SU913158A1 - Method of determination of viscous material humidity - Google Patents
Method of determination of viscous material humidity Download PDFInfo
- Publication number
- SU913158A1 SU913158A1 SU802951044A SU2951044A SU913158A1 SU 913158 A1 SU913158 A1 SU 913158A1 SU 802951044 A SU802951044 A SU 802951044A SU 2951044 A SU2951044 A SU 2951044A SU 913158 A1 SU913158 A1 SU 913158A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- mixture
- moisture
- water
- molding
- determining
- Prior art date
Description
Изобретение относится к методикам определения влажности вязких материалов, например формовочных масс строительных материалов, и может быть применено в промышленности для ускоренного, а также более точного определения влажности, например при производстве акустических плит "акмигран".The invention relates to methods for determining the moisture of viscous materials, such as molding masses of building materials, and can be used in industry for the accelerated, as well as more accurate determination of moisture, for example, in the manufacture of acoustic plates "acmigran".
Известен способ, согласно которому влажность формовочной массы "акмигран" определяют путем отбора проб массой 10 г, сушкой ее при 105°С в течение 24-х ч с последующим охлаждением и рассчетом по убыли массы (,13.There is a method according to which the humidity of the molding material "acigran" is determined by sampling a mass of 10 g, drying it at 105 ° C for 24 hours, followed by cooling and calculating by weight loss (, 13.
Однако такая продолжительность определения влажности не позволяет оперативно влиять на изменение влажности формовочной массы перед формовкой изделий и на режим сушки формовочных плит. Акустические плиты "акмигран" изготавливают из формовочной емассы, включающей минераль2However, such a duration of the determination of humidity does not allow to promptly influence the change in humidity of the molding material before the molding of products and the mode of drying of the molding plates. Acoustic plates "Akmigran" are made from molding emassa, including mineral2
ную вату, крахмал, каолин, парафин, борную кислоту и воду. Влажность состава формовочной массы меняется в пределах 200-ЗП0% (ло отношению к сухой массе). Технические требования к плитам "акмигран" обуславливают необходимость тщательно фиксировать влажность формовочной смеси. Колебания влажности формовочной массы (смеси) вызывает значительный' выход нестандартной продукции, имеющей существенное различие по объемной массе и прочности. Кроме того, погрешность в определении влажности указанным выше методом может достигать 10-20%, так как масса отобранной пробы по сравнению с массой отформованной плиты невелика, а вода в ней распределена неравномерно.cotton wool, starch, kaolin, paraffin, boric acid and water. The moisture content of the molding composition varies within 200-ZP0% (relative to dry weight). Technical requirements for the Akmigran slabs make it necessary to carefully fix the moisture of the molding sand. Fluctuations in the humidity of the molding material (mixture) causes a significant yield of non-standard products, which have a significant difference in bulk weight and strength. In addition, the error in determining the humidity of the above method can reach 10-20%, since the mass of the selected sample compared to the mass of the molded plate is small, and the water in it is unevenly distributed.
Наиболее близким по технической сущности к изобретению является способ определения влажности вязких материалов, например формовочных масс, заключающийся в измерении объемаThe closest in technical essence to the invention is a method for determining the moisture of viscous materials, for example molding masses, consisting in measuring the volume
33
и веса пробы смеси и расчете по полученным результатам влажности (2}.and the weight of the sample mixture and the calculation of the results of humidity (2}.
Этот способ предусматривает фиксирование массы одного литра сырьевого шлама. По этой массе с помощью тарировочной таблицы определяют влажность исходного шлама. Однако данный способ допускает большую погрешность в определении влажности , Ошибка может достигать 100%.This method involves recording the mass of one liter of raw sludge. For this mass, using the calibration table, determine the moisture content of the original sludge. However, this method allows a large error in the determination of humidity. The error can reach 100%.
Целью изобретения является повышение точности и сокращение времени определения влажности вязких материалов, например формовочной массы.The aim of the invention is to improve the accuracy and reduce the time to determine the moisture content of viscous materials, such as molding material.
Поставленная цель достигается тем, что согласно способу определения влажности вязких материалов, например формовочных масс, заключающемся в измерении объема и веса пробы смеси и расчете по полученным результатам влажности, из пробы смеси удаляют газ, путем разбавления исследуемого материала водой при перемешивании, причем разбавление ведут до получения равенства объемов смеси до и после перемешивания, а при расчетах учитывают количество израсходованной на разбавление воды.This goal is achieved by the fact that according to the method for determining the moisture of viscous materials, for example molding masses, consisting in measuring the volume and weight of a sample mixture and calculating the moisture content, the gas sample is removed from the mixture by diluting the material under study with water while stirring obtain equality of the volumes of the mixture before and after mixing, and the calculations take into account the amount of water used for dilution.
