WO2001076884A1 - Procede de production de materiau d'enregistrement d'information et liquide de revetement a utiliser dans ledit procede - Google Patents
Procede de production de materiau d'enregistrement d'information et liquide de revetement a utiliser dans ledit procede Download PDFInfo
- Publication number
- WO2001076884A1 WO2001076884A1 PCT/JP2001/002497 JP0102497W WO0176884A1 WO 2001076884 A1 WO2001076884 A1 WO 2001076884A1 JP 0102497 W JP0102497 W JP 0102497W WO 0176884 A1 WO0176884 A1 WO 0176884A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- coating
- recording material
- coating liquid
- layer
- information recording
- Prior art date
Abstract
L'invention concerne un procédé de production d'un matériau d'enregistrement d'information, qui se caractérise en ce que : (1) un film de liquide de revêtement possédant plusieurs couches est appliqué à la machine à rideau, une couche de revêtement liquide intermédiaire étant prévue entre deux couches liquides de revêtement qui forment un liquide de haute viscosité lorsqu'elles sont mélangées l'une à l'autre ou mises en contact l'une avec l'autre ; (2) un film liquide de revêtement à plusieurs couches est appliqué à la machine à rideau, au moins un ensemble de couches adjacentes formant graduellement un liquide de haute viscosité après avoir été mises en contact ou mélangées l'une avec l'autre ; (3) la surface d'un support est d'abord enduite d'eau ou d'un liquide aqueux, puis, avant que ledit matériau soit séché, un film liquide de revêtement à plusieurs couches est appliqué à la machine à rideau ; et (4) un film liquide de revêtement à plusieurs couches est appliqué à la machine à rideau, une couche liquide de revêtement contenant 90 % en poids ou plus d'eau constituant la couche la plus proche de la surface d'un support. Ledit procédé permet la production avec une productivité élevée de matériau d'enregistrement d'information, présentant d'excellentes qualités, dont, entre autres, à l'application.
Priority Applications (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
DE10196052T DE10196052T1 (de) | 2000-04-11 | 2001-03-27 | Verfahren zur Herstellung eines Informationsaufzeichnungsmaterial und Beschichtungslösungen zur Verwendung in diesem Material |
US10/265,911 US6746718B2 (en) | 2000-04-11 | 2002-10-08 | Process of curtain for producing an information recording material |
Applications Claiming Priority (6)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2000109767 | 2000-04-11 | ||
JP2000-109767 | 2000-04-11 | ||
JP2000-354743 | 2000-11-21 | ||
JP2000354743 | 2000-11-21 | ||
JP2000388227 | 2000-12-21 | ||
JP2000-388227 | 2000-12-21 |
Related Child Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US10/265,911 Continuation US6746718B2 (en) | 2000-04-11 | 2002-10-08 | Process of curtain for producing an information recording material |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2001076884A1 true WO2001076884A1 (fr) | 2001-10-18 |
Family
ID=27343057
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/JP2001/002497 WO2001076884A1 (fr) | 2000-04-11 | 2001-03-27 | Procede de production de materiau d'enregistrement d'information et liquide de revetement a utiliser dans ledit procede |
Country Status (2)
Country | Link |
---|---|
DE (1) | DE10196052T1 (fr) |
WO (1) | WO2001076884A1 (fr) |
Cited By (14)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2005113162A1 (fr) | 2004-05-24 | 2005-12-01 | Fuji Photo Film Co., Ltd. | Procede de fabrication de matériau d’enregistrement d’informations et matériau d’enregistrement d’informations |
WO2006038381A1 (fr) * | 2004-09-30 | 2006-04-13 | Nippon Paper Industries Co., Ltd. | Procédé de fabrication de support d’enregistrement thermosensible |
