TW201105506A - Non-PVC films having barrier layer - Google Patents
Non-PVC films having barrier layer Download PDFInfo
- Publication number
- TW201105506A TW201105506A TW99108386A TW99108386A TW201105506A TW 201105506 A TW201105506 A TW 201105506A TW 99108386 A TW99108386 A TW 99108386A TW 99108386 A TW99108386 A TW 99108386A TW 201105506 A TW201105506 A TW 201105506A
- Authority
- TW
- Taiwan
- Prior art keywords
- film
- layer
- adh
- mil
- ethylene
- Prior art date
Description
201105506 六、發明說明: 【發明所屬之技術領域】 本發明一般係關於聚合物膜。更特別地,本發明係關 於包含新穎之剝式密封層和/或障壁層的非PVC聚合物膜 【先前技術】 多層共擠壓膜在多種工業中被廣泛使用,例如,包括 用於食品或藥品溶液包裝之容器。多層擠壓膜的所欲性質 之一係其韌性或抵抗使用或運送時所造成損壞的能力。另 一所欲性質係其能夠使得剝式密封具有所欲強度以適合其 之應用以及永久密封於永久封閉容器之應用。另所欲的性 質係提供氣體(如氧、二氧化碳或水蒸氣)障壁性以維持 所含溶液的安定性。 傳統軟性聚氯乙烯材料基本上亦曾被用以製造醫藥級 容器。聚氯乙烯(“PVC”)係建構此裝置之成本有效的材 料。但是’ PVC在焚化時會產生無法接受量的氯化氫(或 當與水接觸時’氫氯酸)。PVC有時含有塑化劑,其會漏 入與PVC調合物接觸的藥品或生物流體或組織中。 【發明內容】 本發明一般係關於具有剝式密封層和/或障壁層的膜 。在一般具體例中’本發明提供包含剝式密封層的膜,該 剝式密封層包含熔點高於140 °c的聚丙烯(PP)無規共聚 201105506 物、苯乙烯-乙烯-丁烯-苯乙烯嵌段共聚物(SEBS)和熔 點高於1 15°c的線性低密度聚乙烯(LLDPE)之摻合物。 一具體例中,該摻合物包含約60重量°/。至約80重量°/。 熔點高於140 °C的聚丙烯無規共聚物、約15重量%至約30重 量%苯乙烯-乙烯-丁烯-苯乙烯嵌段共聚物和約2.5重量%至 約2 0重量%熔點高於1 15°C的LLDPE。 另一具體例中,該摻合物包含約70重量%熔點高於145 °C的聚丙烯無規共聚物、約22.5重量%苯乙烯-乙烯-丁烯_ 苯乙烯嵌段共聚物和約7.5重量%熔點高於120°C的LLDPE 。此LLDPE可爲乙烯-辛烯-1共聚物、乙烯-己基-1共聚物 或其組合物。 一具體例中,此膜包含表層和障壁層。例如,該表層 和該剝式密封層可連接至該障壁層的相反面。該表層可包 含聚丙烯無規共聚物 '聚丙烯均聚物、以聚丙烯爲基礎的 TPO、尼龍、苯乙烯-乙烯-丁烯-苯乙烯嵌段共聚物、共聚 酯醚、或其組合物。該障壁層可包含聚醯胺(尼龍),例 如聚醯胺6,6/6,10共聚物、聚醯胺6、非晶狀聚醯胺、橡膠 改質的尼龍、或其組合物。 一具體例中,該膜包含至少一個束縛層,其將該表層 和該剝式密封層中之至少一者連接至該障壁層。該束縛層 可包含順丁烯二酸化的LLDPE、順丁烯二酸化的聚丙烯均 聚物、順丁烯二酸化的聚丙烯共聚物、順丁烯二酸化的 TPO、或其組合物。 另一具體例中’本發明提供一種包含剝式密封層的膜 -6- 201105506 ,其包含熔點高於140 °C的聚丙烯無規共聚物和乙烯-丙烯 橡膠改質的聚丙烯彈性體之摻合物。該摻合物可包含約20 重量%至約40重量%聚丙烯無規共聚物和約60重量%至約80 重量%乙烯-丙烯橡膠改質的聚丙烯彈性體。 —具體例中,該膜包含表層、密封層和障壁層。該表 層和該剝式密封層可連接至該障壁層的相反面。該表層可 包含聚丙烯均聚物、聚丙烯無規共聚物、以聚丙烯爲基礎 的TPO、聚醯胺(尼龍)、苯乙烯-乙烯-丁烯-苯乙烯嵌段 共聚物、共聚酯醚共聚物、或其組合物。該障壁層可包含 —或多種聚醯胺(尼龍),如聚醯胺6、聚醯胺6,6/6,10共 聚物、非晶狀聚醯胺、經橡膠改質者、或其組合物。此膜 可以進一步包含至少一個束縛層,其將該表層和該剝式密 封層中之至少一者連接至該障壁層。 另一具體例中,本發明提供一種包含障壁層的膜’該 障壁層包含不含己內醯胺的尼龍混合物。此不含己內醯胺 的尼龍混合物可包含約75重量%至約95重量%的聚醯胺 6,6/6,1 0共聚物和約5重量%至約2 5重量%的非晶狀聚醯胺 之摻合物。另一具體例中,此不含己內醯胺的尼龍混合物 包含約8 7.5重量%的聚醯胺6,6/6,1 0共聚物和約1 2.5重量% 的非晶狀聚醯胺之摻合物。 一具體例中,該具有不含己內醯胺的尼龍障壁層的膜 包含表層和剝式密封層。該表層和該剝式密封層連接至該 障壁層的相反面。該表層可包含聚丙烯均聚物 '聚丙燃無 規共聚物、以聚丙烯爲基礎的TPO、聚醯胺(尼龍)、苯 201105506 乙烯-乙烯-丁烯-苯乙烯嵌段共聚物、共聚酯醚嵌段共聚物 、或其組合物。該剝式密封層可包含熔點高於14 0 °c的聚 丙烯無規共聚物、苯乙烯-乙烯-丁烯-苯乙烯嵌段共聚物和 熔點高於120 °C的LLDPE之摻合物。該膜可進一步包含至 少一個束縛層,其將該表層和該剝式密封層中之至少一者 連接至該障壁層。 一具體例中*該膜可包括位於表層和剝式密封層之間 的核心層,例如介於表層和障壁層之間,或介於剝式密封層 和障壁層之間。核心層可含有丙烯-乙烯共聚物、間規丙 烯-乙烯共聚物、聚丙烯彈性體、聚丙烯均聚物、以丙烯 爲基礎的彈性體、以乙烯爲基礎的彈性體、苯乙烯-乙烯-丁烯-苯乙烯嵌段共聚物、乙烯-丙举橡膠改質的聚丙烯、 或其組合物。 另一具體例中,此膜可用以製造任何適當容器,例如 ,用以盛裝物質,如醫用或藥用化合物或溶液。本發明提 供一種容器’其包含沿著至少一個周邊密封在一起以界定 流體槽的第一側壁和第二側壁。容器的第一和第二側壁中 之至少一者係膜’其包含1 )剝式密封層,其包含熔點高 於l4〇°C的聚丙烯無規共聚物、苯乙烯-乙烯„ 丁烯-苯乙烯 嵌段共聚物和熔點高於1 1 5 X:的L L D P E之摻合物;和2 )剝 式密封層,其包含熔點高於1 40。(:的聚丙烯無規共聚物和 乙烯-丙烯橡膠改質的聚丙烯彈性體之摻合物;和3)包含 不含己內醯§女的尼龍混合物之障壁層,中之至少一者。 替代具體例中’本發明提供多槽容器,其包含藉膜界 -8 - 201105506 定的主體。該主體可包括藉可剝式封層隔開的二或更多個 槽。該膜可包含1)剝式密封層,其包含熔點高於140 °c的 聚丙烯無規共聚物、苯乙烯-乙烯-丁烯-苯乙烯嵌段共聚物 和熔點高於115°C的LLDPE之摻合物;和2)剝式密封層, 其包含熔點高於140 °C的聚丙烯無規共聚物和乙烯-丙烯橡 膠改質的聚丙烯彈性體之摻合物;和3)包含不含己內醯 胺的尼龍混合物之障壁層,中之至少一者。 本發明的一個優點在於提供改良的非PVC膜。 本發明的另一優點在於提供用於聚合物膜之改良的剝 式密封層。 本發明的又另一優點在於提供用於聚合膜之改良的障 壁層。 本發明的又另一優點在於提供改良之製造非PVC膜之 方法。 本發明的另一優點在於提供改良之包含非PVC膜的容 器。 其他特徵和優點述於此處,且由下列詳述和附圖會更 加瞭解。 【實施方式】 本發明一般係關於具有剝式密封層和/或障壁層的非 PVC膜。此發明提供可用於包裝應用的單層和多層膜. 