US20170189958A1 - Method and apparatus for infiltration of a micro/nanofiber film - Google Patents
Method and apparatus for infiltration of a micro/nanofiber film Download PDFInfo
- Publication number
- US20170189958A1 US20170189958A1 US15/312,216 US201415312216A US2017189958A1 US 20170189958 A1 US20170189958 A1 US 20170189958A1 US 201415312216 A US201415312216 A US 201415312216A US 2017189958 A1 US2017189958 A1 US 2017189958A1
- Authority
- US
- United States
- Prior art keywords
- cavity
- film
- molten material
- tool
- reel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
There is provided an apparatus and method for manufacturing of an infiltrated fiber-based composite film. The apparatus comprises two tool blocks arranged opposite each other enabling a fiber-based film to be arranged between the tool blocks. At least one of the tool blocks comprises a recess so that the recess can form a sealed cavity enclosing a portion of the film when the tool blocks are in contact with each other. At least one of the tool blocks comprises a vacuum channel connecting cavity to a vacuum pump for drawing a vacuum in the cavity; a melt channel connecting the cavity to a source of molten material. The melt channel comprises a valve arrangement controlling delivery of the molten material to the cavity; pressure means to achieve an elevated pressure onto the molten material within the cavity such that a fiber film in the cavity is infiltrated by the molten material; and an ejection piston for ejecting an infiltrated fiber film from the cavity.
Description
- The present invention relates to fabrication of a composite material. In particular, the present invention relates to a method and a machine for manufacturing of a micro/nanofiber based composite material.
- Composite films consisting of a micro- and/or nanofibrous film and an infiltrated metal matrix can be manufactured to have advantageous thermal and mechanical properties. In particular, such thermally conducting films may be used at the interface between two surfaces to facilitate thermal transport. One interesting application area concerns high performance microelectronic components where efficient cooling of components is essential. A thermally conductive film may then be placed between the active component and a cooling device, or between a chip and a heatspreader/lid, to facilitate heat conduction away from the component.
- However, at the present time, it is difficult to infiltrate materials into films consisting of micro and nanofiber films. This is due to the high pressure required to penetrate small pore sizes. It is particularly difficult to form composites which are void free, when there is a large difference in surface energy between the fibers and the metal/alloy matrix material, such as carbon based fibers with metal/alloy matrix, or polymer based fibers with metal/alloy matrix.
- Existing continuous processes based on lamination techniques cannot achieve sufficient pressure to infiltrate the small pores of micro and nanofiber based films, and result in unwanted pores.
- In order to provide such composite materials, a commercially viable process for the infiltration of micro and/or nanofiber networks with metallic/alloy matrix materials is desirable.
- In view of the above-mentioned desired properties of infiltration of nanomaterials, and the above-mentioned and other drawbacks of the prior art, it is an object of the present invention to provide an improved method and apparatus for manufacturing of an infiltrated fiber-based composite film.
- According to a first aspect of the invention, it is therefore provided an apparatus for manufacturing of an infiltrated fiber-based composite film. The apparatus comprises: two tool blocks arranged opposite each other enabling a fiber-based film to be arranged between the tool blocks, wherein at least one of the tool blocks comprising a recess; wherein at least one of the tool blocks is movable towards the opposing tool block such that the recess form a sealed cavity configured to enclose a portion of the film when the tool blocks are in contact with each other; and wherein at least one of the tool blocks comprises: a vacuum channel in a first end connected to the recess and in a second end connectable to a vacuum pump for drawing a vacuum in the cavity; a melt channel in a first end connected to the recess and in a second end connected to a source of molten material; the melt channel comprising a valve arrangement configured to control delivery of the molten material to the cavity; pressure means configured to achieve an elevated pressure within the cavity such that a fiber film in the cavity is infiltrated by the molten material; and an ejection piston configured to eject an infiltrated fiber film from the cavity, when the tool blocks are in a retracted position spaced apart from each other.
- The tool blocks are movable towards each other, either by moving only one of the tool blocks towards the other or by moving both tool blocks towards each other. Accordingly, one or both of the tool blocks may comprise a recess forming the cavity when the tool blocks are pressed together. The tool blocks may for example be moved by means of one or more actuators. Furthermore, the tool blocks may comprise inserts which define the recess. If inserts are used, the inserts may be removable so that the size and geometry of the recess determining the configuration of the cavity may be easily varied in the apparatus by changing inserts.
