US20170029971A1 - Process to deposit zinc-iron alloy layer material - Google Patents
Process to deposit zinc-iron alloy layer material Download PDFInfo
- Publication number
- US20170029971A1 US20170029971A1 US15/290,058 US201615290058A US2017029971A1 US 20170029971 A1 US20170029971 A1 US 20170029971A1 US 201615290058 A US201615290058 A US 201615290058A US 2017029971 A1 US2017029971 A1 US 2017029971A1
- Authority
- US
- United States
- Prior art keywords
- zinc
- iron
- iron alloy
- ions
- alloy layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A process for depositing a zinc-iron alloy layer material having a body centred cubic crystal structure of the Γ-phase, a (330) texture and an iron content of 12 to 20 wt.-% including the steps (i) providing a metallic substrate, (ii) contacting the substrate with an alkaline aqueous zinc-iron alloy plating bath containing 4 to 6 g/l zinc ions, 1 to 3 g/l iron ions, 25 to 35 g/l hydroxyl ions, 0.5 to 2.5 g/l of a quaternary ammonium polymer and at least one complexing agent selected from the group consisting of hydroxyl carboxylic acids and salts thereof and simultaneously applying a current to the substrate. The zinc alloy layer material provides a high corrosion protection to metallic substrates, has a high hardness and a bright appearance.
Description
- The present application is a U.S. divisional application which claims benefit of and priority under 35 U.S.C. §§120 and 121 to co-pending U.S. National Stage application Ser. No. 13/985,294, which was filed on 14 Aug. 2013, now ______, which is based on and claims benefit and priority under 35 U.S.C. §371 of International Application No. PCT/EP2012/051468, filed 30 Jan. 2012, which in turn claims benefit of and priority to European Application No. EP 11154475.5, filed 15 Feb. 2011, the entirety of each of which is hereby incorporated herein by reference.
- The invention relates to a hard zinc-iron alloy layer material having a bright appearance and which is useful to provide corrosion protection to a metallic substrate.
- Zinc-nickel alloys are well known as corrosion protection layers for metallic substrates. Such alloys are deposited from alkaline plating baths by electroplating. Typical plating bath compositions are disclosed for example in U.S. Pat. No. 5,405,523, U.S. Pat. No. 5,435,898, U.S. Pat. No. 6,652,728 B1 and U.S. Pat. No. 6,706,167 B1. The nickel content in zinc-nickel alloy layers deposited from such plating bath compositions ranges from 12 to 16 wt.-%. Zinc-nickel alloy layers provide a sufficient corrosion protection to metallic substrates such as iron based alloys and at the same time have a bright appearance and a Vickers hardness of >500 HV0.0025.
- Due to the toxicity of nickel ions released in small quantities from such zinc-nickel alloy layers alternative zinc alloy layers with lower toxicity but similar properties in terms of corrosion protection, bright appearance and sufficient hardness are needed.
- Plating bath compositions as those disclosed in U.S. Pat. No. 5,405,523, U.S. Pat. No. 5,435,898, U.S. Pat. No. 6,652,728 B1 and U.S. Pat. No. 6,706,167 B1 can be used to deposit zinc-iron alloys as well. However, zinc-iron alloys deposited from such plating bath compositions have an iron content of ≦1 wt.-% iron and do not fulfil the requirements in terms of corrosion protection and hardness of the alloy layer. Zinc-iron alloys having a higher iron content deposited from such plating bath compositions show an inhomogeneous iron distribution in the deposited layers and therefore provide no sufficient corrosion protection to the underlying substrate.
- In case of a higher iron ion concentration in such zinc-iron alloy plating bath compositions a mixture of various intermetallic zinc-iron phases is deposited. Furthermore, a non-uniform grain structure is obtained. This leads to a poor reproducibility of deposit properties such as corrosion protection properties, hardness and appearance.
- An alkaline process for deposition of zinc-iron alloy layers having an iron content of 15-25 wt.-% is described by V. Narasimhamurthy, B. S. Sheshadri, Metal Finishing (1997) 44. However, the process suffers from a steep increase of iron content in the coating at current densities lower than 1 A/dm2. Hence, such a plating bath is unsuitable for plating of substrates having a complex shape.
- A plating bath for deposition of zinc-iron alloy layers having an iron content of 17-20 wt.-% is disclosed in CN 101545125 A. A zinc-iron alloy layer material deposited from such a plating bath and successively coated with a Cr3+ ion containing passivation layer provides a corrosion protection which is not sufficient for most applications. Formation of 5% white rust in a neutral salt spray test was already observed after 65 h in case of a zinc-iron layer material containing 17.5 wt.-% iron. Furthermore, use of up to 1 g/l EDTA in the process is a severe limitation for industrial application.
