!273973 九、發明說明： 【發明所屬之技術領域】 ，尤“一種具有較佳彈 種更為舒適之彈性衣著 本發明係-種高彈性複合材料 性及保溫性之複合材料，以提供一 布料來源。 【先前技術】 #性複合材料係為構成彈性衣 ♦則已知彈性複合材料之f |木源，目 卞·^ I作方法概有以下數種方式： 其-者’係利用機具將橡膠發泡體之上、下兩!273973 IX. Description of the invention: [Technical field to which the invention pertains], in particular, a composite material having a more elastic type and a more comfortable elastic coating of the present invention, a high elastic composite material and a heat insulating composite material, to provide a fabric [Prior Art] #性复合材料 is a kind of elastic composite ♦ is known as elastic composite material f | wood source, witness · ^ I method has the following several ways: Rubber foam above and below
加熱而形成光潛矣； $ , U 苴…， 月表面，再依需求裁切成一適當厚度，並在 声相& 布或早布，用以與人體皮 用相接觸’ &供較為柔赴 一孝之觸感。然而，此種方式因橡膦 I泡體經受熱後必須依使 夕 从、 攸使用者而求來予以切割，故在切割 具過私中僅取一所需的厚度’而剩下的橡勝發泡體即益法 利用’故易造成材料的浪費，此外，因内襯布或 、、且織鬆散且彈性差，使得當橡膠發泡體與單布貼固時，易 造成膠水從部分單布的縫隙中渗出，故當製成彈性衣 枓時，易造成穿著者的不適感，又因單布的組織鬆散 在製成彈性衣著布料時，其車縫 斷裂之缺點。 太低而易屋生早縫處 其二者，係取一適當厚度之橡勝發泡體，並在其外層 表面鋪設-色料與接合劑相混後形成之著色膝，該著色： 係在橡膝發泡體的外層表面形成一著色層，另在該著色： 上貼固有-層透明彈性薄膜’並在該橡膠發泡體的内側： 4 1273973 ，固有-層内襯布’以形成-彈性衣著布料。然而，當以内 概布為與人體接觸之主要接觸面時，因該内襯布接觸面接 觸到水分時會吸收大量水分，且因内襯布外部附著有發泡 橡膠體’使得已吸收之水分不易散失，一直存在於内襯布 中，而使穿著者感到寒冷，故容易造成失溫，因而此種布 料不具保溫效果。 又，上述該些彈性複合材料皆為利用具有低彈性及高 •硬度之橡膠發泡體所製成，因而上述彈性複合材料所製成 之彈性衣著布料的可伸縮性不佳，在穿著及行動時皆會造 成束缚感及具有穿脫不便的缺點。 【發明内容】 為此，本發明之主要目的係提供一種高彈性複合材 料，該複合材料係為-種高彈性及具有保溫效果之複合材 料’以利製成彈性衣著布料後，用以提供一種具有較佳的 保護性及伸縮性之彈性衣著布料來源。 • 前揭目的’本發明所使用的主要技術手段係令 該高彈性複合材料包含有： 一彈性織布層； 一耐水解接著劑層，分別鋪設於該彈性織布層兩側； 以及 一彈性皮層，係分別鋪設於談彈性織布層之耐水解接 著劑層的外側面。 上述複口材料係主要利用在彈性織布層兩側分別鋪設 -而ί水解接著劑層，並在二耐水解接著劑層與彈性織布層 5 1273973 相接合之另一面分別鋪設二彈性皮層，藉由此種層疊的方 式來形成一高彈性複合材料。Heating to form a light snorkel; $ , U 苴..., the moon surface, and then cut to a suitable thickness according to demand, and in the sound phase & cloth or early cloth, used to contact with the human skin ' & Soft to the touch of filial piety. However, in this way, since the rubber phosphide I foam is subjected to heat, it must be cut according to the user, so that only a desired thickness is taken in the cutting tool, and the remaining rubber is won. The foam is easy to use, so it is easy to cause waste of materials. In addition, because the inner lining cloth or the woven fabric is loose and the elasticity is poor, when the rubber foam is adhered to the single cloth, the glue is easily caused from a part of the single cloth. The crevices ooze out, so when it is made into an elastic placket, it is easy to cause discomfort to the wearer, and the looseness of the seam is caused by the looseness of the structure of the single cloth when the elastic cloth is made. Too low and easy to sew in the early part of the house, take a suitable thickness of the rubber foam, and lay on the outer surface of the surface - the pigment and the bonding agent are mixed to form the colored knee, the coloring: The outer surface of the rubber-kneaded foam forms a colored layer, and in the coloring: an intrinsic-layer transparent elastic film is attached and is on the inner side of the rubber foam: 4 1273973, intrinsic-layer interlining fabric to form-elasticity Clothing cloth. However, when the inner contact surface is the main contact surface in contact with the human body, the contact surface of the inner