US20170226656A1 - Apparatus and method for supplying plating solution to plating tank, plating system, powder container, and plating method - Google Patents
Apparatus and method for supplying plating solution to plating tank, plating system, powder container, and plating method Download PDFInfo
- Publication number
- US20170226656A1 US20170226656A1 US15/426,631 US201715426631A US2017226656A1 US 20170226656 A1 US20170226656 A1 US 20170226656A1 US 201715426631 A US201715426631 A US 201715426631A US 2017226656 A1 US2017226656 A1 US 2017226656A1
- Authority
- US
- United States
- Prior art keywords
- plating
- solution
- powder
- tank
- plating solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Description
- This document claims priorities to Japanese Patent Application Number 2016-023224 filed Feb. 10, 2016 and Japanese Patent Application Number 2016-220952 filed Nov. 11, 2016, the entire contents of which are hereby incorporated by reference.
- The present invention relates to an apparatus and a method for supplying a plating solution to a plating tank. The present invention also relates to a plating system having such an apparatus. The present invention also relates to a powder container for holding metal powder to be used in plating. Further, the present invention relates to a method of plating a substrate using a plating solution to which metal powder for use in plating has been added.
- As electronics are becoming smaller in size, higher speed, and less power consumption, interconnect patterns in a semiconductor device are becoming finer and finer. With the progress toward finer interconnect patterns, materials used for interconnects are changing from conventional aluminum and aluminum alloys to copper and copper alloys. The resistivity of copper is 1.67 μΩcm, which is about 37% lower than the resistivity (2.65μΩcm) of aluminum. Therefore, compared to aluminum interconnects, copper interconnects can not only reduce power consumption, but can also be made finer with the same interconnect resistance. In addition, because of the lower resistance, copper interconnects have the advantage of reduced signal delay.
- Filling of copper into trenches is generally performed by electroplating which can form a film faster than PVC or CVD. In the electroplating, a voltage is applied between a substrate and an anode in the presence of a plating solution to deposit a copper film on a low-resistance seed layer (or a feeding layer) which has been formed in advance on the substrate. Such a seed layer is generally comprised of a thin copper film (copper seed layer) formed by, for example, PVD. Since there is a demand for a thinner seed layer with the progress toward finer interconnects, the thickness of the seed layer, which is generally of the order of 50 nm, is expected to decrease to not more than 10 nm to 20 nm in the future.
- The applicant has proposed a plating apparatus that uses a plurality of concentrically-divided separate anodes which are individually connected to a plating power source (see Japanese Patent Laid-Open Publication No. 2002-129383). According to this plating apparatus, a current density of a centrally-located separate anode is made higher than an outer separate anode for a certain period of time when an initial plating film is formed on a substrate, thereby preventing a plating current from concentrating in the peripheral portion of the substrate, and allowing the plating current to flow also in the central portion of the substrate. This makes it possible to form a plating film having a uniform thickness even when a sheet resistance is high. The applicant has also proposed a plating technique that uses an insoluble anode (see Japanese Patent Laid-Open Publication No. 2005-213610 and Japanese Patent Laid-Open Publication No. 2008-150631). An anode holder for holding the insoluble anode is provided with a plating-solution discharge section for sucking and discharging a plating solution out of an anode chamber, and is also provided with a plating-solution injection section connected to a plating-solution supply pipe extending from a plating-solution supply apparatus.
- In order to meet the recent demand for a smaller circuit system using semiconductors, implementation of semiconductor circuits in a package having approximately the same size as a chip has come into practical use. A packaging method called wafer level package (WLP) has been proposed as a method to perform implementation of semiconductor circuits in such a package. The wafer level package is generally classified into fan-in technique (also called WLCSP (Wafer-Level Chip-Scale Package)) and fan-out technique. The fan-in WLP is a technique for providing external electrodes (external terminals) in a chip-size area. The fan-out WLP, on the other hand, is a technique for providing external terminals in an area larger than a chip, for example, forming a re-distribution layer and external electrodes on a substrate formed of an insulating resin in which a plurality of chips are embedded. An electroplating technique is sometimes used for forming a re-distribution layer, an insulating layer, etc. on a wafer, and is expected to be applied also in the fan-out WLP. A higher level of technique, especially in control of a plating solution, is required in order to apply the electroplating technique in the fan-out WLP or the like for which finer pitches are strongly required.
- With a view to performing so-called bottom-up plating, the applicant has proposed a method of plating a substrate, such as a wafer, while preventing a generation of an electrolyte component which inhibits bottom-up plating (see Japanese Patent Laid-Open Publication No. 2016-074975). This method involves bringing an insoluble anode and a substrate into contact with a copper sulfate plating solution containing additives, and applying a predetermined plating voltage from a plating power source to between the substrate and the insoluble anode to plate the substrate.
- On the other hand, in order to replenish a plating solution with objective metal ions in a plating apparatus which uses an insoluble anode as described above, it is conceivable to use a method in which a powdery metal salt is fed into a circulation tank or a method in which metal pieces are dissolved in a separate tank for replenishment. When the powdery metal salt is supplied into a plating solution, fine particles increases in the plating solution and may cause a defect in a surface of a plated substrate. In view of this, the applicant has proposed a technique which can keep concentrations of components of a plating solution constant over a long period of time in a plating apparatus that uses an insoluble anode (see Japanese Patent Laid-Open Publication No. 2007-051362). This technique, which involves circulating and reusing a plating solution while recovering the plating solution, can minimize the amount of the plating solution used. Further, the use of an insoluble anode can eliminate the need for replacement of the anode, thereby facilitating maintenance and management of the anode. Furthermore, the concentration of a component(s) of the plating solution, which changes with the circulation and reuse of the plating solution, can be maintained within a certain range by supplying a replenishing solution, containing the plating solution component(s) at a concentration high than the plating solution, to the plating solution.
- When plating of a substrate with copper is performed using an insoluble anode, copper ions in a plating solution decrease gradually. It is therefore necessary for a plating-solution supply apparatus to adjust the copper ion concentration in the plating solution. One possible method to replenish the plating solution with copper is to add copper oxide powder to the plating solution. However, if the powder scatters in a semiconductor manufacturing plant, it will cause pollution of a clean room. Further, the plating-solution supply apparatus is required to add a necessary amount of copper oxide powder to the plating solution without decreasing the throughput. In addition, there is an increasing demand for a plating technique which can form a higher-quality copper film on a substrate with use of such a plating solution to which copper oxide has been added.
- In one embodiment, there is provided an improved apparatus and method for adding powder comprising at least a metal, such as copper, to a plating solution, and supplying the plating solution to a plating tank. In one embodiment, there is provided a plating system including such an apparatus. In one embodiment, there is provided a powder container for holding therein powder comprising at least a metal, such as copper, to be used in the above-described apparatus. In one embodiment, there is provided a plating method which can form a higher-quality metal film on a substrate with use of a plating solution to which powder comprising at least a metal, such as copper, has been added.
- According to an embodiment, there is provided an apparatus for supplying a plating solution, in which powder comprising at least a metal to be used in plating has been dissolved, to a plating tank, comprising: a hopper having an inlet which is connectable to a powder conduit of a powder container holding the powder therein; a feeder which communicates with a bottom opening of the hopper; a motor coupled to the feeder; and a plating-solution tank coupled to an outlet of the feeder and configured to dissolve the powder in the plating solution.