- The apparatus according to embodiment of the present invention allows for sequential manufacturing of a composite film consisting of a micro/nanofiber-based film infiltrated with a metal-based matrix, thereby enabling a more efficient manufacturing method. Moreover, the apparatus enables uniform and complete infiltration of the molten material into the fiber film to achieve advantageous composite properties.
- According to one embodiment of the invention, the recess may have a depth in the range of 5 to 500 micrometers to enable manufacturing of infiltrated films having a corresponding thickness.
- According to one embodiment of the invention, the valve arrangement may advantageously comprise a channel valve configured to control the delivery of molten material from the source to the melt channel and an injector valve configured to control the delivery of molten material from the melt channel to said cavity. Thereby, the amount of molten metal to be delivered to the cavity can be controlled by the channel valve, and the injector valve controls the injection of molten metal into the cavity.
- In one embodiment of the invention, the pressure means are advantageously configured to provide a pressure within the cavity higher than 30 MPa. Such a pressure will act to force the molten material into the pores of the film so that the film is fully infiltrated. The force pressing the two tool blocks towards each other must be controlled so that the cavity remains sealed also when the high pressure is applied to the cavity in order to avoid any leakage from the cavity during infiltration.
- According to one embodiment of the invention, the pressure means may advantageously comprise an injector piston connected to the melt channel such that the molten material is infiltrated at an elevated pressure into the fiber film in the cavity by means of actuation of said injector piston. The injector piston, actuated by a suitable actuator enables application of sufficiently high pressure onto the molten material to achieve infiltration of the molten material into the film.
- In one embodiment of the invention, the tool block and/or the tool inserts may advantageously comprise a heater configured to heat the cavity to a temperature exceeding a melting temperature of the molten material. By heating the cavity prior to injection of the molten metal, the metal will not solidify in the cavity which enables the infiltration. The heater may advantageously comprise one or more heating elements having an effect of several kW.
- According to one embodiment of the invention, the tool block may advantageously comprise cooling means configured to cool the cavity to a temperature lower than said meting temperature of said molten material after injection of the metal and infiltration of film. Through the cooling means, the infiltrated film can be rapidly cooled down so that the metal solidifies enabling the infiltrated film to be removed from the cavity. This improves the cycling time thereby providing a faster manufacturing process. Heating and cooling the cavity should in the present context be understood as heating and cooling the portions of the apparatus forming the cavity, such that any material, i.e. film and/or metal, located in the cavity is heated or cooled.
- In one embodiment of the invention, the cooling means may advantageously comprise a cooling channel containing a fluidic cooling medium such as oil or water. Preferably, cooling channels and heating elements are provided to enable process cycle times less than 3 minutes. The cycle time is preferably as short as possible to provide an efficient process. In general, the cycle time is related to the heating and cooling capabilities of the apparatus.
- According to one embodiment of the invention, the molten material may advantageously be selected from the group comprising SnAgCu, Sn, SnBi, SnBiAg, SnZn, In, BiSnAg, and eutectic InSnBi.
- According to one embodiment of the invention, the each tool block may advantageously comprise a recess, and the tool blocks may thus be arranged such that the recesses face each other so that a cavity is formed when the two tool blocks are pressed together.
- In one embodiment of the invention, there is provided an assembly for reel-to-reel manufacturing of an infiltrated fiber-based composite film. The assembly comprises an apparatus according to any one of the embodiments discussed above, a micro/nanofiber film, a storage reel holding the film, and a collecting reel configured to receive the film. The film is arranged between the storage reel and the collecting reel such that a path of the film from the storage reel to the collecting reel runs between the tool blocks. Through the above discussed assembly reel-to-reel manufacturing is enabled meaning that an entire roll of infiltrated film preforms may be sequentially manufactured without interruptions. In such a process, the film is unwound from the storage reel and passed through the tool and then stored on the collecting reel.
- According to one embodiment of the invention, the micro/nanofiber film may advantageously comprise fibers selected from the group comprising polyimide, polyurethane, polyacrylonitrile, polyaramid, high density polyethylene, PEEK, Kevlar, polyester, boron nitride, carbon fibers, carbon nanotubes, inorganic fibers and graphene coated fibers. Microfibers refer to fibers having a diameter on the order of micrometers, and nanofibers refer to fibers having a sub-micrometer diameter.
