US20150165591A1 - Superhard constructions and methods of making same - Google Patents
Superhard constructions and methods of making same Download PDFInfo
- Publication number
- US20150165591A1 US20150165591A1 US14/407,958 US201314407958A US2015165591A1 US 20150165591 A1 US20150165591 A1 US 20150165591A1 US 201314407958 A US201314407958 A US 201314407958A US 2015165591 A1 US2015165591 A1 US 2015165591A1
- Authority
- US
- United States
- Prior art keywords
- superhard
- strata
- region
- layers
- grains
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
- 238000010276 construction Methods 0.000 title claims abstract description 59
- 238000000034 method Methods 0.000 title claims description 54
- 239000000463 material Substances 0.000 claims abstract description 182
- 238000011049 filling Methods 0.000 claims abstract description 8
- 230000001747 exhibiting effect Effects 0.000 claims abstract description 7
- 239000010432 diamond Substances 0.000 claims description 190
- 229910003460 diamond Inorganic materials 0.000 claims description 189
- 239000000758 substrate Substances 0.000 claims description 58
- 239000003054 catalyst Substances 0.000 claims description 50
- 239000011230 binding agent Substances 0.000 claims description 49
- 239000002245 particle Substances 0.000 claims description 43
- 239000000203 mixture Substances 0.000 claims description 36
- UONOETXJSWQNOL-UHFFFAOYSA-N tungsten carbide Chemical compound [W+]#[C-] UONOETXJSWQNOL-UHFFFAOYSA-N 0.000 claims description 28
- GUTLYIVDDKVIGB-UHFFFAOYSA-N cobalt atom Chemical compound [Co] GUTLYIVDDKVIGB-UHFFFAOYSA-N 0.000 claims description 26
- 229910017052 cobalt Inorganic materials 0.000 claims description 23
- 239000010941 cobalt Substances 0.000 claims description 23
- 238000005520 cutting process Methods 0.000 claims description 20
- 229910052751 metal Inorganic materials 0.000 claims description 19
- 239000002184 metal Substances 0.000 claims description 19
- 238000009826 distribution Methods 0.000 claims description 18
- PXHVJJICTQNCMI-UHFFFAOYSA-N Nickel Chemical compound [Ni] PXHVJJICTQNCMI-UHFFFAOYSA-N 0.000 claims description 17
- 239000002904 solvent Substances 0.000 claims description 16
- 238000005259 measurement Methods 0.000 claims description 14
- 238000005553 drilling Methods 0.000 claims description 13
- 229910052759 nickel Inorganic materials 0.000 claims description 12
- 239000000843 powder Substances 0.000 claims description 11
- 239000011435 rock Substances 0.000 claims description 11
- OKTJSMMVPCPJKN-UHFFFAOYSA-N Carbon Chemical compound [C] OKTJSMMVPCPJKN-UHFFFAOYSA-N 0.000 claims description 9
- XEEYBQQBJWHFJM-UHFFFAOYSA-N Iron Chemical group [Fe] XEEYBQQBJWHFJM-UHFFFAOYSA-N 0.000 claims description 8
- 238000003801 milling Methods 0.000 claims description 8
- 229910052804 chromium Inorganic materials 0.000 claims description 7
- WFKWXMTUELFFGS-UHFFFAOYSA-N tungsten Chemical compound [W] WFKWXMTUELFFGS-UHFFFAOYSA-N 0.000 claims description 7
- 229910052721 tungsten Inorganic materials 0.000 claims description 7
- 239000010937 tungsten Substances 0.000 claims description 7
- 229910045601 alloy Inorganic materials 0.000 claims description 5
- 239000000956 alloy Substances 0.000 claims description 5
- 229910052799 carbon Inorganic materials 0.000 claims description 5
- 229910002804 graphite Inorganic materials 0.000 claims description 4
- 239000010439 graphite Substances 0.000 claims description 4
- 238000000227 grinding Methods 0.000 claims description 4
- 150000001247 metal acetylides Chemical class 0.000 claims description 4
- 150000002739 metals Chemical class 0.000 claims description 4
- 239000002113 nanodiamond Substances 0.000 claims description 4
- 229910052742 iron Inorganic materials 0.000 claims description 3
- 229910052719 titanium Inorganic materials 0.000 claims description 3
- 229910052720 vanadium Inorganic materials 0.000 claims description 3
- 238000007792 addition Methods 0.000 claims description 2
- 150000004767 nitrides Chemical class 0.000 claims description 2
- 229910052763 palladium Inorganic materials 0.000 claims description 2
- 238000009527 percussion Methods 0.000 claims description 2
- 230000000737 periodic effect Effects 0.000 claims description 2
- 238000005096 rolling process Methods 0.000 claims description 2
- 150000003839 salts Chemical class 0.000 claims description 2
- 239000010410 layer Substances 0.000 description 122
- 238000005245 sintering Methods 0.000 description 24
- OKKJLVBELUTLKV-UHFFFAOYSA-N Methanol Chemical compound OC OKKJLVBELUTLKV-UHFFFAOYSA-N 0.000 description 18
- 239000002002 slurry Substances 0.000 description 13
- 238000002386 leaching Methods 0.000 description 10
- 239000002253 acid Substances 0.000 description 8
- 239000002131 composite material Substances 0.000 description 7
- 230000001965 increasing effect Effects 0.000 description 7
- 229910052582 BN Inorganic materials 0.000 description 6
- PZNSFCLAULLKQX-UHFFFAOYSA-N Boron nitride Chemical compound N#B PZNSFCLAULLKQX-UHFFFAOYSA-N 0.000 description 6
- 239000000654 additive Substances 0.000 description 5
- 238000006243 chemical reaction Methods 0.000 description 5
- 239000011651 chromium Substances 0.000 description 5
- 238000000151 deposition Methods 0.000 description 5
- 230000000694 effects Effects 0.000 description 5
- 238000010191 image analysis Methods 0.000 description 5
- 239000011159 matrix material Substances 0.000 description 5
- 239000002243 precursor Substances 0.000 description 5
- 238000012545 processing Methods 0.000 description 5
- 238000005299 abrasion Methods 0.000 description 4
- 230000015556 catabolic process Effects 0.000 description 4
- 238000006731 degradation reaction Methods 0.000 description 4
- 230000001976 improved effect Effects 0.000 description 4
- 235000012431 wafers Nutrition 0.000 description 4
- -1 PCD or PCBN Substances 0.000 description 3
- 238000004458 analytical method Methods 0.000 description 3
- 230000002902 bimodal effect Effects 0.000 description 3
- 239000000919 ceramic Substances 0.000 description 3
- 229910021446 cobalt carbonate Inorganic materials 0.000 description 3
- ZOTKGJBKKKVBJZ-UHFFFAOYSA-L cobalt(2+);carbonate Chemical compound [Co+2].[O-]C([O-])=O ZOTKGJBKKKVBJZ-UHFFFAOYSA-L 0.000 description 3
- 239000000945 filler Substances 0.000 description 3
- 238000003384 imaging method Methods 0.000 description 3
- 229910052758 niobium Inorganic materials 0.000 description 3
- 239000010955 niobium Substances 0.000 description 3
- 238000001878 scanning electron micrograph Methods 0.000 description 3
- VYZAMTAEIAYCRO-UHFFFAOYSA-N Chromium Chemical compound [Cr] VYZAMTAEIAYCRO-UHFFFAOYSA-N 0.000 description 2
- 239000002202 Polyethylene glycol Substances 0.000 description 2
- CDBYLPFSWZWCQE-UHFFFAOYSA-L Sodium Carbonate Chemical compound [Na+].[Na+].[O-]C([O-])=O CDBYLPFSWZWCQE-UHFFFAOYSA-L 0.000 description 2
- 230000002159 abnormal effect Effects 0.000 description 2
- 238000000231 atomic layer deposition Methods 0.000 description 2
- ZJRWDIJRKKXMNW-UHFFFAOYSA-N carbonic acid;cobalt Chemical compound [Co].OC(O)=O ZJRWDIJRKKXMNW-UHFFFAOYSA-N 0.000 description 2
- 238000005229 chemical vapour deposition Methods 0.000 description 2
- 238000000576 coating method Methods 0.000 description 2
- UFMZWBIQTDUYBN-UHFFFAOYSA-N cobalt dinitrate Chemical compound [Co+2].[O-][N+]([O-])=O.[O-][N+]([O-])=O UFMZWBIQTDUYBN-UHFFFAOYSA-N 0.000 description 2
- 229910000001 cobalt(II) carbonate Inorganic materials 0.000 description 2
- 238000012937 correction Methods 0.000 description 2
- 238000002848 electrochemical method Methods 0.000 description 2
- 239000008187 granular material Substances 0.000 description 2
- 238000003475 lamination Methods 0.000 description 2
- 230000000670 limiting effect Effects 0.000 description 2
- 238000011068 loading method Methods 0.000 description 2
- 238000001000 micrograph Methods 0.000 description 2
- 238000002156 mixing Methods 0.000 description 2
- 230000002093 peripheral effect Effects 0.000 description 2
- 238000005240 physical vapour deposition Methods 0.000 description 2
- 229920001223 polyethylene glycol Polymers 0.000 description 2
- 230000001737 promoting effect Effects 0.000 description 2
- 230000002829 reductive effect Effects 0.000 description 2
- 238000004901 spalling Methods 0.000 description 2
- 238000010972 statistical evaluation Methods 0.000 description 2
- 238000010345 tape casting Methods 0.000 description 2
- XLYOFNOQVPJJNP-UHFFFAOYSA-N water Substances O XLYOFNOQVPJJNP-UHFFFAOYSA-N 0.000 description 2
- INZDTEICWPZYJM-UHFFFAOYSA-N 1-(chloromethyl)-4-[4-(chloromethyl)phenyl]benzene Chemical compound C1=CC(CCl)=CC=C1C1=CC=C(CCl)C=C1 INZDTEICWPZYJM-UHFFFAOYSA-N 0.000 description 1
- BVKZGUZCCUSVTD-UHFFFAOYSA-L Carbonate Chemical compound [O-]C([O-])=O BVKZGUZCCUSVTD-UHFFFAOYSA-L 0.000 description 1
- 229910000531 Co alloy Inorganic materials 0.000 description 1
- 238000004125 X-ray microanalysis Methods 0.000 description 1
- 239000003082 abrasive agent Substances 0.000 description 1
- 230000000996 additive effect Effects 0.000 description 1
- 230000001668 ameliorated effect Effects 0.000 description 1
- 239000010426 asphalt Substances 0.000 description 1
- 230000015572 biosynthetic process Effects 0.000 description 1
- 239000002775 capsule Substances 0.000 description 1
