US20170362687A1 - Structural direct-write additive manufacturing of molten metals - Google Patents
Structural direct-write additive manufacturing of molten metals Download PDFInfo
- Publication number
- US20170362687A1 US20170362687A1 US15/625,161 US201715625161A US2017362687A1 US 20170362687 A1 US20170362687 A1 US 20170362687A1 US 201715625161 A US201715625161 A US 201715625161A US 2017362687 A1 US2017362687 A1 US 2017362687A1
- Authority
- US
- United States
- Prior art keywords
- alloy
- beads
- intermetallic
- present
- eutectic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Description
- The present application claims benefit of U.S. Provisional Patent Application No. 62/350,749, filed on Jun. 16, 2016, all of the contents of which are incorporated herein by reference.
- This invention was made with government support under Prime Contract No. DE-AC05-00OR22725 awarded by the U.S. Department of Energy. The government has certain rights in the invention.
- This invention generally relates to the field of direct-writing additive manufacturing. The invention relates, more particularly, to direct-writing additive manufacturing of metallic materials.
- Additive manufacturing or three-dimensional (3D) printing is a process for making a 3D object of any shape by depositing and joining materials layer by layer from 3D models. The capability of freeform in fabrication of 3D complex objects without the need for expensive tooling or machining has made additive manufacturing promising for a wide variety of applications.
- However, current additive manufacturing technologies lack the capability to efficiently produce 3D objects composed of high melting point materials, particularly metals and metal alloys. Most metal additive manufacturing approaches are based on powder-bed melting techniques, such as laser selective melting or electron beam (e-beam) melting. These technologies are often restricted to a select few materials (i.e., relatively expensive metal powders having particles greater than 1 μm in size) and involve the use of expensive laser and e-beam systems. Therefore, metal additive manufacturing has been heretofore economically unattractive for most applications.
- Welding-based additive manufacturing makes use of an electrical arc generated by a non-consumable electrode or directly from a feed material. A plasma plume is generated by the interaction of the electric arc with the gas surrounding the build zone. The high kinetic energy of the plasma coupled with the high thermal gradients associated with the weld pool leads to poor control of deposited materials resulting in low dimensional tolerances and general build quality.
- Structural direct-write additive-manufacturing is a method wherein liquid material is deposited from a print head directly onto a print bed, where the material solidifies, retaining an intended shape and bonding with a layer of the same material upon which it is deposited. Costs for structural direct-write additive manufacturing systems are much lower than selective laser sintering and e-beam commonly used in metal additive manufacturing. In addition, structural direct-write additive manufacturing is less time intensive than selective laser sintering and e-beam. However, there remains a need to develop metallic materials that can be more suitably integrated with structural direct-write additive manufacturing.
- In one aspect, the invention is directed to an alloy for structural direct-write additive manufacturing. The alloy described herein includes a base element selected from the group consisting of aluminum and/or nickel, and a rare earth element selected from the group consisting of cerium and/or lanthanide. A eutectic intermetallic of the alloying elements is present in the alloy in an amount ranging from about 0.5 wt. % to 7.5 wt. %.
- In another aspect, the invention is directed to a method of fabricating a 3D metallic object using structural direct-write additive manufacturing. The method generally involves heating the above-described alloy to a temperature within 15% above or below a melting point of the alloy in an inert atmosphere, extruding the alloy through a nozzle in the presence of an oxygen-containing atmosphere to form beads of the alloy having a surface tension ranging from about 0.3 N/m to 2.0 N/m. A stabilizing shell is formed surrounding a liquid core of each bead when the beads are exposed to the oxygen-containing atmosphere. The stabilizing shell is rare earth-rich, including oxides of alloying elements and at least one metastable intermetallic of the alloying elements. The method further includes depositing the beads on a substrate and contacting the beads with each other. The rare earth-rich shells of adjacent beads fuse on contact as the beads are cooled down in the oxygen-containing atmosphere. During fusion, a eutectic intermetallic of the alloying elements is formed at an interface of the adjacent beads in an amount greater than that within each of the adjacent beads.
