TW473519B - Pleochroism powder and pleochroism printed article - Google Patents
Pleochroism powder and pleochroism printed article Download PDFInfo
- Publication number
- TW473519B TW473519B TW089105295A TW89105295A TW473519B TW 473519 B TW473519 B TW 473519B TW 089105295 A TW089105295 A TW 089105295A TW 89105295 A TW89105295 A TW 89105295A TW 473519 B TW473519 B TW 473519B
- Authority
- TW
- Taiwan
- Prior art keywords
- coated
- color
- polychromatic
- mica
- powder
- Prior art date
Description
473519 A7 經 濟 部 智 慧 財 局· 員 X. 消 費 合 作 社 印 製 五、發明說明(1 ) [技術領域] 本發明係關於多色性粉體及多色性塗裝體,特別是關 於改良色調用之多色性粉體及多色性塗裝體。 [技術背景] - 雲母欽系顏料大多會產生干涉色,因此,多應用在真 •珠顏料等方面。另外,為賦與特定色調,將雲母鈦系顏料 .和有色顏料一起使用,然而這種有色顏料通常其耐光性較 差。所以研究開發一種將雲母鈦系顏料中之一部分二氧化 鈦層還原而成為暗色低度氧化鈦,而強調雲母鈦系顏料本 來所/、有的干涉色性質,藉此獲得表面呈有色性之有色顏 料(參照日本專利特公平4-61032號公報等)。 上述無機性有色顏料在化學上極為安定,耐光性優 異,優點不少。 另外,就最近的趨勢而觀,顏料除強調其美麗色調之 外,更要求具備各種其他功能。例如從不同角度可見到不 同色調之色調猝然跳動變化性等’能容易獲得此種特性的 顏料,由於报難藉彩色複印複製其塗裝體而受到重視。 ^然而,一般顏料從任何角度觀看,通常表現.相同色調, :調配以干擾性物質始能隨觀望角度多少看到干涉色程度而 獲得變色性。 [發明揭示] 本發明轉於前述過去技術之問題點,目的係提供依 據觀察方向變化色調之多變色性顏料。 為了達成前述之目的’本發明之多色性粉體之 本紙張尺度適用中國國家標準(CNS)A4規格(210 x 297公釐) 311253
-----I ^--— — — — — — ^--- (請先閱讀背面之注意事項再填寫本頁) --線- 473519 A7 五、發明說明(2 ) — =含薄片狀雲母基板與被覆在前述雲母基板上之錯卜 物,且構成前述錯合氧化物之金屬包含欽、始、及:。 又,本發明之多色性粉體中,較佳者為在以 破覆雲母之雲母鈇表面上被覆銘及銘之錯合氧化 之鋁酸鈷被覆之雲母鈇。 形成 又,本發明之多色性粉體中,構成前述錯合氧 金屬調配莫爾比率較佳者為,二氧化鈦5〇至915 之 7·5 至 49% ,鋁 1 至 20% 。 又’本發明之多色性粉體中,構成前述錯合氧化物之 金屬調配莫爾比率較佳者為,二氧化鈦5〇 2.5 至 7.5% ,紹 u 47 5% 。 · ’° 始 又,本發明之多色性粉體中,構成前述錯合氧化物之 金屬調配莫爾比率較佳者為,二氧化鈦5〇至72 5%,鈷 7.5 至 30% ,鋁 20 至 42.5% 。 又,本發明之多色性粉體中,構成前述錯合氧化物之 金屬調配莫爾比率較佳者為,二氧化鈦50至98%,鈷丨 至 2.5% ,鋁 1 至 49% 。 又,本發明之多色性粉體中,多色性粉體所呈現外觀 色之色相可以以予特色澤計(Hunter)之Lab值表示,且 較佳者為a值_31·13至1ί·35、b值-29.46至31.22、L值 31.82 至 88.23 之間。 本發明之多色性粉體特徵為將氧化鈦披覆在雲母表面 上產生反射干涉色之氧化鈦披覆雲母,與具有與前述氧化 丨&㈣雲母產生之反射干涉色互補色關係色調之顏料或染 本紙張尺度適用中ϋ標準(CNS)A4規格⑽x 297公髮)---— 訂 ί 473519 A7 五、發明說明(3 ) 料混合。 又,本發明之多色性粉體中,較佳者為前 覆之雲母所產生之反射干涉色色調為金色, 化欽被 料之色調為青色。 ’顏料或染 又 ’本發明之多色性粉體中,較佳者為與 化鈦 •被覆之雲母混合之顏料或染料之調配量較佳為2 -重量% 。 至 30.0 錄藍 又’本發明之多色性粉體中,較佳之顏料或染料包含 經濟部智慧財產局員!f消費合作社印製 又’本發明之多色性塗裝體之特徵為藉由 多色性粉體之組成物塗佈在基材上,可依據相 觀察角度觀察不同之色調。 、又,本發明之多色性塗裝體之特徵為,藉 塗佈含有將氧化鈦被覆在雲母表面上產生反射 化鈦被覆雲母組成物,且在含有前述氧化鈦組 塗佈含有具有與前述氧化鈦被覆雲母所產生之 呈現互補色關係色調之顏料或染料之透明著色 .依據相對入射光之觀察角度觀察到不同之色調 又’本發明之多色性塗裝體之特徵為,藉 被覆在雲母表面上產生反射干涉色之氧化鈦被 含有具有與前述氧化鈦被覆雲母所產生之反射 互補色關係色調之顏料或染料之透明著色組成 之組成物塗佈在基材上,且依據相對入射光之 察不同之色調》 適用ϋ國家標準(CNS)A4規;|各(21〇 x 297公以 將含有前述 對入射光之 由在基材上 干涉色之氧 成物之上, 反射干涉色 組成物,且 〇 由將氧化鈦 覆雲母,與 干涉色呈現 物混合所得 觀察角度觀 311253 !! I i! t---------^ (請先閱讀背面之注意事項再填寫本頁) 473519 A7 B7 五、發明說明(4 ) 又’本發明之多色性塗裝體中,前述基材之色調較佳 在白至黑之灰色等級範圍内。 又’本發明之多色性塗裝體中,前述基材之色調較佳 者為青色系。 又’本發明之多色性塗裝體中,含有塗佈在基材上之 前述多色性粉體之組成物膜厚較好在5微米以上。 {附圖之簡要說明} 第1(a)、(b)、(c)圖為顯示本發明之Ti_c〇_A1系錯合 氧化物被覆型多變色性粉體合成方法之說明圖。 第2圖為本發明之Ti_c〇_A1系錯合氧化物被覆型多變 色性粉體之模式圖。 第3圖顯示本發明之Ti_c〇_A1系錯合氧化物被覆型多 變色性粉體中調配金屬之調配比例與色調之關係說明圖。 第4圖為本發明之Ti_c〇_A1系錯合氧化物被覆型多變 色性粉體變色度測定方法之說明圖。 第5圖顯不本發明之Ti_c〇_A1系錯合氧化物被覆型多 變色性粉體變色度測定結果之ab圖。 經濟部智慧財產局員工消費合作社印製 第6圖顯示調配本發明之Ti_c〇_A1系錯合氧化物被覆 型多變色性粉體之塗料組成物之膜厚與變色度關係之說明 圖。 第7(a)、(b)圖係自塗佈實施例1中調配之包含本發明 Ti-Co-Al系錯合氧化物被覆型多變色性粉體之塗料組成物 之基材上之反射光波長分布圖。 第8圖顯示表5、表6結果之ab圖。 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 4 311253 A7 ---------------B7___ 五、發明說明(5 K ^ —- 第9圖顯示實驗6測定方法之概要說明圖。 第10圖顯示表7、表8結果之“圖。 (請先閱讀背面之注意事項再填寫本頁) 第11圖為由表13、表14、表15結果之受光角與色相 變化關係圖示化之圖。 第12圖為由表13、表14、表15結果之受光角與明亮 *度關係圖示化之圖。 -[實施本發明之最佳型態] 本發明者等為了達成本發明之目的而積極進行研究之 '··»果,發現藉由在雲母表面上形成鈦、銘、鋁之錯合氧化 物層,可以得到優良之色調及多變色性,而完成本發明。 亦即,本發明之多變色性粉體特徵為含有薄片狀雲母 基板與被覆在前述雲母基板上之錯合氧化物,且構成前述 錯合氧化物之金屬包含鈦、鈷、鋁。 經濟部智慧財產局員工消費合作社印製 本發明中所使用雲母並無特別限制,一般採用市售之 白雲母系雲母(muscovite mica),有些情況下也可以利用黑 士母等。雲母之粒徑也無特別限制,做為真珠光澤顏料利 用時’採用一般市售雲母中粒徑較小,粒形比較扁平者, .容易產生美麗色調,能發揮真珠之光澤者較佳。雲母之粒 徑為1微米至150微米,且較佳者為5微米至60微米。 本發明之多色性粉體較好係在將雲母被覆以二氧化鈦 之雲母鈦上被覆钻及鋁之錯合氧化物所形成之鋁酸姑被覆 之雲母鈦。 本發明之Ti-Co-Al系錯合氧化物被覆型之多變色性 粉體製造方法’可依據在雲母鈦上被覆始及鋁之各種方法 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 5 311253 A7 A7 經濟部智慧財產局員工消費合作社印製 ------------ 五、發明說明(6 ) ' ' 製造。列舉者為筮, 為第1圖之固相法、液相法(尿素法)、氫氧 化鈉中和分解法三種方法。 第 1 ( a )蔭| — 〒所不之固相法,可將雲母鈦與碳酸鈷、 草酸始、氫氧化銘、氧化料始化合物,與碳酸紹、草酸 &氮氧化銘、氧化銘等銘化合物一起混合,且在700°C 至1100 c下燒成’得到本發明之Ti c〇 Ai系錯合氧化物被 覆型之多變色性粉體。 液相法(尿素法)如第1(b)圖所*,可將氯化銘或硫 酸鋁與氯化鈷或硫酸鈷、尿素、水混合,隨後添加雲母鈦, 且在100 c下回流4小時,經乾燥後,在7〇〇»c至11〇〇〇c 下燒成,得到本發明之Ti_c〇_A1系錯合氧化物被覆型之多 變色性粉體。 