US20050183785A1 - Fiber reinforced pipe - Google Patents
Fiber reinforced pipe Download PDFInfo
- Publication number
- US20050183785A1 US20050183785A1 US11/108,776 US10877605A US2005183785A1 US 20050183785 A1 US20050183785 A1 US 20050183785A1 US 10877605 A US10877605 A US 10877605A US 2005183785 A1 US2005183785 A1 US 2005183785A1
- Authority
- US
- United States
- Prior art keywords
- layer
- pipe
- reinforcing fibers
- fibers
- glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Description
- Flexible pipes are needed for conveying fluids under pressure such as sour gas, carbon dioxide and hydrocarbons.
- It is desirable that the pipe be spoolable without collapsing or buckling, even in low temperature environments. The pipe must also be capable of containing high pressure flows under conditions of use, such as when buried, unrestrained and bent.
- A flexible, fiber reinforced pipe has been invented for conveying fluids. The pipe is flexible enough to be spoolable, even under winter temperature conditions. The pipe can contain pressure, when buried, unrestrained and bent. The pipe exhibits impact resistance under normal handling and can be formed using a continuous process, such that it can be manufactured as it is being laid.
- In accordance with one aspect of the present invention, there is provided a flexible, fiber reinforced pipe comprising: an inner tubular liner having an inner surface and an outer surface; a first layer of reinforcing fibers helically wrapped about the inner liner and in direct contact therewith; an outer layer of reinforcing fibers helically wrapped about an underlying layer of reinforcing fibers and in direct contact therewith; and an outer tubular sheath applied over the outer layer in direct contact therewith.
- The underlying layer of reinforcing fibers can be the first layer of reinforcing fibers or intermediate layers of reinforcing fibers applied between the first layer and the outer layer. Where the pipe includes only two layers of reinforcing fibers, the first layer and the outer layer, the outer layer is wrapped in a helical direction opposite (clockwise or counterclockwise) to the first.
- Where the pipe includes one or more intermediate layers of reinforcing fibers in addition to the first layer and an outer layer, there must be at least one layer of reinforcing fibers wrapped in a positive helical direction and at least one layer of reinforcing fibers wrapped in an negative helical direction.
-
FIG. 1 is a side view, partly broken away in successive layers, of an embodiment of a pipe in accordance with the present invention. -
FIG. 2 .is a sectional view taken along lines II-I ofFIG. 1 . -
FIG. 3 is a side view, partly broken away in successive layers, of another embodiment of a pipe in accordance with the present invention. - Referring to
FIG. 1 , a pipe according to the present invention is shown. The pipe includes aninner tubular liner 10 having aninner surface 12 and anouter surface 14, afirst layer 16 of reinforcing fibers helically wrapped about the inner liner and in direct contact with the outer surface thereof, asecond layer 18 of reinforcing fibers helically wrapped about the first layer of reinforcing fibers in direct contact therewith and anouter sheath 20 applied over the second layer and in direct contact with the second layer of reinforcing fibers. The first layer of reinforcing fibers are wrapped either clockwise or counterclockwise and the second layer is wrapped in the other of the clockwise or counterclockwise direction, when compared to the first layer. Thus, it is said that one layer is wrapped at a positive helical angle and the other layer is wrapped in a negative helical angle. - Inner
tubular liner 10 provides little or no structural support for the pipe. Preferably, the liner is selected to support the loads induced by application of the outer layers about it such as during the winding process and the subsequent extrusion ofouter sheath 20. Further, the liner is selected to act as a leak and permeation bladder. The liner should be formed of the most molecularly impervious polymer that meets acceptable material costs, as determined by a cost benefit analysis. Generally, the liner should be selected such that the only leakage is diffusion of gaseous components of the fluid being conveyed. Obviously, the elimination of gaseous diffusion through the liner is preferred. As will be appreciated, the liner is selected to be substantially resistant to degradation by the fluid to be passed therethrough. - The liner is formed of a polymer having bending strains of about 2 to 5 percent such as a thermoplastic or an elastomer. Thermoplastics can include, for example, nylons, cross-linked polyethylene (PEX), polytetrafluroethylene (PTFE), higher temperature engineered polymers or high density polyethylene (HDPE). Elastomers can include, for example, rubbers and nitrites. For petroleum operations, HDPE is particularly useful as it provides good chemical compatibility with many oilfield chemicals at a low cost.
- In some embodiments, the liner is filled, for example, with amorphous clays, chopped glass or carbon fibers. These materials can enhance liner stability, for example, against low temperature cracking, against polymer creep for long term integrity and may enhance the initial strength of the liner following extrusion. The fibers can be aligned or random.
