WO2001094111A1 - Structures de films thermoformables destinees a l'emballage de produits alimentaires - Google Patents
Structures de films thermoformables destinees a l'emballage de produits alimentaires Download PDFInfo
- Publication number
- WO2001094111A1 WO2001094111A1 PCT/US2001/018035 US0118035W WO0194111A1 WO 2001094111 A1 WO2001094111 A1 WO 2001094111A1 US 0118035 W US0118035 W US 0118035W WO 0194111 A1 WO0194111 A1 WO 0194111A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- poly
- thermoplastic film
- ethylene
- disposed
- Prior art date
Abstract
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
AU2001265353A AU2001265353A1 (en) | 2000-06-08 | 2001-06-04 | Thermoformable film structures useful for packaging food products |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US58983400A | 2000-06-08 | 2000-06-08 | |
US09/589,834 | 2000-06-08 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2001094111A1 true WO2001094111A1 (fr) | 2001-12-13 |
Family
ID=24359746
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/US2001/018035 WO2001094111A1 (fr) | 2000-06-08 | 2001-06-04 | Structures de films thermoformables destinees a l'emballage de produits alimentaires |
Country Status (4)
Country | Link |
---|---|
AR (1) | AR029936A1 (fr) |
AU (1) | AU2001265353A1 (fr) |
PA (1) | PA8518901A1 (fr) |
WO (1) | WO2001094111A1 (fr) |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2008003842A2 (fr) * | 2006-07-05 | 2008-01-10 | Bongrain S.A. | Dispositif de conditionnement d'un produit alimentaire, tel qu'un fromage, et son procede de fabrication |
US11292234B2 (en) | 2012-09-13 | 2022-04-05 | Dow Global Technologies Llc | Polyolefin based films suitable for thermoforming |
Citations (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4380567A (en) * | 1980-10-09 | 1983-04-19 | Mitsui Petrochemical Industries, Ltd. | Ethylenic composite film structure |
US4668575A (en) * | 1985-06-12 | 1987-05-26 | Wolff Walsrode Aktiengesellschaft | Heat sealable multilayer films with low permeability to gas and their use as packaging material |
US4692386A (en) * | 1985-05-11 | 1987-09-08 | Wolff Walsrode Aktiengesellschaft | Sealable multilayer polyolefin films |
US5026594A (en) * | 1988-02-18 | 1991-06-25 | Fuji Photo Film Co., Ltd. | Packaging material for photosensitive materials |
US5310584A (en) * | 1992-04-14 | 1994-05-10 | Amoco Corporation | Thermoformable polypropylene-based sheet |
US5874139A (en) * | 1994-10-21 | 1999-02-23 | The Dow Chemical Company | Multilayer polyolefin with balanced sealant properties |
US6083629A (en) * | 1995-12-19 | 2000-07-04 | Sumitomo Chemical Company, Limited | Resin composition and shaped article having a layer comprising the same |
-
2001
- 2001-06-04 WO PCT/US2001/018035 patent/WO2001094111A1/fr active Application Filing
- 2001-06-04 AU AU2001265353A patent/AU2001265353A1/en not_active Abandoned
- 2001-06-07 PA PA8518901A patent/PA8518901A1/es unknown
- 2001-06-07 AR ARP010102724A patent/AR029936A1/es unknown
Patent Citations (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4380567A (en) * | 1980-10-09 | 1983-04-19 | Mitsui Petrochemical Industries, Ltd. | Ethylenic composite film structure |
US4692386A (en) * | 1985-05-11 | 1987-09-08 | Wolff Walsrode Aktiengesellschaft | Sealable multilayer polyolefin films |
US4668575A (en) * | 1985-06-12 | 1987-05-26 | Wolff Walsrode Aktiengesellschaft | Heat sealable multilayer films with low permeability to gas and their use as packaging material |
US5026594A (en) * | 1988-02-18 | 1991-06-25 | Fuji Photo Film Co., Ltd. | Packaging material for photosensitive materials |
US5310584A (en) * | 1992-04-14 | 1994-05-10 | Amoco Corporation | Thermoformable polypropylene-based sheet |
