US20170040471A1 - Method for forming structures in a solar cell - Google Patents
Method for forming structures in a solar cell Download PDFInfo
- Publication number
- US20170040471A1 US20170040471A1 US15/299,753 US201615299753A US2017040471A1 US 20170040471 A1 US20170040471 A1 US 20170040471A1 US 201615299753 A US201615299753 A US 201615299753A US 2017040471 A1 US2017040471 A1 US 2017040471A1
- Authority
- US
- United States
- Prior art keywords
- film layer
- solar cell
- forming
- contact pattern
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A conductive contact pattern is formed on a surface of solar cell by forming a thin conductive layer over at least one lower layer of the solar cell, and ablating a majority of the thin conductive layer using a laser beam, thereby leaving behind the conductive contact pattern. The laser has a top-hat profile, enabling precision while scanning and ablating the thin layer across the surface. Heterocontact patterns are also similarly formed.
Description
- This application is a continuation of U.S. Ser. No. 14/576,293, filed Dec. 19, 2014, entitled “Method for Forming Structures in a Solar Cell”, which published Apr. 16, 2015, as U.S. Patent Publication No. 2015/0104900 A1. U.S. Ser. No. 14/576,293 is a continuation of U.S. Ser. No. 13/265,438, filed Nov. 15, 2011, entitled “Method for Forming Structures in a Solar Cell”, which published Mar. 8, 2012, as U.S. Patent Publication No. 2012/0055546 A1. U.S. Ser. No. 13/265,438 is a §371 National Phase application of International Application No. PCT/US2010/031874, filed Apr. 21, 2010, entitled “Method for Forming Structures in a Solar Cell”, and claims the benefit of previously filed U.S. Provisional Application entitled “Method for Forming Structures in a Solar Cell,” filed Apr. 21, 2009, and assigned application Ser. No. 61/171,187; and is related to the commonly-assigned, previously filed U.S. Provisional Application entitled “High-Efficiency Solar Cell Structures and Methods of Manufacture,” filed Apr. 21, 2009, and assigned application Ser. No. 61/171,194; and to commonly-assigned, co-filed International Patent Application entitled “High-Efficiency Solar Cell Structures and Methods of Manufacture” filed Apr. 21, 2010, and assigned International Application number PCT/US2010/031869. Each of these Applications is hereby incorporated by reference herein in its entirety. All aspects of the present invention may be used in combination with any of the disclosures of the above-noted Applications.
- The present invention relates to solar cells. More particularly, the present invention relates to improved solar cell structures and methods of their manufacture.
- The formation of metalized structures, typically fingers and bus-bars, on the front (illuminated) side of solar cells is a necessary step in many cell designs. It is typically desirable that these structures be as fine (minimal width) as possible to minimize shading and contact recombination losses. Heterocontact structures which can be subsequently metalized may also be used to reduce contact recombination losses.
- The present invention addresses these requirements and others by providing a method for the formation of front/back side metal structures and selective heterocontact structures.
- The present invention in one aspect comprises a method of forming a conductive contact pattern on a surface of solar cell, including forming a thin conductive layer over at least one lower layer of the solar cell, and ablating a majority of the thin conductive layer using a laser beam, thereby leaving behind the conductive contact pattern. A self-aligned metallization may be formed on the conductive contact pattern.
- The lower layer may include a passivation and/or antireflective layer beneath the thin conductive layer, wherein the conductive contact pattern forms an electrical contact through the at least one lower layer to a semiconductor layer of the solar cell.
- Etching or cleaning the conductive contact pattern may be used after ablating to remove residue.
- In another aspect, the present invention comprises a method of forming a heterocontact pattern on a solar cell, including forming a thin layer over at least one lower layer of the solar cell; and ablating a majority of the thin layer using a laser beam, thereby leaving behind the heterocontact pattern. Metallization may be formed over the heterocontact pattern to facilitate a conductive connection to the at least one lower layer through the heterocontact pattern.
- The thin layer may comprise multiple, different layers.
- Etching the surface of the solar cell after ablating may be used to form a surface texture and/or to remove any laser ablation damage. The heterocontact pattern may be modified by in-situ heat treatment.
- All or part of the thin layer may include a doped semiconductor material or a surface passivation layer.
- The laser beam may have a top hat beam profile, and be projected through a mask. The laser beam shape created by the mask may be a regular polygon, possibly obstructed by a thin line running across the polygon. Multiple masks or a dynamically changing mask may be used.
