WO1998004609A1 - Modifiziertes epoxysiloxan-kondensat, verfahren zu dessen herstellung und dessen einsatz als low-stress-giessharz für die elektronik und die elektrotechnik - Google Patents
Modifiziertes epoxysiloxan-kondensat, verfahren zu dessen herstellung und dessen einsatz als low-stress-giessharz für die elektronik und die elektrotechnik Download PDFInfo
- Publication number
- WO1998004609A1 WO1998004609A1 PCT/DE1997/001303 DE9701303W WO9804609A1 WO 1998004609 A1 WO1998004609 A1 WO 1998004609A1 DE 9701303 W DE9701303 W DE 9701303W WO 9804609 A1 WO9804609 A1 WO 9804609A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- condensation
- epoxysiloxane
- condensate
- silanol
- reaction
- Prior art date
Abstract
Description
Claims