US20110303638A1 - Method for Fabricating a Micromirror - Google Patents
Method for Fabricating a Micromirror Download PDFInfo
- Publication number
- US20110303638A1 US20110303638A1 US13/161,241 US201113161241A US2011303638A1 US 20110303638 A1 US20110303638 A1 US 20110303638A1 US 201113161241 A US201113161241 A US 201113161241A US 2011303638 A1 US2011303638 A1 US 2011303638A1
- Authority
- US
- United States
- Prior art keywords
- layer
- wafer
- lto
- features
- silicon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A method for fabricating a micromirror is disclosed. A set of coarse features is formed in a low-temperature oxide (LTO) layer deposited on a front side of a wafer. A set of fine features is then formed in a photosensitive material layer deposited on top of the LTO layer. After removing a portion of the LTO layer to align the width of the coarse features with the width of the fine features, the first silicon dioxide layer and the first and second silicon device layers are etched to form stator comb fingers and rotor comb fingers accordingly. Finally, a portion of the substrate on a back side of the wafer is removed, and the silicon dioxide layers are removed from the front and back sides of the wafer to form a rotatable mirror.
Description
- The present application is a continuation-in-part of U.S. Non-provisional application Ser. No. 12/193,501, filed on Aug. 18, 2008, published on Feb. 10, 2010 under Pub. No. US 2010/00039687, which claims priority to U.S. Provisional Application No. 60/965,417, filed on Aug. 20, 2007, the contents of which are incorporated herein by reference.
- 1. Technical Field
- The present invention relates to microscanners in general, and, in particular, to a method for fabricating a micromirror.
- 2. Description of Related Art
- Microscanners are essential components for the miniaturization of optical diagnostic equipments such as endoscopes. For example, silicon-based microscanners have been integrated into confocal and other instruments for providing images. However, conventional microscanners have small reflection angle and high actuation power. In addition, conventional microscanners require complex fabrication procedures that are not compatible with standard silicon fabrication techniques used in the industry.
- Consequently, it would be desirable to provide an improved method for fabricating microscanners.
- In accordance with a preferred embodiment of the present invention, a set of coarse features is formed in a low-temperature oxide (LTO) layer deposited on a front side of a wafer having a substrate, a first and second silicon device layers separated from each other by a first and second silicon dioxide layers. Next, a set of fine features is formed in a photosensitive material layer deposited on top of the LTO layer. The fine features are constrained laterally within the coarse features. After removing a portion of the LTO layer to align the width of the coarse features with the width of the fine features, the first silicon dioxide layer and the first and second silicon device layers are etched to form stator comb fingers and rotor comb fingers accordingly. Finally, a portion of the substrate on a back side of the wafer is removed, and the silicon dioxide layers are removed from the front and back sides of the wafer to form a rotatable mirror.
- All features and advantages of the present invention will become apparent in the following detailed written description.
- The invention itself, as well as a preferred mode of use, further objects, and advantages thereof, will best be understood by reference to the following detailed description of an illustrative embodiment when read in conjunction with the accompanying drawings, wherein:
-
FIG. 1 is an isomeric view of a micromirror, in accordance with a preferred embodiment of the present invention; -
FIG. 2 shows a set of combdrive actuators within the micromirror fromFIG. 1 , in accordance with a preferred embodiment of the present invention; and -
FIGS. 3 a-3 i graphically illustrates a method for fabricating the micromirror fromFIG. 1 , in accordance with a preferred embodiment of the present invention. - Referring now to the drawings and in particular to
FIG. 1 , there is depicted a diagram of a micromirror (or microscanner), in accordance with a preferred embodiment of the present invention. As shown, amicromirror 174 has two axes, and electrostatic vertical combdrives can be utilized to provide fast, high-torque rotary actuation about the two axes ofmicromirror 174. For example, two sets of staggeredvertical combdrive actuators combdrive actuators Combdrive actuators - The performance of
