US20170084434A1 - Diffusion-bonded sputter target assembly and method of manufacturing - Google Patents
Diffusion-bonded sputter target assembly and method of manufacturing Download PDFInfo
- Publication number
- US20170084434A1 US20170084434A1 US15/364,403 US201615364403A US2017084434A1 US 20170084434 A1 US20170084434 A1 US 20170084434A1 US 201615364403 A US201615364403 A US 201615364403A US 2017084434 A1 US2017084434 A1 US 2017084434A1
- Authority
- US
- United States
- Prior art keywords
- target
- backing plate
- assembly
- alloy
- metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A method of making a diffusion bonded sputter target assembly is provided. A target blank comprising a first metal or alloy has a first surface defining a sputtering surface and a second surface. A second metal or alloy is placed around the target blank. A backing plate is provided adjacent the second metal or alloy that is positioned alongside of the second target surface. This assembly is then diffusion bonded, and a portion of the second metal overlying the sputtering surface of the target is removed to expose the target sputtering surface. W target or W alloy target/Ti or Ti alloy backing plate assemblies are provided with an Al interlayer positioned intermediate the W or W alloy target and backing plate. The assembly has a bond strength exceeding 50 MPa.
Description
- This application claims the priority benefit of U.S. Provisional Patent Application Ser. No. 61/442,427 filed Feb. 14, 2011; International Application No. PCT/US2012/024469 filed Feb. 9, 2012; and U.S. patent application Ser. No. 13/984,961 filed Oct. 18, 2013.
- The present application pertains to methods and structural combinations that provide diffusion bonding (DB) of a sputtering target to a backing plate wherein the target and backing plate may have different coefficients of thermal expansion (CTE).
- Cathodic sputtering is widely used for the deposition of thin layers of materials onto desired substrates. Basically, this process requires gas ion bombardment of a target having a sputtering surface formed of a material that is to be deposited as a thin film or layer on a substrate. Ion bombardment of the target not only causes atoms or molecules of the target material to be sputtered, but imparts considerable thermal energy to the target. This heat is dissipated by use of a cooling fluid typically circulated beneath or around a heat conducting backing plate that is positioned in heat exchange relation with the target.
- The target forms a part of a cathode assembly which together with an anode is placed in an evacuated chamber that contains an inert gas, preferably argon. A high voltage electrical field is applied across the cathode and anode. The inert gas is ionized by collision with the electrons ejected from the cathode. Positively charged gas ions are attracted to the cathode and, upon impingement with the target surface, dislodge the target material. The dislodged target materials traverse the evacuated enclosure and deposit as a thin film on the desired substrate that is normally located proximate the anode.
- In addition to the use of an electrical field, increasing sputtering rates have been achieved by the concurrent use of an arch-shaped magnetic field that is superimposed over the electrical field and formed in a closed loop configuration over the surface of the target. These methods are known as magnetron sputtering methods. The arch-shaped magnetic field traps electrons in an annular region adjacent the target surface thereby increasing the number of electron-gas atom collisions in the area to produce an increase in the number of positively charged gas ions in the region that strike the target to dislodge the target material. Accordingly, the target material becomes eroded (i.e., consumed for subsequent deposition on the substrate) in a generally annular section of the target face, known as the target raceway.
- In conventional target cathode assemblies, the target is attached to a nonmagnetic backing plate. The backing plate is normally water-cooled to carry away the heat generated by the ion bombardment of the target. Magnets are typically arranged beneath the backing plate in positions such that the above-noted magnetic field forms the shape of a loop or tunnel extending around the exposed face of the target.
- There has been a growing interest in sputtering target assemblies with increasingly different thermal expansion coefficients between the target material and the backing plate material. Although sputtering target assemblies may be made by solder bonding backing plates of various materials to a target, solder bonding has the disadvantage of not being able to withstand high power sputtering applications. Thus, diffusion bonded sputtering target assemblies are preferred.
- Diffusion bonds are produced by pressing the surfaces into contact while applying heat to induce metallurgical joining and diffusion to varying extent across the bond interface. A variety of different metal combinations may be used as bonding aids. These metals are applied as coatings to one or more of the DB interfacial surfaces to promote DB bonding and may be applied via conventional electroplating, electroless plating, vacuum cadmium plating, physical vapor deposition, or other techniques. In some cases, a metal foil is positioned between the surfaces to be joined by DB. Commonly, the surfaces to be joined are prepared by chemical or other means to remove oxides or their chemical films which may interface with the bonding process.
