coating compositions comprising silyl blocked components, coating, coated substrates and methods related thereto
AU770696B2 (en) Cured coatings having improved scratch resistance, coated substrates and methods related thereto
AU2000263930B2 (en) Dual cure coating compositions having improved scratch resistance, coated substrates and methods related thereto
AU771279B2 (en) Coating compositions having improved scratch resistance, coated substrates and methods related thereto
US6803408B2 (en) Coating compositions having improved scratch resistance, coated substrates and methods related thereto
US6610777B1 (en) Flexible coating compositions having improved scratch resistance, coated substrates and methods related thereto
CA2380415C (fr) Compositions de revetement souple presentant une resistance a la rayure amelioree, substrats revetus et procedes associes
AU2000263930A1 (en) Dual cure coating compositions having improved scratch resistance, coated substrates and methods related thereto
JP2003508595A5 (fr)
WO2002010298A1 (fr) Compositions de revetement comprenant des constituants, des revetements, des substrats revetus a blocage silyle, et procedes afferents a ces compositions

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BY BZ CA CH CN CR CU CZ DE DK DM DZ EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT TZ UA UG UZ VN YU ZA ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA GN GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

122 Ep: pct application non-entry in european phase
NENP Non-entry into the national phase

Ref country code: JP