-
FIG. 1 is a schematic diagram showing a droplet of a molten alloy of the present invention suspended from a nozzle. -
FIG. 2 is a graph showing surface tension vs. drop-shape (ds vs. de) for alloys with different densities including Al—Li, Al—Mg, Al-rare earth alloys, Mg-rare earth alloys, and Fe-rare earth alloys. -
FIG. 3 is a graph showing bead size vs. nozzle diameter defined by ds for various alloys with different densities including Al-rare earth alloys, Mg-rare earth alloys, and Fe-rare earth alloys. -
FIG. 4 is a graph showing a ternary isotherm for an Al—Ce—La alloy at 500° C. -
FIG. 5 is a low percentage binary phase diagram for an Al—Ce alloy. -
FIG. 6 is a low percentage binary phase diagram for an Al—La alloy. -
FIG. 7 is a depiction of a first continuous filament of beads of an alloy of the present invention being deposited on a substrate by a nozzle. -
FIG. 8 is a depiction of a second continuous filament of beads of the alloy ofFIG. 7 being formed onto the first continuous filament by the nozzle. -
FIG. 9 is a cross-sectional view through A-A′ ofFIG. 8 . -
FIG. 10 is a cross-sectional diagram showing the outcome of beads of the alloy ofFIG. 7 being deposited too quickly and/or at too high of a temperature. -
FIG. 11 is a cross-sectional diagram showing the outcome of beads of the alloy ofFIG. 7 being deposited too slowly and/or at too low of a temperature. -
FIG. 12 is a flowchart illustrating a first mechanism that may account for the formation of fused layers of beads of an alloy of the present invention. -
FIG. 13 is a flowchart illustrating a second mechanism that may account for the formation of fused layers of beads of an alloy of the present invention. -
FIG. 14 is a flowchart illustrating a third mechanism that may account for the formation of fused layers of beads of an alloy of the present invention. -
FIG. 15 is a flowchart illustrating a fourth mechanism that may account for the formation of fused layers of beads of an alloy of the present invention. -
FIG. 16 is a flowchart illustrating a fourth mechanism that may account for the formation of fused layers of beads of an alloy of the present invention. -
FIG. 17 is a graph showing photoelectron spectroscopy (XPS) data for the surface of an as-cast sample of Al-6Ce. Intensity of detected photoelectrons is measured in arbitrary units (a.u.) -
FIG. 18 is a graph showing XPS data for an as-cast sample of Al-6Ce after sputter etching to a depth of 12 nm. -
FIG. 19 is a graph showing XPS data for the surface of a heat treated sample of Al-6Ce. -
FIG. 20 is a graph showing XPS data for a heat treated sample of Al-6Ce after sputter etching to a depth of 12 nm. -
FIG. 21 is a graph showing XPS data for an oxidized sample of Al-6Ce. -
FIG. 22 is a graph showing XPS data for an oxidized sample of Al-6Ce after sputter etching to a depth of 12 nm. -
FIG. 23 is a low-magnification scanning electron micrograph (SEM) image of Al-6Ce. -
FIG. 24 is a high magnification SEM image of Al-6Ce. -
FIG. 25 is a graph showing differential scanning calorimetry (DSC) data for Al-6Ce shown inFIGS. 25 and 26 . -
FIG. 26A is a SEM image of fused beads of Al-6Ce.FIG. 26B is a higher magnification SEM image showing the wetting surface of the fused beads ofFIG. 26A . -
FIG. 27 is a graph showing a ternary isotherm for Al—Ce—Si alloy family at 639° C.; a few of the many phases are labeled. -
FIG. 28 is a graph showing an enlarged portion ofFIG. 27 below the 10 mass percent line. Details and phases of interest are shown. -
FIG. 29 is a graph showing the isopleth along the constant 93 wt. % Al composition line 42 shown inFIG. 27 . -
FIG. 30 is a graph showing the isopleth along the constant 97 wt. % Al composition line 44 shown inFIG. 27 . -