氫氧化鈉中和分解法如第1(c)圖所示,將雲母鈦分散 在水中,且升溫至80°C左右,接著逐滴滴加氣化鋁或硫酸 鋁與氣化鈷或硫酸鈷後,滴加氫氧化鈉將{)11值調整至9, 且經過濾、洗滌及乾燥後,在7〇〇°c至11〇〇〇c下燒成,得 到本發明之Ti-Co-Al系錯合氧化物被覆型之多變色性粉 體。 又’第1(c)圖之方法可藉由將氫氧化鈉滴加至升溫至 約80t之雲母鈦分散液中,將pH調整至9,同時將氯化 銘或硫酸銘’氣化始或硫酸姑滴加於其中之方法,製得本 發明之Ti-Co-Al系錯合氧化物被覆型之多變色性粉體。 再者,雖然此處顯示將鋁或鈷同時被覆在雲母欽表面 上之方法,但亦可先被覆鋁後被覆鈷,或先被覆钻後被覆 ---------丨丨 丨----I-!訂_—,— — - (請先閱^面☆注意免項再填寫本頁) 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 6 311253 經濟部智慧財產局員工*消費合作社印製 473519 A7 -—----- B7 _ 五、發明說明(7 ) " · ~ 銘。其中,當作材料之碳酸始、草酸姑、氮氧化姑、氧化 鈷、氣化鈷、%酸鈷與碳酸鋁、草酸鋁、氫氧化鋁、氧化 鋁、氣化鋁、硫酸鋁之組合並沒有特別的限制。其中當鋁 與姑分別被覆時,亦可使用此處所示之 ,氫氧化納中和分解法各種方法之組合' • 製造本發明之Ti-Co-Al系錯合氧化物被覆型之多變色 _性粉體之方法,為了在雲母鈦表面上被覆鋁、鈷,且在 。(:至1100°C下燒成製得,並不僅限於此處所示之方法可 藉由在雲母鈦表面上被覆鋁、鈷之各種方法製得。 再者’當分別被覆鋁、鈷時’被覆之後雖然形成鋁與 钻之個別層’但藉由燒成可使鋁與鈷成為一層錯合氧化物 層。 第2圖中顯示本發明之Ti_c〇_A1系錯合氧化物被覆型 之多色性粉體之模式圖。如同一圖所示,本發明之Ti_c〇_Al 系錯合氧化物被覆型之多色性粉體1〇,係在中心存在有雲 >母12’在其外圍形成二氧化鈦層14,接著在其外圍形成 Co-Al系錯合氧化物層16。 · 具有此型態之本發明之Ti-Co-Al系錯合氧化物被覆型 之多色性粉體係依據二氧化鈦、鋁、鈷之調配比例而呈現 不同之外觀色。 構成被覆在Ti-Co-Al系錯合氧化物被覆型多色性粉體 之雲母表面上之錯合氧化物之金屬調配比例,可為二氧化 鈦50至91.5% ,鈷7.5至49% ,鋁1至20% ,且所得之
Ti-Co-Al系錯合氧化物被覆型多色性粉體之外觀顏色,呈 ----------I-----裝 il — 丨! — 訂.! I 線 (請先閱讀背面之注意事項再填寫本頁) 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 7 311253 473519 經濟部智慧財產局員工消費合作社印製 主
綠色至青綠色 A7 五、發明說明(8 ) 現換算成予特(Hunter )之Lab值,a為-20.00至5.〇〇、b 為〇至30.00、L為40.00至70.00之黃綠色。 又’構成被覆在Ti-Co-Al系錯合氧化物被覆型多色性 粉體之雲母表面上之錯合氧化物金屬調配比例,可為二氧 化欽50至96.5% ’鈷2.5至7.5% ,鋁1至47.5% ,且所 得之Ti-Co-Al系錯合氧化物被覆型多色性粉體之外觀顏 色’呈現換算成予特(Hunter )之Lab值,a為-20 ·〇〇至 5.00、1)為-30.〇〇至_8.〇〇、[為5〇00至8〇〇〇之青色。 再者’構成被覆在Ti-Co-Al系錯合氧化物被覆型多色 性粉體之雲母表面上之錯合氧化物金屬調配比例,可為二 氧化鈦 50 至 72.5% ,鈷 7.5 至 30% ,鋁 20 至 42.5% ,,”
’ i>S 及二氧化鈦50至98% ,鈷1至2.5% ,鋁1至49% ,且 所得之Ti-Co-Al系錯合氧化物被覆型多色性粉體之外觀 顏色’呈現換算成亨特(Hunter)之Lab值,a為_2〇 〇〇 至5_00、b為-8.00至〇、L為40.00至85 〇〇之綠色至青綠 色。 上述之結果以下表1表示。 1% 至 2.5% 而且,第3圖顯示表1圖示化之圖 藉由改變Ti02-Al-Co之調配比率,發招7 β , I現可得到色調名 私紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 311253 •丨;----------%裝----------:訂 (請先閲讀t·面之注意臬項再填寫本頁)
經濟部智慧財-1局員«I.消費合作社印製 A7 --------—-B7______ 五、發明綱(9 ) . :~ -- 黃綠色至青色廣泛範圍中之外觀顏色。亦即,㈣統之外 觀顏色藉由改變Tl〇2_A1_co之調配比率,使外觀顏色產生 微妙之變化》因此,雲母表面上被覆此種Ti〇2_Ai_c〇之 Τι-Al-Co系錯氧化物被覆型多色性粉體顯現依據觀看之角 度產生色彩變化之獨特性f。此處再參照第2圖,以說明 顯示本發明之Ti-Co-Al系錯合氧化物被覆型多色性粉體 之多變色性。 如前述般,本發明之Ti-C〇_A1系錯合氧化物被覆型多 色性粉體10係在中心存在有雲母i 2,於其外圍形成二氧 化鈦層14’接著在其外圍形成c〇_A1系錯合氧化物層16。 在該Ti-Co-Al系錯合氧化物被覆型多色性粉體1〇之 上照射白色光18,且以Co_A1系錯合氧化物層16反射— 部份之白色光18,形成反射光20。該反射光20可呈現
Ti-Co-Al系錯合氧化物被覆型多色性粉體1〇原有的外觀 色色調。
Co-A1系錯合氧化物層16表面上反射之白色光is在 Ti-Co-Al系錯合氧化物被覆型多色性粉體1〇内部前進, 藉由在二氧化鈦層14之表面以及雲母12表面之屈折率大 幅度的變化產生反射光。因此,二氧化鈦層14之反射光 22與雲母12表面處之反射光24係藉由二氧化鈦層14之 層厚度造成之光路徑差異產生特定色調之反射干擾光 26 〇 由無法觀察之反射干涉光26之角度,可藉由反射光 20觀察到Ti-Co-Al系錯合氧化物被覆型多色性粉體1〇之 — — — — — — — — — — i I I HI I — — — — — — — — ^ (請先閱讀背面之注意事項再填寫本頁) 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 9 311253 473519 經濟部智慧財產局員工消費合作社印製 A7 五、發明說明(10 ) 原有色調’錢察反射干涉光26之該,可相該反射干 擾光26與一般之反射光2〇混合狀態之顏色。 因此本發明之特徵為c〇_A1系錯合氧化物層16之透明 度非常的南,幾乎不會受反射干涉光26之影響,反射干涉 光26之色調可藉由調整被覆在雲母12表面之二氧化鈦層 14之層厚度操作,本發明中之Ti_c〇_A1系錯合氧化物被 覆型多色性粉體10可藉由組合外觀色、及反射干涉光26 之色調’得到各種不同色調之多變色性。 又’不在前述TiCVAl-Co調配比率範圍内之Ti_c〇_A1 系錯合氧化物被覆雲母,雖然在其多變色性之面上會有劣 化之現象’但由於其具有美麗之光澤及色調,因此亦可當 作顏料使用。 此處說明使用二氧化鈦及鋁酸鈷當作本發明Ti_c〇_A1 系錯合氧化物被覆型多色性粉體之雲母表面被覆之物質之 理由。本發明之多變色性粉體中使用二氧化鈦之理由為前 述之二氧化鈦被覆在雲母上會產生反射干涉色。又使用銘 酸銘之理由為在二氧化鈦上被覆鋁酸鈷,最外層之鋁酸録 對於濃酸、濃鹼為安定’且具有優良之耐熱性,及高的透 明性,由於包含具有高彩度之青色顏料,因此藉由與二氧 化鈦被覆雲母之干涉色組合’可觀察到高的多變色性。 再者一氧化欽層14及Co-Al系錯合氧化物層16雖然 並沒有限定必須連績,但可在二者間設置比二氧化鈦層屈 折率低之層,以改變控制光學之氧化鈦膜厚度,使反射干 涉色之色調改變,由於會使反射干涉色之色調明顯的降 ------------裝·! - *---^訂 *17--- (請先閱讀背面办注意事『項再填寫本頁) 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 10 311253 473519 經濟部智慧財產局員工•消費合作社印製 A7 五、發明說明(11 / 低’因此為了得到多變色性,應盡量避免設置此層。 又,雲母上之被覆順序由内側向外較好為雲母、 化鈦、鋁酸鈷。例如’以雲母、鋁酸鈷、二氧化鈦之順 =覆所產生之反射干涉色對於多變色性會有顯著之不良影 .,而且’此Ti-Co-A1系錯合氧化物被覆型多色性粉體因 -為形成無機化合物被覆之粉體,因此具有極佳之耐光性、 及優良之長期安定性、化學安定性之特徵。 、 又本發明者發現當將氧化欽被覆雲母與顏料或染料單 純的混合時,顏料或染料具有與氧化欽被覆雲母所產生之 反射干涉色成互補色關係之色調,因此顯示非常大之變色 性’可簡單的製造,且發現所選用之材料具有充分之耐光 性及長期安定性,因此完成本發明之混合型多色性粉體。 本發明之多色性粉體之特徵為以在被覆於雲母表面上 之氧化鈦上產生反射干涉色之氧化鈦被覆雲母與具有與前 述氧化鈦被覆雲母產生之反色干涉色呈互補色關係色調之 顏料或染料混合》 氧化鈦被覆雲母與顏料或染料混合之方法可使用過去 週知之各種方法❶ 此處之多色性粉體中,氧化鈦被覆雲母所產生之反射 干涉色為了得到明顯強的干涉光,因此以金色者較佳。此 時’使用對金色呈現互補色之青色色調顏料或染料較佳。 又本發明之多色性粉體中,顏料或染料較好包含姑 藍,以得到高的多變色性 ^張尺度適用中國國家標準(CNS)A4規格(21G x 297公髮) -裝! —訂---------線 (請先閲讀背面之注意事項再填寫本頁) 473519 A7 經濟部智慧財產局員工消費合作社印製 五、發明說明(i2 又本發明之多變色性粉體中,係使用無機系顏料令 ’、前述之氧化鈦被覆雲母混合之顏料或染料,前述 :料之調配量較好為2.5至3一,以得到高的:、變: 又本發明之多色性粉體中,使用有機系顏料或 作與前述氧化欽被覆雲母混合之顏料或染料,前述^有: 系顏料或染料之調配量較好在〇 5 較高之變色性。 · ί里/"以得到 ▲又本發明之多色性塗裝體之特徵係在基材上塗佈含 前述多色性粉體之組成物。 使用本發明之多色性粉體當作顏料時,可藉由將本發 明之多色性粉體適量的調配在塗料組成物中使用。塗料龟 合物中之多色性粉體調配量’視使用該組合物之對象而異 並沒有特別限定’但相對於組成物之總量通常較好為5至 35重量%。多色性粉體之調配量低,會降低其遮蔽力,調 配量過多時,多色體粉體在組成物中之分散不均,塗裝體 之外觀產生不整齊’組成物黏度增加而影響作業或印刷適 性等不良結果。 所用之塗料組成物並沒有特別之限制,但可配合黏接 劑樹脂、溶劑等一起使用。黏接劑樹脂,採用可以將多色 性粉體穩定地黏接在基材上的樹脂,塗料組成物塗裝於基 材上之後,該組成物中之溶劑揮散而能使多色性粉體以包 埋狀態在基材上形成被膜者。黏接劑樹脂考慮和基材之適 性、所形成被膜之強度、膜厚等加以選擇但並無特別限制 t紙張尺度適用中國國家標準(CNS)A4規格άΐ〇 χ 297公爱) 12 311253
