TWI625425B - Etching liquid, replenishing liquid, and method of forming copper wiring - Google Patents
Etching liquid, replenishing liquid, and method of forming copper wiring Download PDFInfo
- Publication number
- TWI625425B TWI625425B TW103141630A TW103141630A TWI625425B TW I625425 B TWI625425 B TW I625425B TW 103141630 A TW103141630 A TW 103141630A TW 103141630 A TW103141630 A TW 103141630A TW I625425 B TWI625425 B TW I625425B
- Authority
- TW
- Taiwan
- Prior art keywords
- aromatic heterocyclic
- etching
- ring
- heterocyclic compound
- group
- Prior art date
Abstract
提供不損及銅配線的直線性並可抑制側面蝕刻之蝕刻液、其補給液、及銅配線的形成方法。 A method of forming an etching liquid, a replenishing liquid, and a copper wiring which do not impair the linearity of the copper wiring and suppress side etching can be provided.
本發明之蝕刻液,係銅的蝕刻液,前述蝕刻液為含有酸、氧化性金屬離子及芳香雜環化合物之水溶液。 The etching solution of the present invention is an etching solution for copper, and the etching solution is an aqueous solution containing an acid, an oxidizing metal ion, and an aromatic heterocyclic compound.
前述芳香雜環化合物係在分子內含有:具有1個以上的氮作為構成環之雜原子之5員芳香雜環、以及具有1個以上的氮作為構成環之雜原子之6員芳香雜環。 The aromatic heterocyclic compound contains, in the molecule, a 5-membered aromatic heterocyclic ring having one or more nitrogens as a hetero atom constituting the ring, and a 6-membered aromatic heterocyclic ring having one or more nitrogen atoms as a hetero atom constituting the ring.
Description
本發明係關於銅的蝕刻液、其補給液、及銅配線的形成方法。 The present invention relates to an etching solution for copper, a replenishing liquid thereof, and a method of forming a copper wiring.
於印刷電路板的製造中,以光刻法形成銅配線圖案時係使用氯化鐵系蝕刻液、氯化銅系蝕刻液、鹼性蝕刻液等作為蝕刻液。若使用該等蝕刻液,則會有抗蝕劑(etching resist)下面的銅從配線圖案側面溶解,亦稱為側面蝕刻之情形產生。亦即,本來以抗蝕劑覆蓋而不希望在蝕刻中被去除的部分(亦即銅配線部分)會被蝕刻液去除,而產生該銅配線之寬度從底部到頂部變細之現象。尤其銅配線圖案較微細時必須盡量減少如此側面蝕刻。為了抑制該側面蝕刻,已提出有一種調配有5員芳香雜環化合物之唑化合物的蝕刻液(例如可參考下述專利文獻1)。 In the production of a printed circuit board, a ferric chloride-based etching solution, a copper chloride-based etching solution, an alkaline etching solution, or the like is used as an etching liquid when a copper wiring pattern is formed by photolithography. When such an etching liquid is used, copper under the resist resist is dissolved from the side surface of the wiring pattern, which is also referred to as side etching. That is, a portion (i.e., a copper wiring portion) which is originally covered with a resist and which is not desired to be removed by etching is removed by the etching liquid, resulting in a phenomenon in which the width of the copper wiring is tapered from the bottom to the top. In particular, when the copper wiring pattern is fine, the side etching must be minimized. In order to suppress the side etching, an etching solution in which an azole compound having a 5-membered aromatic heterocyclic compound is formulated has been proposed (for example, refer to Patent Document 1 below).
專利文獻1:日本特開2005-330572號公報 Patent Document 1: Japanese Laid-Open Patent Publication No. 2005-330572
根據專利文獻1記載的蝕刻液而可抑制側面蝕刻,但若以通常方法使用專利文獻1記載的蝕刻液,則有銅配線的側面產生形狀不均之虞。若銅配線的側面產生形狀不均則會使銅配線的直線性降低,再從印刷電路板上方光學檢査銅配線寬度時,會有造成誤判之虞。又,若直線性極端惡化則有印刷電路板的阻抗特性降低之虞。 According to the etching liquid described in Patent Document 1, the side etching can be suppressed. However, when the etching liquid described in Patent Document 1 is used in a usual manner, the side surface of the copper wiring is uneven in shape. If the shape of the copper wiring is uneven, the linearity of the copper wiring is lowered, and when the copper wiring width is optically inspected from above the printed circuit board, a misjudgment may occur. Further, if the linearity is extremely deteriorated, the impedance characteristics of the printed circuit board are lowered.
如上述,以往的蝕刻液係難以不損及銅配線的直線性並抑制側面蝕刻。 As described above, in the conventional etching liquid, it is difficult to suppress the linearity of the copper wiring and suppress the side etching.
本發明係鑑於前述實際情況而完成者,提供不損及銅配線的直線性並可抑制側面蝕刻之蝕刻液、其補給液、以及銅配線的形成方法。 The present invention has been made in view of the above-described actual circumstances, and provides an etching solution for suppressing side etching without damaging the linearity of copper wiring, a replenishing liquid thereof, and a method of forming a copper wiring.
本發明的蝕刻液係銅的蝕刻液,前述蝕刻液為含有酸、氧化性金屬離子及芳香雜環化合物之水溶液;前述芳香雜環化合物係在分子內含有:具有1個以上的氮作為構成環之雜原子之5員芳香雜環、以及具有1個以上的氮作為構成環之雜原子之6員芳香雜環。 In the etching liquid for etching copper according to the present invention, the etching liquid is an aqueous solution containing an acid, an oxidizing metal ion, and an aromatic heterocyclic compound, and the aromatic heterocyclic compound contains one or more nitrogens as a constituent ring in the molecule. A 5-membered aromatic heterocyclic ring of a hetero atom and a 6-membered aromatic heterocyclic ring having one or more nitrogens as a hetero atom constituting the ring.
本發明的補給液係在連續或重複使用前述本發明之蝕刻液時,添加於前述蝕刻液;前述補給液為含有酸及芳香雜環化合物之水溶液;前述芳香雜環化合物係在分子內含有:具有1個以上的氮作為構成環之雜原子之5員芳香雜環、以及具有1個以上的氮作為構成環之雜原子之6員芳香雜環。 The replenishing liquid of the present invention is added to the etching liquid when the etching liquid of the present invention is continuously or repeatedly used; the replenishing liquid is an aqueous solution containing an acid and an aromatic heterocyclic compound; and the aromatic heterocyclic compound contains in the molecule: A 5-membered aromatic heterocyclic ring having one or more nitrogen atoms as a hetero atom constituting the ring, and a 6-membered aromatic heterocyclic ring having one or more nitrogen atoms as a hetero atom constituting the ring.
本發明的銅配線的形成方法係蝕刻銅層未被覆抗蝕劑的部分,並使用前述本發明之蝕刻液進行蝕刻。 The copper wiring of the present invention is formed by etching a portion of the copper layer which is not covered with a resist, and etching using the etching liquid of the present invention.
又,前述本發明中的「銅」可為包含銅者,也可為包含銅合金者。又,本說明書中「銅」是指銅或銅合金。 Further, the "copper" in the above invention may be a copper-containing one or a copper alloy. In the present specification, "copper" means copper or a copper alloy.
根據本發明可提供不損及銅配線的直線性並可抑制側面蝕刻之蝕刻液、其補給液、及銅配線的形成方法。 According to the present invention, it is possible to provide an etching solution capable of suppressing the side surface etching without impairing the linearity of the copper wiring, a replenishing liquid thereof, and a method of forming the copper wiring.
1‧‧‧銅配線 1‧‧‧Bronze wiring
2‧‧‧抗蝕劑 2‧‧‧Resist
3‧‧‧保護皮膜 3‧‧‧Protective membrane
W1‧‧‧底部寬度 W1‧‧‧ bottom width
W2‧‧‧頂部寬度 W2‧‧‧ top width
圖1係表示以本發明的蝕刻液蝕刻後的銅配線的一例之剖面圖。 Fig. 1 is a cross-sectional view showing an example of a copper wiring which is etched by the etching solution of the present invention.