FIG. 31 is a graph showing the equilibrium phase fraction diagram of Al—Ce—Si alloy family along the 93 wt. % Al line 42 shown inFIG. 27 . -
FIG. 32 is a graph showing the equilibrium phase fraction diagram of Al—Ce—Si alloy family along the 97 wt. % Al line 44 shown inFIG. 27 . -
FIG. 33 is a graph showing minimum ratios needed to achieve 0.549 weight % non-Al phase content. -
FIG. 34 is a graph showing minimum ratios needed to achieve 0.549 weight % non-Al phase content. -
FIG. 35 is a diagram showing Al—Si—Ce ternary alloy isotherm at 100° C. -
FIG. 36 is a diagram showing Al—Si—Ce ternary alloy isotherm at 500° C. -
FIG. 37 is a diagram showing Al—Si—Ce ternary alloy isotherm at 650° C. -
FIG. 38 is a diagram showing Al—Si—Ce ternary alloy liquidus. - In one aspect, the invention is directed to an alloy that is suitable for structural direct-write additive manufacturing. The alloy described herein includes a base element selected from the group consisting of aluminum (Al) and/or nickel (Ni), and a rare earth element selected from the group consisting of cerium (Ce) and/or lanthanide (La). In some embodiments, the alloy is a binary alloy, such as an Al—Ce alloy, Ni—Ce alloy, Al—La alloy, or Ni—Al alloy. In other embodiments, the alloy is a ternary alloy, such as an Al—Ni—Ce alloy, Al—Ni—La alloy, Al—Ce—La alloy, Ni—Ce—Al alloy, Al—Ce—Si alloy, Ni—Ce—Si alloy, Al—La—Si alloy, or Ni—Al—Si alloy. In yet other embodiments, the alloy is a quaternary alloy, such as an Al—Ni—Ce—La alloy, Al—Ni—Ce—Si alloy, Al—Ni—La—Si alloy, Al—Ce—La—Si alloy, or Ni—Ce—Al—Si alloy. Any of the above alloy compositions may or may not also include iron (Fe) and/or magnesium (Mg) and/or carbon (C) to form a higher alloy.
- The alloy of the present invention has the following characteristics which make it feasible to be used in structural direct-write additive manufacturing. First, when molten, a surface tension of the molten alloy falls within a specific range in ambient atmosphere such that the molten alloy forms free-standing beads as the molten alloy is extruded from a nozzle of a 3D printing system and deposited either upon a substrate or upon a previously deposited layer of beads. In one embodiment, the molten alloy has a surface tension ranging from about 0.3 N/m to 2.0 N/m. This range encompasses unprintable metals, such as mercury and molten iron. It has herein been found that a molten alloy having a surface tension below 0.3 N/m is largely incapable of forming beads, and instead flows freely, which is deleterious to structural direct-write additive manufacturing. It has also herein been found that a molten alloy having a surface tension above 2.0 N/M is largely incapable of forming beads, and instead forms clumps, which is also deleterious to structural direct-write additive manufacturing.
-
FIG. 1 depicts a droplet (i.e., bead) of amolten alloy 10 suspended from anozzle 12. The surface tension of the droplet can be calculated by the following formula: -
γ=(Δpgde2)×(1/H) - where γ is surface tension, Δp is density difference between the two fluids of interest (e.g., for Al extrusion in a gaseous atmosphere the density of aluminum is an appropriate approximation), g is gravity acceleration, and 1/H is a correction factor determined from ds/de via second order partial differential Laplacian approximations of droplet shape. Additional information on the calculation of the surface tension of droplet can be found in J. M. Andreas, et al. “Boundary Tension by Pendant Drops”, presented at the Fifteenth Colloid Symposium, held at Cambridge, Mass., Jun. 9-11, 1938, the contents of which are herein incorporated by reference in their entirety.