- 125000005587 carbonate group Chemical group 0.000 description 1
- 238000005266 casting Methods 0.000 description 1
- 239000004568 cement Substances 0.000 description 1
- GVEHJMMRQRRJPM-UHFFFAOYSA-N chromium(2+);methanidylidynechromium Chemical compound [Cr+2].[Cr]#[C-].[Cr]#[C-] GVEHJMMRQRRJPM-UHFFFAOYSA-N 0.000 description 1
- 239000011248 coating agent Substances 0.000 description 1
- 230000001427 coherent effect Effects 0.000 description 1
- 230000006835 compression Effects 0.000 description 1
- 238000007906 compression Methods 0.000 description 1
- 238000012669 compression test Methods 0.000 description 1
- 230000008602 contraction Effects 0.000 description 1
- 238000005336 cracking Methods 0.000 description 1
- 230000003247 decreasing effect Effects 0.000 description 1
- 230000000593 degrading effect Effects 0.000 description 1
- 230000001419 dependent effect Effects 0.000 description 1
- 230000008021 deposition Effects 0.000 description 1
- 238000000866 electrolytic etching Methods 0.000 description 1
- 238000001493 electron microscopy Methods 0.000 description 1
- 238000005516 engineering process Methods 0.000 description 1
- 230000002708 enhancing effect Effects 0.000 description 1
- 238000001704 evaporation Methods 0.000 description 1
- 230000008020 evaporation Effects 0.000 description 1
- 238000001125 extrusion Methods 0.000 description 1
- 239000010419 fine particle Substances 0.000 description 1
- 239000007770 graphite material Substances 0.000 description 1
- 229910052735 hafnium Inorganic materials 0.000 description 1
- 238000010438 heat treatment Methods 0.000 description 1
- 230000001939 inductive effect Effects 0.000 description 1
- 230000002401 inhibitory effect Effects 0.000 description 1
- 230000016507 interphase Effects 0.000 description 1
- 150000002500 ions Chemical class 0.000 description 1
- 238000010902 jet-milling Methods 0.000 description 1
- 238000005304 joining Methods 0.000 description 1
- 239000007788 liquid Substances 0.000 description 1
- 238000003754 machining Methods 0.000 description 1
- 239000000155 melt Substances 0.000 description 1
- 229920000609 methyl cellulose Polymers 0.000 description 1
- 239000001923 methylcellulose Substances 0.000 description 1
- 235000010981 methylcellulose Nutrition 0.000 description 1
- 238000005065 mining Methods 0.000 description 1
- 229910052750 molybdenum Inorganic materials 0.000 description 1
- 210000003739 neck Anatomy 0.000 description 1
- GUCVJGMIXFAOAE-UHFFFAOYSA-N niobium atom Chemical compound [Nb] GUCVJGMIXFAOAE-UHFFFAOYSA-N 0.000 description 1
- 238000013001 point bending Methods 0.000 description 1
- 238000000197 pyrolysis Methods 0.000 description 1
- 239000003870 refractory metal Substances 0.000 description 1
- 238000001226 reprecipitation Methods 0.000 description 1
- 230000035945 sensitivity Effects 0.000 description 1
- 238000000926 separation method Methods 0.000 description 1
- 239000002356 single layer Substances 0.000 description 1
- 238000004513 sizing Methods 0.000 description 1
- 229910000029 sodium carbonate Inorganic materials 0.000 description 1
- 239000007787 solid Substances 0.000 description 1
- 239000006104 solid solution Substances 0.000 description 1
- 239000000243 solution Substances 0.000 description 1
- 238000005507 spraying Methods 0.000 description 1
- 238000004544 sputter deposition Methods 0.000 description 1
- 229910052715 tantalum Inorganic materials 0.000 description 1
- 238000012360 testing method Methods 0.000 description 1
- 238000007751 thermal spraying Methods 0.000 description 1
- 229910003470 tongbaite Inorganic materials 0.000 description 1
- 230000007704 transition Effects 0.000 description 1
- 239000002023 wood Substances 0.000 description 1
- 229910052726 zirconium Inorganic materials 0.000 description 1
Images
Classifications
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B24—GRINDING; POLISHING
- B24D—TOOLS FOR GRINDING, BUFFING OR SHARPENING
- B24D3/00—Physical features of abrasive bodies, or sheets, e.g. abrasive surfaces of special nature; Abrasive bodies or sheets characterised by their constituents
- B24D3/02—Physical features of abrasive bodies, or sheets, e.g. abrasive surfaces of special nature; Abrasive bodies or sheets characterised by their constituents the constituent being used as bonding agent
- B24D3/04—Physical features of abrasive bodies, or sheets, e.g. abrasive surfaces of special nature; Abrasive bodies or sheets characterised by their constituents the constituent being used as bonding agent and being essentially inorganic
- B24D3/06—Physical features of abrasive bodies, or sheets, e.g. abrasive surfaces of special nature; Abrasive bodies or sheets characterised by their constituents the constituent being used as bonding agent and being essentially inorganic metallic or mixture of metals with ceramic materials, e.g. hard metals, "cermets", cements
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
- C04B35/515—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on non-oxide ceramics
- C04B35/52—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on non-oxide ceramics based on carbon, e.g. graphite
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
- C04B35/515—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on non-oxide ceramics
- C04B35/58—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on non-oxide ceramics based on borides, nitrides, i.e. nitrides, oxynitrides, carbonitrides or oxycarbonitrides or silicides
- C04B35/583—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on non-oxide ceramics based on borides, nitrides, i.e. nitrides, oxynitrides, carbonitrides or oxycarbonitrides or silicides based on boron nitride
- C04B35/5831—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on non-oxide ceramics based on borides, nitrides, i.e. nitrides, oxynitrides, carbonitrides or oxycarbonitrides or silicides based on boron nitride based on cubic boron nitrides or Wurtzitic boron nitrides, including crystal structure transformation of powder
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
- C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
- C04B35/64—Burning or sintering processes
- C04B35/645—Pressure sintering
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C26/00—Alloys containing diamond or cubic or wurtzitic boron nitride, fullerenes or carbon nanotubes
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23F—NON-MECHANICAL REMOVAL OF METALLIC MATERIAL FROM SURFACE; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL; MULTI-STEP PROCESSES FOR SURFACE TREATMENT OF METALLIC MATERIAL INVOLVING AT LEAST ONE PROCESS PROVIDED FOR IN CLASS C23 AND AT LEAST ONE PROCESS COVERED BY SUBCLASS C21D OR C22F OR CLASS C25
- C23F1/00—Etching metallic material by chemical means
- C23F1/02—Local etching
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23F—NON-MECHANICAL REMOVAL OF METALLIC MATERIAL FROM SURFACE; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL; MULTI-STEP PROCESSES FOR SURFACE TREATMENT OF METALLIC MATERIAL INVOLVING AT LEAST ONE PROCESS PROVIDED FOR IN CLASS C23 AND AT LEAST ONE PROCESS COVERED BY SUBCLASS C21D OR C22F OR CLASS C25
- C23F1/00—Etching metallic material by chemical means
- C23F1/10—Etching compositions
- C23F1/14—Aqueous compositions
- C23F1/16—Acidic compositions
- C23F1/28—Acidic compositions for etching iron group metals
-
- E—FIXED CONSTRUCTIONS
- E21—EARTH OR ROCK DRILLING; MINING
- E21B—EARTH OR ROCK DRILLING; OBTAINING OIL, GAS, WATER, SOLUBLE OR MELTABLE MATERIALS OR A SLURRY OF MINERALS FROM WELLS
- E21B10/00—Drill bits
- E21B10/46—Drill bits characterised by wear resisting parts, e.g. diamond inserts
-
- E—FIXED CONSTRUCTIONS
- E21—EARTH OR ROCK DRILLING; MINING
- E21B—EARTH OR ROCK DRILLING; OBTAINING OIL, GAS, WATER, SOLUBLE OR MELTABLE MATERIALS OR A SLURRY OF MINERALS FROM WELLS
- E21B10/00—Drill bits
- E21B10/46—Drill bits characterised by wear resisting parts, e.g. diamond inserts
- E21B10/56—Button-type inserts
- E21B10/567—Button-type inserts with preformed cutting elements mounted on a distinct support, e.g. polycrystalline inserts
-
- E—FIXED CONSTRUCTIONS
- E21—EARTH OR ROCK DRILLING; MINING
- E21B—EARTH OR ROCK DRILLING; OBTAINING OIL, GAS, WATER, SOLUBLE OR MELTABLE MATERIALS OR A SLURRY OF MINERALS FROM WELLS
- E21B10/00—Drill bits
- E21B10/46—Drill bits characterised by wear resisting parts, e.g. diamond inserts
- E21B10/56—Button-type inserts
- E21B10/567—Button-type inserts with preformed cutting elements mounted on a distinct support, e.g. polycrystalline inserts
- E21B10/573—Button-type inserts with preformed cutting elements mounted on a distinct support, e.g. polycrystalline inserts characterised by support details, e.g. the substrate construction or the interface between the substrate and the cutting element
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B22—CASTING; POWDER METALLURGY
- B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
- B22F5/00—Manufacture of workpieces or articles from metallic powder characterised by the special shape of the product
- B22F2005/001—Cutting tools, earth boring or grinding tool other than table ware
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
- C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
- C04B2235/30—Constituents and secondary phases not being of a fibrous nature