本發明的銅蝕刻液係含有酸、氧化性金屬離子、芳香 雜環化合物之水溶液。本發明的銅蝕刻液中調配有前述芳香雜環化合物,該芳香雜環化合物係在分子內含有:具有1個以上的氮作為構成環之雜原子之5員芳香雜環、以及具有1個以上的氮作為構成環之雜原子之6員芳香雜環。圖1係表示以本發明的蝕刻液蝕刻後的銅配線的一例之剖面圖。銅配線1上係形成有抗蝕劑2。接著,抗蝕劑2的端部的正下方之銅配線1的側面係形成有保護皮膜3。一般若以氯化銅系蝕刻液或氯化鐵系蝕刻液而形成銅配線,則隨著蝕刻進行會產生一價銅離子及其鹽類。配線間液體的交換變慢,故尤其是微細配線之情形,會因為一價銅離子及其鹽類的影響,垂直方向的蝕刻會漸漸變得難以進行,結果會使側面蝕刻增大。此認為根據本發明的蝕刻液而在蝕刻進行同時,以前述芳香雜環化合物捕捉所生成之一價銅離子及其鹽類,藉此可使垂直方向的蝕刻迅速進行,同時可在不易受到噴霧直接衝撃之銅配線1的側面,均勻地形成由一價銅離子及其鹽類與前述芳香雜環化合物所構成之保護皮膜3。由前述芳香雜環化合物所形成保護皮膜3係均勻的,故認為可不損及銅配線1的直線性並抑制側面蝕刻。因此,根據本發明的蝕刻液而可改善印刷電路板的製造步驟中的產率。又,保護皮膜3可在蝕刻處理後藉由去除液之處理而簡單地去除。前述去除液較佳為稀鹽酸水溶液或稀硫酸水溶液等的酸性水溶液等。 The copper etching solution of the present invention contains an acid, an oxidizing metal ion, and a fragrance. An aqueous solution of a heterocyclic compound. In the copper etching solution of the present invention, the aromatic heterocyclic compound containing one or more nitrogens as a hetero atom of a hetero atom constituting a ring and having one or more impurities is contained in the molecule. The nitrogen acts as a 6-membered aromatic heterocyclic ring constituting the hetero atom of the ring. Fig. 1 is a cross-sectional view showing an example of a copper wiring which is etched by the etching solution of the present invention. A resist 2 is formed on the copper wiring 1. Next, a protective film 3 is formed on the side surface of the copper wiring 1 directly under the end portion of the resist 2. Generally, when a copper wiring is formed by a copper chloride-based etching solution or a ferric chloride-based etching solution, monovalent copper ions and salts thereof are generated as the etching progresses. The exchange of liquid in the wiring closes is slow, so especially in the case of fine wiring, the etching in the vertical direction becomes gradually difficult due to the influence of the monovalent copper ions and their salts, and as a result, the side etching is increased. It is considered that the etching of the etching liquid according to the present invention simultaneously captures the generated one-valent copper ions and salts thereof by the above-mentioned aromatic heterocyclic compound, whereby the vertical etching can be performed rapidly, and the spraying can be easily performed. The protective film 3 composed of a monovalent copper ion and a salt thereof and the above aromatic heterocyclic compound is uniformly formed on the side surface of the copper wiring 1 which is directly washed. Since the protective film 3 formed of the above aromatic heterocyclic compound is uniform, it is considered that the linearity of the copper wiring 1 can be prevented and the side etching can be suppressed. Therefore, the yield in the manufacturing steps of the printed circuit board can be improved according to the etching liquid of the present invention. Further, the protective film 3 can be easily removed by the treatment of the removing liquid after the etching treatment. The removal liquid is preferably an acidic aqueous solution such as a dilute hydrochloric acid aqueous solution or a dilute sulfuric acid aqueous solution.
又,相較於以本發明的蝕刻液蝕刻之情形,認為若以 前述專利文獻1的蝕刻液形成銅配線,會形成較厚之不均勻之保護皮膜,故推測會損及銅配線的直線性。 Moreover, compared with the case of etching with the etching solution of the present invention, it is considered that In the etching liquid of Patent Document 1, the copper wiring is formed, and a thick and uneven protective film is formed. Therefore, it is presumed that the linearity of the copper wiring is impaired.
又,使用前述專利文獻1的蝕刻液時蝕刻速度慢,故會導致處理速度降低、生產性降低,但本發明的蝕刻液可維持與一般氯化鐵系蝕刻液或氯化銅系蝕刻液同等的蝕刻速度,因此不會降低生產性並可改善產率。 In addition, when the etching liquid of the above-mentioned Patent Document 1 is used, the etching rate is slow, so that the processing speed is lowered and the productivity is lowered. However, the etching liquid of the present invention can be maintained to be equivalent to a general ferric chloride-based etching solution or a copper chloride-based etching solution. The etching speed, therefore, does not reduce productivity and can improve yield.
本發明的蝕刻液所使用的酸可適當選擇無機酸及有機酸。前述無機酸可舉出硫酸、鹽酸、硝酸、磷酸等。前述有機酸可舉出蟻酸、醋酸、草酸、馬來酸、安息香酸、乙醇酸等。以蝕刻速度的安定性及銅的溶解安定性之觀點來看,前述酸中較佳為鹽酸。 The acid used in the etching liquid of the present invention can be appropriately selected from inorganic acids and organic acids. Examples of the inorganic acid include sulfuric acid, hydrochloric acid, nitric acid, phosphoric acid, and the like. Examples of the organic acid include formic acid, acetic acid, oxalic acid, maleic acid, benzoic acid, and glycolic acid. From the viewpoint of the stability of the etching rate and the dissolution stability of copper, hydrochloric acid is preferred among the above acids.
前述酸的濃度較佳為5g/L~180g/L,更佳為7g/L~150g/L。酸的濃度為5g/L以上時蝕刻速度較快,故可快速蝕刻銅。又,酸的濃度為180g/L以下時可維持銅的溶解安定性,同時可抑制作業環境惡化。 The concentration of the acid is preferably from 5 g/L to 180 g/L, more preferably from 7 g/L to 150 g/L. When the acid concentration is 5 g/L or more, the etching speed is fast, so that copper can be quickly etched. Moreover, when the acid concentration is 180 g/L or less, the dissolution stability of copper can be maintained, and the deterioration of the working environment can be suppressed.
本發明的蝕刻液所使用之氧化性金屬離子只要是可氧化金屬銅之金屬離子即可,例如可舉出二價銅離子、三價鐵離子等。從可抑制側面蝕刻及蝕刻速度的安定性之觀點來看,較佳為使用二價銅離子作為氧化性金屬離子。 The oxidizing metal ion used in the etching liquid of the present invention may be a metal ion which can oxidize metallic copper, and examples thereof include a divalent copper ion and a ferric ion. From the viewpoint of suppressing the stability of the side etching and the etching rate, it is preferred to use divalent copper ions as the oxidizing metal ion.
可藉由調配氧化性金屬離子源而使前述氧化性金屬離子含有於蝕刻液中。例如使用二價銅離子源作為氧化性金屬離子源時,其具體例可舉出氯化銅、硫酸銅、溴化銅、有機酸的銅鹽、氫氧化銅等。例如,使用三價鐵離子源作為氧化性金屬離子源時,其具體例可舉出氯化鐵、溴化鐵、碘化鐵、硫酸鐵、硝酸鐵、有機酸的鐵鹽等。 The oxidizing metal ion may be contained in the etching solution by disposing an oxidizing metal ion source. For example, when a divalent copper ion source is used as the oxidizing metal ion source, specific examples thereof include copper chloride, copper sulfate, copper bromide, a copper salt of an organic acid, and copper hydroxide. For example, when a ferric ion source is used as the oxidizing metal ion source, specific examples thereof include iron chloride, iron bromide, iron iodide, iron sulfate, iron nitrate, and an iron salt of an organic acid.
前述氧化性金屬離子的濃度較佳為10g/L~300g/L,更佳為10g/L~250g/L,又更佳為15g/L~220g/L,又再更佳為30g/L~200g/L。氧化性金屬離子的濃度為10g/L以上時蝕刻速度較快,故可快速蝕刻銅。又,氧化性金屬離子的濃度為300g/L以下時,可維持銅的溶解安定性。 The concentration of the oxidizing metal ion is preferably 10 g/L to 300 g/L, more preferably 10 g/L to 250 g/L, still more preferably 15 g/L to 220 g/L, and even more preferably 30 g/L. 200g/L. When the concentration of the oxidizing metal ion is 10 g/L or more, the etching speed is fast, so that copper can be quickly etched. Further, when the concentration of the oxidizing metal ion is 300 g/L or less, the dissolution stability of copper can be maintained.