本發明之具體例中的膜具有改良的韌性和剝式密封能 力並維持良好的氣體障壁性質。此可藉由混合材料以提供 -9 - 201105506 適當密封層(其提供適當的剝式密封範圍及韌性)並選擇 改良膜之韌性的表層而達成。一具體例中,剝式密封層和 障壁層可具有如下性質:韌性或吸收衝擊能量的能力、於 121 °C的滅菌性、低濁度、氣體障壁性、使用熱密封機械 之剝式密封性及可供應性。 在圖1所示的一般具體例中,本發明提供包括剝式密 封層的膜10,該剝式密封層含有熔點高於140 °c的聚丙烯 無規共聚物(PP)、苯乙烯-乙烯-丁烯-苯乙烯嵌段共聚物 和熔點高於115 °c的LLDPE之摻合物。適當的聚丙烯無規 共聚物包括Flint Hills Resources以HUNTSMAN註冊名稱及 Borealis以BOREALIS和TOTAL註冊名稱銷售者。適當的苯 乙烯-乙烯-丁烯-苯乙烯嵌段共聚物包括Kraton以KRATON 註冊名稱銷售者。適當的LLDPE包括Exxon以EXXON註冊 名稱和Dow以DOWLEX註冊名稱銷售者。 一具體例中,該剝式密封層摻合物包含約6 0重量%至 約80重量%熔點高於145 °C的聚丙烯無規共聚物、約15重量 %至約30重量%苯乙烯-乙烯-丁烯-苯乙烯嵌段共聚物和約 2.5重量%至約20重量%熔點高於120 °C的LLDPE。另一具體 例中,該摻合物包含約7〇重量%熔點高於145 °C的聚丙烯無 規共聚物、約22.5重量%苯乙烯-乙烯-丁烯-苯乙烯嵌段共 聚物和約7.5重量%熔點高於120 °C的LLDPE。此LLDPE可 爲乙烯-辛烯-1共聚物、乙烯-己基-1共聚物或其組合物。 圖2所示的具體例中,該膜係具有表層20、障壁層24 和剝式密封層2 8的五層膜。例如,該表層2 0和剝式密封層 -10- 201105506 28可以直接或間接連接至障壁層24的相反面。該表層20可 以含有聚丙烯無規共聚物、聚丙烯均聚物、尼龍、苯乙 烯-乙烯-丁烯-苯乙烯嵌段共聚物、共聚酯醚、或其組合物 。該障壁層可含有一或多種聚醯胺(尼龍),例如,聚醯
I 胺6、聚醯胺6,6/6,10共聚物、非晶狀聚醯胺、或其組合物 。適當的聚丙烯均聚物包括Flint Hills Resources以 HUNTSMAN註冊名稱銷售者。適當的尼龍包括EMS以 GRIVORY和GRILON註冊名稱銷售者。適當之乙燃-丙烯橡 膠改質的聚丙烯彈性體包括Mitsubishi以ZELAS註冊名稱 銷售者。 圖2所示具體例中,多層膜包括一或多個束縛層22和 26用以將表層20和/或剝式密封層28連接至障壁層24。束 縛層22和26可以含有任何適當的黏著材料,例如,順丁烯 二酸化的LLDPE、順丁稀二酸化的聚丙燃均聚物、順丁嫌 二酸化的聚丙烯共聚物、順丁烯二酸化之以聚丙烯爲基礎 的TPO、或其組合物。 另一具體例中’本發明提供一種包括剝式密封層的膜 ,該剝式密封層含有熔點高於1 4 5 °c的聚丙烯無規共聚物 和乙烯-丙烯橡膠改質的聚丙烯彈性體之摻合物。此慘合 物可含有約2〇重量%至4〇重量%熔點高於140°C的聚丙締無 規共聚物和約6 0重量%至約8 0重量%乙烯-丙烯橡膠改質的 聚丙烯彈性體之摻合物。 一具體例中’前述膜可以進一步包括表層和障壁層。 該表層和該剝式密封層可以連接至該障壁層的相反面。該 -11 - 201105506 表層可含有聚丙烯均聚物、聚丙烯無規均聚物、以聚丙烯 爲基礎的彈性體、聚醯胺(尼龍)、苯乙烯-乙烯-丁烯-苯 乙烯嵌段共聚物、共聚酯醚嵌段共聚物、或其組合物。該 障壁層可包括一或多種聚醯胺(尼龍)’如聚醯胺6、聚 醯胺6,6/6,10共聚物、非晶狀聚醯胺、或其組合物。此膜 可以進一步包含至少一個束縛層,其將該表層和該剝式密 封層中之至少一者連接至該障壁層。 在本發明之具體例中之包括障壁層的膜可以含有不含 己內醯胺的障壁材料,該障壁材料具有良好的氣體障壁性 和足夠的韌性,以用於醫藥溶液容器應用的多層膜中。傳 統上,尼龍-6 (聚醯胺-6 )或以尼龍-6爲基礎的摻合物提 供良好的氣體障壁和耐衝擊性之組合。但是,在某些國家 (如日本、韓國和中國),尼龍-6因爲這些國家的藥典規 定而無法用於塑膠溶液容器應用。這些國家的藥典規定包 括對於自容器膜材料萃入溶液中之化合物的UV /可見光 波長之限制;這些限制嚴重限制容器膜中的己內醯胺允許 量。因爲聚醯胺-6係自己內醯胺合成得到,而其以提供有 用的障壁性之厚度存在時將會使得容器膜無法通過標準。 另一具體例中,本發明提供一種包括不含己內醯胺的 尼龍(即,聚醯胺或PA )混合物之障壁層的膜。此不含己 內醯胺的尼龍混合物可包含約75重量%至約95重量%聚醯 胺6,6/6,10共聚物和約5重量%至約25重量%非晶狀聚醯胺 之摻合物》另一具體例中,此不含己內醯胺的尼龍混合物 包含約87.5重量%聚醯胺6,6/6,1〇共聚物和約^^重量%非 -12- 201105506 晶狀聚醯胺之摻合物。適當的非晶狀聚醯胺包括,但不限 於,聚醯胺6I/6T和聚醯胺MXD6/MXDI共聚物。 圖3所示的具體例中,該膜包括表層30、不含己內醯 胺的尼龍障壁層36和剝式密封層40。表層30和剝式密封層 40可以在障壁層36的相反面連接至障壁層36。表層30可以 含有聚丙烯均聚物、聚丙烯無規共聚物 '以聚丙烯爲基礎 的TPO、聚醯胺(尼龍)、苯乙烯-乙烯-丁烯-苯乙烯嵌段 共聚物、共聚酯醚嵌段共聚物、或其組合物。該剝式密封 層40可以含有熔點高於140 °C的聚丙烯無規共聚物、苯乙 烯-乙烯-丁烯·苯乙烯嵌段共聚物和熔點高於115 °C的 LLDPE之摻合物。 如圖3所示者,此膜進一步包括位於表層30和障壁層 36之間的核心層32。該核心層32可含有丙烯-乙烯無規共 聚物、丙烯-乙烯間規共聚物、聚丙烯彈性體、聚丙烯均 聚物、以丙烯爲基礎的彈性體 '以乙烯爲基礎的彈性體、 苯乙烯-乙烯-丁烯-苯乙烯嵌段共聚物、乙烯-丙烯橡膠改 質的聚丙烯、和其組合物。適當的丙烯-乙烯共聚物包括 Exxon以VISTAMAXX註冊名稱、Dow以VERSIFY註冊名稱 、Total以AT OF INA註冊名稱及Bas ell以.PRO FAX註冊名稱 銷售者。此膜可進一步包含一或多個束縛層3 4和3 8用以使 得表層30、剝式密封層40、障壁層36和/或核心層34彼此 連接。 本發明之具體例中的膜可用以製造任何適當容器,例 如,用以盛裝物質,如醫用或藥用化合物或溶液。圖4所 -13- 201105506 示具體例中’本發明提供容器50,其包含第一側壁52和在 第一側壁相反面的第二側壁(未示),其沿著周圍接縫54 密封在一起,以界定流體槽。容器50可包含一或多個接管 56和58用以塡充和掏空容器50的內容物。側壁的任何一或 多者可以製自則述單層或多層膜之一。亦將瞭解此容器可 以由開口經密封之擠壓的管狀膜形成。此情況中,周圍接 縫54可由在管的相反端上的兩個接縫所組成。此容器的構 造可以使得接縫位於容器頂端和底端或沿著其直立側處。 一具體例中,第一側壁和/或第二側壁是膜,其具有 1 )剝式密封層,其包含熔點高於1 4〇°C的聚丙烯無規共聚 物、苯乙烯-乙烯-丁烯-苯乙烯嵌段共聚物和熔點高於115 C的LLDPE之慘合物;和2)剝式密封層,其包含熔點高 於140 °C的聚丙烯無規共聚物和乙烯-丙烯橡膠改質的聚丙 烯彈性體之摻合物;和3)包含不含己內醯胺的尼龍混合 物之障壁層,中之至少一者。 圖5所示的替代具體例中,本發明提供多槽容器7〇, 其包含藉膜界定的主體72»此多槽容器70包含兩個槽74和 76。應瞭解在替代具體例中,容器中可以有超過兩個槽。 槽7 4和7 6經設計以分別儲存物質和/或溶液。 