US20170292332A1 - Polycrystalline Diamond Compact Cutter Having Surface Texturing - Google Patents
Polycrystalline Diamond Compact Cutter Having Surface Texturing Download PDFInfo
- Publication number
- US20170292332A1 US20170292332A1 US15/510,547 US201515510547A US2017292332A1 US 20170292332 A1 US20170292332 A1 US 20170292332A1 US 201515510547 A US201515510547 A US 201515510547A US 2017292332 A1 US2017292332 A1 US 2017292332A1
- Authority
- US
- United States
- Prior art keywords
- polycrystalline diamond
- volume
- textured surface
- cutter
- chamfer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Description
- The present disclosure relates to a polycrystalline diamond compact (PCD) cutter having a textured surface for increasing surface area for heat transfer, decreasing chipping or breaking of the cutter and/or providing a termination point for crack formation.
- Abrasive compacts consist of a mass of diamond or cubic boron nitride particles bonded into a coherent, polycrystalline hard conglomerate. The abrasive particle content of abrasive compacts is high and there is an extensive amount of direct particle-to-particle bonding. Abrasive compacts tend to be brittle and in use they are frequently supported by being bonded to a cemented carbide substrate or support.
- Polycrystalline diamond (“PCD”) abrasive compacts are used extensively in cutting, milling, grinding, drilling and other abrasive operations. In some of these applications large forces act on the point or cutting edge and cracks develop in or behind the cutting edge or point. These cracks can propagate through the compact layer.
- Cutter performance is limited by the amount of surface area to dissipate heat, as well as friction generated by the chip and coolant flow running across the face of the cutter. Additionally, cutters experience impact damage, resulting in large cracks which propagate through the diamond, leading to large loss of the diamond table.
- To limit crack propagation it is known to provide a pattern on the top surface of the diamond table. However, focusing the pattern on the top surface of the cutter does not effectively limit crack propagation or other damage.
- Another problem is that in order to effectively limit propagation of cracks and to limit breaking, spalling or chipping, a fairly large amount of diamond volume is required to be removed when forming the pattern along the top surface of the compact. This compromises the abrasion resistance of the cutter.
- In one embodiment a polycrystalline diamond compact cutter for a tool includes a substrate of cemented carbide and a volume of polycrystalline diamond bonded to the substrate. At least one chamfer extends along an outer circumference of the volume of polycrystalline diamond. A textured surface is disposed on at least the at least one chamfer. The textured surface provides a termination point for crack formation, an increased surface area for heat transfer, and decreases chipping of the volume of polycrystalline diamond.
- In another embodiment a method for forming a polycrystalline diamond compact cutter includes the steps of providing a cemented carbide substrate and disposing a volume of polycrystalline diamond material on the cemented carbide substrate. The substrate and volume of diamond material are subjected to a high pressure and a high temperature condition to bond the volume of polycrystalline diamond material and substrate. A textured surface is formed on at least at least one chamfer disposed along an outer circumference of the volume of polycrystalline diamond to provide a termination point for crack formation, an increased surface area for heat transfer, and to decrease chipping of the volume of polycrystalline diamond.
- In yet another embodiment, a drilling bit includes a cutting element of a volume of polycrystalline diamond. The cutting element includes a cutting edge formed by at least one chamfer extending along an outer circumference of the cutting element. A textured surface is disposed on at least the at least one chamfer to provide a termination point for crack formation, an increased surface area for heat transfer, and decreasing chipping of the volume of polycrystalline diamond. The drill bit includes a substrate of cemented carbide, the cutting element being bonded to the substrate.
- In one aspect, having a textured surface with features patterned on the chamfer of the cutter enhances the toughness of a given cutter in an impact damage mode thereby minimizing spalling and chipping at the cutting edge.
- In another aspect, the textured surface provides a greater surface area to increase heat transfer at the cutting edge.
- In yet another aspect, the textured surface being provided on the chamfer of the cutter limits the amount of diamond removed from the volume allowing the cutter to be leached.