FIG. 2 shows surface tension vs. droplet aspect ratio (ds/de) for alloys with different densities, e.g., alloys with low density, medium-to-low density, medium-to-high density, and high density. These alloys include Al—Li, Al—Mg, Al-rare earth alloys having densities in the range of 1-2.7 g/cm3, Mg-rare earth alloys having densities in the range of 1.5-2.2 g/cm3, and Fe-rare earth alloys having densities in the range of 7-8 g/cm3. It can be seen that operable surface tension for alloys of different densities generally falls in the range of 0.3 N/m to 2.0 N/m. - Beads of the alloy may have any shape. Typically, the beads are substantially spherical or ovoid. The sizes of the beads are primarily determined by the size of the
nozzle 12 and physical properties of the alloy.FIG. 3 shows projected bead size for various alloys with different densities in the operable surface tension range vs. nozzle diameter. These alloys include Al-rare earth alloys having densities in the range of 1-2.7 g/cm3, Mg-rare earth alloys having having densities in the range of 1.5-2.2 g/cm3, and Fe-rare earth alloys having densities in the range of 7-8 g/cm3. It can be seen that, for a given nozzle size, the bead size increases with higher alloy density. - The proportions of the alloying elements in the alloy are chosen such that a eutectic intermetallic of the alloying elements is present in the alloy as a segregated phase in an amount ranging from about 0.5 to 7.5 wt. %, preferably about 0.5 to 7 wt. %. In different embodiments, the eutectic intermetallic is present in an amount of, for example, 0.5, 1, 1.5, 2, 2.5, 3, 3.5, 4, 4.5, 5, 5.5, 6, 6.5, 7, or 7.5 wt. %, or within a range bounded by any two of the foregoing values. The eutectic intermetallic can affect the viscosity of the molten alloy, thereby affecting its printability.
- The alloy of the present invention also exhibits a unique coupling of surface tension and surface chemistry to stabilize the material mechanical properties once printed. Once the molten alloy is extruded through the
nozzle 12 to form freestanding beads, each bead is stabilized mechanically by a stabilizing shell that is formed spontaneously on its surface when the beads are exposed to an oxygen-containing atmosphere, such as, for example, ambient atmosphere. The stabilizing shell stabilizes the surface tension on material flow and protects the bulk composition of the alloy from degradation. The stabilizing shell is composed of oxides of the alloying elements (e.g., native oxides of the alloy elements and secondary oxide) and at least one metastable intermetallic of the alloying elements. The stabilizing shell has a rare earth content higher than that in the eutectic intermetallic (i.e., it is “rare-earth rich”). The stabilizing shell may be formed to have a thickness ranging from, for example, about 10 to 15 nm. - Beads of the alloy of the present invention also have a self-welding ability. Upon contact with each other, the reaction between the stabilizing shells of adjacent beads produces a higher concentration eutectic intermetallic at the interface, thereby fusing the beads together.
- In some embodiments, the alloy may contain Ce in an amount up to about 8 wt. %, such as an alloy containing Al and Ce with a Ce content in an amount up to about 8 wt. %. In one embodiment, the alloy includes Ce in an amount of about 0.5 to about 7 wt. %, or more specifically, about 1 to about 6 wt. %. The eutectic intermetallic present in the Al—Ce alloy may be, for example, Al11Ce3.
- In some embodiments, at least a portion of the Ce in the alloy is substituted by La. In some embodiments, each part by weight of Ce is substituted by 1.2 parts by weight of La. In other embodiments, all of the Ce in the alloy is substituted by La, and the alloy includes Al and La, with a La content in an amount up to about 10 wt. %. The eutectic intermetallic present in the Al—La alloy may be, for example, Al11La3.
-
FIG. 4 is an isotherm for an Al—Ce—La alloy at 500° C. Mirroring in the phases is observed as compositional amounts of Ce and La are varied, indicating the high similarity between Ce and La.FIGS. 5 and 6 are low percentage binary phase diagrams for an Al—Ce alloy and an Al—La alloy. Notably, the foregoing phase diagrams appear nearly identical except for a slight suppression in the melting temperature of the hyper and hypo-eutectic regions. - In some embodiments, the alloy may also include one or more additional alloying elements such as, for example, iron (Fe), silicon (Si), and magnesium (Mg). The alloy may contain up to about 2 wt. % of Fe, up to about 2 wt. % of Si, or up to about 30 wt. % of Mg. Some particular examples of alloys include Al—Ce, Al—La, Al—Ce—La, Al—Ce—La—Si, Al—Ce—Si, Al—La—Si, Al—Ce—Ni, and Ce—Ni alloys.
