US20130340966A1 - Blade outer air seal hybrid casting core - Google Patents
Blade outer air seal hybrid casting core Download PDFInfo
- Publication number
- US20130340966A1 US20130340966A1 US13/529,041 US201213529041A US2013340966A1 US 20130340966 A1 US20130340966 A1 US 20130340966A1 US 201213529041 A US201213529041 A US 201213529041A US 2013340966 A1 US2013340966 A1 US 2013340966A1
- Authority
- US
- United States
- Prior art keywords
- core
- sacrificial
- distinct parts
- boas
- ceramic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A hybrid sacrificial core for forming an impingement space and an internal cooling passageway network separate from the impingement space of a part may comprise a ceramic core having a first surface portion for forming the impingement space, and a refractory metal core that forms a plurality of passages of the internal cooling passageway network.
Description
- This invention was made with government support under F33615-03-D-2354-0009 awarded by The United States Air Force. The government has certain rights in the invention.
- The invention relates to gas turbine engines. More particularly, the invention relates to casting of cooled shrouds or blade outer air seals (BOAS).
- BOAS segments may be internally cooled by bleed air. For example, there may be an array of cooling passageways within the BOAS. Cooling air may be fed into the passageways from the outboard (OD) side of the BOAS (e.g., via one or more inlet ports). The cooling air may exit through the outlet ports.
- The BOAS segments may be cast via an investment casting process. In an exemplary casting process, a casting core is used to form the passageway legs and other features. The core has legs corresponding to the passageway legs that extend between portions of the core. The core may be placed in a die. Wax may be molded in the die over the core legs to form a pattern. The pattern may be shelled (e.g., a stuccoing process to form a ceramic shell). The wax may be removed from the shell. Metal may be cast in the shell over the core. The shell and core may be destructively removed. After core removal, the core legs leave the passageway legs in the casting. The as-cast passageway legs are open at both circumferential ends of the raw BOAS casting. At least some of the end openings are closed via plug welding, braze pins, welded-on coverplate or other means. Air inlets to the passageway legs may be drilled from the OD side of the casting.
- In one embodiment, a hybrid sacrificial core for forming an impingement space and an internal cooling passageway network separate from the impingement space of a part may comprise a ceramic core having a first surface portion for forming the impingement space, and a refractory metal core that forms a plurality of passages of the internal cooling passageway network.
- In another embodiment, the method comprises fabricating a refractory metal core to define a plurality of passages of an internal cooling passageway network, fabricating a ceramic core to define an impingement cavity, molding a sacrificial material over the refractory metal core and ceramic core to form a hybrid casting core, and casting a component containing the hybrid core.
- In yet another embodiment, a sacrificial core forms a cooling network in a part that includes a network of closed cooling passages and an open channel on at least one face that contains at least one terminating aperture for at least one cooling passage. The core comprises a refractory metal core with a plurality of extensions connected together to form the cooling passages, and a protrusion connected to at least one of the extensions to form the channel.