- In an embodiment, the apparatus further comprises: a weight measuring device configured to measure a weight of the hopper and the feeder; and an operation controller configured to control an operation of the motor based on a change in a measured value of the weight.
- In an embodiment, the operation controller is configured to calculate an amount of the powder added to the plating solution from a change in the measured value of the weight, and instruct the motor to operate until the amount of the added powder reaches a target value.
- In an embodiment, the inlet of the hopper has a connecting seal whose inner diameter gradually decreases with a distance from a distal end of the inlet.
- In an embodiment, the connecting seal is composed of an elastic material.
- In an embodiment, the apparatus further comprises an airtight chamber in which the inlet of the hopper is located, the airtight chamber including a door which allows the powder container to be carried into the airtight chamber, and a glove which constitutes part of a wall of the airtight chamber.
- In an embodiment, the airtight chamber further includes an exhaust port for connecting an interior space to a negative-pressure source.
- In an embodiment, a vibrating device capable of vibrating the powder container is disposed in the airtight chamber.
- In an embodiment, a vacuum clamp capable of holding the powder container is disposed in the airtight chamber.
- In an embodiment, the plating-solution tank includes an agitation device for agitating the plating solution.
- In an embodiment, the plating-solution tank includes an agitation tank in which the agitation device is disposed, and an overflow tank coupled to a through-hole formed in a lower portion of the agitation tank.
- In an embodiment, the plating-solution tank further includes a detour passage located adjacent to the overflow tank.
- In an embodiment, the plating-solution tank further includes a plurality of baffle plates disposed in the overflow tank, the plurality of baffle plates being staggered.
- In an embodiment, the apparatus further comprises: an enclosure cover that surrounds connection portions of the feeder and the plating-solution tank; and an inert-gas supply line which communicates with an interior of the enclosure cover.
- According to one embodiment, there is provided a plating system comprising: a plurality of plating tanks each for plating a substrate; a plating-solution supply apparatus including (i) a hopper having an inlet which is connectable to a powder conduit of a powder container holding therein powder comprising at least a metal to be used in plating of the substrate, (ii) a feeder which communicates with a bottom opening of the hopper, (iv) a motor coupled to the feeder, and (v) a plating-solution tank coupled to an outlet of the feeder and configured to dissolve the powder in a plating solution; and a plating-solution supply pipe extending from the plating-solution supply apparatus to the plating tanks.
- In an embodiment, the plating system further comprises a plating-solution return pipe extending from the plating tanks to the plating-solution supply apparatus.
- According to one embodiment, there is provided a method of supplying powder, comprising at least a metal to be used in plating, to a plating solution, comprising: coupling a powder conduit of a powder container, holding the powder therein, to an inlet of a hopper; supplying the powder from the powder container to the hopper; operating a feeder which communicates with a bottom opening of the hopper while measuring a weight of the feeder and the hopper in which the powder is stored; and adding the powder to the plating solution by the feeder based on a change in a measured value of the weight.
- In an embodiment, the method further comprises agitating the plating solution to which the powder has been added.
- In an embodiment, the method further comprises: calculating an amount of the powder added to the plating solution from a change in the measured value of the weight; and operating the feeder until the amount of the added powder reaches a target value.
- According to one embodiment, there is provided a powder container for holding powder comprising at least a metal to be used in plating, comprising: a container body capable of holding the powder therein; a powder conduit coupled to the container body; and a valve attached to the powder conduit.
- In an embodiment, a distal end of the powder conduit has a shape of a truncated cone.
- According to one embodiment, there is provided a method of plating a substrate, comprising: delivering a plating solution from a plating tank to a plating-solution tank; calculating an amount of powder to be added to the plating solution held in the plating-solution tank based on a metal ion concentration in the plating solution in the plating tank, the powder comprising at least a metal to be used in plating; supplying the powder to the plating solution held in the plating-solution tank; dissolving the powder in the plating solution held in the plating-solution tank; supplying the plating solution, in which the powder has been dissolved, from the plating-solution tank to the plating tank; bringing a substrate into contact with the plating solution held in the plating tank; and causing an electrochemical reaction in the plating solution held in the plating tank to deposit the metal on a surface of the substrate.
- In an embodiment, the plating tank comprises a plurality of plating tanks, and wherein the plating solution is supplied from the plating-solution tank to each of the plating tanks while controlling a flow rate of the plating solution.
- In an embodiment, the plating tank comprises a plurality of plating tanks, and a metal ion concentration in the plating solution in the plurality of plating tanks is continually monitored; and when the metal ion concentration has become lower than a predetermined value, the plating solution in the plating tanks is delivered to the plating-solution tank, while the plating solution in the plating-solution tank is supplied to one of the plurality of plating tanks.
- According to one embodiment, there is provided a non-transitory computer-readable storage medium that stores a computer program for performing a method of electroplating a substrate, the method comprising: delivering a plating solution from a plating tank to a plating-solution tank; supplying powder to the plating solution held in the plating-solution tank, the powder comprising at least a metal to be used in plating; dissolving the powder in the plating solution held in the plating-solution tank; supplying the plating solution, in which the powder has been dissolved, from the plating-solution tank to the plating tank; bringing a substrate into contact with the plating solution held in the plating tank; and causing an electrochemical reaction in the plating solution held in the plating tank to deposit the metal on a surface of the substrate.
- According to one embodiment, there is provided a non-transitory computer-readable storage medium that stores a computer program for performing a method of electroplating a substrate, the method comprising: monitoring whether a concentration of metal ions contained in a plating solution in a plating tank is lower than a predetermined value; calculating an amount of powder to be added to the plating solution when the concentration of metal ions is lower than the predetermined value, the powder comprising at least a metal; delivering the plating solution from the plating tank to a plating-solution tank; supplying the powder to the plating solution held in the plating-solution tank until an amount of the added powder reaches the calculated amount; dissolving the powder in the plating solution held in the plating-solution tank; supplying the plating solution, in which the powder has been dissolved, from the plating-solution tank to the plating tank; bringing a substrate into contact with the plating solution held in the plating tank; and causing an electrochemical reaction in the plating solution held in the plating tank to deposit the metal on a surface of the substrate.
- The above-described embodiments can provide an apparatus and a method which can add the powder to a plating solution and dissolve the powder in the plating solution while preventing scattering of the powder. Further, according to the above-described embodiments, a high-quality metal film (e.g. copper film) can be formed on a substrate using a plating solution to which powder comprising at least a metal, such as copper, has been added.
- The powder container, the plating system, and the plating method described above can be used also when a substrate is to be plated with a metal species such as indium, nickel, cobalt, or ruthenium, other than copper. Examples of powders usable in such a case may include: sulfates such as indium sulfate, nickel sulfate and cobalt sulfate; sulfamates such as nickel sulfamate and cobalt sulfamate; halides such as nickel bromide, nickel chloride and cobalt chloride; and indium oxide.