- It is therefore the objective of the present invention to provide a zinc-iron alloy layer material having a high homogeneity in terms of alloy composition, corrosion protection properties, hardness and bright appearance.
- Another object of the present invention is to provide an alkaline aqueous plating bath suitable for deposition of a zinc-iron alloy layer material with a high homogeneity in terms of alloy composition, corrosion protection properties, hardness and bright appearance.
- Still another object of the present invention is to provide a process for deposition of zinc-iron alloy layer material with a high homogeneity in terms of alloy composition, corrosion protection properties, hardness and bright appearance.
- The first objective is solved by a zinc-iron alloy layer material having a body centred cubic crystal structure of the Γ-phase with a (330) texture and an iron content in the range of 12 to 20 wt.-%.
- The second objective is solved by an alkaline aqueous zinc-iron alloy plating bath comprising
-
- 4 to 6 g/l zinc ions
- 1 to 3 g/l iron ions
- 25 to 35 g/l hydroxyl ions,
- 0.5 to 2.5 g/l of a quaternary ammonium polymer and
- at least one complexing agent selected from the group consisting of hydroxyl carboxylic acid salts.
- The third objective is solved by a process for depositing a zinc-iron alloy layer material having a body centred cubic crystal structure of the Γ-phase with a (330) texture and an iron content in the range of 12 to 20 wt.-% comprising the steps
-
- (i) providing a metallic substrate and
- (ii) contacting the substrate with said alkaline aqueous plating bath and simultaneously applying a current to the substrate.
- Formation of less than 1% white rust in a neutral salt spray test according to ISO 9227 NSS of a steel substrate coated with a zinc-iron alloy layer material according to the present invention and a passivation layer containing Cr3+ ions is only observed after 672 h.
- The zinc-iron alloy layer material has a bright appearance and a Vickers hardness exceeding 380 HV0.0025.
-
FIG. 1 shows the position and height of the Γ-ZnFe alloy phase (330) reflection (Cu k alpha) as a function of the iron content in the deposited layer. -
FIG. 2 shows the results from X-ray diffraction measurements (Cu k alpha) of a zinc-iron alloy layer having an iron content of 15.5 wt.-% deposited by the process according to the present invention. - The zinc-iron alloy layer material shows a narrow range of 12 to 20 wt.-% iron. The average concentration of iron is 16 wt.-%. The observed concentration of iron and further evidence by X-ray diffraction measurements of zinc-iron alloy layers having an iron content in the range of 12 to 20 wt.-% show that an exclusive presence of the body centred cubic Γ-ZnFe alloy phase is obtained by the process according to the present invention.
FIG. 1 shows the peak position of the (330) reflection of the Γ-ZnFe alloy phase as determined by X-ray diffraction measurements using Cu k alpha radiation. The average (330) reflection position is 42.8° (Cu k alpha). - Surprisingly, the zinc-iron alloy layer material according to the present invention has a strong crystallographic (330) texture which is reflected by the exclusive occurrence of the (330) reflection of the Γ-ZnFe alloy phase determined by X-ray diffraction measurements (
FIG. 2 ). All other reflections observed belong to the underlying copper substrate coated for the measurement. - The term “texture” as used herein carries the meaning that would be understood by those of skill in the crystallographic arts. The crystallographic texture is caused by a preferred orientation of individual crystallites in the polycrystalline zinc-iron layer material according to the present invention.
- The (330) plane has the highest density of atoms in the body centred cubic crystal structure of the Γ-ZnFe alloy phase. Said strong crystallographic (330) texture is observed within the whole current density range of 0.01 to 10 A/dm2 which means on all areas of a substrate having a complex shape. Accordingly, the zinc-iron alloy layer material shows very homogeneous corrosion protection properties for an underlying substrate, a high hardness and a bright appearance.
- The body centred cubic crystal structure of the Γ-phase with a (330) texture and an iron content in the range of 12 to 20 wt.-% is obtained in a current density range from 0.01 to 10 A/dm2.
- Hence, the homogeneous properties are also achieved in case of substrates having a complex shape, such as fasteners, fixing elements, door hinges, lock casings, and the like.
- Up to date, the Γ-ZnFe alloy phase can only be obtained in form of a bulk material without the beneficial crystallographic (330) texture by powder metallurgical preparation methods.
- The zinc-iron alloy layer material according to the present invention is not only obtained by a wet chemical deposition method but also reveals a strong crystallographic (330) texture and is, accordingly to XRD measurements (Example 3), obtained in a pure form, i.e. the Γ-ZnFe alloy phase.