- In one embodiment of the invention, the film may advantageously have a surface which is modified to facilitate wetting of the molten material to the film. In particular, the fibers of the film may be coated with Ag, Cu, Au, Ni, Pd, Ti and/or Pt or a combination thereof.
- According to a second aspect of the invention, there is provided a method for reel-to-reel manufacturing of a composite film, consisting of a micro/nanofiber-based fiber film with a metal-based matrix, the method comprising the steps of; arranging micro/nanofiber-based film between a storage reel holding the film and a collecting reel receiving the film; enclosing a portion of the film in a cavity formed by pressing together a first and a second tool block arranged opposite each other, wherein at least one of the tool blocks comprises a recess forming the cavity; providing a molten material to the cavity; elevating a pressure onto the molten material such that a fiber film in the cavity is infiltrated by the molten material; and cooling the cavity to a temperature below a melting temperature of the molten material; and releasing the composite film by moving apart the tool blocks. The infiltrated portion of the film is then ejected it using an ejection mechanism.
- Effects and features of this second aspect of the present invention are largely analogous to those described above in connection with the first aspect of the invention.
- Further features of, and advantages with, the present invention will become apparent when studying the appended claims and the following description. The skilled person realize that different features of the present invention may be combined to create embodiments other than those described in the following, without departing from the scope of the present invention.
- These and other aspects of the present invention will now be described in more detail with reference to the appended drawings showing an example embodiment of the invention, wherein:
-
FIGS. 1a and 1b schematically illustrates an apparatus according to an embodiment of the invention; and -
FIG. 2 is a flow chart outlining the general steps of a method according to an embodiment of the invention. - The present invention will now be described more fully hereinafter with reference to the accompanying drawings, in which currently preferred embodiments of the invention are shown. This invention may, however, be embodied in many different forms and should not be construed as limited to the embodiments set forth herein; rather, these embodiments are provided for thoroughness and completeness, and fully convey the scope of the invention to the skilled person. Like reference characters refer to like elements throughout.
- The invention relates to a process for making complete and uniform infiltration of a metal/alloy matrix material into films of continuous micro and/or nanofibers. More specifically, this invention relates to the process and tool for forming such composite in a reel-to-reel production.
-
FIG. 1 schematically illustrates anapparatus 100 for reel-to-reel manufacturing of an infiltrated micro/nanofiber film. The apparatus comprises a first tool block 102 a and asecond tool block 102 b which are arranged opposite each other. Each tool block comprises arespective recess composite film 106 is arranged between the tool blocks 102 a, 102 b and between therecesses film 106 is enclosed in the cavity when the twotool blocks second tool block 102 b, comprises a delivery system for providing a molten material to the recess. A molten metal material is stored in acontainer 108 which is connected to amelt channel 110 of thetool block 102 b. Achannel valve 112 is arranged between thecontainer 108 and themelt channel 110 to control the delivery of molten material to the melt channel. Aninjector valve 114 is arranged to control the delivery of molten material from themelt channel 110 to the cavity. Thetool block 102 b further comprises aninjector piston 116 arranged in connection with themelt channel 110 and configured to inject the molten material into the cavity at an elevated pressure. The channel arrangement of thetool block 102 b also comprises avacuum channel 116 connecting avacuum pump 118 to the cavity via avacuum valve 120. Anejection piston 122 is arranged in the first tool block 102 a for ejecting infiltrated portion of thefilm 106 from therecess 104 a. Theejection piston 122 may also comprise cooling channels. -
FIG. 1a further illustrates that the micro/nanofiber film 106 is arranged on astorage reel 124 holding the film. Thefilm 106 runs between the tool blocks 104 a, 104 b to a collectingreel 126. -
FIG. 1b illustrates the apparatus in a position where the twotool blocks recesses cavity 150 in which a portion of thefilm 106 is enclosed. -
