US20110309410A1 - Reduced dark current photodetector - Google Patents
Reduced dark current photodetector Download PDFInfo
- Publication number
- US20110309410A1 US20110309410A1 US13/167,992 US201113167992A US2011309410A1 US 20110309410 A1 US20110309410 A1 US 20110309410A1 US 201113167992 A US201113167992 A US 201113167992A US 2011309410 A1 US2011309410 A1 US 2011309410A1
- Authority
- US
- United States
- Prior art keywords
- photo
- layer
- absorbing layer
- photo absorbing
- barrier layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A photo-detector comprising: a photo absorbing layer comprising an n-doped semiconductor exhibiting a valence band energy level; a barrier layer, a first side of the barrier layer adjacent a first side of the photo absorbing layer, the barrier layer exhibiting a valence band energy level substantially equal to the valence band energy level of the doped semiconductor of the photo absorbing layer; and a contact area comprising a doped semiconductor, the contact area being adjacent a second side of the barrier layer opposing the first side, the barrier layer exhibiting a thickness and a conductance band gap sufficient to prevent tunneling of majority carriers from the photo absorbing layer to the contact area and block the flow of thermalized majority carriers from the photo absorbing layer to the contact area. Alternatively, a p-doped semiconductor is utilized, and conductance band energy levels of the barrier and photo absorbing layers are equalized.
Description
- This application is a continuation of U.S. patent application Ser. No. 12/656,739 filed Feb. 16, 2010, the entire contents of which is incorporated herein by reference.
- The invention relates generally to the field of semiconductor based photo-detectors and in particular to a photo-detector exhibiting a barrier region between an active semiconductor region and a contact semiconductor region.
- Photo-detectors are used in a wide variety of applications including imaging. A specific type of photo-detector sensitive to the infra-red wavelengths of light is also known as an infra-red detector. Infra-red covers a broad range of wavelengths, and many materials are only sensitive to a certain range of wavelengths. As a result, the infra-red band is further divided into sub-bands such as near infra-red defined conventionally as 0.75-1.4 μm; short wavelength infra-red defined conventionally as 1.3-3 μm; mid wavelength infra-red defined conventionally as 3-8 μm; and far infra-red defined conventionally as 15-1,000 μm. Infra-red in the range of 5 μm to 8 μm is not well transmitted in the atmosphere and thus for many infra-red detection applications mid-wavelength infra-red is referred to as 3-5 μm.
- Infra-red detectors are used in a wide variety of applications, and in particular in the military field where they are used as thermal detectors in night vision equipment, air borne systems, naval systems and missile systems. Highly accurate thermal detectors have been produced using InSb and HgCdTe p-n junction diodes, however these thermal detectors require cooling to cryogenic temperatures of around 77 K which is costly. The cryogenic temperatures primarily are used to reduce the dark current generated in the p-n junction diode by among other effects Shockley Reed Hall (SRH) generation.
- There are three main contributions to the dark current, denoted as Idark, of photodiodes based on narrow band gap semiconductors. The fluctuations of the dark current components are a major factor in the noise that limits the device performance. These components are:
-
- a) a generation current associated with the Shockley-Reed-Hall (SRH) process in the depletion region, Isrh;
- b) a diffusion current associated with auger or radiative processes in the extrinsic area, Idiffand
- c) a surface current associated with the surface states in the junction, Isurf. The surface current depends primarily on the passivation process done for the device.
Thus, Idark can be expressed as:
-
I dark =I srh +I diff +I surf Equation 1 - The SRH generation process is very efficient in the depletion region of photodiodes where the mid-gap traps are highly activated. It is the main source of the dark current in photodiodes operable for mid-wavelength infrared at temperatures below 200K. The current associated with this source is:
-
- where ni is the intrinsic concentration of the semiconductor, Wdep is the depletion width (typically in the range of 1 μm), and τsrh is the SRH lifetime of minority carriers in the extrinsic area. The SRH lifetime of minority carriers in the extrinsic area depends on the quality of the material, i.e. the trap concentration, and is typically in the range of ˜1 μsec in low doped material (˜1016 cm−3). The dependence of SRH current on ni produces an activation energy of Eg/2 (ni˜exp(−Eg/2/kT)), because the source of this generation process is through mid-gap traps. A secondary source of dark current in photodiodes is thermal generation in the neutral regions and diffusion to the other side of the junction. This thermal generation current depends on the auger or radiative process in this area, and is expressed as:
-
- where τdiff is the lifetime, and in an n-type material exhibiting a doping concentration, denoted Nd, of ˜1-2·1016 cm−3 is in the range of ˜0.5 μsec, depending only slightly on temperature. L is the width of the neutral region of the device or the diffusion length of minority carriers (the smaller of the two) and pn is the hole concentration in the active n type semiconductor in equilibrium and it equal to ni 2/Nd. The activation energy of the diffusion current is Eg, (ni 2˜exp(−Eg/kT)) as the process involves band to band excitation.
- Additionally, p-n junction diodes, and particularly those produced for thermal imaging require a passivation layer in the metallurgic junction between the p and n layers. Unfortunately this is often difficult to achieve and significantly adds to the cost of production.