- The different crystallographic structure of the zinc-iron alloy layer material according to the present invention compared to zinc-iron alloy layer materials known in the art is furthermore demonstrated by enhanced corrosion protection properties. It is assumed by the inventors, that zinc-iron alloy layer materials having an iron content in the range of 17-20 wt.-% as disclosed in CN 101545125 A are a mixture of different zinc-iron alloy phases.
- Typical metallic substrate materials are steel and other ferrous base metals.
- Formation of less than 1% white rust in a neutral salt spray test according to ISO 9227 NSS of a steel substrate coated with a zinc-iron alloy layer material according to the present invention and a passivation layer containing Cr3+ ions is only observed after 600 to 1000 h.
- The zinc-iron alloy layer material has a bright appearance and a Vickers hardness exceeding 380 HV0.001.
- The zinc-iron alloy layer material having a body centred cubic crystal structure of the Γ-phase with a (330) texture and an iron content in the range of 12 to 20 wt.-% is obtainable by a process comprising the steps of
-
- (i) providing a metallic substrate,
- (ii) contacting the substrate with said alkaline aqueous plating bath comprising
- 4 to 6 g/l zinc ions
- 1 to 3 g/l iron ions
- 25 to 35 g/l hydroxyl ions,
- 0.5 to 2.5 g/l of a quaternary ammonium polymer and
- at least one complexing agent selected from the group consisting of hydroxyl carboxylic acid salts
and simultaneously applying a current to the substrate.
- The aqueous plating bath comprises zinc ions in a concentration of 4 to 6 g/l. Suitable sources for the zinc ions are water soluble zinc salts, zinc oxide and zinc metal. The water soluble zinc salts are selected from the group comprising zinc sulphate, zinc chloride, zinc nitrate, zinc gluconate and zinc citrate.
- The preferred sources of zinc ions are ZnO and zinc metal.
- The Zn content is generally maintained during use of the alkaline plating bath by dissolution of Zn metal.
- The concentration of iron ions in the aqueous plating bath ranges from 1 to 3 g/l, more preferably from 1.5 g/l to 2.5 g/l. Suitable sources for iron ions are water soluble salts of iron, such as ferrous sulphate, ferric sulphate and ferric chloride. The oxidation state of iron in the source material of the iron ions is not important as long as the source of iron ions is soluble in the alkaline plating bath.
- The aqueous plating bath contains 25 to 35 g/l hydroxyl ions which can be added as NaOH, KOH and NH4OH.
- The aqueous plating bath further contains a quaternary ammonium polymer in a concentration of 0.5 to 5 g/l, more preferably from 1 g/l to 2 g/l.
- Preferably, the quaternary ammonium polymer is an ureylene quaternary ammonium polymer.
- More preferably, the quaternary ammonium polymer is selected from polymers according formula (1)
- wherein m is 2 or 3, n is at least 2, R1, R2, R3 and R4 are the same and are selected from methyl, ethyl and hydroxyethyl, p ranges from 3 to 12 and X− is selected from Cl−, Br− and I−.
- The aqueous plating bath contains at least one complexing agent which is selected from hydroxyl carboxylic acid salts with sodium and potassium. The concentration of the at least one hydroxyl carboxylic acid salt ranges from 5 to 15 g/l, more preferably from 7 g/l to 12 g/l. Suitable complexing agents are selected from the group comprising citrates, tartrates, gluconates, glucoheptonates and glycollates of sodium and potassium.
- Optionally the aqueous zinc-iron plating bath further comprises at least one alkanolamine compound. The concentration of the at least one optional alkanolamine compound ranges from 5 to 20 g/l, more preferably 8 g/l to 12 g/l. The at least one optional alkanolamine compound is selected from the group comprising monoethanolamine, diethanolamine, triethanolamine, propanolamine, N-methylethanolamine and N,N,N′,N′-tetrakis-(2-hydroxypropyl)-ethylenediamine.
- The aqueous plating bath according to the present invention is free of strong complexing agents such as ethylenediamine tetraacetic acid, (nitrilo-triacetic acid, diethyl triamine penta-acetic acid, 1,3-propylene diamine penta-acetic acid and salts thereof.
- The process for depositing a zinc-iron alloy having an iron content of 12 to 20 wt.-% comprises the steps
-
- (i) providing a metallic substrate,
- (ii) contacting the substrate with said alkaline aqueous plating bath comprising
and simultaneously applying a current to the substrate.
- The substrate to be plated is cleaned by a typical pretreatment cycle for ferrous base materials, i.e. soak cleaning, electrocleaning, pickling and rinsing.
