WO1998049244A1 - Wässriges überzugsmittel - Google Patents
Wässriges überzugsmittel Download PDFInfo
- Publication number
- WO1998049244A1 WO1998049244A1 PCT/EP1998/002548 EP9802548W WO9849244A1 WO 1998049244 A1 WO1998049244 A1 WO 1998049244A1 EP 9802548 W EP9802548 W EP 9802548W WO 9849244 A1 WO9849244 A1 WO 9849244A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- binder
- agents
- acid
- component
- phosphoronium
- Prior art date
Abstract
Description