micromirror 174 is characterized by its response to various electrical signal inputs. For example, one input can be a sinusoidal variable-frequency voltage with suitable offset (to ensure the applied voltage was always positive) between ground and one ofcombdrive actuators combdrive actuators combdrive actuators - With reference now to
FIG. 2 , there is illustrated a detailed diagram ofcombdrive actuators 260 fromFIG. 2 , in accordance with a preferred embodiment of the present invention. As shown,combdrive actuators 260 includerotor comb fingers 306 andstator comb fingers 308. Preferably, each ofstator comb fingers 308 has a width between about 0.5 μm and 50 μm, each ofrotor comb fingers 306 has a width between about 0.5 μm and 50 μm, and a target gap spacing g ranges between 0.5 μm and 50 μm. As their names imply,rotor comb fingers 306 are capable of being rotated, whilestator comb fingers 308 remain stationary throughout. - In response to a voltage being applied at
stator comb fingers 308,rotor comb fingers 306 rotate about atorsion bar 304. Specifically, when a voltage is applied atstator comb fingers 308, an electrostatic torque is experienced byrotor comb fingers 306, which subsequently rotatesrotor comb fingers 306 because they are constrained primarily to rotary motion bytorsion bar 304.Rotor comb fingers 306 are capable of being rotated to a maximum rotation angle of θmax. Asrotor comb fingers 306 are being rotated, a shear stress is developed withintorsion bar 304 due to twisting, and the shear stress offers a mechanical restoring torque against such twisting. The rotation ofrotor comb fingers 306 reaches an equilibrium at a rotation angle at which the electrostatic torque exactly matches the mechanical restoring torque. - With reference now to
FIGS. 3 a-31, there are illustrated a method for fabricating a micromirror, such asmicromirror 174 fromFIG. 1 , in accordance with a preferred embodiment of the present invention. The process begins with a fusion bonded double silicon-on-insulator (DSOI) wafer 400. Wafer 400 includes asubstrate 420 having two <100>silicon device layers silicon dioxide layers FIG. 3 a. Each ofsilicon device layers silicon dioxide layers - Before further processing of
wafer 400, pre-fabrication of any complementary-metal-oxide semiconductor (CMOS) circuitry can be performed at this point, if necessary. For example, CMOS circuitry may include control electronics and sensors to adaptively correct for aberrations in a micromirror. - Following the CMOS circuitry pre-fabrication (if performed),
wafer 400 is cleaned by immersingwafer 400 in a 9:1 solution of H2SO4:H2O2 for approximately 8 minutes. After rinsing with de-ionized water,wafer 400 is spun dry. The above-mentioned cleaning process is commonly known as Piranha clean. - Next,
wafer 400 is placed into a furnace in which a low-temperature oxide (LTO)layer 422 is deposited on top ofsilicon device layer 412 via a low-pressure chemical vapor deposition (LPCVD) process at a low temperature (450° C.) in order to reduce thermal budget.LTO layer 422 is preferably a silicon dioxide layer having a thickness between about 50 nm and about 1.5 μm.LTO layer 422 serves to protect any CMOS circuitry and to act as a hard mask for the deep trench etching to be performed to create vertical comb finger structures. - A first photolithography step is performed on
LTO layer 422 to etch a set ofcoarse features silicon device layer 412. The photolithography step involves coating a layer of hexamethyldisilazane (HMDS) onLTO layer 422, which serves as an adhesion promoter betweenLTO layer 422 and a photosensitive material to be added. Coarse features 424, 426 are etched inLTO layer 422 via a reactive ion etching (RIE) step using CHF3 and O2 gases, as shown inFIG. 3 b. - A
photosensitive material layer 428, such as Shipley SPR 220-3 positive photoresist, is then spun onLTO layer 422. A second photolithographic step is then performed onphotosensitive material layer 428 to etch a set offine features LTO layer 422. Fine features 430, 432 are constrained laterally within respectivecoarse features FIG. 3 c. - The misalignment tolerance for the second photolithography step, which includes a self-alignment step, is half of the gap spacing between stator comb fingers and rotor comb fingers. A significant advantage of the second photolithography step is that if the alignment is deemed to be unsatisfactory on inspection after the second photolithography step, the photoresist can be removed by a Piranha clean, and the self-alignment step can be repeated as many times as necessary. This flexibility eliminates the uncertainty in determining whether or not self-alignment has been achieved, as may happen when the self-alignment is performed to a layer buried deep within a material stack. The minimum comb gap spacing achievable can be determined by the maximum aspect ratio that a silicon deep reactive ion etching (DRIE) tool used in subsequent steps can achieve.