- In some embodiments, the alloy may further include a minor additive, such as SiC, carbon nanotube (CNT), alumina, or boron nitride. The minor additive can typically constitute up to about 30 vol % of the alloy. The minor additive may be employed, for example, to increase the loss modulus (i.e., viscosity) of the molten alloy. Increasing the loss modulus can stabilize the molten and semi-solid beads as the beads cool down.
- In another aspect, the invention is directed to a method for fabricating a 3-D metallic object from the alloy described above using structural direct-write additive manufacturing. The method entails first providing an alloy, as described above, and feeding the alloy into a feed chamber of a 3D printing system. The feed chamber is connected to the
nozzle 12, shown inFIG. 1 . In some embodiments, thenozzle 12 has a diameter up to about 10 mm, or more typically from about 0.1 mm to 2 mm. Inert gas, such as nitrogen or argon, is supplied to the feed chamber and thenozzle 12 to create an inert atmosphere; thus, before exiting thenozzle 12, the alloy is protected by the inert atmosphere. The alloy can be provided in any suitable form, such as an alloy wire, alloy ingot, or as a mixture of constituent alloying element powders. - The method further includes heating the alloy to provide a molten alloy. The alloy can be heated to a temperature at which the alloy can consistently be extruded through the
nozzle 12. The alloy is typically heated to a temperature within 15%, within 10%, within 5%, or within 2% above or below a melting point of the alloy. For example, when the alloy is an Al—Ce alloy, the Al—Ce alloy can generally be heated above 650° C. In some embodiments, heating the alloy includes heating with one or more heating elements surrounding the feed chamber and thenozzle 12. Energy can be coupled to the alloy inside the feed chamber and thenozzle 12 either via conduction heating or electromagnetic heating in order to precisely control the extrusion temperature of the alloy. In some embodiments, one or more heating elements are resistance heating elements. In some embodiments, the one or more heating elements are disposed inside thenozzle 12. In some embodiments, the one or more heating elements are configured to provide a nozzle temperature that increases toward an extrusion opening of thenozzle 12. In some embodiments, the heating elements are arranged in increasing density toward the extrusion opening of thenozzle 12, operating at increasing power toward the extrusion opening of thenozzle 12, or both. - Subsequently, the molten alloy is extruded through the
nozzle 12 via pneumatic or mechanical pressure to form beads. These beads have a surface tension ranging from about 0.3 N/m to 2.0 N/m. Upon exiting thenozzle 12, a stabilizing shell composed of oxides of the alloying elements and at least one metastable intermetallic of the alloying elements is formed on a surface of each alloy bead, surrounding a liquid core of the bead as the bead is exposed to an oxygen-containing atmosphere (e.g., ambient atmosphere). The at least one metastable intermetallic can be a rare earth-rich intermetallic having a rare earth content greater than that in the eutectic intermetallic or a rare earth-deficient intermetallic having a rare earth content lower than that in the eutectic intermetallic. In one embodiment, when the alloy is an Al—Ce alloy, the at least one metastable intermetallic formed in the stabilizing shell may include Al2Ce and/or Al4Ce. As the bead cools, the liquid core begins solidifying. - Next, referring to
FIG. 7 , the beads of the alloy are deposited one by one by contacting previously deposited beads on asubstrate 16 from thenozzle 12. The stabilizing shells of adjacent beads fuse on contact as beads are cooled down in the oxygen-containing atmosphere at ambient temperature, forming a firstcontinuous filament 14 on thesubstrate 16 in a predetermined pattern. After fusion, the eutectic intermetallic is formed at an interface of adjacent beads in a higher concentration than that within each bead. - Referring to