-
FIG. 1 is a schematic overall view of a plating system according to a first embodiment; -
FIG. 2 is a side view of a powder container capable of holding copper oxide powder therein; -
FIG. 3 is a view showing the powder container with a cap off and a valve open; -
FIG. 4 is a perspective view of an airtight chamber; -
FIG. 5 is a view showing the interior of the airtight chamber; -
FIG. 6 is a view showing a distal end of a powder conduit of the powder container and an inlet of a hopper; -
FIG. 7 is a view showing the distal end of the powder conduit of the powder container and the inlet of the hopper when they are in tight contact with each other; -
FIG. 8 is a flow chart showing processes of supplying copper oxide powder from the powder container to the hopper; -
FIG. 9 is a side view showing the hopper and a feeder; -
FIG. 10 is a perspective view of a plating-solution tank; -
FIG. 11 is a plan view of the plating-solution tank; -
FIG. 12 is a vertical cross-sectional view of the plating-solution tank as viewed in a direction of arrow A shown inFIG. 11 ; -
FIG. 13 is a schematic view of another embodiment of a plating-solution tank; -
FIG. 14 is a schematic view of yet another embodiment of a plating-solution tank; -
FIG. 15 is a diagram showing results of an experiment which was conducted to examine the influence of the number of baffle plates on dissolution of copper oxide powder; -
FIG. 16 is a schematic overall view of a plating system according to a second embodiment; -
FIG. 17 is a flow chart showing a control sequence for adding copper oxide powder to a plating solution in the plating system according to the first embodiment; and -
FIG. 18 is a flow chart showing a control sequence for adding copper oxide powder to a plating solution in the plating system according to the second embodiment. - Embodiments will now be described with reference to the drawings.
FIG. 1 is a schematic overall view of a plating system according to a first embodiment. The plating system includes aplating apparatus 1 installed in a clean room, and a plating-solution supply apparatus 20 installed in a downstairs room. In this embodiment, theplating apparatus 1 is an electroplating unit for electroplating a substrate (e.g., a wafer) with copper, and the plating-solution supply apparatus 20 is a plating-solution supply unit for supplying powder, comprising at least copper, into a plating solution to be used in theplating apparatus 1. In this embodiment, copper oxide powder is used as the powder comprising at least copper, while it is also possible to use pelletized materials comprising at least copper. In this embodiment, an average particle size of the copper oxide powder is in the range of 10 micrometers to 200 micrometers, more preferably in the range of 15 micrometers to 50 micrometers. If the average particle size is too small, the powder is likely to scatter as dust. On the other hand, if the average particle size is too large, the solubility of the powder, when fed into a plating solution, may be poor. - In this specification, the term “powder” or “particles” herein encompasses solid particles, shaped granular materials, pelletized solid materials, small-diameter solid copper balls, a strip-shaped material obtained by shaping solid copper into a ribbon-like or tape-like shape, or a combination thereof.
- The
plating apparatus 1 has fourplating tanks 2. Eachplating tank 2 includes aninner tank 5 and anouter tank 6. Aninsoluble anode 8, held by ananode holder 9, is disposed in theinner tank 5. Further, in theplating tank 2, a neutral membrane (not shown) is disposed around theinsoluble anode 8. Theinner tank 5 is filled with a plating solution, which is allowed to overflow theinner tank 5 into theouter tank 6. Theinner tank 5 is also provided with a agitation paddle (not shown) comprised of a rectangular plate-like member having a constant thickness of 3 mm to 5 mm, made of a resin such as PVC, PP or PTFE, or a metal, such as stainless steel or titanium, coated with a fluororesin or the like. The agitation paddle reciprocates parallel to a substrate W to agitate the plating solution, so that sufficient copper ions and additives can be supplied uniformly to a surface of the substrate W. - The substrate W, such as a wafer, is held by a
substrate holder 11 and is immersed, together with thesubstrate holder 11, in the plating solution held in theinner tank 5 of theplating tank 2. The substrate W, as an object to be plated, may be a semiconductor substrate, a printed circuit board, etc. In the case of using a semiconductor substrate as the substrate W, the semiconductor substrate is flat or substantially flat (a substrate having a groove(s), a tube(s), a resist pattern(s), etc. is herein regarded as substantially flat). When plating such a flat object, it is necessary to control a plating condition over time in consideration of the in-plane uniformity of a plating film formed on the substrate, while preventing a deterioration in the quality of the film. - The
insoluble anode 8 is electrically connected via theanode holder 9 to a positive pole of aplating power source 15, while the substrate W held by thesubstrate holder 11 is electrically connected via thesubstrate holder 11 to a negative pole of theplating power source 15. When a voltage is applied from theplating power source 15 between theinsoluble anode 8 and the substrate W that are both immersed in the plating solution, an electrochemical reaction occurs in the plating solution held in theplating tank 2, whereby copper is deposited on the surface of the substrate W. In this manner, the surface of the substrate W is plated with copper. Theplating apparatus 1 may have less than four or more than four platingtanks 2. - The
plating apparatus 1 includes aplating controller 17 for controlling the plating process of the substrate W. The platingcontroller 17 has a function of calculating a concentration of copper ions contained in the plating solution in eachplating tank 2 from a cumulative value of electric current that has flowed in the substrate W. Copper in the plating solution is consumed as the substrate W is plated. The consumption of copper is proportional to the cumulative value of electric current that has flowed in the substrate W. The platingcontroller 17 can therefore calculate the copper ion concentration in the plating solution in eachplating tank 2 from the cumulative value of electric current. - The plating-
solution supply apparatus 20 includes anairtight chamber 24 into which apowder container 21, holding copper oxide powder therein, is to be carried, ahopper 27 for storing the copper oxide powder supplied from thepowder container 21, afeeder 30 which communicates with a bottom opening of thehopper 27, amotor 31 coupled to thefeeder 30, a plating-solution tank 35 coupled to an outlet of thefeeder 30 and configured to dissolve the copper oxide powder in a plating solution, and anoperation controller 32 for controlling the operation of themotor 31. Thefeeder 30 is actuated by themotor 31. An acidic copper sulfate plating solution containing sulfuric acid, copper sulfate, halogen ions, and organic additives, in particular a plating accelerator e.g. comprising SPS (bis(3-sulfopropyl) disulfide), a suppressor e.g. comprising PEG (polyethylene glycol) and a leveler e.g. comprising PEI (polyethylenimine), may be used as the plating solution. Chloride ions are preferably used as the halogen ions. - The
plating apparatus 1 and the plating-solution supply apparatus 20 are coupled to each other by a plating-solution supply pipe 36 and a plating-solution return pipe 37. More specifically, the plating-solution supply pipe 36 extends from the plating-solution tank 35 to a bottom of theinner tank 5 of eachplating tank 2. The plating-solution supply pipe 36 is divided into fourbranch pipes 36 a, which are coupled to the bottoms of theinner tanks 5 of the fourplating tanks 2, respectively. The fourbranch pipes 36 a are provided withrespective flow meters 38 and respectiveflow control valves 39. Theflow meters 38 and theflow control valves 39 are coupled to theplating controller 17. The platingcontroller 17 is configured to control a degree of opening of eachflow control valve 39 based on a flow rate of the plating solution measured by theflow meter 38. Therefore, the flow rates of the plating solutions supplied to theplating tanks 2 through the fourbranch pipes 36 a are regulated by theflow control valves 39, provided upstream of theplating tanks 2, so that the flow rates are kept substantially the same. The plating-solution return pipe 37 extends from the bottom of theouter tank 6 of eachplating tank 2 to the plating-solution tank 35. The plating-solution return pipe 37 has fourdischarge pipes 37 a coupled to the bottoms of theouter tanks 6 of the fourplating tanks 2, respectively. - The plating-