liner cloth absorbs a large amount of moisture when it contacts the moisture, and the foamed rubber body adheres to the outside of the inner liner cloth, so that the absorbed moisture is not easily lost. It always exists in the inner lining cloth, and the wearer feels cold, so it is easy to cause temperature loss, so the cloth does not have a heat preservation effect. Moreover, the elastic composite materials described above are all made of a rubber foam having low elasticity and high hardness, and thus the elastic coating material made of the above elastic composite material has poor scalability, and is worn and acted upon. Both of them cause a sense of restraint and have the disadvantage of being inconvenient to wear and tear. SUMMARY OF THE INVENTION Accordingly, the main object of the present invention is to provide a high-elastic composite material which is a high-elasticity and heat-insulating composite material to provide an elastic garment fabric to provide a A source of elastic clothing with better protection and flexibility. • The main technical means used in the present invention is that the high elastic composite material comprises: an elastic woven fabric layer; a hydrolysis resistant adhesive layer, respectively laid on both sides of the elastic woven fabric layer; and an elastic The skin layers are respectively laid on the outer side of the hydrolysis resistant adhesive layer of the elastic woven fabric layer. The above-mentioned double-layered material is mainly used for laying the two layers on the elastic woven fabric layer, and hydrolyzing the adhesive layer, and laying the two elastic skin layers on the other side of the two hydrolysis-resistant adhesive layer and the elastic woven fabric layer 5 1273973. A highly elastic composite material is formed by such lamination.
本發明之次一目的為提供一具有表面較佳平滑性及低 吸水性之複合材料，係可在上述之複合材料的二彈性皮層 的外側，鋪設一層主要由聚胺基甲酸酯所形成之塗佈^ (polyurethane coating)，利用聚胺基甲酸酯具有的柔曲 性、而才撕強度及耐老化強度之特性，來提供複合材料有^ 多的功能性’ X ’亦在二彈性皮層的外表面以高溫熱壓連 續的網狀金屬壓印形成一具有連續網狀的表面紋路，來達 到上述之增加表面較佳平滑性及低吸水性之效果。“ 本發明之又-次要目的在提供一具有較佳彈性之二彈 性皮層，係上述二彈性皮層主要以聚氯丁二烯（氯平 所形成之密閉式橡膠發泡材f來組成，因聚氯丁二稀且有 較佳的彈性，…述之複合材料製成衣物時 少肢體運動時，衣物所產生的束缚感，並可增加穿衣、脫 衣及活動的方便性。 本發明之再一次要目的為提供複合材料間接合的緊密 卜上述耐水解接著劑層係主要為聚氯丁二烯及里氰酸睡 所組成，因異氰酸鹽具有耐水解（ 、 孤 的μ nu k 孑不可次泡於濃度10% 的㈣Η水溶液24小時後，無龜裂情況產 因而該耐水解接著劑層不易受酸驗二 解接著劑層可不受外在環境變化的亥财水 層及二彈性皮層作緊密的接合。 Ρ將彈性織布 本發明之更一次要目的為蔣 "、、1、一具有保溫效果之複合 1273973 材料’係上述彈性織布層主要A + 叩席要為耐綸（Nylon )及彈性紗 、、且成’因該彈性織布層之斷裂伸 ,^ 呵装评長率（物品斷裂瞬間伸 長率之比值）為450%以上，又 ^ L ^ 八、、且、哉為六角形結構，故 ::性織布層雙面被彈性皮層所貼合時，彈性織布層内部 所夹帶之空氣不易散失，因 八α 1示/皿效果，又因彈性皤 布層具有較佳的彈性，故 因㈣Λ 凤评性衣者布料時，不會因 縫強度太低而產生車縫處斷裂之缺點。 【實施方式】 請參閱第一圖所示，係為本發 其主要包含有： 本“之第-較佳實施例’ 一彈性織布層（1 〇 ); =讀接著劑層（40)，分別舖設於該彈性織布 曰（1 0 )兩側；以及 一彈性皮層（20) r Q Π , 钟右思 ）係刀別鋪設於該彈性 d曰（1 0 )兩側之耐水解接著㈣（4 Q )的外側面； 係經由上述層疊的方式來形成—高彈性複合材料。 在本較佳實施例中，上述二彈性皮層（2 〇 ) (3 〇 ) :使::且要包含有聚氣丁二稀所製成之密閉式橡膠發泡材 口貝，使。有較佳的彈性’使得上述複合材料製成衣物時， 可用以減少肢體運動時’衣物所產生的束缚感，並可增加 穿衣、脫衣及活動的方便性。 >因=上述彈性皮層（20) (3〇)之成形，係以聚 乳丁一烯為主要成分’並加入補強劑、加工助劑、架橋助 劑及發泡劑等，經混練及壓出成型後’利用加硫及二段式 1273973 模壓加硫發泡，而製造屮且古 ^ Ρ Μ田雜 定厚度之密閉式發泡彈性 材貝，再利用劈刀機劈成定 ^ ^、 "予度，其中上述二彈Μ古 層（20)(3〇)的斯妒柚具安 斷裂伸長率介為710%〜750%之間、 硬度（shore 〇〇〇)於 择 — 、 又間的选閉式發泡彈性材質 厚度介於1·5〜3.5mm之間。 @ 八 二：上述耐水解接著劑層（4〇)主要為聚氯丁二婦 及異虱S文鹽所組成，其中該里奢 八T垓異虱酸鹽所佔比例約為總成分 的，因異氰酸鹽具有耐水 成刀 的力月b ’故_耐水解接签 劑層（4 0 )可不受酸鹼侵蝕 , ^ _ x 的衫響，糟由耐水解接著劑 曰（40)將彈性織布層 <叩僧（10)及二彈性皮層（2 (3 0 )作緊密的接合。 