WO1997022473A1 - Method for making a laminate and device for the application of this method - Google Patents
Method for making a laminate and device for the application of this method Download PDFInfo
- Publication number
- WO1997022473A1 WO1997022473A1 PCT/BE1996/000133 BE9600133W WO9722473A1 WO 1997022473 A1 WO1997022473 A1 WO 1997022473A1 BE 9600133 W BE9600133 W BE 9600133W WO 9722473 A1 WO9722473 A1 WO 9722473A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- resin
- plate
- plates
- mask
- Prior art date
Abstract
Description
Claims