- There is thus a long felt need for a photo-detector having reduced dark noise. Preferably the photo-detector would be sensitive to the mid wavelength infra-red band and not require expensive passivation in production. Further preferably the photo-detector would be operable at significantly higher temperatures than 77K.
- Accordingly, it is a principal object of the present invention to overcome the disadvantages of prior art photo-detectors, and in particular mid wavelength infra-red detectors. This is provided in the present invention by a photo-detector sensitive to a target waveband comprising a photo absorbing layer, preferably exhibiting a thickness on the order of the optical absorption length. In an exemplary embodiment the photo absorbing layer is deposited to a thickness of between one and two times the optical absorption length. A contact layer is further provided, and a barrier layer is interposed between the photo absorbing layer and the contact layer. The barrier layer exhibits a thickness sufficient to prevent tunneling of majority carriers from the photo absorbing layer to the contact layer, and a band gap barrier sufficient to block the flow of thermalized majority carriers from the photo absorbing layer to the contact layer. The barrier layer does not significantly block minority carriers.
- An infra-red detector in accordance with the principle of the invention can be produced using either an n-doped photo absorbing layer or a p-doped photo absorbing layer, in which the barrier layer is designed to have no offset for minority carriers and a band gap barrier for majority carriers. Current in the detector is thus almost exclusively by minority carriers. In particular, for an n-doped photo absorbing layer the junction between the barrier layer and the absorbing layer is such that there is substantially zero valence band offset, i.e. the band gap difference appears almost exclusively in the conduction band offset. For a p-doped photo absorbing layer the junction between the barrier layer and the absorbing layer is such that there is substantially zero conduction band offset, i.e. the band gap difference appears almost exclusively in the valence band offset.
- Advantageously the photo-detector of the subject invention does not exhibit a depletion layer, and thus the dark current is significantly reduced. Furthermore, in an exemplary embodiment passivation is not required as the barrier layer further functions to achieve passivation.
- The invention provides for a photo-detector comprising: a photo absorbing layer comprising an n-doped semiconductor exhibiting a valence band energy level and a conducting band energy level; a barrier layer, a first side of the barrier layer adjacent a first side of the photo absorbing layer, the barrier layer exhibiting a valence band energy level substantially equal to the valence band energy level of the photo absorbing layer and a conduction band energy level exhibiting a significant band gap in relation to the conduction band of the photo absorbing layer; and a contact area comprising a doped semiconductor, the contact area being adjacent a second side of the barrier layer opposing the first side, the barrier layer exhibiting a thickness, the thickness and the band gap being sufficient to prevent tunneling of majority carriers from the photo absorbing layer to the contact area and block the flow of thermalized majority carriers from the photo absorbing layer to the contact area.
- In one embodiment the barrier layer comprises an undoped semiconductor. In another embodiment the contact area is n-doped. In a further embodiment, the contact area exhibits a valence band energy level substantially equal to the valence band energy level of the n-doped semiconductor of the photo absorbing layer.
- In one embodiment the contact area is p-doped. In one further embodiment the contact area exhibits a valence band energy level greater than the valence band energy level of the n-doped semiconductor of the photo absorbing layer. In another further embodiment the barrier layer comprises an undoped semiconductor.
- In one embodiment the photo absorbing layer is operable to generate minority carriers in the presence of light energy exhibiting a wavelength of 3-5 microns. In another embodiment the photo-detector further comprises a substrate exhibiting a first side adjacent a second side of the photo absorbing layer, the second side of the photo absorbing layer opposing the first side of the photo absorbing layer, the substrate exhibiting a second side in contact with a metal layer. Preferably, the photo-detector further comprises an additional metal layer in contact with the contact area.
- In one embodiment the barrier layer comprises one of AlSb, AlAsSb, GaAlAsSb, AlPSb, AlGaPSb and HgZnTe. In a further embodiment the photo absorbing layer is constituted of one of n-doped InAs, n-doped InAsSb, n-doped InGaAs, n-doped Type II super lattice InAs/InGaSb and n-doped HgCdTe. In a yet further embodiment the contact area is constituted of one of InAs, InGaAs, InAsSb, Type II super lattice InAs/InGaSb, HgCdTe and GaSb. In a yet further embodiment the contact area and the photo absorbing layer exhibit substantially identical compositions.
- In one embodiment the photo absorbing layer and the contact area arc constituted of n-doped HgCdTe and the barrier layer is constituted of HgZnTe, and in another embodiment the photo absorbing layer and the contact layer are constituted of n-doped type II super lattice InAs/InGaSb and the barrier layer is constituted of AlGaAsSb. In another embodiment the photo absorbing layer is constituted of n-doped InAsSb, the barrier layer is constituted of AlGaAsSb and the contact layer is constituted of p-doped GaSb. In one embodiment the photo absorbing layer exhibits a thickness on the order of the optical absorption length.