本發明的蝕刻液中,為了不損及銅配線的直線性並抑制側面蝕刻而調配前述芳香雜環化合物。前述芳香雜環化合物係在分子內含有具有1個以上的氮作為構成環之雜原子之5員芳香雜環、以及具有1個以上的氮作為構成環之雜原子之6員芳香雜環。前述5員芳香雜環及前述6員芳香雜環只要皆具有1個以上氮作為雜原子即可,亦可具有氮以外的雜原子。為了不損及銅配線的直線性並有效抑制側面蝕刻,前述5員芳香雜環及前述6員芳香雜環較佳為僅具有氮作為雜原子者、或僅具有氮及硫作為雜原子者。又,前述5員芳香雜環及前述6員芳香雜環皆可以胺基、烷基、芳烷基、芳基、硝基、亞硝基、羥基、羧基、 醛基、烷氧基、鹵基、偶氮基、氰基、亞胺基、膦基、巰基、磺酸基等的取代基進行取代。 In the etching liquid of the present invention, the aromatic heterocyclic compound is blended so as not to impair the linearity of the copper wiring and suppress side etching. The aromatic heterocyclic compound contains a 5-membered aromatic heterocyclic ring having one or more nitrogen atoms as a hetero atom constituting the ring, and a 6-membered aromatic heterocyclic ring having one or more nitrogen atoms as a hetero atom constituting the ring. The above-mentioned five-membered aromatic heterocyclic ring and the above-mentioned six-membered aromatic heterocyclic ring may have one or more nitrogen atoms as a hetero atom, and may have a hetero atom other than nitrogen. The above-mentioned five-membered aromatic heterocyclic ring and the above-mentioned six-membered aromatic heterocyclic ring are preferably those having only nitrogen as a hetero atom or only nitrogen and sulfur as a hetero atom in order not to impair the linearity of the copper wiring and to effectively suppress side etching. Further, the above-mentioned 5-membered aromatic heterocyclic ring and the above-mentioned 6-membered aromatic heterocyclic ring may be an amine group, an alkyl group, an aralkyl group, an aryl group, a nitro group, a nitroso group, a hydroxyl group or a carboxyl group. A substituent such as an aldehyde group, an alkoxy group, a halogen group, an azo group, a cyano group, an imido group, a phosphino group, a fluorenyl group or a sulfonic acid group is substituted.
所謂前述芳香雜環化合物在分子內含有前述5員芳香雜環及前述6員芳香雜環,係例如可為如下述式(I)所示腺嘌呤般,為5員芳香雜環與6員芳香雜環縮合形成縮合環之芳香雜環化合物(以下稱為芳香雜環化合物A),也可為5員芳香雜環與6員芳香雜環以單鍵或二價連結基所連結之芳香雜環化合物(以下稱為芳香雜環化合物B)。 The aromatic heterocyclic compound contains the above-mentioned 5-membered aromatic heterocyclic ring and the above-mentioned 6-membered aromatic heterocyclic ring in the molecule, and may be, for example, an adenine represented by the following formula (I), and is a 5-membered aromatic heterocyclic ring and a 6-membered aromatic compound. An aromatic heterocyclic compound (hereinafter referred to as an aromatic heterocyclic compound A) which condenses a heterocyclic ring to form a condensed ring, and may also be an aromatic heterocyclic ring in which a 5-membered aromatic heterocyclic ring and a 6-membered aromatic heterocyclic ring are bonded by a single bond or a divalent linking group. Compound (hereinafter referred to as aromatic heterocyclic compound B).
但本發明所使用之前述芳香雜環化合物不包括以下環狀化合物,即如下述式(II)所示之鳥嘌呤般,為含有羰基的碳而作為構成雜環的原子者。 However, the above-mentioned aromatic heterocyclic compound used in the present invention does not include the following cyclic compound, that is, a guanine represented by the following formula (II), and is a carbon containing a carbonyl group as an atom constituting a hetero ring.
前述5員芳香雜環與前述6員芳香雜環以單鍵連結之芳香雜環化合物B可舉例如下述式(III)所示之2-(4-吡啶基)苯並咪唑(2-(4-pyridyl)benzimidazole)等。 The aromatic heterocyclic compound B in which the above-mentioned 5-membered aromatic heterocyclic ring is bonded to the above-mentioned 6-membered aromatic heterocyclic ring by a single bond is, for example, 2-(4-pyridyl)benzimidazole (2-(4) represented by the following formula (III). -pyridyl)benzimidazole).
前述5員芳香雜環與前述6員芳香雜環以二價連結基連結之芳香雜環化合物B可舉例如下述式(IV)所示之2,4-二胺基-6-[2-(2-甲基-1-咪唑基)乙基]-1,3,5-三嗪(2,4-diamine-6-[2-(2-methyl-1-imidazolyl)ethyl]-1,3,5-triazine)等。二價連結基可舉例如二價烴衍生基、-O-、-S-等。又,前述烴衍生基是指烴基的部分碳或氫可以其他原子或取代基取代者。 The aromatic heterocyclic compound B in which the above-mentioned 5-membered aromatic heterocyclic ring is bonded to the above-mentioned 6-membered aromatic heterocyclic ring by a divalent linking group may, for example, be a 2,4-diamino-6-[2-() represented by the following formula (IV). 2-methyl-1-imidazolyl)ethyl]-1,3,5-triazine (2,4-diamine-6-[2-(2-methyl-1-imidazolyl)ethyl]-1,3, 5-triazine) and so on. The divalent linking group may, for example, be a divalent hydrocarbon-derived group, -O-, -S- or the like. Further, the aforementioned hydrocarbon-derived group means that a part of carbon or hydrogen of a hydrocarbon group may be substituted with another atom or a substituent.
前述二價烴衍生基不僅是伸烷基,也可為伸烯基、伸炔基等。又,前述二價烴衍生基的碳數並無特別限定,但以溶解性之觀點來看較佳為1~6,更佳為1~3。 The aforementioned divalent hydrocarbon-derived group may be not only an alkylene group but also an alkenyl group, an alkynyl group or the like. Further, the carbon number of the divalent hydrocarbon-derived group is not particularly limited, but is preferably from 1 to 6, more preferably from 1 to 3, from the viewpoint of solubility.
又,具有上述芳香雜環化合物A與上述芳香雜環化合物B兩者之構造特徴之化合物,係視為「芳香雜環化合物B」。此種化合物的具體例可舉出硫唑嘌呤(azathioprine)等。 Further, a compound having the structural characteristics of both the aromatic heterocyclic compound A and the above aromatic heterocyclic compound B is regarded as "aromatic heterocyclic compound B". Specific examples of such a compound include azathioprine and the like.
