WO2001096124A1 - Substrat receptif a l'encre et procede d'impression - Google Patents
Substrat receptif a l'encre et procede d'impression Download PDFInfo
- Publication number
- WO2001096124A1 WO2001096124A1 PCT/GB2001/002351 GB0102351W WO0196124A1 WO 2001096124 A1 WO2001096124 A1 WO 2001096124A1 GB 0102351 W GB0102351 W GB 0102351W WO 0196124 A1 WO0196124 A1 WO 0196124A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- substrate
- ink
- water
- polyester
- parts
- Prior art date
Abstract
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
AU2001260454A AU2001260454A1 (en) | 2000-06-13 | 2001-05-25 | Ink receptive substrate and printing process |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
GB0014397.4 | 2000-06-13 | ||
GB0014397A GB0014397D0 (en) | 2000-06-13 | 2000-06-13 | Process |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2001096124A1 true WO2001096124A1 (fr) | 2001-12-20 |
Family
ID=9893531
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/GB2001/002351 WO2001096124A1 (fr) | 2000-06-13 | 2001-05-25 | Substrat receptif a l'encre et procede d'impression |
Country Status (3)
Country | Link |
---|---|
AU (1) | AU2001260454A1 (fr) |
GB (1) | GB0014397D0 (fr) |
WO (1) | WO2001096124A1 (fr) |
Citations (14)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4892779A (en) | 1988-03-18 | 1990-01-09 | Ppg Industries, Inc. | Multilayer article of microporous and substantially nonporous materials |
EP0539946A1 (fr) * | 1991-10-30 | 1993-05-05 | Canon Kabushiki Kaisha | Moyen d'enregistrement et méthode d'impression par jet d'encre |
EP0569003A1 (fr) * | 1992-05-08 | 1993-11-10 | Toyo Boseki Kabushiki Kaisha | Composition de polyester dispersable dans l'eau pour support d'enregistrement d'images |
WO1994008796A1 (fr) * | 1992-10-20 | 1994-04-28 | Mobil Oil Corporation | Structure de film multi-couche |
EP0657849A2 (fr) | 1993-11-30 | 1995-06-14 | Hewlett-Packard Company | Méthode et dispositif pour imprimer en couleur au jet d'encres utilisant un précurseur incolore |
WO1996019361A1 (fr) | 1994-12-19 | 1996-06-27 | Robert Bosch Gmbh | Circuiterie pour modules de fonction pouvant etre disposes dans une automobile |
WO1998014524A1 (fr) | 1996-10-01 | 1998-04-09 | Zeneca Limited | Compositions d'encres aqueuses |
WO1998014523A1 (fr) | 1996-10-01 | 1998-04-09 | Zeneca Limited | Compositions d'encre aqueuses |
US5804293A (en) | 1995-12-08 | 1998-09-08 | Ppg Industries, Inc. | Coating composition for recording paper |
US5880196A (en) | 1997-06-13 | 1999-03-09 | Ppg Industries, Inc. | Inkjet printing media |
GB2332438A (en) * | 1997-12-19 | 1999-06-23 | Zeneca Ltd | Ink and Coating Compositions |
EP0972651A1 (fr) * | 1998-07-17 | 2000-01-19 | Xerox Corporation | Compositions pour l'amélioration d'images |
WO2000006390A1 (fr) * | 1998-07-27 | 2000-02-10 | Seiko Epson Corporation | Procede d'enregistrement par jet d'encre avec deux fluides |
EP1072430A2 (fr) * | 1999-07-30 | 2001-01-31 | Eastman Kodak Company | Procédé pour l'impression par jet d'encre, |
-
2000
- 2000-06-13 GB GB0014397A patent/GB0014397D0/en not_active Ceased
-
2001
- 2001-05-25 WO PCT/GB2001/002351 patent/WO2001096124A1/fr active Application Filing
- 2001-05-25 AU AU2001260454A patent/AU2001260454A1/en not_active Abandoned
Patent Citations (15)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4892779A (en) | 1988-03-18 | 1990-01-09 | Ppg Industries, Inc. | Multilayer article of microporous and substantially nonporous materials |
EP0539946A1 (fr) * | 1991-10-30 | 1993-05-05 | Canon Kabushiki Kaisha | Moyen d'enregistrement et méthode d'impression par jet d'encre |
EP0569003A1 (fr) * | 1992-05-08 | 1993-11-10 | Toyo Boseki Kabushiki Kaisha | Composition de polyester dispersable dans l'eau pour support d'enregistrement d'images |
WO1994008796A1 (fr) * | 1992-10-20 | 1994-04-28 | Mobil Oil Corporation | Structure de film multi-couche |
