WO1994029377A1 - Stabilization of damaged thermoplastics - Google Patents
Stabilization of damaged thermoplastics Download PDFInfo
- Publication number
- WO1994029377A1 WO1994029377A1 PCT/EP1994/001663 EP9401663W WO9429377A1 WO 1994029377 A1 WO1994029377 A1 WO 1994029377A1 EP 9401663 W EP9401663 W EP 9401663W WO 9429377 A1 WO9429377 A1 WO 9429377A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- plastic
- process according
- weight
- stabilized
- tert
- Prior art date
Abstract
Description
Claims