solution supply pipe 36 is provided with apump 40 for delivering the plating solution, and afilter 41 disposed downstream of thepump 40. The plating solution that was been used in theplating apparatus 1 is delivered through the plating-solution return pipe 37 to the plating-solution supply apparatus 20. The plating solution to which the copper oxide powder has been added in the plating-solution supply apparatus 20 is fed through the plating-solution supply pipe 36 to theplating apparatus 1. Thepump 40 may continually circulate the plating solution between theplating apparatus 1 and the plating-solution supply apparatus 20, or may intermittently deliver a predetermined amount of the plating solution from theplating apparatus 1 to the plating-solution supply apparatus 20, and may intermittently return the plating solution, to which the copper oxide powder has been added, from the plating-solution supply apparatus 20 to theplating apparatus 1. - In order to replenish the plating solution with pure water (DIW), a pure-
water supply line 42 is coupled to the plating-solution tank 35. This pure-water supply line 42 is provided with an on-off valve 43 (which is usually open) for stopping the supply of pure water when the operation of theplating apparatus 1 is stopped, aflow meter 44 for measuring a flow rate of the pure water, and aflow control valve 47 for controlling a flow rate of the pure water. Theflow meter 44 and theflow control valve 47 are coupled to theplating controller 17. The platingcontroller 17 is configured to control a degree of opening of theflow control valve 47 to supply the pure water into the plating-solution tank 35 in order to dilute the plating solution when the copper ion concentration in the plating solution has exceeded a set value. - The plating
controller 17 is coupled to theoperation controller 32 of the plating-solution supply apparatus 20. The platingcontroller 17 is configured to send a signal indicating a replenishment demand value to theoperation controller 32 of the plating-solution supply apparatus 20 when the copper ion concentration in the plating solution has become lower than a set value. Upon receipt of the signal, the plating-solution supply apparatus 20 adds the copper oxide powder to the plating solution until the amount of the added copper oxide powder reaches the replenishment demand value. Although in this embodiment the platingcontroller 17 and theoperation controller 32 are constructed as separate devices, in one embodiment the platingcontroller 17 and theoperation controller 32 may be constructed as one controller. In that case, the controller may be a computer that operates in accordance with a program. The program may be stored in a storage medium. - The
plating apparatus 1 may includeconcentration measuring devices 18 a each for measuring the copper ion concentration in the plating solution. Theconcentration measuring devices 18 a are attached to the fourdischarge pipes 37 a of the plating-solution return pipe 37, respectively. A measured value of the copper ion concentration obtained by eachconcentration measuring device 18 a is sent to theplating controller 17. The platingcontroller 17 may compare the above-described set value with a copper ion concentration in the plating solution calculated from the cumulative value of electric current as discussed previously, or may compare the above-described set value with a copper ion concentration measured by the concentration measuring device(s) 18 a. The platingcontroller 17 may correct the calculated value of the copper ion concentration based on a comparison of a copper ion concentration in the plating solution, calculated from the cumulative value of electric current (i.e., calculated value of the copper ion concentration), with a copper ion concentration measured by the concentration measuring device(s) 18 a (i.e. measured value of the copper ion concentration). For example, the platingcontroller 17 may determine a correction factor by dividing a measured value of the copper ion concentration by a calculated value of the copper ion concentration, and correct a calculated value of the copper ion concentration by multiplying the calculated value by the correction factor. The correction factor may preferably be updated periodically. - The plating-
solution supply pipe 36 may have abranch pipe 36 b, which is provided with aconcentration measuring device 18 b to monitor the copper ion concentration in the plating solution. Thebranch pipe 36 b may be further provided with an analyzer(s) (e.g. a CVS device or a colorimeter) to perform quantitative analysis and monitoring of the concentration of a dissolved chemical component(s) in addition to the copper ion. Such a construction makes it possible to analyze the concentration of the chemical component, e.g. an impurity, in the plating solution existing in the plating-solution supply pipe 36 before the plating solution is supplied to theplating tanks 2. This can prevent the dissolved impurity from affecting the plating performance and can more ensure highly-precise plating. Only one of theconcentration measuring devices - With the above-described construction, the plating system according to the first embodiment can replenish the plating solution with copper while keeping the copper ion concentration in the plating solution substantially equal among the plating
tanks 2. -
FIG. 2 is a side view of thepowder container 21 capable of holding copper oxide powder therein. As shown inFIG. 2 , thepowder container 21 includes acontainer body 45 capable of holding copper oxide powder therein, apowder conduit 46 coupled to thecontainer body 45, and avalve 48 attached to thepowder conduit 46. Thecontainer body 45 is composed of a synthetic resin, such as polyethylene. Thecontainer body 45 has ahandle 49 so that a worker can grip thehandle 49 to carry thepowder container 21. While there is no particular limitation on the volume of thepowder container 21, the volume should be such that a worker can carry thepowder container 21 filled with the copper oxide powder. In one example, the volume of thepowder container 21 is 4 L. Not only non-shaped copper oxide powder but pellets (granules) that have been shaped from copper oxide powder can also be used as copper oxide to be filled into thepowder container 21. The use of the pelletized copper oxide powder can more effectively prevent scattering of dust. - The
powder conduit 46 has been joined to thecontainer body 45 by a joining technique, such as welding. Thepowder conduit 46 is comprised of a pipe that allows the copper oxide powder to pass therethrough. Thepowder conduit 46 is inclined at an angle of about 30 degrees with respect to the vertical direction. The copper oxide powder can pass through thepowder conduit 46 when thevalve 48, mounted to thepowder conduit 46, is open, while the copper oxide powder cannot pass through thepowder conduit 46 when thevalve 48 is closed.FIG. 2 shows thepowder conduit 46 with thevalve 48 closed. A cap (or lid) 50 is attached to adistal end 46 a of thepowder conduit 46. -
FIG. 3 is a view showing thepowder container 21 with thecap 50 off and thevalve 48 open. The copper oxide powder is fed through thepowder conduit 46 into thepowder container 21 in the state shown inFIG. 3 . After the completion of feeding of the copper oxide powder, thevalve 48 is closed, and thecap 50 is mounted on thedistal end 46 a of the powder conduit 46 (seeFIG. 2 ). Thepowder container 21 with thevalve 48 closed, filled with the copper oxide powder, is carried into theairtight chamber 24 shown inFIG. 1 . -