- The invention independently provides for a photo-detector comprising: a photo absorbing layer comprising a p-doped semiconductor exhibiting a conduction band energy level and a valence band energy level; a barrier layer, a first side of the barrier layer adjacent a first side of the photo absorbing layer, the barrier layer exhibiting a conduction band energy level substantially equal to the conduction band energy level of the photo absorbing layer and a valence band energy level exhibiting a significant band gap in relation to the valence band of the photo absorbing layer; and a contact area comprising a doped semiconductor, the contact area adjacent a second side of the barrier layer opposing the first side, the barrier layer exhibiting a thickness, the thickness and the band gap being sufficient to prevent tunneling of majority carriers from the photo absorbing layer to the contact area and to block the flow of thermalized majority carriers from the photo absorbing layer to the contact area.
- In one embodiment the barrier layer comprises an undoped semiconductor. In another embodiment the contact area is p-doped. In one further embodiment the contact area exhibits a conduction band energy level substantially equal to the conduction band energy level of the p-doped semiconductor of the photo absorbing layer.
- In one embodiment the contact area is n-doped. In one further embodiment the contact area exhibits a conduction band energy level less than the conduction band energy level of the p-doped semiconductor of the photo absorbing layer. In another further embodiment the barrier layer comprises an undoped semiconductor.
- In one embodiment the photo absorbing layer is operable to generate minority carriers in the presence of light energy exhibiting a wavelength of 3-5 microns. In another embodiment the photo-detector further comprises a substrate exhibiting a first side adjacent a second side of the photo absorbing layer, the second side of the photo absorbing layer opposing the first side of the photo absorbing layer, the substrate exhibiting a second side in contact with a metal layer. In a further embodiment the photo-detector further comprises a metal layer in contact with the contact area.
- In one embodiment the barrier layer comprises one of AlSb, AlAsSb, GaAlAsSb, AlPSb, AlGaPSb, InAlAs, InAlAsSb, and HgZnTe. In one further embodiment the photo absorbing layer is constituted of one of p-doped InAs, p-doped InAsSb, p-doped InGaAs, p-doped Type II super lattice InAs/InGaSb and p-doped HgCdTe. In one yet further embodiment the contact area is constituted of one of InAs, InGaAs, InAsSb, Type II super lattice InAs/InGaSb, HgCdTe and GaSb. In one yet further embodiment the contact area and the photo absorbing layer exhibit substantially identical compositions.
- The invention independently provides for a method of producing a photo-detector, the method comprising: providing a substrate; depositing on the substrate a photo absorbing layer comprising a doped semiconductor exhibiting an energy level associated with non-conducting majority carriers; depositing on the deposited photo absorbing layer a barrier layer exhibiting a thickness, an energy level associated with minority carriers of the photo absorbing layer substantially equal to the energy level of the photo absorbing layer and a band gap associated with majority carriers of the photo absorbing layer; and depositing on the deposited barrier layer a contact layer comprising a doped semiconductor, the thickness and the band gap of the barrier layer being sufficient to prevent tunneling of majority carriers from the photo absorbing layer to the contact layer and to block the flow of thermalized majority carriers from the photo absorbing layer to the contact layer.
- In one embodiment the method further comprises selectively etching the deposited contact layer to define a plurality of contact areas. In another embodiment at least one of depositing the photo absorbing layer, depositing the barrier layer and depositing the contact layer is done via one of molecular beam epitaxy, metal organic chemical vapor deposition, metal organic phase epitaxy and liquid phase epitaxy.
- Additional features and advantages of the invention will become apparent from the following drawings and description.
- For a better understanding of the invention and to show how the same may be carried into effect, reference will now be made, purely by way of example, to the accompanying drawings in which like numerals designate corresponding elements or sections throughout.
- With specific reference now to the drawings in detail, it is stressed that the particulars shown are by way of example and for purposes of illustrative discussion of the preferred embodiments of the present invention only, and are presented in the cause of providing what is believed to be the most useful and readily understood description of the principles and conceptual aspects of the invention. In this regard, no attempt is made to show structural details of the invention in more detail than is necessary for a fundamental understanding of the invention, the description taken with the drawings making apparent to those skilled in the art how the several forms of the invention may be embodied in practice. In the accompanying drawings:
-
FIG. 1A illustrates a high level schematic view of the layers of a single photo-detector according to an embodiment of the principle of the invention; -
FIG. 1B illustrates a side view of a multi-pixel photo-detector according to an embodiment of the principle of the invention; -
FIG. 1C illustrates a top level view of the multi-pixel photo-detector ofFIG. 1B according to a principle of the invention; -
FIG. 2A illustrates the energy band levels of an embodiment of the structure ofFIG. 1 according to the principle of the invention in which the photo absorbing layer is n-doped and the contact layer is n-doped; -
FIG. 2B illustrates the energy band levels of an embodiment of the structure ofFIG. 1 according to the principle of the invention in which the photo absorbing layer is p-doped and the contact layer is p-doped; -
FIG. 3A illustrates the energy band levels of an embodiment of the structure ofFIG. 1 according to the principle of the invention in which the photo absorbing layer is n-doped and the contact layer is p-doped; -
FIG. 3B illustrates the energy band levels of an embodiment of the structure ofFIG. 1 according to the principle of the invention in which the photo absorbing layer is p-doped and the contact layer is n-doped; and -
FIG. 4 illustrates a high level flow chart of the process of manufacture of the multi pixel photo-detector ofFIGS. 1B-1C . - The present embodiments enable a photo-detector sensitive to a target waveband comprising a photo absorbing layer, preferably exhibiting a thickness on the order of an optical absorption length of the target waveband. In an exemplary embodiment the photo absorbing layer is deposited to a thickness of between one and two times the optical absorption length. A contact layer is further provided, and a barrier layer is interposed between the photo absorbing layer and the contact layer. The barrier layer exhibits a thickness sufficient to prevent tunneling of majority carriers from the photo absorbing layer to the contact layer, and a band gap barrier sufficient to block the flow of thermalized majority carriers from the photo absorbing layer to the contact layer. The barrier layer does not significantly block minority carriers.