-
Outer sheath 20 surroundsfiber reinforcements outer sheath 20 can be selected to be substantially resistant to degradation by environmental effects (i.e. ultraviolet light, weather, etc.) and by the chemicals that may come in contact with it. - As desired, the outer sheath can include or have attached thereto identifiers such as, for example, paint, coloration, bar-coding, chips, etc. or materials facilitating use or installation such as, for example, electrically conductive wire or survey locatable metal parts. Where such materials are used however, which can abrade fiber reinforcements, such materials should be spaced or shielded from contact with the fiber reinforcements, as by imbedding or encapsulating within the outer sheath.
- In a two layer pipe such as is shown in
FIG. 1 ,layers - The
layers - The fiber layers in the pipe act to react axial and radial loads resulting from, for example, internal pressure and tensile loading. Primary load is in the fiber tensile direction, since generally little side load is induced from operational conditions. Thus, preferred fibers for use in the pipe provide low elongation to failure, for example, of less than 2%. The fibers should also be resistant to degradation by chemicals, such as hydrocarbons and water, intended to be handled, or environmentally present, during use of the pipe. Suitable fibers include glass such as E-glass, E-CR glass or S-glass, carbon, nylon, polyester or aramid. For petroleum operations, E- and E-CR-glass is preferred due to its low cost and ability to carry the required loads. Elongation to failure of glass is generally less than 0.5%.
- The use of metal wires which can cause failure, as by abrasion or cutting, of reinforcement fibers should be avoided or should be out of contact with the reinforcement layers.
- The fibers in the layers are substantially free floating between
liner 14 andsheath 18, being unbonded, as by use of separate adhesives, or curable, cured or uncured polymers, so that the separate fibers, bundles and layers remain independent and can react loads in conjunction with each other, rather than in combination as a rigid body. For example, fibers should be used that are substantially dry such that they will not chemically bond or fuse with other fibers or to the liner or sheath. It is to be noted that the fibers can be untreated, treated or coated and yet considered dry. Each fiber bundle can include one or more individual fibers sometimes twisted together (i.e. in the form of yarn). In one embodiment, a useful fiber bundle contains thousands of individual fibers and is encapsulated with a polymer coating, which does not penetrate the bundle such that the inner fibers remain dry and not chemically bonded or fused together, but are held together as a bundle by the polymer coating. Of course, where fibers are wound onto the liner when it is in the soft or semi-uncured state or theouter sheath 20 is applied by extrusion, as will be described below with respect to a method for producing the pipe, the material of the liner or sheath may mold, and adhere to some degree, to the adjacent fibers. This may reduce the effective free floating characteristics of the inner and outer-most fibers, although the materials of the liner and sheath should preferably be selected to avoid infiltration past the fiber reinforcements which actually come into contact with it. Release agents or other means can be used on the sheath, liner or fibers to reduce adhesion between the fibers and the sheath or liner. - The fibers should be capable of close fitting, thus the use of larger outer diameter fibers, which do not permit close fitting should be avoided. In one embodiment using E-glass fibers, a packing density of 75 to 80% has been found to be desirable. Winding tension effects packing density. A tension force should be used that permits packing of the fiber tows in a manner useful for carrying the required load for the intended application of the pipe. If the fiber tows are not packed sufficiently tight, there will be tightly wound fibers and loosely wound fibers in the pipe. The loose fibers will react loads differently than the tight fibers, so that not all fibers are being employed to carry loads simultaneously. If not all fibers are loaded substantially uniformly, then some fibers may break sooner, as their respective load limits will be reached earlier than the designed optimal limit. In embodiments using fibers with low elongation to failure, such as glass, it is to be understood that the fibers will tend not to stretch to accommodate slack in adjacent fibers. The effects of differential elongation to failure should also be considered when using more than one fiber type in a particular layer. On the other hand, if the fibers are wound with undesirably high tension, fibers will tend to be broken during processing and handling.
- The use of tapes is generally not desirable, as close fitting and independent reaction of loads are jeopardized.
- The angle of winding of each
layer - Referring to
FIG. 3 , there is shown another embodiment of a pipe including an innertubular membrane 110, afirst layer 116 of reinforcing fibers helically wound about the inner liner, anintermediate layer 117 of reinforcing fibers helically wrapped about the first layer of reinforcing fibers, anouter layer 118 of reinforcing fibers helically wrapped about the intermediate layer of reinforcing fibers and acoating 120 applied overouter layer 118. - In the embodiment of
FIG. 3 , thelayers - Production
- With reference to
FIG. 1 , a pipe in accordance with the present invention can be produced by winding fiber reinforcements about aninner liner 10 to form at least onefiber reinforcement layer 16 wrapped helically in a first direction and at least onefiber reinforcement layer 18 wrapped in an opposite direction. Then acoating 20 is applied over the outer most fiber layer. Preferably, the pipe is produced using a substantially continuous process, wherein long lengths, for example of 0.5 km or more, are produced either just before installing the pipe or for spooling to be used later. - The liner can be formed in any desired way, with consideration as to the above noted description of the liner. In a preferred embodiment, the liner is produced by extrusion, providing continuous production thereof, of course limited by raw material supply, reel handling size considerations, shipping, etc.
