US20160042827A1 - Scintillator Plate - Google Patents
Scintillator Plate Download PDFInfo
- Publication number
- US20160042827A1 US20160042827A1 US14/918,904 US201514918904A US2016042827A1 US 20160042827 A1 US20160042827 A1 US 20160042827A1 US 201514918904 A US201514918904 A US 201514918904A US 2016042827 A1 US2016042827 A1 US 2016042827A1
- Authority
- US
- United States
- Prior art keywords
- layer
- scintillator
- protective layer
- buffer layer
- parylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A scintillator plate includes a substrate, a buffer layer, a scintillator layer arranged on the buffer layer, and a protective layer. The buffer layer and/or the protective layer is colored. The buffer layer and/or the protective layer include a proportion of carbonyl groups of greater than 5000 ppm.
Description
- This application is a continuation of U.S. application Ser. No. 14/409,828, filed Dec. 19, 2014, which is a §371 nationalization of PCT Application No.: PCT/EP2013/060186, filed May 16, 2013, designating the United States, which claims the benefit of
DE 10 2012 210 487.9, filed on Jun. 21, 2012. All related applications cited above are hereby incorporated by reference in their entirety. - The present invention relates to a scintillator plate for detecting X-rays.
- Scintillator plates serve to convert X-ray or gamma radiation into visible light and are used in medical technology and for non-destructive material testing. Typically, scintillator plates include a substrate on which a scintillator layer is arranged. The material of a scintillator layer is suitable for absorbing high-energy photons of X-ray and gamma radiation and for re-emitting the energy of the high-energy photons in the form of a large number of low-energy photons, e.g., in the visible region (therefore referred to in the following as light photons). It is thereby possible to process the information of the X-ray or gamma radiation with common optical sensors. The two-dimensional detection of an image is possible when using a matrix of photodetectors, such as for example CCD sensors made of crystalline silicon or photodiode arrays made of amorphous silicon.
- In order to achieve a high resolution in the image, as many as possible of the light photons generated by a single high-energy photon are received by a single photodetector of the matrix in order to obtain the information concerning the spatial correlation.
- One of the scintillator materials used is caesium iodide (referred to below as CsI). A scintillator layer made of CsI is typically generated by vapor-deposition of CsI onto a substrate in a vacuum. The CsI tends, under suitable manufacturing conditions, to form columnar microstructures or needles, which are separate from one another and which grow upwardly away from the substrate. The microstructures typically have structure sizes in the lateral direction of the order of 10 μm. Due to the effect of total reflection, these microstructures are suitable for conducting a large part of the photons generated in the interior thereof along the microstructure, similarly to a light guide. Only light photons that meet the surface at too large an angle leave the respective microstructure and scatter in the wider surroundings.
- If the layer thickness of the scintillator layer is selected to be larger, the microstructures tend to grow together and to come into contact with one another. This effect arises, e.g., in layer thicknesses from 300 μm upward. At contact sites of this type, the conditions, in part, no longer exist for total reflection, so that additional light photons are scattered out of the microstructures. Such layer thicknesses are used, e.g., when X-ray or gamma radiation with relatively high energies is used because, with the increasing energy, the absorption in the CsI decreases. The scintillator layer is configured thicker in order to absorb the majority of the X-ray or gamma photons. Typical layer thicknesses may be between 500 μm and 2000 μm. At these layer thicknesses, the spatial resolving power is consequently significantly reduced due to the light photons emerging laterally from the microstructures.
- In order to counteract this effect, as described in the published application DE 10242006 A1, it has been attempted to structure the scintillator layer in a targeted manner. As mentioned above, however, from a thickness of 300 μm, said scintillator layer tends to grow together again, so that at greater layer thicknesses, the desired effect cannot be achieved.
- In published applications DE 4433132 A1 and DE 10116803 A1, there are described attempts to color the surface of the microstructures in order to absorb light photons emerging laterally from the microstructure. However, the coloration is not restricted to the surface, but also extends into the interior of the microstructures. A raised level of absorption of the light photons in the interior of the microstructure is also associated therewith, which leads to a reduction in the desired signal.
- The publication “Structured CsI (T1) Scintillators for X-Ray Imaging Applications” by V. V. Nagarkar, IEEE Transactions on Nuclear Science, vol. 45, No. 3, June 1998, describes covering the microstructures with an optically absorptive protective layer.