- An infra-red detector in accordance with the principle of the invention can be produced using either an n-doped photo absorbing layer or a p-doped photo absorbing layer, in which the barrier layer is designed to have substantially no offset for minority carriers and a band gap barrier for majority carriers. Current in the detector is thus almost exclusively by minority carriers. In particular, for an n-doped photo absorbing layer the junction between the barrier layer and the absorbing layer is such that there is substantially zero valence band offset, i.e. the band gap difference appears almost exclusively in the conduction band offset. For a p-doped photo absorbing layer the junction between the barrier layer and the absorbing layer is such that there is substantially zero conduction band offset, i.e. the band gap difference appears almost exclusively in the valence band offset.
- Advantageously the photo-detector of the subject invention does not exhibit a depletion layer, and thus the dark current is significantly reduced. Furthermore, in an exemplary embodiment passivation is not required as the barrier layer further functions to achieve passivation.
- Before explaining at least one embodiment of the invention in detail, it is to be understood that the invention is not limited in its application to the details of construction and the arrangement of the components set forth in the following description or illustrated in the drawings. The invention is applicable to other embodiments or of being practiced or carried out in various ways. Also, it is to be understood that the phraseology and terminology employed herein is for the purpose of description and should not be regarded as limiting.
-
FIG. 1A illustrates a high level schematic view of the layers of a photo-detector 10 according to an embodiment of the principle of the invention comprising asubstrate 20, aphoto absorbing layer 30, abarrier layer 40, acontact layer 50, ametal layer 60 and ametal layer 65.Substrate 20 is provided as a base for deposition and has deposited on oneface metal layer 60 for connection to electronic circuitry. In an exemplaryembodiment metal layer 60 is constituted of gold.Photo absorbing layer 30 is deposited on the second face ofsubstrate 20 opposing the first face.Photo absorbing layer 30 comprises a doped semiconductor responsive to photons of the object wavelength, and preferably is deposited to a thickness on the order of an optical absorption length. In one embodimentphoto absorbing layer 30 is deposited to a thickness of between one and two times the optical absorption length. In an exemplary embodimentphoto absorbing layer 30 comprises one of n-doped InAs; n-doped InAsSb; n-doped InGaAs; n-doped type II super lattice of the type InAs/InGaSb; and n-doped HgCdTe. In an alternativeembodiment absorbing layer 30 comprises one of p-doped InAs; p-doped InAsSb; p-doped InGaAs; p-doped type II super lattice of the type InAs/InGaSb; and p-doped HgCdTe. -
Barrier layer 40 is deposited directly onphoto absorbing layer 30 without requiring passivation.Barrier layer 40 is deposited to a thickness sufficient to substantially prevent tunneling of majority carriers fromphoto absorbing layer 30 to contactlayer 50, and in an exemplary embodiment is deposited to a thickness of 50-100 nm.Barrier layer 40 comprises a material selected to exhibit a high band gap barrier for majority carriers fromphoto absorbing layer 30 and substantially no band gap barrier for minority carriers.Barrier layer 40 is thus sufficient to block both the flow of thermalized majority carriers and the tunneling of majority carriers fromphoto absorbing layer 30 to contactlayer 50. Thus, for an n-typephoto absorbing layer 30, the band gap difference appears in the conduction band, whereas substantially no band gap offset appears in the valence band. In oneembodiment barrier layer 40 comprises one of AlSb, AlAsSb, GaAlAsSb, AlPSb, AlGaPSb and HgZnTe. In an exemplary embodimentphoto absorbing layer 30 comprises n-doped InAs andbarrier layer 40 is comprised of AlAsxSb1−x with x˜0.15, and thus there is ˜0 valence band offset. -