所示具體例中,容器70的任何部分製自膜,該膜具有 1 )剝式密封層’其包含熔點高於1 40 °C的聚丙烯無規共聚 物、苯乙烯-乙烯-丁烯-苯乙烯嵌段共聚物和熔點高於U5 °C的LLDPE之摻合物;和2 )剝式密封層,其包含熔點高 於140 °C的聚丙烯無規共聚物和乙烯-丙烯橡膠改質的聚丙 _ 14 - 201105506 烯彈性體之摻合物;和3)包含不含己內醯胺的 物之障壁層,中之至少一者。 此容器70可製自兩個膜片,其例如,沿其邊 82、84和86)熱封而形成永久密封。在所示具體 用兩個膜片》這些片於容器70周圍的邊緣80、82 處沿著周圍密封。或者,此溶液可以製自於其開 的擠壓管狀膜。此情況中,容器只有兩個相反的 如邊緣8 2和8 6 )須被密封》在膜片之間配備可剝 以形成槽74和76。當然,如果配備額外的槽,則 額外之可剝式封層。 容器70和可剝式封層88可以由具有根據本發 例之剝式密封層的膜所構成。此剝式密封層可以 離和永久密封二者。因此,可以由膜的相同層製 封層80、82、84和86及可剝式封層88。 如圖5所不者,容器70可進一步包含一或多 、92、94 和 96° 通口 90、92、94 和 96提供槽 74和 連通,但可位於容器70上的任何適當處。這些通 體可加至槽74和76或自槽74和76移出。通口 90、 96亦可包括被施用組合品的套管或長釘刺破的膜 。應瞭解通口的一或多者可以模製構造形式配備 別採用以密封至容器的表面介於片之間(各情況 將通口構造稱爲“吊艙(gondola) ”)或直接導向 瞭解通口可以包括簡單膜以外的閥或類似的密閉 替代通口構造的例子包括藥物通口 (美國1 尼龍混合 緣(80、 例中,使 、84和 86 口端密封 邊緣(例 式封層88 可以配備 明之具體 製造可剝 造永久側 個通口 90 76內部之 口使得流 92 、 94和 (未示) ,具有特 中,有時 壁。亦將 構造。此 Ϊ利案第 -15- 201105506 6,994,699號中描述者)和各種接入通口 (美國專利案第 2005/0083132號中描述者),茲將各者以引用方式納入本 文中,和 取決於製造容器所用的方法,可以完全不須要塡充通 口。例如,如果容器係由塑膠膜的連續卷製造,則此膜可 經縱向折疊,製造第一個永久密封,以溶液充塡第一槽室 ,然後製造可剝式封層,充塡第二槽室,製造永久密封.. 等0 實例 以下列實例說明本發明之多種具體例,且下列實例並 非用於限制本發明。 實例1 將含有共聚丙烯、SEBS嵌段共聚物和LLDPE之摻合物 擠壓成單層膜。評估經高壓滅菌的膜之密封性能及一些其 他性質,如透明度(濁度)、抗拉和高壓滅菌性(經由觀 察表面外觀)。進行包括市售品的膜(CAWITON® PR458 1 A -比較例-1 )和兩個組成爲60%/25%/15%共聚丙烯 / SEBS/LLDPE的膜(比較例-2和比較例-3 )及本發明之 調合摻合物之比較用的測試。此外,本發明的一些剝式密 封層摻合物與其他層共擠壓以製造多層膜,以其評估剝式 密封性能。 I. 單層膜 -16- 201105506 表1 :不同的單層膜之比較(峰力,形態)
剝式密封摻合物之調合物 (PP+SEBS+LLDPE) 調合物 市售品 (Cawiton) 3M& 34-1&36-1 31-2 & 34-2 31-3 34-3 36-2 31-19 34-9 34-10 36-8 36-9 36-10 36-11 (比較例-1) (比較例-2) (比較例-3) Huntsman 43M5A 60 60 70 75 70 75 75 70 70 Kraton G 1652 25 0 0 0 0 0 0 0 0 Kraton G1643 0 25 25 17.5 22.5 17.5 17.5 22.5 22.5 Exxon LL3003 15 15 5 7.5 7.5 7.5 0 7.5 0 Dowlex 2047G 0 0 0 0 0 0 7.5 0 7.5 總計 100 100 100 100 100 100 100 100 100 剝式密封性 (髙壓滅菌後) 峰力(牛頓/ 15毫米) 120°C 1.0 0.7 2.0 1.0 0.7 0.7 0.7 0.7 1.7 1.2 130°C 7.1 1.3 3.2 2.5 4.7 2.2 0.8 1.1 3.8 4.8 140°C 363 11.1 27.7 19.2 26.5 25.4 25.8 30.7 24.3 31.1 150°C 44.8 39.0 43.2 48.6 50.5 50.7 60.3 61.1 53.8 56.1 剝式密封形態 120°C Adh. Adh. Adh. Adh. Adh. Adh. Adh. Adh. Adh. Adh. 130°C Adh. Adh. Adh. Adh. Adh. Adh. Adh. Adh. Adh. Adh. 140°C Adh. Adh. Adh. Adh. Adh. Adh. Adh. Adh. Adh. Adh. 150°C 4/5 RMS 1/5 RBS Adh. Adh. Adh. 2/5 Adh. 3/5 RES Adh. 5/5 Adh. 5/5 SMS 1/5 RES 5/5 Adh. 5/5 SMS 4/5 RES 5/5 Adh. 4/5 SMS 1/5 SES 3/5 RES 5/5 Adh 5/5 SMS -17- 201105506 表2:不同的單層膜之比較(濁度、抗拉、表面外觀)
市售品 (Cawiton) 31-1 & 34-1 & 36-1 31-2 & 34-2 31-3 & 34-3 & 36·2 3M9 34-9 34-10 36-8 36-9 36-10 36-11 濁度(髙壓 滅菌後) 濁度撫水),% 65.4 40.3 23.4 ... 18.6 17.3 17.2 16.9 15.7 13.9 濁度(密封側 上潤濕),% 51.9 25.2 17.8 -- 15.4 11.2 11.1 12.8 9.6 8.7 濁度(兩側 上潤濕),% 18.8 10.0 10.3 — 6.3 6.2 5.6 3.9 4.4 3.1 抗拉(髙壓 滅菌後) Young's 模數fei) 45.7 55.5 42.4 — 57.4 56.8 63.6 61.9 50.7 47.0 屈服伸長率 (Z-Zip)(%) 28.2 28.7 44.8 — 31.4 35.3 31.1 33.6 41.1 39.3 屈服強度 (Z-Slp)(psi) 1882 2335 1993 … 2483 2447 2508 2451 2257 2105 拉伸強度(psi) 4342 5169 3284 … 4230 4081 4143 3981 4007 3772 破裂拉長度(¾吋) 18 15 15 ... 17 17 18 17 19 18 拉伸伸長率(%) 634 521 565 … 649 626 687 652 655 695 髙壓滅菌後 的表面外觀 OK OK OK OK OK OK OK OK OK OK 註:
