US20200259218A1 - Battery grid lead scrap melting apparatus and method - Google Patents
Battery grid lead scrap melting apparatus and method Download PDFInfo
- Publication number
- US20200259218A1 US20200259218A1 US16/274,644 US201916274644A US2020259218A1 US 20200259218 A1 US20200259218 A1 US 20200259218A1 US 201916274644 A US201916274644 A US 201916274644A US 2020259218 A1 US2020259218 A1 US 2020259218A1
- Authority
- US
- United States
- Prior art keywords
- lead
- pool
- briquettes
- scrap
- compacting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Description
- The present invention relates generally to the melting and use of lead scrap and more particularly to the melting and use of lead scrap in the manufacture of grids for lead acid batteries.
- The grids of a lead acid battery are made of a lead or a lead alloy (hereinafter referred to as lead) and the commercial manufacture of lead grids, particularly for positive electrodes, produces a significant amount of solid lead scrap in the form of small pieces of lead from punching, slitting, and trimming operations which must be re-melted for reuse in making lead grids.
- Grids for lead acid batteries may each have a plurality of spaced apart wire segments interconnected at nodes and a plurality of open spaces between the wire segments. The manufacture of a web of a plurality of serially connected lead grids by punching holes through a cast or cast and rolled solid strip of lead typically produces 80% or more by weight of scrap from the solid lead strips. Thus, to economically form lead grids, it is necessary to re-melt and use this scrap in forming long strips of solid lead. While these punched pieces of scrap vary in geometry, they most generally have a thickness in the range of about 0.020 to 0.045 of an inch and a width and length typically each of which does not exceed about 0.6 of an inch. Punched scrap or slugs often are generally rectangular in shape but may be square, trapezoidal, triangular, etc.
- When casting solid lead strip the scrap typically is returned to a furnace which already has a pool of liquid lead therein. The scrap pieces tend to float on the surface of the liquid lead where they are quickly oxidized with a significant portion by weight becoming dross and also may have their alloy content significantly reduced. A portion of the scrap may also sink into the liquid lead to the bottom of the furnace where it often piles up into a glob or mass of small lead particles that require excessively high furnace temperatures to melt and liquefy them which also creates increased oxidation, dross, and shorter equipment life. Significant oxidation and dross produces lead scrap that cannot be reused and thus must be removed, typically manually, from the surface of the pool of lead in the furnace and smelted in a separate furnace usually with alloys being added before it can be re-used to cast a solid lead strip. Significant oxidation and dross of lead alloy scrap dramatically changes and reduces its alloy content. Excessive dross also significantly increases lead dust and vapor fumes in the air which may have a negative effect on human health and the environment.
- In at least some implementations, a process of liquefying a plurality of pieces of solid scrap lead may include providing a pool of liquid lead having a surface, compacting a plurality of pieces of lead scrap into a briquette, and submerging the briquette in the pool of liquid lead and completely below the surface of the pool of liquid lead. In at least some implementations the pool of liquid lead may have a temperature of at least 650° F. and desirably in the range of 750° F. to 950° F. The briquettes may have a density of at least 10.3 g/cc3, desirably at least 10.6 g/cc3 and preferably about 11.0 g/cc3 and a weight of at least 1 kg, desirably 1-2 kg and preferably 8-25 kg.
- In at least some implementations, the process may include casting a solid lead strip from a pool of liquid lead, punching the solid lead strip to form a web of serially connected battery grids and a plurality of pieces of scrap lead punched from the solid strips, compacting a plurality of the pieces of scrap lead into briquettes and submerging the briquettes in the pool of liquid lead to melt the briquettes. The pool of liquid lead may be maintained at a temperature of at least 650° F. and desirably in the range of 750° F. to 950° F. The briquettes may be formed with a density of at least 10.3 g/cc3 desirably at least 10.6 g/cc3 and preferably 11.0 g/cc3 when at room temperature and may have a weight of at least 1 kg, desirably 2 kg and preferably 8 kg to 25 kg.