請-先 閱 讀 背, 之· 注 意 事- 項^I·:裝 頁I 訂 i 473519
-------1—---*裝-------訂---------線 (請先閱讀背面之注意事項再填寫本頁) 13 311253 473519 A7
473519 經濟部智慧財產局員工.消費合作社印製 過濾
A7 ---- B7__ 五、發明說明(15 ) 而言’印刷方法有凸版印刷’凹版印刷,照相凹版印刷, 網版印刷,膠版印刷,平版印刷,油墨注塑印刷,靜電印 刷等。另外’毛刷,喷刷,滾刷,模板塗,靜電刷,澆塗, 浸塗’輥刷,喷塗等各種塗裝方法也可以採用》 ,而且本發明之多色性塗裝體係將含有被覆於雲母表面 •上之氧化鈦可產生反射干涉色之氧化鈦被覆雲母之组成物 —塗佈在基材上,且在上述含有氧化鈦組成物上塗佈含有與 上述氧化鈦被覆雲母所產生之反射干涉色呈互補色關係之 色調之顏料或染料之透明著色組成物,或者在基材上塗佈 混合有可使被覆在雲母表面上之氧化鈦產生反射干涉色之 氧化鈦被覆雲母及含有與前述氧化鈦被覆雲母所產生之反 射干涉色成互補色關係色調之顏料或染料之透明色組成物 所得到之組成物’而藉由相對於入射光之觀察角度檢查觀 察色調之差異。 [實施例] 實施例1 依據第1(c)圖’製造本發明一實施例之Ti_c〇_A1系錯 '合氧化物被覆型多色性粉體。 • 亦即’相對於100.00重量份之二氧化鈦被覆雲母,添 加1000重量份之水,且攪拌分散。接著將溶解在水中之 11.89重量份之水合氣化钻(c〇Cl2· 6H2〇)、72 27重— 之水合硫酸鋁(Al2(S〇4)3· 14Η2〇)之水溶液逐滴滴加於 其中’且在攪拌下升溫至80°C。接著,滴加2莫爾/升之 氫氧化鈉水溶液(NaOH )’將溶液之pH值調整至9 、 裝--------訂---------線 (請先閱讀背面之注意事項再填寫本頁) 473519 經濟部智慧財產局員工消費合作社印製 A7 B7 五、發明說明(16 ) 產生之Ti-Co-Al系錯合氧化物被覆雲母,經水洗滌,在 15〇°C下乾燥12小時後,於900°C之溫度燒成1小時。 再者,所得Ti-Co-Al系錯合氧化物被覆型多色性粉體 為在二氧化鈦67.6% 、鈷4·7% 、鋁27.7%之錯合氧化物 調配莫爾比例下,具有水色之外觀,且會產生黃色干涉色 者。 實施你丨? 依據第1(c)圖,製造本發明一實施例之Ti-Co-Al系錯 合氧化物被覆型多色性粉體。 相對於100.00重量份之與實施例1之二氧化鈦含有量 (被覆雲母之二氧化鈦層厚度)不同之二氧化鈦被覆雲 母,添加1000重量份之水,且攪拌分散。接著將溶解在水 中之12_1〇重量份之水合氣化鈷(c〇Cl2 · 6H20)、73.53 重量份之水合硫酸鋁(A12(S〇4)3· 14H2〇)之水溶液逐滴 滴加於其中,且在攪拌下升溫至80°C。接著,滴加2莫爾 ’升之氫氡化納水溶液(NaOH )’將溶液之pH值調整至9。 過濾、產生之Ti-Co-Al系錯合氧化物被覆雲母,經水洗滌, 在l5〇°C下乾燥12小時後,於90(rc之溫度燒成i小時。 而且’所得Ti_c〇_A1系錯合氧化物被覆型多色性粉體 係與實施例1之二氧化鈦層厚度不同者,為在二氧化鈦 616%、鈷4.7%、鋁27.7%之與實施例i相同之錯合氧化 物調配莫爾比下’具有水色之外觀,且會產生紅色干涉色 者。 - - - - ---------------Ί ^ J I I I I I I (請先閲讀r面之注意幕項再填寫本頁) 實施你丨3
16 311253 473519
經 濟 部 智 慧 財 產 局 員 工 消 費 合 作 杜 印 製 A7 B7 五、發明說明(17 ) 依據第1(c)圖’製造本發明一實施例之Ti_c〇_A1系錯 合氧化物被覆型多色性粉體。 相對於100.00重量份之與實施例1、2之二氧化鈦含有 量(被覆雲母之二氧化鈦層厚度)不同之二氧化鈦被覆雲 4母,添加1000重量份之水,且攪拌分散。接著將溶解在水 中之14.28重量份之水合氣化鈷(c〇Cl2 · 6H20)、86.22 重量份之水合硫酸鋁(AldSO4)3· 14^0)之水溶液逐滴 滴加於其中,且在攪拌下升溫至8(rc。接著,滴加2莫爾 /升之風氧化鈉水溶液(NaOH ),將溶液之pH值調整至9。 過濾產生之Ti-Co-Al系錯合氧化物被覆雲母,經水洗滌, 在150。(:下乾燥12小時後,於9〇(rc之溫度燒成i小時。 而且,所得Ti-Co-Al系錯合氧化物被覆型多色性粉體 係與實施例1、2之二氧化鈦層厚度不同者,且係在二氧化 鈦67.6% 、鈷4.7% 、鋁27·7%之與實施例i、2相同之錯 合氧化物調配莫爾比下,具有水色之外觀,且會產生綠色 干涉色者。 實施你丨4 '依據第〗(c)圖,製造本發明一實施例之Ti-Co-Al系錯 合氧化物被覆型多色性粉體。 相對於100.00重量份與實施例i相同之二氧化鈦含有 量(被覆雲母之二氧化鈦層厚度)之二氧化鈦被覆雲母, 添加1000重量份之水’且攪拌分散。接著將溶解在水中之 8.91重量份之水合氣化鈷(c〇cl2· 6H2〇)、54 21重量份 之水合硫睃鋁(Al2(S〇4)3· l4H2〇)之水溶液逐滴滴加於 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公爱) Π 311253 _____________裝---1----訂---------線 (請先閱讀背面之注意事項再填寫本頁) 473519
經濟部智慧財產局員工消費合作社印製 五、發明說明(18) 其中,且在攪拌下升溫至8(TC。接著,滴加2莫爾/升之 氫氧化納水溶液(NaOH ) ’將溶液之pH值調整至9。過濾 產生之Ti-Co-Al系錯合氧化物被覆雲母,經水洗滌,在 150°C下乾燥12小時後’於9〇〇〇c之溫度燒成1小時。 而且’所得Ti-Co-Al系錯合氧化物被覆型多色性粉體 係在錯合氧化物調配莫爾比為二氧化鈦73 5%、鈷3 9% 、 鋁22.6%之下’具有水色之外觀,且會產生黃色干涉色者。 實施例5 依據第1(c)圖,製造本發明一實施例之Ti_c〇_A1系錯 合氧化物被覆型多色性粉體。 相對於100·00重量份與實施例1相同之二氧化鈦含有 量(被覆雲母之二氧化鈦層厚度)之二氧化鈦被覆雲母, 添加1000重量份之水,且攪拌分散。接著將溶解在水中之 5·95重量份之水合氣化鈷(c〇cl2 · 61^0)、36.14重量份 之水合硫酸鋁(AldSO4)3· 141^0)之水溶液逐滴滴加於 其中’且在攪拌下升溫至8(rc。接著’滴加2莫爾/升之 氮氧化鈉水溶液(NaOH ),將溶液之pH值調整至9。過渡 產生之Ti-Co-Al系錯合氧化物被覆雲母,經水洗滌,在 150 C下乾燥12小時後,於900°C之溫度燒成1小時。 而且’所得Ti-Co-Al系錯合氧化物被覆型多色性粉體 係在錯合氧化物調配莫爾比為二氧化鈦80.7¾、鈷2.8% 、 鋁16.5%之下,具有水色之外觀,且會產生黃色干涉色者。 實施例6 依據第1(a)圖’製造本發明一實施例之Ti_c〇_A1系錯
----------丨 裝·- I (請先閱讀背面之注意事項再填寫本頁) 訂·· i 473519