FIG. 4 is a perspective view of theairtight chamber 24. In this embodiment, theairtight chamber 24 is a rectangular box capable of forming a hermetically-space therein. Theairtight chamber 24 includes adoor 55 which allows thepowder container 21 to be carried into the interior space of theairtight chamber 24, and twogloves 56 which constitute part of a wall of theairtight chamber 24. A mount frame on which thedoor 55 is mounted is comprised of a member having a sealing function, such as a rubber, so that the interior of theairtight chamber 24 can be hermetically sealed. Each of thegloves 56 is comprised of a membrane formed by a flexible material (e.g. synthetic rubber, such as polyvinyl chloride) which can deform so as to follow a shape of a worker's hand, and is configured to be able to project into theairtight chamber 24 so that a worker can conduct operations inside theairtight chamber 24. The twogloves 56 are located at both sides of thedoor 55. Theairtight chamber 24 has anexhaust port 58 for connecting the interior space of theairtight chamber 24 to a negative-pressure source. The negative-pressure source is, for example, a vacuum pump. A negative pressure is created in theairtight chamber 24 through theexhaust port 58. -
FIG. 5 is a view showing the interior of theairtight chamber 24. In theairtight chamber 24 are disposed avacuum clamp 61 for holding thepowder container 21 by vacuum suction, a vibratingdevice 65 for vibrating thepowder container 21, and apedestal 66 for supporting thepowder container 21. Thepowder container 21, with itspowder conduit 46 facing downward, is set on thevacuum clamp 61 and thepedestal 66. Thevacuum clamp 61 is secured to aframe 68, and the vibratingdevice 65 is secured to thevacuum clamp 61. Thevacuum clamp 61 has a vibration-proof rubber 61 a which is to make contact with thepowder container 21. The vibration-proof rubber 61 a has a through-hole (not shown) in which a vacuum is to be created. The operations of the vibratingdevice 65 and thevacuum clamp 61 are controlled by theoperation controller 32 shown inFIG. 1 . - The
vacuum clamp 61 is coupled to anejector 70 which is a vacuum creating device. Theejector 70 and the vibratingdevice 65 are coupled to a compressed-air supply pipe 72. The compressed-air supply pipe 72 is divided into two pipes; one is coupled to theejector 70, and the other is coupled to the vibratingdevice 65. When compressed air is fed into theejector 70, theejector 70 creates a vacuum in thevacuum clamp 61, so that thepowder container 21 can be held on the vibration-proof rubber 61 a of thevacuum clamp 61 by vacuum suction. The vibratingdevice 65 is configured to operate by the compressed air. The vibratingdevice 65 transmits the vibration to thepowder container 21 through thevacuum clamp 61, thereby vibrating thepowder container 21 held by thevacuum clamp 61. A frequency of vibration of the vibratingdevice 65 is controlled by a vibration controller (not shown) of the plating-solution supply apparatus 20. The vibration controller may be comprised of theoperation controller 32. The vibratingdevice 65 may directly contact the side surface of thepowder container 21. In an embodiment, the vibratingdevice 65 may be an electric vibrating device. - An
inlet 26 of thehopper 27, which is connectable to thepowder container 21, is located in theairtight chamber 24. Thedistal end 46 a (seeFIG. 3 ) of thepowder conduit 46 of thepowder container 21 is inserted into theinlet 26 of the hopper 27 (seeFIGS. 6 and 7 ), whereby thedistal end 46 a of thepowder conduit 46 of thepowder container 21 is coupled to theinlet 26 of thehopper 27. When thevalve 48 is opened after thepowder conduit 46 and theinlet 26 are coupled (seeFIG. 7 ), the copper oxide powder in thepowder container 21 flows through thepowder conduit 46 into theinlet 26, and finally falls into thehopper 27. - A bridge phenomenon of copper oxide powder may occur in the
powder container 21 in the vicinity of thepowder conduit 46. The bridge phenomenon is a phenomenon in which thepowder container 21 is clogged with the copper oxide powder due to an increase in the density of the powder. In order to prevent such bridge phenomenon, the vibratingdevice 65 vibrates thepowder container 21, thereby fluidizing the copper oxide powder in thepowder container 21. The frequency of the vibration of the vibratingdevice 65 may be in the range of 1000 to 10000 per minute, more preferably 7000 to 8000 per minute. - The
powder conduit 46 is fixed at such a position on thepowder container 21 that the entirety of thepowder container 21, with itspowder conduit 46 coupled to theinlet 26 of thehopper 27, is inclined. In particular, when thepowder conduit 46 is connected to theinlet 26 of thehopper 27, one side of thepowder container 21 is inclined at an angle of 50 to 70 degrees with respect to a horizontal plane, while other side is inclined at an angle of 20 to 40 degrees with respect to the horizontal plane. In this manner, when thepowder conduit 46 is coupled to theinlet 26 of thehopper 27, the right and left sides of thepowder container 21 are inclined toward thepowder conduit 46 at different angles. Accordingly, the pressure of powder, which concentrates in the vicinity of thepowder conduit 46, differs between the right and left sides of thepowder conduit 46, thereby effectively preventing the occurrence of the bridge phenomenon. Consequently, the copper oxide powder can be quickly discharged and, in addition, is unlikely to remain in thepowder container 21. -
FIG. 6 is a view showing thedistal end 46 a of thepowder conduit 46 of thepowder container 21 and theinlet 26 of thehopper 27. Thedistal end 46 a of thepowder conduit 46 has a shape of a truncated cone. Theinlet 26 of thehopper 27 has a shape corresponding to the shape of thedistal end 46 a of thepowder conduit 46. More specifically, theinlet 26 of thehopper 27 has a connectingseal 28 whose inner diameter gradually decreases with a distance from a distal end (upper end) of theinlet 26. The connectingseal 28 is composed of an elastic material, such as rubber. As shown inFIG. 7 , when thedistal end 46 a of thepowder conduit 46 is inserted into theinlet 26 of thehopper 27, thedistal end 46 a of thepowder conduit 46 comes into tight contact with the connectingseal 28 of theinlet 26, so that a gap between thedistal end 46 a of thepowder conduit 46 and theinlet 26 of thehopper 27 is sealed by the connectingseal 28. Scattering of the copper oxide powder can therefore be prevented. - The operation of supplying the copper oxide powder from the
powder container 21 to thehopper 27 will now be described with reference toFIG. 8 . Instep 1, thepowder container 21, filled with the copper oxide powder, is prepared. Instep 2, thedoor 55 of theairtight chamber 24 is opened, and instep 3, thepowder container 21 is carried into theairtight chamber 24. Thedoor 55 is closed instep 4 and, instep 5, a worker wears thegloves 56 and takes off thecap 50 of thepowder container 21 in theairtight chamber 24. Instep 6, thepowder conduit 46 of thepowder container 21 is coupled to theinlet 26 of thehopper 27, and instep 7, thevalve 48 of thepowder container 21 is opened, and instep 8 thepowder container 21 is vibrated by the vibratingdevice 65 while thepowder container 21 is held on thevacuum clamp 61. The copper oxide powder in thepowder container 21 is supplied through theinlet 26 into thehopper 27. Upon completion of the feeding of the copper oxide powder, the vibration of thepowder container 21 is stopped instep 9, thevalve 48 is closed instep 10, and the vacuum suction of thepowder container 21 by thevacuum clamp 61 is stopped instep 11. Instep 12, thepowder container 21 is removed from thevacuum clamp 61 and thepedestal 66, and instep 13 thecap 50 is attached to thepowder conduit 46. Instep 14, thedoor 55 is opened, and instep 15 thepowder container 21 is taken out of theairtight chamber 24. - All the
above steps 1 to 15 are performed while a negative pressure is produced in the interior of theairtight chamber 24. Thepowder container 21 is in theairtight chamber 24 from when thevalve 48 is opened to when thevalve 48 is closed. Therefore, even if the copper oxide powder spills from thepowder container 21, the copper oxide powder does not leak from theairtight chamber 24. A volume of thehopper 27 is several times larger than the volume of thepowder container 21; therefore, theabove steps 1 to 15 are repeated until a sufficient amount of copper oxide powder is stored in thehopper 27. - The