- Diffusion bonding techniques include hot isostatic pressing (HIP) and uniaxial hot pressing (UHP). In UHPing, the target and backing plate are placed between a pair of platens, or the like, in a chamber which provides for careful control of temperature, pressure and other atmospheric conditions. The controlled atmosphere may be that of a vacuum, inert, or reducing gas. The assembly is heated to a temperature that is below that of the lower melting member of the target/backing plate combination. As the assembly is heated, pressure is applied by the platens acting in a uniaxial direction. The assembly is maintained in the control chamber until a strong DB bond is formed.
- In the HIPing process, the target/backing plate assembly is placed within a canister. A vacuum is drawn on the canister and then it is placed in a HIPing chamber. An argon or helium atmosphere is charged into the canister and temperature and pressure are increased. The HIPing canister is subjected to pressure from all sides. As in the UHPing process, the temperature approaches the melting joint of the lower melting member of the target/backing plate combination. Then, the HIPed assembly is maintained at the desired temperature, pressure, and atmospheric conditions to form a strong DB bond.
- After bonding has occurred, the assembly is cooled. The cooled target usually bows or deflects to one direction. This deflection is usually caused by unequal shrinkage or expansion of the target and backing plate due to the differing CTE of each. Cracking of the bond between the target and backing plate, or delamination may also occur during cooling. In addition, the different CTE materials render the assembly susceptible to other stresses, degradations or distortions during the high temperatures that occur during sputtering. To remove the deflection and create a “flat” assembly target surface, the target is typically flattened mechanically.
- This diffusion bonding and subsequent flattening process is suitable for ductile targets such as titanium or tantalum. For brittle targets such as tungsten, however, the likelihood of delamination is greater throughout the process. The bond strengths between the layers of such target assemblies are typically less than 45 MPa.
- In accordance with one aspect of the invention, a method is provided for making a target/backing plate assembly. A target blank of a first metal or alloy is provided with the blank having a first surface defining a sputtering surface during the sputtering operation and an opposed second surface. A second metal or alloy is placed alongside the first and second target surfaces. A backing plate and placed adjacent the second metal or alloy that is positioned alongside the second target surface. The target, second metal, and backing plate thereby define a combined assembly.
- In accordance with one preferred embodiment, the combined assembly of target, second metal, and backing plate is diffusion bonded to form a diffusion bonded assembly. Then, at least a portion of the second material alongside the sputtering surface of the target is removed to thereby expose at least a portion of the sputtering surface.
- In certain embodiments of the invention, the target is W or alloy thereof, and the first and second surfaces of the target may be coated with an optional thin layer of Ti, Ni, or Cr prior to the step of placing the second metal or alloy alongside the first and second target surfaces.
- In other embodiments, the second metal or alloy comprises a metal having a modulus of elasticity in tension of less than or equal to 8.2×104 MPa, and the backing plate may have a coefficient of thermal expansion of less than or equal to 23.0×10−6 m/m/K. In certain instances, the second metal or alloy comprises Al or Al alloys such as Al 6061 or Al 1100.
- In one embodiment, the backing plate may comprise Ti or Ti alloy. In other embodiments, the backing plate may comprise Ti, Zr, Mo, Nb, or Ta and alloys thereof.
- In one exemplary embodiment, the second metal or alloy comprises a pair of plates. The first of the pair is placed adjacent the first surface (sputtering surface) of the target, and the second of the pair is placed adjacent the second surface of the target, thereby forming a sandwich construction of the target blank and the plates. The plates composed of the second metal or alloy may be Al or Al alloy.
- In yet other embodiments, the thickness of each of the plates composed of the second metal or alloy has a thickness of about 0.1-1.0 x wherein x is the thickness of the target blank.
- The target, second metal encapsulating the target, and backing plate assembly may be diffusion bonded at temperatures of between about 400-600 ° C. and at a pressure of not less than about 5 ksi. This diffusion bonding step may be provided in a one-step process or in a two-step process. In the two-step process, a first step comprises diffusion bonding of the target blank and second metal or alloy to form a combination, and then a second step comprises diffusion bonding of the combined target/second metal combination with the backing plate. In certain cases, the second step may be conducted at a temperature different from the temperature used in the first step.
- In other embodiments, the target may be W alloyed with Ta, Ti, or Si.
- In other aspects, the invention is directed toward a diffusion bonded W target/backing plate assembly. The assembly further includes an interlayer positioned intermediately between the W target and the backing plate. The backing plate may comprise Ti or Ti alloy, and the inner layer comprises Al or Al alloy. This assembly has a bond strength exceeding 50 MPa. In other embodiments, the bond strength exceeds 68.94 MPa (10 ksi).