- The patent specification EP 1 793 457 B1 describes covering the microstructures completely from the base to the tip with a light photon-absorbing covering material. A covering of this type has a refractive index close to that of caesium iodide and therefore restricts the total reflection to relatively flat incident angles to the border layer between the caesium iodide and the covering material, such that more light photons enter the covering material and are absorbed there.
- Protective layers made of parylene are known from the patent document U.S. Pat. No. 4,123,308 and the published application DE 19509438 A1.
- The present embodiments may obviate one or more of the drawbacks or limitations in the related art. For example, the present embodiments may address a problem in scintillator plates that the contrast and/or the resolution decreases with increasing thickness of the scintillator layer.
- The present embodiments may provide a scintillator plate that has better contrast, greater conversion efficiency and/or a higher resolution with a comparable thickness of the scintillator layer.
- The present embodiments relate to a scintillator plate having a substrate, a scintillator layer and a protective layer. A method may be provided for producing a scintillator plate of this type.
- The method for producing a scintillator plate includes providing a substrate. A buffer layer is applied to the substrate. The application of a scintillator layer onto the substrate is provided. A protective layer is applied to the scintillator layer. The buffer layer and/or the protective layer is colored by tempering.
- Because the buffer layer and/or the protective layer is colored by tempering, there is no danger that coloring substances will enter the scintillator layer and reduce the efficiency of the scintillator layer through absorption of the propagating light photons there. However, due to the coloring, the protective layer has a raised absorption for scattered light photons. For example, if the light photons do not pass through the protective layer by the shortest route, the light photons propagate at an angle to the propagation direction of the generating gamma or X-ray photons and take a longer path in the protective layer. Thus, due to the absorption of these non-directed light photons, the contrast and the resolution of the scintillator plate is improved. In this way, a colored buffer layer reduces the number of light photons that leave the scintillator layer in the direction toward the substrate at an angle and fall, reflected back from the substrate, in the direction of a detector. Because these light photons are also diffusely distributed around the original generation site, the absorption of the light photons in the buffer layer also improves the resolution and the contrast of the scintillator plate.
- The scintillator plate includes a substrate, a buffer layer on a surface of the substrate, a scintillator layer arranged on the buffer layer, and a protective layer. The buffer layer and/or the protective layer include a proportion of carbonyl groups, such that the buffer layer and/or the protective layer have a yellowish coloration.
- Due to the yellowish coloration of the protective layer, the protective layer has a raised absorption for scattered light photons, e.g., if the light photons do not pass through the protective layer by the shortest route, but propagate at an angle to the propagation direction of the generating gamma or X-ray photon and take a longer path in the protective layer. Thus, due to the absorption of these non-directed photons, the contrast and the resolution of the scintillator plate are improved. In the same way, a colored buffer layer reduces the number of light photons that leave the scintillator layer in the direction toward the substrate at an angle and fall, reflected back from the substrate, in the direction of a detector. Because these light photons are also distributed diffusely around the original generation site, due to the absorption thereof, the resolution and the contrast of the scintillator plate are also improved. The yellow coloration of the buffer layer and/or of the protective layer due to the carbonyl groups may be generated, for example, by tempering in an oxygen-containing atmosphere. Such coloration effects may occur with carbonyl proportions of, for example, more than 5000 ppm, where the coloration and the raised oxygen content levels may be limited to regions of the layer. The coloration may be useful because absorption of light in the visible wavelength region is provided without the protective layer being changed by pigments or coloring agents. The carbonyl groups arise in the buffer layer or the protective layer itself and do not pass into the scintillator layer where the carbonyl groups would reduce the conversion efficiency thereof.
- The protective layer may be made of a parylene from the substance group of poly-p-xylylenes, in particular, one of parylene C, parylene N or parylene D.
- Parylene C, for example, may be deposited from a gaseous phase and does not require water or solvent for application. A water-impervious protective film is formed, which protects the scintillator layer against moisture. This is useful, e.g., for the hygroscopic caesium iodide. Furthermore, parylene C is capable of becoming deposited in interstices by condensation from the gaseous phase.
- In one embodiment of the method, the tempering is implemented in a temperature range from 190° C. to 240° C. in an oxygen-containing atmosphere. In the above-mentioned temperature range, the scintillator layer is stable, whereas suitable protective layers become colored at these temperatures and with a supply of oxygen.
