SU910548A1 - Complex additive - Google Patents
Complex additive Download PDFInfo
- Publication number
- SU910548A1 SU910548A1 SU802958918A SU2958918A SU910548A1 SU 910548 A1 SU910548 A1 SU 910548A1 SU 802958918 A SU802958918 A SU 802958918A SU 2958918 A SU2958918 A SU 2958918A SU 910548 A1 SU910548 A1 SU 910548A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- concrete
- additive
- mix
- workability
- concrete mix
- Prior art date
Description
(5) КОМПЛЕКСНАЯ ДОБАВКА(5) COMPLEX ADDITIVE
Изобретение относитс к области строительства, а именно, к составам; комплексных противоморозных добавок дл бетонных смесей, примен емых при возведении бетонных и железобетонных монолитных конструкций В различных, в том числе в СУРОВЫ.Х климатических , услови х. Известна комплексна добавка дл бетонной смеси , состо ща и.з .алюмината натри и сульфитно-дрожжевой браж ки. Количество алюмината натри составл ет % от массы воды затворениЯ| а сульфитно-дрожжевой бражки 0,1% от массы цемента 1 Известна комплексна добавка . способствует повышению плотности оетонз; но не обеспечивает его твердение при отрицательных температурах. Наиболее близкой к изобретению по технической сущности и достигаемому результату вл етс комплексна добавка |.дл бетонной смеси , включа юща апюминаг натри и хлорное желе30 при следующем соотношении компонентов , массД: Алюминат натри 87,5 . Хлорное железо 12,5 Указанна добавка, также как и предыдуща , повышает плотность бетона, ускор ет сроки его твердени . Однако использование известной добавки не ускор ет твердение бетона при отрицательных температурах, ухудшает удобоукладываемость бетонной смеси. Добавка не обеспечивает повышени морозостойкости и водонепроницаемости бетона, твердеющего при отрицательных температурах. Целью изобретени вл етс повышение удобоукладываемости бетонной смеси, водонепроницаемости и морозостойкости бетона. Достигаетс это тем, что комплексна добавка в бетонную смесь, преимущественно дл зимнего бетонировани , включающа алюминат матрип и хпористую соль, содержит в камее гвр лсм11с 3910 той соли хлористый натрий и дополнительно этиленгликоль при следующем соотношении компонентов, масс,: Алюминат натри 60-85 Хлористый натрий 10-35 Этиленгликоль 0, Количество компонентов добавки, вводимое в бетонную смесь, назначаетс исход из комплекса технических требований, предъ вл емых к бетонной смеси и бетону. Оно колеблетс в интервале значений от 0,1 до S% от массы цемента. Расход добавки на 1 м бетона составл ет в среднем 5 кГ. Дл определени оптимального сое , тава комплексной добавки и сравнени The invention relates to the field of construction, namely, to compositions; complex antifreeze additives for concrete mixtures used in the construction of concrete and reinforced concrete monolithic structures in various, including in SURY.HY climatic conditions. A known complex additive for concrete mix, consisting of sodium aluminate and sulphite yeast mash. The amount of sodium aluminate is% by weight of the mixing water | and sulphite-yeast brew 0.1% by weight of cement 1 A complex additive is known. helps to increase the density of oetons; but does not ensure its hardening at low temperatures. Closest to the invention of the technical nature and the achieved result is a complex additive | .dl concrete mix, including sodium pumin and chlorine gel 30 in the following ratio of components, mass: Sodium aluminate 87.5. Ferric Chloride 12.5 This additive, like the previous one, increases the density of concrete, accelerates its curing time. However, the use of a known additive does not accelerate the hardening of concrete at low temperatures, impairs the workability of the concrete mix. The additive does not provide an increase in frost resistance and water resistance of concrete hardening at low temperatures. The aim of the invention is to improve the workability of the concrete mix, water resistance and frost resistance of concrete. This is achieved by the fact that the complex additive in the concrete mix, mainly for winter concreting, including matriuzed aluminate and hydrochloric salt, contains sodium chloride and, in addition, ethylene glycol in the cameo hvp cm11c 3910 of that salt, in the following ratio of components, masses: sodium aluminate 60-85 chloride sodium 10-35 ethylene glycol 0; the number of additive components introduced into the concrete mix is based on the set of technical requirements for the concrete mix and concrete. It ranges from 0.1 to S% by weight of cement. The consumption of the additive per 1 m of concrete averages 5 kg. To determine the optimal soy, tava complex supplement and
Характеристика бетонных смесей и бетонаCharacteristics of concrete mixes and concrete
СмесиMixes
II
IIII
IIIIII
IVIV
VV
VI (прототип)VI (prototype)
Таблица 1Table 1
Таблица 2table 2
66
Claims (2)