反…〇 ) 此外’上述彈性織布層（ Μ ^ ^ ^ ^ . 1 ◦)主要為耐綸（Nylon ) 及彈性紗織造而成，έ钟妓 成、，且、哉接近六角形結構’故當彈性織布 :10)雙面被二彈性皮層（20)(3〇)所貼合時， β布層（10)内部所夾帶之空氣不易散失，故具有 果：又因彈性織布層（10)具有較佳的彈性，因 1成弹性衣著布料時，不會因車縫強度太低 縫處斷裂之缺點。 早 因而，上述該高彈性複合材料可藉由在一彈性皮層（2 2 =表面上鋪設一層耐水解接著劑層（40)，在财水 多人者層（4 〇 )尚未乾酒之前，與彈性織布| 1 〇 ) 黏合’並加熱一段時間後予以冷卻，接著，在上述另一彈 、 θ υ )的表面上鋪設一層耐水解接著劑層（4 〇 )， 並在耐水解接著劑層（4 〇 )尚未乾酒之前，與上述已接 1273973 著一彈性皮層（20) A彈性織布層（1Q)之複合材料 相黏合’並加熱一段時間後予以冷卻，即可形成一高彈性 複合材料。 由上述實施例可得，該耐水解接著劑層（4 〇 )其斷 裂伸長率為550%，且上述彈性織布層（工〇 )之組成成 在布面上，用以測試該布面之水的滲透程度）介於5〇〜。 又請參閱第二圖所示，係為本發明之第二較佳實施 例’其中二彈性皮層（2〇)(3〇)之外表面尚可鋪設 分中，因耐綸成分所佔比例約為總成分的9()%，且其經向 斷裂伸長率及緯向斷裂伸長率約為72〇%、厚度約為 〇 8mm、母平方公分具有1〇〇〜15〇個組織孔洞及該彈性織 布層（1 G )之撥水強度（AATCC 22，經由將水滴流滴 一層由聚胺基曱酸酯類所形成之塗佈層（2丄），利用聚 胺基甲酸醋具有較優良的柔曲性、耐撕強度及耐老化強度 之特性，來提供複合材料有更好的彈性強度。 故可在上述之複合材料中，將一彈性皮層（2 〇 )的 表面鋪設一層由添加色料及填充劑的聚胺基甲酸酯類之 塗佈層（2 1 )，使其表面撥水強度（AATCC22)為 另一彈性皮層（3 0 )，其表面為二次橡膠發泡製成時自 然產生，使其表面撥水強度（AATCC 22 )為70。 上述方法中，則該一彈性皮層（2 〇 )之斷裂伸長率 為540%、硬度（shore 000 )為63度，且其厚度為; 另一彈性皮層（30)，其斷裂伸長率為470%、硬度（sh〇re 000 )為73度且其厚度為2mm ;且上述彈性織布層（工 1273973 〇 )’其經向斷裂伸長率為590%、 声盘决 $向斷裂伸長率為900%、 7子度為 〇.7mm、每平方公ρ的去 盆主 十方A尺約有400〜WO個組織孔洞及 具表面撥水強度（AATCC 22 )為5〇。 此外，本發明亦可利用离、、w 扪用同，皿熱壓連續的網狀模呈，在 二彈性皮層（2 0 )( 3 〇 )之外本&厂 /、在 矣““ 。）之外表面壓印形成'網狀的 表面紋路，以使彈性皮層（20)表面具有較佳的彈性。 故可在上述之複合材料中，利用—彈性皮層（2〇) :表面為二次橡膠發泡製成時自然產生，使其表面撥水強 度（AATCC22)為70;另一彈性皮層之表w 經過熱壓，150度之連續菱形網狀模具，形成一帶有 :續菱形紋路之彈性皮層（30)表面，其表面 度（AATCC 22)為 70。 此時，其一彈性皮層（2〇)量測所得之斷裂伸長率 為^〇%、硬度（sh〇re 〇〇〇)為63度且其厚度為洳m ;另 -彈性皮層（30)，其斷裂伸長率為47〇%、硬度(讣。“ 〇〇〇)為73度且其厚度為2mm。上述彈性織布層〇 ) “ 其經向斷裂伸長率4 59〇%、緯向斷裂伸長率$ 9〇〇%、厚 度為〇.7麵、每平方公尺約有.44〇個組織孔洞及並: 面撥水強度（AATCC 22)為6〇。故上述該些方法皆^ 效提高彈性皮層的彈性度。 又，本發明可在二彈性皮層（2〇) (3〇)之一側 表面鋪設一層彈性外布層（2 2 )，用以作為衣著布料時， 供予使用者一較柔軟之接觸面。 另本發明可在上述複合材料之一彈性皮層（2 〇 」的 10 1273973 外表面上職-層耐水解接著㈣（4G)，並在 著劑層（4。）帛未乾酒之前，與一彈性外布層 二接 :，並加熱-段時間後予以冷卻，經由上述方法： 味性外布層’達到增加與使用者接觸之接觸面的舒適性。 由上說明可知’本發明係利用二彈性皮層、 接著劑層及-彈性織布層所形成之高彈性複合材 配合對二彈性皮層表面作適當的改良或增設 所形成之塗佈層，來加強複合材料的功能 可在”表面增設-彈性外布層，以供該複合 衣著布料時’提高與使用者肌膚接觸的柔軟觸感，= 述該些方法來形成一具有保溫性、伸縮性上 衣物。 〜有N ?早性之 【圖式簡單說明】 第第明之第—較佳實施例的立體示意圖。 【主弟二較佳實施例的立體示意圖。 L主要兀件符號說明】 (1〇)彈性織布層（2 Q)彈性皮層 0 )彈性皮層 (21)塗佈層 （2 2)彈性外布層 (4 〇 )耐水解接著劑層A second object of the present invention is to provide a composite material having better surface smoothness and low water absorption, and a layer of mainly formed of polyurethane can be laid on the outer side of the second elastic skin layer of the composite material. Polyurethane coating, which utilizes the flexibility, tear strength and aging strength properties of polyurethanes to provide composites with many functional 'X' also in the second elastic skin layer. The outer surface is embossed by a high-temperature hot-pressed continuous mesh metal to form a continuous mesh surface texture to achieve the above-mentioned effect of improving surface smoothness and low water absorption. "Further-secondary object of the present invention is to provide a second elastic skin layer having a preferred elasticity, wherein the above two elastic skin layers are mainly composed of a polychloroprene (a closed rubber foam material f formed of chloroform). Polychloroprene is rare and has better elasticity. When the composite material is made into a garment, the feeling of restraint generated by