Adh.:黏著性剝除 RBS、RMS、RES :膜分別於密封開始、中間和終了 時撕裂。 SMS、SES :膜分別於密封中間和終了時拉伸。 如表1和2中所示者,剝式密封層摻合物調合物3 1 -1 9 、34-9、 34-10、 36-8、 36-9、 36-10和 36-11具有: 1. 剝式密封力的範圍寬廣:約3至30牛頓/ 15毫米 2. 於高壓滅菌溫度(1 20 °C )下的剝離力低:<3牛 -18- 201105506 頓/ 15毫米 3. 永久密封力比三個比較用調合物爲高 4. 透明度比三個比較用調合物爲高 5. 高壓滅菌性。 表3 :剝式密封摻合物的聚合型組份 ΜΗ,克/1盼鐘 (190°C/2.1 讼斤) MFI,克/1盼鐘 (230°C /2.1讼斤) 密度 化學品 HUNTSMAN® 43M5A … 4.5 0.9 無規共聚PP KRATON® G1652 — 5 SEBS KRATON® G1643 — 18 具有髙1-¾喊的 中-軟嵌段的SEBS EXXON® LL3003 3.2 — 0.918 乙烯-己烯-1共聚物 DOWLEX® 2047 2.3 — 0.917 乙烯-辛烯-1共聚物 II.沒有氣體障壁層的多層膜 使用調合物36-9作爲共擠壓膜中之剝式密封層, VistaPeel-2(請見表4)。用於Zcore-Ι和Vista-Ι的剝式密 封層分別是比較例-2和比較例-3。 -19- 201105506 表4:沒有氣體障壁層的多層膜之比較 樣品 表層 核心層 密封層 0.6密耳 4.0密耳 3.4密耳 ZCORE-1 90% Total 6573XHC 10%KratonG1643 ZELAS MC717 60% Huntsman 43M5A 25% Kraton G1652 15% EXXON LL3003 0.6密耳 6密耳 1.4密耳 VISTA-1 90% Huntsman 43M5A 83% Vistamaxx 1100 60% Huntsman 43M5A 10%KratonG1643 17% Huntsman 43M5A 25% Kraton G1643 15% EXXON LL3003 0.6密耳 6密耳 1.4密耳 VistaPeel-2 90% Huntsman 43M5A 83% Vistamaxx 1100 70% Huntsman 43M5 A 10%KratonG1643 17% Huntsman 43M5 A 22.5% Kraton G1643 7.5% Dowlex 2047G 1.5密耳 6密耳 2,7密耳 FFS-14 50%Ze!as MC717 77% Vistamaxx 6102 70% Huntsman 43M5A 45% Huntsman P4G3Z-050F 19% Huntsman X01462 7.5% Dowlex 2247G 5% Profax PF611 4% Kraton G1643 22.5% Kraton G1643 1.5密耳 5.5密耳 2.9密耳 FFS-15 50%Zelas MC717 62.5% Vistamaxx 6102 70% Huntsman 43M5A 45% Huntsman P4G3Z-050F 25%Zelas MC717 7.5% Dowlex 2247G 5% Profax PF611 12.5% Huntsman X01462 22.5% Kraton G1643 ZCORE-1的密封層=比較例-2 VISTA-1的密封層=比較例-3 VistaPeel-Ι 的密封層= 36-9 多層膜的剝式密封性能節錄於表5和圖6。 -20 - 201105506 表5 :表4的多層膜之剝除力 剝除峰力 件頓/15毫米) Zcore-1 Vista-1 Vista Peel-2 FFS-14 FFS-15 T(°C) 118 0.8 1.2 0.7 1.1 0.6 121 0.9 2.0 0.7 1.0 0.6 124 1.1 1.8 0.9 0.9 0.6 127 1.7 2.9 1.2 1.2 0.6 130 2.2 3.7 1.9 1.2 0.7 133 3.5 6.4 3.8 1.7 0.9 136 5.2 12.0 7.8 2.5 1.4 139 9.4 18.4 15.4 3.5 2.3 140 13.2 26.0 18.8 4.4 6.8 142 18.1 28.5 28.9 14.4 13.3 145 18.8 27.7 35.1 19.9 18.2 148 23.1 31.3 35.1 34.1 27.7 150 25.2 28.5 31.9 44.1 43.8 剝式密封層形態 118 Adh. Adh. Adh. Adh. Adh. 121 Adh. Adh. Adh. Adh. Adh. 124 Adh. Adh. Adh. Adh. Adh, 127 Adh. Adh. Adh. Adh. Adh. 130 Adh. Adh. Adh. Adh. Adh. 133 Adh. Adh. Adh. Adh. Adh, 136 Adh. Adh. Adh. Adh. Adh. 139 Adh. Adh. Adh. Adh. Adh. 140 Adh. Adh. Adh. Adh. Adh. 142 Adh. Adh. Adh., SBS 1/5 Adhesive, SW; 4/5 Adhesive 5/5 Adhesive 145 Adh. 2/5 Adh. 3/5 RES Adh., SBS, RBS 5/5 Adhesive, SW 5/5 Adhesive 148 Adh. Adh. Adh. SBS 4/5 SMS, SW; 1/5 Adhesive, SW Adhesive, SW, 4/5; SES, 1/5 150 Adh. RMS Adh., SBS, RBS 4/5 SMS, SW; 1/5 SMS, RES, SW 5/5 Adhesive 失效模式=
Adh :黏著性剝離 S W :應力白化 SBS、SMS、SES :膜分別於密封開始、中間和終了時 拉伸。 RBS、RMS、RES :膜分別於密封開始、中間和終了 時撕裂。 -21 - 201105506 表5和圖6顯示VistaP eel-2於接近高壓滅菌溫度的剝式 密封力低,剝式密封範圍寬(至高約30牛頓/ 15毫米)且 具有最高的永久密封.力。 III.具有氣體障壁層的多層膜 調合物3 6-9作爲在共擠壓膜中的剝式密封層: NylonPeel-2 (請見表6)。而用於Symredad和NB-1的剝式 密封層分別是比較例-1和比較例-3。 表6:具有氣體障壁層的多層膜
樣品 表層 束縛層 壁障層 束縛層 密封層 1.9密耳 0.2密耳 1.1密耳 0.2密耳 3.7密耳 Symredad Borealis RE216CF ADMER OF300E EMS Grilon FG40NL ADMER QF300E Cawiton PR4581A 1.8密耳 0.4密耳 1·1密耳 0.4密耳 3.5密耳 NB-1 90% Huntsman 43M5A I0%KratonG1643 ADMER QB510A EMS Grilon BM20SBG ADMER QB510A 60% Huntsman 43M5A 25% Kraton G1643 15% EXXON LL3003 1.8密耳 0.4密耳 1_1密耳 0.4密耳 3.5密耳 NP-2 90% Huntsman 43M5A 10%KratonG1643 ADMER QB510A EMS Grilon BM20SBG ADMER QB510A 70% Huntsman 43M5 A 22.5% Kraton G1643 7.5% Dowlex 2047G
Symredad的密封層=比較例-1 N B -1的密封層=比較例-3 NP-2的密封層= 36-9 多層膜的剝式密封性能節錄於表7和圖7。 -22- 201105506