前述芳香雜環化合物的具體例可舉例如:腺嘌呤、6-芐基腺嘌呤、腺苷、2-胺基腺苷、2-(4-吡啶基)苯並咪唑、2,4-二胺基-6-[2-(2-甲基-1-咪唑基)乙基]-1,3,5-三嗪、3-(1-吡咯基甲基)吡啶、1H-吡咯並[2,3-b]吡啶(1H-Pyrrolo[2,3-b]pyridine)、2,6-雙(2-苯並咪唑基)吡啶、咪唑並[1,2-b]嗒嗪(imidazo[1,2-b]pyridazine)、嘌呤、6-氯嘌呤、6-氯-7-去氮嘌呤、硫唑嘌呤、6-(二甲基胺基)嘌呤、7-羥基-5-甲基-1,3,4-三氮吲哚利嗪、咪唑並[1,5-a]吡啶-3-羧醛、6-巰基嘌呤、6-甲氧基嘌呤、1H-1,2,3-***並[4,5-b]吡啶、噻胺、1H-吡咯並[2,3-c]吡啶、1H-吡咯並[3,2-c]吡啶、1H-吡咯並[3,2-b]吡啶、7-甲基-1H-吡咯並[2,3-c]吡啶、6-氯-3-[(4-甲基-1-哌嗪基)甲基]-1H-吡咯並[3,2-c]吡啶、2-甲基-1H-吡咯並[2,3-b]吡啶、3-(N-六氫吡啶基甲基)-1H-吡咯並[2,3-b]吡啶(3-(piperidinomethyl) -1H-pyrrolo[2,3-b]pyridine)、3-(1-甲基-1H-吡咯-2-基)吡啶、1-甲基-2-(3-吡啶基)-1H-吡咯、3-(2-吡咯基)吡啶、2-(1-吡咯基)吡啶、3H-咪唑並[4,5-c]吡啶、1-(2-苯基乙基)-1H-咪唑並[4,5-c]吡啶、2-氮吲哚利嗪、2-苯基-1H-咪唑並[4,5-b]吡啶、3-(3-吡啶基)-1H-1,2,4-***、7-甲基-1,2,4-***並[4,3-a]吡啶、[1,2,4]***並[1,5-a]吡啶-6-胺、3-硝基-5-(3-吡啶基)-1H-吡唑、1-(2-吡啶基)-1H-吡唑-4-胺、2,3-二甲基吡唑並[1,5-a]吡啶、2,3,7-三甲基吡唑並[1,5-a]吡啶、8-胺基-2-苯基[1,2,4]***並[1,5-a]吡啶、5-(2-吡啶基)-2H-四唑、2-(2-吡啶基)苯並噻唑、2-(2-吡啶基)-4-噻唑醋酸、4-(芐基胺基)-2-甲基-7H-吡咯並[2,3-d]嘧啶、7-去氮腺嘌呤、5,7-二甲基吡唑並[1,5-a]嘧啶、2,5-二甲基吡唑並[1,5-a]嘧啶-7-胺、4-胺基-1H-吡唑並[3,4-d]嘧啶、1H-吡唑並[4,3-d]嘧啶-7-胺、4-[(3-甲基-2-丁烯基)胺基]-1H-吡唑並[3,4-d]嘧啶、4H-吡唑並[3,4-d]嘧啶-4-胺、咪唑並[1,2-a]嘧啶、5,7-二甲基[1,2,4]***並[1,5-a]嘧啶、8-第三丁基-7,8-二氫-5-甲基-6H-吡咯並[3,2-e][1,2,4]***並[1,5-a]嘧啶、5,7-二胺基-1H-1,2,3-***並[4,5-d]嘧啶、8-氮雜嘌呤、5-胺基-2-(甲基硫基)噻唑並[5,4-d]嘧啶、2,5,7-三氯噻唑並[5,4-d]嘧啶、6-氯-2-[4-(甲基碸基)苯基]咪唑並[1,2-b]嗒嗪、2-甲基咪唑並[1,2-b]嗒嗪、1H-咪唑並[4,5-d]嗒嗪、1,2,4-***並[4,3-b]嗒嗪、6-氯-1,2,4-***並[4,3-b]嗒嗪、6-甲基-1,2,4-***並[4,3-b]嗒嗪、6,7-二甲基-1,2,4-***並[4,3-b]嗒嗪、四唑並[1,5-b]嗒嗪、6-氯四 唑並[1,5-b]嗒嗪、8-甲基四唑並[1,5-b]嗒嗪、6-氯-7-甲基四唑並[1,5-b]嗒嗪、6-甲氧基四唑並[1,5-b]嗒嗪、四唑並[1,5-b]嗒嗪-6-胺、7-甲基吡唑並[1,5-a]-1,3,5-三嗪-2,4-二胺、吡唑並[5,1-c][1,2,4]苯並三嗪-8-醇、6,7-二甲基吡唑並[5,1-c][1,2,4]三嗪-2(6H)-胺、4,6-二氫-3,4-二甲基吡唑並[5,1-c][1,2,4]三嗪、3-肼基-7-甲基-5-苯基-5H-吡唑並[3,4-e]-1,2,4-三嗪、咪唑並[5,1-f][1,2,4]三嗪-2,7-二胺、4,5-二甲基咪唑並[5,1-f][1,2,4]三嗪-2,7-二胺、2-氮雜腺嘌呤、7,8-二氫-5-甲基咪唑並[1,2-a][1,2,4]***並[1,5-c][1,3,5]三嗪、7,8-二氫咪唑並[1,2-a][1,2,4]***並[1,5-c][1,3,5]三嗪、1,2,4-***並[4,3-a][1,3,5]三嗪-3,5,7-三胺、5-氮雜腺嘌呤、7,8-二氫咪唑並[1,2-a][1,2,4]***並[1,5-c][1,3,5]三嗪等。前述芳香雜環化合物可為鹽酸鹽或硫酸鹽等鹽的形態,也可為水合物。本發明的蝕刻液可調配前述芳香雜環化合物的1種或2種以上。 Specific examples of the above aromatic heterocyclic compound include adenine, 6-benzyl adenine, adenosine, 2-aminoadenosine, 2-(4-pyridyl)benzimidazole, and 2,4-diamine. -6-[2-(2-methyl-1-imidazolyl)ethyl]-1,3,5-triazine, 3-(1-pyrrolylmethyl)pyridine, 1H-pyrrolo[2, 3-b]pyridine (1H-Pyrrolo[2,3-b]pyridine), 2,6-bis(2-benzimidazolyl)pyridine, imidazo[1,2-b]pyridazine (imidazo[1, 2-b]pyridazine), anthracene, 6-chloropurine, 6-chloro-7-azepine, azathioprine, 6-(dimethylamino)anthracene, 7-hydroxy-5-methyl-1, 3,4-triazazinidine, imidazo[1,5-a]pyridine-3-carboxaldehyde, 6-mercaptopurine, 6-methoxyfluorene, 1H-1,2,3-triazole [4,5-b]pyridine, thiamine, 1H-pyrrolo[2,3-c]pyridine, 1H-pyrrolo[3,2-c]pyridine, 1H-pyrrolo[3,2-b]pyridine ,7-methyl-1H-pyrrolo[2,3-c]pyridine, 6-chloro-3-[(4-methyl-1-piperazinyl)methyl]-1H-pyrrolo[3,2 -c]pyridine, 2-methyl-1H-pyrrolo[2,3-b]pyridine, 3-(N-hexahydropyridylmethyl)-1H-pyrrolo[2,3-b]pyridine (3 -(piperidinomethyl) -1H-pyrrolo[2,3-b]pyridine), 3-(1-methyl-1H-pyrrol-2-yl)pyridine, 1-methyl-2-(3-pyridyl)-1H-pyrrole, 3-(2-pyrrolyl)pyridine, 2-(1-pyrrolyl)pyridine, 3H-imidazo[4,5-c]pyridine, 1-(2-phenylethyl)-1H-imidazo[4 ,5-c]pyridine, 2-azalazine, 2-phenyl-1H-imidazo[4,5-b]pyridine, 3-(3-pyridyl)-1H-1,2,4- Triazole, 7-methyl-1,2,4-triazolo[4,3-a]pyridine, [1,2,4]triazolo[1,5-a]pyridine-6-amine, 3 -nitro-5-(3-pyridyl)-1H-pyrazole, 1-(2-pyridyl)-1H-pyrazol-4-amine, 2,3-dimethylpyrazolo[1,5 -a]pyridine, 2,3,7-trimethylpyrazolo[1,5-a]pyridine, 8-amino-2-phenyl[1,2,4]triazolo[1,5- a] pyridine, 5-(2-pyridyl)-2H-tetrazole, 2-(2-pyridyl)benzothiazole, 2-(2-pyridyl)-4-thiazoleacetic acid, 4-(benzylamine 2-methyl-7H-pyrrolo[2,3-d]pyrimidine, 7-deaza adenine, 5,7-dimethylpyrazolo[1,5-a]pyrimidine, 2,5 - dimethylpyrazolo[1,5-a]pyrimidin-7-amine, 4-amino-1H-pyrazolo[3,4-d]pyrimidine, 1H-pyrazolo[4,3-d Pyrimidine-7-amine, 4-[(3-methyl-2-butenyl)amino]-1H-pyrazolo[3,4-d]pyrimidine, 4H-pyrazolo[3,4- d]pyrimidine-4 -amine, imidazo[1,2-a]pyrimidine, 5,7-dimethyl[1,2,4]triazolo[1,5-a]pyrimidine, 8-t-butyl-7,8 -Dihydro-5-methyl-6H-pyrrolo[3,2-e][1,2,4]triazolo[1,5-a]pyrimidine, 5,7-diamino-1H-1 , 2,3-triazolo[4,5-d]pyrimidine, 8-azaindole, 5-amino-2-(methylthio)thiazolo[5,4-d]pyrimidine, 2,5 ,7-trichlorothiazolo[5,4-d]pyrimidine,6-chloro-2-[4-(methylindenyl)phenyl]imidazo[1,2-b]pyridazine, 2-methyl Imidazo[1,2-b]pyridazine, 1H-imidazo[4,5-d]pyridazine, 1,2,4-triazolo[4,3-b]pyridazine, 6-chloro-1 , 2,4-triazolo[4,3-b]pyridazine, 6-methyl-1,2,4-triazolo[4,3-b]pyridazine, 6,7-dimethyl- 1,2,4-triazolo[4,3-b]pyridazine, tetrazolo[1,5-b]pyridazine, 6-chlorotetrazide Zizo[1,5-b]pyridazine, 8-methyltetrazolo[1,5-b]pyridazine, 6-chloro-7-methyltetrazolo[1,5-b]pyridazine, 6-methoxytetrazolo[1,5-b]pyridazine, tetrazolo[1,5-b]pyridazine-6-amine, 7-methylpyrazolo[1,5-a]- 1,3,5-triazine-2,4-diamine, pyrazolo[5,1-c][1,2,4]benzotriazin-8-ol, 6,7-dimethylpyrryl Zoxa[5,1-c][1,2,4]triazine-2(6H)-amine, 