- The substrate to be coated with the zinc-iron alloy layer material having an iron content of 12 to 20 wt.-% is contacted with the aqueous plating bath described above. A direct current is passed from an anode to the cathodic substrate during deposition. The current density applied ranges from 0.01 to 10 A/dm2, more preferably from 1 to 3 A/dm2. The aqueous plating bath is held at a temperature in the range of 15 to 45° C., more preferably 20 to 30° C., during deposition.
- In a preferred embodiment of the present invention the zinc-iron alloy layer material is coated with a passivation layer. Such a passivation increases the corrosion protection for the underlying substrate material. Preferred passivation layers comprise Cr3+ ions which can be deposited from aqueous composition containing 2 to 10 g/l of Cr3+ ions, 2 to 20 g/l of nitrate, 0.5 to 2 g/l of fluoride and optionally 5 to 10 g/l of acid soluble colloidal silica and/or 0.2 g/l Co2+ ions. The passivation solution is kept in a pH range of 1.5 to 4.0 at 20 to 60° C.
- In another embodiment of the present invention the passivation layer is coated with a sealing layer which even further enhances the corrosion protection of the underlying substrate and/or serves as a adhesion promoter for a paint.
- The invention will now be illustrated by reference to the following non-limiting examples.
- Steel sheets having a size of 70×70×1 mm3 were immersed in soak cleaner Uniclean 155 at 70° C. for 30 min, rinsed, pickled in 15% hydrochloric acid for 30 s, rinsed, electrolytically cleaned in Nonacid 701 electrocleaner at 22° C. for 30 s under cathodic and 30 s anodic polarization at current density of 2 A/dm2, and finally rinsed in a 3 stage cascade rinse. Next, a zinc-iron alloy layer was deposited from a plating baths discussed in the respective examples.
- The substrates were rinsed with water and then a passivation layer containing Cr3+ ions was deposited onto the zinc-iron alloy layer from a passivation bath EcoTri® HC2 or Tridur® Ultra (products of Atotech Deutschland GmbH).
- The steel sheets were rinsed again with water and dried.
- For determination of alloy composition, separate samples made from Cu substrate were coated under same conditions as respective steel test samples. The alloy composition was measured on the Cu substrates with XRF spectrometry.
- Neutral salt spray tests were performed according to ISO 9227 NSS and evaluated according to ISO 3000258. The results are given with the respective examples.
- The hardness of zinc-iron alloy layer was determined with a Fischerscope H100C by instrumented indentation test according to ISO 14577. The applied stencil force was 10 to 50 mN. Vickers hardness was calculated from the measured indentation hardness HIT according to the theoretical equation HV=0.0945 HIT.
- Optical appearance was determined by optical inspection of the coated steel sheets. The desired appearance is denoted “bright” whereas “technically bright” means less bright than “bright”.
- A Bruker D8 Discover diffractometer was used for all measurements in Examples 3 and 4. The XRD settings were the following:
-
- anode: copper−λ=1.5406 Å;
- detector: Vantec-1 (Position Sensitive Detector, PSD)
- divergence slits: Goebel mirror (parallel beam)−0.6 mm slit+soller slit
- PSD angle: 3°
- receiving slit width: 14 mm
- anti-scattering slit width: 10 mm
- theta/theta configuration—locked coupled 2 theta scan from 30° to 150° with a 0.04° step and 1 s.
- A zinc-iron alloy layer was deposited onto a steel sheet from a plating bath composition disclosed in Example 17 in U.S. Pat. No. 6,652,728 B1.
- The iron content of the zinc-iron alloy is 0.6 wt.-%.
- Formation of white rust was observed after 240 h salt spray test.
- The hardness of the layer ranges from 150 to 220 HV0.0025.
- The layer has a technically bright appearance.
- A zinc-iron alloy layer was deposited onto a steel sheet from a plating bath comprising 7 g/l zinc ions, 1.5 g/l iron ions, 70 g/l NaOH, 25 ml/l of complexing agent and 1.2 g/l of a polymer according to formula (1) wherein R1, R2, R3 and R4 are methyl, m=3 and p=4.
- The iron content of the zinc-iron alloy is 9 wt.-%.
- The hardness of the layer is 300 HV0.001.
- The characteristic (330) reflection of the Γ-ZnFe phase at 2Θ=42.8° was not observed in the X-ray diffraction pattern (
FIG. 1 ). - Formation of 1% white rust was observed after 312 h salt spray test.
- The layer has a bright appearance.