Contact layer 50 is deposited onbarrier layer 40.Contact layer 50 functions to absorb the minority carriers diffused from the absorbinglayer 30 and is essentially a contact layer. In an exemplaryembodiment contact layer 50 is deposited to a thickness of 20-50 nm and is constituted of one of InAs; InAsSb; InGaAs; type II super lattice of the type InAs/InGaSb; HgCdTe and GaSb.Contact layer 50 may be n-doped or p-doped without exceeding the scope of the invention. Advantageously,contact layer 50 may be constituted of the same material asphoto absorbing layer 30.Contact layer 50 is etched, preferably by photolithography, to define the detector area. Advantageously etching ofbarrier layer 40 or absorbinglayer 30 is not required.Metal layer 65 is deposited oncontact layer 50, and in an exemplary embodiment is constituted of gold. Metal layers 60, 65 enable the connection of an appropriate bias, and a connection to detect a flow of current fromphoto absorbing layer 30 to contactlayer 50. -
FIG. 1B illustrates a side view of a multi-pixel photo-detector 100 according to an embodiment of the principle of theinvention comprising substrate 20,photo absorbing layer 30,barrier layer 40, a first andsecond contact area 110, a metal layer 6 and ametal layer 65.Substrate 20 is provided as a base for deposition and has deposited on oneface metal layer 60 for connection to electronic circuitry. In an exemplaryembodiment metal layer 60 is constituted of gold.Photo absorbing layer 30 is deposited on the second face ofsubstrate 20 opposing the first face.Photo absorbing layer 30 comprises a doped semiconductor responsive to photons of the object wavelength, and preferably is deposited to a thickness on the order of an optical absorption length. In one embodimentphoto absorbing layer 30 is deposited to between one and two times the optical absorption length. In an exemplary embodimentphoto absorbing layer 30 comprises one of n-doped InAs; n-doped InAsSb; n-doped InGaAs; n-doped type II super lattice of the type InAs/InGaSb; and n-doped HgCdTe. In an alternativeembodiment absorbing layer 30 comprises one of p-doped InAs; p-doped InAsSb; p-doped InGaAs; p-doped type II super lattice of the type InAs/InGaSb; and p-doped HgCdTe. -
Barrier layer 40 is deposited directly onphoto absorbing layer 30 without requiring passivation.Barrier layer 40 is deposited to a thickness sufficient to substantially prevent tunneling of majority carriers fromphoto absorbing layer 30 to first andsecond contact area 110, and in an exemplary embodiment is deposited to a thickness of 50-100 nm.Barrier layer 40 comprises a material selected to exhibit a high band gap barrier for majority carriers fromphoto absorbing layer 30 and substantially no band gap barrier for minority carriers.Barrier layer 40 is thus sufficient to block both the flow of thermalized majority carriers and the tunneling of majority carriers fromphoto absorbing layer 30 to first andsecond contact area 110. Thus, for an n-typephoto absorbing layer 30, the band gap difference appears in the conduction band, whereas substantially no band gap offset appears in the valence band. In oneembodiment barrier layer 40 comprises one of AlSb, AlAsSb, GaAlAsSb, AlPSb, AlGaPSb and HgZnTe. In an exemplary embodimentphoto absorbing layer 30 comprises n-doped InAs andbarrier layer 40 is comprised of AlAsxSb1−x with x˜0.15, and thus there is ˜0 valence band offset. -
Contact layer 50 as described above in relation toFIG. 1A is deposited onbarrier layer 40.Contact layer 50, which as will be described further is etched to define first andsecond contact area 110, functions to absorb the minority carriers diffused from the absorbinglayer 30 and is essentially a contact layer. In an exemplaryembodiment contact layer 50 is deposited to a thickness of 20-50 nm and is constituted of one of InAs; InAsSb; InGaAs; type II super lattice of the type InAs/InGaSb; HgCdTe and GaSb.Contact layer 50 may be n-doped or p-doped without exceeding the scope of the invention. Advantageously,contact layer 50 may be constituted of the same material asphoto absorbing layer 30.Contact layer 50 is etched, preferably by photolithography, to define first andsecond contact area 110. Advantageously etching ofbarrier layer 40 or absorbinglayer 30 is not required. In an exemplary embodiment a selective etchant is used which does not etchbarrier layer 40.Metal layer 65 is deposited on each of first andsecond contact area 110, and in an exemplary embodiment is constituted of gold. Thus, a single photo absorbing layer and barrier layer is utilized, with each unetched portion ofcontact layer 50 defining a pixel or individual detector. - The above has been described in an embodiment in which two pixels, or detectors are defined, however this is not meant to be limiting in any way. A large array of photo-detectors produced as above is specifically included in the invention.