- The liner is then wound with continuous fiber reinforcements. The reinforcements are generally wound about
outer surface 14 of the liner once it is in the solid state. However, it is possible to apply the fiber reinforcements while the liner is in a molten, semi-molten, uncured or semi-cured state. If the outer surface of the liner is not yet solidified when the fibers are wrapped about it, the first fibers applied over the liner may sink to some degree into the surface of the liner. This can be tolerated, although it is preferred that the fibers not stick at all to the liner and be completely free floating. - One or more reinforcements including fibers of glass, nylon, polyester and/or aramid are wound to form a
first layer 16, which is in contact with and covers entirely the outer surface of the liner. In one embodiment, 32 tows each of multiple fibers are wrapped to form a single layer. However, any number of fibers and tows can be used depending on tow fiber count, layer characteristics which are desired to be achieved and equipment capabilities. - Winding can be accomplished by use of a winder that winds one or more fibers in a helical fashion about the liner, as it is being advanced. The fibers are preferably wound at continuous tension levels using, for example, 5 to 10 pounds of pull force for glass. Winding tension may vary from layer to layer to accommodate differences with respect to the fiber material used in that layer. The level of tension force when winding higher elongation fibers is less important than when winding brittle fibers.
- In a layer winding process, a few individual terminated fibers in a bundle can be ignored and the free ends will usually be brought back into the bundle as winding continues. A broken fiber which is wound back into the layer recovers its loading capability within a few centimeters. While it is desirable to avoid the use of spliced tows in, or the need to splice tows during production of, a length of pipe, some splices can be accommodated without significant adverse effects on pipe performance. An entire broken tow can be spliced back into the process for continued pipe production by introduction back into the winding process, by use of a stitch or glue. Preferably, however, with consideration as to the length and the wind angle of the pipe to be produced, a tow supply is selected that does to ensure that splices need not be present along the length of the pipe.
-
Second layer 18 is then wound about, in contact with, thefirst layer 16. Process considerations as set out above are also applied in the application of the second layer. In one embodiment, the layers are selected to have substantially equal load carrying capability. For example, the first and second layers can have substantially equal but opposite winding angles and fibers applied in substantially equal quantities. - Further fiber reinforcement layers can be wound about
second layer 18, as desired, such as is shown inFIG. 3 . In addition, other layers can be applied such as coatings, etc. provided that they do not interfering with the ability of the fiber reinforcements to carry load, or otherwise significantly adversely effect the pipe performance. -
Sheath 20 is then applied over thesecond layer 18, as by extrusion, spraying, dipping, tape winding, shrink wrapping, braiding, etc. - The liner is generally selected to support the loads induced by application of the outer layers about it such as during the winding process and the subsequent extrusion of the outer sheath. It is useful to control winding tension to avoid collapse of the liner during the winding process. Sometimes, however it is useful to support the liner to a certain extent during production by, for example, the use of rollers or internal pressure. It is also useful to use rollers or other means to urge the liner into a generally circular cross-section prior to winding to control the cross-sectional shape of the finished pipe.
- Performance
- For many hydrocarbon handling operations, a pipe having a 3000 psi burst is considered acceptable, a liner bend strain of about 2 to 5% and preferably a maximum of about 3%, and a minimum bend radius of at least 15× times pipe outer diameter is within desired properties. Other performance properties may be desired for other applications.
- A pipe was produced in accordance with Table I.
TABLE I Production Inner Liner Liner Material HDPE Liner OD in 3.500 Liner SDR ratio (OD/t) 17.0 Liner ID in 3.088 Liner wall thickness (t) in 0.206 Continuous fiber wrap in two layers Fiber Material E-glass Wrap angle inner layer deg. +55.0 Wrap angle outer layer deg. −55.0 Number of yarns per layer 32 Thickness per wrap in 0.054 Cover Cover material HDPE Cover thickness in 0.100 Cover/pipe OD in 3.916 Cover ID in 3.716 Cover SDR 39.2 - At design stage, it was desired that the pipe be useful for 750 psi operating pressure. Experiments showed that the pipe burst at about 3,000 psi.
- Pipe performance is shown in Table II.
TABLE II Performance Design operating pressure psi 750 Burst pressure psi 3,000 Fiber stress safety factor 4.7 Axial strain % 0.3% Radial strain % 0.3% - It will be apparent that many other changes may be made to the illustrative embodiments, while falling within the scope of the invention and it is intended that all such changes be covered by the claims appended hereto.
Claims (31)