- C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
- C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
- C04B2235/30—Constituents and secondary phases not being of a fibrous nature
- C04B2235/38—Non-oxide ceramic constituents or additives
- C04B2235/3804—Borides
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
- C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
- C04B2235/30—Constituents and secondary phases not being of a fibrous nature
- C04B2235/38—Non-oxide ceramic constituents or additives
- C04B2235/3817—Carbides
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
- C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
- C04B2235/30—Constituents and secondary phases not being of a fibrous nature
- C04B2235/38—Non-oxide ceramic constituents or additives
- C04B2235/3852—Nitrides, e.g. oxynitrides, carbonitrides, oxycarbonitrides, lithium nitride, magnesium nitride
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
- C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
- C04B2235/30—Constituents and secondary phases not being of a fibrous nature
- C04B2235/42—Non metallic elements added as constituents or additives, e.g. sulfur, phosphor, selenium or tellurium
- C04B2235/422—Carbon
- C04B2235/427—Diamond
-
- E21B2010/561—
Definitions
- This disclosure relates to superhard constructions and methods of making such constructions, particularly but not exclusively to constructions comprising polycrystalline diamond (PCD) structures attached to a substrate, and tools comprising the same, particularly but not exclusively for use in rock degradation or drilling, or for boring into the earth.
- PCD polycrystalline diamond
- Polycrystalline superhard materials such as polycrystalline diamond (PCD) and polycrystalline cubic boron nitride (PCBN) may be used in a wide variety of tools for cutting, machining, drilling or degrading hard or abrasive materials such as rock, metal, ceramics, composites and wood-containing materials.
- tool inserts in the form of cutting elements comprising PCD material are widely used in drill bits for boring into the earth to extract oil or gas.
- the working life of superhard tool inserts may be limited by fracture of the superhard material, including by spalling and chipping, or by wear of the tool insert.
- Cutting elements such as those for use in rock drill bits or other cutting tools typically have a body in the form of a substrate which has an interface end/surface and an ultra hard material which forms a cutting layer bonded to the interface surface of the substrate by, for example, a sintering process.
- the substrate is generally formed of a tungsten carbide-cobalt alloy, sometimes referred to as cemented tungsten carbide and the ultra hard material layer is typically polycrystalline diamond (PCD), polycrystalline cubic boron nitride (PCBN) or a thermally stable product TSP material such as thermally stable polycrystalline diamond.
- PCD polycrystalline diamond
- PCBN polycrystalline cubic boron nitride
- TSP material such as thermally stable polycrystalline diamond
- PCD Polycrystalline diamond
- PCD material is an example of a superhard material (also called a superabrasive material) comprising a mass of substantially inter-grown diamond grains, forming a skeletal mass defining interstices between the diamond grains.
- PCD material typically comprises at least about 80 volume % of diamond and is conventionally made by subjecting an aggregated mass of diamond grains to an ultra-high pressure of greater than about 5 GPa, and temperature of at least about 1,200° C., for example.
- a material wholly or partly filling the interstices may be referred to as filler or binder material.
- PCD is typically formed in the presence of a sintering aid such as cobalt, which promotes the inter-growth of diamond grains.
- a sintering aid such as cobalt
- Suitable sintering aids for PCD are also commonly referred to as a solvent-catalyst material for diamond, owing to their function of dissolving, to some extent, the diamond and catalysing its re-precipitation.
- a solvent-catalyst for diamond is understood be a material that is capable of promoting the growth of diamond or the direct diamond-to-diamond inter-growth between diamond grains at a pressure and temperature condition at which diamond is thermodynamically stable. Consequently the interstices within the sintered PCD product may be wholly or partially filled with residual solvent-catalyst material.
- PCD is often formed on a cobalt-cemented tungsten carbide substrate, which provides a source of cobalt solvent-catalyst for the PCD.
- Materials that do not promote substantial coherent intergrowth between the diamond grains may themselves form strong bonds with diamond grains, but are not suitable solvent-catalysts for PCD sintering.
- Cemented tungsten carbide which may be used to form a suitable substrate is formed from carbide particles being dispersed in a cobalt matrix by mixing tungsten carbide particles/grains and cobalt together then heating to solidify.
- an ultra hard material layer such as PCD or PCBN
- diamond particles or grains or CBN grains are placed adjacent the cemented tungsten carbide body in a refractory metal enclosure such as a niobium enclosure and are subjected to high pressure and high temperature so that inter-grain bonding between the diamond grains or CBN grains occurs, forming a polycrystalline ultra hard diamond or polycrystalline CBN layer.
- the substrate may be fully cured prior to attachment to the ultra hard material layer whereas in other cases, the substrate may be green, that is, not fully cured. In the latter case, the substrate may fully cure during the HTHP sintering process.
- the substrate may be in powder form and may solidify during the sintering process used to sinter the ultra hard material layer.
- PCD polycrystalline diamond
- a superhard polycrystalline construction comprising a body of polycrystalline superhard material, the body of polycrystalline superhard material comprising a first region and a second region adjacent the first region, the second region being bonded to the first region by intergrowth of grains of superhard material; the first region comprising a plurality of alternating strata or layers, each stratum or layer having a thickness in the range of around 5 to 300 microns; the second region comprising a plurality of strata or layers, one or more strata or layers in the second region having a thickness greater than the thicknesses of the individual strata or layers in the first region, wherein:
- the alternating layers or strata in the first region comprise first layers or strata alternating with second layers or strata, the first layers or strata being in a state of residual compressive stress and the second layers or strata being in a state of residual tensile stress;
- one or more of the layers or strata in the first or second regions comprises:
- a superhard polycrystalline construction comprising a first region and a second region adjacent the first region, the second region being bonded to the first region by intergrowth of diamond grains; the first region comprising a plurality of alternating strata or layers, each layer or stratum in the first region having a thickness in the range of around 5 to 300 microns; one or more of the layers or strata in the first region and/or the second region comprises:
- a method of forming a superhard polycrystalline construction comprising:
- a tool comprising the superhard polycrystalline construction defined above, the tool being for cutting, milling, grinding, drilling, earth boring, rock drilling or other abrasive applications.
- the tool may comprise, for example, a drill bit for earth boring or rock drilling, a rotary fixed-cutter bit for use in the oil and gas drilling industry, or a rolling cone drill bit, a hole opening tool, an expandable tool, a reamer or other earth boring tools.
- a drill bit or a cutter or a component therefor comprising the superhard polycrystalline construction defined above.
- FIG. 1 is a schematic perspective view of an example PCD cutter element for a drill bit for boring into the earth;
- FIG. 2 shows a schematic cross-section view of an example of a portion of a PCD structure
- FIG. 3 shows a schematic longitudinal cross-section view of an example of a PCD element
- FIG. 4 shows a schematic longitudinal cross-section view of an example of a PCD element
- FIG. 5 shows a schematic perspective view of part of an example of a drill bit for boring into the earth
- FIG. 6A shows a schematic longitudinal cross-section view of an example of a pre-sinter assembly for a PCD element
- FIG. 6B shows a schematic longitudinal cross-section view of an example of a PCD element
- FIGS. 7A , 7 B, 7 C and 7 D show schematic cross-section views of parts of examples of PCD structures
- a “superhard material” is a material having a Vickers hardness of at least about 28 GPa.
- Diamond and cubic boron nitride (cBN) material are examples of superhard materials.
- a “superhard construction” means a construction comprising a body of polycrystalline superhard material.
- a substrate may be attached thereto or alternatively the body of polycrystalline material may be free-standing and unbacked.