- The laser may be operated at a wavelength and pulse width at which laser energy is strongly absorbed in the thin conductive layer and weakly absorbed in the at least one lower layer. In one embodiment, more than 80% of the surface area of the thin conductive layer is ablated, and the structures remaining after said ablating are in the pattern of contact fingers and/or busbars.
- Further, additional features and advantages are realized through the techniques of the present invention. Other embodiments and aspects of the invention are described in detail herein and are considered a part of the claimed invention.
- The subject matter which is regarded as the invention is particularly pointed out and distinctly claimed in the claims at the conclusion of the specification. The foregoing and other objects, features, and advantages of the invention are apparent from the following detailed description taken in combination with the accompanying drawings in which:
-
FIG. 1 is a functional block diagram of the main components of a laser machining system, in accordance with an aspect of the present invention; -
FIGS. 2a-d depict solar cell structuring using a square/rectangular top-hat beam profile in accordance with an aspect of the present invention; -
FIGS. 3a-d depict solar cell structuring using a square-with-line top-hat beam profile in accordance with an aspect of the present invention; -
FIGS. 4a-e depict solar cell structuring using combining two different mask shapes in accordance with an aspect of the present invention; and -
FIG. 5 depicts a completed finger/bus-bar structure on the front face of a solar cell created according to an aspect of the present invention; -
FIGS. 6a-b show an exemplary Ti solar cell finger in accordance with the present invention; -
FIG. 7 shows an exemplary Ni solar cell finger in accordance with the present invention; and -
FIGS. 8a-b show exemplary self-aligned metallization of the finger ofFIG. 7 . - The present invention provides, in one aspect, a manufacturing approach for the production of solar cell structures using negative laser ablation to form line structures on the front (and/or rear) face of a solar cell, resulting in very fine features which minimize interference with incident light and provide other advantages.
- Cell structuring is performed by, e.g., laser direct write using mask (or mask-less) projected “top hat” homogenous beam profiles such that a negative of the required line pattern is “written” or ablated, by an incident laser. Homogeneous top hat profiles allow for controlled thin film ablation with minimal pattern overlap and high resolution. Such patterning is not typically possible with gaussian beam profile systems.
-
FIG. 1 is a functional diagram showing the main components of a system for performing laser ablation using masked, projected top hat homogenous beam profiles. Thisexemplary system 10 includes alaser source 12, homogenizer andoptics 14,mask 16, scanner 18 (including a lens in one embodiment), andtranslation stage 20 for holding asolar cell 22 requiring ablation. - The formation of top-hat laser profiles (e.g., known to be a controlled flat top profile rather than Gaussian) can be effected using very high power (>300W) lasers combined with homogenizers, masks, mirrors, translation stages and/or scanners to enable full area exposure and direct writing of repetitive features, with the machined features being defined by the mask, translation stage, and/or scanner. Laser sources used may be high power multimode sources. The laser source wavelength, pulse width, repetition rate, and pulse energy are chosen to best suit the process requirements. Examples of such laser sources include diode pumped solid state Nd:YAG and Excimer lasers. Other examples include pulsed (Q-Switched) lasers or continuous wave lasers. The laser may be operated at a wavelength and pulse width at which laser energy is strongly absorbed in the thin film layer and weakly absorbed in the semiconductor substrate, to effect ablation of the upper layer.
- The exact size and shape of the projected beam which writes the pattern is determined by the system optics and the mask to match the process requirements. In general, and without limitation, the laser beam shape created by the mask may be any regular polygon, possibly obstructed by a thin line running across the polygon. Multiple masks or a dynamically changing mask may be used to process a single solar cell. The laser may be a pulsed laser, have a top hat beam profile, process an area with a single laser pulse, where the overlap of the scanned beam is less than 20% of the single pulse processing area. In accordance with the invention, more than 80% of the surface area of the upper thin film later may be ablated, leaving behind the requisite fine pattern.