- In at least some implementations the solid lead strip may be formed by a continuous casting machine, the web of lead grids and scrap lead pieces may be made by a progressive die punching the solid lead strip, the lead scrap pieces may be formed into briquettes by a compacting press and the briquettes submerged in a pool of liquid lead being supplied to the casting machine forming solid lead strips. In some implementations, the thickness of the solid lead strip may be decreased and its longitudinal length increased by passing it through rolling mills before forming the web of lead grids.
- The following detailed description of certain embodiments and best mode will be set forth with reference to the accompanying drawings, in which:
-
FIG. 1 is a schematic view of a suitable industrial manufacturing line for casting a solid strip of lead, punching it to produce a web of grids for lead acid batteries and to re-melt and use scrap produced by manufacture of webs of multiple grids; -
FIG. 2 is an schematic view of a melting furnace, strip caster, trimmer, and reeler of the manufacturing line ofFIG. 1 ; -
FIG. 3 is a plan view of one grid of a web of connected grids produced by a progressive punching die set of the manufacturing line ofFIG. 1 ; -
FIG. 4 is a fragmentary sectional view taken generally on line 4-4 ofFIG. 3 ; -
FIG. 5 is a fragmentary sectional view taken generally on line 5-5 ofFIG. 3 ; -
FIG. 6 is a semi-schematic view of lead scrap; -
FIG. 7 is a perspective view of a mass of lead scrap compacted into one form of a briquette; -
FIG. 8 is a view of a mass of lead scrap compacted into another form of a briquette; -
FIG. 9 is a perspective view of a scrap compacting press of the lineFIG. 1 ; -
FIG. 10 is a semi-schematic sectional view of a portion of the compacting press ofFIG. 9 ; -
FIG. 11 is a semi-schematic fragmentary sectional view of the press taken generally on line 11-11 ofFIG. 10 ; -
FIG. 12 is a perspective view of a die block of the press ofFIG. 9 ; -
FIG. 13 is a semi-schematic schematic perspective view of the compacting press and a melting furnace of the line ofFIG. 1 . - A process of making a web of serially connected battery grids may include forming holes through a solid strip of lead which produces lead scrap pieces such as slugs from die punching operations. Pieces of the lead scrap may be compacted into briquettes which will readily submerge in a pool of liquid lead completely below the surface of the pool. Liquid lead from the pool may be used to cast a solid strip of lead from which the web of grids may be made. The briquettes of scrap may have a density of at least 10.3, desirably 10.6, and preferably 11.0 grams per cubic centimeter [g/cc3] and a weight of at least 1 kilogram (kg), desirably 2 kg and preferably 8 kg to 25 kg. In mass production of battery grids the briquettes may be added to the pool of liquid lead at a rate of at least 1,900 kg, desirably 2,300 kg and preferably 3,000 kg to 4,800 kg per hour. The pool of liquid lead may be at a temperature of at least 650° F. and desirably in the range of 750° F. to 950° F. The solid strip may be cast by a continuous caster at a rate of 2,300 kg per hour and desirably 3,900 kg to 6,300 kg per hour. For automotive lead acid batteries the solid strip may be reduced to a thickness in the range of about 0.020 to 0.045 of an inch [0.50 to 1.15 centimeters (cm)] and the webs of grids formed at a rate of about 80 to 150 linear feet per minute (24 to 46 lineal meters per minute).