hopper 27 and thefeeder 30 will now be described.FIG. 9 is a side view showing thehopper 27 and thefeeder 30. Thehopper 27 is a powder reservoir (or pellet reservoir) in which copper oxide powder supplied from thepowder container 21 is to be stored. A lower half of thehopper 27 has a shape of a truncated cone so that the copper oxide powder can flow downward smoothly. A top opening of thehopper 27 is covered with alid 74. Theinlet 26, which is to be coupled to thepowder conduit 46 of thepowder container 21, is secured to thelid 74. Further, anexhaust pipe 75 is secured to thelid 74. Thisexhaust pipe 75 communicates with the interior space of thehopper 27, and further communicates with a not-shown negative-pressure source. Therefore, a negative pressure is created in the interior space of thehopper 27 through theexhaust pipe 75. - The
feeder 30 communicates with the bottom opening of thehopper 27. In this embodiment, thefeeder 30 is a screw feeder having ascrew 30 a. Themotor 31 is coupled to thefeeder 3, so that thefeeder 30 is actuated by themotor 31. Thehopper 27 and thefeeder 30 are secured to abracket 73. Thisbracket 73 is supported by aweight measuring device 80. Theweight measuring device 80 is configured to measure the total weight of thehopper 27, thefeeder 30, themotor 31, and the copper oxide powder present in thehopper 27 and thefeeder 30. - The
outlet 30 b of thefeeder 30 is coupled to the plating-solution tank 35. When themotor 31 actuates thefeeder 30, the copper oxide powder in thehopper 27 is fed by thefeeder 30 into the plating-solution tank 35. Anenclosure cover 81, which surrounds connection portions of thefeeder 30 and the plating-solution tank 35, is secured to the plating-solution tank 35. Theoutlet 30 b of thefeeder 30 is located inside theenclosure cover 81. An inert-gas supply line 83 is coupled to theenclosure cover 81, and communicates with the interior of theenclosure cover 81. The inert-gas supply line 83 supplies an inert gas, such as nitrogen gas, into theenclosure cover 81 to fill the interior of theenclosure cover 81 with the inert gas. - The inert gas is supplied into the
enclosure cover 81 for the following reason. The plating-solution tank 35 may be operated such that the plating solution in the plating-solution tank 35 is maintained at a high temperature. In such a case, a vapor generates from the plating solution. The vapor rises and reaches the connection portions of thefeeder 30 and the plating-solution tank 35, and intrudes through theoutlet 30 b into thefeeder 30. When the vapor is adsorbed onto the copper oxide powder existing in thefeeder 30, the copper oxide powder can agglomerate and may clog thefeeder 30. In order to avoid this, the inert gas, such as nitrogen gas, is injected into theenclosure cover 81 so as to expel the vapor downward, thereby preventing the vapor from intruding into thefeeder 30. - The
weight measuring device 80 is coupled to theoperation controller 32, which controls the operation of themotor 31. A measured value of the weight outputted from theweight measuring device 80 is sent to theoperation controller 32. Theoperation controller 32 receives the signal indicating the replenishment demand value that has sent from the plating apparatus 1 (seeFIG. 1 ), and instructs themotor 31 to operate until an amount of the copper oxide powder, which has been added to the plating solution in the plating-solution tank 35, reaches the replenishment demand value, while calculating the amount of the added copper oxide powder from a change in the measured value of the weight outputted from theweight measuring device 80. Themotor 31 actuates thefeeder 30, which adds the copper oxide powder, in the amount corresponding to the replenishment demand value, to the plating solution in the plating-solution tank 35. The replenishment demand value is a value that varies depending on the copper ion concentration in the plating solution so as to reflect the consumption of copper ions in the plating solution held in theplating tanks 2. The replenishment demand value is a target value of an amount of copper oxide powder to be added to the plating solution held in the plating-solution tank 35. - The plating
controller 17 is configured to calculate the replenishment demand value from the copper ion concentration in the plating solution in theplating tanks 2 when the copper ion concentration in the plating solution in theplating tanks 2 has become lower than a set value. As described above, the copper ion concentration in the plating solution in theplating tanks 2 may be the copper ion concentration calculated from the cumulative value of the electric current, or the copper ion concentration measured by the concentration measuring device(s) 18 a and/or theconcentration measuring device 18 b. - If a large amount of copper oxide powder is added to the plating solution in a short time, the copper oxide powder may agglomerate before it is dissolved in the plating solution, and as a result, the copper oxide powder may not be fully dissolved. Moreover, if a rotational speed of the
screw 30 a of thefeeder 30 is too high, the copper oxide powder may agglomerate in thefeeder 30 and may form lumps which are hardly soluble in the plating solution. In order to prevent the formation of such agglomerates and lumps of the copper oxide powder, it is preferred to set an upper limit of the rotational speed of thescrew 30 a. More specifically, theoperation controller 32 preferably controls themotor 31 so that thescrew 30 a rotates at a rotational speed not more than the preset upper limit. - The
operation controller 32 may preferably issue an alarm when an amount of copper oxide powder stored in thehopper 27 has become small. More specifically, theoperation controller 32 may preferably issue an alarm when the measured value of the weight outputted from theweight measuring device 80 has become lower than a lower limit. - The plating-
solution tank 35 will now be described.FIG. 10 is a perspective view of the plating-solution tank 35,FIG. 11 is a plan view of the plating-solution tank 35, andFIG. 12 is a vertical cross-sectional view of the plating-solution tank 35 as viewed in a direction of arrow A shown inFIG. 11 . The plating-solution tank 35 includes anagitation tank 91 in which anagitation device 85 is disposed, and anoverflow tank 92 coupled to a through-hole 95 formed in a lower portion of theagitation tank 91. Theoverflow tank 92 communicates with theagitation tank 91 through the through-hole 95. The plating-solution return pipe 37, which is coupled to theplating tanks 2 as shown inFIG. 1 , is coupled to theagitation tank 91. Thus, the plating solution used in theplating apparatus 1 ofFIG. 1 is returned to theagitation tank 91. - The
outlet 30 b of thefeeder 30 is located above theagitation tank 91, and the copper oxide powder is fed from thefeeder 30 into theagitation tank 91. Theagitation device 85 includes agitatingblades 86 disposed in theagitation tank 91, and amotor 87 coupled to the agitatingblades 86. The copper oxide powder can be dissolved in the plating solution by the agitatingblades 86 which are rotated by themotor 87. The operation of theagitation device 85 is controlled by theoperation controller 32. Theoverflow tank 92 is located adjacent to theagitation tank 91. The plating solution to which the copper oxide powder has been added flows from theagitation tank 91 into theoverflow tank 92 through the through-hole 95. The through-hole 95 may be provided with a filter to prevent passage of undissolved copper oxide powder. - A
detour passage 93 is provided adjacent to theoverflow tank 92. The plating solution overflows theoverflow tank 92 into thedetour passage 93. Thedetour passage 93 in this embodiment is a tortuous or meandering passage formed by a plurality ofbaffle plates 88. Eachbaffle plate 88 has acutout portion 88 a formed in one end. Thecutout portions 88 a of twoadjacent baffle plates 88 are located at different positions with respect to a longitudinal direction of thebaffle plates 88. Accordingly, as illustrated by arrows inFIG. 11 , the flow of the plating solution to which the copper oxide powder has been added meanders through thedetour passage 93. In one embodiment, thedetour passage 93 may be formed by a plurality ofbaffle plates 88 which are staggered and have nocutout portions 88 a. - The