US7364774B2 (en) | 2002-04-12 | 2008-04-29 | Dow Global Technologies Inc. | Method of producing a multilayer coated substrate having improved barrier properties |
US7425246B2 (en) | 2001-04-14 | 2008-09-16 | Dow Global Technologies Inc. | Process for making multilayer coated paper or paperboard |
US7473333B2 (en) | 2002-04-12 | 2009-01-06 | Dow Global Technologies Inc. | Process for making coated paper or paperboard |
JP2009226241A (ja) * | 2008-03-19 | 2009-10-08 | Konica Minolta Holdings Inc | 多層同時塗布方法 |
WO2011046080A1 (fr) | 2009-10-14 | 2011-04-21 | 王子製紙株式会社 | Matière d'enregistrement thermosensible |
JP2011206707A (ja) * | 2010-03-30 | 2011-10-20 | Dainippon Printing Co Ltd | 多層塗工膜の製造方法及び多層塗工膜 |
JP2012236314A (ja) * | 2011-05-11 | 2012-12-06 | Osaka Sealing Printing Co Ltd | 感熱記録体の製造方法 |
JP2012236319A (ja) * | 2011-05-11 | 2012-12-06 | Osaka Sealing Printing Co Ltd | 感熱記録体の製造方法 |
JP2012236315A (ja) * | 2011-05-11 | 2012-12-06 | Osaka Sealing Printing Co Ltd | 感熱記録体の製造方法 |
JP2012236316A (ja) * | 2011-05-11 | 2012-12-06 | Osaka Sealing Printing Co Ltd | 感熱記録体の製造方法 |
JP2013103387A (ja) * | 2011-11-11 | 2013-05-30 | Dainippon Printing Co Ltd | 昇華転写受像シート及び昇華転写受像シートの製造方法 |
WO2016047649A1 (fr) * | 2014-09-25 | 2016-03-31 | 富士フイルム株式会社 | Procédé de fabrication de corps moulé de motif |
Families Citing this family (21)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE102004011230B4 (de) | 2004-03-04 | 2005-12-29 | Papierfabrik August Koehler Ag | Verfahren zur Herstellung eines Thermopapiers |
DE102014107567B3 (de) | 2014-05-28 | 2015-11-05 | Papierfabrik August Koehler Se | Wärmeempfindliches Aufzeichnungsmaterial |
DE102015104306B4 (de) | 2015-03-23 | 2018-05-03 | Papierfabrik August Koehler Se | Wärmeempfindliches Aufzeichnungsmaterial |
DE102015119428B3 (de) | 2015-11-11 | 2016-03-24 | Papierfabrik August Koehler Se | Wärmeempfindliches Aufzeichnungsmaterial und Verfahren zu dessen Herstellung |
EP3219507A1 (fr) | 2016-03-14 | 2017-09-20 | Papierfabrik August Koehler SE | Matériel d'enregistrement autocollant sensible à la chaleur |
DE102016113203B4 (de) | 2016-07-18 | 2018-05-30 | Papierfabrik August Koehler Se | Wärmeempfindliches aufzeichnungsmaterial |
DE102017111439B4 (de) | 2017-05-24 | 2019-08-22 | Papierfabrik August Koehler Se | Wärmeempfindliches aufzeichnungsmaterial |
DE102018111224B4 (de) | 2018-05-09 | 2020-12-10 | Papierfabrik August Koehler Se | Wärmeempfindliches Aufzeichnungsmaterial |
DE102018111495B4 (de) * | 2018-05-14 | 2020-04-09 | Papierfabrik August Koehler Se | Thermoresponsive Papierbeschichtungen auf Basis von Cellulosederivaten |
DE102018133168B4 (de) | 2018-12-20 | 2021-02-18 | Papierfabrik August Koehler Se | Wärmeempfindliches Aufzeichnungsmaterial |
DE102019132401B3 (de) | 2019-11-28 | 2021-02-18 | Papierfabrik August Koehler Se | Polymorphe Formen von N-(4-((4-(3-Phenylureido)phenyl)sulfonyl)phenyl)benzosulfonamid |
DE102020112411B3 (de) | 2020-05-07 | 2021-05-27 | Papierfabrik August Koehler Se | Wärmeempfindliches Aufzeichnungsmaterial |
DE102020123150A1 (de) | 2020-09-04 | 2022-03-10 | Koehler Innovation & Technology Gmbh | Beschichtetes Papier |
DE102020127373A1 (de) | 2020-10-16 | 2022-04-21 | Koehler Innovation & Technology Gmbh | Beschichtetes Papier |
DE102021115909A1 (de) | 2021-06-18 | 2022-12-22 | Koehler Innovation & Technology Gmbh | Wärmeempfindliche Aufzeichnungsmaterialien |
DE102021120941A1 (de) | 2021-08-11 | 2023-02-16 | Koehler Innovation & Technology Gmbh | Wärmeempfindliches Aufzeichnungsmaterial |
DE102021133751A1 (de) | 2021-12-17 | 2023-06-22 | Koehler Innovation & Technology Gmbh | Wärmeempfindliches Aufzeichnungsmaterial |
