SU945126A1 - Light-weight concrete mix - Google Patents
Light-weight concrete mix Download PDFInfo
- Publication number
- SU945126A1 SU945126A1 SU802910083A SU2910083A SU945126A1 SU 945126 A1 SU945126 A1 SU 945126A1 SU 802910083 A SU802910083 A SU 802910083A SU 2910083 A SU2910083 A SU 2910083A SU 945126 A1 SU945126 A1 SU 945126A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- sodium
- paste
- sand
- concrete mix
- cement
- Prior art date
Description
1one
Изобретение относитс к составам легкобетонных смесей с комплексными добавками и может быть использовано при изготовлении ограждающих конструкций из армированного легкого бетона на керамзитовом гравии и вспученном перлитовом песке в составе мелкого заполнител .The invention relates to compositions of light concrete mixes with complex additives and can be used in the manufacture of enclosing structures of reinforced lightweight concrete on expanded clay gravel and expanded perlite sand in the composition of fine aggregate.
Известна бетонна смесь, включающа в жущее, песок, алюминиевую пудру , известь, алкилсульфанол, д1ористый натрий и . воду 1.A concrete mixture is known, comprising, sand, aluminum powder, lime, alkylsulfanol, sodium dorium and. water 1.
Недостатком такой смеси вл етс высока водопотребность.The disadvantage of this mixture is high water demand.
Наиболее близкой по технической сущности и достигаемому эффекту к изобретению вл етс бетонна смесь, включающа минеральное в жущее , заполнитель, воду и комплексную добавку из кремнийорганической жидкости типа силиконата натри , алюминиевой пудры и сульфата натри 2.The closest in technical essence and effect to be achieved to the invention is a concrete mixture comprising a mineral sticking agent, aggregate, water, and a complex additive from silicone fluid such as sodium silicate, aluminum powder and sodium sulfate 2.
Однако добавка алюминиевой пудры несколько повышает жесткость и водопотребность бетонной смеси, что способствует образованию дополнит льного количества открытых пор и капилл ров , снижающих водозащитные свойства бетона.However, the addition of aluminum powder somewhat increases the rigidity and water demand of the concrete mix, which contributes to the formation of an additional number of open pores and capillaries, which reduce the waterproof properties of concrete.
Целью изобретени вл етс снижение капилл рного подсоса, влажностной усадки, увеличение коэффициентов морозостойкости и стойкости при переменном увлажнении и высушивании.The aim of the invention is to reduce capillary suction, moisture shrinkage, increase frost resistance and durability with variable wetting and drying.
Поставленна цель достигаетс тем, что легкобетонна смесь, включающа цемент, керамзитовый гравий, вспученный перлитовый и кварцевый песок, комплексную добавку и воду, содержит в качестве комплексной добавки алюмометилсиликонат натри , скрубберную пасту и гранулированный сульфат натри при следующем соотношении компонентов , мас.1The goal is achieved by the fact that a lightweight concrete mixture, including cement, expanded clay gravel, expanded perlite and quartz sand, a complex additive and water, contains sodium alumomethylsiliconate as a complex additive, scrubbing paste and granulated sodium sulfate in the following ratio of components, wt.