- A zinc-iron alloy layer was deposited onto a steel sheet from a plating bath comprising 6 g/l zinc ions, 4 g/l iron ions, 70 g/l NaOH, 25 ml/l of complexing agent and 1.2 g/l of a polymer according to formula (1) wherein R1, R2, R3 and R4 are methyl, m=3 and p=4.
- The iron content of the zinc-iron alloy is 21 wt.-%.
- The hardness of the layer is 450 HV0.001.
- A steep decrease of the relative intensity of the characteristic (330) reflection characteristic for the Γ-ZnFe phase at 2Θ=42.8° was observed (
FIG. 1 ). New reflections in the X-ray diffraction pattern at 2Θ=35°, 73.2° and 128° were observed indicating a different crystallographic phase of the resulting zinc-iron alloy layer. - Formation of 1% white rust was observed after 480 h salt spray test.
- The layer has a bright appearance.
- A zinc-iron alloy layer was deposited onto a steel sheet from a plating bath comprising 6 g/l zinc ions, 2 g/l iron ions, 70 g/l NaOH, 25 ml/l of complexing agent, 1.2 g/l of a polymer according to formula (1) wherein R1, R2, R3 and R4 are methyl, m=3 and p=4.
- The iron content of the zinc-iron alloy is 16 wt.-%
- The hardness of the layer is 440 HV0.001.
- Formation of 1% white rust was observed after 672 h salt spray test.
- The layer has a bright appearance.
- Different zinc-iron alloy layer materials having an iron content in the range of 8 to 24 wt.-% were deposited onto sample holders made of copper.
- The as deposited zinc-iron alloy layers deposited onto copper sample holders were investigated by means of X-ray diffraction (XRD) measurements.
- The occurrence of the (330) reflection of the Γ-ZnFe phase at 2Θ=42.8° was investigated in respect to the iron content in the deposit by determining the position of said reflection and the relative intensity of said reflection. The data are summarized in
FIG. 1 . - The (330) reflection of the Γ-ZnFe phase is observed in the range of 12 to 20 wt.-% iron in the deposit. A maximum height of the (330) reflection was observed for a deposit having an iron content of approx. 18 wt.-%.
- A zinc-iron alloy layer material having an iron content of 15.5 wt.-% was deposited onto a sample holder made of copper and subjected to a X-ray diffraction measurement.
- The X-ray diffraction pattern of the zinc-iron alloy layer material having an iron content of 15.5 wt.-% is shown in
FIG. 2 together with lines representing calculated reflection positions and relative intensities of the reflections for a Γ-ZnFe phase (data used for calculation taken from De Wit et al., J. Mater. Engineering and Performance, 8 (1999), 531). Reflections of the sample holder made of copper are also present in the diffraction pattern. -
FIG. 2 shows that the layered material of the Γ-ZnFe phase having an iron content of 15.5 wt.-% which was obtained by a process according to the present invention has a (330) texture.
Claims (8)
1. A process for depositing a zinc-iron alloy layer material having a body centred cubic crystal structure of the Γ-phase, a (330) texture and an iron content of 12 to 20 wt.-% comprising the steps
(i) providing a metallic substrate,
(ii) contacting the substrate with an alkaline aqueous zinc-iron alloy plating bath comprising
4 to 6 g/l zinc ions
1 to 3 g/l iron ions
25 to 35 g/l hydroxyl ions,
0.5 to 2.5 g/l of a quaternary ammonium polymer and
at least one complexing agent selected from the group consisting of hydroxyl carboxylic acids and salts thereof and
simultaneously applying a current to the substrate.
2. The process according to claim 1 wherein the quaternary ammonium polymer is an ureylene quaternary ammonium polymer according to formula (1):
3. The process according to 1 the alkaline aqueous zinc-iron alloy plating bath further comprises an alkanolamine compound.
4. The process according to 2 the alkaline aqueous zinc-iron alloy plating bath further comprises an alkanolamine compound.
5. The process according to claim 3 wherein the alkanolamine compound is selected from monoethanolamine, diethanolamine, triethanolamine, propanolamine, N-methylethanolamine and N,N,N′,N′-tetrakis-(2-hydroxypropyl)-ethylenediamine.
6. The process according to claim 4 wherein the alkanolamine compound is selected from monoethanolamine, diethanolamine, triethanolamine, propanolamine, N-methylethanolamine and N,N,N′,N′-tetrakis-(2-hydroxypropyl)-ethylenediamine.
7. The process according to claim 3 wherein the concentration of the alkanolamine compound ranges from 8 to 20 g/l.
8. The process according to claim 4 wherein the concentration of the alkanolamine compound ranges from 8 to 20 g/l.