4,6-dihydro-3,4-dimethylpyrazolo[5,1-c] [1,2,4]triazine, 3-mercapto-7-methyl-5-phenyl-5H-pyrazolo[3,4-e]-1,2,4-triazine, imidazo[ 5,1-f][1,2,4]triazine-2,7-diamine, 4,5-dimethylimidazo[5,1-f][1,2,4]triazine-2 , 7-diamine, 2-azadenine, 7,8-dihydro-5-methylimidazo[1,2-a][1,2,4]triazolo[1,5-c] [1,3,5]triazine, 7,8-dihydroimidazo[1,2-a][1,2,4]triazolo[1,5-c][1,3,5] Pyrazine, 1,2,4-triazolo[4,3-a][1,3,5]triazine-3,5,7-triamine, 5-azadenine, 7,8-dihydrogen Imidazo[1,2-a][1,2,4]triazolo[1,5-c][1,3,5]triazine and the like. The aromatic heterocyclic compound may be in the form of a salt such as a hydrochloride or a sulfate, or may be a hydrate. The etchant of the present invention may be one or more selected from the above-mentioned aromatic heterocyclic compounds.
使用本發明的蝕刻液而形成具有配線間隔不同的複數圖案區域之銅配線圖案時,前述芳香雜環化合物A較佳為使用由後述芳香雜環化合物A1及後述芳香雜環化合物A2所選擇之1種以上(以下將該等總稱為「特定芳香雜環化合物A」)。 When the copper wiring pattern having a plurality of pattern regions having different wiring intervals is formed by using the etching liquid of the present invention, the aromatic heterocyclic compound A is preferably one selected from the aromatic heterocyclic compound A1 described later and the aromatic heterocyclic compound A2 described later. The above (hereinafter collectively referred to as "specific aromatic heterocyclic compound A").
前述芳香雜環化合物A1,係分子中所含之5員芳香雜環及/或6員芳香雜環被胺基、烷基、羥基、烷氧基、 鹵基及巰基所選擇之1種以上的取代基所取代之化合物。前述芳香雜環化合物A2,係構成分子中所含之5員芳香雜環及6員芳香雜環的氮數合計為3個以下之化合物。 The above aromatic heterocyclic compound A1 is a 5-membered aromatic heterocyclic ring and/or a 6-membered aromatic heterocyclic ring contained in a molecule, and is an amine group, an alkyl group, a hydroxyl group, an alkoxy group, A compound substituted with one or more substituents selected from a halogen group and a fluorenyl group. The aromatic heterocyclic compound A2 is a compound having a total nitrogen number of three or less aromatic heterocyclic rings and a six-membered aromatic heterocyclic ring contained in the molecule.
以蝕刻同時形成配線間隔不同的複數圖案區域時,與配線間隔寬的圖案區域相比,配線間隔窄的圖案區域其到蝕刻結束所需之時間較長。因此,間隔窄的圖案區域之蝕刻結束時,間隔寬的圖案區域的銅配線會有成為過度蝕刻狀態之虞。於此情形時,本發明的蝕刻液中係使用特定芳香雜環化合物A,藉此可抑制間隔寬的圖案區域的過度蝕刻。又,上述「具有配線間隔不同的複數圖案區域之銅配線圖案」可舉例如至少包括第1圖案區域及第2圖案區域之銅配線圖案,該第2圖案區域的間隔係較該第1圖案區域的配線間隔窄。尤其,以銅配線圖案之第1圖案區域之配線間隔為D1、第2圖案區域之配線間隔為D2時,,則於形成D1減去D2的值在10μm以上之銅配線圖案時,使用上述特定芳香雜環化合物A會有效果。 When a plurality of pattern regions having different wiring intervals are simultaneously formed by etching, a pattern region having a narrow wiring interval has a longer time required for the end of etching than a pattern region having a wide wiring interval. Therefore, when the etching of the pattern region having a narrow interval is completed, the copper wiring of the pattern region having a wide interval may be in an over-etched state. In this case, the specific aromatic heterocyclic compound A is used in the etching liquid of the present invention, whereby over-etching of the pattern region having a wide interval can be suppressed. Further, the above-mentioned "copper wiring pattern having a plurality of pattern regions having different wiring intervals" may include, for example, a copper wiring pattern including at least a first pattern region and a second pattern region, and the interval between the second pattern regions is smaller than the first pattern region. The wiring interval is narrow. In particular, when the wiring interval of the first pattern region of the copper wiring pattern is D1 and the wiring interval of the second pattern region is D2, the above-described specificity is used when forming a copper wiring pattern in which D1 minus D2 is 10 μm or more. The aromatic heterocyclic compound A has an effect.
又,即使使用芳香雜環化合物B而取代特定芳香雜環化合物A,也可獲得與使用上述特定芳香雜環化合物A時相同的效果。此時,芳香雜環化合物B不論以取代基取代者、或是不經取代者皆可獲得上述效果。又,芳香雜環化合物B不論是構成5員芳香雜環及6員芳香雜環的 氮數合計為3個以下者、或是4個以上者,皆可獲得上述效果。又,不論是僅使用特定芳香雜環化合物A及芳香雜環化合物B的任一者、或是併用兩者,皆可獲得上述效果。 Further, even if the aromatic heterocyclic compound B is used instead of the specific aromatic heterocyclic compound A, the same effect as in the case of using the above specific aromatic heterocyclic compound A can be obtained. In this case, the above-described effects can be obtained by the aromatic heterocyclic compound B whether it is substituted with a substituent or not. Further, the aromatic heterocyclic compound B constitutes a 5-membered aromatic heterocyclic ring and a 6-membered aromatic heterocyclic ring. The above effects can be obtained by a total of three or less nitrogen atoms or four or more. Further, the above effects can be obtained by using only one of the specific aromatic heterocyclic compound A and the aromatic heterocyclic compound B, or both.
以抑制側面蝕刻且提升銅配線的直線性之觀點來看,前述芳香雜環化合物的濃度較佳為0.01g/L~100g/L的範圍,更佳為0.05g/L~30g/L的範圍。 The concentration of the aromatic heterocyclic compound is preferably in the range of 0.01 g/L to 100 g/L, and more preferably in the range of 0.05 g/L to 30 g/L, from the viewpoint of suppressing side etching and improving the linearity of the copper wiring. .