FIGS. 8 and 9 , once the firstcontinuous filament 14 is formed, deposition of the beads begins one by one on top of the previous layer of fused beads (e.g., the first continues filament 14) to form a secondcontinuous filament 18. The stabilizing shells of beads in the secondcontinuous filament 18 fuse with the rare earth-rich shells of beads in the firstcontinuous filament 14 on contact, welding the first and secondcontinuous filaments lower bead 14′ has a stabilizingshell 15 and an at least partially solidifiedcore 20, while theupper bead 18′ has a stabilizingshell 19 and a mostlyliquid core 22. Deposition of beads of the alloy continues in this manner, layer by layer, until the entire 3D metallic object is completed. During deposition, thenozzle 12 may be moved with respect to thesubstrate 16. In one embodiment, either thenozzle 12 may be moved or thesubstrate 16 may be moved. In another embodiment, both of thenozzle 12 and thesubstrate 12 may be moved to cause relative motion between thenozzle 12 and the substrate 16). The dotted line spanning across A and A′ inFIG. 8 refers to the cross-section. The cross-sectional view through A-A′ is provided inFIG. 9 . - The printing conditions employed, such as extruding rate and melting temperature, are carefully controlled to ensure proper welding of the consecutive layers. For example, if beads of the alloy are deposited too quickly and/or at too high of a temperature, the beads will be deformed, as shown in
FIG. 10 , and may even collapse. Conversely, if beads of the alloy are deposited too slowly and/or at too low of a temperature, the beads will solidify too quickly, resulting in unsatisfactory self-welding, as shown inFIG. 11 . - Strong interlayer welding is important to prevent the material from delaminating during printing and end user application. Depending on the composition of the stabilizing shell formed, the self-welding of layers of beads of the alloy of the present invention can be attributed to the following reactions occurred at layer-to-layer interface or bead-to-bead interface in the same layer.
-
FIG. 12 is a flowchart illustrating a first mechanism that may account for the formation of the fused layers of beads of the alloy. As shown, a molten alloy of the present invention is extruded onto a substrate, thereby forming a first layer of beads. A stabilizing shell composed of native oxides of alloying elements is formed on a surface of each bead in the first layer once the bead is contacted with the ambient atmosphere. As beads in the first layer cool, cores of beads partially solidify under ambient temperature. A second layer of beads is then deposited on top of the first layer. A stabilizing shell composed of native oxides of alloying elements is formed on a surface of each bead in the second layer once the bead is contacted with ambient atmosphere. As beads in the second layer cool, an exothermic reaction occurs between the base element and the rare earth oxide present at interfaces of the beads to result in the eutectic intermetallic at these interfaces; the rare earth oxide thus dissolves at the interfaces of the beads. The exothermic reaction causes localized welding of layers. The remaining oxide precipitates of the base element help to strengthen the bonds between layers. -
FIG. 13 is a flowchart illustrating a second mechanism that may account for the formation of fused layers of beads of the alloy. As shown, a molten alloy of the present invention is extruded onto a substrate, thereby forming a first layer of beads. A stabilizing shell composed of metastable intermetallics and mixed oxides of alloying elements is formed on a surface of each bead in the first layer once the bead is contacted with the ambient atmosphere. As beads in the first layer cool, cores of beads partially solidify under ambient temperature. A second layer of beads is deposited on top of the first layer. A stabilizing shell composed of metastable intermetallics and mixed oxides of alloying elements is formed on a surface of each bead in the second layer once the bead is contacted with the ambient atmosphere. Oxides at the layer-to-layer interface dissolve due to the presence of energetically favored metastable intermetallics. In addition, as the beads in the second layer cool, the metastable intermetallics in the stabilizing shells at the layer-to-layer interface decompose and transform into a eutectic intermetallic at the bead-to-bead interfaces. These reactions cause localized welding of layers. -
FIG. 14 is a flowchart illustrating a third mechanism that may account for the formation of fused layers of beads of the alloy. As shown, a molten alloy of the present invention is extruded onto a substrate, thereby forming a first layer of beads. A stabilizing shell composed of native oxides of alloying elements and metastable intermetallics is formed on a surface of each bead in the first layer once the bead is contacted with the ambient atmosphere. As beads in the first layer cool, cores of beads partially solidify under ambient temperature. A second layer of beads is deposited on top of the first layer. A stabilizing shell composed of native oxides of alloying elements and metastable intermetallics is formed on a surface of each bead in the second layer once the bead is contacted with the ambient atmosphere. As beads in the second layer cools, rare earth oxide and metastable intermetallics at the layer-to-layer interface decompose, thereby forming a eutectic intermetallic at the interface. The exothermic reaction causes localized welding of layers. -