- In one embodiment of the scintillator layer, the scintillator layer forms microstructures such that interstices form between the microstructures essentially perpendicularly to the surface of the scintillator plate toward the substrate.
- The microstructure with the interstices extending essentially perpendicularly from the surface of the scintillator plate toward the substrate conducts the light photons generated through conversion of the X-rays and gamma rays, via total reflection, to border surfaces of the microstructures within the scintillator layer, e.g., in the direction toward the surface of the scintillator plate. Due to the small dimensions of the microstructure in the direction parallel to the surface of the scintillator plate, the light photons generated within a microstructure are guided to an area that corresponds to the small dimensions of the microstructure. Because the protective layer, which extends into the interstices between the microstructures, has an appreciable absorption for light photons, the protective layer absorbs the light photons scattered from the microstructure with a high probability and thereby improves the contrast and the resolution of the scintillator plate. Because the protective layer extends only partially into the interstices between the microstructures, and because a region that adjoins the buffer layer remains free, the border surfaces of the microstructure in this region are not in contact with the protective layer. Because the refractive index of the material of the scintillator layer differs more strongly from the surroundings than from the material of the protective layer, the limiting angle for total reflection in the region in which the protective layer does not extend is greater. Therefore, in this region, a greater proportion of the light photons generated in the microstructure by the X-ray or gamma photons is reflected back into the microstructure at the border surface and is guided away from the substrate in the microstructure.
- In one embodiment of the method, the scintillator layer includes caesium iodide and is deposited onto the buffer layer. Caesium iodide is distinguished by a good efficiency level for the conversion of X-ray photons into light photons. Furthermore, caesium iodide tends, when deposited on the substrate, to arrange itself into needle-like microstructures perpendicularly to the surface of the substrate, the microstructures acting as light guides and guiding the majority of the light photons generated in the interior of the microstructures to the surface.
- In one embodiment of the scintillator plate, the scintillator plate has microstructures with interstices. The interstices extend essentially perpendicularly to the surface of the scintillator plate toward the substrate. The microstructure conducts the light photons generated through conversion of the X-rays and gamma rays, via total reflection at border surfaces of the microstructures within the scintillator layer, e.g., in the direction toward the surface of the scintillator plate. Due to the small dimensions of the microstructure in the direction parallel to the surface of the scintillator plate, the light photons generated within a microstructure are guided to an area that corresponds with the small dimensions of the microstructure.
- In one embodiment of the scintillator plate, the scintillator layer includes caesium iodide. Caesium iodide is distinguished by a good efficiency level for the conversion of X-ray photons into light photons. Furthermore, due to the self-organization thereof, caesium iodide tends to be arranged in needle-like microstructures that are oriented perpendicularly to the surface of the substrate.
- The buffer layer and/or the protective layer may include one of parylene C, parylene N or parylene D. A buffer layer or protective layer made of parylene C is impermeable to water and is configured to protect the microstructures of the scintillator layer against moisture, which may be useful, e.g., for the hygroscopic caesium iodide. Furthermore, parylene C is suitable, during deposition from the gaseous phase, also to extend into interstices in the substrate or between the microstructures.
- In one embodiment, the buffer layer and/or the protective layer of parylene includes a proportion of carbonyl groups of, for example, greater than 5000 ppm, which causes a yellowish coloration. The coloration and the raised oxygen content may be limited to regions of the layer. The coloration is useful because absorption of light in the visible wavelength region is provided without the buffer layer and/or the protective layer being changed by pigments or coloring agents.