- polycrystalline diamond is a type of polycrystalline superhard (PCS) material comprising a mass of diamond grains, a substantial portion of which are directly inter-bonded with each other and in which the content of diamond is at least about 80 volume percent of the material.
- interstices between the diamond grains may be at least partly filled with a binder material comprising a catalyst for diamond.
- interstices or “interstitial regions” are regions between the diamond grains of PCD material.
- interstices or interstitial regions may be substantially or partially filled with a material other than diamond, or they may be substantially empty.
- PCD material may comprise at least a region from which catalyst material has been removed from the interstices, leaving interstitial voids between the diamond grains.
- PCBN polycrystalline cubic boron nitride
- cBN cubic boron nitride
- PCBN is an example of a superhard material.
- a “catalyst material” for a superhard material is capable of promoting the growth or sintering of the superhard material.
- substrate as used herein means any substrate over which the ultra hard material layer is formed.
- a “substrate” as used herein may be a transition layer formed over another substrate.
- the terms “radial” and “circumferential” and like terms are not meant to limit the feature being described to a perfect circle.
- integrally formed regions or parts are produced contiguous with each other and are not separated by a different kind of material.
- the superhard construction 1 shown in the FIG. 1 may be suitable, for example, for use as a cutter insert for a drill bit for boring into the earth.
- a cutting element 1 includes a substrate 10 with a layer of ultra-hard material 12 formed on the substrate 10 .
- the substrate may be formed of a hard material such as cemented tungsten carbide.
- the ultra-hard material may be, for example, polycrystalline diamond (PCD), polycrystalline cubic boron nitride (PCBN), or a thermally stable product such as thermally stable PCD (TSP).
- the cutting element 1 may be mounted into a bit body such as a drag bit body (not shown).
- the exposed top surface of the ultra-hard material opposite the substrate forms the cutting face 14 , which is the surface which, along with its edge 16 , performs the cutting in use.
- the substrate 10 is an interface surface 18 that interfaces with the ultra-hard material layer 12 which is attached thereto at this interface surface.
- the substrate 10 is generally cylindrical and has a peripheral surface 20 and a peripheral top edge 22 .
- a PCD grade is a PCD material characterised in terms of the volume content and size of diamond grains, the volume content of interstitial regions between the diamond grains and composition of material that may be present within the interstitial regions.
- a grade of PCD material may be made by a process including providing an aggregate mass of diamond grains having a size distribution suitable for the grade, optionally introducing catalyst material or additive material into the aggregate mass, and subjecting the aggregated mass in the presence of a source of catalyst material for diamond to a pressure and temperature at which diamond is more thermodynamically stable than graphite and at which the catalyst material is molten.
- molten catalyst material may infiltrate from the source into the aggregated mass and is likely to promote direct intergrowth between the diamond grains in a process of sintering, to form a PCD structure.
- the aggregate mass may comprise loose diamond grains or diamond grains held together by a binder material and said diamond grains may be natural or synthesised diamond grains.
- Different PCD grades may have different microstructures and different mechanical properties, such as elastic (or Young's) modulus E, modulus of elasticity, transverse rupture strength (TRS), toughness (such as so-called K 1 C toughness), hardness, density and coefficient of thermal expansion (CTE).
- Different PCD grades may also perform differently in use. For example, the wear rate and fracture resistance of different PCD grades may be different.
- All of the PCD grades may comprise interstitial regions filled with material comprising cobalt metal, which is an example of catalyst material for diamond.
- the PCD structure 20 comprises one or more PCD grades.
- stress state refers to a compressive, unstressed or tensile stress state.
- Compressive and tensile stress states are understood to be opposite stress states from each other. In a cylindrical geometrical system, the stress states may be axial, radial or circumferential, or a net stress state.
- an example of a PCD structure 20 comprises at least two spaced-apart compressed regions 21 in compressive residual stress states and at least one tensioned region 22 in a tensile residual stress state.
- the tensioned region 22 is located between the compressed regions 21 and is joined to them.
- Variations in mechanical properties of the PCD material such as density, elastic modulus, hardness and coefficient of thermal expansion (CTE) may be selected to achieve the configuration of a tensioned region between two compressed regions.
- Such variations may be achieved by means of variations in content of diamond grains, content and type of filler material, size distribution or mean size of the PCD grains, and using different PCD grades either on their own or in diamond mixes comprising a mixture of PCD grades.
- an example of a PCD element 10 comprises a PCD structure 20 integrally joined to a cemented carbide support body 30 .
- the PCD structure 20 comprises several compressed regions 21 and several tensioned regions 22 in the form of alternating (or inter-leaved) strata or layers.
- the PCD element 10 may be substantially cylindrical in shape, with the PCD structure 20 located at a working end and defining a working surface 24 .
- the PCD structure 20 may be joined to the support body 30 at a non-planar interface 25 .
- the compressed and tensioned regions 21 , 22 have a thickness in the range from about 5 microns to about 200 or, in some embodiments, 300 microns and may be arranged substantially parallel to the working surface 24 of the PCD structure 20 .
- a substantially annular region 26 may be located around a non-planar feature 31 projecting from the support body 30 .
- an example of a PCD element 10 comprises a PCD structure 20 integrally joined to a cemented carbide support body 30 at a non-planar interface 25 opposite a working surface 24 of the PCD structure 20 .
- the PCD structure 20 may comprise about 10 to 20 alternating compressed and tensioned regions 21 , 22 in the form of extended strata or layers.
- a region 26 that, in this embodiment, does not contain strata may be located adjacent the interface 25 .
- the strata 21 , 22 may be curved or bowed and yet generally aligned with the interface 25 , and may intersect a side surface 27 of the PCD structure. Some of the strata may intersect the working surface 24 .
- the region 26 may be of a substantially greater thickness than the individual strata or layers 21 , 22 and, in some embodiments, the thickness of the region comprising the alternating layers 21 , 22 may be of a greater thickness than the thickness of the region 26 adjacent the cemented carbide support body 30 which forms a substrate for the PCD material.
- the region 26 adjacent the support body 30 may include multiple layers or strata (not shown) that are of substantially greater thickness than the individual layers or strata 21 , 22 , for example, the layers 21 , 22 may have a thickness in the range from about 5 to 200 microns, and the layers in the region 26 adjacent the support body 30 may have a thickness of greater than about 200 microns.
- the alternating strata, 21 , 22 may have a thickness or thicknesses in the range of from about 5 to 300 microns with the diamond material being formed of PCD with two or more different average diamond grain sizes, for example a mixture of two or more grades of PCD.
- strata 21 may be formed of an aggregated diamond mix having average diamond grain sizes A and B and strata 22 may also be formed of a diamond mix having average diamond grain sizes A and B but in a different ratio to that of strata 21 .
- the strata 21 may be formed of a diamond mix having average diamond grain sizes A and B and the strata 22 may be formed of a diamond mix having an average diamond grain size C.
- the region 26 adjacent the support body 30 may be formed of a single layer substantially thicker than the individual strata 21 , 22 , for example, greater than around 200 microns.
- the region 26 may be formed of multiple layers, individual layers or strata comprising diamond grains of average grain size A and B, and/or C as used to form the diamond mixes of the strata 21 , 22 or another material or diamond grain size may be used to form the layers in this region 26 adjacent the support body 30 .
- the diamond layers or strata 21 , 22 and/or strata formed in region 26 adjacent the support body 30 may include, for example, one or more of nanodiamond additions in the form of nanodiamond powder up to 20 wt %, salt systems, borides, metal carbides of Ti, V, Nb or any of the metals Pd or Ni.
- the strata 21 , 22 and/or strata formed in region 26 adjacent the support body 30 may lie in a plane substantially perpendicular to the plane through which the longitudinal axis of the diamond construction 10 extends.
- the strata may be planar, curved, bowed, domed or distorted, for example, as a result of being subjected to ultra-high pressure during sintering.
- the alternating strata 21 , 22 may be aligned at a predetermined angle to the plane through which the longitudinal axis of the diamond construction 10 extends to influence performance through crack propagation control.
- an example of a drill bit 60 for drilling into rock is shown as comprising example PCD elements 10 mounted onto a bit body 62 .
- the PCD elements 10 are arranged so that the respective PCD structures 20 project from the bit body 62 for cutting the rock.
- the grains of superhard material which are to form one or more layers or strata in any one or more of the regions may be for example diamond grains or particles.
- the feed comprises a mixture of a coarse fraction of diamond grains and a fine fraction of diamond grains which are to form one or more of the alternating layers or strata.
- the coarse fraction may have, for example, an average particle/grain size ranging from about 10 to 60 microns.
- average particle or grain size it is meant that the individual particles/grains have a range of sizes with the mean particle/grain size representing the “average”.
- the average particle/grain size of the fine fraction is less than the size of the coarse fraction, for example between around 1/10 to 6/10 of the size of the coarse fraction, and may, in some embodiments, range for example between about 0.1 to 20 microns.
- the weight ratio of the coarse diamond fraction to the fine diamond fraction ranges from about 50% to about 97% coarse diamond and the weight ratio of the fine diamond fraction may be from about 3% to about 50%. In other embodiments, the weight ratio of the coarse fraction to the fine fraction will range from about 70:30 to about 90:10.