- Next, a second RIE step is utilized to remove exposed
LTO layer 422 in order to trimcoarse features LTO layer 422 to match the widths of corresponding fine features 430, 432 withinphotosensitive material layer 428, in order to complete the self-alignment process, as illustrated inFIG. 3 d. - Using
coarse features LTO layer 422 andfine features photosensitive material layer 428 as masks, a DRIE is utilized to remove a portion of silicon device layer 412 (stopped on silicon dioxide layer 416) to form stator comb features 438 and rotor comb features 440 on top ofsilicon dioxide layer 416, as shown inFIG. 4 e. The DRIE is preferably performed in an inductively-coupled plasma generator using SF6/O2 and C4F8 gases in a pulsed scheme (commonly known as a Bosch process). - A third RIE step is then utilized to remove
silicon dioxide layer 416, usingcoarse features LTO layer 422 andfine features photosensitive material layer 428 as masks.Photosensitive material layer 428 is subsequently removed, leaving rotor comb features 440 unprotected by any masking element, while stator comb features 438 are still protected byLTO layer 422, as illustrated inFIG. 3 f. - A second DRIE step is utilized to remove portions of silicon device layers 412 and 414 (stopped on silicon dioxide layer 418) to define rotor comb
fingers 444 insilicon device layer 414. After the completion of the second DRIE step, rotor comb features 444 reside only insilicon device layer 414, while stator comb features 442 reside in both silicon device layers 412 and 414, as illustrated inFIG. 3 g. - The lower section of stator comb features 442 (portions located in silicon device layer 414) is redundant from an actuation perspective, but they do not affect the operation of a micromirror.
- A third photolithographic step using a
photoresist layer 446 is then performed on a backside ofwafer 400 using a third photomask to align to the features on the front side ofwafer 400. Preferably,photoresist layer 446 is approximately 15 μm thick and is capable of protecting the underlying silicon through a substrate DRIE step.Photoresist layer 446 can be, for example, Shipley SPR 220-7 positive resist. The third photomask contains the outline of arotatable mirror structure 445 and is used to remove all silicon directly beneathrotatable mirror structure 445, as illustrated inFIG. 4 h. - Since the feature on the third photomask is relatively large (comparable to the size of the entire device), a significant amount of misalignment can be tolerated.
Wafer 400 is bound by photoresist to a second silicon substrate (not shown) serving as a mechanical handle in preparation for the backside substrate DRIE step onsubstrate 420. The backside DRIE step releases the devices and creates dicing lines to facilitate cleaving ofwafer 400 into individual chips. -
Wafer 400 can be separated from its handle wafer by soakingwafer 400 in acetone, following which a fourth RIE is performed on the front and back sides ofwafer 400 to remove any remaining exposed hard mask inLTO layer 422 andsilicon dioxide layer 418. The result is an optical scanning device havingmultiple bond pads 448, stator combfingers 450, rotor combfingers 452, and arotatable mirror 454, as illustrated inFIG. 3 i. - As a final step, an E-beam evaporation is used to coat a thin film (approximately 500-1000 Å) of metal on the surface of
mirror 454 to improve reflectivity. The metal can be aluminum, gold, chromium, etc. Preferably,mirror 454 has a circular shape with a 500 μm diameter to facilitate illumination at artibrary angle of incidence by a 500 μm diameter laser beam, which allows for uncomplicated optical paths and easy integration into an imaging system. - As has been described, the present invention provides an improved method for fabricating a micromirror. The self-alignment of the coarse silicon oxide layer and fine photoresist layer ensures the fine and convenient alignment for the comb-drive structure. The entire fabrication process requires only three photomasks, and the three-mask fabrication process allow simpler processing flow with reduced cost.
- While the invention has been particularly shown and described with reference to a preferred embodiment, it will be understood by those skilled in the art that various changes in form and detail may be made therein without departing from the spirit and scope of the invention.
Claims (5)
1. A method of fabricating a micromirror, said method comprising:
forming a set of coarse features in a low-temperature oxide (LTO) layer deposited on a front side of a wafer having a substrate, a first and second silicon device layers separated from each other by a first and second silicon dioxide layers;
forming a set of fine features in a photosensitive material layer deposited on top of said LTO layer, wherein said fine features are constrained laterally within said coarse features;
removing a portion of said LTO layer to align the width of said coarse features with the width of said fine features;
etching said first silicon dioxide layer and said first and second silicon device layers to form stator comb fingers and rotor comb fingers; and
removing a portion of said substrate on a back side of said wafer, and said silicon dioxide layers from said front and back sides of said wafer to form a rotatable minor.
2. The method of claim 1 , wherein said wafer is a double silicon-on-insulator (DSOI) wafer.
3. The method of claim 1 , wherein said etching further includes
etching said first silicon device layer by using said LTO layer and said photosensitive material layer as a mask;
etching said first silicon dioxide layer by using said LTO layer and said photosensitive material layer as a mask; and
removing said photosensitive material layer.
4. The method of claim 1 , wherein said etchings are performed by a Deep Reactive Ion Etching (DRIP process.
5. The method of claim 1 , wherein said method further includes coating a thin metal film on a surface of said micromirror.