the garment is less, and the convenience of dressing, undressing and activities can be increased. Once again, the purpose is to provide a close bond between the composite materials. The above-mentioned hydrolysis-resistant adhesive layer is mainly composed of polychloroprene and cyanic acid, which is resistant to hydrolysis by isocyanate (isphan μ nu k孑 孑 孑 孑 孑 孑 孑 孑 孑 孑 孑 孑 孑 孑 孑 24 24 24 24 24 24 24 24 24 24 24 24 24 24 24 24 24 24 24 24 24 24 24 24 24 24 24 24 24 24 24 24 24 24 24 24 24 24 24 The skin layer is tightly joined. ΡThe elastic woven fabric The second purpose of the invention is that Jiang ", 1, a composite 1273973 material with thermal insulation effect is the main elastic woven fabric layer of the above-mentioned elastic woven fabric layer. (Nylon) and flexibility And , because of the elongation of the elastic woven fabric layer, the ratio of the evaluation rate (the ratio of the elongation at break of the article) is 450% or more, and ^ L ^ 八, and 哉 is a hexagonal structure. Therefore: When the two sides of the woven fabric layer are attached by the elastic skin layer, the air entrained inside the elastic woven fabric layer is not easily lost, and the elastic layer of the elastic woven fabric layer has better elasticity due to the effect of the eight α 1 show/dish. Therefore, because (4) 凤 评 评 性 性 性 评 评 评 评 评 评 评 评 评 评 评 评 评 评 评 评 评 评 评 评 评 评 评 评 。 。 。 。 。 。 。 。 。 。 。 。 。 。 。 。 。 "First - preferred embodiment" - an elastic woven fabric layer (1 〇); = a read adhesive layer (40), respectively laid on both sides of the elastic woven fabric (10); and an elastic skin layer (20) r Q Π , 钟右思) The outer surface of the knife is placed on both sides of the elastic d曰(10) to resist hydrolysis and then (4) (4 Q); the high elastic composite material is formed by the above lamination. In the preferred embodiment, the two elastic skin layers (2 〇) (3 〇) are made of: and contain a gas condensate The closed rubber foam material has a better elasticity, so that when the composite material is made into clothes, it can be used to reduce the restraint of the clothes when the body moves, and can increase the dressing and undressing. Convenience of activity. >Because of the formation of the above-mentioned elastic skin layer (20) (3〇), it is based on polybutyrene-ene as a main component, and a reinforcing agent, a processing aid, a bridging aid, a foaming agent, etc. are added. After kneading and extrusion molding, 'using sulfurizing and two-stage 1273973 molding and sulphurization foaming, and manufacturing a closed foaming elastic material shell of 屮 古 古 古 杂 杂 , , , , , , , , , , , , , , , , , , , , , , Cheng Ding ^ ^, " degree, wherein the above two elastic layer (20) (3 〇) of the 妒 妒 grapefruit with an elongation at break between 710% ~ 750%, hardness (shore 〇〇〇) The thickness of the selected closed foam elastic material is between 1. 5 and 3.5 mm. @八二: The above-mentioned hydrolysis-resistant adhesive layer (4〇) is mainly composed of polychloroprene and iso-S-salt, wherein the proportion of the eucalyptus is about the total composition. Because the isocyanate has the resistance to water-forming knives, the hydrolysis-resistant sealant layer (40) is not attacked by acid and alkali, ^_x is stunned, and the hydrolysis-resistant adhesive 曰(40) will The elastic woven fabric layer < 叩僧 (10) and the two elastic skin layers (2 (30) are tightly joined. Inverse 〇) In addition, the above elastic woven fabric layer ( Μ ^ ^ ^ ^ . 