US5310584B1 (en) * | 1992-04-14 | 1999-02-16 | Amoco Corp | Thermoformable polypropylene-based sheet |
US5874139A (en) * | 1994-10-21 | 1999-02-23 | The Dow Chemical Company | Multilayer polyolefin with balanced sealant properties |
US6083629A (en) * | 1995-12-19 | 2000-07-04 | Sumitomo Chemical Company, Limited | Resin composition and shaped article having a layer comprising the same |
Cited By (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2008003842A2 (fr) * | 2006-07-05 | 2008-01-10 | Bongrain S.A. | Dispositif de conditionnement d'un produit alimentaire, tel qu'un fromage, et son procede de fabrication |
FR2903391A1 (fr) * | 2006-07-05 | 2008-01-11 | Bongrain Sa Sa | Dispositif de conditionnement d'un produit alimentaire,tel qu'un fromage,et son procede de fabrication. |
WO2008003842A3 (fr) * | 2006-07-05 | 2008-03-06 | Bongrain Sa | Dispositif de conditionnement d'un produit alimentaire, tel qu'un fromage, et son procede de fabrication |
US11292234B2 (en) | 2012-09-13 | 2022-04-05 | Dow Global Technologies Llc | Polyolefin based films suitable for thermoforming |
Also Published As
Publication number | Publication date |
---|---|
PA8518901A1 (es) | 2002-07-30 |
AU2001265353A1 (en) | 2001-12-17 |
AR029936A1 (es) | 2003-07-23 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US4810541A (en) | Plastic container having a surface to which a lid may be peelably sealed | |
US4735855A (en) | Thermoformable laminate | |
US6562476B2 (en) | Thermoformable multilayer polymeric film | |
EP1448390B1 (fr) | Film pelable et emballage fabrique a partir dudit film | |
EP1924434B1 (fr) | Materiau d'operculage faisant appel a des fluoropolymeres orientes | |
EP2147783B1 (fr) | Film thermorétrécissable scellable en superposition | |
EP3946758B1 (fr) | Film recyclable pour thermoformage | |
US6815057B2 (en) | Laminated thermoformable film structures useful for packaging food products | |
EP2679517A1 (fr) | Structures barrieres multicouches, procedes de fabrication de ces dernieres et emballages fabriques a partir desdites structures | |
EP3601071B1 (fr) | Film récupérant après une stérilisation en autoclave | |
US4927690A (en) | Thermoformable laminated packaging material | |
AU705748B2 (en) | Film/substrate composite material | |
EP2679518B1 (fr) | Structures barrières multicouches, procédés de structures multicouches, emballages et procédés de fabrication de structures multicouches | |
EP0275102A2 (fr) | Film multicouche en polymère, pour la fabrication de récipients utilisables dans les fours à micro-ondes | |
US20020015811A1 (en) | Film/substrate composite material | |
WO2001094111A1 (fr) | Structures de films thermoformables destinees a l'emballage de produits alimentaires | |
EP0247664B1 (fr) | Produits stratifiés multicouches et récipient avec couche d'arrêt pour cornues | |
JP3294762B2 (ja) | 密封容器 | |
US20180222161A1 (en) | Packaging tray with capping layer | |
JPH02299836A (ja) | 積層物 | |
US20190047267A1 (en) | Packaging tray with surface-treated capping layer | |
WO1998014327A1 (fr) | Laminats et films de polyolefines | |
JPH02209241A (ja) | 積層長尺物 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AK | Designated states |
Kind code of ref document: A1 Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT TZ UA UG US UZ VN YU ZA ZW |
|
AL | Designated countries for regional patents |
Kind code of ref document: A1 Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE TR BF BJ CF CG CI CM GA GN GW ML MR NE SN TD TG |
|
121 | Ep: the epo has been informed by wipo that ep was designated in this application | ||
REG | Reference to national code |
Ref country code: DE Ref legal event code: 8642 |
|
122 | Ep: pct application non-entry in european phase | ||
NENP | Non-entry into the national phase |
Ref country code: JP |