為了進一步提高側面蝕刻抑制效果及直線性提升效果,本發明的蝕刻液可含有具有5員環~7員環的脂肪族雜環之脂肪族雜環式化合物。以構造安定性及對酸性液之溶解性之觀點來看,前述脂肪族雜環式化合物較佳為僅具有氮作為構成環的雜原子。前述脂肪族雜環式化合物的具體例可舉出具有吡咯啶骨架之吡咯啶化合物、具有哌啶骨架之哌啶化合物、具有哌嗪(piperazine)骨架之哌嗪化合物、具有高哌嗪(homopiperazine)骨架之高哌嗪化合物、具有六氫-1,3,5-三嗪(hexahydro-1,3,5-triazine)骨架之六氫-1,3,5-三嗪化合物等。上述列舉之化合物,其脂肪族雜環可被胺基、烷基、芳烷基、芳基、硝基、亞硝基、羥基、羧基、羰基、烷氧基、鹵基、偶氮基、氰基、亞胺基、膦基、巰基、磺酸基等的取代基取代。本發明的蝕刻液可調配該等的脂肪族雜環式化合物的1種或2種以上。 In order to further improve the side etching suppressing effect and the linearity improving effect, the etching liquid of the present invention may contain an aliphatic heterocyclic compound having an aliphatic heterocyclic ring of a 5-membered to 7-membered ring. The aliphatic heterocyclic compound is preferably a hetero atom having only nitrogen as a constituent ring from the viewpoint of structural stability and solubility in an acidic liquid. Specific examples of the aliphatic heterocyclic compound include a pyrrolidine compound having a pyrrolidine skeleton, a piperidine compound having a piperidine skeleton, a piperazine compound having a piperazine skeleton, and a homopiperazine. a high piperazine compound having a skeleton, a hexahydro-1,3,5-triazine compound having a hexahydro-1,3,5-triazine skeleton, and the like. The above-exemplified compounds may have an aliphatic heterocyclic ring which may be an amine group, an alkyl group, an aralkyl group, an aryl group, a nitro group, a nitroso group, a hydroxyl group, a carboxyl group, a carbonyl group, an alkoxy group, a halogen group, an azo group or a cyanogen group. Substituents such as a group, an imido group, a phosphino group, a fluorenyl group, a sulfonic acid group or the like are substituted. The etching liquid of the present invention may be one or more selected from the group of the aliphatic heterocyclic compounds.
於本發明的蝕刻液調配前述脂肪族雜環式化合物時,脂肪族雜環式化合物的濃度較佳為0.01g/L~100g/L,更佳為0.02g/L~80g/L。若在該範圍內則可進一步提升銅配線的直線性,且可更有效地抑制側面蝕刻。 When the above-mentioned aliphatic heterocyclic compound is blended in the etching liquid of the present invention, the concentration of the aliphatic heterocyclic compound is preferably from 0.01 g/L to 100 g/L, more preferably from 0.02 g/L to 80 g/L. If it is within this range, the linearity of the copper wiring can be further improved, and the side etching can be more effectively suppressed.
為了進一步提高側面蝕刻抑制效果及直線性提升效果,本發明的蝕刻液可含有僅具有5員環及6員環的任一者作為芳香雜環之芳香雜環化合物(以下稱為「芳香雜環化合物」)。以構造安定性及對酸性液之溶解性之觀點來看,芳香雜環化合物較佳為僅具有氮作為構成環之雜原子者。又,以下說明中,「芳香雜環化合物」係指分子內含有5員芳香雜環及6員芳香雜環兩者之芳香雜環化合物。 In order to further improve the side etching suppressing effect and the linearity improving effect, the etching liquid of the present invention may contain an aromatic heterocyclic compound having only an aromatic heterocyclic ring, which has only a 5-membered ring and a 6-membered ring (hereinafter referred to as "aromatic heterocyclic ring"). Compound"). The aromatic heterocyclic compound preferably has only nitrogen as a hetero atom constituting the ring from the viewpoints of structural stability and solubility in an acidic liquid. In the following description, the "aromatic heterocyclic compound" means an aromatic heterocyclic compound containing both a 5-membered aromatic hetero ring and a 6-membered aromatic heterocyclic ring in the molecule.
前述芳香雜環化合物的具體例可舉例如:具有咪唑骨架之咪唑化合物、具有吡唑骨架之吡唑化合物、具有***骨架之***化合物、具有四唑骨架之四唑化合物等的唑化合物、具有吡啶骨架之吡啶化合物、具有吡嗪骨架之吡嗪化合物、具有嘧啶骨架之嘧啶化合物、具有嗒嗪骨架之嗒嗪化合物、具有1,3,5-三嗪骨架之1,3,5-三嗪化合物等。上述列舉的化合物的芳香雜環可以胺基、烷基、芳烷基、芳基、硝基、亞硝基、羥基、羧基、羰基、烷氧基、鹵基、偶氮基、氰基、亞胺基、膦基、巰基、磺基等的取代基取代。本發明的蝕刻液可調配該等之芳香雜環化合物的1種或2種以上。 Specific examples of the aromatic heterocyclic compound include an imidazole compound having an imidazole skeleton, a pyrazole compound having a pyrazole skeleton, a triazole compound having a triazole skeleton, an azole compound having a tetrazole skeleton, and the like. a pyridine compound having a pyridine skeleton, a pyrazine compound having a pyrazine skeleton, a pyrimidine compound having a pyrimidine skeleton, a pyridazine compound having a pyridazine skeleton, and 1,3,5-three having a 1,3,5-triazine skeleton Pyrazine compounds and the like. The aromatic heterocyclic ring of the above-exemplified compounds may be an amine group, an alkyl group, an aralkyl group, an aryl group, a nitro group, a nitroso group, a hydroxyl group, a carboxyl group, a carbonyl group, an alkoxy group, a halogen group, an azo group, a cyano group, or a sub Substituents such as an amine group, a phosphino group, a fluorenyl group, a sulfo group and the like are substituted. One or two or more kinds of the aromatic heterocyclic compounds of the present invention can be added to the etching liquid of the present invention.
於本發明的蝕刻液調配前述芳香雜環化合物時,芳香雜環化合物的濃度較佳為0.01g/L~30g/L,更佳為0.01g/L~20g/L。若在該範圍內則可進一步提升銅配線的直線性,且可更有效地抑制側面蝕刻。 When the above-mentioned aromatic heterocyclic compound is blended in the etching liquid of the present invention, the concentration of the aromatic heterocyclic compound is preferably from 0.01 g/L to 30 g/L, more preferably from 0.01 g/L to 20 g/L. If it is within this range, the linearity of the copper wiring can be further improved, and the side etching can be more effectively suppressed.
本發明的蝕刻液中除了上述成分以外,在不妨礙本發明效果的程度內可以添加其他成分。例如可以添加界面活性劑、成分安定劑、消泡劑等。添加前述其他成分時,其濃度為0.001g/L~5g/L左右。 In addition to the above components, the etching liquid of the present invention may contain other components to the extent that the effects of the present invention are not impaired. For example, a surfactant, a component stabilizer, an antifoaming agent, or the like can be added. When the other components are added, the concentration is about 0.001 g/L to 5 g/L.
可藉由將前述各成分溶解於水而輕易地調製前述蝕刻液。前述水較佳為去除離子性物質及雜質的水,例如離子交換水、純水、超純水等。 The etching liquid can be easily prepared by dissolving the above components in water. The water is preferably water which removes ionic substances and impurities, such as ion-exchanged water, pure water, ultrapure water, and the like.
前述蝕刻液可在使用時調配各成分而成為特定濃度,也可先調製濃縮液並在使用前稀釋使用。前述蝕刻液的使用方法並無特別限定,但以有效抑制側面蝕刻而言,較佳為如後述般使用噴霧而蝕刻。又,使用時蝕刻液的溫度並無特別限制,以維持高生產性且有效抑制側面蝕刻而言,較佳為於20℃~60℃使用。 The etchant may be formulated to have a specific concentration at the time of use, or the concentrate may be prepared and diluted before use. The method of using the etching liquid is not particularly limited. However, in order to effectively suppress side etching, it is preferable to use a spray and etch as described later. Moreover, the temperature of the etching liquid at the time of use is not particularly limited, and it is preferably used at 20 to 60 ° C in order to maintain high productivity and effectively suppress side etching.