-
FIG. 1C illustrates a top level view of multi-pixel photo-detector 100 ofFIG. 1B according to a principle of the invention showingbarrier layer 40, first andsecond contact area 110 andmetal layer 65 defined on each of first andsecond contact area 110. -
FIG. 2A illustrates the energy band levels of an embodiment of the structure ofFIG. 1 according to the principle of the invention in which the photo absorbing layer is n-doped and the contact layer is n-doped, in which the x-axis indicates position along the structure ofFIG. 1 and the y-axis indicates energy levels in an arbitrary illustrative manner. Three energy band levels are depicted: Ev, the valence band energy band level; Ef, the Fermi energy band level; and Ec the conducting band energy level.Area 100 represents the energy band levels withinphoto absorbing layer 30,area 110 represents the energy band levels withinbarrier layer 40 andarea 120 represent the energy band levels withincontact layer 50. - The valence band energy level is substantially constant throughout
areas photo absorbing area 100 to contactarea 120. It is to be noted that due to the energy levels the minority carriers are captured incontact area 120.Barrier layer 40, represented byarea 110, is thick enough so that there is negligible tunneling of majority carriers through it. In an exemplaryembodiment barrier layer 40 is deposited to a thickness of 50-100 nm, and the band gap barrier ofarea 110 is high enough so that there is negligible thermal excitation of majority carriers over it.Area 120 shows energy band levels on a par with that ofarea 100 however this is not meant to be limiting in any way. In one embodiment Ef incontact layer area 120 is slightly higher than their values inphoto absorbing area 100 with the increase being attributed to an increased doping concentration. It is to be noted that no depletion layer is present and therefore there is no SRH current. Photocurrent is a result of optically generated minority carriers which diffuse fromphoto absorbing area 100 to contactarea 120. -
FIG. 2B illustrates the energy band levels of an embodiment of the structure ofFIG. 1 according to the principle of the invention in which the photo absorbing layer is p-doped and the contact layer is p-doped; in which the x-axis indicates position along the structure ofFIG. 1 and the y-axis indicates energy levels in an arbitrary illustrative manner. Three energy band levels are depicted: Ev, the valence band energy level; Ef, the Fermi energy band level; and Ec the conducting band energy level.Area 150 represents the energy band levels withinphoto absorbing layer 30,area 160 represents the energy band levels withinbarrier layer 40 andarea 170 represent the energy band levels withincontact layer 50. - The conduction band energy level is substantially constant throughout
areas photo absorbing area 150 to contactarea 170. It is to be noted that due to the energy levels the minority carriers are captured incontact area 170.Barrier layer 40, represented byarea 160, is thick enough so that there is negligible tunneling of majority carriers through it. In an exemplaryembodiment barrier layer 40 is deposited to a thickness of 50-100 nm, and the band gap barrier ofarea 160 is high enough so that there is negligible thermal excitation of majority carriers over it.Area 170 shows energy band levels on a par with that ofarea 150 however this is not meant to be limiting in any way. In one embodiment Ef incontact layer area 170 is slightly higher than their values inphoto absorbing area 150 with the increase being attributed to an increased doping concentration. It is to be noted that no depletion layer is present and therefore there is no SRH current. Photocurrent is a result of optically generated minority carriers which diffuse fromphoto absorbing area 150 to contactarea 170. -
FIG. 3A illustrates the energy band levels of an embodiment of the structure ofFIG. 1 according to the principle of the invention in which the photo absorbing layer is n-doped and the contact layer is p-doped; in which the x-axis indicates position along the structure ofFIG. 1 and the y-axis indicates energy levels in an arbitrary illustrative manner. Three energy band levels are depicted: Ev, the valence band energy level; Ef, the Fermi energy band level; and Ec the conducting band energy level.Area 200 represents the energy band levels withinphoto absorbing layer 30,area 210 represents the energy band levels withinbarrier layer 40 andarea 220 represent the energy band levels withincontact layer 50. - The valence band energy level is substantially constant throughout
areas area 220, and thus minority carriers are not obstructed from flowing fromphoto absorbing area 200 to contactarea 220. It is to be noted that due to the energy levels the minority carriers are captured incontact area 220.Barrier layer 40, represented byarea 210, is thick enough so that there is negligible tunneling of majority carriers through it. In an exemplaryembodiment barrier layer 40 is deposited to a thickness of 50-100 nm, and the band gap barrier ofarea 210 is high enough so that there is negligible thermal excitation of majority carriers over it. It is to be noted that no depletion layer is present and therefore there is no SRH current. Photocurrent is a result of optically generated minority carriers which diffuse fromphoto absorbing area 200 to contactarea 220. -
FIG. 3B illustrates the energy band levels of an embodiment of the structure ofFIG. 1 according to the principle of the invention in which the photo absorbing layer is p-doped and the contact layer is n-doped; in which the x-axis indicates position along the structure ofFIG. 1 and the y-axis indicates energy levels in an arbitrary illustrative manner. Three energy band levels are depicted: Ev, the valence band energy level; Ef, the Fermi energy band level; and Ec the conducting band energy level.Area 250 represents the energy band levels withinphoto absorbing layer 30,area 260 represents the energy band levels withinbarrier layer 40 andarea 270 represent the energy band levels withincontact layer 50. - The conduction band energy level is substantially constant throughout