-
FIG. 1 is a cross-sectional view of a turbine section of a gas turbine engine. -
FIG. 2 is a top perspective view of a BOAS. -
FIG. 3 is a bottom perspective view of the BOAS. -
FIG. 4 is a cross-sectional view of the BOAS. -
FIG. 5 is a perspective view of a hybrid casting core for the BOAS. -
FIG. 6 is a perspective view of the BOAS with an enlarged view of one side. - Referring to
FIG. 1 , a section of agas turbine engine 10 includes a blade outer air seal 12 (hereinafter “BOAS”) disposed between a plurality of circumferentially disposedrotor blades 14 of arotor stage 16 and an annular outer engine case 18 (hereinafter “engine case”). In one embodiment, theBOAS 12 includes a plurality of circumferentially extending segments and is adapted to limit air leakage betweenblade tips 20 and theengine case 18 that are evenly spaced about an engine centerline C/L. -
FIG. 2 is a top perspective view ofBOAS 12, andFIG. 3 is a bottom perspective view of theBOAS 12.FIG. 4 is a cross-section ofBOAS 12. BOAS 12 has amain body portion 22 having a leading/upstream/forward end 24 and a trailing/downstream/aft end 26. The body has first and second circumferential ends ormatefaces ID face 32 and anOD face 34. To mount BOAS 12 to environmental structure of gas turbine engine 10 (FIG. 1 ), BOAS 12 has a plurality of mounting hooks includingforward mounting hooks 42 having a forwardly-projecting distal portion recessed aft of theforward end 24, andaft hooks 44. Cooling air enters center cavity viaaperture 63 onOD face 34 betweenforward mounting hooks 42 andaft hooks 44 and exits center cavity viaaperture 62 onID face 32. - A circumferential ring array of a plurality of
BOAS 12 may encircle an associated blade stage ofgas turbine engine 10. The assembled ID faces 32 thus locally bound an outboard extreme of the core flowpath for gases exiting the combustor. BOAS 12 may have features for interlocking the array. Exemplary features include finger and shiplap joints. - BOAS 12 is air-cooled. Bleed air may be directed to a chamber (
FIG. 1 ) immediately outboard of theface 34. The bleed air may be directed throughports cooling passageway network 60. The exemplary network includes a plurality of passages from the interior chamber ofBOAS 12 to a plurality of outlets. Exemplary outlets may include outlets along thecircumferential ends exemplary BOAS 12, some outlets areports 54 are formed along the firstcircumferential end 28 and some outlets areports 50 formed along the secondcircumferential end 30. As is discussed in further detail below, adjacent ports may be interconnected by interconnecting passageways. - In operation, exits from the
ID face 32 are fed by passages from internalcooling passageway network 60. In addition,apertures 62 extend from central cavity toID face 32, and apertures 63 feed central cavity with bleed air fromOD face 34. In some embodiments, center cavity may contain animpingement plate 65 to regulate or meter the flow of bleed air from the chamber above. Internalcooling passageway network 60 provides convection cooling of the perimeter ofBOAS 12.Apertures 62 allow for film cooling ofID face 32 ofBOAS 12. - BOAS 12 is a cast engine component. The casting system includes the base shape formed from a metal or metal alloy such as a nickel based superalloy.
FIG. 5 is a perspective view of ahybrid casting core 70 for BOAS 12. Hybrid casting core is comprised of refractory metal core (hereinafter “RMC”) 72 andceramic core 90.RMC core 72 may be formed by any suitable metallic material known in the art. -
RMC 72 contains leadingedge core 74, trailingedge core 76, andside cores side cores BOAS 12 based on the geometry ofBOAS 12.Side cores axial portions 80 andradial portions 82.Radial portions 82 contain angled legs that allow for the formation of passages that extend throughBOAS 12 to connect airflow to the generallyaxial outlet ports axial portion 80 is utilized to create a recessedchannel 58 inmatefaces 28 and 30 (seeFIG. 6 ).Casting channel 58 rather than machining the same structure desensitizes flow through adjacent passages and apertures to machining burrs. The design also simplifies the casting process through the use ofRMC 72, which produceschannel 58 without additional concerns of a fully enclosed passage. - Similar to the construction of
side cores edge core 74 contains both flataxial portions 84 and radialangled portions 86. The angles between theaxial portion 84 andradial portions 86 may vary, and typically are designed to be either 45°, 60°, or 90° with respect to one another. Leadingedge core 74, trailingedge core 76, andside cores -
Ceramic core 90 may be comprised of twoseparate core pieces Core pieces portion Ceramic core 90 is utilized to create central cavity inBOAS 12. Upon the part being cast,apertures -