FIG. 2 is a flow chart outlining the general steps of the manufacturing method for forming an infiltrated micro/nanofiber film. The method ofFIG. 2 will be discussed with reference toFIGS. 1a -b. - The film that is infiltrated in the described process can comprise continuous micro and/or nanofibers made of a polymeric, boron nitride or carbon based composition. The film can be formed through, but not limited to, an electrospinning process, followed by additional processes such as nitration or carbonization. Typically the films have a porosity of 60±20%, a total thickness of 5-200 μm, and are made from fibers with diameters of 100 nm-15 μm. The film can also have an additional layer such as a thin coating on the fibers to facilitate the wetting of the molten material, which can be formed through both dry and wet deposition techniques, such as CVD, sputtering, electroplating, and electroless plating. In an example embodiment the reel/spool/
roller 124 is carrying a 30 meter long continuous film of continuous polyimide submicron fibers coated with Ag particles. Movement of the film from thestorage reel 124 to the collecting reel is controlled by a motor. - In one embodiment, the tool blocks 102 a-b are made from aluminum alloy, and incorporate electrical heating elements with several kW heating effect, channels for oil cooling, and with a geometry that allows an ejection piston. The tool blocks 102 a-b comprises insert blocks 128 a-b made from stainless steel, having polished surfaces and a cavity of a geometry that corresponds to the desired geometry of the final composite film. The tool blocks and tool inserts have channels connected to an
injection piston 116 which can push liquid melt into the tool insert cavity with high pressure. - First 202, the tool blocks 102 a-b closes around the
film 106 with a sufficiently high locking force and the recesses 104 a-b forms acavity 150 which is sealed in part by the film itself and in which cavity a portion of the film is in a non-compressed state - Next, 204, the
vacuum valve 120 is opened and thevacuum pump 118 is activated to draw vacuum in the cavity. Thevacuum valve 120 is then closed. - After vacuum is formed in the cavity, heating elements heats 206 the tool blocks 102 a, 102 b and in particular the
inserts - Next 208, the
channel valve 112 is opened to allow molten metal to flow from themolten metal container 108 into themelt channel 110. Thechannel valve 112 is open until themelt channel 110 is filled. Filling of the melt channel may include retracting theinjector piston 116 to facilitate additional filling of molten metal in the channel system. Themelt channel 110 may also be fully or partially filled with a molten material from a previous cycle. The heating elements for heating the cavity are thus arranged to also ensure that the melt channel is sufficiently heated to enable a flow of molten material through the channel. - After delivery of molten metal to the
melt channel 110, theinjector valve 114 is opened so that the molten metal flows into thecavity 150, helped by the vacuum in thecavity 150, to fill 210 the cavity and to enclose the film. After filling of the cavity, thechannel valve 112 is closed. - In the
next step 212, a high pressure, typically above 30 MPa, is applied by the injection piston (116) to force infiltration of the melt metal/alloy matrix material into the pores of the film. The force applied on the injection piston is then reduced and the injector valve is closed. - After infiltration of the film, the tool blocks and inserts are cooled 214 down to a temperature of about 187° C., which is 30 degrees below the melting point of the SnAgCu alloy, by flowing oil in the cooling channels in the tool, the tool inserts and
ejection piston 122. - Once the cavity and the film therein has reached the target temperatures, the tool blocks 104 a-b are moved apart and the infiltrated portion of the film is ejected 216 by the
ejection piston 122. After ejection of the film, the film may be moved a distance and a new film portion may be infiltrated by restarting the cycle. - Through the above described method consecutive portions of the film can be sequentially infiltrated in an efficient manner. If reel-to-reel production is undesirable, the
apparatus 100 may equally well be used for infiltration of individual pieces of film. - Even though the invention has been described with reference to specific exemplifying embodiments thereof, many different alterations, modifications and the like will become apparent for those skilled in the art. For example, the channels and valves may be arranged in a different manner, while still achieving the same effect as the above described apparatus. Also, it should be noted that other parts of the system may be omitted, interchanged or arranged in various ways, the apparatus yet being able to perform the functionality of the present invention.
- Additionally, variations to the disclosed embodiments can be understood and effected by the skilled person in practicing the claimed invention, from a study of the drawings, the disclosure, and the appended claims. In the claims, the word “comprising” does not exclude other elements or steps, and the indefinite article “a” or “an” does not exclude a plurality. The mere fact that certain measures are recited in mutually different dependent claims does not indicate that a combination of these measured cannot be used to advantage.