- The foregoing summary, as well as the following detailed description of the embodiments, will be better understood when read in conjunction with the appended drawings. It should be understood that the embodiments depicted are not limited to the precise arrangements and instrumentalities shown.
-
FIG. 1 is an image of a conventional PCD cutter having impact damage. -
FIG. 2 is a perspective view of an embodiment of a surface textured PCD cutter according to the present disclosure. -
FIG. 3 is a top view of the cutter ofFIG. 2 . -
FIG. 4 is a side view of the cutter ofFIG. 2 . -
FIG. 5 is a perspective view of another embodiment of a surface textured PCD cutter. -
FIG. 6 is a top view of the cutter ofFIG. 5 . -
FIG. 7 is a side view of the cutter ofFIG. 5 . -
FIG. 8 is a perspective view of yet another embodiment of a surface textured PCD cutter. -
FIG. 9 is a top view of the cutter ofFIG. 8 . -
FIG. 10 is a side view of the cutter ofFIG. 8 . -
FIG. 11 is a cross-section of the cutter taken along line I-I ofFIG. 9 . -
FIG. 12 is still another embodiment of a surface textured PCD cutter. -
FIG. 13 is an enlarged view of the textured pattern of the cutter ofFIG. 12 . -
FIG. 14 is a top view of the cutter ofFIG. 12 . -
FIG. 15 is a side view of the cutter ofFIG. 12 . -
FIG. 16 is another embodiment of a surface textures PCD cutter. -
FIG. 17 is a top view of the cutter ofFIG. 16 . -
FIG. 18 is a side view of the cutter ofFIG. 16 . -
FIG. 19 is yet another embodiment of a surface textures PCD cutter. -
FIG. 20 is a top view of the cutter ofFIG. 19 . -
FIG. 21 is a side view of the cutter ofFIG. 19 . -
FIG. 22 is still another embodiment of a surface textures PCD cutter. -
FIG. 23 is a top view of the cutter ofFIG. 22 . -
FIG. 24 is a side view of the cutter ofFIG. 22 . -
FIG. 25 is an image of a PCD cutter of the present disclosure having limited crack propogation. - A polycrystalline diamond (“PCD”) cutter may be formed by placing a cemented carbide substrate into the container of a press. A mixture of diamond grains or diamond grains and catalyst binder is placed atop the substrate and compressed under high pressure, high temperature conditions. In so doing, metal binder migrates from the substrate and passes through the diamond grains to promote a sintering of the diamond grains. As a result, the diamond grains become bonded to each other to form the diamond layer, and the diamond layer is subsequently bonded to the substrate. The substrate is often a metal-carbide composite material, such as sintered tungsten carbide (tungsten carbide/cobalt).
- As set forth above, PCD compacts are used extensively in cutting, milling, grinding, drilling and other abrasive operations. In some of these applications large forces act on the point or cutting edge and cracks develop in or behind the cutting edge or point. Referring to
FIG. 1 , a conventional PCD cutter 5 is shown having frontal impact damage 7. In order to improve cutter performance the embodiments of the present disclosure have a textured surface along the top and chamfer, and/or bevel that are patterned in a way such as to increase the surface area for heat transfer, to act as a chip breaker, and/or to act as a termination point for crack formation. Moreover, improved toughness and thermal stability occur due to the pattern feature on the diamond table. - As used herein, the articles “a” and “an” are used herein to refer to one or more than one object of the article. By way of example, “an element” means one or more than one element. The term “about” will be understood by persons of ordinary skill in the art to depend on the context in which it is used. As used herein, “about” encompasses variations from ±10% of the reported nominal value. For example, “about 40” is meant to encompass from 36 to 44.