EP0657849A2 (fr) | 1993-11-30 | 1995-06-14 | Hewlett-Packard Company | Méthode et dispositif pour imprimer en couleur au jet d'encres utilisant un précurseur incolore |
WO1996019361A1 (fr) | 1994-12-19 | 1996-06-27 | Robert Bosch Gmbh | Circuiterie pour modules de fonction pouvant etre disposes dans une automobile |
US5804293A (en) | 1995-12-08 | 1998-09-08 | Ppg Industries, Inc. | Coating composition for recording paper |
WO1998014524A1 (fr) | 1996-10-01 | 1998-04-09 | Zeneca Limited | Compositions d'encres aqueuses |
WO1998014523A1 (fr) | 1996-10-01 | 1998-04-09 | Zeneca Limited | Compositions d'encre aqueuses |
US5880196A (en) | 1997-06-13 | 1999-03-09 | Ppg Industries, Inc. | Inkjet printing media |
GB2332438A (en) * | 1997-12-19 | 1999-06-23 | Zeneca Ltd | Ink and Coating Compositions |
EP0972651A1 (fr) * | 1998-07-17 | 2000-01-19 | Xerox Corporation | Compositions pour l'amélioration d'images |
WO2000006390A1 (fr) * | 1998-07-27 | 2000-02-10 | Seiko Epson Corporation | Procede d'enregistrement par jet d'encre avec deux fluides |
EP1022151A1 (fr) * | 1998-07-27 | 2000-07-26 | Seiko Epson Corporation | Procede d'enregistrement par jet d'encre avec deux fluides |
EP1072430A2 (fr) * | 1999-07-30 | 2001-01-31 | Eastman Kodak Company | Procédé pour l'impression par jet d'encre, |
Also Published As
Publication number | Publication date |
---|---|
GB0014397D0 (en) | 2000-08-02 |
AU2001260454A1 (en) | 2001-12-24 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US6533408B1 (en) | Ink jet printing method | |
US5835116A (en) | Image forming method employing ink-jet recording system | |
CN103192620B (zh) | 图像形成方法 | |
US5764263A (en) | Printing process, apparatus, and materials for the reduction of paper curl | |
JP3912212B2 (ja) | 記録材料セット | |
MXPA03007282A (es) | Tintas resistentes al agua para impresoras de chorros de tinta que contienen una resina curable por radiacion ultravioleta. | |
US20020156153A1 (en) | Polymeric additives to improve print quality and permanence attributes in ink-jet inks | |
US20040011249A1 (en) | Ink composition, recording medium, inkjet recording method, and recording | |
US20030027893A1 (en) | Ink jet printing method | |
EP1322712B1 (fr) | Procede d'impression a jet d'encre et compositions pour impression a jet d'encre | |
US7705069B2 (en) | Ink jet composition | |
US6485139B1 (en) | Ink-jet printing process using polymeric biguanides | |
JP2009113499A (ja) | 組成物と方法 | |
US6406526B1 (en) | Pyridonazo dyes and inks containing them | |
EP1159140B1 (fr) | Impression a jets d'encre utilisant des biguanides polymeres | |
JP2009066946A (ja) | インク、インクメディアセット、インクジェット記録方法および記録物 | |
EP1194490B1 (fr) | Compositions d'encre | |
US7172274B2 (en) | Process for preparing chain extended thermoplastic guanidinium polymers | |
US6028180A (en) | Ink compositions | |
WO2001096124A1 (fr) | Substrat receptif a l'encre et procede d'impression | |
WO2008005403A2 (fr) | Perfectionnement à la qualité d'impression d'encres pigmentées sur supports brillants | |
US20030187097A1 (en) | Inkjet ink composition | |
US6303763B1 (en) | Pyridonazo dyes and inks containing them | |
WO2000036030A1 (fr) | Compositions pour encre et leur utilisation pour une impression par jet d'encre | |
JP2002371209A (ja) | インクジェット記録用インク及びインクジェット記録方法 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AK | Designated states |
Kind code of ref document: A1 Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT TZ UA UG US UZ VN YU ZA ZW |
|
AL | Designated countries for regional patents |
Kind code of ref document: A1 Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE TR BF BJ CF CG CI CM GA GN GW ML MR NE SN TD TG |
|
121 | Ep: the epo has been informed by wipo that ep was designated in this application | ||
DFPE | Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101) | ||
REG | Reference to national code |
Ref country code: DE Ref legal event code: 8642 |
|
122 | Ep: pct application non-entry in european phase | ||
NENP | Non-entry into the national phase |
Ref country code: JP |