areas area 270, and thus minority carriers are not obstructed from flowing from thephoto absorbing area 250 to contactarea 270. It is to be noted that due to the energy levels the minority carriers are captured incontact area 270.Barrier layer 40, represented byarea 260, is thick enough so that there is negligible tunneling of majority carriers through it. In an exemplaryembodiment barrier layer 40 is deposited to a thickness of 50-100 nm, and the band gap barrier ofarea 260 is high enough so that there is negligible thermal excitation of majority carriers over it. It is to be noted that no depletion layer is present and therefore there is no SRH current. Photocurrent is a result of optically generated minority carriers which diffuse fromphoto absorbing area 250 to contactarea 270. -
FIG. 4 illustrates a high level flow chart of the process of manufacture of the photo-detector ofFIG. 1 . In stage 1000 a substrate material is provided as a support for deposition. Instage 1010, a photo absorbing layer is deposited on the substrate. Preferably the photo absorbing layer is deposited to a thickness on the order of the optical absorption length and in an exemplary embodiment is deposited to a thickness of between one and two times the optical absorption length. - In
stage 1020, a barrier material is selected such that the flow of thermalized majority carriers from the photo absorbing layer deposited instage 1010 would be negligible, and the flow of minority carriers is not impeded. Instage 1030, the barrier material selected instage 1020 is deposited to a thickness sufficient to prevent tunneling of majority carriers through the barrier material. In an exemplary embodiment the thickness is between 50 and 100 nm. Preferably the barrier material is deposited directly on the photo absorbing layer deposited instage 1010. - In
stage 1040, a contact layer is deposited, preferably directly on the barrier material deposited instage 1030. Instage 1050, the desired contact areas are defined. Preferably, the contact areas are defined by photolithography and a selective etchant which stops on the top of the barrier layer. Alternatively, the etchant may be controlled to stop once the uncovered portions ofcontact layer 50 are removed. Thus, the depth of the etch is equivalent to the thickness of thecontact layer 50. Advantageously, in an exemplary embodiment no other layer is etched. - In stage 1060 a metal layer is deposited on the contact areas defined in
stage 1050 so as to enable electrical connection. Preferably the metal layer is deposited directly on the contact areas defined instage 1050. Instage 1070, a metal layer is deposited onsubstrate 20 provided instage 1000 so as to enable electrical connection. - Deposition of the photo absorbing layer of
stage 1010, the barrier layer ofstage 1030 and the contact layer ofstage 1040 may be accomplished by any means known to those skilled in the art including, without limitation molecular beam epitaxy, metal organic chemical vapor deposition, metal organic phase epitaxy or liquid phase epitaxy. - Thus the present embodiment enable a photo-detector sensitive to a target waveband comprising a photo absorbing layer, preferably exhibiting a thickness on the order of the optical absorption length. In an exemplary embodiment the photo absorbing layer is deposited to a thickness of between one and two times the optical absorption length. A contact layer is further provided, and a barrier layer is interposed between the photo absorbing layer and the contact layer. The barrier layer exhibits a thickness sufficient to prevent tunneling of majority carriers from the photo absorbing layer to the contact layer, and a band gap barrier sufficient to block the flow of thermalized majority carriers from the photo absorbing layer to the contact layer. The barrier layer does not block minority carriers.
- An infra-red detector in accordance with the principle of the invention can be produced using either an n-doped photo absorbing layer or a p-doped photo absorbing layer, in which the barrier layer is designed to have no offset for minority carriers and a band gap barrier for majority carriers. Current in the detector is thus almost exclusively by minority carriers. In particular, for an n-doped photo absorbing layer the junction between the barrier layer and the absorbing layer is such that there is substantially zero valence band offset, i.e. the band gap difference appears almost exclusively in the conduction band offset. For a p-doped photo absorbing layer the junction between the barrier layer and the absorbing layer is such that there is substantially zero conduction band offset, i.e. the band gap difference appears almost exclusively in the valence band offset.
- Advantageously the photo-detector of the subject invention does not exhibit a depletion layer, and thus the dark current is significantly reduced. Furthermore, in an exemplary embodiment passivation is not required as the barrier layer further functions to achieve passivation.
- It is appreciated that certain features of the invention, which are, for clarity, described in the context of separate embodiments, may also be provided in combination in a single embodiment. Conversely, various features of the invention which are, for brevity, described in the context of a single embodiment, may also be provided separately or in any suitable sub-combination.
- Unless otherwise defined, all technical and scientific terms used herein have the same meanings as are commonly understood by one of ordinary skill in the art to which this invention belongs. Although methods similar or equivalent to those described herein can be used in the practice or testing of the present invention, suitable methods are described herein.
- All publications, patent applications, patents, and other references mentioned herein are incorporated by reference in their entirety. In case of conflict, the patent specification, including definitions, will prevail. In addition, the materials, methods, and examples are illustrative only and not intended to be limiting.
- It will be appreciated by persons skilled in the art that the present invention is not limited to what has been particularly shown and described hereinabove. Rather the scope of the present invention is defined by the appended claims and includes both combinations and sub-combinations of the various features described hereinabove as well as variations and modifications thereof, which would occur to persons skilled in the art upon reading the foregoing description.