表7 :表6的多層膜之剝除力 T(°C) 剝除峰力(牛頓/15毫米) 和剝式密封層形態 Symredad NB-l NP-2 118 1.9 Adh. 1.6 Adh. 0.7 Adh. 121 2.5 Adh. 1.7 Adh. 0.8 Adh. 124 4.3 Adh. 2.5 Adh. 1.1 Adh. 127 7.5 Adh. 4.9 Adh. 2.8 Adh. 130 14.9 Adh. 7.6 Adh. 6.6 Adh. 133 24.3 Adh. 14.0 Adh. 14.5 Adh. 136 33.7 Adh, 1/5 Delam. 22.2 Adh. 23.9 Adh. 139 37.8 Adh. 2/5 Delam. 33.9 Adh. 32.7 Adh. 140 40.9 Adh, 1/5 Delam. 30.8 Adh. 41.5 Adh. 142 50.8 Adh. 4/5 Delam. 34.7 Adh. 43.4 Adh. 145 53.2 5/5 Delam 41.9 Adh. 49.5 Adh. 148 55.1 5/5 Delam 48.1 Adh. 62.5 Adh. 2/5 SES 150 51.8 5/5 Delam 51.4 Adh. 66.8 Adh., SES 152 50.4 5/5 Delam 40.1 Adh. 65.6 4/5 Adh. SES 1/5 SBS 155 53.9 5/5 Delam 43.8 Adh. 53.1 Adh., SES
Adh :黏著性剝離 SBS、SES :膜分別於密封開始和終了時拉伸。 D el am :層離 -23- 201105506 表7和圖7顯示NP-2於接近高壓滅菌溫度具有的剝式密 封力低,剝式密封範圍寬(至鬲約50牛頓/ 15毫米)且具 有最高的永久密封力(於密封溫度介於147和1 55°C之間處 實例2 實例1提供的證據指出包含聚丙烯共聚物 /SEBS/LLDPE之摻合物提供改良之能夠用於許多應用的剝 式密封層》此硏究針對藉由令彈性材料和/或低熔點聚烯 烴混入多層膜的適當層中的方式改良這些膜的韌性並同時 維持剝式密封特性。例如,本調合物包括混入多種多層共 擠壓膜之剝離和/或表層中的材料。此外,PCCE (聚( 環伸己基二伸甲基環己二羧酸酯)、甘油和酸共聚單體) 亦作爲強韌表層而與新混合的剝式密封層倂用。然後,以 所得構造測試剝式密封性、濁度、韌性(使用ASTM D3 763 > ctHigh Speed Puncture Properties of Plastics Using Load and Displacement Sensors”和/或官能性容器墜落測 試)。 本實例中,進行四個不同的剝式密封硏究並與 C a w i t ο η基線比較。用於這些剝式密封層硏究之典型的調 合物如下。 1 . 樣品1 :此剝式密封調合物包含約6 0 % ρ ρ、2 5 % SEBS和15% ΡΕ之摻合物。所用ρρ的熔點約145。匚 -24- 201105506 2. 樣品2 :此剝式密封調合物包含約6〇% TOTAL®8573 PP、25% SEBS 和 15% LLDPE 之摻 合物。TOTAL®8 573 PP是較軟、熔點略低(I” °C )且增加一些韌性的材料。 3· 樣品3 :此剝式密封調合物包含約60%
Hunstman® 43M5A PP ' 25% SEBS和 15% LLDPE 之摻合物。Hunstman® 43M5A PP是熔點略高( 148°C )的PP ’其將剝式密封曲線遷移至較高溫 度以因應日本剝式要求》 4. 樣品4 :此剝式密封調合物包含約6 0 % HUNSTMAN® 43M5A PP、25% KRATON® G1643 SEBS (其爲更高度支化且與PP更相容者)和15% LLDPE之摻合物。 5. 樣品5 :此剝式密封調合物包含約70% Zelas 7023 (一種以聚丙烯爲基礎的熱塑性彈性體)和3 0% Huntsman 43M5 A之摻合物。Z E L A S ® 7 0 2 3 的溶點 約1 6 1 °C,其使得易於符合日本剝式要求。 這些剝式密封層擠壓成數個多層構造,得到之幾乎相 同的剝式密封曲線。不同樣品調合物之基本剝式密封曲線 示於圖8。圖8顯示樣品3、樣品4和樣品5皆提供符合所欲 性質的剝式密封特性。於溫度高於1 2 1 °C,這些調合物可 用以在介於4牛頓/ 15毫米至約30牛頓/毫米之間產生剝 式密封。 -25- 201105506 製造並測試含有尼龍障壁層及樣品3、樣品4和樣品5 剝式密封層之三個不同的疊接膜之替代具體例。第一疊接 膜包括具有樣品3剝式層和/或PCCE表層的構造,其爲圖 2所示之五層膜構造的替代具體例,其具有下列順序:表 層20 /束縛層22 /障壁層24 /束縛層26 /密封層28。膜層 的細節述於表8。各膜末尾的單位代表層的厚度。 表8:第一疊接膜調合物 TP-1 TP-4 PCCE-5 PCCE-6 表層: Borealis Re216CF PP, 1_8密耳 Eastman Ecdel 9966 PCCE, 1.8密耳 束縛層: Dupont Bynel 4104, 0.4密耳 Admer QF300E, 0.4密耳 Dupont Bynel 4104 0.4密耳 障壁層: EMS Grilon EMS Grilon EMS Grilon EMS Grilon FG40NL, BM20SBG, 1.1密耳 FG40 NL, 1.1密耳 BM20SBG, U密耳 1_1密耳 束縛層: Dupont Bynel 4104, 0.4密耳 Admer QF300E, 0.4密耳 Dupont Bynel 4104 0.4密耳 密封層: 60% Huntsman 43M5A 15% Exxon LL3003 25% Kraton G1652, 3.5密耳 PP/PE/SEBS Cawiton Med PR4581, 3.5密耳 60% Huntsman 43M5A 15% Exxon LL3003 25% SEBS Kraton G1652, 3.5密耳
第二疊接膜的替代具體例包括具有樣品3或樣品4剝式 密封層,和,在此二構造中,PP/SEBS表層,之構造。此 第二疊接膜構造包括經順丁烯二酸酐改質的均聚物( ADMER® QF300E 和 QB510A)和共聚物(ADMER® 551A )束縛層。這些膜構造的所有具體例皆爲圖2中所示的五 層構造,其具有下列順序:表層2〇 /束縛層?.2 /障壁層24 /束縛層2 6 /密封層2 8。膜層的細節述於表9。 -26- 201105506 表9 :第二疊接膜調合物 N-1 N-2 N-3 N-4 N-5. 表層: Huntsman 43M5A, 1.8密耳 90% Huntsman 43M5A 10% Kraton G1643 1.8密耳 Huntsman 43M5A, 1.8密耳 束縛層: Admer QF300E, 0.4 密耳 Admer QF551A, 0.4密耳 Admer QB510A, 0.4密耳 障麵: liMS Grilon FG40 NL,1.1 密耳 束縛層: Admer QF300E,0.4 密耳 Admer QF551A, 0.4 密耳 Admer QB510A, 0.4 密耳 密封層: 60% PP Huntsman 43M5A 15% LLDPE Exxon LL3003 25% SEBS Kraton G1652, 3.5密耳 60% PP Huntsman 43M5A 15% LLDPE Exxon LL3003 25% SEBS Kraton G1643, 3.5密耳 60% PP Huntsman 43M5A 15% LLDPE Exxon LL3003 25% SEBS Kraton G1652, 3.5密耳 第三疊接膜構造的替代具體例包括具有樣品3、樣品4 或樣品5之摻合的密封層及PCCE或PP/SEBS表層。同樣地 ,PT-4包括經順丁烯二酸酐改質的均聚物pp,其摻有 SEBS以進一步韌化此構造。