WO1995005856A1 - Aqueous fluid absorbent polymers having a superior balance of absorptive properties - Google Patents
Aqueous fluid absorbent polymers having a superior balance of absorptive properties Download PDFInfo
- Publication number
- WO1995005856A1 WO1995005856A1 PCT/US1994/009665 US9409665W WO9505856A1 WO 1995005856 A1 WO1995005856 A1 WO 1995005856A1 US 9409665 W US9409665 W US 9409665W WO 9505856 A1 WO9505856 A1 WO 9505856A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- aqueous fluid
- fluid absorbent
- inhibitor
- absorbent polymer
- grams
- Prior art date
Abstract
Description
Claims