本發明的補給液係在連續或重複使用本發明的蝕刻液時添加於前述蝕刻液之補給液,為含有酸與前述芳香雜 環化合物之水溶液。前述補給液中的各成分係與可調配於上述本發明蝕刻液之成分相同。藉由添加前述補給液而可適當保持前述蝕刻液的各成分比,故可安定維持上述本發明蝕刻液的效果。又,本發明的補給液中可進一步在二價銅離子濃度不超過14g/L的濃度之範圍內含有氯化銅等的二價銅離子源。又,本發明的補給液中除了前述成分以外也可調配添加於蝕刻液的成分。 The replenishing liquid of the present invention is added to the replenishing liquid of the etching liquid when the etching liquid of the present invention is continuously or repeatedly used, and contains an acid and the aforementioned aromatic compound. An aqueous solution of a cyclic compound. Each component in the above-mentioned replenishing liquid is the same as the component which can be blended in the above-described etching liquid of the present invention. By adding the above-mentioned replenishing liquid, the respective component ratios of the etching liquid can be appropriately maintained, so that the effect of the above-described etching liquid of the present invention can be stably maintained. Further, in the replenishing liquid of the present invention, a divalent copper ion source such as copper chloride may be further contained in a concentration range in which the concentration of divalent copper ions does not exceed 14 g/L. Further, in the replenishing liquid of the present invention, components added to the etching liquid may be added in addition to the above components.
前述補給液中的各成分的濃度可因應蝕刻液中各成分的濃度而適宜設定,但以安定維持上述本發明蝕刻液的效果之觀點來看,酸的濃度較佳為5g/L~360g/L,且前述芳香雜環化合物的濃度較佳為0.05g/L~800g/L。 The concentration of each component in the replenishing liquid can be appropriately set in accordance with the concentration of each component in the etching solution. However, from the viewpoint of maintaining the effect of the etching liquid of the present invention, the acid concentration is preferably 5 g/L to 360 g/ L, and the concentration of the above aromatic heterocyclic compound is preferably from 0.05 g/L to 800 g/L.
本發明的銅配線的形成方法特徵如下:在蝕刻銅層未被覆抗蝕劑的部分之銅配線的形成方法中,使用上述本發明的蝕刻液進行蝕刻。藉此,以如上述方式而不損及銅配線的直線性並可抑制側面蝕刻。又,在採用本發明的銅配線的形成方法之銅配線形成步驟中,較佳為於連續或重複使用本發明的蝕刻液時,一邊添加上述本發明的補給液一邊蝕刻。因適當保持前述蝕刻液的各成分比,故可安定維持上述本發明的蝕刻液的效果。 The method for forming a copper wiring according to the present invention is characterized in that, in the method of forming a copper wiring in a portion where a copper layer is not coated with a resist, etching is performed using the etching liquid of the present invention. Thereby, the linearity of the copper wiring can be prevented as described above, and the side etching can be suppressed. Moreover, in the copper wiring forming step using the method for forming a copper wiring of the present invention, it is preferable to etch while adding the above-described replenishing liquid of the present invention when the etching liquid of the present invention is continuously or repeatedly used. Since the respective component ratios of the etching liquid are appropriately maintained, the effect of the etching liquid of the present invention described above can be stably maintained.
本發明的銅配線的形成方法中,較佳為藉由噴霧將前述蝕刻液噴霧於前述銅層未被覆抗蝕劑的部分。可有效抑 制側面蝕刻。噴霧時噴嘴並無特別限定,可使用扇形噴嘴或圓錐型噴嘴等。 In the method for forming a copper wiring according to the present invention, it is preferred that the etching liquid is sprayed on a portion of the copper layer which is not covered with a resist by spraying. Effective Side etching. The nozzle is not particularly limited in the case of spraying, and a fan nozzle or a conical nozzle can be used.
以噴霧蝕刻時,噴壓較佳為0.04MPa以上,更佳為0.08MPa以上。噴壓若在0.04MPa以上,則可在銅配線側面形成適當厚度之保護皮膜。藉此可有效防止側面蝕刻。又,從防止抗蝕劑破損之觀點來看,前述噴壓較佳為0.30MPa以下。 In the case of spray etching, the spray pressure is preferably 0.04 MPa or more, more preferably 0.08 MPa or more. When the spray pressure is 0.04 MPa or more, a protective film of an appropriate thickness can be formed on the side surface of the copper wiring. Thereby, side etching can be effectively prevented. Further, from the viewpoint of preventing breakage of the resist, the pressure is preferably 0.30 MPa or less.
其次,一併說明本發明的實施例與比較例。又,本發明不應解釋為限定於下述實施例。 Next, examples and comparative examples of the present invention will be described together. Further, the present invention should not be construed as being limited to the embodiments described below.
調製表1~3所示組成的各蝕刻液,並以後述條件進行蝕刻,並以後述評價方法評價各項目。又,表1~3所示組成的各蝕刻液中剩餘部分為離子交換水。又,表1~3所示鹽酸的濃度為氯化氫的濃度。 Each of the etching liquids having the compositions shown in Tables 1 to 3 was prepared and etched under the conditions described later, and each item was evaluated by an evaluation method described later. Further, the remaining portion of each etching liquid having the composition shown in Tables 1 to 3 was ion-exchanged water. Further, the concentration of hydrochloric acid shown in Tables 1 to 3 is the concentration of hydrogen chloride.
準備厚度12μm的電解銅箔(三井金屬礦業公司製,商品名3EC-III)所積層之銅箔積層板,以含鈀觸媒之處理液(奥野製藥公司製,商品名:Addcopper Series)處理前述銅箔後,使用無電解銅鍍敷液(奥野製藥公司製,商品名:Addcopper Series)形成無電解銅鍍敷膜。接著 使用電解銅鍍敷液(奥野製藥公司製,商品名:Top Lucina SF),在前述無電解銅鍍敷膜上形成厚度10μm的電解銅鍍敷膜,銅層的總厚度為22.5μm。在所得電解銅鍍敷膜的表面被覆厚度15μm的乾膜抗蝕劑(Asahi Kasei E-materials公司製,商品名:SUNFORT SPG-152)。其後使用線寬/線距(L/S)=33μm/27μm的玻璃遮罩曝光,並藉由顯像處理去除未曝光部,藉此製作L/S=33μm/27μm的抗蝕劑圖案。 A copper-clad laminate laminated with an electrolytic copper foil (manufactured by Mitsui Mining and Mining Co., Ltd., trade name: 3EC-III) having a thickness of 12 μm was prepared, and the above-mentioned treatment liquid containing palladium catalyst (manufactured by Okuno Pharmaceutical Co., Ltd., trade name: Addcopper Series) was used to treat the foregoing. After the copper foil, an electroless copper plating film was formed using an electroless copper plating solution (manufactured by Okuno Pharmaceutical Co., Ltd., trade name: Addcopper Series). then An electrolytic copper plating film having a thickness of 10 μm was formed on the electroless copper plating film using an electrolytic copper plating solution (trade name: Top Lucina SF, manufactured by Okuno Chemical Co., Ltd.), and the total thickness of the copper layer was 22.5 μm. A dry film resist (manufactured by Asahi Kasei E-materials Co., Ltd., trade name: SUNFORT SPG-152) having a thickness of 15 μm was coated on the surface of the obtained electrolytic copper plating film. Thereafter, exposure was performed using a glass mask having a line width/line pitch (L/S) = 33 μm / 27 μm, and the unexposed portion was removed by a developing process, thereby producing a resist pattern of L/S = 33 μm / 27 μm.
蝕刻係使用扇形噴嘴(IKEUCHI公司製,商品名:ISVV9020),以噴壓0.12MPa、處理溫度45℃的條件進行。蝕刻加工時間設定為蝕刻後銅配線的底部寬度(W1)到達30μm之時間點。蝕刻後進行水洗、乾燥並進行以下所示評價。 The etching was carried out under the conditions of a spray pressure of 0.12 MPa and a treatment temperature of 45 ° C using a fan nozzle (manufactured by IKEUCHI Co., Ltd., trade name: ISVV9020). The etching processing time was set to a time point at which the bottom width (W1) of the copper wiring after etching reached 30 μm. After the etching, it was washed with water, dried, and evaluated as shown below.