detour passage 93 is provided in order to ensure a sufficient time for the copper oxide powder to be dissolved in the plating solution. The time required for the plating solution to pass through thedetour passage 93 is preferably not less than 10 seconds.Such detour passage 93 enables the copper oxide powder to be fully dissolved in the plating solution. -
FIG. 13 is a schematic view of another embodiment of the plating-solution tank 35. In this embodiment,baffle plates 88 are installed in theoverflow tank 92, and are staggered in the vertical direction. Adetour passage 93 for the plating solution is formed by thesebaffle plates 88. -
FIG. 14 is a schematic view of yet another embodiment of the plating-solution tank 35. In this embodiment, anagitation tank 91 in which anagitation device 85 is disposed is installed in the center of the plating-solution tank 35. Anoverflow tank 92 is disposed outside theagitation tank 91 and communicates with a through-hole 95 formed in the lower end of theagitation tank 91. Adetour passage 93 is provided adjacent to theoverflow tank 92 and is coupled to the plating-solution supply pipe 36. Thedetour passage 93 is located outside theagitation tank 91 and theoverflow tank 92. In this embodiment, thedetour passage 93 is a spiral passage that extends spirally. The plating solution flows from theagitation tank 91 into theoverflow tank 92 through the through-hole 95, and overflows theoverflow tank 92 into thedetour passage 93. The plating solution that has flowed through thedetour passage 93 flows into the plating-solution supply pipe 36. Thedetour passage 93 in a spiral shape, i.e., in a circular shape, enables the plating solution to stay for a long time in the plating-solution tank 35 without use of thebaffle plates 88. Further, there is no corner in the plating-solution tank 35. Thus, there is no sedimentation of powder in a corner where the plating solution is likely to stagnate. Furthermore, the plating-solution tank 35 can be made compact. - In both the embodiment shown in
FIGS. 11 and 12 and the embodiment shown inFIG. 13 , the time it takes for the plating solution to pass through thedetour passage 93 can be increased by increasing the number ofbaffle plates 88. In the case of the embodiment shown inFIG. 14 in which no baffle plate is provided, the time it takes for the plating solution to pass through thedetour passage 93 can be increased by increasing the length of thedetour passage 93 as well. -
FIG. 15 is a diagram (SEM diagram) showing results of an experiment which was conducted to examine an influence of the number of baffle plates on dissolution of copper oxide powder under a room-temperature condition. In this experiment, a solution to which copper oxide powder had been added was passed through thedetour passage 93 in which zero, one, two, or three baffle plates were provided. After the passage of the solution, sediment of copper oxide powder on the bottom of thedetour passage 93 was collected and microphotographed.FIG. 15 shows SEM images at magnifications of 50 times, 100 times, and 150 times. - In view of a friction loss in the plating-
solution supply pipe 36 and a loss by a valve, a meter, a pipe joint, etc., the flow velocity of the plating solution flowing in the plating-solution tank 35 needs to be high to a certain degree in order to increase the copper ion concentration in the plating solution in theplating tanks 2. On the other hand, if the flow velocity of the plating solution is too high, the copper oxide powder may not be completely dissolved in the plating solution. - As can be seen from the experimental results shown in
FIG. 15 , almost no copper oxide powder remained in thedetour passage 93 in the case of three baffle plates, whereas some copper oxide powder remained in thedetour passage 93 in the case of zero baffle plate. These results show that the dissolution of copper oxide film is improved as the number of baffle plates increases. The time it takes for the plating solution to pass through thedetour passage 93 was about 4 seconds in the case of zero baffle plate, about 8 seconds in the case of one baffle plate, about 12 seconds in the case of two baffle plates, and about 16 seconds in the case of three baffle plates. - These experimental results indicate that the time required for the plating solution to pass through the
detour passage 93 should be more than 10 seconds corresponding to the use of one-and-a-half baffle plates, preferably more than about 12 seconds corresponding to the use of two baffle plates, and more preferably more than 16 seconds corresponding to the use of three baffle plates. - While the influence of the number of baffle plates on the dissolution of copper oxide powder has been described, an approach to promote the dissolution of copper oxide powder is not limited to the adjustment of the number of baffle plates. For example, it is possible to install a heater in the plating-
solution tank 35, e.g. in theagitation tank 91, to promote the dissolution of copper oxide powder in the plating solution. However, if the plating solution is heated to a too high temperature, then coexisting components, such as additives, in the plating solution can be decomposed and deactivated. From this viewpoint, it is preferred to set an upper limit of the temperature of the plating solution in theagitation tank 91 to be not more than 50 C° so as not to cause decomposition of the additive(s). In the case of installing such a heater for heating the plating solution, only one baffle plate may be installed in thedetour passage 93 so that it takes at least about 8 seconds for the plating solution to pass through thedetour passage 93, or no baffle plate may be installed in the plating-solution tank 35. The heater installed in theagitation tank 91 makes it possible to fully dissolve the copper oxide powder in the plating solution when the plating solution is merely passing through the plating-solution tank 35. - A plating system according to a second embodiment will now be described with reference to
FIG. 16 . The plating system according to the second embodiment differs from the plating system according to the first embodiment in that the fourplating tanks 2 are coupled in series. More specifically, theouter tank 6 and theinner tank 5 of eachplating tank 2 are coupled to theinner tank 5 and theouter tank 6 of theadjacent plating tank 2 by afirst connection pipe 110 and asecond connection pipe 112, respectively. Thefirst connection pipes 110 and thesecond connection pipes 112 are provided withpumps 113, respectively, for delivering the plating solution. - The plating-
solution supply pipe 36 is coupled to theinner tank 5 of one of the fourplating tanks 2, and the plating-solution return pipe 37 is coupled to theouter tank 6 of another one of the fourplating tanks 2. The plating-solution supply pipe 36 is provided with aflow meter 38 and aflow control valve 39, and the plating-solution return pipe 37 is provided with aflow meter 115 and a plating-solution discharge valve 116. Aconcentration measuring device 118 for measuring the copper ion concentration in the plating solution is coupled to theouter tank 6 to which the plating-solution return pipe 37 is coupled. The same reference numerals are used for the same elements in the first embodiment, and duplicate descriptions thereof are omitted. - The plating system according to the second embodiment automatically measures the copper ion concentration in the plating solution while keeping the copper ion concentration in the plating solution substantially equal among the plating
tanks 2. When it is necessary to replenish the plating solution with copper, the plating solution is delivered from theplating apparatus 1 to the plating-solution supply apparatus 20, while the plating solution containing copper in a relatively high concentration is supplied from the plating-solution supply apparatus 20 in the downstairs room to theplating apparatus 1. - A control sequence for adding copper oxide powder to the plating solution in the plating system according to the first embodiment will be described with reference to