- Referring in more detail to the drawings,
FIG. 1 illustrates asuitable production line 20 which may implement this process by casting longitudinally elongate solid strips of lead and producing longitudinally elongate webs each with a plurality of lead acid battery grids connected in series, and by recovering, re-melting and using scrap pieces of lead produced by trimming and/or punching operations in making a web of a series of connected grids from a solid strip of lead. This production line may include a lead solidstrip casting line 22, agrid forming line 24, ascrap compacting line 26, and one ormore furnaces 28 which melt lead and supply liquid lead to thecasting line 22. - The
casting line 22 may have acasting machine 30 which in use casts a longitudinally elongatecontinuous strip 32 of solidified solid lead. This strip is typically passed through a series ofrolling mills 34 which successively reduce the thickness and increase the longitudinal extent or length of the cast strip. In eachrolling mill 34, the strip may pass through the nip of a pair of co-rotating rollers to reduce the thickness of the strip. Thestrip 32′ emerging from the downstream rollingmill 34 may pass through an edge trim cutter and/orslitter 36 and may be wound into a coil or coils by areeler machine 38 for subsequent further processing. If the trim cutter orslitter 36 produces long pieces of scrap they may be broken into smaller pieces of scrap by achipper 40. Typically, the caster may produce a leadsolid strip 32 with a thickness in the range of 0.18 to 0.5 of an inch (4.5 to 13.0 mm) and a width in the range of 4 to 14 inches (100 to 360 mm) at a rate in the range of 3 to 20 lineal feet (1 to 6 meters) per minute. Typically therolling mills 34 collectively may reduce the nominal thickness of thecast strip 32 to anelongate strip 32′ of about 0.020 to 0.045 of an inch (0.5 to 1.15 mm) thick. A suitable lead solid strip casting line is disclosed in United States Published Application US-2018-0342770-A1 of the present Applicant, Wirtz Manufacturing Company of Port Huron, Mich., U.S.A., the disclosure of which is incorporated herein by reference in its entirety and thus the casting line will not be described in further detail herein. - The
grid forming line 24 may include areeler 42 which unwinds coils ofsolid lead strips 32′ which may advance through awelder 44, to aloop feeder 46 which supplies the solid strip to apress 48 with aprogressive die set 50 which punches holes through the lead strip to form aweb 52 of a series of connectedlead grids 54. Thewelder 44 may butt weld together the adjacent ends of individual solid lead strips to provide a substantially continuous longitudinallyelongate strip 32′ fed to the progressive die set. Theweb 52 oflead grids 54 may pass through anultrasonic cleaner 56 and be wound into coils by areeler 58 for further processing of thewebs 52 of connected grids. - As shown in
FIG. 3 theprogressive die set 50 may form eachgrid 54 of theweb 52 with a plurality of generally horizontally or longitudinally extendingwire segments 60 and a plurality of generally vertically extendingwire segments 62 intersecting and joined with the horizontal wire segments atnodes 64. Each grid perimeter may also include aframe 66 of generally horizontally extendingsegments 68 and generally vertically extendingsegments 70. The frame and wire segments may be formed by punching out portions of the solid strip to form through openings, holes orspaces 72 between the wire segments. The punching die will initially form the wire segments with a generally rectangular cross-section which if desired may be stamped or coined by asuitable die 74 as shown inFIGS. 4 and 5 to formangled lands 76 on the wire segments which are inclined to the generally planar and parallelouter faces angled lands 76 may be formed by either a portion of theprogressive die set 50 or by a separate stamping or coining die set and press downstream of theprogressive die set 50. To increase the adhesion of subsequently applied and cured battery paste to the grid wires, some or all of their exterior surfaces may be formed with a controlledsurface roughness 82 which may be produced by stamping or coining operations. A suitable method, apparatus and line for punching a lead solid strip to produce a web of grids is disclosed in U.S. Pat. No. 8,875,361 of Applicant the disclosure of which is incorporated herein by reference in its entirety and thus thisgrid forming line 24 will not be described in further detail herein. - The punching of the lead