所有的三個疊接膜構造皆爲圖 2中所示的五層構造,其具有下列順序:表層20 /束縛層 22 /障壁層24 /束縛層26 /密封層28。膜層的細節述於表 1 0 〇 -27- 201105506 表ι〇 :第三疊接膜調合物 PT-1 PT-2 PT-3 PT-4 FGN-2 表層: 100% PCCE Eastman Ecdel 9966, 1.8密耳 90% PP Huntsman 43M5A 10% SEBS Kraton G1643, 1.8密耳 90% PP Huntsman X01466 10% SEBS Kraton G1643, i.8密耳 束縛層: Bynel4109f 0.4密耳 Admer QB510A, 0.4密耳 90% Admer QB510A 10% SEBS Kraton G1643, 0.4密耳 Modic P604V 0·4密耳 障壁層: 100% PA EMS Grilon FG40 NL,1.1 密耳 束縛層: Admer QB510A, 0.4密耳 90% Admer QB510A 10% SEBS Kraton G1643, 0.4密耳 Modic P604V 0.4密耳 密封層: 60% PP Huntsman 43M5A 15%LLDPE Exxon LL3003 25% SEBS Kraton G1652, 3.5密耳 70% Zelas 7023 30% PP Huntsman 43M5A, 3.5密耳 60% PP Huntsman 43M5A 15% LLDPE Exxon LL3003 25% SEBS Kraton G1643, 3·5密耳 60% PP Huntsman 43M5A 15% LLDPE Exxon LL3003 25% SEBS Kraton G1652, 3_5密耳 70% PP Huntsman X01466 22.5% SEBS Kraton G1643 7.5% Dowlex 2247G 3.5密耳 衝擊試驗和濁度的結果示於表11。結果顯示含有疊接 #2和#3及標準EMS FG40NL尼龍(TP-4和N-1至N-5)之具 體例的膜具有優於市售Maestro膜之改良的衝擊韌性。結 果亦顯示含有PCCE表層和標準EMS FG40NL尼龍的膜亦具 有優於市售Maestro膜之改良的衝擊韌性。 -28- 201105506 表11:障壁膜的衝擊和濁度性質 濁度 衝擊 膜名稱 濁度 嘸水), % 濁度(密 封側上 潤濕),% 最高載量, 千牛頓 最高標準化 能量,焦耳 /毫米 失效時的標 準化能量,焦 耳/毫米 形態 :^ wmmt m mmB 隱驗 PCCE-5 30.6 19.2 0.119 ΝΑ 5.82 韌性 PCCE-6 16.7 10.0 0.136 8.66 9.04 韌性 ToughPeeI-1 20.0 13.7 0.131 ΝΑ 6.66 韌性 ToughPeel-4 21.5 19.4 0.149 ΝΑ 7.99 韌性 Nylon-1 21·8 14.9 1.620 8.00 8.30 韌性 Nylon-2 21.3 15.0 1.550 7.60 8.00 韌性 Nylon-3 19.6 16.9 1.590 7.90 8.30 韌性 Nylon-4 26.5 20.2 1.470 6.90 7.70 軔性 Nylon-5 24.4 18.4 1.520 7.80 8.20 韌性 PTie-1 14.2 7.0 1.500 7.30 7.70 酿 PTic-2 12.2 6.0 1.370 7.40 7.80 韌性 PTie.3 18.3 13.6 1.430 7.30 7.50 韌性 PTie-4 21.2 16.7 1.360 6.70 7.10 韌性 以製造的材料混合物和製造的膜構造及測得的結果爲 基礎,發展新穎的剝式密封混合物和多層膜。這些剝式密 封混合物和膜構造的例子如下: 替代具體例中’剝式密封層膜能夠藉由將能夠剝開的 多層擠壓膜置於受熱的模具中而製造密封且不會有廢料形 成。藉由改變溫度’應該能夠於多種膜構造和厚度,在相 同的剝式層混合物上製造介於3牛頓/ 15毫米和30牛頓/ 1 5毫米之間的剝離力。必須於高於1 2 2 製造剝式密封。 此密封層必須能夠在121 °C滅菌且不會對剝離力造成負面 影響。此材料的一個例子是60%熔點高於145»c的pp無規 共聚物、25°/。SEBS和15%熔點高於12〇。〇的1^]:)11£。第二 個例子是60%-80% PP爲基礎的τρο (如ZeUs 7〇23 )與 -29- 201105506 20%-40%熔點高於130°C的無規共聚物PP之摻合物 個例子是70%熔點高於145 °C的PP無規共聚物、 3丑83和7.5%熔點高於120°(:的1^〇?£之摻合物。 前述具體例係針對強韌和透明之含有剝式密封 層膜。該膜的耐重錘衝擊性(dart impact resistan 示其提供產物中之容器受損耐性之良好的關聯性。 例中,多層膜的所欲耐重錘衝擊性高於7焦耳/毫 外,希望膜的一表面上潤濕時的濁度維持低於20% ,希望此膜的C02穿透性低於200立方公分/平方米 氣壓。此膜的例子是TP-4、N-l、N-3、N-4、N-5、 PT-3 和 FGN-2 » 實例3 自用於多層障壁膜的擠壓觀點,發現不含己內 尼龍 _6,6/6,10共聚物(BM20SBG,得自 EMS-Grivo 良好選擇。但是,以此構造爲基礎的膜的墜落耐性 錘衝擊性和氣體(〇2和C02 )穿透性明顯比目前含 龍-6爲基礎的障壁層者來得差。非晶狀尼龍本質上 著改良的氣體障壁性。(使用穿透率數據和混合物 可以計算指定等級之提供足夠的氣體障壁性的最低 。)據此,此硏究方式係令適當量的非晶狀尼龍劈 6,6/6,10共聚物摻合,以改良耐衝擊性和氣體障壁 持可接受的透明度,及全球醫療法規要求可接受白 收値。 。第三 2 2.5% 層的多 ce )顯 一具體 米。此 。最後 _天-大 PT-1 、 醯胺的 ry)係 、耐重 有以尼 具有顯 規貝IJ , 摻合量 !尼龍-性並維 勺UV吸 -30- 201105506 非晶狀尼龍與尼龍-6,6/6,10共聚物摻合並擠壓成單層 ,以得到耐衝擊性、透明度和穿透性的最佳平衡。辨視有 潛力的摻合物並摻入圖9(a) -9(c)中所示之下列膜構 造的一或多者中。圖9(a)係針對具有下列順序的多層膜 構造:表層110 /束縛層120 /障壁層130 /束縛層140 /密 封層150。圖9(b)係針對具有下列順序的多層膜構造: 表層210 /束縛層220 /障壁層230 /束縛層240 /核心層 25〇 /密封層260。圖9 ( c )係針對具有下列順序的多層膜 構造:表層310 /核心層320 /束縛層330 /障壁層340 /束 縛層3 5 0 /密封層3 6 0。之後測定多層膜的透明性、物理性 質、和/或墜落耐性。 目前結果 可取得的非晶狀尼龍等級(其包括EMS GRIVORY® G21 (尼龍 6I/6T ) 、EMS GRIVORY® HB5299 (尼龍 MXD6/MXDI共聚物)、EMS GRIVORY® HB7103(相同) 、和Dupont SELAR PA (尼龍6I/6T))進行小規模方法摻 合試驗。發現EMS GRIVORY® HB7103非晶狀尼龍具有透 明度、穿透耐性和機械性質的最佳組合。之後使用EMS GRILON® BM20SBG 尼龍-6,6/6,10 共聚物和 EMS GRIVORY® HB71 03 非晶狀尼龍的 50% : 50% 和 85% : 1 5% 摻合物製得單層膜。然後,這些單層的濁度、耐重錘衝擊 性和預測的穿透性與基線EMS FG40NL (其以尼龍-6爲基 礎)和BM20SBG比較。此比較的結果示於下面的表12。