RMC 72 may be bonded toceramic core 90, such as by adhesives. The exemplary ceramic adhesive may initially be formed of a slurry comprising ceramic powder and organic or inorganic binders. With a binder combination, the organic binder(s) (e.g., acrylics, epoxies, plastics, and the like) could allow for improved room temperature strength of a joint while the inorganic binder(s) (e.g., colloidal silica and the like) may convert to ceramic(s) at a moderate temperature (e.g., 500C). Adhesives may be used to secure RMCs to pre-formed green cores or may be used to secure RMCs to fired ceramic cores. Adhesive may be used in combination with further mechanical interlocking features. - An
exemplary RMC 72 may easily be formed from sheetstock. RMCs with various features may be cast or machined, or assembled from multiple sheet pieces or folded from a single sheet piece. Exemplary RMC materials are refractory alloys of Mo, Nb, Ta, and W. These are commercially available in standard shapes, such as sheets, which can be cut as needed to form cores using processes such as laser cutting, shearing, piercing and photo etching. The cut shapes can be deformed by bending and twisting. The standard shapes can be corrugated or dimpled to produce passages which induce turbulent airflow. Holes can be punched into sheet to produce posts or turning vanes in passageways. - Refractory metals are generally prone to oxidize at elevated temperatures and are also somewhat soluble in molten superalloys. Accordingly, the RMCs may advantageously have a protective coating to prevent oxidation and erosion by molten metal. These may include coatings of one or more thin continuous adherent ceramic layers. Suitable coating materials include silica, alumina, zirconia, chromia, mullite and hafnia. Preferably, the coefficient of thermal expansion (CTE) of the refractory metal and the coating are similar. Coatings may be applied by CVD, PVD, electrophoresis, and sol gel techniques. Individual layers may typically be 0.1 to 1 mil thick. Metallic layers of Pt, other noble metals, Cr, and Al may be applied to the RMCs for oxidation protection, in combination with a ceramic coating for protection from molten metal erosion.
- Refractory metal alloys and intermetallics such as Mo alloys and MoSi2, respectively, which form protective SiO2 layers may also be used for RMCs. Such materials are expected to allow good adherence of a non-reactive oxide such as alumina. Silica, though an oxide, is very reactive in the presence of nickel based alloys and is advantageously coated with a thin layer of other non-reactive oxide. However, by the same token, silica readily diffusion bonds with other oxides such as alumina forming mullite.
- After the casting process is complete, the shell and core assembly are removed. The shell is external and can be removed by mechanical means to break the ceramic away from the casting, followed as necessary by chemical means usually involving immersion in a caustic solution to remove to core assembly. Typically, ceramic cores are removed using caustic solutions, often under conditions of elevated temperatures and pressures in an autoclave. The same caustic solution core removal techniques may be employed to remove the present ceramic cores. The RMCs may be removed from superalloy castings by acid treatments. For example, to remove Mo cores from a nickel superalloy, one may use an exemplary 40 parts HNO3, 30 parts H2SO4, with balance H2O at temperatures of 60-100° C. For refractory metal cores of relatively large cross-sectional dimensions thermal oxidation can be used to remove Mo which forms a volatile oxide. In Mo cores of small cross-sections, thermal oxidation may be less effective.
-
Hybrid casting core 70 allows for an exemplary method for investment casting. Other methods are possible, including a variety of prior art methods and yet-developed methods.Hybrid casting core 70 assembly is overmolded with an easily sacrificed material such as a natural or synthetic wax (e.g., via placing the assembly in a mold and molding the wax around it). There may be multiple such assemblies involved in a given mold. - The overmolded hybrid core assembly (or group of assemblies) forms a casting pattern with an exterior shape largely corresponding to the exterior shape of the part to be cast. The pattern may then be assembled to a shelling fixture (e.g., via wax welding between end plates of the fixture). The pattern may then be shelled (e.g., via one or more stages of slurry dipping, slurry spraying, or the like). After the shell is built up, it may be dried. The drying provides the shell with at least sufficient strength or other physical integrity properties to permit subsequent processing. For example, the shell containing the invested core assembly may be disassembled fully or partially from the shelling fixture and then transferred to a dewaxer (e.g., a steam autoclave). In the dewaxer, a steam dewax process removes a major portion of the wax leaving the core assembly secured within the shell. The shell and core assembly will largely form the ultimate mold. However, the dewax process typically leaves a wax or byproduct hydrocarbon residue on the shell interior and core assembly.