- In still further embodiments, the target has a density in excess of 99.7%, a grain size of less than 100 μm, an oxygen content of less than 100 ppm, a carbon content of less than 30 ppm, and the purity of the W may be 99.999% and greater.
- In further embodiments, the target assembly comprises an exposed W target face. By this, it is meant that the face of the sputtering target has been exposed after performance of the processes above described so as to leave an adequate sputtering surface. Further, the assembly may comprise a sidewall portion having exposed Al or Al alloy and exposed Ti or Ti alloy surfaces thereof. A coating formed from the sputtering material is provided along the sidewall via conventional techniques such as plasma coating. This coating may have, for example, a thickness of about 0.001-0.020 inches. The interlayer may, for example, be Al 6061 or Al 1100, and the bond strength of the overall diffusion bonded assembly may exceed 60 MPa.
-
FIG. 1 is a schematic illustration showing one embodiment of the method with individual elements of the target assembly shown prior to diffusion bonding; -
FIG. 2 is a schematic illustration of the embodiment shown inFIG. 1 with the elements of the target assembly shown after diffusion bonding; and -
FIG. 3 is a schematic illustration of the embodiment shown inFIGS. 1 and 2 with the elements shown in a final assembly after finishing. - It has been surprisingly discovered that encapsulating brittle targets with a second material during the DB process produces diffusion-bonded sputtering target assemblies with bond strengths between the layers of equal to, or greater than 45 MPa.
- Turning now to
FIG. 1 , there is shown a diffusion bonded targetbacking plate assembly 100 in its pre-assembled state. The assembly comprises target blank 102 comprised of a first metal or alloy such as W. The target comprises a first ortop surface 104 that will serve as a sputtering surface upon completion of the assembly. The target blank also includes an opposedbottom surface 106. An optionalthin coating 112 can be applied to both surfaces of the target if desired. This coating layer may be comprised of Ti, Ni, or Cr and can be deposited on the target blank surfaces via conventional techniques. - As shown in
FIG. 1 , a second metal or alloy is provided in the form of a pair ofopposed plates plates first plate 108 is disposedadjacent sputtering surface 104 of the target blank, and theplate 110 is placed alongside thebottom surface 106 of the target and its optimalthin coating layer 112. - As shown, each of the
plates flanges - As further shown in
FIG. 1 , abacking plate 120 is also one of the assembly components, and this backing plate has atop surface 122 adapted to interfacially mate with the bottom surface of theplate 110 composed of the second metal or alloy. As shown, the lower orbottom surface 124 of thebacking plate 120 is exposed and is adapted for heat exchange contact with a cooling medium, such as water, typically used in cathodic sputter operations to help cool the target. - Turning now to
FIG. 2 , the assembly is shown after it has been subjected to a diffusion bonding operation of the aforementioned types. Here, the target can be seen surrounded or encapsulated within a matrix of the second metal or alloy comprised of the twoplates interfacial boundary 126. Theoverall assembly 100 can be provided with aslight champer 116 so as to facilitate insertion of the assembly into mechanical devices that are adapted to remove portions of the second metal or alloy 108 (and optional coating 112) adjacent the sputtering surface of the target blank. At present, it is preferred to machine away the metal oralloy 108 to expose at least a portion of thesputtering surface 104 of the target blank. -
FIG. 3 shows the finished assembly having an exposedsputtering surface 104. Asidewall area 128 is shown around the periphery of the target/second metal 110 interface. If desired, athin coating 330 of the target material may be placed over the exposed metals at this sidewall so as to help prevent unintended sputtering of the second metal and/or backing plate during the coating operation. The coating can be applied by conventional methods such as plasma coating and can be on the order of 0.001-0.020 inches in thickness. - In one embodiment of the method, the second metal or metal plates are formed from a material with a modulus of elasticity in tension of less than or equal to about 8.2×104 MPa. Further, the backing plate may be formed from a material with a coefficient of thermal expansion of less than or equal to 23.0×10−6 m/m/K.
- In one exemplary embodiment, the target blank is placed between the
plates - The target blank may comprise one or more of the materials selected from the group consisting of W, Ta, Ti, Si and alloys thereof.
- In another embodiment, one or more of the
plates plate - In another embodiment, the target blank is pre-treated with a bonding aid by coating the surface of the plate with a
thin layer coating 112 composed of one or more materials selected from the group consisting of Ti, Ni, Cr, and alloys thereof. The pre-treatment step occurs prior to encapsulating the target ingot within the plates. - In another embodiment, the backing plate comprises one or more of the materials selected from the group consisting of Ti, Zr, Mo, Nb, Ta, and alloys thereof.