五、發明說明(19 ) 合氧化物被覆型多色性粉體。 經濟部智慧財產局員工'消費合作社印製 將100·00重量份與實施例1相同之二氧化鈦含有量(被 覆雲母之鈦層厚度)之二氧化鈦被覆雲母,與816重量份 之氧化鈷(CoO )、24.19重量份之氧化鋁(Al2〇3)混合在 一起,於900°C之溫度燒成i小時。 而且’所得Ti-Co-Al系錯合氧化物被覆型多色性粉體 -係在錯合氧化物調配莫爾比為二氧化鈦55 6% 、鈷12 2 % 、銘32.2%之下’具有青綠色之外觀,且會產生黃色干 涉色者。 實施例7 依據第1 (b)圖’製造本發明一實施例之Ti_c〇_A1系錯 合氧化物被覆型多色性粉體。 1000重量份之水中溶解25 91重量份之水合氯化鈷 (CoCl2 · 6H20 )、27.37 重量份之水合硫酸鋁(A12(S04)3 · 14 Η: 0)、44.8重量份尿素之水溶液中,添加loooo重量 份之與實施例1相同二氧化鈦含有量(被覆雲母之鈦層厚 度)之二氧化鈦被覆雲母,升溫至1 〇〇艺,且回流4小時。 過濾所得之生成物’經水洗滌且在1 5 0 °c下乾燥1 2小時 後’於900°C之溫度燒成i小時。 而且’所得Ti-Co-Al系錯合氧化物被覆型多色性粉體 係在錯合氧化物調配莫爾比為二氧化鈦60.0% 、鈷27.5 % 、鋁12.5%之下,具有黃綠色之外觀’且會產生黃色干 涉色者。 實施例8 --------------裝--------訂---------線 (請先閱讀背面之注意事項再填寫本頁) 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公爱〉 19 311253 473519 A7 -------------- 五、發明說明(20 ) 依據第1 (c)圖’製造本發明一實施例之Ti-Co-A1系錯 合氧化物被覆型多色性粉體。 (請先閱讀背面之注意事項再填寫本頁) 亦即’相對於100.00重量份之二氧化鈦被覆雲母’添 加1000重量份之水’攪拌分散且升溫至8(rc。接著將溶 解在水中之11.89重量份之水合氣化鈷(c〇C12.6H20)、 72.27重量份之水合硫酸鋁(Al2(s〇4)3 · 14H2〇)水溶液逐 滴滴加於其中,另外滴加藉由滴加2莫爾/升之氫氧化鈉水 溶液(NaOH)而將溶液之ρΗ值調整至9之含水合氣化鈷、 水合硫酸鋁之混合水溶液。過濾產生之Ti_c〇_A1系錯合氧 化物被覆雲母’經水洗滌’在1 5(rc下乾燥i 2小時後,於 9〇〇°C之溫度燒成1小時。 再者’所得Ti-Co-Al系錯合氧化物被覆型多色性粉體 為在二氧化鈦67.6% 、鈷4.7% 、鋁27.7%之錯合氧化物 調配莫爾比下,具有水色之外觀,且會產生黃色干涉色者。 後續係檢視本發明之Ti-Co-Al系錯合氧化物被覆型多 色性粉體所示之特性。 實驗1 經濟部智慧財產局員工消費合作社印製 本發明之Ti-Co-Al系錯合氧化物被覆型多色性粉體調 配而成之塗料組成物塗佈在基材上所形成之塗裝體中,為 了使本發明之Ti-Co-Al系錯合氧化物被覆型多色性粉體 發揮充分的效果,因此進行了解基材色調之底色對其所產 生之影響。此處因為本發明之Ti_Co_A丨系錯合氧化物被覆 型多色性粉體之透明性高,因此Ti_c〇_A1系錯合氧化物被 覆型多色性粉體所有之外觀色,以及干涉色會輸給基材色 本紙張尺度適用中關家標準(CNS〉A4規格⑽χ撕公髮) 20 311253 A7
經濟部智慧財產局員工•消費合作社印製 473519 五、發明說明(21 ) 調之底色,造成Ti-Co-Al系錯合氧化物被覆型多色性粉體 具有之色調或多變色性受阻礙。 本發明者在此處檢討基材色調之底色與變色度之關 係。 首先,使用4·5重量份之硝基纖維素當作黏接劑樹脂, 且使用10_5重量份之由10至20%乙酸丁酯、5至1〇%之 _一甲笨、3至10%之乙酸乙醋、5至1〇%之甲基乙基酮、 3〇至40%之甲苯構成之溶劑’使該黏接劑樹脂與溶劑混 合’且調配4重量份之本文實施例1中呈現水色外觀色及 η色干涉色之Ti-Co-Al系錯合氧化物被覆型多色性粉 體,經分散製造成塗料組成物’該組成物此處稱之為試料 接著使用同量之與試料1相同量之黏接劑樹脂及溶 劑’將4重量份實施例2之外觀色為水色及具有紅色干涉 色之Ti-Co-Al系錯合氧化物被覆型多色性粉體調配在該 黏接劑樹脂與溶劑中,經分散製造塗料組成物,該組成物 稱之為試料2。 將此等試料1及2以刮板(間隙:110微米)塗佈在各 種顏色之色紙上’以變角測色機進行顏色測定,以測定其 變色度。 第4圖顯示測定本發明之Ti-Co-Al系錯合氧化物被覆 型多色性粉體變色度之方法說明圖。同一圖中所示之印刷 有調配本發明之Ti-Co-Al系錯合氧化物被覆型多色性粉 體之塗料組成物之被檢測物30相對之垂直轴32為基準, I-----------I -lull--訂----III — (請先閱讀背面之注意事項再填寫本頁) 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 21 311253 473519
五、發明說明(22 ) 由-45度之方向,藉由白色光光源^昭 定藉由以-25度與35度配置之受先器“、、射白色光36,以測 色,該測色值換算成Hunter之L 38、4〇受光之光顏 (請先閱讀背面之注意事項再填寫本頁) 以-25度與35度測定,在_25度|列斷。 化物被覆型多色性粉體之干涉色 Tl_Co-Al系錯合氧 觀色,而在35度下,會受到Ti_c〇乎不受影響僅觀測到外 型多色性粉體干涉色強烈影響,:::系錯合氧化物被覆 之混合物’因而判斷與該兩點所」到外觀色與干涉色 變色度越大。 色差異越大表示 該測定結果之-部份分別顯示於表2之試料工中及表3 之試料2中。又’分別將表2之ab圖顯示在第5⑷圖中, 表3之ab圖顯示在第5(b)圖中。 表2 底色1 白 L 87.7 「_.細隹_, m 2.94 b -5.56 L 61.77 -25·#· a -2.48 b -28.06 L 12506 351受光 a -6 23 b 9A 1Q 黑 18.53 0.11 -0.6 44.97 -3.2 -1.01 118.82 灰色 53.99 -1.77 1.41 52.65 -3.32 -12Λ1 121,47 *6❶1 <59.9^ 體色 87.74 -13.91 51.26 62.78 -1Β.9β 一 2§TS3 — 126-5 -10.61 47.74 氷色 67.31 -18.81 •2324 56.94 -7.04 -2M 122.42 -7.4 25.08 經濟部智慧財產局員工消費合作社印製 表3 基树色 -25B 35· #光 底色 L a b L a b L a b 白 87.7 2.94 -5.56 69·62 -10.52 -20^3 Π7.16 14.65 5.43 黑 18.53 0.11 -0.6 3S.5« 6.5 -11.02 100.14 21.78 1579 灰色 53.9» -t.77 1.41 51.64 -3S4 -14.39 108j67 18.15 12.39 觸色 87.74 -13S1 51.26 66.01 -2253 31.35 111Λ1 β.85 28.16 水色Ί 67.31 -18B1 -23.24 60.98 -1W2 -26.24 112,71 12*29 3.99 藉由表2、第5(a)圖及表3、第5(b)圖所示之基材色之 底色,可顯示相同色調之Ti-Co-Al系錯合氧化物被覆型多 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公楚) 22 311253 473519 A7 B7 五、發明說明(23 ) 色性粉體呈現出不同色調。因此可獲知對本發明之Ti-Co-Al系錯合氧化物被覆型多色性粉體特徵之多變色性之 影響。 -----!1* 裝 i I ^請先閱讀背面之注意事項再填寫本頁) 但是’由第5(a)、(b)圖可了解由具有無色彩之白色至 -黑之灰色範圍之底色基材,在-25度與35度受光所得之測 •色值有相當大之差異因此變色性高。又,可了解到由與粉 -體之物體色同色之水色底色基材,在_25度與35度受光所 1得之測色值有相當大差異而變色性高。又當使用與粉體之 物體色同色之水色底色基材時,Ti-Co-Al系錯合氧化物被 覆型多色性粉體之外觀色對底色之影響具有相乘之效果, 因此所觀察之外觀色相當鮮豔。 線· 塗佈有調配本發明之Ti-Co-Al系錯合氧化物被覆型多 色性粉體之塗料組成物之基材色調若在無色彩之白至黑之 灰色範圍’以及與Ti-Co-Al系錯合氧化物被覆型多色性粉 體之外觀色同色系統之黃綠色至藍色之青色系,可以充分 發揮本發明Ti-Co-Al系錯合氧化物被覆型多色性粉體之 效果,因此較佳。 經濟部智慧財產局員工 •消費合作社印製 ,針對此,當使用具有除前述以外之底色之基材色時, 本發明之Ti-Co-Al系錯合氧化物被覆型多色性粉體之外 觀色及干涉色會受基材底色之影響,而損害其變色性。其 他顏色之例之檸檬色如表2、第5(a)圖及表3、第5(b)圖所 示者。由第5(a)、(b)圖可發現,在-25度與35度受光測得 之測色值之差異少,會阻害本發明之Ti-Co-Al系錯合氧化 物被覆型多色性粉體特徵之變色性。 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 23 311253 473519 A7 經 濟 部 智 慧 財 產 局 員 工 消 費 合 作 社 印 製 五、發明說明(24 ) 實驗2 接著本發明者針對調配本發明之Ti_c〇_A]系錯合氧化 物被覆型多色性粉體之塗料組成物之塗佈厚度與變色度之 關係進行檢討。 以刮刀將前述實驗1中之試料丨,以不同之臈厚产下 塗佈在具有灰色規格_底色之基材上,且如前述:實驗 般’如第4圖所示般自_45度照射白色光,且將_25度與w 度受光之測色值換算成Hunter之Lab值,計算狁圖中 度與35度2點間之距離判斷其變色度,將膜之厚度加厚, 粉末之色調可在不受底色之影響下確實的變色。 第6圖顯示變色度與膜厚度之關係。如第6圖中所示, 膜之厚度不可以在極厚之範圍中,且膜厚度加厚會使後續 之變色度增大。實驗結果,當塗佈薄膜之厚度比3〇微米薄 時,發現具有在白至L:31.83a:_〇.〇lb:l86之範圍間 顏色之基材之良好變色度,當塗佈膜厚度高於3〇微米以上 時,不會文底色之影響,因此可產生在白至黑色全範圍之 高變色度。 調配本發明之Ti-Co_A1系錯合氧化物被覆型多色性粉 體之塗料組成物之骐厚度,一般之膜厚度範圍係在5微米 以上,且較好在20微米以上,且在3〇微米以上時不會受 基材色之影響’可得到最佳之變色度。 由以上之實驗1、以及實驗2之結果’塗佈有調配本 發月之Ti Co A1系錯合氧化物被覆型多色性粉體之塗料 組成物之基材色調不在無色彩之白至黑之灰色規格範圍 本紙張尺度適用t _冢標準(CNS〉A4沒格⑵G χ 297公爱 311253 ---------- (請先閱讀背面•之注意事項再填寫本頁) n n n ϋ ·
Ji I I I I .