- After the dewax, the shell is transferred to a furnace (e.g., containing air or other oxidizing atmosphere) in which it is heated to strengthen the shell and remove any remaining wax residue (e.g., by vaporization) and/or converting hydrocarbon residue to carbon. Oxygen in the atmosphere reacts with the carbon to form carbon dioxide. Removal of the carbon is advantageous to reduce or eliminate the formation of detrimental carbides in the metal casting. Removing carbon offers the additional advantage of reducing the potential for clogging the vacuum pumps used in subsequent stages of operation.
- The mold may be removed from the atmospheric furnace, allowed to cool, and inspected. The mold may be transferred to a casting furnace (e.g., placed atop a chill plate in the furnace). The casting furnace may be pumped down to vacuum or charged with a non-oxidizing atmosphere (e.g., inert gas) to prevent oxidation of the casting alloy. The casting furnace is heated to preheat the mold. This preheating serves two purposes: to further harden and strengthen the shell; and to preheat the shell for the introduction of molten alloy to prevent thermal shock and premature solidification of the alloy.
- After preheating and while still under vacuum conditions, the molten alloy is poured into the mold and the mold is allowed to cool to solidify the alloy (e.g., after withdrawal from the furnace hot zone). After solidification, the vacuum may be broken and the chilled mold removed from the casting furnace. The shell may be removed in a deshelling process (e.g., mechanical breaking of the shell).
- The core assembly is removed in a decoring process to leave a cast article (e.g., a metallic precursor of the ultimate part). The cast article may be machined, chemically and/or thermally treated and coated to form the ultimate part. Some or all of any machining or chemical or thermal treatment may be performed before the decoring.
- The design of
BOAS 12 may involve providing increased cooling to the BOAS. In an exemplary design situation, shifting of the inlets provides the resulting flows with shorter flowpath length than the length (circumferential) of the baseline passageway. In some situations the baseline passages may have been flow-limited due to the pressure loss from the friction along the relatively larger flowpath length. The ratio of pressures just before to just after the outlet determines the flow rate (and thus the cooling capability). For example, a broader design of the engine may increaseBOAS 12 heat load and thus increase cooling requirements. Thus, reducing the pressure drop by shortening the flowpath length may provide such increased cooling.RMC core 72 provides an alternative to circumferentially shortening the BOAS (which shortening leads to more segments per engine and thus more cost and leakage) or further complicating the passageway configuration. Alternatively, the design may increase the BOAS circumferential length and decrease part count/cost and air loss. - There may be one or more of several advantages to using the
exemplary RMC core 72 withceramic core 90. The combination of microcircuit and impingement/film technologies allow for a greater use of design configurations to obtain proper cooling of the component. Impingement provided throughceramic core 90 with film cooling fromaperture 62 control the thermal gradient of the component and provides adequate thermal mechanical fatigue life forBOAS 12.RMC 72 creates microcircuit passages, which are arranged at the perimeter ofBOAS 12 to provide better cooling to those regions most susceptible to oxidation.Hybrid casting core 70 isolates the center region from secondary distress by mitigating the risk of burn through progressing from the edges. - Use of RMC core may avoid or reduce the need for plug welding. Use of
RMC core 72 for internalcooling passageway network 60 relative to a ceramic core may permit the casting of finer passageways. Where the finer passageways are not needed, i.e., central cavity,ceramic core 90 may be utilized. For example, core thickness and passageway height may be reduced relative to those of a baseline ceramic core and its cast passageways by utilizingRMC core 72. Exemplary RMC thicknesses are typically 0.5-11.0 mm, and more narrowly, less than 1.25 mm.RMC core 72 may also readily be provided with features (e.g., stamped/embossed or laser etched recesses) for casting internal trip strips or other surface enhancements. Meanwhile,ceramic core 90 is cheaper to create, and the size and location ofapertures - The following are non-exclusive descriptions of possible embodiments of the present invention.
- A hybrid sacrificial core for forming an impingement space and an internal cooling passageway network separate from the impingement space of a part may comprise a ceramic core having a first surface portion for forming the impingement space, and a refractory metal core that forms a plurality of passages of the internal cooling passageway network.