- As shown in
FIGS. 2-4 , a polycrystalline diamond “PCD”cutter 10 includes asubstrate 12, preferably comprised of cemented metal carbide, and a bed orvolume 14 of diamond particles or grains disposed onsubstrate 12.Substrate 12 is preferably a cobalt bonded tungsten carbide (Co-WC) substrate. However, it should be appreciated that other metal or cemented carbide materials can be used for the substrate. Moreover, volume ofPCD 14 andsubstrate 12 can be coated with a suitable material. -
PCD volume 14 includes a cuttingsurface 16 and anouter circumference 18 along which acutting edge 20 is disposed. Achamfer 24 extends along anouter circumference 18 from cuttingedge 20 by an angle, for example 45°. Although only one chamfer is shown it should be appreciated that a plurality of chamfers, either stacked above one another or extending along portions of theouter circumference 18, can be provided. Moreover,chamfer 24 can extend only partially along the height of anouter circumference 18 of the PCD volume. - Cutting
surface 16 andchamfer 24 includes atextured surface 30 formed therein. As will be described further herein, texturedsurface 30 can be applied into a plurality of different patterns by using a laser cutting technique. The laser cutting technique may incorporate a laser having wavelength and power selected to super-heat metal solvent catalyst material that remains in the polycrystalline diamond from the synthesis procedure. The superheating of the solvent metal catalyst may vaporize the solvent metal catalyst, and may carry diamond away, thereby forming a channel in the underlying diamond. The channel generally has a “u-shaped” form having a round bottom at positions generally parallel with the underlying diamond surface into which the channel is formed. The laser cutting technique may also cut diamond through an ablation mechanism. The laser cutting technique may be applied across multiple areas of the diamond, thereby forming atextured surface 30 on the diamond. When evaluated macroscopically, the channel appears as a line that is formed in the exterior surfaces of the diamond. As shown inFIGS. 2-4 textured surface 30 is formed by a radially-arrayedgrid pattern 32 formed by a plurality of intersectingradial lines 34 and radial circles 36. In some embodiments, thetexture surface 30 may not extend to the cylindrical surface of thePCD volume 14 that is spaced apart from thechamfer 24 and positioned opposite from the cuttingsurface 16. The radially arrayed elements that form thetextured surface 30 on thechamfer 24 may include at least two adjacent repeating elements that are spaced apart about 6 degrees or less from one another. The radially arrayed elements that form thetextured surface 30 on thechamfer 24 may include at least three adjacent repeating elements, where the outside repeating elements are spaced apart from the center repeating element by about 6 degrees or less from one another. The adjacent repeating elements may be spaced apart from one another in a range from out 2 degrees to about 6 degrees, for example, from about 3.6 to about 4.4 degrees, for example, about 4 degrees, or from about 2 degrees to about 4.4 degrees, for example, from about 2.7 degrees to about 4.4 degrees. In some embodiments, the repeating elements may be evenly spaced around the circumference of thechamfer 24. In other embodiments, the repeating elements may be unevenly spaced around the circumference of thechamfer 24. - As shown in
FIGS. 2 and 3 , texturedsurface 30 can be provided along aperiphery portion 28 of cuttingsurface 16. For example,periphery portion 28 having texturedsurface 30 can be approximately 20% of the geometric area of the cuttingsurface 16. It should be appreciated that more or less of the cuttingsurface 16 can include the texturing, for example, up to about 50% of the geometric area, as long as the volume of diamond is not decreased to the point to negatively affect performance. Also by providing the textured surface pattern on only a portion of surface versus across the entire diamond table, the percentage loss of diamond is smaller, for example, less than 5%. -
Radial lines 34 andradial circles 36 can have a depth of about 10 μm to about 0.1 mm and a width of about 0.002″ (inches) to about 0.004″ (inches).Radial lines 34 are spaced at about 4 degrees. Radial circles 36 are spaced at about 0.020″ from one another. ThePCD volume 14 has a nominal outer diameter of 16 mm. - As shown in
FIGS. 5-7 , texturedsurface 30 can be formed by a pattern of a plurality of the radial circles 36. In this embodiment, the radial circles can have the same depth and width as described above, however, the spacing of the lines alongperiphery portion 28 can be decreased to about 0.004″. - Referring to