- the weight ratio of the coarse fraction to the fine fraction may range for example from about 60:40 to about 80:20.
- the particle size distributions of the coarse and fine fractions do not overlap and in some embodiments the different size components of the compact are separated by an order of magnitude between the separate size fractions making up the multimodal distribution.
- the embodiments consists of at least a wide bi-modal size distribution between the coarse and fine fractions of superhard material, but some embodiments may include three or even four or more size modes which may, for example, be separated in size by an order of magnitude, for example, a blend of particle sizes whose average particle size is 20 microns, 2 microns, 200 nm and 20 nm.
- Sizing of diamond particles/grains into fine fraction, coarse fraction, or other sizes in between, may be through known processes such as jet-milling of larger diamond grains and the like.
- the diamond grains used to form the polycrystalline diamond material may be natural or synthetic.
- the binder catalyst/solvent may comprise cobalt or some other iron group elements, such as iron or nickel, or an alloy thereof.
- Carbides, nitrides, borides, and oxides of the metals of Groups IV-VI in the periodic table are other examples of non-diamond material that might be added to the sinter mix.
- the binder/catalyst/sintering aid may be Co.
- the cemented metal carbide substrate may be conventional in composition and, thus, may be include any of the Group IVB, VB, or VIB metals, which are pressed and sintered in the presence of a binder of cobalt, nickel or iron, or alloys thereof.
- the metal carbide is tungsten carbide.
- both the bodies of, for example, diamond and carbide material plus sintering aid/binder/catalyst are applied as powders and are sintered simultaneously in a single UHP/HT process.
- the alternating layers or strata of diamond, and mass of carbide to form the substrate are placed in an HP/HT reaction cell assembly and subjected to HP/HT processing.
- the HP/HT processing conditions selected are sufficient to effect intercrystalline bonding between adjacent grains of abrasive particles and, optionally, the joining of sintered particles to the cemented metal carbide support.
- the processing conditions generally involve the imposition for about 3 to 120 minutes of a temperature of at least about 1200 degrees C. and an ultra-high pressure of greater than about 5 GPa.
- the substrate may be pre-sintered in a separate process before being bonded together in the HP/HT press during sintering of the ultrahard polycrystalline material.
- both the substrate and a body of polycrystalline superhard material are pre-formed.
- the bimodal or multimodal feed of ultrahard grains/particles with optional carbonate binder-catalyst also in powdered form are mixed together, and the mixture is packed in alternating layers or strata into an appropriately shaped canister and is then subjected to extremely high pressure and temperature in a press.
- the pressure is at least 5 GPa and the temperature is at least around 1200 degrees C.
- the preformed body of polycrystalline superhard material is then placed in the appropriate position on the upper surface of the preform carbide substrate (incorporating a binder catalyst), and the assembly is located in a suitably shaped canister.
- the assembly is then subjected to high temperature and pressure in a press, the order of temperature and pressure being again, at least around 1200 degrees C. and 5 GPa respectively.
- the solvent/catalyst migrates from the substrate into the body of superhard material and acts as a binder-catalyst to effect intergrowth in the layer and also serves to bond the layer of polycrystalline superhard material to the substrate.
- the sintering process also serves to bond the body of superhard polycrystalline material to the substrate.
- a PCD element An further example method for making a PCD element is now described.
- Aggregate masses in the form of sheets containing diamond grains held together by a binder material may be provided.
- the sheets may be made by a method known in the art, such as by extrusion or tape casting methods, in which slurries comprising diamond grains having respective size distributions suitable for making the desired respective bimodal or multimodal PCD grades, and a binder material is spread onto a surface and allowed to dry.
- Other methods for making diamond-containing sheets may also be used, such as described in U.S. Pat. Nos. 5,766,394 and 6,446,740.
- Alternative methods for depositing diamond-bearing layers include spraying methods, such as thermal spraying.
- the binder material may comprise a water-based organic binder such as methyl cellulose or polyethylene glycol (PEG) and different sheets comprising diamond grains having different size distributions, diamond content or additives may be provided.
- PEG polyethylene glycol
- the sheets may also contain catalyst material for diamond, such as cobalt, and/or additives for inhibiting abnormal growth of the diamond grains or enhancing the properties of the PCD material.
- the sheets may contain about 0.5 weight percent to about 5 weight percent of vanadium carbide, chromium carbide or tungsten carbide.
- each of the sets may comprise about 10 to 20 discs.
- a support body comprising cemented carbide in which the cement or binder material comprises a catalyst material for diamond, such as cobalt, may be provided.
- the support body may have a non-planar end or a substantially planar proximate end on which the PCD structure is to be formed and which forms the interface.
- a non-planar shape of the end may be configured to reduce undesirable residual stress between the PCD structure and the support body.
- a cup may be provided for use in assembling the diamond-containing sheets onto the support body.
- the first and second sets of discs may be stacked into the bottom of the cup in alternating order. In one version of the method, a layer of substantially loose diamond grains may be packed onto the uppermost of the discs.
- the support body may then be inserted into the cup with the proximate end going in first and pushed against the substantially loose diamond grains, causing them to move slightly and position themselves according to the shape of the non-planar end of the support body to form a pre-sinter assembly.
- the pre-sinter assembly may be placed into a capsule for an ultra-high pressure press and subjected to an ultra-high pressure of at least about 5.5 GPa and a high temperature of at least about 1,300 degrees centigrade to sinter the diamond grains and form a PCD element comprising a PCD structure integrally joined to the support body.
- the binder material within the support body melts and infiltrates the strata of diamond grains. The presence of the molten catalyst material from the support body is likely to promote the sintering of the diamond grains by intergrowth with each other to form an integral, stratified PCD structure.
- the aggregate masses may comprise substantially loose diamond grains, or diamond grains held together by a binder material.
- the aggregate masses of multimodal grains may be in the form of granules, discs, wafers or sheets, and may contain catalyst material for diamond and/or additives for reducing abnormal diamond grain growth, for example, or the aggregated mass may be substantially free of catalyst material or additives.
- the aggregate masses may be assembled onto a cemented carbide support body.
- the pre-sinter assembly may be subjected to a pressure of at least about 6 GPa, at least about 6.5 GPa, at least about 7 GPa or even at least about 7.5 GPa.
- an example of a pre-sinter assembly 40 for making a PCD element may comprise a support body 30 , a region 46 comprising diamond grains packed against a non-planar end of the support body 30 , and a plurality of alternating diamond-containing aggregate masses in the general form of discs or wafers 41 , 42 stacked on the region 46 .
- the aggregate masses may be in the form of loose diamond grains or granules.
- the pre-sinter assembly may be heated to remove the binder material comprised in the stacked discs.
- an example of a PCD element 10 comprises a PCD structure 20 comprising a plurality of alternating strata 21 , 22 formed of different respective multimodal grades of PCD material, and a portion 26 that does not comprise strata.
- the portion 26 may be cooperatively formed according to the shape of the non-planar end of the support body 30 to which it has integrally bonded during the treatment at the ultra-high pressure.
- the alternating strata 21 , 22 of different grades of PCD or mixes of diamond grain sizes or grades are bonded together by direct diamond-to-diamond intergrowth to form an integral, solid and stratified PCD structure 20 .
- the shapes of the PCD strata 21 , 22 may be curved, bowed or distorted in some way as a result of being subjected to the ultra-high pressure.
- the aggregate masses may be arranged in the pre-sinter assembly to achieve various other configurations of strata within the PCD structure, taking into account possible distortion of the arrangement during the ultra-high pressure and high temperature treatment.
- the strata 21 , 22 may comprise different respective PCD grades as a result of the different mean diamond grain sizes of the strata. Different amounts of catalyst material may infiltrate into the different types of discs 41 , 42 comprised in the pre-sinter assembly since they comprise diamond grains having different mean sizes, and consequently different sizes of spaces between the diamond grains.
- the corresponding alternating PCD strata 21 , 22 may thus comprise different, alternating amounts of catalyst material for diamond.
- the content of the filler material in terms of volume percent within the tensioned region may be greater than that within each of the compressed regions.
- the compressed strata may comprise diamond grains having mean size greater than the mean size of the diamond grains of the tensioned strata.
- the alternating strata containing different amounts of metal catalyst material may contract at different rates. This may be because metal contracts much more substantially than diamond does as it cools from a high temperature. This differential rate of contraction may cause adjacent strata to pull against each other, thus inducing opposing stresses in them.
- the PCD element 10 described with reference to FIG. 6B may be processed by grinding to modify its shape to form a PCD element substantially as described with reference to FIG. 4 . This may involve removing part of some of the curved strata to form a substantially planar working surface and a substantially cylindrical side surface. Catalyst material may be removed from a region of the PCD structure adjacent the working surface or the side surface or both the working surface and the side surface. This may be done by treating the PCD structure with acid to leach out catalyst material from between the diamond grains, or by other methods such as electrochemical methods.
- a thermally stable region which may be substantially porous, extending a depth of at least about 50 microns or at least about 100 microns from a surface of the PCD structure, may thus be provided.
- the substantially porous region may comprise at most 2 weight percent of catalyst material.