表 -31 - 201105506 12中,以可取得的供應商數據或測定的Baxter數據之混合 物規則爲基礎,計算不同相對濕度條件時的穿透性。過去 的工業經驗已顯示C02穿透性約比02高出四倍。 表12中的結果顯示,最佳摻合物是BM20SBG和 Η B 7 1 0 3的8 5 % : 1 5 %摻合物。此摻合物的耐重錘衝擊性約 是純BM20SBG的兩倍且預測的穿透性約等同於目前用於 Baxter’s Maestro膜的 FG40NL尼龍。85%: 15 % 慘合物的濁 度高於純化合物,但仍爲用於多層膜可接受者。當摻合比 改變爲50% : 50%時,未改良抗錘擊衝擊性質且因爲單層 膜於之後呈霧狀而使得濁度之提高無法被接受。摻合比可 能最適化,但8 5 % : 1 5 %摻合物的單層性質在目前的應用 上令人滿意。進一步試驗顯不將比例調整爲87.5 % BM20SBG / 12.5% HB7103 >提供或多或少較佳的性能。 -32- 201105506 表1 2 :不同尼龍和尼龍摻合物之性質 #1 #2 U5 #8 #10 ί調合物讎纖 Grilon F40NL 100 0 0 0 0 Grilon BM 20 SBG 0 100 0 50 85 Grivory HB7103 0 0 100 50 15 總計 100 100 100 100 100 雜f麵擊麵轉 最髙載量處的標準化 能量,焦耳/毫米 19.5 2.6 *a 3.6 5.0 失效的標準化能量, 焦耳/毫米 26.1 3.1 *a 4.1 6.0 形態 5/5韌性 1/5韌性, 4/5易碎 *a 5/5易碎 1/2韌性, 1/2易碎 菌之後的&觀 透明 透明 霧狀 透明 波狀指數,1=無波狀, 3=對照(40-10),5=最差 3 3 *a 3 3 5¾穿透性 ' 立方公分V平方米/ ‘ 薇米巴)·,ϋ 於〇%相對濕度測定 56b 110b 20b 於〇%相對濕度測定 34 66 於40%相對濕度測定 24b ΝΑ 16b 於40%相對濕度測定 TBD TBD 於85%相對濕度測定 56» 150b 20b msmm 於85%相對濕度測定 35 76 :雜_性-、'、 城龙方公分/平方米 .天-25微米巴> 於40%相對濕度測定 TBD TBD NA NA NA mmmrnmmm 濁度(乾燥>,% 7.5 6.3 1.6 19.4 11.8 濁度(密封側上潤濕),% 5.4 5.4 1.2 19.0 11.8 濁度(兩側上潤濕),% 4.3 3.7 0.9 18.3 11.2 *a =無法以單層形式高壓滅菌 b =得自EMS-Grivory數據表和公開報告之數據 比較在五層共擠壓膜構造中之85% : 15%摻合的尼龍 對純BM20SBG或FG40NL而完成硏究。硏究的膜的構造係 如圖2中所示的五層構造,其具有下列順序:表層20 /束 縛層22 /障壁層24 /束縛層26 /密封層28。此構造包括實 例2中描述的PT-3及表13中所示的下列構造。 -33- 201105506 表1 3 :膜調合物 NB-1 CF-1 CF-2 表層: 90% PP 10% SEI huntsman 43M5A 3S Kraton G1643, 1.8密耳 束縛層: Admer QB510A, 0.4密耳 Modic P604V, 0.4密耳 障壁層: 100% PA EMS Grilon BM20SBG,1.1 密耳 85% PA Grilon BM20SBG 15% PA GrivoryHB7103, 1.1密耳 束縛層: Admer QB510A, 0.4密耳 Admer QB510A, 0.4密耳 Modic P604V, 0.4密耳 密封層: 60% PP Huntsman 43M5A 15% LLDPE Exxon LL3003 25% SEBS Kraton G1643, 3.5密耳 70% PP Huntsman 43M5A 7.5% LLDPE Dowlex 2247G 22.5% SEBS Kraton G1643, 3.5密耳 濁度和衝擊試驗結果示於表14。CF-1 & CF-2膜(其 含有8 5 % : 1 5 %尼龍摻合物)的濁度和衝擊優於N B -1 (其 含有構造類似的純BM20SBG) 。CF-2的耐衝擊性優於CF-1 ,此因其含有以聚丙烯均聚物爲基礎的束縛層而非以共聚 物爲基礎的束縛層之故,此與在之前的操作所觀察到的趨 勢一致。CF-3的濁度亦明顯優於市售Maestro (其含有 FG40NL ),且耐衝擊性幾乎對等。構造類似的PT-3 (其 含有FG40NL)的濁度和耐衝擊性皆優於CF-3。 -34- 201105506 表14:具有不同的尼龍之五層尼龍障壁層的性質 濁度 衝 i ' - 膜名稱 濁度 嘸水), % 濁度(密 封側上 潤濕),% 最高載 量,千牛 頓 最高標準 化能量,焦 耳/毫米 失效時的標 準化能量 焦耳/毫米 形態 _ 麵 PTie-3 18.3 J3.6 0.143 7.3 7.5 細性 NylonBlend-l 22.8 17.8 0.128 5.2 6.2 wJlx_ 前性 CaproFree-2 17.7 14.9 0.138 5,8 6.4 韶性 CaproFree-3 19.6 16.1 0.139 6.3 7.2 韌性 圖9(b)和9(c)中所示的六層構造已展現優於五層 構造的耐衝擊性。經擠壓的多層膜構造樣品示於圖3。此 多層膜構造具有下列順序:表層30 /核心層32 /束縛層34 /障壁層36 /束縛層38 /密封層40。膜層的細節述於表15 -35- 201105506 表15 :六層膜調合物 CF-4 CF-5 CF-6 CF-7 CF-21 ZN-1 ZN-2 表層: 50%Zelas717 50% Zelas 90% 50% Zelas 50% Zelas 717 Huntsman 717 717 50% PP Huntsman P4G3Z-050F, X01466 0.5密耳 50% PP 50% PP 50% PP Huntsman 】0% Kraton Huntsman Huntsman P4G3Z, G1643, P4G3Z- P4G3Z, 0.5密耳 1.0密耳 050F, 0.5密耳 0_5密耳 核心層: 77% 70% Infuse 77% Vistamaxx 6102 77% 100% Zelas 717, Vistamaxx 9007 Vistamaxx 4.0密耳 6102 19% PP Huntsman 6102 30% PP X01462 19%PP Huntsman 19% PP Huntsman 43M5A, 4% Kraton G1643, Huntsman X01462 4密耳 4.0密耳 X01466 4% Kraton 4% Kraton G1643, G1643, 4.0密耳 4密耳 束縛層: ModicP604V » Admer Modic P604V, Admer 0.4密耳 QB510A, 0.4密耳 QB510A, 0.2密耳 0.2密耳 障壁層: 85% PA Grilon BM20SBG 87.5% PA 85% PA Grilon Grilon BM20SBG 15% PA Grivory HB7103, BM20SBG 1_1密耳 12.5% PA 15% PA Grivory HB7103, U 密耳 Grivory HB7103, 1.1密耳 束縛層: ModicP604V, Admer Modic P604V, Admer 0.4密耳 QB510A, 0.4密耳 QB510A, 0.2密耳 0.2密耳 密封層: 70% PP Huntsman 70% PP Huntsman 75% PP Huntsman 70% PP Huntsman 70% PP Huntsman 100% Zelas 100% Zelas X01462 X01462 X01462 X01462 X01466 7023, 7023 1.4密耳 1.8密耳 7.5% 7.5% 25% Versify 7.5% 7.5% LLDPE LLDPE DE3300, LLDPE LLDPE Dowlex Dowlex 1.4密耳 Dowlex Dowlex 2247G 2247G 2247G 2247G 22.5% 22.5% 22.5% 22.5% SEBS SEBS SEBS SEBS Kraton Kraton Kraton Kraton G1643, G1643, G1643, G1643, 1.4密耳 1·4密耳 1_8密耳 2.0密耳 以製造的材料混合物、製造的膜構造及測得的結果爲 基礎,可以藉由摻入符合所欲容器性質之不含己內醯胺的 尼龍摻合物,製造新穎的五和六或更多層的尼龍障壁膜構 造。