DE102021125950A1 (de) | 2021-10-06 | 2023-04-06 | Koehler Innovation & Technology Gmbh | Siegelfähiges Verpackungspapier |
DE102021133333A1 (de) | 2021-12-15 | 2023-06-15 | Koehler Innovation & Technology Gmbh | Bahnförmiges wärmeempfindliches Aufzeichnungsmaterial |
DE102022109277A1 (de) | 2022-04-14 | 2023-10-19 | Koehler Innovation & Technology Gmbh | Barrierepapier |
DE102022122470A1 (de) | 2022-09-05 | 2024-03-07 | Koehler Innovation & Technology Gmbh | Barrierepapier |
Citations (14)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS5839078B2 (ja) * | 1980-03-11 | 1983-08-27 | 株式会社リコー | 感熱記録材料 |
JPS59189967A (ja) * | 1983-04-14 | 1984-10-27 | Fuji Photo Film Co Ltd | 塗布方法 |
JPH01222992A (ja) * | 1988-03-02 | 1989-09-06 | Fuji Photo Film Co Ltd | 多色記録材料 |
JPH04179578A (ja) * | 1990-11-14 | 1992-06-26 | Honshu Paper Co Ltd | 感熱記録材料の製造方法 |
JPH054441A (ja) * | 1991-06-27 | 1993-01-14 | Mitsubishi Paper Mills Ltd | ノーカーボン感圧複写紙の製造方法 |
JPH06344666A (ja) * | 1993-06-04 | 1994-12-20 | Fuji Photo Film Co Ltd | 感熱記録材料の製造方法 |
JPH07159925A (ja) * | 1993-12-03 | 1995-06-23 | Fuji Photo Film Co Ltd | ハロゲン化銀写真感光材料の製造方法 |
JPH07164732A (ja) * | 1993-12-16 | 1995-06-27 | Nippon Paper Ind Co Ltd | インクジェット記録用紙の製造方法 |
JPH08108615A (ja) * | 1994-10-07 | 1996-04-30 | Mitsubishi Paper Mills Ltd | インクジェット記録シート及びその製造方法 |
JPH09150571A (ja) * | 1995-11-30 | 1997-06-10 | Oji Paper Co Ltd | インクジェット記録用シート及びその製造方法 |
JPH1134481A (ja) * | 1997-07-16 | 1999-02-09 | Konica Corp | インクジェット記録用紙およびその製造方法 |
JPH1148602A (ja) * | 1997-08-07 | 1999-02-23 | Konica Corp | インクジェット記録用紙 |
JPH11192777A (ja) * | 1998-01-05 | 1999-07-21 | Fuji Photo Film Co Ltd | 記録用シート |
JP2001105715A (ja) * | 1999-10-06 | 2001-04-17 | Fuji Photo Film Co Ltd | 記録用シートの製造方法及び装置 |
-
2001
- 2001-03-27 WO PCT/JP2001/002497 patent/WO2001076884A1/fr active Application Filing
- 2001-03-27 DE DE10196052T patent/DE10196052T1/de not_active Withdrawn
Patent Citations (14)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS5839078B2 (ja) * | 1980-03-11 | 1983-08-27 | 株式会社リコー | 感熱記録材料 |
JPS59189967A (ja) * | 1983-04-14 | 1984-10-27 | Fuji Photo Film Co Ltd | 塗布方法 |
JPH01222992A (ja) * | 1988-03-02 | 1989-09-06 | Fuji Photo Film Co Ltd | 多色記録材料 |
JPH04179578A (ja) * | 1990-11-14 | 1992-06-26 | Honshu Paper Co Ltd | 感熱記録材料の製造方法 |
JPH054441A (ja) * | 1991-06-27 | 1993-01-14 | Mitsubishi Paper Mills Ltd | ノーカーボン感圧複写紙の製造方法 |
JPH06344666A (ja) * | 1993-06-04 | 1994-12-20 | Fuji Photo Film Co Ltd | 感熱記録材料の製造方法 |
JPH07159925A (ja) * | 1993-12-03 | 1995-06-23 | Fuji Photo Film Co Ltd | ハロゲン化銀写真感光材料の製造方法 |
JPH07164732A (ja) * | 1993-12-16 | 1995-06-27 | Nippon Paper Ind Co Ltd | インクジェット記録用紙の製造方法 |
JPH08108615A (ja) * | 1994-10-07 | 1996-04-30 | Mitsubishi Paper Mills Ltd | インクジェット記録シート及びその製造方法 |
JPH09150571A (ja) * | 1995-11-30 | 1997-06-10 | Oji Paper Co Ltd | インクジェット記録用シート及びその製造方法 |
JPH1134481A (ja) * | 1997-07-16 | 1999-02-09 | Konica Corp | インクジェット記録用紙およびその製造方法 |
JPH1148602A (ja) * | 1997-08-07 | 1999-02-23 | Konica Corp | インクジェット記録用紙 |
JPH11192777A (ja) * | 1998-01-05 | 1999-07-21 | Fuji Photo Film Co Ltd | 記録用シート |
JP2001105715A (ja) * | 1999-10-06 | 2001-04-17 | Fuji Photo Film Co Ltd | 記録用シートの製造方法及び装置 |
Cited By (17)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US7425246B2 (en) | 2001-04-14 | 2008-09-16 | Dow Global Technologies Inc. | Process for making multilayer coated paper or paperboard |
US7364774B2 (en) | 2002-04-12 | 2008-04-29 | Dow Global Technologies Inc. | Method of producing a multilayer coated substrate having improved barrier properties |
US7473333B2 (en) | 2002-04-12 | 2009-01-06 | Dow Global Technologies Inc. | Process for making coated paper or paperboard |