- In yet another embodiment, one or more sidewalls of the finished assembly are coated with the sputtering material. In another embodiment, this
coating 112 has a thickness ranging from about 0.001 to about 0.020 inches. The coating may be applied using a plasma spray method. - In another embodiment, a diffusion-bonded sputtering target assembly (DBSTA) is disclosed comprising an exposed target sputtering surface and a backing plate, wherein the exposed target ingot and the backing plate are separated by, and diffusion bonded to, an interlayer.
- Another embodiment discloses a diffusion bonded sputter target assembly (DBSTA) wherein the target blank comprises one or more of the materials selected from the group consisting of W, Ta, Ti, Si and alloys thereof. In another embodiment, the backing plate comprises one of more of the materials selected from the group consisting of Ti, Zr, Mo, Nb, Ta, and alloys thereof. In yet another embodiment, the interlayer comprises one or more of the materials selected from the group consisting of aluminum and aluminum alloys. The interlayer may have a thickness ranging from about 0.1 to about 1 times a thickness of the target blank thickness.
- In another embodiment, a DBSTA is disclosed wherein the bond strength between the target and the interlayer and between the interlayer and the backing plate is equal to or greater than about 45 MPa. In yet another embodiment, the bond strength between the DBSTA is equal to or greater than about 60 MPa.
- A diffusion bonded sputtering target assembly was made by a method comprising the steps of encapsulating a W blank by contacting a top side of the blank with an Al 1100 metal plate and contacting a bottom side of the blank with an Al 1100 plate to form a W plate “sandwiched” between the two Al 1100 plates. The bottom side of the sandwich was superposed over a Ti backing plate. The W target blank, Al 1100 plates, and Ti backing plate were diffusion bonded at temperatures ranging from 400 to 600° C. and pressures greater than or equal to 34 MPa to form a sputtering target assembly intermediate. Then, the assembly was machined to remove the Al layer that covered the sputtering surface of the target.
- The diffusion bonded sputtering target assembly of Example 1 was tested in a sputtering device. The target survived 100 kWh while at a maximum sputtering power of 17 kWh. After sputtering, the target was measured for deflection and bond strength. The deflection on the back side of the target assembly was approximately 0.005 inches. The W-Al 1100 bond strength was measured to be between 46 and 55 MPa.
- A diffusion bonded sputtering target assembly was made as in Example 1, where after finishing, the sidewalls of the target were coated with W by plasma spray.
- A diffusion bonded sputtering target assembly was made as in Example 1, but Al 6061 was substituted for Al 1100. The W-Al 6061 bond strength was measured to be greater than 60 MPa.
- This written description uses examples to disclose the invention, including the best mode, and also to enable any person skilled in the art to practice the invention, including making and using any devices or systems and performing any incorporated methods. The patentable scope of the invention is defined by the claims, and may include other examples that occur to those skilled in the art. For example, although the embodiment discloses diffusion bonding the target, second metal plates, and the backing plate all in one step, the diffusion process may include multiple steps. Such other examples are intended to be within the scope of the claims if they have structural elements that do not differ from the literal language of the claims, or if they include equivalent structural elements with insubstantial differences from the literal languages of the claims.
Claims (5)
1. A diffusion bonded target/backing plate assembly wherein said target is composed of a target material consisting of W or W alloy, said assembly further comprising an interlayer positioned intermediate said W target and said backing plate, said backing plate comprising Ti or Ti alloy and said interlayer comprising Al or Al alloy, said assembly having a bond strength exceeding 50 MPa, wherein said assembly comprises a sidewall portion having exposed Al or Al alloy and exposed Ti or Ti alloy surfaces, said assembly having a plasma coating overlying said sidewall, wherein said plasma coating consists of said target material.
2. A diffusion bonded W target/backing plate assembly as recited in claim 1 wherein said bond strength exceeds 68.94 MPa (10 ksi).
3. A diffusion bonded W target/backing plate assembly as recited in claim 1 wherein said W target has a density in excess of 99.7%, a grain size of less than 100 microns, oxygen content of less than 100 ppm, carbon content of less than 30 ppm, and W metallic purity of 99.999% and greater.
4. A diffusion bonded W target/backing plate assembly as recited in claim 1 wherein said plasma coating has a thickness of about 0.001-0.020 inches.
5. A diffusion bonded W target/backing plate assembly as recited in claim 1 wherein said interlayer is Al 6061 and said bond strength exceeds 60 MPa.