WO2001045809A1 - Vessie équilibrée pour ballon gonflable - Google Patents

Vessie équilibrée pour ballon gonflable Download PDF

Info

Publication number
WO2001045809A1
WO2001045809A1 PCT/IN1999/000074 IN9900074W WO0145809A1 WO 2001045809 A1 WO2001045809 A1 WO 2001045809A1 IN 9900074 W IN9900074 W IN 9900074W WO 0145809 A1 WO0145809 A1 WO 0145809A1
Authority
WO
WIPO (PCT)
Prior art keywords
compounded
former
latex
natural rubber
shell
Prior art date
Application number
PCT/IN1999/000074
Other languages
English (en)
Inventor
Satish Jain
Naresh Jain
Anil Jain
Jinesh Jain
Vipin Jain
Original Assignee
Satish Jain
Naresh Jain
Anil Jain
Jinesh Jain
Vipin Jain
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Satish Jain, Naresh Jain, Anil Jain, Jinesh Jain, Vipin Jain filed Critical Satish Jain
Priority to GB0213254A priority Critical patent/GB2373193B/en
Priority to JP2001546747A priority patent/JP3823054B2/ja
Priority to PCT/IN1999/000074 priority patent/WO2001045809A1/fr
Priority to AU26871/00A priority patent/AU2687100A/en
Publication of WO2001045809A1 publication Critical patent/WO2001045809A1/fr

Abstract

Cette vessie équilibrée pour ballon gonflable a pour caractéristique de suivre la trajectoire souhaitée ainsi que celle de rebondir tout au long de la trajectoire suivie par le ballon. Cette vessie comporte une enveloppe et une valve montée dans une ouverture ménagée dans cette enveloppe. L'enveloppe est constituée d'au moins une couche ou de deux couches de latex synthétique et/ou de latex de caoutchouc naturel ainsi que d'une couche supplémentaire partielle de latex synthétique et/ou de latex de caoutchouc naturel située à l'opposé, sur le plan du diamètre, de l'ouverture de ladite enveloppe. Cette couche supplémentaire partielle se caractérise par le fait qu'elle vient se superposer sur 2 à 20 % de la surface de l'enveloppe et que son poids est en rapport avec celui de la valve. L'invention a également trait à un procédé de fabrication de cette vessie équilibrée. Dans le cadre de ce procédé, on produit l'enveloppe, constituée d'au moins une couche de latex de caoutchouc naturel et/ou de latex synthétique et d'une couche supplémentaire partielle de latex de caoutchouc naturel et/ou de latex synthétique, par immersion de la forme tant dans un bain de latex de caoutchouc naturel que dans un bain de latex synthétique. Dans un autre mode de réalisation, on immerge la forme dans un bain constitué d'un mélange de latex de caoutchouc naturel et de latex synthétique. La valve est enfin montée dans l'ouverture ménagée dans l'enveloppe ainsi obtenue.
PCT/IN1999/000074 1999-12-21 1999-12-21 Vessie équilibrée pour ballon gonflable WO2001045809A1 (fr)

Priority Applications (4)

Application Number Priority Date Filing Date Title
GB0213254A GB2373193B (en) 1999-12-21 1999-12-21 A balanced bladder for inflatable balls
JP2001546747A JP3823054B2 (ja) 1999-12-21 1999-12-21 膨張式ボール用のバランスされたブラダー
PCT/IN1999/000074 WO2001045809A1 (fr) 1999-12-21 1999-12-21 Vessie équilibrée pour ballon gonflable
AU26871/00A AU2687100A (en) 1999-12-21 1999-12-21 A balanced bladder for inflatable balls

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/IN1999/000074 WO2001045809A1 (fr) 1999-12-21 1999-12-21 Vessie équilibrée pour ballon gonflable

Publications (1)

Publication Number Publication Date
WO2001045809A1 true WO2001045809A1 (fr) 2001-06-28

Family

ID=11076684

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/IN1999/000074 WO2001045809A1 (fr) 1999-12-21 1999-12-21 Vessie équilibrée pour ballon gonflable

Country Status (4)

Country Link
JP (1) JP3823054B2 (fr)
AU (1) AU2687100A (fr)
GB (1) GB2373193B (fr)
WO (1) WO2001045809A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8727920B2 (en) 2008-09-05 2014-05-20 Warrior Sports, Inc. Inflatable latex neoprene bladders