US7862861B2 (en) | 2004-05-24 | 2011-01-04 | Fujifilm Corporation | Method of manufacturing information recording materials, and information recording materials |
WO2005113162A1 (fr) | 2004-05-24 | 2005-12-01 | Fuji Photo Film Co., Ltd. | Procede de fabrication de matériau d’enregistrement d’informations et matériau d’enregistrement d’informations |
WO2006038381A1 (fr) * | 2004-09-30 | 2006-04-13 | Nippon Paper Industries Co., Ltd. | Procédé de fabrication de support d’enregistrement thermosensible |
JP2009226241A (ja) * | 2008-03-19 | 2009-10-08 | Konica Minolta Holdings Inc | 多層同時塗布方法 |
US8629082B2 (en) | 2009-10-14 | 2014-01-14 | Oji Holdings Corporation | Heat-sensitive recording material |
WO2011046080A1 (fr) | 2009-10-14 | 2011-04-21 | 王子製紙株式会社 | Matière d'enregistrement thermosensible |
JP2011206707A (ja) * | 2010-03-30 | 2011-10-20 | Dainippon Printing Co Ltd | 多層塗工膜の製造方法及び多層塗工膜 |
JP2012236319A (ja) * | 2011-05-11 | 2012-12-06 | Osaka Sealing Printing Co Ltd | 感熱記録体の製造方法 |
JP2012236315A (ja) * | 2011-05-11 | 2012-12-06 | Osaka Sealing Printing Co Ltd | 感熱記録体の製造方法 |
JP2012236316A (ja) * | 2011-05-11 | 2012-12-06 | Osaka Sealing Printing Co Ltd | 感熱記録体の製造方法 |
JP2012236314A (ja) * | 2011-05-11 | 2012-12-06 | Osaka Sealing Printing Co Ltd | 感熱記録体の製造方法 |
JP2013103387A (ja) * | 2011-11-11 | 2013-05-30 | Dainippon Printing Co Ltd | 昇華転写受像シート及び昇華転写受像シートの製造方法 |
WO2016047649A1 (fr) * | 2014-09-25 | 2016-03-31 | 富士フイルム株式会社 | Procédé de fabrication de corps moulé de motif |
JPWO2016047649A1 (ja) * | 2014-09-25 | 2017-07-06 | 富士フイルム株式会社 | パターン形成体の製造方法 |
Also Published As
Publication number | Publication date |
---|---|
DE10196052T1 (de) | 2003-02-27 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
WO2001076884A1 (fr) | Procede de production de materiau d'enregistrement d'information et liquide de revetement a utiliser dans ledit procede | |
US6228475B1 (en) | Ink jet recording element | |
US6497926B1 (en) | Method of producing information recording material | |
US6746718B2 (en) | Process of curtain for producing an information recording material | |
US6447111B1 (en) | Ink jet printing method | |
US6645582B2 (en) | Ink jet recording element | |
JP2001293956A (ja) | 情報記録材料の製造方法 | |
EP1127709B1 (fr) | Procédé d' impression par jet d' encre | |
US6447882B1 (en) | Ink jet recording element | |
EP0965459B1 (fr) | Milieu d'enregistrement et méthode d'enregistrement l'utilisant | |
US6635319B1 (en) | Glossy ink jet recording element | |
JP2001018526A (ja) | 感熱記録材料およびその製造方法 | |
US20040022968A1 (en) | Ink jet recording element | |
US6908191B2 (en) | Ink jet printing method | |
US6623819B2 (en) | Ink jet recording element | |
JPH1134481A (ja) | インクジェット記録用紙およびその製造方法 | |
JP3983433B2 (ja) | 情報記録材料の製造方法 | |
US6335395B1 (en) | Method of preparing a stable coating | |
JP2001138632A (ja) | 情報記録材料の製造方法 | |
JPH08230311A (ja) | 記録媒体および画像形成方法 | |
JP2001138631A (ja) | 情報記録材料の製造方法 | |
WO2005032834A1 (fr) | Support de reproduction | |
US6623831B2 (en) | Ink jet printing method | |
JP3752902B2 (ja) | インクジェット記録用紙及びその製造方法並びにカラーインクジェット記録方法 | |
US6632486B1 (en) | Ink jet recording element |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AK | Designated states |
Kind code of ref document: A1 Designated state(s): DE JP US |
|
DFPE | Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101) | ||
ENP | Entry into the national phase |
Ref country code: JP Ref document number: 2001 574379 Kind code of ref document: A Format of ref document f/p: F |
|
WWE | Wipo information: entry into national phase |
Ref document number: 10265911 Country of ref document: US |
|
REG | Reference to national code |
Ref country code: DE Ref legal event code: 8629 |