- Two exemplary shapes and scanning patterns which can be used to remove a thin film from the majority front of a solar cell are shown in
FIGS. 2 and 3 in accordance with the present invention. - As one example,
FIGS. 2a-d show a simple square or rectangle exposure unit 132 (FIG. 2d ) which is moved along translation pattern 130 (FIG. 2c ). The fine structure in the resultantthin film 126 is formed by negative laser ablation during appropriate translation of the beam and/or solar cell relative to each other. More particularly, a substrate 122 (shown in side view ofFIG. 2a —and possibly including other layers) has formed thereon athin film layer 124 requiring ablation. Thelaser exposure unit 132 is translated/stepped/scanned in a planar translation pattern 130 (FIG. 2c ) over the film, avoidingareas 140, resulting in a finely patterned structure 126 (FIG. 2b ). - As another example,
FIGS. 3a-d show a square or rectangle exposure unit 232 (FIG. 3d ) which has a central blockedsegment 233 in the mask which is moved along translation pattern 230 (FIG. 3c ). This blocked segment can be used to form thefine structure 226 in the thin film by negative ablation. More particularly, a substrate 222 (shown in side view ofFIG. 3a —and possibly including other layers) has formed thereon athin film layer 224 requiring ablation. Thelaser exposure unit 232 with blockedarea 233 is translated/stepped/scanned in a planar translation pattern 230 (FIG. 3c ) over the film, blockingareas 240, resulting in a finely patterned structure 226 (FIG. 3b ). - The exposure unit shapes illustrated in
FIGS. 2d and 3d can be combined into a single laser scan sequence, as shown inFIGS. 4a -e. More particularly, a substrate 322 (shown in side view ofFIG. 4a —and possibly including other layers) has formed thereon athin film 324 requiring ablation. Thelaser exposure unit 332 with blocked area 333 (FIG. 4d ), and also rectangular pattern 334 (FIG. 4e ), are translated/stepped/scanned in a planar translation pattern 330 (FIG. 4c ) over the film, avoidingareas 340, resulting in a finely patterned structure 326 (FIG. 4b ). Very rapid changing of the mask shapes 332 and 334 may be achieved by, for example, using a high speed galvanometer which inserts a beam blocking element at (or very close to) the plane of the mask. Therefore, transition between the shapes shown inFIGS. 2 and 3 may be done very quickly (in milliseconds) without adversely affecting the overall processing time. Such dynamic mask changing techniques can be synchronized with beam and/or stage translations to provide more flexibility in the types of patterns which can be economically produced. -
FIG. 5 shows a solar cell 422 having a pattern offingers 426 andbus bars 427 on a surface thereof, formed in accordance with any of the above-described aspects of the present invention. The resulting structures can be very fine (<10 um line width). The minimum pattern resolution is nominally defined by the optical resolution of the system. With this technique many types of thin films may be cost effectively patterned to form solar cell structures. As an example consider a thin film with an ablation threshold of 3 J/cm2. A 300W laser source would be capable of patterning the entire area of a 250 cm2 solar cell in as little as 2.5 seconds. Such high throughput supports the demanding economics of solar cell production. - One improvement involves using any form of texture on the substrate (122, 222, 322) where this texture is of a scale comparable to that of spatial inhomogeneities present in the intensity profile of the top hat laser beam. Such texture provides an important beam-homogenizing function—as it is generally desirable to operate the laser beam with a fluence at or close to the ablation threshold of the layer (124, 224, 324) and hence, a locally homogenized beam adds a greater deal of control and precision.
- The present invention has been described as applying to the front, light receiving, surface of a solar cell but can be equally applied to structures on the rear surface. Application of the invention to both sides of a solar cell will result in a bifacial solar cell which could be capable converting photons incident on both front and rear surfaces.
- With reference to the above figures, the present invention provides a method for forming, e.g., contact metallization or other fine structures in a solar cell, the method including the steps of:
- A1) On the front (or back) surface of a solar cell (e.g., semiconductor substrate) a continuous thin film metal layer (124, 224, 324) is deposited, the metal film material and thickness being selected such that it has desirable adhesion, contact resistance, plating and laser ablation properties. Examples of metals or metal alloys which may have suitable properties include: nickel, nickel-vanadium, nickel-niobium, nickel-tantalum, aluminum, aluminum-silicon, chromium, titanium, silver and tungsten.
- A2) By laser ablation the thin film metal layer is removed from the majority of the front surface leaving behind structures (126, 226, 326) for example fingers or bus-bars, which can form the front contact metallization for the solar cell.
- A3) Self-aligned metallization of these thin film metal structures can optionally be performed. Nominally this is done to reduce series resistance losses. Typically this metallization is performed by selective electroplating, light-induced-plating and/or electroless plating onto the existing thin film metal structures.