solid strip 32′ to form thegrids 54 produces significant quantities of scrap lead pieces 84 (FIG. 6 ) which may be advanced by aconveyor 86 to a compactingpress 88 which forms briquettes of the scrap which are returned to thefurnace 28. Typically, thegrid forming press 48 and progressive punching die set 50 will produce about 125 to 175 lineal feet (40 to 55 lineal meters) per minute of aweb 52 ofconnected grids 54 with a thickness of about 0.020 to 0.045 of an inch (0.5 to 1.15 mm) and a transverse web width of about 4 to 14 inches (100 to 360 mm) and typically produce four or more tons (3,100 kg) per hour ofscrap lead pieces 84 which is usually at least 65% and typically about 80% to 85% by weight of thesolid lead strip 32′.Scrap 84 from thetrimmer 36 andchipper 40 may also be advanced by aconveyor 90 to theconveyor 86 and thus to the compactingpress 88. - In the compacting line 26 a plurality of pieces of
scrap 84 may be compacted into a block or briquette having sufficient integrity that it will not readily separate into small pieces and of sufficient density so that when dropped onto the top surface of a pool of liquid lead in a furnace it will readily sink below the surface of the pool of liquid lead and toward the bottom of the pool of lead. It is believed that the ability of a briquette of scrap lead pieces to submerge below the surface of a pool of liquid lead and toward the bottom of a pool of liquid lead is primarily a function of the buoyancy of the liquid lead acting on the briquette. Unless dropped or propelled from above the top surface of the pool of liquid lead in theory and in accordance with Archimedes' principle the briquette must have sufficient density (weight per unit of volume) at least substantially equal to the buoyancy of the liquid lead in the furnace which for liquid lead at a temperature of about 650° F. to 750° F. is about 10.58 g/cm3 and at a temperature of 950° F. is about 10.43 g/cm3. - It is believed that lead scrap compacted into a briquette weighing at least about 1 kg and having a density of at least about 10.6 g/cm3 when dropped from at least 0.5 feet (0.15 meter) above the top surface of a pool of liquid lead at a temperature of 750° F. substantially vertically into such pool will readily and rapidly sink below the top surface of such pool (assuming the same gravitational force on both the briquette and the pool of liquid lead) and be melted therein. Some empirical testing and resulting data indicates that a briquette in the form of a cylinder 90 (
FIG. 7 ) of lead scrap having a density of 11.0 g/cm3 and a weight within a range of 5 to 10 lbs. (2 to 4 kg) when dropped from 0.5 feet (0.15 meter) above and substantially vertically into a pool of liquid lead at 750° F. readily and rapidly is submerged completely below the surface of the pool of liquid lead and melted therein without producing any significant dross and without a loss of Calcium and tin alloys in a lead calcium tin alloy typically used in making lead acid battery grids. A briquette of scrap lead pieces in the form of a block, hexahedron, or parallelepiped 92 (FIG. 8 ) having a density of about 11.1 g/cc3 and a weight of about 30 pounds (12.6 kg) when dropped from 0.5 feet (0.15 meter) above the surface of and substantially vertically into a pool of liquid lead at 750° F. readily and rapidly submerges completely below the surface of the pool of liquid lead and is melted therein without producing any significant dross and without loss of its calcium, tin, and calcium tin alloys. Thesebriquettes - A
suitable press 88 for compacting scrap lead pieces into briquettes is semi-schematically illustrated inFIGS. 9-13 . This press compacts scrappieces 84 in two stages to form a briquette. The compacting press may have ahopper 94 in which scrappieces 84 are received and moved by rotatingaugers 96 toward an intermittently rotatingauger 98 which intermittently feeds scrap pieces into an elongate chamber orcavity 100 in which a pressing plate 102 (FIG. 11 ) is movable between retracted and extended positions by ahydraulic ram 104 which in operation is actuated by pressurized hydraulic oil supplied by ahydraulic pump 106 driven by anelectric motor 108. As shown inFIGS. 10 and 11 in the first stage theram 104 extends theplate 102 to partially compact a quantity or batch ofscrap pieces 84 in thecavity 100. In the second stage, this partially compacted scrap is transferred into one of two transversely spaced apart diecavities FIG. 12 ) and further compacted therein to form a briquette by aplunger 114 with a complimentary cross-section being advanced through thechamber 100 and into one of thedie cavities hydraulic ram 116. The distal end of this die cavity is closed or covered by an adjacent planar face of aplate 118. Thedie plate 112 is moved back and forth by ahydraulic ram 120 to alternately align one and then the other of thedie cavities plunger 114. - This briquette is removed from its associated