將蝕刻處理之各試驗基板的一部分裁切,並將其埋入聚酯製冷間埋入樹脂,並以可觀察銅配線剖面之方式進行研磨加工。接著使用光學顯微鏡並以200倍觀察前述剖面,確認銅配線的底部寬度(W1)為30μm,同時測量頂部寬度(W2),以抗蝕劑圖案寬度差(33-W2)為側面蝕刻量(μm)(參照圖1)。結果示於表1~3。 A part of each of the test substrates subjected to the etching treatment was cut, embedded in a polyester refrigeration chamber, and the resin was polished to observe the copper wiring cross section. Next, the cross section was observed at 200 times using an optical microscope, and it was confirmed that the bottom width (W1) of the copper wiring was 30 μm while measuring the top width (W2), and the resist pattern width difference (33-W2) was the side etching amount (μm). ) (Refer to Figure 1). The results are shown in Tables 1-3.
將蝕刻處理之各試驗基板以50℃的3重量%氫氧化鈉水溶液浸漬60秒鐘間,並去除抗蝕劑。其後使用鹽酸(氯化氫濃度:7重量%),並以扇形噴嘴(IKEUCHI公司製,商品名:ISVV9020)、噴壓0.12MPa、處理溫度30℃、處理時間10秒鐘而去除保護皮膜。接著使用光學顯微鏡以200倍觀察試驗基板上表面,以20μm之間隔測量銅配線的頂部寬度(W2)10處,並以其標準偏差作成直線性(μm)。結果示於表1~3。 Each of the test substrates subjected to the etching treatment was immersed in a 3 wt% aqueous sodium hydroxide solution at 50 ° C for 60 seconds, and the resist was removed. Thereafter, hydrochloric acid (hydrogen chloride concentration: 7 wt%) was used, and a protective film was removed by a fan nozzle (manufactured by IKEUCHI Co., Ltd., trade name: ISVV9020), a spray pressure of 0.12 MPa, a treatment temperature of 30 ° C, and a treatment time of 10 seconds. Next, the upper surface of the test substrate was observed at 200 times using an optical microscope, and the top width (W2) of the copper wiring was measured at intervals of 20 μm, and linearity (μm) was made with the standard deviation. The results are shown in Tables 1-3.
如表1、2所示,本發明的實施例於任一評價項目都獲得良好的結果。另一方面如表3所示,與實施例相比,比較例於部分評價項目所得結果較差。由該結果來看可知根 據本發明可不損及銅配線的直線性並抑制側面蝕刻。 As shown in Tables 1 and 2, the examples of the present invention obtained good results in any of the evaluation items. On the other hand, as shown in Table 3, compared with the examples, the results obtained by the comparative examples in the partial evaluation items were inferior. From this result, we can see that the root According to the present invention, the linearity of the copper wiring can be prevented and the side etching can be suppressed.
接著說明形成具有配線間隔不同之二個圖案區域的銅配線圖案的例子。 Next, an example of forming a copper wiring pattern having two pattern regions having different wiring intervals will be described.
調製表4所示之組成的各蝕刻液並以後述條件進行蝕刻,並以後述評價方法評價各項目。又,表4所示組成的各蝕刻液中,剩餘部分為離子交換水。又,表4所示之鹽酸濃度為氯化氫的濃度。 Each of the etching liquids having the composition shown in Table 4 was prepared and etched under the conditions described later, and each item was evaluated by an evaluation method described later. Further, in each of the etching liquids having the compositions shown in Table 4, the remainder was ion-exchanged water. Further, the hydrochloric acid concentration shown in Table 4 is the concentration of hydrogen chloride.
除了在製作抗蝕劑圖案時,製作混有L/S=33μm/27μm的圖案區域與L/S=60μm/150μm的圖案區域之抗蝕劑圖案以外,準備與上述相同的試驗基板。 A test substrate similar to the above was prepared except that a resist pattern in which a pattern region of L/S = 33 μm / 27 μm and a pattern region of L / S = 60 μm / 150 μm were mixed in the production of the resist pattern.
蝕刻使用扇形噴嘴(IKEUCHI社製,商品名:ISVV9020),以噴壓0.12MPa、處理溫度45℃的條件進行。蝕刻加工時間設定為L/S=33μm/27μm的抗蝕劑圖案區域中銅配線的底部寬度(W1)到達30μm之時間點。蝕刻後進行水洗、乾燥,並進行以下所示評價。 The etching was carried out under the conditions of a spray pressure of 0.12 MPa and a treatment temperature of 45 ° C using a fan nozzle (manufactured by IKEUCHI Co., Ltd., trade name: ISVV9020). The etching processing time was set to a time point at which the bottom width (W1) of the copper wiring in the resist pattern region of L/S = 33 μm / 27 μm reached 30 μm. After the etching, it was washed with water, dried, and evaluated as shown below.
將蝕刻處理之各試驗基板的一部分裁切,並將其埋入 聚酯製冷間埋入樹脂,並以可觀察銅配線剖面之方式進行研磨加工。接著使用光學顯微鏡並以200倍觀察前述剖面,測量L/S=33μm/27μm的抗蝕劑圖案區域、以及L/S=60μm/150μm的抗蝕劑圖案區域各自的銅配線的頂部寬度(W2),而將與抗蝕劑圖案寬度的差作為側面蝕刻量(μm)。亦即L/S=33μm/27μm的抗蝕劑圖案區域的側面蝕刻量為33-W2(μm),L/S=60μm/150μm的抗蝕劑圖案區域的側面蝕刻量為60-W2(μm)。結果示於表4。 Cutting a part of each test substrate of the etching process and embedding it The polyester refrigerating compartment is embedded with a resin and polished in such a manner that the copper wiring cross section can be observed. Next, the cross section was observed at 200 times using an optical microscope, and the top width of the copper wiring of each of the resist pattern regions of L/S = 33 μm / 27 μm and the resist pattern regions of L / S = 60 μm / 150 μm was measured (W2 The difference from the width of the resist pattern is taken as the side etching amount (μm). That is, the side etching amount of the resist pattern region of L/S = 33 μm / 27 μm is 33 - W2 (μm), and the side etching amount of the resist pattern region of L / S = 60 μm / 150 μm is 60 - W2 (μm) ). The results are shown in Table 4.
將蝕刻處理之各試驗基板以50℃的3重量%氫氧化鈉水溶液浸漬60秒鐘間,並去除抗蝕劑。其後使用鹽酸(氯化氫濃度:7重量%),並以扇形噴嘴(IKEUCHI公司製,商品名:ISVV9020)、噴壓0.12MPa、處理溫度30℃、處理時間10秒鐘而去除保護皮膜。接著使用光學顯微鏡以200倍觀察試驗基板上表面,以20μm之間隔測量於L/S=33μm/27μm的抗蝕劑圖案區域所形成銅配線的頂部寬度(W2)10處,並以其標準偏差為直線性(μm)。結果示於表4。 Each of the test substrates subjected to the etching treatment was immersed in a 3 wt% aqueous sodium hydroxide solution at 50 ° C for 60 seconds, and the resist was removed. Thereafter, hydrochloric acid (hydrogen chloride concentration: 7 wt%) was used, and a protective film was removed by a fan nozzle (manufactured by IKEUCHI Co., Ltd., trade name: ISVV9020), a spray pressure of 0.12 MPa, a treatment temperature of 30 ° C, and a treatment time of 10 seconds. Next, the upper surface of the test substrate was observed at 200 times using an optical microscope, and the top width (W2) 10 of the copper wiring formed in the resist pattern region of L/S = 33 μm / 27 μm was measured at intervals of 20 μm with the standard deviation thereof. It is linear (μm). The results are shown in Table 4.
【表4】
如表4所示,與不調配特定芳香雜環化合物A及芳香雜環化合物B之任一者之實施例35~37相比,調配特定芳香雜環化合物A或芳香雜環化合物B作為芳香雜環化合物之實施例24~34,係可抑制L/S=60μm/150μm的抗蝕劑圖案區域之銅配線的側面蝕刻。又,與上述表3的結果相同地,相較於實施例,比較例13、14係在一部分評價項目獲得較差的結果。 As shown in Table 4, the specific aromatic heterocyclic compound A or the aromatic heterocyclic compound B was formulated as an aromatic hybrid as compared with Examples 35 to 37 in which either the specific aromatic heterocyclic compound A or the aromatic heterocyclic compound B was not formulated. Examples 24 to 34 of the ring compound were side etching of a copper wiring which can suppress a resist pattern region of L/S = 60 μm / 150 μm. Further, in the same manner as in the above Table 3, Comparative Examples 13 and 14 obtained poor results in some of the evaluation items as compared with the Examples.
Claims (7)