FIGS. 8-10 , texturedsurface 30 can also be a pattern formed solely byradial lines 34, with the dimensions thereof being the same as described above. The spacing between at least two adjacent radial lines may be selected in a range from about 2 degrees to about 6 degrees, for example, from about 3.6 to about 4.4 degrees, for example, about 4 degrees, or from about 2 degrees to about 4.4 degrees, for example, from about 2.7 degrees to about 4.4 degrees. In some embodiments, the spacing between adjacent radial lines may be approximately even when evaluated around the diameter of thePCD volume 14. In other embodiments, the spacing between adjacent radial lines may be uneven when evaluated around the diameter of thePCD volume 14.Radial lines 34 can extend completely through the volume of diamond or as shown inFIG. 11 , the radial lines can extend a distance into the volume of diamond that is less than the complete thickness of the diamond, as will be described further herein. - Referring to
FIGS. 12-15 , texturedsurface 30 can be formed with a pattern of a plurality ofradial circles 38 having repeating spherical shapes that are superimposed on theradial circles 38 and located along bothperiphery portion 28 andchamfer 24, forming so-called spherical radial circles 38. In one example, the repeating spherical shapes may have a nominal diameter of from about 0.010″ to about 0.050″. Spherical radial circles 38 can have the same depth and width as described above. - It should be appreciated that radial lines are not limited to straight or smooth lines. Wavy, or irregular lines may also assist with heat dissipation.
- As shown in
FIGS. 16-18 ,PCD cutter 10 has a texturedsurface 30 having apattern 40 cut into theperiphery portion 28. As shown inFIG. 18 ,lines 42 ofpattern 40 extend intochamfer 24. The width of eachline 42 of the pattern can be about 10 μm to about 0.5 mm and the depth about 10 μm to about 0.1 mm, measured into the surface. -
Pattern 40 can be a repeat ofpattern sections 44, for example, from about 3 (as shown) to about 5 sections disposed about theperiphery portion 28. Accordingly, the cutter may have a plurality of areas such that when onesection 44 is worn, the cutter can be rotated to another section in which thepattern 40 repeats, and the cutter may be run again, presenting equivalent textured surfaces for the material removal operation. - Referring to
FIGS. 19-21 ,PCD cutter 10 can have the texturedsurface 30 only onchamfer 24. As shown, cuttingsurface 16 can be free of texturing/patterning.Textured surface 30 can be formed byradial lines 46. As depicted inFIG. 19 , theradial lines 46 may be oriented to be non-planar with an axis of symmetry of thePCD cutter 10. In other embodiments (see, e.g., the radial lines along thechamfer 24 ofFIGS. 2-4 ), theradial lines 46 may be oriented to be planar with an axis of symmetry of thePCD cutter 10. The radial lines 46 terminate at locations corresponding to the termination of thechamfer 24 at the cuttingsurface 16 and the generally-cylindrical surface along the outer diameter of thevolume 14 of diamond particles.Radial lines 46 have a maximum depth of about 10 μm to about 0.1 mm and a width of about 0.002″ to about 0.004″. It should be appreciated that the depth of each radial line can vary from, for example, the inside to outside (cutting edge to substrate). - The radial lines can be spaced from about 0.01″ to about 0.02″ apart from one another. The spacing between the radial lines determines how aggressively the cutter engages the rock or other material being drilled. As can be seen from
FIGS. 19-21 , the size and the spacing of the radial lines provides more diamond along thechamfer 24 than void along thechamfer 24. For example, with a spacing of 0.01″ and a width of 0.004″, diamond accounts for approximately 60% of the material along thechamfer 24. With a spacing of 0.02″ and a width of 0.002″, diamond accounts for approximately 90% of the material along thechamfer 24. - Referring to
FIGS. 22-24 ,PCD cutter 10 can have a texturedsurface 50 having a plurality ofdifferent patterns patterns surface 50 located onperiphery portion 28 can havecircle pattern 52, sphericalradial circle 54 and curved radial lines 56.Textured surface 50 located on chamfer can have a similar pattern or adifferent pattern 58 as shown. It should be appreciated that the negative portions of patterned,textured surfaces - The PCD cutters of the present disclosure can be formed by providing a cemented carbide substrate, disposing a volume of polycrystalline diamond material on the cemented carbide substrate and subjecting the substrate and volume of diamond material to a high pressure and a high temperature condition to bond the volume of diamond material and substrate.