2020
20,4-2,120.4-2.1
Цемент Керамзитовый Ceramsite Cement
5,8-50,6 гравий Вспученный перлитовый ,6-6,5 Кварцевый 7.-9.3 Алюмометилсиликонат натри 0,02-0,05 Скрубберна паста 0,06-0,14 Гранулированный сульфат натри 0,183-0,260 Вода Остальное Добавка скрубберной пасты пластифицирует легкобетонную смесь, что повышает ее удобоукладываемость и сни жает войопотребность, уменьша тем самым количество открытых пор и капилл ров , определ ющих водопоглощени и капилл рную всасываемость бетона. Порообразующие свойства скрубберной пасты способствуют образованию замкнутын , равномерно распределенных ререзвных пор, повышающих стойкость бе тона к знакопеременным воздействи м (попеременное увлажнение - высушивание , замораживание - оттаивание). Кремнийорганическа жидкость АМСР-З придает водоотталкивающие свойства материалу, в результате чего его водопоглощение и капилл рный подсо уменьшаютс . Дл предупреждени тормоз щего действи скрубберной паст1 Ри кремний органической жидкости АМСР-3 на процессы охватывани и твердени бетона в состав комплексной добавки входит сульфат натри , способствующий упрочнению структуры керамзитоперлитобетона на ранних стади х твердени за счет ускоренного образовани гидросульфоалюминатного каркаса. Предлагаемые составы легкого Сетона и комплекснойдобавки приведены в табл.1. Свойства конструктивно-теплоизол ционного керамзитоперлитобетона с известной и предлагаемой добавками представлены в табл.2. Исследовани показывают, что предлагаема добавка снижает водопотребность легкрбетонной смеси и повышает ее удобоукладываемость в большей степени, чем добавка из алюминиевой пудрь, кремнийорганической жидкости ГКЖ-10 или ГКЖ-11 и сульфата натри (табл.1). При этом комплексна добавка со скрубберной пастой снижает водопоглощение и капилл рный подсос легкого бетона, имеющего в составе мелкого заполнител вспученный перлитовый песок, и способствует увеличению его прочности при сжатии (табл..2).. . Использование предложенного состава позвол ет примен ть конструктивно-теплоизол ционный керамзитоперлитобетон в однослойных .стеновых конструкци х жилых и промышленных здани х. При этом даже частична замена кварцевого или керамзитового песка вспученным перлитовым песком улучшает теплотехнические показатели ограждени , что позвол ет уменьшить его толщину,, а при сохранении - улучшить микроклимат помещений.5.8-50.6 gravel Expanded perlite, 6-6.5 Quartz 7.-9.3 Sodium aluminomethylsilonate 0.02-0.05 Scrubber paste 0.06-0.14 Granular sodium sulfate 0.183-0.260 Water Else Scrubber paste additive plasticizes the light concrete mix, which improves its workability and reduces your need, thereby reducing the number of open pores and capillaries that determine the water absorption and capillary absorption of concrete. The pore-forming properties of the scrubber paste contribute to the formation of closed, uniformly distributed rezving pores, which increase the resistance of the concrete to alternating effects (alternate moistening — drying, freezing — thawing). The silicone fluid, AMCP-3, imparts water-repellent properties to the material, as a result of which its water absorption and capillary pressure are reduced. To prevent the inhibitory effect of the scrubber paste 1 Silicon organic liquid AMCP-3 on the process of embracing and hardening of concrete, the complex additive includes sodium sulfate, which strengthens the structure of expanded clay peritone-concrete in the early stages of hardening due to the accelerated formation of the hydrosulfoaluminate cage. The proposed formulations of light Seton and complex additives are given in table 1. The properties of the structural thermal insulation keramzitoperlitobeton with known and proposed additives are presented in table 2. Studies show that the proposed additive reduces the water demand of a lightweight concrete mixture and increases its workability to a greater extent than an additive made of aluminum powder, silicone fluid GKZh-10 or GKZH-11 and sodium sulfate (Table 1). At the same time, the complex additive with scrubber paste reduces water absorption and capillary suction of lightweight concrete, which has expanded perlite sand in the fine aggregate, and contributes to an increase in its compressive strength (Table 2). The use of the proposed composition allows the use of structurally-insulated expanded clay perperite concrete in single-layer wall structures of residential and industrial buildings. At the same time, even a partial replacement of quartz or expanded clay sand with expanded perlite sand improves the thermal performance of the enclosure, which makes it possible to reduce its thickness, and, if saved, to improve the indoor microclimate.
г оо см --g oo see -
чОcho
vv
ооoo
чО Оcho o
г со см t-g with cm t-
о гabout g
-4о М-4o M
оо оLtd
олol
чО СПCHO SP
-3VO lA-3VO lA
г-«g- "
LALA
оabout
lAlA
оabout
чрchr
см cm
о о vOabout o vO
г- СПMr. SP
оо . 1А -аoo 1A-a
ОоOoh
- - .- -.
ш оw o
Claims (2)