-
FIG. 1 is a cross-section through a scintillator plate with a small thickness of the scintillator layer according to the prior art. -
FIG. 2 is a cross-section through a scintillator plate with a large thickness of the scintillator layer according to the prior art. -
FIG. 3 is a schematic view of a portion of the scintillator plate ofFIG. 2 . -
FIG. 4 is a schematic, cross-sectional view of a scintillator plate configured in accordance with one embodiment. -
FIG. 5 is a graphical representation of transmission spectra of a layer of parylene before and after tempering. -
FIG. 1 is a cross-section through a scintillator plate 1 according to the prior art. The scintillator plate 1 has asubstrate 10 on which ascintillator layer 20 is arranged. If the material of thescintillator layer 20 is caesium iodide, then when growing on thesubstrate 10, the material forms microstructures in the form of columns or needles that extend away from thesubstrate 10. Thescintillator layer 20 is relatively thin, typically thinner than, for example, 300 μm, so that the individual columns or needles are separate from one another. Arranged on thescintillator layer 20 is aprotective layer 30, which is intended to protect thescintillator layer 20 against environmental influences. Such environmental influences may be dirt, liquids, gases or moisture. -
FIG. 2 shows, by contrast, a scintillator plate 1 with ascintillator layer 20 made of caesium iodide, as is typical for a thickness of 1000 μm. The individual microstructures in the form of columns or needles tend, at this thickness, to come into contact with one another atcontact sites 21. -
FIG. 3 shows, in a detail view ofFIG. 2 , how X-ray radiation incident in thescintillator layer 20 is converted into visible light and how this light spreads out. AnX-ray photon 60 interacts, at a respective probability, with the electrons of the scintillator layer 20 (by absorption, Compton effect). Due to the changes caused thereby in the electron shells of atoms of thescintillator layer 20,photons light photons 62 impinges at a steep angle on outer border surfaces of the microstructures of thescintillator layer 10, so that theselight photons 62 leave the microstructure. Another portion of thelight photons 61 is incident on the outer border surface of the microstructure at an angle smaller than the angle for total reflection and is completely reflected back into the microstructure. Theselight photons 61 are therefore conducted by the microstructure along the microstructure as by a light guide. However, if the outer border surface is in contact with another microstructure, then alight photon 63 may also cross over into an adjacent microstructure. Both thelight photons 62 that leave the microstructure as well as thelight photons 63 that cross over into other microstructures leave the scintillator layer at adistance 64 from the microstructure in which the X-ray photon was converted. Theselight photons -
FIG. 4 shows a cross-section through a scintillator plate 1 according to one embodiment. The scintillator plate 1 includes asubstrate 10 onto which abuffer layer 11 is applied. Arranged thereon is thescintillator layer 20. Thescintillator layer 20 is structured into microstructures between which interstices 22 extend from an upper side facing toward aphotodetector 100 to thesubstrate 10. Theinterstices 22 extend essentially perpendicularly to the surface of thesubstrate 10. - The
protective layer 30 is applied to the upper side facing toward thephotodetector 100 and extends into theinterstices 22 between the microstructures of thescintillator layer 20. Theprotective layer 30 may extend into theinterstices 22 whilst with thin layers theprotective layer 30 extends as far as thebuffer layer 11. Theprotective layer 30 may extend into theinterstices 22 only part of the way from the upper side facing toward thephotodetector 100 to thebuffer layer 11. Theprotective layer 30 may extend from the upper layer up to 500 μm into the interstices 22. - The
protective layer 30 is colored so as to absorb visible light appreciably. The coloration relates both to a region of theprotective layer 30 applied to the upper side facing toward thephotodetector 100, as well as to a region of theprotective layer 30 that extends into theinterstices 22 between the microstructures of thescintillator layer 20. A significant to overwhelming proportion oflight photons scintillator layer 20 are absorbed by theprotective layer 30 within the dimensions of thescintillator layer 20. This may be, for example, a coloration in which at least 10% of the light is absorbed in a propagation distance of 1000 μm. - However, the
buffer layer 11 may also or only be colored. Acolored buffer layer 11 reduces the number of light photons propagating in the direction of thesubstrate 10 and being reflected therefrom. Due to the angular distribution and the large distance that these light photons have to cover to the detector on the side of the scintillator plate 1 facing away from the substrate, the photons are distributed over a wide region. If, however, the light photons are absorbed in thecolored buffer layer 11, the resolution and the contrast of the scintillator plate 1 increase accordingly. - The coloration may be evoked, for example, by the formation of carbonyl groups in the
buffer layer 11 and/or theprotective layer 30, if these are made, for example, of parylene. The carbonyl groups are noticeable, e.g., due to a yellowish coloration, which may also become a brownish color tone. A possible route to creating the carbonyl groups is described in the method set forth below. For example, the coloration may be provided via a carbonyl proportion in the protective layer of more than 5000 ppm. The presence of the carbonyl groups in an infrared spectrum of parylene may also be shown through absorption at the wave number of 1700 cm−1.FIG. 5 shows acorresponding transmission spectrum 110 of a parylene layer before tempering and atransmission spectrum 120 following tempering. Shown on the y-axis is the transmission in percentage values. Shown on the x-axis is the wavelength of the infrared light in the form of the wave number. Shown in thespectrum 120 is anabsorption peak 121 at a wave number of approximately 1700 cm−1, which is caused by the carbonyl groups and is not visible in thespectrum 110 before the tempering. In order to determine a relative concentration of the carbonyl groups, a ratio of the amplitude of the peak to the amplitude of an absorption line of the parylene, which is not changed by the tempering, may be taken. For this purpose, theabsorption peak - A corresponding coloration occurs if a quotient of the relevant absorption at the absorption peak of the wave number 820 cm−1 due to the relative absorption at the absorption peak of the wave number 1700 cm−1 is smaller than 10.