Способ определения влажности вязких материалов, например формовочной массы "акмигран", осуществляется следующим образом.The method for determining the moisture of viscous materials, such as molding material "Acmigran", as follows.
Отбирают пробу вязкого материала, например формовочной массы, помещают ее в мерный сосуд и разбавляют водой, перемешивают и дают отстояться. Если объем разбавленной водой массы ниже уровня отметки мерного сосуда - добавляют воду, если объем разбавленной выше уровня отметки мерного сосуда - излишек воды сливают, Снова перемешивают смесь и дают отстояться. Если объем не изменился (уровень воды на уровне отметки мерного сосуда), это свидетельствует о полном удалении газовой фазы из смеси. После этого взвешивают сосуд с исследуемым материалом и из тарировочной таблицы определяют его влажность. Тарировочную таблицу составляют на основании опытных данных, связывающих влажность исследуемого вязкого материала с массой единицы объема разбавленной водой смеси. Ни же приводятся примеры определения влажности формовочной массы "акмигран" предложенным способом.A sample is taken of a viscous material, for example a molding compound, placed in a measuring vessel and diluted with water, mixed and allowed to stand. If the volume of the mass diluted with water is below the level of the measuring vessel, water is added, if the volume of the measuring vessel diluted above the level is the excess water is drained, Mix the mixture again and allow it to settle. If the volume has not changed (the water level is at the level of the vessel measuring mark), this indicates the complete removal of the gas phase from the mixture. After that, the vessel with the test material is weighed and its humidity is determined from the calibration table. The calibration table is based on the experimental data linking the humidity of the viscous material under investigation with a mass of a unit volume of the mixture diluted with water. There are also examples of determining the moisture content of the molding material "acigran" by the proposed method.
Пример 1 . Навеску пробы формовочной массы "акмигран" массойExample 1 A portion of the sample molding mass "Akmigran" mass
913158913158
4four
450 г разбавляют водой массой 640 г, перемешивают. Контролируют полноту удаления газовой фазы добавлением или убавлением воды до достижения450 g diluted with water weighing 640 g, mix. Control the completeness of the removal of the gas phase by adding or subtracting water to achieve
5 постоянства объема по мерной отметке сосуда при отстаивании. Взвешивают 1 л смеси, его масса составляет 1077. Из таблицы находим исходную влажность формовочной массы. Она соЮ ставляет в данном случае 205%.5 constancy of the volume at the measured elevation of the vessel when standing. Weigh 1 liter of the mixture, its weight is 1077. From the table we find the initial moisture content of the molding compound. It puts in this case 205% in this case.
Пример 2 . Навеску пробыExample 2 Sample sample
формовочной массы "акмигран" массой 450 г разбавляют водой массой 640 г и перемешивают. Контролируют полно15 ту удаления газовой фазы добавлением или убавлением воды до достижения постоянства объема по мерной отметке сосуда при отстаивании. Взвешивают 1 л смеси, его масса составляетmolding mass "acmigran" weighing 450 g is diluted with water weighing 640 g and stirred. Controlling the complete removal of the gas phase by adding or subtracting water until a constant volume is reached at the vessel's measured level during settling is monitored. Weigh 1 liter of the mixture; its mass is
20 Ю57.20 J57.
Из таблицы находят исходную влажность формовочной массы. Она составляет в данном случае 255%. Массы исходной пробы материала и воды подби25 рают таким образом, чтобы обеспечитьFrom the table find the initial moisture content of the molding material. It is in this case 255%. The masses of the initial sample of material and water are selected in such a way as to ensure
полноту удаления из материала газовой фазы. Для формовочной массы "акмигран" с влажностью от 200¾ и выше это соотношение определено какcomplete removal of the gas phase from the material. For the molding material "acmigran" with humidity from 200¾ and above, this ratio is defined as
30 2:3 и более, где на 2 части исследуемого материала приходится не менее 3-х частей воды.30 2: 3 and more, where 2 parts of the studied material have at least 3 parts of water.
Предложенный способ позволяет ус35 коренно в течение 3-6 мин зафиксировать влажность формовочной массы и таким образом оперативно корректировать технологический процесс производства плит; "акмигран".The proposed method allows us 35 radically for 3 - 6 minutes to fix the moisture of the molding material and thus promptly correct the technological process of production of plates; "Akmigran".
4040
Технико-экономическии эффект изобретения заключается в сокращении времени на определение влажности материала с 24 ч до 3-6 мин и уменьшением максимальной погрешности определения влажности с 20% до 5%.Feasibility effect of the invention is to reduce the time for determining the moisture content from 24 hours to 3 - 6 minutes and the maximum decrease of the error in determining the humidity from 20% to 5%.
В результате оперативного воздействия на технологический процесс снижается выход нестандартной продукции.As a result of the operational impact on the process, the output of non-standard products is reduced.
Claims (1)