1 ◦) is mainly resistant Nylon and elastic yarn are woven, έ 妓 、 , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , The air entrained inside the β-layer (10) is not easily lost, so it has the effect that the elastic woven fabric layer (10) has better elasticity, and the fabric strength is not too low due to the elastic clothing layer. The disadvantage of cracking at the seam. As a result, the above-mentioned high-elastic composite material can be laid on a layer of elastic skin layer (2 2 = a layer of hydrolysis-resistant adhesive layer (40) on the surface, before the drinker layer (4 〇) has not dried yet, Elastic woven fabric | 1 〇) Bonding 'and cooling after heating for a while, then laying a layer of hydrolysis-resistant adhesive layer (4 〇) on the surface of the other elastic, θ υ ), and in the hydrolysis-resistant adhesive layer (4 〇) Before the wine is dry, it is bonded to the composite material of the elastic skin layer (20) A elastic woven fabric layer (1Q) which has been attached to 1273973 and heated for a period of time to form a high elastic composite. material. According to the above embodiment, the hydrolysis resistant adhesive layer (4 〇) has an elongation at break of 550%, and the elastic woven fabric layer is formed on the cloth surface to test the cloth surface. The degree of water penetration is between 5 〇 ~. Please also refer to the second embodiment, which is a second preferred embodiment of the present invention. The surface of the second elastic skin layer (2〇) (3〇) can be laid, because the proportion of the nylon component is about It is 9 (%) of the total composition, and its elongation at break and latitudinal elongation at break are about 72%, the thickness is about 8 mm, and the square of the square has 1 to 15 组织 tissue pores and the elasticity. Water-repellent strength of the woven fabric layer (1 G ) (AATCC 22, by coating a water-repellent layer of a coating layer (2 丄) formed of polyamino phthalic acid ester, using polyurethane vinegar has excellent Flexibility, tear strength and aging strength to provide a composite with better elastic strength. Therefore, in the above composite material, a layer of elastic skin (2 〇) can be laid with a layer of added color and The coating layer (21) of the polyurethane of the filler has a water repellent strength (AATCC22) as another elastic skin layer (30), and the surface thereof is naturally produced when the secondary rubber is foamed. , the surface water repellency (AATCC 22) is 70. In the above method, the elastic skin layer (2 〇) has an elongation at break of 540%, a hardness (shore 000) of 63 degrees, and a thickness of; the other elastic skin layer (30) has an elongation at break of 470% and a hardness (sh〇re 000 ) of 73 degrees. And the thickness thereof is 2 mm; and the above-mentioned elastic woven fabric layer (work 1273973 〇) has a warp elongation at break of 590%, a sound disk has a tensile elongation