- In addition to the steps A1) to A3) listed above, many variations and additions are possible in accordance with the present invention. For example after step A2) a chemical clean may be performed to remove any residual metal. Further a thermal anneal step may be performed prior to self-aligned metallization in step A3). In some embodiments, surface passivation and/or anti-reflective layers can be deposited on the solar cell prior to deposition of the thin film metal layer in step A1). Such passivation and anti-reflection layers could allow, or be modified in-situ, for electrical contact with the underlying semiconductor substrate. Alternatively or further in some embodiments surface passivation and/or antireflective layers may be deposited on the solar cell at some stage after final metallization in step A3).
- Another improvement involves the use of multi-layered metal as the thin layer (124,224,324). A single metal (or metal-alloy) layer may not provide optimal process or solar cell device performance. By using a multi-layered metal stack different metal properties may be exploited to provide better performance. For example in a two layer metal stack it is desirable that the bottom metal (next to
substrate - With reference to the above figures, another embodiment of the present invention involves a method for forming selective heterocontact (or as could otherwise more generally be described as selective emitter) structures in a solar cell, the method includes the steps of:
- B1) On the front surface of a semiconductor substrate a continuous thin film layer (124, 224, 324) is deposited. This thin film layer may consist of multiple stacked films, the film stack being designed with desirable contact resistance, contact recombination, series resistance, laser ablation, adhesion and etch resistance properties.
- Films used in this stack may include:
-
- doped semiconductor films such as polycrystalline or amorphous silicon, silicon, polycrystalline or amorphous silicon-carbide, polycrystalline or amorphous diamond-like-carbon; and/or
- undoped films such as silicon oxide, silicon nitride, intrinsic amorphous silicon, intrinsic polycrystalline silicon, aluminum oxide, aluminum nitride, phosphorus nitride, titanium nitride, intrinsic amorphous silicon carbide, intrinsic polycrystalline silicon carbide.
- B2) By laser ablation the thin film layer is removed from the majority of the front surface leaving behind structures (126, 226, 326), for example fingers and bus-bars. These structures can subsequently be metalized.
- B3) The front surface of the cell may be etched to form a surface texture and/or to remove any laser ablation damage, the laser patterned thin film structures having been designed to be resistant to this etch will remain.
- B4) Self-aligned metallization of these thin film structures may be performed.
- Typically this metallization is performed by selective electroplating, light-induced-plating, and/or electroless plating onto the existing thin film structures.
- In addition to the steps B1) to B4) listed above, many variations and additions are possible. For example after step B3) a dopant diffusion and/or thermal oxidation may be performed in order to form an emitter and/or effectively passivate the front surface of the cell. This has the additional advantage that the thermal oxide can aid in the selective plating of thin film structures. Another variation may involve the addition of a thermal treatment after step B2) to change properties, such as etch resistance, of the thin film layer. Typically in all schemes an anti-reflection and/or additional passivation layer may be deposited at some stage after final metallization in step B4).
- The invention can be applied to many solar cell structures, including any of those listed in the above-incorporated Patent Applications. The following are merely examples, but the invention is not limited to these examples.
- Example 1:
- A thin layer of Titanium metal is ablated from a passivated and random pyramid textured mono-crystalline silicon wafer to form thin metal fingers. Titanium is deposited on the front of the wafer by physical vapor deposition to a thickness of approximately 500 Å. This metal is ablated from the majority of the wafer surface to leave behind thin metal fingers with a width of approximately 50 μm. Such metal ablation can be performed using an Nd:YAG laser. When such a laser is imaged through a mask and a top-hat (or pseudo top-hat) profile created then single shot ablation with minimal shot overlap (<20%) can be used to create fine line metal features which form the finger and bus-bar pattern of the solar cell. In this example an industrial laser system capable of delivering 140W to the sample can process a 250 cm2 solar cell in approximately 4 sec. Further it can be shown, by cell lifetime measurements before and after laser ablation, that the required operating fluence is below the damage threshold of the cell passivation. An exemplary solar cell finger created by this large area laser ablation is depicted in
FIGS. 6a -b. - Example 2:
- A thin layer is Nickel-7% Vanadium metal alloy is ablated from a passivated and random pyramid textured mono-crystalline silicon to form thin metal fingers. Ni(7% V) is deposited by physical vapor deposition and to a thickness of approximately 500 Å. This metal is ablated from the majority of the wafer surface to leave behind thin metal fingers with a width of approximately 50 μm. Such metal ablation can be performed using an Nd:YAG laser. When such a laser is imaged through a mask and a top-hat (or pseudo top-hat) profile created then two shot per area can be used to create fine line metal features which form the finger and bus-bar pattern for a solar cell. Further such a patterned nickel film can directly act as a suitable seed layer for self-aligned metallization. Such metallization of the patterned nickel seed can, for example, be performed by electro-plating of Ni to a thickness of ˜1 μm followed by electro-plating of Cu to a thickness of approximately 20 μm. The resulting completed metal stack can thus have sufficiently high electrical conductance to function as front metal fingers with low series resistance power loss. An exemplary solar cell finger created by this large area laser ablation is depicted in
FIG. 7 ; and the self-aligned metallization is shown inFIGS. 8a -b. - One or more of the process control aspects of the present invention can be included in an article of manufacture (e.g., one or more computer program products) having, for instance, computer usable media. The media has embodied therein, for instance, computer readable program code means for providing and facilitating the techniques of the present invention. The article of manufacture can be included as a part of a computer system or sold separately.