Claims (20)
1. A photo-detector comprising:
a photo absorbing layer comprising a doped semiconductor exhibiting a valence band energy level and a conducting band energy level;
a barrier layer, a first side of said barrier layer adjacent a first side of said photo absorbing layer, said barrier layer exhibit a valence band energy level substantially equal to said valence band energy level of said photo absorbing layer and a conduction band energy level exhibiting a significant band gap in relation to the conduction band of said photo absorbing layer; and
a contact layer comprising a doped semiconductor, said contact layer being adjacent a second side of said barrier layer opposing said first side,
said barrier layer exhibiting a thickness, said thickness and said band gap being sufficient to prevent tunneling of majority carriers from said photo absorbing layer to said contact layer and blow the flow of thermalized majority carriers from said photo absorbing layer to said contact layer.
2. A photo-detector according to claim 1 , wherein said barrier layer comprises an undoped semiconductor.
3. The photo-detector according to claim 1 , wherein the photo absorbing layer and the contact layer are either both n-doped or both p-doped.
4. A photo-detector according to claim 1 , wherein said contact layer exhibits a valence band energy level substantially equal to or greater than said valence band energy level of said doped semiconductor of said photo absorbing layer.
5. A photo-detector according to claim 1 , further wherein said photo-detector has not been subjected to a passivation process.
6. The photo-detector according to claim 1 , wherein the alignments of respective edges of the valence band energy and conduction band energy at interfaces between the photo absorbing layer and the barrier layer and between the contact layer and the barrier layer occur with minimized depletion zones.
7. A photo-detector according to claim 1 , wherein said photo absorbing layer is operable to generate carriers in the presence of light energy exhibiting a wavelength of 3-5 microns.
8. A photo-detector according to claim 1 , further comprising a substrate exhibiting a first side adjacent a second side of said photo absorbing layer, said second side of said photo absorbing layer opposing said first said of said photo absorbing layer, said substrate exhibiting a second side in contact with a first metal layer.
9. A photo-detector according to claim 1 , wherein said barrier layer comprises one of AlSb, AlAsSb, GaAlAsSb, AlPSb, AlGaPSb and HgZnTc.
10. A photo-detector comprising:
a photo absorbing layer comprising an p-doped semiconductor exhibiting a conduction band energy and valence band energy;
a barrier layer exhibiting a thickness, a first side of said barrier layer adjacent a first side of said photo absorbing layer; and
a contact layer comprising a doped semiconductor, said contact layer adjacent a second side of said barrier layer opposing said first side,
wherein said barrier layer exhibits a conduction band energy substantially equal to said conduction band energy of said photo absorbing layer and a valence band energy less than the valence band energy of said photo absorbing layer such that a valence energy band gap is formed between the photo absorbing layer and the barrier layer,
wherein said barrier layer thickness and said valence energy band gap are sufficient to prevent tunneling of majority carriers from said photo absorbing layer to said contact layer and to substantially block the flow of thermalized majority carriers from said photo absorbing layers to said contact layer, and
further wherein during operation said barrier layer functions to achieve passivation of the photo-detector.
11. A photo-detector according to claim 10 , wherein said barrier layer comprises an undoped semiconductor.
12. A photo-detector according to claim 10 , wherein said contact layer is either n-doped or p-doped.
13. A photo-detector according to claim 10 , wherein said contact layer exhibits a conduction band energy equal to or less than said conduction band energy of said barrier layer, and
wherein said conduction band energy of said barrier layer is less than said conduction band energy of said p-doped semiconductor of said photo absorbing layer.
14. A photo-detector according to claim 14 , wherein said photo absorbing layer is operable to generate minority carriers in the presence of light energy exhibiting a wavelength of 3-5 microns.
15. A photo-detector according to claim 10 , further comprising a second metal layer in contact with said contact layer.
16. A photo-detector according to claim 10 , wherein said barrier layer comprises one of AlSb, AlAsSb, GaAlAsSb, AlPSb, AlGaPSb, InAlAs, InAlAsSb, and HgZnTe.
17. A photo-detector according to claim 10 , wherein said photo absorbing layer is constituted of one of p-doped InAs, p-doped InAsSb, p-doped InGaAs, p-doped Type II super lattice InAs/InGaSb and p-doped HgCdTe.
18. A method of producing a photo-detector, the method comprising:
providing a substrate;
depositing on said substrate a photo-absorbing layer comprising a doped semiconductor exhibiting an energy level associated with non-conducting majority carriers;
depositing on said deposited photo absorbing layer a barrier layer exhibiting a thickness, an energy level associated with minority carriers of said photo absorbing layer substantially equal to said energy level of said photo absorbing layer and a band gap associated with majority carriers of said photo absorbing layer; and
depositing on said deposited photo absorbing layer a contact layer comprising a doped semiconductor,
said thickness and said band gap of said barrier layer being sufficient to prevent tunneling of majority carriers from said photo absorbing layer to said contact layer and to block the flow of thermalized majority carriers from said photo absorbing layer to said contact layer.
19. A method according to claim 18 , further comprising selectively etching said deposited contact layer to define a plurality of contact areas.
20. A method according to claim 18 , wherein at least one of depositing said photo absorbing layer, depositing said barrier layer and depositing said contact layer is done via one of molecular beam epitaxy, metal organic chemical vapor deposition, metal organic phase epitaxy and liquid phase epitaxy.