FIG. 17 , and a control sequence for adding copper oxide powder to the plating solution in the plating system according to the second embodiment will be described with reference toFIG. 18 . In the plating system according to the first embodiment, as shown inFIG. 17 , instep 1, when the copper ion concentration in the plating solution has become lower than a set value, the platingcontroller 17 sends the signal indicating the replenishment demand value to theoperation controller 32. Instep 2, upon receipt of the signal, theoperation controller 32 instructs themotor 31 to operate until the amount of copper oxide powder added to the plating solution reaches the replenishment demand value, so that thefeeder 30 adds the copper oxide powder to the plating solution in the plating-solution tank 35 by the amount corresponding to the replenishment demand value. - In
step 3, theoperation controller 32 activates theagitation device 85, which agitates the plating solution to which the copper oxide powder has been added. Theoperation controller 32 stops the agitating operation of theagitation device 85 when a preset time has elapsed. Instep 4, the plating solution to which the copper oxide powder has been added flows through theoverflow tank 92 and thedetour passage 93, while the copper oxide powder is dissolved in the plating solution. Instep 5, the plating solution in which the copper oxide powder has been dissolved is supplied to theplating tanks 2 of theplating apparatus 1 through the plating-solution supply pipe 36. In this manner, the copper ion concentration in the plating solution used in theplating apparatus 1 is maintained at a set value. According to this embodiment, a necessary amount of copper oxide powder can be automatically added to and dissolved in the plating solution, and a predetermined amount of the plating solution can be supplied to eachplating tank 2. Therefore, the copper ion concentration in the plating solution in eachplating tank 2 can be regulated and maintained at a predetermined value without decreasing the throughput of theplating apparatus 1. - In the plating system according to the second embodiment, copper oxide powder is added to the plating solution in the following manner. The copper ion concentration in the plating solution held in the
plating tanks 2 is continually measured by theconcentration measuring device 118, and the measured value of the copper ion concentration is monitored by the platingcontroller 17. As shown inFIG. 18 , instep 1, when the copper ion concentration in the plating solution in theplating tanks 2 has become lower than a set value, the platingcontroller 17 sends the signal indicating the replenishment demand value to theoperation controller 32 of the plating-solution supply apparatus 20. Instep 2, the plating-solution discharge valve 116 for discharging the plating solution from theplating tanks 2 is opened to deliver the plating solution from theplating tanks 2 to the plating-solution tank 35. This plating-solution discharge valve 116 is kept open for a predetermined period of time so that the plating solution is delivered in an amount of not more than the maximum volume of the plating-solution tank 35. - In
step 3, upon receipt of the above signal, theoperation controller 32 instructs themotor 31 to operate until the amount of copper oxide powder added to the plating solution reaches the replenishment demand value, so that thefeeder 30 adds the copper oxide powder, in an amount corresponding to the replenishment demand value, to the plating solution in the plating-solution tank 35.Step 2 andstep 3 may be performed simultaneously, orstep 3 may be performed prior tostep 2. Instep 4, theoperation controller 32 activates theagitation device 85, which agitates the plating solution to which the copper oxide powder has been added. Theoperation controller 32 stops the agitating operation of theagitation device 85 when a preset time has elapsed. - In
step 5, the plating solution to which the copper oxide powder has been added flows through theoverflow tank 92 and thedetour passage 93, while the copper oxide powder is dissolved in the plating solution. Instep 6, the plating solution in which the copper oxide powder has been dissolved is supplied to one of theplating tanks 2 of theplating apparatus 1 through the plating-solution supply pipe 36. Theplating tanks 2 communicate with each other through thefirst connection pipes 110 and thesecond connection pipes 112, and the plating solution circulates through all of theplating tanks 2 by the operations of thepumps 113 attached to thefirst connection pipes 110 and thesecond connection pipes 112 that couple theplating tanks 2 to each other. In this manner, the copper ion concentration in the plating solution used in theplating apparatus 1 is maintained at a set value. - As shown in
FIG. 1 , in the plating system according to the first embodiment, the plating-solution supply pipe 36 has thebranch pipes 36 a coupled to theplating tanks 2, respectively, and the plating solutions having the same concentration are supplied to theplating tanks 2. In the plating system according to the second embodiment, theplating tanks 2 communicate with each other and the plating-solution supply pipe 36 is coupled to one of theplating tanks 2. Therefore, in both of these embodiments, the concentration of the plating solution in theplating tanks 2 can be kept uniform. According to these embodiments, a quality of a copper film formed by plating can be improved and, in addition, a variation in the results of plating among the platingtanks 2 can be prevented. - The average particle size of copper oxide powder (as measured by a laser diffraction/scattering method) is preferably in the range of 10 micrometers to 200 micrometers, more preferably in the range of 20 micrometers to 100 micrometers. If the average particle size is too small, copper oxide powder can scatter in the air during the supply of the powder. If the average particle size is too large, the powder may not be quickly dissolved in the solution.
- A plating method capable of forming a higher-quality copper film on a substrate can be provided by using a plating solution to which pelletized solid materials comprising metal copper have been added. The use of such pelletized solid materials comprising metal copper allows copper powder containing few impurities to coexist with copper oxide powder, leading to an enhanced plating film quality. Further, the use of such pellets can more effectively prevent scattering of powder upon the supply of the powder.
- While an alkali metal in a powder form is generally at risk for firing or explosion, powder of metal copper is at low risk for firing or explosion. Powder of metal copper can therefore be shaped into pellets. As described above e.g. with reference to
FIG. 1 , instead of or together with copper oxide powder, such pelletized solid materials comprising metal copper can be supplied to the plating-solution tank 35. It is also possible to use pellets of metal copper together with pellets of copper oxide. - If the pelletized solid materials are too hard, such materials can cause a trouble in the plating-
solution supply apparatus 20. If the pelletized solid materials are too soft, it is possible that scattering of powder may not be effectively prevented. Thus, it is preferred to use pellets having an appropriate hardness. - While the pelletized solid materials have been described, it is also possible for copper plating to use small-diameter solid copper balls or a strip-shaped material, obtained by shaping solid copper into a ribbon-like or tape-like shape. In that case, a shaft of the
feeder 30 may have a function of crushing such solid materials. - While the powder container, the plating-solution supply apparatus, etc. have been described with reference to the case of plating a substrate with copper, the powder container, the plating system and the plating method described above can be used also in a case of plating a substrate with other metal such as indium.
- The previous description of embodiments is provided to enable a person skilled in the art to make and use the present invention. Moreover, various modifications to these embodiments will be readily apparent to those skilled in the art, and the generic principles and specific examples defined herein may be applied to other embodiments. Therefore, the present invention is not intended to be limited to the embodiments described herein but is to be accorded the widest scope as defined by limitation of the claims.
Claims (26)