- Arranged on the upper side of the
scintillator layer 20 facing away from thesubstrate 10 and having theprotective layer 30 is aphotodetector 100. Thephotodetector 100 may be, for example, a 2-dimensional CCD matrix for recording a 2-dimensional X-ray image. The CCD matrix may have active elements made of crystalline semiconductors. A one-dimensional detector row may be moved over the scintillator plate 1 as thephotodetector 100. Photodiode arrays made of amorphous silicon may be used as thephotodetector 100. A maximum resolution is achieved when the dimensions of theindividual detector elements 101 correspond to the cross section of the microstructures in thescintillator layer 20 on the upper side. Smaller detector elements do not result in a higher resolution because, in the total reflections of the light photons in the microstructure, the spatial information regarding the X-ray photon becomes lost in the microstructure. - The substrate itself may be sufficiently thin and transparent or may be a fiber optic plate, so that the photodetector is arranged on the side of the
substrate 10 facing away from thescintillator layer 20. With a suitable photodetector that undergoes the process steps for generating thescintillator layer 20 without significant worsening of the detection properties, thescintillator layer 20 may be applied directly, or on alayer 11, onto the photodetector. - A method for manufacturing a scintillator plate 1 is now described.
- A
suitable substrate 10 is provided. Essentially all materials having a sufficiently clean and even surface for the growth of ascintillator layer 20 are suitable as the substrate. At the same time, the substrate is transparent to X-rayradiation 60. For example, glass, aluminum or amorphous carbon may be used as the material for the substrate. - A
buffer layer 11 may be applied to one of the above-mentioned base materials of thesubstrate 10. Thebuffer layer 11 may be made of the same substances as theprotective layer 30 and the substances are suitable, due to the particularly good properties thereof, both to protect asubsequent scintillator layer 20 against environmental influences and to form a suitable base for deposition of the scintillator layer, and are considered in greater detail below in relation to theprotective layer 30. - The
buffer layer 11 may be colored with one of the methods described in relation to theprotective layer 30. - As stated above, the
photodetector 100 may be used as thesubstrate 10. - In a further act, a
scintillator layer 20 is applied to thesubstrate 10. In one embodiment, caesium iodide serves as the scintillator material. Caesium iodide may be vapor-deposited under vacuum and becomes deposited on the substrate. During the deposition, the caesium iodide grows perpendicularly away from the surface of thesubstrate 10 in column-shaped or needle-shaped microstructures. As mentioned above in relation to thescintillator plate 10, these microstructures are useful for the imaging properties thereof. Furthermore, caesium iodide distinguishes itself, e.g., when doped with thallium, by an effective conversion of X-rays into visible light. - Other materials are also possible, which are suitable for converting X-ray radiation into visible light. Even if these materials do not themselves tend toward microstructuring, such structuring may be possible using technical means. Structuring of this type, for example, may be possible via photolithographic methods of semiconductor technology. For example, Gd2O2S may be used.