Claims (19)
1. An apparatus for manufacturing of an infiltrated fiber-based composite film, said apparatus comprising:
two tool blocks (102 a, 102 b) arranged opposite each other enabling a fiber-based film (106) to be arranged between said tool blocks, wherein at least one of said tool blocks comprising a recess (104 a, 104 b); wherein at least one of said tool blocks is movable towards the opposing tool block such that said recess forms a sealed cavity configured to enclose a portion of said film when said tool blocks are in contact with each other; and
wherein at least one of said tool blocks comprises:
a vacuum channel (116) in a first end connected to said recess and in a second end connectable to a vacuum pump for drawing a vacuum in said cavity;
a melt channel (110) in a first end connected to said recess and in a second end connected to a source of molten material (108); said melt channel comprising a valve arrangement configured to control delivery of said molten material to said cavity;
a heater configured to heat said cavity to a temperature exceeding a melting temperature of said molten material;
pressure means configured to achieve an elevated pressure within said cavity such that a fiber film in said cavity is infiltrated by said molten material; and
an ejection piston (122) configured to eject an infiltrated fiber film from the cavity, when the tool blocks are in a retracted position spaced apart from each other.
2. The apparatus according to claim 1 , wherein said recess has a depth in the range of 5 to 500 micrometers.
3. The apparatus according to claim 1 , wherein said valve arrangement comprises:
a channel valve (112) configured to control the delivery of molten material from said source to said melt channel; and
an injector valve (114) configured to control the delivery of molten material from said melt channel (7) to said cavity.
4. The apparatus according to claim 1 , wherein said pressure means are configured to provide a pressure within said cavity higher than 30 MPa
5. The apparatus according to claim 1 , wherein said pressure means comprises an injector piston (116) connected to said melt channel such that said molten material is infiltrated at an elevated pressure into said film in said cavity by means of actuation of said injector piston.
6. (canceled)
7. The apparatus according to claim 1 , wherein said tool block comprises cooling means configured to cool said cavity to a temperature lower than said meting temperature of said molten material.
8. The apparatus according to claim 6 , wherein said cooling means comprises a cooling channel containing a fluidic cooling medium.
9. The apparatus according to claim 1 , wherein each tool block comprises a recess, and wherein said tool blocks are arranged such that said recesses face each other.
10. (canceled)
11. (canceled)
12. An assembly for reel-to-reel manufacturing of an infiltrated fiber-based composite film, said assembly comprising:
an apparatus according to claim 1 ;
a micro/nanofiber film (12);
a storage reel (8) holding said film;
a collecting reel (9) configured to receive said film;
wherein said film is arranged between said storage reel and said collecting reel such that a path of said film from said storage reel to said collecting reel runs between said tool blocks.
13. The assembly according to claim 12 , wherein said micro/nanofiber film comprise fibers selected from the group comprising polyimide, polyurethane, nylon, polyimide, polyacrylonitrile, polyaramid, high density polyethylene, PEEK, Kevlar polyester, boron nitride, carbon fibers, carbon nanotubes, inorganic fibers and graphene coated fibers.
14. The assembly according to claim 13 , wherein said film has a surface modified to facilitate wetting of the molten material to said film, wherein said surface modification compirses coating fibers of said film with Ag, Cu, Au, Ni, Pd, Ti and/or Pt or a combination thereof.
15. A method for reel-to-reel manufacturing of a micro/nanofiber-based film infiltrated with metal or metal alloy matrix material, said method comprising the steps of;
arranging micro/nanofiber-based film between a storage reel holding said film and a collecting reel receiving said film;
enclosing a portion of said film in a cavity formed by pressing together a first and a second tool block arranged opposite each other, wherein at least one of said tool blocks comprises a recess forming said cavity;
providing a molten material to said cavity;
elevating a pressure onto said molten material within said cavity such that a fiber film in said cavity is infiltrated by said molten material; and
cooling said cavity to a temperature below a melting temperature of said molten material; and
releasing said film by moving apart said tool blocks.
16. The method according to claim 15 , wherein providing a molten material to said cavity comprises:
opening a channel valve (112) to allow molten metal to flow from the source of molten material (108) into the melt channel (110);
closing the channel valve;
opening an injector valve (114) such that the molten metal flows into the cavity;
closing the injector valve; and
activating said injection piston (117) to push liquid melt into the cavity.
17. The apparatus according to claim 1 , wherein the valve arrangement comprises an injection piston (117) arranged to push liquid melt into the tool insert cavity.
18. The apparatus according to claim 1 , wherein the valve arrangement comprises a channel valve (112) configured to be opened to allow molten metal to flow from the source of molten material (108) into the melt channel (110).
19. The apparatus according to claim 1 , wherein the valve arrangement comprises an injector valve (114) configured to be opened such that the molten metal flows into the cavity.