WO1999009220A1 - Verfahren und anlage zur direktreduktion von teilchenförmigem eisenoxidhältigem material - Google Patents
Verfahren und anlage zur direktreduktion von teilchenförmigem eisenoxidhältigem material Download PDFInfo
- Publication number
- WO1999009220A1 WO1999009220A1 PCT/AT1998/000191 AT9800191W WO9909220A1 WO 1999009220 A1 WO1999009220 A1 WO 1999009220A1 AT 9800191 W AT9800191 W AT 9800191W WO 9909220 A1 WO9909220 A1 WO 9909220A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- fluidized bed
- bed reactor
- iron oxide
- containing material
- gas
- Prior art date
Abstract
Description
Claims