- In a further act, a
protective layer 30 is applied to thescintillator layer 20. For example, caesium iodide is hygroscopic and requires protection against contact with moisture. - In one embodiment, parylene C, which belongs together with the other parylenes to the group of poly-p-xylylenes, is applied as the
protective layer 30. The deposition of parylene C is implemented from a gaseous phase without solvent. The starting molecules polymerize to aprotective layer 30 directly onto the surface of thescintillator layer 20. In this process, the individual gaseous starting molecules are also capable of penetrating intointerstices 22 of thescintillator layer 20 and of forming aprotective layer 30 there that also extends into the interstices 22. - However, other materials may be used for the
protective layer 30, provided the materials are tolerable with the respective materials of thescintillator layer 20 and are capable of forming into a protective layer extending into theinterstices 22 between the microstructures. These materials may be, for example, other substances of the substance group of poly-p-xylylenes, such as parylene D or parylene N or also epoxy resins. - In one embodiment of the method, in a further act, the
protective layer 30 is colored by tempering. By heating theprotective layer 30 to a temperature in a range between 190° C. and 240° C. in an oxygen-containing atmosphere, the protective layer of parylene C becomes colored yellowish to yellow-brownish, depending on the temperature and duration of the heat treatment. Below 190° C., the coloration occurs so slowly that practicable production is not possible. Above 240° C., the structural stability and therefore the protective effect of the protective layer of parylene C no longer exists. Through tempering given these conditions, oxidation of the parylene occurs, so that oxygen is included into the parylene layer as carbonyl groups, which leads to the desired yellowish or brownish coloration. In one embodiment, the proportion of carbonyl groups in theprotective layer 30 or in portions of theprotective layer 30 amounts to more than 5000 ppm. - Due to the coloration achieved, light photons are absorbed in the
interstices 22 and, as a result, as described above, the contrast and resolution are improved. - Coloration through tempering may also be achieved with
protective layers 30 other than those mentioned above made of parylene C. The process parameters of duration, temperature and atmosphere composition are dependent on the respective materials of theprotective layer 30. A possible material for theprotective layer 30 may be, for example, an epoxy resin. - The
protective layer 30 may be already colored when the layer is applied. This may be possible, for example, in the case of gas deposition, in that a further component is added during the creation of theprotective layer 30, provided this does not color thescintillator layer 20 itself. - The
protective layer 30 may be colored following application, using a suitable coloring method. For example, theprotective layer 30 may be exposed to a further gaseous component, provided this does not damage thescintillator layer 20. - It is to be understood that the elements and features recited in the appended claims may be combined in different ways to produce new claims that likewise fall within the scope of the present invention. Thus, whereas the dependent claims appended below depend from only a single independent or dependent claim, it is to be understood that these dependent claims can, alternatively, be made to depend in the alternative from any preceding or following claim, whether independent or dependent, and that such new combinations are to be understood as forming a part of the present specification.
- While the present invention has been described above by reference to various embodiments, it should be understood that many changes and modifications can be made to the described embodiments. It is therefore intended that the foregoing description be regarded as illustrative rather than limiting, and that it be understood that all equivalents and/or combinations of embodiments are intended to be included in this description.
Claims (12)
1. A scintillator plate, comprising:
a substrate;
a buffer layer arranged on the substrate;
a scintillator layer arranged on the buffer layer; and
a protective layer; wherein the buffer layer, the protective layer, or both the buffer layer and the protective layer comprise a proportion of carbonyl groups, such that the buffer layer, the protective layer, or both the buffer layer and the protection layer have a yellowish coloration, and wherein the buffer layer, the protective layer, or both the buffer layer and the protective layer comprise a proportion of carbonyl groups of greater than 5000 ppm.
2. The scintillator plate of claim 1 , wherein the scintillator layer forms microstructures such that interstices extend between the microstructures essentially perpendicularly to the surface of the scintillator plate toward the substrate, and the protective layer extends into the interstices.
3. The scintillator plate of claim 1 , wherein the scintillator layer comprises caesium iodide.
4. The scintillator plate of claim 1 , wherein the buffer layer, the protective layer, or both the buffer layer and the protective layer are made of parylene from the substance group of poly-p-xylylenes.
5. The scintillator plate of claim 4 , wherein the buffer layer, the protective layer, or both the buffer layer and the protective layer are made of parylene C, parylene D or parylene N.
6. (canceled)
7. The scintillator plate of claim 2 , wherein the scintillator layer comprises caesium iodide.
8. The scintillator plate of claim 2 , wherein the buffer layer, the protective layer, or both the buffer layer and the protective layer are made of parylene from the substance group of poly-p-xylylenes.
9. The scintillator plate of claim 3 , wherein the buffer layer, the protective layer, or both the buffer layer and the protective layer are made of parylene from the substance group of poly-p-xylylenes.
10. The scintillator plate of claim 7 , wherein the buffer layer, the protective layer, or both the buffer layer and the protective layer are made of parylene from the substance group of poly-p-xylylenes.
11. The scintillator plate of claim 5 , the scintillator layer further comprising:
microstructures such that interstices form between the microstructures essentially perpendicularly to the surface of the scintillator plate toward the substrate, wherein the protective layer penetrates into the interstices during application.
12. The scintillator plate of claim 11 , wherein the scintillator layer comprises caesium iodide.