at break of 900%, and a sub-degree of 〇.7 mm per square. The ρ 的 盆 主 十 十 十 十 400 400 400 400 400 400 400 400 400 400 400 400 400 400 400 400 400 400 400 400 400 400 400 400 400 400 400 400 400 400 400 400 400 400 400 400 400 400 400 400 400 400 400 400 A continuous mesh mold is formed by embossing the surface of the surface of the second elastic layer (20) (3 〇) outside the / “ “ “ “ “ “ “ “ “ “ “ , , , , , , , , , , ' ' ' (20) The surface has better elasticity. Therefore, in the above composite material, the elastic skin layer (2〇) is used: when the surface is made of secondary rubber foam, it is naturally produced, and the surface water repellency (AATCC22) is 70; the surface of the other elastic skin layer w After hot pressing, a 150-degree continuous diamond-shaped mesh mold forms a surface of an elastic skin layer (30) with a continuous diamond-shaped pattern having a surface degree (AATCC 22) of 70. At this time, the elongation at break of an elastic skin layer (2 〇) measured is 〇%, the hardness (sh〇re 〇〇〇) is 63 degrees and the thickness thereof is 洳m; the other-elastic skin layer (30), The elongation at break is 47%, the hardness (讣. "“" is 73 degrees and its thickness is 2 mm. The above elastic woven layer 〇) "the elongation at break in the warp direction is 4 59 %, and the latitudinal elongation at break The rate is $9〇〇%, the thickness is 〇.7 faces, there are about .44〇 tissue holes per square meter and the surface water intensity (AATCC 22) is 6〇. Therefore, the above methods all improve the elasticity of the elastic skin layer. Further, in the present invention, an elastic outer layer (22) can be laid on one side of the side of the second elastic skin layer (2 inch) for providing a softer contact surface for the user as a clothing cloth. In addition, the present invention can be used on the outer surface of the elastic skin layer (2 273 10 10 1 1 上 层 接着 接着 接着 接着 接着 接着 接着 接着 接着 接着 接着 接着 接着 接着 接着 接着 接着 接着 接着 接着 接着 接着 10 10 10 10 10 10 10 10 10 10 10 10 10 10 10 10 The elastic outer cloth layer is connected two times: and heated for a period of time and then cooled, through the above method: the scented outer cloth layer 'to achieve the comfort of increasing the contact surface with the user. As can be seen from the above description, the invention utilizes two The elastic composite layer formed by the elastic skin layer, the adhesive layer and the elastic woven fabric layer is combined with the coating layer formed by appropriately modifying or adding the surface of the two elastic skin layers to enhance the function of the composite material. An elastic outer cloth layer for improving the soft touch of contact with the user's skin when the composite fabric is worn, and the above-mentioned methods are used to form a heat-resistant and stretchable upper garment. BRIEF DESCRIPTION OF THE DRAWINGS A first perspective view of a preferred embodiment of the present invention. [Schematic illustration of a preferred embodiment of the main brother. L. Description of the main components of the L] (1) Elastic woven layer (2 Q) elastic skin layer 0) Elastic cortex (21) Coating layer (2 2) Elastic outer layer (4 〇) hydrolysis resistant adhesive layer