die cavity outlet troughs plunger 114, lateral movement of thedie plate 112 by thehydraulic ram 120 to align thecavity plate 118, and thereafter advancement of associated ejector pins 126, 126′ by thehydraulic ram 116 which also simultaneously again advances theplunger 114 through thecavity 100 and into the otherempty die cavity 110′ or 110 to form another briquette therein. Thedie plate 112 also has a clearance throughhole 127′ for theejector pin 126′. Each time theplunger 114 is retracted from one of thecavities hydraulic ram 120 to align theother cavity 110′ or 100 with the plunger. Theram 104 andauger 98 are cycled to recharge thecavity 100 with a new batch of scrap pieces and partially or pre compact them therein for transfer and further compaction in the empty one of the two diecavities press 88 alternately compacts a briquette in onedie cavity other die cavity 110′ or 110 and onto one of the twotroughs - As shown in
FIG. 13 , once a trough is full of abuting briquettes, each transfer of another briquette into the trough also advances all downstream briquettes and typically discharges a briquette from the other end of the trough either onto a conveyor 128 (FIG. 1 ) which delivers the briquettes to thefurnace 28 or directly into the furnace 28 (FIG. 13 ). The briquettes produced by this press may be generally cylindrical 90 as shown inFIG. 7 or desirably rectilinear 92 as shown inFIG. 8 . The compacted briquettes may be in the form of a cylinder, square, hexahedron, parallelpiped, or of another shape as will apparent to one skilled in the art. A suitable compacting press is available from RUF US, Inc., 771 Sugar Lane, Elyria, Ohio, USA 44035 as model No. RUF 1100. - As shown in
FIG. 13 thefurnace 28 may typically have a container orpot 130 with an open top 132, and in which lead is melted by heat produced typically by natural gas fired burners underlying and in some cases partially surrounding portions of the pot. Melted liquid lead from the furnace may be delivered by a moltenlead pump assembly 134 to thestrip caster 30 desirably without exposing the liquid lead to the atmosphere to at least substantially preclude migration of lead impurities and dross to the caster. Thepump assembly 134 may have a centrifugal pump 136 with aninlet 138 submergible in the pool of liquid lead in thepot 130 of the furnace or in a holding well (not shown) of liquid lead transferred from the furnace. The pump may be driven by anelectric motor 140 through a shaft connected to an impeller. Desirably thepump inlet 138 is positioned in the range of about ¼ to ¾ of the vertical height or extent of the pool of liquid lead in the furnace or holding well. Typically, thepump assembly 134 may deliver excess liquid lead to the castingmachine 30 through a pipe orconduit 140 with the portion not used by the casting machine being returned to the furnace or holding well through a pipe orconduit 142 below the surface of the pool of molten lead in the melting furnace or holding well. If needed, theconduit 140 for delivering lead to the casting machine and theconduit 142 for returning excess liquid lead from the castingmachine 30 may be thermally insulated and if needed equipped with heaters such as electric heaters to ensure that in use the lead remains in a liquid state and at a desirable temperature as it flows through the conduits to and from the casting machine. Typically, the pump assembly may deliver liquid lead to the casting machine at a pressure in the range of 30 to 40 psi gauge (207 to 276 kPa gauge) and a flow rate of 400 to 600 lbs. (181 to 272 kg) of liquid lead per minute. A suitable liquid lead transfer pump assembly is commercially available from the Applicant hereof, Wirtz Manufacturing Company of Port Huron, Mich., USA. A suitable pump assembly is also believed to be disclosed in U.S. Pat. No. 7,507,367 the disclosure of which is incorporated herein by reference in its entirety. - The forms of the invention herein disclosed constitute presently preferred embodiments and many other forms and embodiments are possible. It is not intended herein to mention all the possible equivalent forms or ramifications of the invention. It is understood that the terms used herein are merely descriptive, rather than limiting, and that various changes may be made without departing from the spirit or scope of the invention.
Claims (21)