- Additionally, at least one program storage device readable by a machine embodying at least one program of instructions executable by the machine to perform the capabilities of the present invention can be provided.
- The flow diagrams and steps disclosed herein are just examples. There may be many variations to these diagrams or the steps (or operations) described therein without departing from the spirit of the invention. For instance, the steps may be performed in a differing order, or steps may be added, deleted or modified. All of these variations are considered a part of the claimed invention.
- Although preferred embodiments have been depicted and described in detail herein, it will be apparent to those skilled in the relevant art that various modifications, additions, substitutions and the like can be made without departing from the spirit of the invention and these are therefore considered to be within the scope of the invention as defined in the following claims.
Claims (14)
1. A method comprising forming a contact pattern on a surface of a solar cell, the solar cell comprising a textured semiconductor substrate, the forming comprising:
forming at least one film layer of a layer of the solar cell, the at least one film layer comprising a material having an ablation threshold;
irradiating a first portion of the at last one film layer with a laser, without irradiating a second portion of the at least one film layer, the laser having an intensity profile of a non-Gaussian top-hat laser beam, and the irradiating ablating the entire first portion of the at least one film layer, leaving the second portion of the at least one film layer as the contact pattern, the laser being operated at a fluence near or at the ablation threshold of the material of the at least one film layer;
wherein the texture semiconductor substrate comprises a random pyramid-shaped texture.
2. The method of claim 1 , further comprising forming self-aligned metallization on the contact pattern.
3. The method of claim 1 , wherein the material of the at least one film layer comprises a conductive material, and the contact pattern is a conductive contact pattern.
4. The method of claim 3 , wherein the at least one film layer comprises at least one film layer of a plurality of film layers, and wherein the forming comprises forming a plurality of film layers, the plurality of film layers comprising at least one film layer, wherein at least two film layers of the plurality of film layers comprise different conductive materials.
5. The method of claim 3 , wherein the conductive contact pattern comprises a plurality of conductive fingers having a width of approximately 50 μm or less.
6. The method of claim 1 , wherein the material of the at least one film layer comprises a semiconductor material, and the contact pattern is a hetero-contact pattern.
7. The method of claim 6 , wherein the semiconductor material further comprises a conductive dopant.
8. The method of claim 6 , wherein the at least one film layer comprises at least one film layer of a plurality of film layers, and wherein the forming comprises forming a plurality of film layers, the plurality of film layers comprising at least one film layer, wherein at least two film layers of the plurality of film layers comprise different semiconductor materials.
9. The method of claim 6 , wherein the hetero-contract pattern comprises a plurality of at least partially conductive fingers having a width of approximately 50 μm or less.
10. The method of claim 1 , wherein the non-Gaussian top-hat laser beam is projected through a mask.
11. The method of claim 10 , wherein the mask shapes the laser beam into a regular polygon.
12. The method of claim 10 , wherein the mask shapes the laser beam into a regular polygon obstructed by a thin line running across the regular polygon.
13. The method of claim 1 , wherein the non-Gaussian top-hat laser beam is projected through multiple masks or a dynamically changing mask.
14. The method of claim 1 , wherein the first portion of the film layer ablated by the non-Gaussian top-hat laser beam comprises more than 80% of the film layer.