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20100112254A1 (en) * 2007-03-21 2010-05-06 Data F. S.R.L. Coloured playing bowl

Citations (18)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE820878C (de) * 1947-11-06 1951-11-12 Arthur George Ulbrich Im Tauchverfahren hergestellte, aufblasbare Innendruckblase aus Gummi mit Aufblaseschlauch fuer Hohlbaelle
DE921357C (de) * 1952-02-29 1954-12-16 Us Rubber Co Verfahren zum Herstellen einer blasenfreien, mehrfach getauchten oder aufgebrachten Schicht von Butylkautschuk
US3031423A (en) 1958-12-29 1962-04-24 Goodyear Tire & Rubber Method of curing butyl rubber in the presence of an oil
DE7006647U (de) * 1970-02-24 1970-07-30 Nickl Richard Gummiballon.
US4022848A (en) 1974-08-05 1977-05-10 The Goodyear Tire & Rubber Company Bladder composition containing low unsaturation butyl rubber
US5098097A (en) 1991-03-14 1992-03-24 Lisco, Inc. Football
WO1992016119A1 (fr) * 1991-03-12 1992-10-01 Parkinson Kevin G Article impermeable sans coutures
EP0511681A1 (fr) * 1991-04-30 1992-11-04 Sumitomo Rubber Industries Limited Gants et leur procédé de fabrication
EP0592175A1 (fr) * 1992-10-05 1994-04-13 JOHNSON & JOHNSON MEDICAL, INC. Gant médical avec les couches minces sur les doigts
US5342043A (en) 1993-08-30 1994-08-30 Lisco, Inc. Split weight bladder football
US5470060A (en) 1994-11-04 1995-11-28 Premium Products, Inc. Football with odd number of panels
WO1996023643A1 (fr) * 1995-02-02 1996-08-08 Baxter International Inc. Procede de fabrication d'un gant revetu d'une couche de polyurethane
US5545451A (en) * 1992-06-10 1996-08-13 Maxxim Medical, Inc. Flexible rubber article and method of making
US5577724A (en) 1995-02-08 1996-11-26 Gandolfo; Paul J. Football
DE19704778A1 (de) * 1996-02-12 1997-11-27 Ulrich Plaetke Spielball sowie Verfahren zu dessen Herstellung
US5709622A (en) 1996-11-27 1998-01-20 Premium Products, Inc. Football with odd number of panels
DE19738906A1 (de) * 1997-09-05 1999-03-11 Saga Sports Pvt Ltd Blase für einen Ball
JPH1180438A (ja) * 1997-09-15 1999-03-26 Toyo Tire & Rubber Co Ltd ゴム組成物及び加硫ゴム

Family Cites Families (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US1505802A (en) * 1923-05-18 1924-08-19 Spalding & Bros Ag Football
GB9601638D0 (en) * 1996-01-26 1996-03-27 Umbro Uk Ltd Improvements in and relating to balls
US5772545A (en) * 1996-12-20 1998-06-30 Ou; Tsung Ming Sportsball and manufacturing method thereof