- alternating layers or strata with different grain sizes may controllably give a different structure when acid leaching is applied to the PCD construction 10 , especially for the embodiments in which the binder does not contain V and/or Ti.
- Such a structure may be created as a result of different residual tungsten in each layer during HCl acid leaching.
- the rate of leaching is likely to be different in each layer (unless HF-containing acid is used) and this may enable preferential leaching especially at the edges of the PCD material. This may be more pronounced for layers thicker than 120 microns. This is unlikely to occur if HF acid leaching were applied to the PCD material. The reason for this is that, in such a process, the HCl acid removes Co and leaves behind tungsten, whilst HF acid leaching would remove everything in the binder composition.
- an example variant of a PCD structure 20 comprises at least three substantially planar strata 21 , 22 strata arranged in an alternating configuration substantially parallel to a working surface 24 of the PCD structure 20 and intersecting a side surface 27 of the PCD structure.
- an example variant of a PCD structure 20 comprises at least three strata 21 , 22 strata arranged in an alternating configuration, the strata having a curved or bowed shape, with at least part of the strata inclined away from a working surface 24 and cutting edge 28 of the PCD structure.
- an example variant of a PCD structure 20 comprises at least three strata 21 , 22 strata arranged in an alternating configuration, at least part of the strata inclined away from a working surface 24 of the PCD structure and extending generally towards a cutting edge 28 of the PCD structure.
- an example variant of a PCD structure 20 comprises at least three strata 21 , 22 strata arranged in an alternating configuration, at least part of some of the strata being substantially aligned with a working surface 24 of the PCD structure and at least part of some of the strata generally aligned with a side surface 27 of the PCD structure.
- Strata may be generally annular of part annular and substantially concentric with a substantially cylindrical side surface 27 of the PCD structure 20 .
- the PCD structure may have a surface region proximate a working surface, the region comprising PCD material having a Young's modulus of at most about 1,050 MPa, or at most about 1,000 MPa.
- the surface region may comprise thermally stable PCD material.
- PCD structures may have at least 3, at least 5, at least 7, at least 10 or even at least 15 compressed regions, with tensioned regions located between them.
- each stratum or layer may have a thickness of at least about 5 microns, in others at least about 30 microns, in others at least about 100 microns, or in others at least about 200 microns. In some embodiments, each stratum or layer may have a thickness of at most about 300 microns or at most about 500 microns. In some example embodiments, each stratum or layer may have a thickness of at least about 0.05 percent, at least about 0.5 percent, at least about 1 percent or at least about 2 percent of a thickness of the PCD structure measured from a point on a working surface at one end to a point on an opposing surface. In some embodiments, each stratum or layer may have a thickness of at most about 5 percent of the thickness of the PCD structure.
- residual stress state refers to the stress state of a body or part of a body in the absence of an externally-applied loading force.
- the residual stress state of a PCD structure, including a layer structure may be measured by means of a strain gauge and progressively removing material layer by layer.
- at least one compressed region may have a compressive residual stress of at least about 50 MPa, at least about 100 MPa, at least about 200 MPa, at least about 400 MPa or even at least about 600 MPa.
- the difference between the magnitude of the residual stress of adjacent strata may be at least about 50 MPa, at least about 100 MPa, at least about 200 MPa, at least about 400 MPa, at least about 600 MPa, at least about 800 MPa or even at least about 1,000 MPa.
- at least two successive compressed regions or tensioned regions may have different residual stresses.
- the PCD structure may comprise at least three compressed or tensioned regions each having a different residual compressive stress, the regions arranged in increasing or decreasing order of compressive or tensile stress magnitude, respectively.
- each of the regions may have a mean toughness of at most 16 MPa ⁇ m1 ⁇ 2. In some embodiments, each of the regions may have a mean hardness of at least about 50 GPa, or at least about 60 GPa. Each of the regions may have a mean Young's modulus of at least about 900 MPa, at least about 950 MPa, at least about 1,000 or even at least about 1,050 MPa.
- transverse rupture strength is measured by subjecting a specimen in the form of a bar having width W and thickness T to a load applied at three positions, two on one side of the specimen and one on the opposite side, and increasing the load at a loading rate until the specimen fractures at a load P.
- the TRS is then calculated based on the load P, dimensions of the specimen and the span L, which is the distance between the two load positions on one side.
- Such a measurement may also be referred to as a three-point bending test and is described by D. Munz and T. Fett in “Ceramics, mechanical properties, failure behaviour, materials selection” (1999, Springer, Berlin).
- the TRS corresponding to a particular grade of PCD material is measured measuring the TRS of a specimen of PCD consisting of that grade.
- One way of influencing the magnitude of the stress that a region may experience is by selecting the relative thicknesses of adjacent regions. For example, by selecting the thickness of a tensioned region to be greater than that of the adjacent compressive regions is likely to reduce the magnitude of tensile stress within the tensioned region.
- the residual stress states of the regions may vary with temperature.
- the temperature of the PCD structure may differ substantially between points proximate a cutting edge and points remote from the cutting edge.
- the temperature proximate the cutting edge may reach several hundred degrees centigrade. If the temperature exceeds about 750 degrees centigrade, diamond material in the presence of catalyst material such as cobalt is likely to convert to graphite material, which is not desired. Therefore, in some uses, the alternating stress states in adjacent regions as described herein should be considered at a temperature of up to about 750 degrees centigrade.
- the K1C toughness of a PCD disc is measured by means of a diametral compression test, which is described by Lammer (“Mechanical properties of polycrystalline diamonds”, Materials Science and Technology, volume 4, 1988, p. 23.) and Miess (Miess, D. and Rai, G., “Fracture toughness and thermal resistances of polycrystalline diamond compacts”, Materials Science and Engineering, 1996, volume A209, number 1 to 2, pp. 270-276).
- Young's modulus is a type of elastic modulus and is a measure of the uni-axial strain in response to a uni-axial stress, within the range of stress for which the material behaves elastically.
- C L and C T are respectively the measured longitudinal and transverse speeds of sound through it and ⁇ is the density of the material.
- the longitudinal and transverse speeds of sound may be measured using ultrasonic waves, as is well known in the art.
- the mean Young's modulus may be estimated by means of one of three formulas, namely the harmonic, geometric and rule of mixtures formulas as follows:
- the expression “formed of” means “consists of, apart from possible minor or non-substantial deviations in composition or microstructure”.
- the hardness of cemented tungsten carbide substrate may be enhanced by subjecting the substrate to an ultra-high pressure and high temperature, particularly at a pressure and temperature at which diamond is thermodynamically stable.
- the magnitude of the enhancement of the hardness may depend on the pressure and temperature conditions.
- the hardness enhancement may increase the higher the pressure. Whilst not wishing to be bound by a particular theory, this is considered to be related to the Co drift from the substrate into the PCD during press sintering, as the extent of the hardness increase is directly dependent on the decrease of Co content in the substrate.
- solvent/catalyst material may be included or introduced into the aggregated mass of diamond grains from a source of the material other than the cemented carbide substrate.
- the solvent/catalyst material may comprise cobalt that infiltrates from the substrate in to the aggregated mass of diamond grains just prior to and during the sintering step at an ultra-high pressure.
- an alternative source may need to be provided in order to ensure good sintering of the aggregated mass to form PCD.
- Solvent/catalyst for diamond may be introduced into the aggregated mass of diamond grains by various methods, including blending solvent/catalyst material in powder form with the diamond grains, depositing solvent/catalyst material onto surfaces of the diamond grains, or infiltrating solvent/catalyst material into the aggregated mass from a source of the material other than the substrate, either prior to the sintering step or as part of the sintering step.
- Methods of depositing solvent/catalyst for diamond, such as cobalt, onto surfaces of diamond grains are well known in the art, and include chemical vapour deposition (CVD), physical vapour deposition (PVD), sputter coating, electrochemical methods, electroless coating methods and atomic layer deposition (ALD). It will be appreciated that the advantages and disadvantages of each depend on the nature of the sintering aid material and coating structure to be deposited, and on characteristics of the grain.
- cobalt may be deposited onto surfaces of the diamond grains by first depositing a pre-cursor material and then converting the precursor material to a material that comprises elemental metallic cobalt.
- cobalt carbonate may be deposited on the diamond grain surfaces using the following reaction:
- the deposition of the carbonate or other precursor for cobalt or other solvent/catalyst for diamond may be achieved by means of a method described in PCT patent publication number WO/2006/032982.
- the cobalt carbonate may then be converted into cobalt and water, for example, by means of pyrolysis reactions such as the following:
- cobalt powder or precursor to cobalt such as cobalt carbonate
- cobalt carbonate may be blended with the diamond grains.
- a precursor to a solvent/catalyst such as cobalt
- the cemented carbide substrate may be formed of tungsten carbide particles bonded together by the binder material, the binder material comprising an alloy of Co, Ni and Cr.
- the tungsten carbide particles may form at least 70 weight percent and at most 95 weight percent of the substrate.
- the binder material may comprise between about 10 to 50 wt. % Ni, between about 0.1 to 10 wt. % Cr, and the remainder weight percent comprises Co.