- The textured surface is formed by laser cutting. The compact is placed in a laser cutting machine and aligned properly so that the CAD-driven laser cuts the pattern appropriately. The pattern of the textured surface can be applied to a desired portion of the PCD volume. However, the textured surface if formed on at least a chamfer disposed along an outer circumference of the volume of polycrystalline diamond to provide a termination point for crack propagation and to decrease chipping of the volume of polycrystalline diamond. As set forth below, when a crack does occur it may run along the pre-cut line of the textured surface in the chamfer and terminate before the crack grows into the cutting surface, thereby preserving the structural integrity of the surrounding portions of the cutter.
- As set forth above, the textured surface can have a variety of patterns. The more patterns/lines cut into the PCD volume the greater the surface area and increased heat transfer and more cutting edges.
- After the textured surface is applied to the PCD volume the cutter can be finished, for example, leached, cleaned or machined.
- Another feature of the PCD cutter of the present disclosure is that leaching to remove retained metal solvent catalyst that remains in the diamond from the synthesis process is improved due to the positioning of the radial lines of the pattern and volume removal. It is believed that it is not feasible to leach a cutter that has been cut deeply. Such cutters that are deeply cut may expose the carbide to the leaching acid, thereby impairing the structural integrity of the cutter. The PCD cutter of the present disclosure having cuts that extend a distance less than the thickness of the diamond will still allow the cutter to be leachable. Referring again to
FIG. 11 , leaching flow, shown byline 70, varies from leached to non-leached portions, i.e., where the leaching agent extends into the grooves of the patterns of the textured surface. The thermal expansion difference is improved between the leached to non-leached portions and this limits stress within the PCD volume decreasing the frequency and size of chips and limiting crack propagation. - Additionally, less volume of diamond is removed while still benefiting from the crack arresting features.
- Laboratory tests of cutter performance were conducted using a series of instrumentation. Frontal impact testing was performed to observe crack propagation in a surface textured and a conventional, untextured cutter. In this test, cutters are mounted to a dead-weight drop system at an inclined angle, and dropped against a hard work piece, such as a hardened steel block, tungsten carbide block, or volume of sintered diamond. Cutters are dropped from various heights to control the energy of impact. Testing was also performed in an interrupted milling of rock. Cutters are mounted on a fly wheel and rotated at high speed as a slab of rock is feed into the rotating path of the cutter. In this work, the rock used was barre granite. As the cutter rubs across the face of the rock without coolant, rapid heating of the cutter occurs, leading to accelerated thermal breakdown of the PCD cutter.
- Referring to Table 1 below although the pattern of the textured surface acts as a crack arrestor, see
FIG. 25 , whereby acrack 50 was arrested bysurface texture 30, surface texturing did not alter cutter performance (no degradation) in a thermally challenging test. Hence the ability to arrest impact cracking thereby improves the overall durability of the cutters. -
TABLE 1 Interrupted Mill Cutter Test Score Standard Cutter 3.36 Surface Textured 3.44 Cutter (see FIG. 25) - 1. A polycrystalline diamond cutter for a tool, comprising:
- a substrate of cemented carbide;
- a volume of polycrystalline diamond bonded to said substrate;
- at least one chamfer extending along an outer circumference of the volume of polycrystalline diamond; and
- a textured surface disposed on at least the at least one chamfer, wherein the textured surface has at least about 60% diamond along the at least one chamfer, and the textured surface provides a termination point for crack formation, an increased surface area for heat transfer, and decreasing chipping of the volume of polycrystalline diamond.
- 2. The polycrystalline diamond cutter of item 1, wherein the textured surface is a pattern formed in the volume of polycrystalline diamond.