Patent Citations (18)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE820878C (de) * 1947-11-06 1951-11-12 Arthur George Ulbrich Im Tauchverfahren hergestellte, aufblasbare Innendruckblase aus Gummi mit Aufblaseschlauch fuer Hohlbaelle
DE921357C (de) * 1952-02-29 1954-12-16 Us Rubber Co Verfahren zum Herstellen einer blasenfreien, mehrfach getauchten oder aufgebrachten Schicht von Butylkautschuk
US3031423A (en) 1958-12-29 1962-04-24 Goodyear Tire & Rubber Method of curing butyl rubber in the presence of an oil
DE7006647U (de) * 1970-02-24 1970-07-30 Nickl Richard Gummiballon.
US4022848A (en) 1974-08-05 1977-05-10 The Goodyear Tire & Rubber Company Bladder composition containing low unsaturation butyl rubber
WO1992016119A1 (fr) * 1991-03-12 1992-10-01 Parkinson Kevin G Article impermeable sans coutures
US5098097A (en) 1991-03-14 1992-03-24 Lisco, Inc. Football
EP0511681A1 (fr) * 1991-04-30 1992-11-04 Sumitomo Rubber Industries Limited Gants et leur procédé de fabrication
US5545451A (en) * 1992-06-10 1996-08-13 Maxxim Medical, Inc. Flexible rubber article and method of making
EP0592175A1 (fr) * 1992-10-05 1994-04-13 JOHNSON & JOHNSON MEDICAL, INC. Gant médical avec les couches minces sur les doigts
US5342043A (en) 1993-08-30 1994-08-30 Lisco, Inc. Split weight bladder football
US5470060A (en) 1994-11-04 1995-11-28 Premium Products, Inc. Football with odd number of panels
WO1996023643A1 (fr) * 1995-02-02 1996-08-08 Baxter International Inc. Procede de fabrication d'un gant revetu d'une couche de polyurethane
US5577724A (en) 1995-02-08 1996-11-26 Gandolfo; Paul J. Football
DE19704778A1 (de) * 1996-02-12 1997-11-27 Ulrich Plaetke Spielball sowie Verfahren zu dessen Herstellung
US5709622A (en) 1996-11-27 1998-01-20 Premium Products, Inc. Football with odd number of panels
DE19738906A1 (de) * 1997-09-05 1999-03-11 Saga Sports Pvt Ltd Blase für einen Ball
JPH1180438A (ja) * 1997-09-15 1999-03-26 Toyo Tire & Rubber Co Ltd ゴム組成物及び加硫ゴム

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
PATENT ABSTRACTS OF JAPAN vol. 1999, no. 08 30 June 1999 (1999-06-30) *

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8727920B2 (en) 2008-09-05 2014-05-20 Warrior Sports, Inc. Inflatable latex neoprene bladders

Also Published As

Publication number Publication date
GB0213254D0 (en) 2002-07-17
GB2373193A (en) 2002-09-18
JP2003517905A (ja) 2003-06-03
AU2687100A (en) 2001-07-03
JP3823054B2 (ja) 2006-09-20
GB2373193B (en) 2004-07-21

Similar Documents

Publication Publication Date Title
US6544608B1 (en) Bladder shell for inflatable balls
CN104271233B (zh) 高度吸收性泡沫内衬
EP3535317A1 (fr) Composites latex de polyisoprène-graphène et leurs procédés de production
US8398511B2 (en) Inflatable latex neoprene bladders
US20100095429A1 (en) Production of Gloves and Other Articles of Flexible Polymer Material
EP1511793B1 (fr) Procede de production d'un gant presentant des caracteristiques d'enfilage ameliorees
CN107189237A (zh) 一种轻量化汽车密封条及其生产工艺
WO2001026750A1 (fr) Vessie pour ballons gonflables
WO2001045809A1 (fr) Vessie équilibrée pour ballon gonflable
US8353793B2 (en) Carboxylated acrylonitrile butadiene latex seamless bladder and a process for manufacturing thereof
ZA200203780B (en) A balanced bladder for inflatable balls.
EP1509257B1 (fr) Gants a caracteristiques d'enfilage ameliorees
WO2008107914A2 (fr) Vessie stratifiée sans couture en latex acrylonitrile butadiène carboxyle et son procédé de fabrication
CN105086122B (zh) 一种狼牙瑜伽柱的制备方法
US2053450A (en) Production of play balls
CN103387801B (zh) 自洁式涂覆胶布
JP2002309043A (ja) ゴムラテックス組成物およびそれを用いた手袋
WO2013030849A1 (fr) Vessie sans couture en latex acrylonitrile butadiène carboxylé à adhésion améliorée pour corps de soupape et son procédé de fabrication
JPH09168611A (ja) 糸巻きゴルフボール

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AE AL AM AT AU AZ BA BB BG BR BY CA CH CN CR CU CZ DE DK DM EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT TZ UA UG US UZ VN YU ZA ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GH GM KE LS MW SD SL SZ TZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA GN GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
WWE Wipo information: entry into national phase

Ref document number: 2002/03780

Country of ref document: ZA

Ref document number: 200203780

Country of ref document: ZA

ENP Entry into the national phase

Ref country code: GB

Ref document number: 200213254

Kind code of ref document: A

Format of ref document f/p: F

ENP Entry into the national phase

Ref country code: JP

Ref document number: 2001 546747

Kind code of ref document: A

Format of ref document f/p: F

REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

122 Ep: pct application non-entry in european phase