WO1997000747A1 - Coulee continue de pieces minces - Google Patents
Coulee continue de pieces minces Download PDFInfo
- Publication number
- WO1997000747A1 WO1997000747A1 PCT/JP1996/001668 JP9601668W WO9700747A1 WO 1997000747 A1 WO1997000747 A1 WO 1997000747A1 JP 9601668 W JP9601668 W JP 9601668W WO 9700747 A1 WO9700747 A1 WO 9700747A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- piece
- thickness
- short side
- reduction
- cooling
- Prior art date
Description
Claims