- the size distribution of the tungsten carbide particles in the cemented carbide substrate ion some embodiments has the following characteristics:
- the binder additionally comprises between about 2 to 20 wt. % tungsten and between about 0.1 to 2 wt. % carbon
- a layer of the substrate adjacent to the interface with the body of polycrystalline diamond material may have a thickness of, for example, around 100 microns and may comprise tungsten carbide grains, and a binder phase.
- This layer may be characterised by the following elemental composition measured by means of Energy-Dispersive X-Ray Microanalysis (EDX):
- the elemental composition includes between about 0.5 to 2.0 wt % cobalt, between about 0.05 to 0.5 wt. % nickel and between about 0.05 to 0.2 wt. % chromium, the remainder is tungsten and carbon.
- the layer of substrate may further comprise free carbon.
- the “mean free path” (MFP) of a composite material such as cemented carbide is a measure of the mean distance between the aggregate carbide grains cemented within the binder material.
- the mean free path characteristic of a cemented carbide material may be measured using a micrograph of a polished section of the material. For example, the micrograph may have a magnification of about 1000 ⁇ .
- the MFP may be determined by measuring the distance between each intersection of a line and a grain boundary on a uniform grid.
- the matrix line segments, Lm are summed and the grain line segments, Lg, are summed.
- the mean matrix segment length using both axes is the “mean free path”. Mixtures of multiple distributions of tungsten carbide particle sizes may result in a wide distribution of MFP values for the same matrix content. This is explained in more detail below.
- the substrate comprises Co, Ni and Cr.
- the binder material for the substrate may include at least about 0.1 weight percent to at most about 5 weight percent one or more of V, Ta, Ti, Mo, Zr, Nb and Hf in solid solution.
- the catalysing material may be removed from a region of the polycrystalline layer adjacent an exposed surface thereof. Generally, that surface will be on a side of the polycrystalline layer opposite to the substrate and will provide a working surface for the polycrystalline diamond layer. Removal of the catalysing material may be carried out using methods known in the art such as electrolytic etching, and acid leaching and evaporation techniques. It has been found that multimodal distributions of some embodiments may assist in achieving a very high degree of diamond intergrowth while still maintaining sufficient open porosity to enable efficient leaching.
- a quantity of sub-micron cobalt powder sufficient to obtain 2 mass % in the final diamond mixture for forming one of the types of strata or layers was initially de-agglomerated in a methanol slurry in a ball mill with WC milling media for 1 hour.
- a fine fraction of diamond powder with an average grain size of 2 ⁇ m was then added to the slurry in an amount to obtain 10 mass % in the final mixture.
- Additional milling media was introduced and further methanol was added to obtain suitable slurry; and this was milled for a further hour.
- a coarse fraction of diamond, with an average grain size of approximately 20 ⁇ m was then added in an amount to obtain 88 mass % in the final mixture for forming one of the types of strata or layers.
- the slurry was again supplemented with further methanol and milling media, and then milled for a further 2 hours. The slurry was removed from the ball mill and dried to obtain the diamond powder mixture.
- the diamond powder mixture was then placed in alternating layers or strata, alternating with another diamond mixture which may or may not be formed of a multimodal mixture of diamond grades into a suitable HpHT vessel, adjacent to a tungsten carbide substrate and sintered at a pressure of around 6.8 GPa and a temperature of about 1500° C.
- a quantity of sub-micron cobalt powder sufficient to obtain 2.4 mass % in the final diamond mixture for forming one of the types of strata or layers was initially de-agglomerated in a methanol slurry in a ball mill with WC milling media for 1 hour.
- a fine fraction of diamond powder with an average grain size of 2 ⁇ m was then added to the slurry in an amount to obtain 29.3 mass % in the final mixture for forming one of the types of strata or layers.
- Additional milling media was introduced and further methanol was added to obtain a suitable slurry; and this was milled for a further hour.
- a coarse fraction of diamond, with an average grain size of approximately 20 ⁇ m was then added in an amount to obtain 68.3 mass % in the final mixture for forming one of the types of strata or layers.
- the slurry was again supplemented with further methanol and milling media, and then milled for a further 2 hours.
- the slurry was removed from the ball mill and dried to obtain the diamond powder mixture for forming one of the types of strata or layers.
- first and second sheets each containing diamond grains having a different mean size and held together by an organic binder were made by the tape casting method. This method involved providing respective slurries of diamond grains suspended in liquid binder, casting the slurries into sheet form and allowing them to dry to form self-supportable diamond-containing sheets.
- the diamond-containing wafers were placed into the cup, alternately stacked on top of each other with discs from the first and second sets inter-leaved.
- a layer of loose diamond grains to form a second region in which no alternating layers or strata were present having a mean size in the range from about 18 microns to about 25 microns was placed into the upturned cup, on top of the uppermost of the wafers, and the support body was inserted into the cup, with the non-planar end pushed against the layer.
- the diamond content of the sintered diamond structure is greater than 90 vol % and the coarsest fraction of the distribution may, in some embodiments, be greater than 60 weight % or greater than weight 70%.
- individual diamond particles/grains are, to a large extent, bonded to adjacent particles/grains through diamond bridges or necks.
- the individual diamond particles/grains retain their identity, or generally have different orientations.
- the average grain/particle size of these individual diamond grains/particles may be determined using image analysis techniques. Images are collected on a scanning electron microscope and are analysed using standard image analysis techniques. From these images, it is possible to extract a representative diamond particle/grain size distribution.
- the body of polycrystalline diamond material will be produced and bonded to the cemented carbide substrate in a HPHT process.
- the binder phase and diamond particles in each layer or strata to be arranged such that the binder phase is distributed homogeneously and is of a fine scale.
- the PCD element was processed by grinding and lapping to form a cutter element having a substantially planar working surface and cylindrical side. A cross-section through the PCD structure was then examined micro-structurally by means of a scanning electron microscope (SEM).
- SEM scanning electron microscope
- the homogeneity or uniformity of the sintered structure is defined by conducting a statistical evaluation of a large number of collected images.
- the distribution of the binder phase which is easily distinguishable from that of the diamond phase using electron microscopy, can then be measured in a method similar to that disclosed in EP 0974566.
- This method allows a statistical evaluation of the average thicknesses of the binder phase along several arbitrarily drawn lines through the microstructure.
- This binder thickness measurement is also referred to as the “mean free path” by those skilled in the art.
- the material which has the smaller average thickness will tend to be more homogenous, as this implies a “finer scale” distribution of the binder in the layers or strata of the diamond phase.
- the smaller the standard deviation of this measurement the more homogenous is the structure.
- a large standard deviation implies that the binder thickness varies widely over the microstructure, i.e. that the structure is not even, but contains widely dissimilar structure types.
- binder and diamond mean free path measurements were obtained for various samples in the manner set out below.
- dimensions of mean free path within the body of PCD material refer to the dimensions as measured on a surface of, or a section through, a body comprising PCD material and no stereographic correction has been applied.
- the measurements are made by means of image analysis carried out on a polished surface, and a Saltykov correction has not been applied in the data stated herein.
- samples In measuring the mean value of a quantity or other statistical parameter measured by means of image analysis, several images of different parts of a surface or section (hereinafter referred to as samples) are used to enhance the reliability and accuracy of the statistics.
- the number of images used to measure a given quantity or parameter may be, for example between 10 to 30. If the analysed sample is uniform, which is the case for PCD, depending on magnification, 10 to 20 images may be considered to represent that sample sufficiently well.
- the resolution of the images needs to be sufficiently high for the inter-grain and inter-phase boundaries to be clearly made out and, for the measurements stated herein an image area of 1280 by 960 pixels was used.
- Images used for the image analysis were obtained by means of scanning electron micrographs (SEM) taken using a backscattered electron signal.
- SEM scanning electron micrographs
- the back-scatter mode was chosen so as to provide high contrast based on different atomic numbers and to reduce sensitivity to surface damage (as compared with the secondary electron imaging mode).
- Q1 is typically referred to as the first quartile (also called the lower quartile) and is the number below which lies the 25 percent of the bottom data.
- Q3 is typically referred to as the third quartile (also called the upper quartile) has 75 percent of the data below it and the top 25 percent of the data above it.
- alpha> 0.50 and beta ⁇ 0.60
- a PCD element comprising a PCD structure bonded to a cemented carbide support body can be provided.
- the PCD element may be substantially cylindrical and have a substantially planar working surface, or a generally domed, pointed, rounded conical or frusto-conical working surface.
- the PCD element may be for a rotary shear (or drag) bit for boring into the earth, for a percussion drill bit or for a pick for mining or asphalt degradation.