3. The polycrystalline diamond cutter of items 1 or 2, wherein the textured surface is disposed only on the at least one chamfer.
4. The polycrystalline diamond cutter of any one of the above items, wherein the volume of polycrystalline diamond includes a cutting surface having a periphery portion, the textured surface being disposed on the periphery portion and the at least one chamfer.
5. The polycrystalline diamond cutter of any one of the above items, wherein the periphery portion is about 20% of an area of the cutting surface.
6. The polycrystalline diamond cutter of any one of the above items, wherein the pattern is a grid formed by a plurality of intersecting radial lines and radial circles.
7. The polycrystalline diamond cutter of any one of the above items, wherein the pattern is a plurality of radial lines.
8. The polycrystalline diamond cutter of any one of the above items, wherein the pattern is a plurality of radial circles.
9. The polycrystalline diamond cutter any one of items 6-8, wherein each of the radial circles and/or each of the radial lines has a depth of about 10 μm to about 0.1 mm and a width of about 0.002″ to about 0.004″.
10. The polycrystalline diamond cutter of any one of the above items, wherein the pattern is formed by a plurality of different intersecting patterns.
11. The polycrystalline diamond cutter of any one of the above items, wherein the pattern is a formed by a plurality of pattern sections extending along the periphery portion and at least one chamfer.
12. The polycrystalline diamond cutter of any of the above items, wherein spacing between at least two adjacent radial lines is in a range from about 2 degrees to about 6 degrees.
13. The polycrystalline diamond cutter of any of the above items, wherein spacing between at least two adjacent radial lines is in a range from about 3.6 degrees to about 4.4 degrees.
14. A method for forming a polycrystalline diamond cutter, comprising the steps of: - providing a cemented carbide substrate;
- disposing a volume of polycrystalline diamond material on the cemented carbide substrate;
- subjecting said substrate and volume of diamond material to a high pressure and a high temperature condition to bond said volume of diamond material and substrate; and
- forming a textured surface on at least at least one chamfer disposed along an outer circumference of the volume of polycrystalline diamond, wherein the textured surface has at least about 60% diamond along the at least one chamfer, and the textured surface providing a termination point for crack formation, an increased surface area for heat transfer, and to decrease chipping of the volume of polycrystalline diamond.
- 15. The method of
item 14, wherein the textured surface is a pattern formed in the volume of polycrystalline diamond.
16. The method ofitems 14 or 15, wherein the textured surface is formed only on the at least one chamfer.
17. The method of any one of items 14-16, wherein the volume of polycrystalline diamond includes a cutting surface having a periphery portion, the textured surface being disposed on the periphery portion and the at least one chamfer.
18. The method of any one of items 14-17, wherein the periphery portion is about 20% of an area of the cutting surface.
19. The method of any one of items 14-18, wherein the pattern is a grid formed by a plurality of intersecting radial lines and radial circles.
20. The method of any one of items 14-19, wherein the pattern is a plurality of radial lines.
21. The method of any one of items 14-20, wherein the pattern is a plurality of radial circles.
22. The method of any one of items 19-21, wherein each of the radial circles and/or each of the radial lines has a depth of about 10 μm to about 0.1 mm and a width of about 0.002″ to about 0.004″.
23. The method of any one of items 14-22, wherein the pattern is formed by a plurality of different intersecting patterns.
24. The method of any one of items 14-23, wherein the pattern is a formed by a plurality of pattern sections extending along the periphery portion and at least one chamfer.
25. The method of any one of items 14-24, further comprising the step of leaching the volume of polycrystalline diamond.
26. The method of any one of items 14-25, wherein spacing between at least two adjacent radial lines is in a range from about 2 degrees to about 6 degrees. - Although the present embodiment(s) has been described in relation to particular aspects thereof, many other variations and modifications and other uses will become apparent to those skilled in the art. It is preferred therefore, that the present embodiment(s) be limited not by the specific disclosure herein, but only by the appended claims.
Claims (30)