473519 五、發明說明(25 ) 内’且無黃綠色至藍色之青色系之情況,則亦可事先藉由 上漆、繪圖及其他之著色手段將基材色著色成同色系,而 以塗佈膜厚度30微米以上塗佈調配有本發明之Ti-C〇-A1 系錯合氧化物被覆型多色性粉體之塗料組成物。 -實驗3 接著,使用實施例1使用之塗料組成物之試料丨,以 3〇微米之膜厚度塗佈在底色為白色與灰色之基材上。試料 1之塗料組成物之塗佈膜所形成底色為白色之基材稱之為 試料3,試料1之塗料組成物之塗佈膜所形成底色為灰色 之基材稱之為試料4。該試料3、4以與前述第4圖中所示 之測定方法般,自-45度方向照射白色光,且測定_25度與 35度之反射光波長分布。又使用與實施例丨中所用之雲母 欽上未被覆紹酸鈷之狀態之試料1相同之黏接劑樹脂與溶 劑之混合物當作比較對象,以與試料3、4相同之膜厚度下 塗佈在底色為白色之基材上,當作比較試料1。度之反 射光波長分布示於第7(a)圖中,在35度之反射光波長分布 示於第7(b)圖中。 因為幾乎無法檢測出干涉光,因此Ti-C〇-A1系錯合氧 化物被覆型多色性粉體所觀察之外觀色-25度波長分布, 如第7(a)圖中,試料3、4兩者之短波長側之反射率高,但 長波長之反射率低。因此,可發現短波長側之反射率與長 波長側之反射率之差異相當的大。針對此等,包含雲母鈦 塗佈膜之比較試料1會有短波長側之波長高,長波長側之 波長低之傾向,因此常波長側之反射率與短波長側之反糸 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) — ·裝!—訂----------線 (請先閱讀背面之注意事項再填寫本頁) 15 473519 A7 經 濟 部 智 慧 財 產 局 員 工 消 費 合 社 印 製 五、發明說明(26 ) 率間之差異並不會太大,而使得全體均可觀察到白色光。 又’因為檢出強的干涉光,因此Ti-Co-Al系錯合氧化 物被覆型多色性粉體所觀察到之外觀色與干涉色之混合顏 色在35度之波長分布,如第7(b)圖般,試料3、4兩者之 短波長側之反射率低’但長波長之反射率高。因此,可發 現短波長側之反射率與長波長侧之反射率之差異相當的 大。此等對雲母鈦塗佈膜之比較試料丨會有短波長侧之波 長低,長波長侧之波長高之傾向。 由該第7(a)、(b)圖檢討變色性,可發現試料3、4同 時會由青色系統之顏色變化至黃色至橙色之顏色,且以目 視可確定變色度非常大。相對於此,比較試料〗為自白色 之顏色變化至黃色至橙色之顏色,以目視可確定由白色變 成黃色至橙色之顏色,變色度不足而難以觀察。 實驗4 使用實施例1之塗料組成物之試料丨,以3〇微米之膜 厚度塗佈在底色為白色之基材上。試料丨之塗料组成物之 塗佈膜所形成底色為白色之基材稱之為試料5。又於與試 料1相同之黏接劑樹脂與溶劑中混合與實施例丨具有相同 外觀色與干涉色但Ti〇2、Co、A1調配比率不同所構成之 實施例4及5,以與試料5相同膜厚度下塗佈在底色為白 色之基材上。含實施例4之塗佈膜所形成之基材稱之為試 料6’且含實施例5之塗佈膜所形成之基材稱之為試料7。 該試料5至7以前述第4圖所示之測定方法,自_4 5 度之方向照射白色光,自-25度至65度以每5度之間隔接 本紙張尺度適用中國國家標準(CNS)A4規格(21〇 x 297公釐) 26 311253 (請先閱讀背面·之注意事項再填寫本頁) 裝 ♦ 473519 A7
經濟部智慧財產局員工消費合作社印製 五、發明說明(27 ) 受反射光’將其測色值換算成Hunter之Lab值,檢視其變 色度。結果列於下表4中。 表4 - fer«LA H«L-7 iR光角 L a b L 籲 b L a b -25 64.56 -1Λ5 -26.73 66*22 -2.91 -23^3 67 95 -2 -21.59 «20 64.99 -2.05 -26.34 66.71 -3.05 -23.49 68.41 ^2.14 -21.17 H5 65.45 -2.17 -25.Β1 67.34 -3 13 -22.72 69 -994 -20.55 -10 66.17 _ -2.1 a -24.35 68.25 -3.27 -21 57 69 82 -23 -IS.55 -5 67.225 '2.33 .-23.55 69.55 -3 27 -1991 71 m -2 4 -17.99 0 88.9 -2.5 -21.5 71.47 -3.38 -17.49 73.03 -2.58 -15.58 5 71.37 -2.69 -18.38 74.45 -3 58 -13.76 76 〇β 286 -Ι1Λ4 10 75.18 *2.98 -13Β 78.75 -3 81 •85 8052 -3 28 -6.51 15 60.92 __ *3.49 *β·64 85.1 -4.23 -t.04 87.11 -3.84 1J6 20 88.97 -4.1 β 2.61 93.72 -4.89 843 96 29 •477 11.13 __ 25 100.78 UM 106.05 -5.75 20.26 109 49 -6.14 23.68 30 11752 -6·5β 28.06 122.83 -6,6 32 127 09 -7.55 36.16 _ 35 147.35 -7.βϊ 39.33 153.43 -7.16 41.33 159J6 -8.25 4549 40 192.56 -6.34 42.63 192.93 -5.77 43.32 203 88 -6 57 46.16 45 210.60 •5.21 39.15 216.92 -5.37 42.34 21065 -5.67 41.8 —5〇 201.96 _ -6.77 42.9β 190.64 42.98 196.14 -75 4537 55 159Ό8 -9.15 39.99 155.38 -8.32 39.45 157 67 -9.41 42.73 60 129.36 -9.27 31.28 12&.52 •8.S3 31.14 130.3 -9.12 33.B5 6S 115.51 -8*73 22.85 116 -8.3 23.46 117.74 -8.55 25.84 由表4可明顯的看出,試料5至7自_2 5度增加角度而 使Lab值產生變化’可理解角度之變化產生變色。特別是 變色度係考量與-25度下之值之差異,且顯示在45度附近 之變色度最大,當超過45度以上之角度時,會再回復到原 來之顏色。因此,考量與-2 5度最大之差異,可理解到本 發明之Ti-Co-Al系錯合氧化物被覆型多色性粉體具有多 大之變色性。 實驗5 使用實施例1之塗料組成物之試料1,以3〇微米之膜 厚度塗佈在底色為白色之基材及灰色之基材上。試料 塗料組成物之塗佈膜所形成底色為白色之基材稱之為試料 8、試料1之塗料組成物之塗佈膜所形成底色為灰色之基 -------------裝--------訂---------線 (請先閱讀背面之注意事項再填寫本頁) 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 27 311253 473519 A7 ------------B7________ 五、發明說明(28 ) 稱之為試料9又於與試料1相同之黏接劑樹脂與溶劑中 混合具有與實施例i相同外觀色及不同干涉色之Ti〇2、
Co、A1調配比率相同所構成之實施例2及3,在與試料8、 9相同膜厚度下塗佈在底色為白色與灰色之基材上。含實 施例2之塗佈膜所形成之底色為白色之基材稱之為試料 10,且含實施例2之塗佈膜所形成之底色為灰色之基材稱 之為試料11’含實施例3之塗佈膜所形成之底色為白色之 基材稱之為試料12,且含實施例3之塗佈膜所形成之底色 為灰色之基材稱之為試料〗3。 該試料8至13如前述之實驗4般,以前述第4圖所示 之測定方法’自-45度之方向照射白色光,自_25度至65 度以母5度之間隔接受反射光,將其測色值換算成Hunter 之Lab值而檢視。 底色為白色之基材之試料8、10、12之結果列於下表5 中’表5轉換成ab圖’示於第8(a)圖中。又,底色為灰色 基材之試料9、11、13之結果列於下表6中,表6轉換成 ab圖,示於第8(b)圖中。 (請先閱讀背面•之注意^項再填寫本頁)
經濟部智慧財產局員工消費合作社印製 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 28 311253 473519 A7 B7
五、發明說明(29 )表5 K»8 K»1 Q K料 1 2 受光角度 L a b L a b L 塞 b -25 64.56 -1.95 -26.73 70.2 -12.47 -18.28 66.75 157 -18i •20 64.99 -2.05 -26.34 70.52 -12.44 -17.78 66.89 1.66 -18.3 -15 65.45 -2.17 "25.81 70.8 -12.22 -17.34 67.11 1.63 -18.19 -10 66.17 -2.18 -24.95 71.17 -11.89 •16.78 67.46 1.43 -17.98 _5 67.225 -2.33 -23.55 71.64 -11.19 -16.32 68.03 1.04 -17.64 0 68.9 -2.5 -21.5 72.32 -10.02 -15.B2 69.04 0.13 -16.87 5 71.37 -2.69 -18.36 73.39 -8.34 -15.06 70.61 -1.26 15.8 10 75.18 -2.98 -13j6 75.08 •5.57 H4.02 73.11 -3.3Ϊ -14.3 15 80.92 -3.49 -6.64 77.79 -1.62 -12.3 77,08 -6.47 *12.33 20 88.97 -4.18 2.61 &2.2 3.83 -9.44 83.05 -10.79 -10.24 25 100.78 *5.3 14.68 89.15 10.4 -S.14 92.42 -16.34 -8.23 30 117.52 -6.56 28.06 101.32 17.56 1.39 106別 -21.91 -6.7 35 147.35 -7.83 39.33 124.77 21·β4 9.8 130.95 -23.8 -4.38 40 192.56 -6.34 42.63 177.73 19.76 18.91 178.55 •19.55 t.44 45 210.60 -5.21 39.15 203.41 15.41 22.82 213.89 -14,83 5.86 50 201.96 -6.77 42.98 ΊΒ6.43 18.21 22.6 184.23 -17.91 0.97 55 159.08 -9.15 39.99 138.69 18.46 17.11 139.76 -21.69 -7.13 60 129.36 -9.27 31.28 111.34 15.28 10.65 115.27 -21.9 -12.17 65 115.51 -8.73 22.85 100.1 11.35 5.15 102.83 -20.05 -14.32 -----------------(請先閱讀背面之注意事項再填寫本頁) 表6 試軲9 K«1 1 3 受光角 L a b L a b L a b -25 47.59 -3J3 -22.95 50.59 -10.19 -19.08 4&.01 -3.82 -18.26 -20 4β.5β -3.22 -21.7 51.1 -9.74 -18.43 49.39 -3.91 -17.84 -15 49.64 -3.31 -20.2 51.51 -9.13 -17.82 49.49 -4.05 -17,35 -10 51.3 -3.36 -18.16 52.28 -8.2 -16.98 50.eS -4.49 -16.52 -5 53.6 -3.47 -15.3 53.31 -6.78 -16.03 52.23 -5.46 -15.4 0 56.95 -3.78 -11.25 54 J3 -4.76 -14.75 54.23 -6.63 -14.08 5 61.69 -4.18 -5.8 57.08 -Γ94 -13.09 57.27 -8.47 -12.15 10 67.92 -4.67 U5 60.25 1.91 -10.92 61.58 -11.07 -9.93 15 76.42 -5.36 10.07 64.73 6.57 -7.91 67.4 -14.42 -7.72 20 87.12 •6.17 20.14 71.2t 12.13 -3.88 75.75 •18.54 -5.61 25 101.54 -7.25 31.35 80.47 17J2 1.15 87.27 -22.79 -4.18 30 121.21 -8.13 40.74 95.95 22.66 7.52 104.91 -25.73 -3.02 35 155.3 -8.31 46.1 123.73 23.37 14.32 132.02 -24.48 -0.57 40 191.73 -7.3 46.13 170.8 20.78 20.89 172.43 -19.77 3.43 45 208.08 «7.63 43.89 197.64 17.68 23^8 193.99 -16J1 4.8t 50 191.26 -7.53 45.45 181.92 18.B2 25.05 181.97 -17.19 3.71 55 157.29 -9.42 43.56 141.16 19.36 22.11 144.09 -20.71 -2.B1 60 ~127.85 -10.36 38.06 109.57 17.75 18.18 117.12 -23.55 -8.87 65 112.93 -10.39 Γ 31.46 95.43 14.79 14.15 10t.11 -23.93 -12.09 由以上之結果可了解具有相同之外觀色,但二氧化鈦層 之厚度不同者會有不同之變色性。