FIG. 15 is a flowchart illustrating a fourth mechanism that may account for the formation of fused layers of alloy beads. As shown, a molten alloy of the present invention is extruded onto a substrate, thereby forming a first layer of beads. A stabilizing shell composed of native oxides of alloying elements and metastable intermetallics is formed on a surface of each bead in the first layer once the bead is contacted with the ambient atmosphere. As beads in the first layer cool, cores of beads partially solidify under ambient temperature. A second layer of beads is deposited on top of the first layer. A stabilizing shell composed of native oxides of alloying elements and metastable intermetallics is formed on a surface of each bead in the second layer once the bead is contacted with ambient atmosphere. As beads in the second layer cools, oxides break up and metastable intermetallics decompose at the layer-to-layer interface, thereby forming a eutectic intermetallic at the interface. The exothermic reaction causes localized welding of layers. -
FIG. 16 is a flowchart illustrating a fifth mechanism that may account for the formation of fused layers of alloy beads. As shown, a molten alloy of the present invention is extruded onto a substrate, thereby forming a first layer of beads. A stabilizing shell composed of metastable intermetallics is formed on a surface of each bead in the first layer once the bead is contacted with the ambient atmosphere. As beads in the first layer cool, cores of beads partially solidify under the ambient temperature. A second layer of beads is deposited on top of the first layer. A stabilizing shell composed of metastable intermetallics is formed on a surface of each bead in the second layer once the bead is contacted with the ambient atmosphere. As beads in the second layer cools, the metastable intermetallics decompose at the layer-to-layer interface, thereby forming a eutectic intermetallic at the interface. The exothermic reaction causes localized welding of layers. - An Al-6Ce alloy containing 6 wt. % of Ce was tested and found to have suitable beading characteristics attributable to formation of a rare earth-rich shell at the exposed surface of the bead.
-
FIG. 17 is a plot of photoelectron spectroscopy (XPS) data for an as-cast sample of an Al-6Ce alloy, whileFIG. 18 shows XPS data for the Al-6Ce alloy following sputter etching to remove about 12 nm of surface material. The peak resulting from the presence of oxide has near zero intensity, which indicates that the stabilizing shell is on the order of 10-15 nm in thickness. -
FIGS. 19 and 20 show respective XPS data for heat-treated and heat-treated sputter-etched samples of the Al-6Ce alloy.FIGS. 21 and 22 show respective XPS data for oxidized and oxidized sputter-etched samples of the Al-6Ce alloy. The data show that, after 12 nm of etching, the oxide present at the surface of the material has dissipated and the internal structure is bulk metallic material. -
FIGS. 23 and 24 show respective low and high magnification SEM images of the Al-6Ce alloy respectively. The SEM images show a low content (˜6.7 weight %) of a eutectic Al11Ce3 intermetallic phase. Al11Ce3 eutectic intermetallic and Al microconstituent surrounds the primary Al FCC grains. The microstructure shows a divorced morphology. -
FIG. 25 shows DSC data for the Al-6Ce alloy. It can be seen that the Al-6Ce alloy starts to melt at approximately 640° C., and there are no measurable phase shifts before the Al-6Ce alloy melts. -
FIG. 26A shows a SEM image of fused beads of the Al-6Ce alloy.FIG. 26B is a higher magnification SEM image showing the wetting surface of the fused beads ofFIG. 26A . The light gray areas represent eutectic Al11Ce3 phases, and the dark gray area represents an Al phase. It can be seen the amount of the eutectic Al11Ce3 phases in the interface of the beads is greater than that of the eutectic Al11Ce3 phases within the beads. The formation of the Al11Ce3 eutectic intermetallic at the interface is believed to be primarily involved in the welding of the beads. - Al—Ce—Si alloys exhibit similar rheological properties to that of the binary Al—Ce alloy. At high intermetallic contents (>7.5 wt. %), the Al—Ce—Si alloys flow too well and, as a result, will not bead sufficiently for printing. Thus, it is necessary to maintain an overall low content of intermetallic (0.50 to up to 7.5 wt %) when utilizing ternary or quaternary additions to the binary alloy.