一具體例中,就用於多層膜的尼龍障壁材料而言,所 -36- 201105506 欲的耐重錘衝擊性高於4.5焦耳/毫米。同時,尼龍障壁 層必須具有良好的耐熱性以因應高於130 °C的熱封溫度且 在兩側皆濕潤時的濁度低於1 5%。最後,於約85%相對濕 度(相對濕度),02穿透性必須低於80立方公分/平方 米-天-25微米巴。 在替代具體例中,摻有不含己內醯胺的尼龍障壁層的 多層膜之描述和它們的所欲性質如下: 一具體例中,多層膜係圖9(a)所示的五層膜,其具 有不含己內醯胺的尼龍障壁層。此膜的C02穿透性低於200 立方公分/平方米-天-大氣壓9此膜亦包含剝式密封層, 其可於介於4牛頓/ 15毫米和30牛頓/ 15毫米之間,藉由 在高於122 °C的溫度加熱的方式製造。膜的耐重錘衝擊性 顯示其提供與產品的容器受損耐性之良好關聯性。就多層 膜而言,所欲的耐重錘衝擊性可以高於6焦耳/毫米。替 代具體例中,希望膜在一表面上濕潤時,濁度維持低於 20%。此膜的一個例子是CF-3。 另一具體例中,多層膜是圖9(b) -9(c)所示的六 層膜,其具有不含己內醯胺的尼龍障壁層和強韌核心。此 膜的C02穿透性低於2〇〇立方公分/平方米-天-大氣壓。此 膜亦可包含剝式密封層’其可於介於4牛頓/ 15毫米和30 牛頓/ 15毫米之間,藉由在高於122 °C的溫度加熱的方式 製造。膜的耐重錘衝擊性顯示其提供與產品的容器受損耐 性之良好關聯性。就多層膜而言’所欲的耐重錘衝擊性可 以高於8焦耳/毫米。替代具體例中,希望膜在一表面上 -37- 201105506 濕潤時,濁度維持低於20%。此膜的例子是CF-4至CF-7。 此多層膜亦可包含的原料中,該原料不含有會自膜漏 出的物質(如硬脂酸鈣或鎂、芥醯胺、其他脂肪酸..等) 和/或在pH範圍介於2和10之間的溶液中形成微粒物質之 沉澱物。 應瞭解此處所述之目前較佳具體例的多種變化和修飾 將爲嫻於此技藝者顯見者。可以不偏離本主題之精神和範 圍且未減少其意圖優點的情況下作出這樣的變化和修飾。 因此,意圖藉所附申請專利範圍涵蓋這樣的變化和修飾。 【圖式簡單說明】 圖1係本發明之具體例中之單層膜的截面圖。 圖2係本發明之具體例中之五層膜的截面圖。 圖3係本發明之具體例中之六層膜的截面圖。 圖4係自本發明之具體例中的膜製造之容器的截面圖 〇 圖5係自本發明之具體例中的膜製造之多槽容器的截 面圖。 圖6係多層膜之剝式密封性能圖。 圖7係多層膜之剝式密封性能圖。 圖8係不同的膜調合物之典型剝式密封曲線圖。 圖9(a) - (c)係本發明之具體例中的多層膜之截面 圖。 -38- 201105506 【主要元件符號說明】 10 :膜 20 :表層 2 2 :束縛層 24 :障壁層 26 :束縛層 28 :剝式密封層 3 0 :表層 3 2 :障壁層 34 :束縛層 36 :障壁層 3 8 :束縛層 40 :剝式密封層 50 :容器 5 2 :第一側壁 54 :周圍接縫 56 :接管 58 :接管 7〇 :容器 72 :主體 74 :槽 76 :槽 80 :邊緣 82 :邊緣 -39 201105506 84 :邊緣 86 :邊緣 8 8 :可剝式封層 90 :通口 92 :通口 94 :通口 96 :通口 1 1 0 :表層 1 20 :束縛層 1 30 :障壁層 1 4 0 :束縛層 1 5 0 :密封層 2 1 0 :表層 2 2 0 :束縛層 2 3 0 :障壁層 2 4 0 :束縛層 2 5 0 :核心層 2 6 0 :密封層 3 1 0 :表層 3 2 0 :核心層 3 3 0 :束縛層 3 40 :障壁層 3 5 0 :核心層 3 6 0 :密封層
Claims (1)
- 201105506 七、申請專利範圍: 1. —種包含障壁層之膜,該障壁層包含不含己內醯 胺的尼龍混合物》 2. 如申請專利範圍第1項之膜,其中該不含己內醯胺 的尼龍混合物包含約75重量%至約95重量%聚醯胺6,6/6,10 共聚物和約5重量%至約25重量%非晶狀聚醯胺之摻合物。 3·如申請專利範圍第1項之膜,其中該不含己內醯胺 的尼龍混合物包含約87.5重量%聚醯胺6,6/6,10共聚物和約 1 2.5重量%非晶狀聚醯胺之摻合物。 4·如申請專利範圍第2或3項之膜,其中該非晶狀聚 醯胺選自聚醯胺MXD6/MXDI共聚物、聚醯胺6I/6T共聚物 、和它們的組合。 5.如申請專利範圍第1項之膜,其進一步包含表層和 剝式密封層(peel seal Uyer ),該表層和該剝式密封層接 合至障壁層的反面上。 6·如申請專利範圍第5項之膜,其中該表層包含選自 聚丙烯無規共聚物、聚丙烯均聚物、尼龍、苯乙烯-乙烯_ 丁烯-苯乙烯嵌段共聚物、共聚酯醚嵌段共聚物和彼等之 組合之組份。 7 ·如申請專利範圍第5項之膜,其中該剝式密封層包 含熔點高於140 °C的聚丙烯無規共聚物、苯乙烯-乙烯-丁 烯-苯乙烯嵌段共聚物和熔點高於n5〇c的直鏈低密度聚乙 烯之摻合物。 8 ·如申請專利範圍第5項之膜,其進一步包含至少一 -41 - 201105506 束縛層’該束縛層接合該表層及該剝式密封層中之至少一 者至障壁層。 9. 如申請專利範圍第8項之膜,其中該束縛層包含選 自順丁烯二酸化的直鏈低密度聚乙烯、順丁烯二酸化的聚 丙烯均聚物、順丁烯二酸化的聚丙烯共聚物和彼等之組合 之組份。 10. 如申請專利範圍第5項之膜,其進一步包含位於 介於該表層和該障壁層之間的核心層。 11. 如申請專利範圍第5項之膜,其進一步包含位於 介於該障壁層和該剝式密封層之間的核心層。 1 2 ·如申請專利範圍第1 〇或11項之膜,其中該核心層 包含選自聚丙烯均聚物、丙烯-乙烯無規共聚物、丙烯-乙 烯間規共聚物、聚丙烯彈性體、以丙烯爲基礎的彈性體、 以乙烯爲基礎的彈性體、苯乙烯-乙烯-丁烯-苯乙烯嵌段共 聚物、乙烯-丙烯橡膠改質的聚丙烯和彼等之組合之組份 〇 13.如申請專利範圍第10或11項之膜,其中該膜的 C02穿透性低於200立方公分/平方米-天-大氣壓。 1 4 .如申請專利範圍第1 0或1 1項之膜,其中當根據 ASTM D3763測定時,該膜的耐重錘衝擊性高於6焦耳/毫 米。 15. 如申請專利範圍第10或1 1項之膜,其中該膜的一 表面潤濕時,’濁度低於20%。 16. —種容器,其包含: -42- 201105506 藉包含障壁層的膜定義之主體,該障壁層包含不含己 內醯胺之尼龍混合物。 17. —個多槽容器,其包含: 藉膜定義之主體,該主體包括藉可剝式封層(peelable seal )分隔的至少兩個槽,該膜包含障壁層,該障壁層包 含不含己內醯胺之尼龍混合物。 -43-