因此,可理解其變色性 大。 實驗6 線. 經濟部智慧財♦產局員r消費合作社印製 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 29 311253 A7 五、發明說明(30 ) 通常,當基材上塗佈之塗料藉由 π± „%有之角度觀測其變色 夺,先源之位置與觀察之位置大 177巧不改變,且大容籍 由轉動基材面而觀察。此包含 Μ人手握住基材觀察之 況,照明或其他光源均固定之情況,轉動頭部改變觀察角 度與轉動手上握住之基材比較’以較容易之一種進行。此 狀癌下,由於衡量光源之仂罟、極& , 尤愿之位置觀察位置等均不動,發現 照射光之入射角度與由基材之反射光所觀察到之受光角度 之總^均維持-定。如此’在入射角與受光角之總合維持 在一定之狀態下,可充分發揮其變色度。 第9圖為顯示實驗6之測定方法概要之說明圖。 如第9圖中所示之白色光源42之光軸46,與受光器 44之受光方向軸48之角度總合固定在45度,基材50以 相對於地面之垂直軸’以自_25度傾斜到65度之受光器44 受光,將反射光之測色值換算成Hunter之Lab值,測定其 變色度°測定之對象係使用前述實驗5中所用之試料8至 13 ° 底色為白色基材之試料8、10、12之結果列於下表7 中’將表7轉換成ab圖,示於第10(a)圖中。又’底色為. 灰色基材之試料9、11、13之結果列於下表8中’將表8 轉換成ab圖,示於第10(b)圖中。 請 先 閱 讀. 背 面. 之 注 意 事-項 再 寫驻 頁 訂
經濟部智慧財產局員工消費合作社印製 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 30 311253 473519 A7 B7 五、發明說明(31 ) _VMS smi 〇 K«1 2 受光角 L a b L a b L a b -25 63.81 -3.17 -2626 67.64 -9.47 -22.02 65.78 -0.62 -19.22 -20 64.63 -2.96 -26.4 6Θ.77 -9.88 -21.47 66.39 0.01 -19.03 -15 65.15 -2.81 -26.31 69.46 -10.06 -20.73 66.79 0.51 -18.75 -10 65.77 -2.58 -25.7 70.13 -10.11 -19.91 67.11 0.89 -18.43 -5 66.89 *2.47 -24.33 70.91 -9.67 -18.86 67.79 0.86 -17.93 0 69.15 -2.5 -21.35 72.31 -8.3 -17.59 691 -Λ01 -16.67 5 74.53 -2.71 -14.51 74.81 -4.76 -15.4 72.68 -2.68 -14.4 10 66.2d -3.22 -0.23 80.52 2.59 -11.71 81.41 -9.13 -10.01 15 112.87 -4.39 25.33 96.11 15.36 -4.88 103.69 -21.26 -3.31 20 177.07 -4.28 40.17 15423 20.23 2.84 163.78 -26.1 2.15 25 162.43 -4.78 41.79 138.24 21.99 1.71 146.42 -27.42 1.21 30 106.34 -4.12 20.06 91.94 13.41 -6.72 97.97 -19.03 -4.87 35 82.88 -3.01 -4.87 78.9 0.82 -13.12 7B.87 -7.04 -11.72 40 72.9 -2.43 -17.73 74.29 -5.8 -16.85 71.74 -1.5 -16,09 45 68.87 -2.28 -23.75 72.44 -8.66 -19.13 69.18 0.59 -16.48 50 67.57 -2.34 -26.65 72.02 -9.83 -20.84 68.52 1.2 -19.94 55 67.58 -2,54 -28.15 72.23 -10.25 -22.16 68.96 1.03 -20.81 60 68.39 -2.92 •28,76 73.34 -10.47 -23*27 69.97 0.46 -21.22 65 69.46 -3.46 -28.64 74.01 -10.49 -23.5 71.21 -0.26 -21.07 --------------裝--- (請先閱讀背面之注意事項再填寫本頁) 表 訂- K料9 K料1 1 K«1 3 受光角 L a b L a b L a b -25 45.96 -4.19 -24,86 49.36 -10,37 -21.06 4S.32 -4.77 -20.4 -20 46.64 -3.94 -24.34 50.07 -10^6 -20.66 48.69 -4.39 -19.97 -15 47.6 -23.18 50.77 -9J8 -19.73 49.09 -4.07 -19.33 -10 49.02 -3.58 -21.44 51.55 -9.22 -18.71 49.93 -4.22 -18.21 -5 51.54 -3.55 -18.2 52.84 -7.67 -17.21 51.6 -4*91 -16.57 0 56.08 -3.71 -12.39 55.16 -4.54 -15.06 54.92 -6.88 -13.84 5 64.45 -3.98 -2.39 59.43 1.56 -12.12 6f.S6 -1*1·,6 - 9.42 10 80.18 -4.76 14.85 68.48 12*26 一 7.55 76.33 19.15 -3.76 15 108.15 -5.44 36.52 86.69 26.12 -1.39 107.34 -29.02 1.49 20 164.49 -5.03 44.94 147.36 28.58 4.5 161.5« -2B.78 Λ 22 25 161.67 -5.41 46.56 mn 30.68 3.52 136.17 -27.98 2.B3 30 106.47 -5.67 36.18 83.9 24.54 -2.74 69.98 -24.1 -t.06 35 78.75 -4.57 12.72 66.27 9.98 -8.92 68.37 -14.69 -6.89 40 63.93 -3.85 -4.14 58.57 0.1 -13.48 52.24 -8.69 -12.25 45 56.08 -3.47 -14.37 55.03 -5.32 -16.61 53.54 -5.66 -tG.09 50 52.3 -3.3 •20.16 53.46 -8.05 -18.87 51.51 -4.36 *18.67 55 50.73 -3.39 -23.64 53.12 -9.57 -20,62 51.06 -3.98 -20.32 60 50.49 —3-69 -25.57 53.47 -10.44 -21.78 S1.44 -4.28 -2Ϊ.38 65 50.82 -4.07 -26.54 54.2 -10.96 -22.58 52^9 -4.91 •21.75 經濟部智慧財•產局員·工消費合作社印製 由上述之結果可確定,當照射光之入射角度與由基材 之反射光觀察到之受光角度之總合維持一定,在後續之狀 態下觀察基盤色時,本發明之Ti-Co-Al系錯合氧化物被覆 型之多色性粉體確實具有大的變色性。 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 31 311253 473519 Α7 Β7 五、發明說明(32 ) 實驗7 前述實施例1中所得之本發明Ti_c〇_A1系錯合氧化物 被覆型之多色性粉體所具有之多變色性,進行比較實驗是 否需被覆Ti-Co-Al系錯合氧化物才可得變色性。 比較之對象係使用雲母鈦(比較例1 )、鈷被覆雲母(比 較例2 )、銘被覆雲母(比較例3 )、姑被覆雲母欽(比較例 4 )、铭被覆雲母鈦(比較例5 )、及僅Ti-Co-Al系錯合氧 化物(比較例6 )。此等比較例中含有之雲母表面上所被覆 之一氧化鈦、姑、铭等各種金屬之量係調整到與實施例1 中包含之各金屬量相同。 而且’色調之比較,係將各被檢物以下表9中所示調 配成組成物,以刮刀將組成物以30微米之膜厚度塗佈在黑 色紙上,所得之色紙經乾燥後’如第4圖所示般,自_45 度照射光線’在-25度及35度下以肉眼進行觀察。因此, 以肉眼觀察之顏色變化良好則評價為〇,顏色之變化務有 不良變化則評價為△,顏色沒有變化則評價為χ 。 (請先閱讀背面·之注意t項再填寫本頁) 經濟部智慧財產局員工消費合作社印製 表9 被檢物 15重量% 硝基纖維素 10重量!% 丁基溶纖素 10重量% 石油腦 20重量% 環己烷 45重量% 結果示於表1 〇中。 本紙張尺度適用中國國家標準(CNS)A4規格(210 χ 297公釐) 311253 32 473519 A7 B7
五、發明說明(33 )
實施例1 tbfe例 1 (πο2+雲 母) t嫩例2 (Co+雲母) 罐歹丨J3 (A1+雲母) t嫩例4 (Co+Ti02 +雲母) 5 (Α1+Ή02+ 雲母) 匕嫩例6 (A1+CO+-11(¾) -25度 觀察色 青色 白色 茶色 白色 綠色 白色 青色 35度 觀察色 黃色 黃色 茶色 白色 黃色 黃色 青色 變色度 〇 Δ X X Δ Δ X 由表10可明白得知,Ti-Co-Al系錯合氧化物被覆型之 多色性粉體,與同一金屬比之僅錯合氧化物,或者為中間 體之錯合氧化物被覆雲母有不同色彩,特別是相對於含有 Ή、Co、A1之—種或兩種金屬之錯合氧化物被覆雲母中所 無法觀察到之色調多變色性,Ti_c〇_A1系錯合氧化物被覆 型多色性粉體可觀察到清楚之色調多變色性。據此,可了 解本發明之Ti-Co-Al系錯合氧化物被覆型之多色性粉體 係藉由將Ti、Co、A1三種金屬之錯合氧化物被覆在雲母 之上而得到特殊色調及多變色性。 -下面列舉本發明之調配例,但本發明並不受此等調配 例之限制。而且,若沒有特別限定,則調配量係表= .% 。 夏置 遇配例1 一麗相凹版印劁油黑
Tl_C〇_A1系錯合氧化物被覆型多色性粉體30.0% 乙烯-乙酸乙烯酯共聚合樹脂 7 5% 氣化聚丙烯 55 甲苯 各紙張尺度適用中國國家標準(CNS)A4規格⑵〇 χ 297公爱) 311253 ------!_!-裝-----ί — 訂 ----— ! 線 (請先閱讀背面之注意事項再填寫本頁) 經濟部智慧財I局員Μ消費合作社印製· 473519 A7 B7 _ 五、發明說明(34 ) 28.0 乙酸乙酯 8.5 甲基乙基酮 17.0 異丙醇 2.5 聚乙烯臘 0.8 靜電防止劑 0.2 調配例2 照相凹版印刷油墨
Ti-Co-Al系錯合氧化物被覆型多色性粉體15.0% 聚醯胺樹脂 15.0 松脂 4.0 頌基纖維素 3.0 異丙酵 46.0 甲苯 10.0 聚乙烯臘 0.8 調配例3 照相凹版印刷油墨
Ti-Co-Al系錯合氧化物被覆型多色性粉體20.0% 硬化松脂 15.0 石油系樹脂 1〇 〇 甲苯 55.0 調配例4 照相凹版印刷油墨
Ti-Co-Al系錯合氧化物被覆型多色性粉體3〇 〇% 确基纖維素 100 丁基溶纖素 10 0 石油腦 250 裝 i — (請先閱讀背面•之注意事項再填寫本頁) M5. 經濟部智慧財產局員工消費合作社印製 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 34 311253 經濟部智慧財•產局員Μ消費合作社印製 473519 A7 _ B7 五、發明說明(35 ) 環己烷 25.0 調配例5 照相E?版印刷油墨
Ti_Co-Al系錯合氧化物被覆型多色性粉體η.〇〇^ 乙烯-乙酸乙烯酯共聚合樹脂 7.2% 氯化聚丙婦 5.8 甲苯 58.0 乙酸乙醋 110 異丙醇 3,0 聚乙稀臘 0.8 靜電防止劑 0.2 調配例6 網版印刷油暴
Ti-Co-Al系錯合氧化物被覆型多色性粉體15.0% 丙烯酸系樹脂 20.0 石油腦 35.0 丁基溶纖素 30.0 調配例7 網版印刷油畧
Ti-Co-Al系錯合氧化物被覆型多色性粉體15.0% 硝基纖維素 15.0 環己酮 40.0 異佛爾酮 10.0 石油腦 10.0 二丁基酞酸酯 10.0 绸配例8 網版g卩麻丨油黑
Ti-Co-Al系錯合氧化物被覆型多色性粉體20.0% ^--------t---------線 (請先閱讀背面之注意事項再填寫本頁) 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 35 311253 473519 五、發明說明(36 ) 硝基纖維素 20.0 45.0 10.0 5.0 環己酮 異佛爾酮 (請先閱讀背面,之注意事項再填寫本頁) 二辛基駄酸酯 下面檢測本發明之混合 &夕色性粉體所示之特性。 f 驗 8 了1土 首先相對於產生金色千 干涉色之氧化鈦被覆雲母,如下 表η中所示,將無機系顏料之添加量在1〇、25、5〇、 10 ' 25、50重量%間變化,還有將有機系顏料 料之添加量在0.50、i 〇 ' a Λ 1Λ _ 例尔示 υ 3·0、10重量%間變化,且使用 小型粉碎裝置混合,將1公克之各種混合粉末添加於15 公克之頌基纖維素漆料編號第6341ΤΜ(武藏塗料株式會社 製造)中,以分散器授拌且分散,以到刀(間隙·· 101微 米)將該塗料塗佈在白黑遮蓋力試驗紙上,製成塗裝體。 經濟部智慧財產局員工消費合作社印製 將白色光照射在上述之塗裝體上,相對於上述之白色 入射光,改變觀察之角度,且以目視觀察顏色變化,色相 變化愈大則判定彩度愈高,且前述之色相變化最大,可良 好觀察彩度高者,而判定顏料或染料之添加量。 下表11中所示之4種無機系顏料在目視下,金-青色 之2色性最大,且觀察到彩度高者係在添加量為1 〇 〇重量 %時。又’在一種有機系顏料、二種有機系染料下,在目 視下,金-青色之2色性最大,且觀察到彩度高者係在添加 量為0.50重量% 、1.0重量%時。 本紙張尺度適用令國國家標準(CNS)A4規格(210 公釐) 36 311253 473519 A7 _ B7_五、發明說明(37 ) 接著對無機系顏料之添加量為10.0重量% ,有機系顏 料、有機系染料之添加量為1.0重量%之塗裝體,判定所 觀察之色相變化大小及彩度高低,得到表11中所述之結 果。而且2色性及彩度之判定係以相當優良◎、優良〇、 普通△、不良X而評價。• 表11
經濟部智慧財_產局員·工消費合作社印製 顔料或染料名稱(化學式) 色調 分類 對基髋之添加量 (wt%) 二色性 彩度 1 普魯士藍 化學式:FeK[Fe(GN)e] 育 無機系顔料 1.0、2,5、5.0、15、25、50 〇 Δ 2 米洛醮 化學式:FeK[Fe(CN)J:50% +雲母:50% 靑 無機系顔料 1.0、2.5、5.0、15、25、50 ο Δ 3 姑藍 化學式:GoAl2〇4 資 無檐系顔料 1.0. 2.5. 5.0. 10. 25. 50 ◎ ◎ 4 第一藍 化學式 AagAleSieC^Sx 靑 無機系顔料 1.0、2.5、5.0、15、25、50 〇 ◎ 5 麵青藍 靑 有機系顔料 0.50,10, 3.0. 10 ◎ ◎ 6 亮藍 青 有機系染料 0·50、1Q、3.0、10 Δ 〇 7 m菁綠 青〜綠 有機系染料 0.50、IQ、3.0、10 Δ 〇 如表11中所示,得到2色性及彩度均良好結果之顏料 或染料為使用添加鈷藍與酞青藍之多色性粉體之塗裝體。 實驗9 接著試驗本發明之混合型多色性粉體之耐光性。 相對於產生金色干涉色之氧化鈦被覆雲母,分別添加添 加量10.0重量%之無機系顏料,添加量1.0重量%之有機 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 37 311253 -------------裝·-- (請先閱讀背面之注意事項再填寫本頁) -線_ 473519 A7 五、發明說明(38 ) 系顏料、有機系染料,且使用 使用小型粉末粉碎裝置混合,得 到本發明之混合型多声神去、士 色性杨末。將各多色性粉體加於石英 玻璃製之元件中,且以氙惫焐 风虱燈照射(照射度285瓦/平方公 尺,累積照射量.約30MJ/平方& p 1 丁歹a尺)30小時,照射前後 以分光測色機(MIN0LTA照相機株式會社製造,I 1〇〇〇ΤΜ)測定顏色,藉由照射測定色差。 注 意 事- 訂 又將1 A克以上述相同方法調製而成之本發明各種混 合型多色性粉體添加於15公克之石肖基纖維素漆料編號第 634i-(武藏塗料株式會社製造)中,以分散器攪拌且分 散’且以刮刀(間隙:101微米)將該塗料塗佈在白黑遮 蓋力試驗紙上,製成塗裝體。如此般製得之塗裝體以氙氣 燈照射(照射度285瓦/平方公尺,累積照射量·約3〇則 平方公尺)30小時,照射前後以分光測色機(min〇lta 照相機株式會社製造,CM_1〇〇〇tm)測定顏色,藉由照射 測定色差。 再者使用Ti-Co-Al系錯合氧化物被覆型多色性粉體及 利用此等之塗裝體當作比較例7 β 經濟部智慧財產局員工消費合作社印製 各混合型多色性粉體以及塗裝體之色差測定結果列於 表12中。 311253 473519 A7 _B7 五、發明說明(39 ) 表12 添加顔料·染料 照射氙總(xenon lamp) 30小時後之色差 名稱 分類 添加量 粉末元件 白色紙塗布 黒色紙塗布 1 普魯士藍 青色無機系顔料 10.0X 2.21 4.45 2.20 2 米洛麗藍 音色無機系顔料 10.0% 3.08 3.47 1.23 3 鈷藍 青色無機系顔料 10.0% 0.44 3.31 0.92 4 第一藍 育色無機系顔料 10.0% 0.56 3.13 2.00 5 銅酞青藍 靑色有搛系顔料 1.0% 6.32 2.57 1.75 6 亮藍 青色有機系染料 1.0X 1.66 18.93 4.96 7 酲菁綠 靑色有機系染料 1.0% 5.61 19.39 6.03 8 比較例7 一 — 0.45 2.63 1.52 --------------裝--- (請先閱讀背面之注意事項再填寫本頁) . 由表12可看出,塗佈在白色紙上之塗裝體所混合之多 色性粉體之外觀色,為塗佈在黑色紙上之塗裝體所混合之 多色性粉體所引起之反射干涉色狀態下所觀察之粉體色。
經濟部智慧財產局員工消費合作社印製 --線_ 如表12所示般,發現添加有機系顏料、染料之多色性 粉體,以及多色性粉體在以燈光照射前後,會有色差大之 傾向,但添加鈷藍之多色性粉體顯示與比較例7之Ti-Co-Al系錯合氧化物被覆型多色性粉體幾乎有同樣高之耐 光性。 由實驗8及實驗9之結果可了解氧化鈦被覆雲母中混 合之青色顏料最佳者為钻藍。 下面本發明者將詳細的檢討鈷藍之添加量與多色性粉 體色調之關係。 相對於產生金色干涉色之氧化鈦被覆雲母,鈷藍之添 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 39 311253 473519 B7 五、發明說明(40 ) ——
加量在 u'umo.omoM ^間變化’且使用小型粉碎裝置混合、得到不同話藍二 之各種多色性粉體。將1公克所得之各種現合於體添加 =公克之頌基纖維素漆料編號第6341TM (武藏 式會社製造)中’以分散器授拌且分散,以:株 =微米)將該塗料塗佈在白黑遮蓋力試驗紙上心塗 將白色光照射在上述塗裝體上,相對於前述 光’改變觀察角度’且以目視觀察顏色之變化,判定色: 之變化大小及彩度高低。 以目視觀察,當添加量為u重量%日夺,因為青色相 當淡、,因此無法充分發揮其兩色性,色彩感亦相當的淡, 當超過2.5重量%以上時’可觀察到相當高的青—金二色 性。但是’當其量增加至40重量%時,青色會增濃,導致 失去珍珠光澤顏料獨特之光輝性。 此時底色系為白色之塗裝體以變角分光測色系統(村 上色彩技術研究所社(株)製’ GCMS-3型GSP_lTM)測定顏 色。而且測定之方法係與上述實驗4、5中所述之方法相. 同,入射白色光之入射角為45。,受光角為_25。至65。, 且以每5。之間隔測定顏色,測色值換算成Hunter之乙讣 值。 所得之結果分別顯示於下表13、14、15中。又將該結 果之受光角與色相變化之關係圖顯示於第U圖中,受光角 與亮度關係之圖顯示於第12圖中。 丨本—國國~^~^r-
itr· (請先聞讀背面'之注意事項再填寫本頁) #*
473519
經濟部智慧財產局員工消費合作社印製 A7 B7 A1 五、發明說明() 又,表16中在-2 5°與+35°觀察角度下觀察時,觀察 色之色調差異係藉由色差(△ Lab)、色相差(Aab)、亮度 差(△!〇表示。 表13 (請先閱讀背面之注意事項再填寫本頁) 添加置 1.0X 2.5X 5.0X L a b L a b L a b -25 73.29 0.92 -15.87 71.63 -0.07 -20.11 68.04 -1.13 -25.59 -20 73.60 0.66 -15.68 71.97 "0.33 -19.84 68.39 -1.34 -25.27 -15 73.97 0.41 -15.32 72.40 -0.57 -19.38 68.85 -1.56 -24.76 -10 74.43 0,25 -14.81 72.94 -0.74 -18.73 69.41 -1.67 -24.09 -5 75.08 0.14 -14.03 73.63 *0.81 -17.89 70.18 -1.75 -23.15 0 76.12 0.06 -12.75 74.81 »0.89 -16.43 71.39 -1.84 -21.60 5 77.92 -0.10 -10.62 76.76 -1.03 -14.08 73.39 -1.99 -19.26 10 80.72 -0.31 -7.33 79.89 -1.26 -10.31 76.41 -2.23 -15.41 15 85.25 -0.67 -2.00 84.74 Η.61 -4.49 81.12 -2.54 -9.72 20 92.28 -1.24 6.10 92.61 -2.24 4.68 88.73 -3.09 -0.68 25 103.88 -2.24 18.85 104.76 - 3.25 18.16 100.42 -4.12 12.58 30 120.85 -3.88 35.92 123.28 -4.90 36.64 118.26 -5.70 30.93 35 148.98 -6.55 56.74 153.05 -7.45 57.15 146.86 -7.96 51.97 40 197.79 -7.99 65.65 208.80 "8.09 63.51 198.29 -8.81 60.65 45 279.93 -2.15 57.56 276.14 -2.73 59.25 272.96 -3.02 57.02 50 234.66 -7.62 59.01 218.17 -8.62 58.03 223.73 -8.29 55.53 55 177.86 -11.29 66.83 172.02 -11.68 63.07 170.26 -12.27 60.66 60 147.90 -9.47 53.37 144.40 -10.08 49.45 141.85 -11.01 46^5 65 129.00 -7.44 40.01 126.16 -8.21 36.26 123.14 -9.25 32.34 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 41 311253 473519 A7 B7_ 五、發明說明(42 ) 表14 經濟部智慧財產局員工消費合作社印製 添加置 10.0X 20.0% 30.0% L a b L a b L a b -25 63.66 -1.37 -32.53 59.34 -0.53 -39.51 55.51 0.95 -45.04 -20 64.10 -1.59 -32.00 59.86 -0.73 -38.89 56.17 0.63 -44.31 -15 64.71 -1.76 -31.34 60.53 -0.97 -38.11 56.88 0.37 -43.48 -10 65.43 -1.89 - 30.50 61.34 -1.13 -37.14 57.76 0.13 -42.38 66.34 -1.96 -29.31 62.39 -1.29 -35.79 58.84 -0.18 -40.96 0 67.81 -2.11 -27.46 63.89 -1.54 -33.84 60.51 -0.57 -38.81 5 70.08 -2.36 -24.62 66.21 -1.92 -30.85 62.94 -1.07 »35.72 10 73.60 -2.71 «20.26 69.80 -2.44 -26.37 66.56 -1.83 -31.13 15 78.86 -3.19 -13.79 75.06 -3.19 -19.84 71.79 -2.91 -24,55 20 87.13 -3.97 -3.90 83.15 -4.27 -9.98 79.51 -4.24 -15.13 25 99.35 -5.14 9.98 95.03 -5.65 3.63 90.76 -5.92 -2.30 30 117.61 -6.84 28.56 112.31 -7.59 21.33 107.54 -7.91 14.56 35 147.17 -9.23 48.76 141.99 -9.75 41.40 135.73 -9.75 32.95 40 200.12 -8.64 56.58 198.95 -8.66 51.37 187.86 -8.40 44.78 45 270.30 -2.62 55.67 262.92 -2.13 54.35 246.35 -1.65 51.28 50 211.66 -8.76 52.81 202.77 -9.13 48.81 211.68 -8.87 46.57 55 164.82 -12.90 54.51 157.27 -13.20 46.73 153.58 -12.84 38.92 60 137.35 -11.85 40.29 130.92 -12.33 32.41 124.29 -12.06 25.45 65 119.27 -10.20 26.86 113.44 -10.73 19.22 109.44 -11.02 13.34 (請先閱讀背ft之注意r項再填寫本頁)
本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 42 311253 473519 A7 B7 五、發明說明(43 )
經濟部智慧財I局員!^消費合作社印製 表15 添加置 40.0% 50.0% L a b L a b -25 53.49 1.85 -47.79 52.30 2.54 -49.70 -20 54.18 1.54 -47.04 52.98 2.30 -48.94 -15 54.91 1.29 -46.22 53.75 1.89 -48.00 -10 55.83 0.96 -45.03 54.63 1.52 -46.92 -5 57.04 0.58 -43.44 55.83 1.15 -45.36 0 58.69 0.12 -41.35 57.43 0.62 -43.30 5 61.12 -0.55 -38.23 59.81 -0.09 -40.25 10 64.74 -1.46 -33.5分 63.25 -1.10 -35.86 15 69.89 -2.67 -27.11 68.20 -2.40 -29.64 20 77.63 -4.23 -17.66 75.54 -4.05 -20.74 25 88.63 -6.03 -5.09 86.21 -5.94 -8.60 30 105.08 -8.13 11.45 102.37 -8.01 7.41 35 132.78 -9.87 29.42 130.40 -9.84 25.14 40 182.20 -8.50 41.33 181.65 -8.00 38.41 45 246.28 -1.02 50.45 240.12 -0.55 49.31 50 207.67 -8.66 44.02 199.92 -8.60 40.85 55 148.91 -12.84 35.26 143.89 -12.74 30.33 60 120.44 -12.02 21.44 116.37 -11.72 16.56 65 106.04 -11.01 9.42 102.45 -10.61 4.87 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 43 311253 —— — — — — — — — — — — II I I (請先閱讀背面之注意事項再填寫本頁) -SJ_ . •線- 473519 Α7 Β7 五 發明說明(44 ) 表16 钻藍 量 受光角: -25。 受光角:+35° 色調差 L a b L a b A (Lab): 色差 A(L): 亮度差 A(ab); 色相差 1.0X 73.29 0.92 —15.87 148.98 -6.55 56.74 105 2 757 73 0 2.5% 71.63 -0.07 *20.11 153.05 -7.45 57.15 1125 81 4 77 β 5.0X 68.04 -1.13 -25.59 146.86 -7.96 51.97 1108 788 77 9 10.0X 63.66 -1.37 - 32.53 147.17 -9.23 48.76 1168 83 5 81 7 20.0* 59.34 -0.53 -39.51 141.99 -9.75 41.40 1160 82 7 81 4 30.0X 55.51 0.95 -45.04 135.73 -9.75 32.95 112.4 802 787 40.0X 53.49 1.85 -47.79 132.78 •9.87 29.42 111.3 79 3 781 50.0X 52.30 2.54 -49.70 130.40 -9.84 25.14 108 9 78 1 7ς q (請先閱讀背面之注意事項再填寫本頁) 經濟部智慧財產局員工消費合作社印製 依據表13、14、15、16及第U、12圖可知,當鈷藍 之添加量為2·5至30.0重量%時,藉由改變相對於入射光 之觀察角度,可了解到色相之對比相當的大。特別是由於 相對於塗裝體,當添加量為10·0至2〇 〇重量%時,其色 相差及焭度差均相當的大,因此色調之對比差異相當的 大’因此可觀察到美麗之兩色性。 本發明之混合型多色性粉體’調配在氧化鈦被覆雲母 之無機系顏料之調配量較好為2.5至30_0重量% ,最好為 10.0 至 20.0 重量 % 。 而且’當得到塗裝體之多變色性時,將含有在雲母表 面上被覆氧化鈦產生反射干涉色之氧化欽被覆雲母之版成 物塗佈在基材上’在含有該氧化鈦之組成物上塗佈含有具 有與上述氧化鈦被覆雲母所產生之反射干涉色呈互補色 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公爱) 44 311253 A7 A7
五、發明說明(45 係色調之顏料或染料之透明著色組成物之塗裝體,或雲母 表面上被覆氧化鈦而產生反射干涉色之氡化鈦被覆雲母, 與含有具有與域氧化鈦被覆雲母所產生之反射干涉色呈 互補色關係色調之顏料或染料之透明著色組成物混合得到 -之組成物塗佈在基材上所得之塗裝體,藉由相對於入射光 之觀察角度,觀察色調之不同。但是此時,透明著色組成 ,物不會阻礙氧化鈦被覆雲母所觀察之反射干涉色,而且, 1必要將透明著色組成物之著色狀態調製成不濃不薄之狀 態0 、如以上之說明,由於本發明之Ti_c〇_Al系錯合氧化物 被覆型多色性粉體係藉由在雲母上形成含有欽、始、銘之 錯合氧化物層,因此可藉由不同之觀察角度看到不同之色 調。 又本發明之混合型多色性粉體之製造簡單,且可藉由 不同之觀察角度看到不同之色調。 又,本發明之多色性塗裝體可賦與基材多變色性之色 調。 (請先閱讀背面之注意事項再填寫本頁} 經濟部智慧財^局員卫消費合作社印製
311253
Claims (1)
- H3 經濟部中央標準局員工福利委員會印製附件二 φ 105295號專利申請案 -一il請專利範圍修正本 修正 着年月月1§ 曰 一種多色性粉體組成物’其特徵為4 一有薄基板 與被覆在前述雲母基板上之錯合氧化物,且構成前述錯 合氧化物之金屬包含具有選自下列a、b、c、d中任— 調配比之鈇'鈷、鋁: A.莫爾比為二氧化鈦5〇至915% ,鈷7 5至49% , 鋁1至20% ; 莫爾比為二氧化鈦5〇至96 5% ,鈷2.5至7_5% , 銘 1 至 47.5% ; 莫爾比為二氧化鈦50至72 5% ,鈷7 5至3〇% , 銘 20 至 42.5% ; 莫爾比為二氧化鈦50至98% ,鈷1至2.5% ,铭]^ 至 49% » 2.如申請專利範圍第1項之多色性粉體組成物,其中,係 將始及銘之錯合氧化物被覆在以二氧化鈦被覆雲母形 成之雲母鈦表面所構成之鋁酸鈷被覆之雲母鈦。 如申請專利範圍第1或2項之多色性粉體組成物,其 中’多色性粉體所呈現外觀色之色相可以以Huntei·之 Lab值表示,a值之範圍為·3113至1135,b值之範圍 為-29.46至31.22,L值之範圍為30.82至88.23。 4. 一種多色性粉體組成物,其特徵為將氧化鈦被覆在雲母 表面上產生反射干涉色之氧化鈦被覆雲母,與具有與前 述氧化鈦被覆雲母產生之反射干涉色呈互補色關係之 ff ^ ^ *«fi Jil d? gl g] ·:·?* v , ^ \ . . , .v ‘ B C D 3 —衣纸ϊί又度通用中钃國家標準(CNS )A4規格(210+X 297公I) 1 311253 473519 473519 --------- Η3 色調之顏料或染料混合。 5. 如申請專利範圍第4項之多色性粉體組成物,其中,前 述之氧化鈦被覆雲母產生之反射干涉色為金色色調,且 顏料或染料為青色色調。 6. 如申請專利範圍第4或$項之多色性粉體組成物,其 中’與前述氧化鈥被覆雲母混合之顏料或染料之調配量. 為2.5至30.0重量% 。 7. 如申請專利範圍第6項之多色性粉體組成物,其中,該 顏料或染料為鈷藍。 8· —種多色性塗裝體’其特徵為將包含如申請專利範圍第 1至7項中任一項之多色性粉體組成物之組成物塗佈在 選自紙、紙板、布、皮革 '金屬、塑膠,或預先在此等 物品上施以塗裝、印刷、塗布處理而成之基材上,且依 據相對入射光之觀察角度可觀察到不同之色調。 經濟部中央標準局員工福利委員會印製 9·如申請專利範圍第8項之多色性塗裝體,其申,將含有 在雲母表面上被覆氧化鈦產生反射干涉色之氧化鈦被 覆雲之組成物塗佈在基材上,且在含有前述氧化鈦之組 成物上,塗佈具有與前述之氧化鈦被覆雲母所產生之反 射干涉色呈互補色關係色調之顏料或染料之透明著色 魟成物,依據相對於入射光之觀察角度觀察到不同之色. 調。 10.如申請專利範圍第8項之多色性塗裝體,其中,將在雲 母表面上被覆氧化欽產生反射干涉色之氧化欽被覆雲 母’與含有與前述之氧化鈦被覆雲母所產生之反射干涉 _色呈互補色關係色調之顏料或染料之透明著色組志物 度適用中國國篆標準(CNS )Α4規格C 210Χ 297公澄) ------ ~~取物 311253 473519 473519 經濟.部中央標準局員工福利委員會印製 ____________H3__ 混合得到之組成物塗佈在基材上,且依據粗對於入射光 之觀察角度觀察到不同之色調。 11. 如申請專利範圍第8至10項中任一項之多色性塗裝 體’其中’前述基材之色調為白至黑之灰色範圍。 12. 如申請專利範圍第g至1〇項中任一項之多色性塗裝 體,其中,前述基材之色調為青色。 13 _如申請專利範圍第8項之多色性塗裝體,其中,塗佈在 基材上之含多變色性粉體組成物之組成物膜厚度為5 微米以上。 311253 衣紙張XJl通用中國國緖準(C N S ) A 4規格(210 X 297公釐)