-
FIGS. 27-32 provide detailed characteristics of the Al—Ce—Si alloy family and intermetallic properties thereof.FIG. 27 shows a full ternary isotherm for the Al—Ce—Si ternary alloy family at 639° C., andFIG. 28 shows an enlarged portion of the Al—Ce—Si ternary alloy family shown inFIG. 27 below the 10 wt.% line 40. Heavy dashed lines 42 and 44 represent respective position of isopleths and property diagrams at 93 wt. % Al and 97 wt. % Al.FIGS. 29 and 31 show the isopleth and property diagrams along the 93 wt. % Al composition line A shown inFIG. 27 .FIGS. 30 and 32 show the isopleth and property diagrams along 97 wt. % Al composition line B shown inFIG. 27 . - The data in
FIGS. 27-32 show that in instances where Al content is held constant but the Si and Ce are varied to balance, the different phases which precipitate form out of the melt and the base Al-6Ce contains roughly 7 weight % intermetallic, which is near the maximum intermetallic content that is suitable for structural direct-write additive manufacturing. Thus, in order to precipitate the same weight percent of Al—Ce—Si intermetallic, it is required that the overall composition is greater than 7 wt. % alloying additions. In the case of the Al—Ce—Si alloy, the highest weight % of alloying elements which produce the necessary low amount of ternary intermetallic is about 9 wt. % of alloying additions, including 2 weight % of Si and 7 wt. % of Ce. - A low percentage of intermetallic (also called non-aluminum) phase fraction is preferable for the alloy. For example, for Al—Ce—Si alloys, an upper limit for 7 weight % of Ce results in an intermetallic content of about 6.66 weight %. Taking 6.66 weight % of intermetallic phase to be the upper limit for the Al—Ce—Si alloys, the amount of Ce and Si that should be present in the alloy can be calculated. Taking into account the lower limit of 0.5 wt. % Ce, which results in an intermetallic content of 0.549 wt. % intermetallic, the same relationship can be drawn.
-
FIG. 33 shows a plot of the lower limits of Ce and Si that result in 0.549 wt. % of intermetallic phase, where (Si)=−0.4004 (Ce)+0.5254. An asymptotic behavior is observed at 0.5 wt. % cerium, wherein a small addition of Si greatly increases the amount of alloying addition necessary to reach the 0.549 wt. % intermetallic phase due at least in part to the good solubility of Si in Al. However, following the quick asymptotic behavior, the relation is linear. The intercept value reflects the weight percentage of Si necessary to obtain 0.549 wt. % of non-aluminum phase. -
FIG. 34 shows a similar relationship for the upper limits of Ce and Si that result in 6.66 wt. % of intermetallic phase, where (Si)=−0.454 (Ce)+6.896. At the upper limit of 7 wt. % Ce, there is a distinct asymptotic behavior, but as Si is added, the relationship quickly becomes linear. -
FIG. 35 is a ternary phase diagram that shows a more graphical representation of the data presented inFIGS. 33 and 34 .FIG. 36 shows an Al—Ce—Si ternary isotherm at 100° C. in the Al-rich region of the ternary phase diagram.FIG. 37 shows an Al—Ce—Si ternary isotherm at 500° C.FIG. 38 shows the presence of the liquid phase in the Al-rich region of the Al—Ce—Si ternary liquidus phase diagram. Heavy lines 52, 54 inFIGS. 35-38 represent phase compositional boundaries within which intermetallic content limits are satisfied. The area within lines 52, 54 represents Ce and Si contents of suitable compositions for structural direct-write additive manufacturing. Reference is also made to the respective isothermal lines inFIGS. 27 and 28 . - While there have been shown and described what are at present considered the preferred embodiments of the invention, those skilled in the art may make various changes and modifications which remain within the scope of the invention defined by the appended claims.
Claims (20)