- The core of the preceding paragraph can optionally include, additionally and/or alternatively any one or more of the following features, configurations, and/or additional components:
- the ceramic core is comprised of at least two distinct parts;
- the two distinct parts are of the same geometry;
- the refractory metal core is comprised of four distinct parts;
- refractory metal cores may be minor images of one another;
- the refractory metal core is comprised of a leading edge core, a trailing edge core, and two side cores;
- the four distinct parts are joined together;
- at least one of the distinct parts contains an axial portion and a radial portion;
- the four distinct parts are arranged at ninety degrees with respect to each adjacent part, and a generally rectangular space is contained among the four distinct parts;
- the ceramic core is placed in the generally rectangular space;
- the ceramic core is attached to the refractory metal core.
- A method comprises fabricating a refractory metal core to define a plurality of passages of an internal cooling passageway network, fabricating a ceramic core to define an impingement cavity, molding a sacrificial material over the refractory metal core and ceramic core to form a hybrid casting core, and casting a component containing the hybrid core.
- The assembly of the preceding paragraph can optionally include, additionally and/or alternatively any one or more of the following features, configurations, steps, and/or additional components:
- shelling the sacrificial material;
- removing the shell;
- the component being cast is a blade outer air seal;
- drilling a plurality of apertures on an inner diameter face to the impingement cavity;
- drilling a plurality of apertures on an outer diameter face to the impingement cavity;
- the impingement cavity is centrally located within the component, and internal cooling passageway network is peripherally located within the component.
- A sacrificial core forms a cooling network in a part that includes a network of closed cooling passages and an open channel on at least one face that contains at least one terminating aperture for at least one cooling passage. The core comprises a refractory metal core with a plurality of extensions connected together to form the cooling passages, and a protrusion connected to at least one of the extensions to form the channel.
- The core of the preceding paragraph can optionally include, additionally and/or alternatively any one or more of the following features, configurations, and/or additional components:
- the refractory metal core is comprised of four distinct parts, each distinct part containing a plurality of extensions;
- the refractory metal core is comprised of a leading edge core, a trailing edge core, and two side cores, wherein at least one of the side cores contains the protrusion connected to at least one of the extensions;
- the four distinct parts are joined together;
- at least one of the distinct parts contains an axial portion and a radial portion.
- While the invention has been described with reference to an exemplary embodiment(s), it will be understood by those skilled in the art that various changes may be made and equivalents may be substituted for elements thereof without departing from the scope of the invention. In addition, many modifications may be made to adapt a particular situation or material to the teachings of the invention without departing from the essential scope thereof. Therefore, it is intended that the invention not be limited to the particular embodiment(s) disclosed, but that the invention will include all embodiments falling within the scope of the appended claims.
Claims (12)
1. A hybrid sacrificial core for forming an impingement space and an internal cooling passageway network separate from the impingement space of a part, the core comprising:
a ceramic core having a first surface portion for forming the impingement space, wherein the ceramic core is comprised of at least two separate distinct parts; and
a refractory metal core that forms a plurality of passages of the internal cooling passageway network.
2. (canceled)
3. The sacrificial core of claim 1 , wherein the two separate distinct parts are of the same geometry.
4. The sacrificial core of claim 1 , wherein the refractory metal core is comprised of four distinct parts.
5. The sacrificial core of claim 4 , wherein the refractory metal core is comprised of a leading edge core, a trailing edge core, and two side cores.
6. The sacrificial core of claim 4 wherein the four distinct parts are joined together.
7. The sacrificial core of claim 4 wherein at least one of the distinct parts contains an axial portion and a radial portion.
8. The sacrificial core of claim 4 , wherein the four distinct parts are arranged at ninety degrees with respect to each adjacent part, and wherein a generally rectangular space is contained among the four distinct parts.
9. The sacrificial core of claim 4 , wherein at least two of the leading edge core, trailing edge core, and two side cores are minor images of one another.
10. The sacrificial core of claim 1 , wherein the ceramic core is attached to the refractory metal core.
11.-20. (canceled)
21. The sacrificial core of claim 3 wherein the two separate distinct parts each contain an axial portion and a radial portion.