Landscapes
- Engineering & Computer Science (AREA)
- Chemical & Material Sciences (AREA)
- Ceramic Engineering (AREA)
- Geology (AREA)
- Life Sciences & Earth Sciences (AREA)
- Mining & Mineral Resources (AREA)
- Mechanical Engineering (AREA)
- Materials Engineering (AREA)
- Organic Chemistry (AREA)
- Manufacturing & Machinery (AREA)
- Crystallography & Structural Chemistry (AREA)
- Fluid Mechanics (AREA)
- General Life Sciences & Earth Sciences (AREA)
- Geochemistry & Mineralogy (AREA)
- Physics & Mathematics (AREA)
- Environmental & Geological Engineering (AREA)
- Structural Engineering (AREA)
- Inorganic Chemistry (AREA)
- Metallurgy (AREA)
- Chemical Kinetics & Catalysis (AREA)
- General Chemical & Material Sciences (AREA)
- Earth Drilling (AREA)
- Investigation Of Foundation Soil And Reinforcement Of Foundation Soil By Compacting Or Drainage (AREA)
- Drilling Tools (AREA)
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US14/407,958 US20150165591A1 (en) | 2012-06-15 | 2013-06-14 | Superhard constructions and methods of making same |
Applications Claiming Priority (5)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US201261660542P | 2012-06-15 | 2012-06-15 | |
GB1210658.9 | 2012-06-15 | ||
GBGB1210658.9A GB201210658D0 (en) | 2012-06-15 | 2012-06-15 | Superhard constructions & methods of making same |
PCT/EP2013/062429 WO2013186382A1 (en) | 2012-06-15 | 2013-06-14 | Superhard constructions & methods of making same |
US14/407,958 US20150165591A1 (en) | 2012-06-15 | 2013-06-14 | Superhard constructions and methods of making same |
Publications (1)
Publication Number | Publication Date |
---|---|
US20150165591A1 true US20150165591A1 (en) | 2015-06-18 |
Family
ID=46640995
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US14/407,958 Abandoned US20150165591A1 (en) | 2012-06-15 | 2013-06-14 | Superhard constructions and methods of making same |
Country Status (4)
Country | Link |
---|---|
US (1) | US20150165591A1 (zh) |
CN (1) | CN104507891A (zh) |
GB (2) | GB201210658D0 (zh) |
WO (1) | WO2013186382A1 (zh) |
Cited By (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2017106388A1 (en) * | 2015-12-14 | 2017-06-22 | Smith International, Inc. | Direct casting of ultrahard insert in bit body |
GB2569895A (en) * | 2017-12-31 | 2019-07-03 | Element Six Uk Ltd | Polycrystalline diamond constructions |
WO2020056436A1 (de) * | 2018-09-19 | 2020-03-26 | Österreichische Akademie der Wissenschaften | Verfahren zur herstellung eines metall-diamant-verbundwerkstoffes für schmuck oder uhren |
Families Citing this family (9)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
GB201215565D0 (en) * | 2012-08-31 | 2012-10-17 | Element Six Abrasives Sa | Polycrystalline diamond construction and method for making same |
GB201305871D0 (en) * | 2013-03-31 | 2013-05-15 | Element Six Abrasives Sa | Superhard constructions & methods of making same |
RU2630159C2 (ru) * | 2015-10-22 | 2017-09-05 | Федеральное государственное автономное образовательное учреждение высшего образования "Национальный исследовательский технологический университет "МИСиС" | Композиционный материал с металлической матрицей и упрочняющими наночастицами и способ его изготовления |
GB201600001D0 (en) * | 2016-01-01 | 2016-02-17 | Element Six Uk Ltd | Superhard constructions and methods of making same |
GB201622458D0 (en) * | 2016-12-31 | 2017-02-15 | Element Six Ltd | Superhard constructions & methods of making same |
US20190071932A1 (en) * | 2017-09-06 | 2019-03-07 | Varel International Ind., L.L.C. | Superhard cutter having shielded substrate |
CN111664978B (zh) * | 2020-05-28 | 2021-12-07 | 哈尔滨工业大学 | 一种球面异形件的残余应力表征方法 |
CN113232380B (zh) * | 2021-04-30 | 2023-03-28 | 咸阳职业技术学院 | 一种高强高韧层状互通结构钢结硬质合金及其制备方法 |
CN114905420A (zh) * | 2022-04-18 | 2022-08-16 | 郑州磨料磨具磨削研究所有限公司 | 一种多元跨尺度叠层复合金刚石砂轮及成型方法 |
Citations (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3850614A (en) * | 1970-05-08 | 1974-11-26 | Carmet Co | Production of tungsten and carbide powder |
WO2012152874A2 (en) * | 2011-05-10 | 2012-11-15 | Element Six Abrasives S.A. | Polycrystalline diamond structure |
Family Cites Families (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CA2585439C (en) * | 2004-10-29 | 2013-01-08 | Element Six (Production) (Pty) Ltd | Cubic boron nitride compact |
US8419814B2 (en) * | 2006-03-29 | 2013-04-16 | Antionette Can | Polycrystalline abrasive compacts |
GB0909350D0 (en) * | 2009-06-01 | 2009-07-15 | Element Six Production Pty Ltd | Ploycrystalline diamond material and method of making same |
GB0913304D0 (en) * | 2009-07-31 | 2009-09-02 | Element Six Ltd | Polycrystalline diamond composite compact elements and tools incorporating same |
WO2011041693A2 (en) * | 2009-10-02 | 2011-04-07 | Baker Hughes Incorporated | Cutting elements configured to generate shear lips during use in cutting, earth-boring tools including such cutting elements, and methods of forming and using such cutting elements and earth-boring tools |
GB0921393D0 (en) * | 2009-12-07 | 2010-01-20 | Element Six Production Pty Ltd | A polycrystalline superhard structure, method for making same and tools comprising same |
-
2012
- 2012-06-15 GB GBGB1210658.9A patent/GB201210658D0/en not_active Ceased
-
2013
- 2013-06-14 GB GB1310668.7A patent/GB2504839A/en not_active Withdrawn
- 2013-06-14 CN CN201380040879.6A patent/CN104507891A/zh active Pending
- 2013-06-14 WO PCT/EP2013/062429 patent/WO2013186382A1/en active Application Filing
- 2013-06-14 US US14/407,958 patent/US20150165591A1/en not_active Abandoned
Patent Citations (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3850614A (en) * | 1970-05-08 | 1974-11-26 | Carmet Co | Production of tungsten and carbide powder |
WO2012152874A2 (en) * | 2011-05-10 | 2012-11-15 | Element Six Abrasives S.A. | Polycrystalline diamond structure |
Cited By (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2017106388A1 (en) * | 2015-12-14 | 2017-06-22 | Smith International, Inc. | Direct casting of ultrahard insert in bit body |
US10871037B2 (en) | 2015-12-14 | 2020-12-22 | Smith International, Inc. | Mechanical locking of ovoid cutting element with carbide matrix |
US11021913B2 (en) | 2015-12-14 | 2021-06-01 | Schlumberger Technology Corporation | Direct casting of ultrahard insert in bit body |
US11492852B2 (en) | 2015-12-14 | 2022-11-08 | Schlumberger Technology Corporation | Mechanical locking of cutting element with carbide matrix |
GB2569895A (en) * | 2017-12-31 | 2019-07-03 | Element Six Uk Ltd | Polycrystalline diamond constructions |
WO2019129716A1 (en) * | 2017-12-31 | 2019-07-04 | Element Six (Uk) Limited | Polycrystalline diamond constructions |
WO2020056436A1 (de) * | 2018-09-19 | 2020-03-26 | Österreichische Akademie der Wissenschaften | Verfahren zur herstellung eines metall-diamant-verbundwerkstoffes für schmuck oder uhren |
Also Published As
Publication number | Publication date |
---|---|
GB2504839A (en) | 2014-02-12 |
CN104507891A (zh) | 2015-04-08 |
WO2013186382A1 (en) | 2013-12-19 |
GB201310668D0 (en) | 2013-07-31 |
GB201210658D0 (en) | 2012-08-01 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US20150165591A1 (en) | Superhard constructions and methods of making same | |
US20170067294A1 (en) | Superhard constructions and methods of making same | |
US20210269313A1 (en) | Polycrystalline diamond structure | |
US10737327B2 (en) | Super hard constructions and methods of making same | |
US20230135812A1 (en) | Superhard constructions and methods of making same | |
US20150298292A1 (en) | A polycrystalline super hard construction and a method for making same | |
US10221629B2 (en) | Polycrystalline super hard construction and a method for making same | |
US20150284827A1 (en) | Polycrystalline super hard construction and a method for making same | |
WO2014161818A2 (en) | Superhard constructions & methods of making same | |
US20190184524A1 (en) | Polycrystalline diamond construction & method of making | |
US20150165590A1 (en) | Superhard constructions and methods of making same | |
US20190330118A1 (en) | Super hard constructions & methods of making same | |
US20150259987A1 (en) | Polycrystalline super hard construction and a method for making same | |
US20190344350A1 (en) | Superhard constructions & methods of making same | |
US20210316362A1 (en) | Superhard constructions & methods of making same | |
US20170355017A1 (en) | Super hard components and powder metallurgy methods of making the same |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: ELEMENT SIX ABRASIVES S.A., LUXEMBOURG Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:ELEMENT SIX (PRODUCTION)(PTY) LTD;REEL/FRAME:044871/0891 Effective date: 20120817 |
|
AS | Assignment |
Owner name: ELEMENT SIX (PRODUCTION)(PTY) LTD, SOUTH AFRICA Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:CAN, NEDRET;SITHEBE, HUMPHREY SAMKELO LUNGISANI;REEL/FRAME:044403/0536 Effective date: 20120827 |
|
STCV | Information on status: appeal procedure |
Free format text: NOTICE OF APPEAL FILED |
|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION |