SU691423A1 - Optical glass - Google Patents

Optical glass

Info

Publication number
SU691423A1
SU691423A1 SU782605317A SU2605317A SU691423A1 SU 691423 A1 SU691423 A1 SU 691423A1 SU 782605317 A SU782605317 A SU 782605317A SU 2605317 A SU2605317 A SU 2605317A SU 691423 A1 SU691423 A1 SU 691423A1
Authority
SU
USSR - Soviet Union
Prior art keywords
glass
cao
quality
optical glass
mgo
Prior art date
Application number
SU782605317A
Other languages
Russian (ru)
Inventor
Ефим Исарович Галант
Original Assignee
Предприятие П/Я Р-6681
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Предприятие П/Я Р-6681 filed Critical Предприятие П/Я Р-6681
Priority to SU782605317A priority Critical patent/SU691423A1/en
Application granted granted Critical
Publication of SU691423A1 publication Critical patent/SU691423A1/en

Description

(54) -ОПТИЧЕСКОЕ СТЕКЛО(54) OPTICAL GLASS

Изобретение относитс  к области производства оптического стекла типа боросиликатного крона с показателем преломлени  птз l,Slo, коэффициентом дисперсии Уд 64. Стекло предна значено дл  использовани  в качеств линз, призм, пластин любого размера и качества в оптических и других при борах и устройствах различного назна чени ; оно может буть также эффектив но использовано в волоконной оптике в частности, дл  линий св зи. Известно оптическое стекло, включающее , вес.%: 40-61 12-36 AEjOj 3-6 7-12 ЫагО 1, S-4 0,5-2 0,1-0,6 0,5-5 1-4 до 2 ДО 2 0,5-0,5 Стекло имеет показатель преломле ни  п-д- 1,5-1,ЬЗ и низкую кристалли зационную способность. Наиболее близким к изобретению по технической смутности и Достигаемому результату  вл етс  оптическое стекло 17.1 ,которое включает слеттх гпие компоненты, вес.%: SiOi69 BiOj 11 ASiOj0,3 ВаО2,8 ,5 NajO 10,4 Однако указанному стеклу присущи такие недостатки, как высока  летучесть его компонентов из расплава, котора  составл ет при - 50 мг/см час, широкий интервал температуры кристаллизации от 600 до 1400°С при в адержке 24 ч, во многом вызванна  изменени ми состава поверх ностного сло  стекла. Указанные недостатки практически исключают возможность получени  крупных однородных заготовок, делают невозможным использование передовых производственных процессов непрерывной плавки и формовани  самого массового оптического стекла. Цель изобретени  - снижение летучести компонентов при варке и температурного интервала кристаллизации.The invention relates to the field of production of optical glass of the borosilicate crown type with refractive index ls, Slo, dispersion coefficient Ud 64. The glass is intended for use as lenses, prisms, plates of any size and quality in optical and other devices and devices. ; it can also be effectively used in fiber optics, in particular, for communication lines. Known optical glass, including, wt.%: 40-61 12-36 AEjOj 3-6 7-12 LiO 1, S-4 0.5-2 0.1-0.6 0.5-5 1-4 to 2 TO 2 0.5-0.5 Glass has a refractive index of p-d-1.5-1, b3 and low crystallization ability. The closest to the invention in technical confusion and Achievable result is optical glass 17.1, which includes the following components, wt%: SiOi69 BiOj 11 ASiOj0.3 BaO2.8, 5 NajO 10.4 However, this glass has disadvantages such as high The volatility of its components from the melt, which is at –50 mg / cm h, is a wide range of crystallization temperatures from 600 to 1400 ° C with at 24 hours, largely due to changes in the composition of the surface layer of glass. These drawbacks practically exclude the possibility of obtaining large homogeneous blanks, make it impossible to use advanced industrial processes for continuous melting and molding the mass optical glass itself. The purpose of the invention is to reduce the volatility of the components during cooking and the temperature range of crystallization.

691423691423

Это достигаетс  тем, что оптикое стекловключает ингредиенты в следующем соотношении. вес.%: SiOi66-68This is achieved in that the optical glass includes the ingredients in the following ratio. wt.%: SiOi66-68

BtOj 8,5-9,5 BaO . 2,5-5 KjOIlrl4BtOj 8.5-9.5 BaO. 2.5-5 KjOIlrl4

„.„:..,....„...-« JJajО. 3-:S„.„: .., .... „...-“ JJaJO. 3-: S

CeOj 0,2-2 MgO 2-4 CaO0,5-2 Шихту плав т в кварцевых сосудах емкостью 100 л в газовых печах при 14ЗО-с, осветл ют, охлаждают в печи ;при размещивании (60-30 об/мин) в об ласти 1450-1050 С, с последующей студкой вне печи до комнатной тем:пературы под кожухом. Длительность всей плавки составл ет 18-20 ч. Крем неземным сырьем служит молотый кварц с 0,003% железа. Отдельные йлавки провод т-в мал ой-, электропечи в: платиновыхТигл х. . Полученное стекло испытано на лётучест .ь при и на кристаллизацию -Ъри выдержке 24 ч в градиентной печи. Летучесть стекла при 1400 составл ет 29 мг/см час; область п©верхностной кристаллизации стекла ТОО-бЗО С. . Стекло практически не кристаллиэуетс .в рабочей зоне температур при непрерывной, или периодической плав ке. Описываемое стекло позволит усовершенствовать технологию нового стекла, особенно перевод его на непрерывный способ плавки, чтобы обес CeOj 0.2-2 MgO 2-4 CaO0.5-2 The mixture is melted in quartz vessels with a capacity of 100 liters in gas ovens at 143-s, clarified, cooled in a furnace; during placement (60-30 rpm) in Oblasts 1450-1050 С, followed by an omega out of the oven to room temperature: temperatures under the casing. The duration of the entire melting is 18-20 hours. The cream of unearthly raw materials is ground quartz with 0.003% iron. Separate fishing pins lead into small oi and electric furnaces in: platinum crucibles. . The resulting glass was tested for volatility with and for crystallization — at 24 h in a gradient furnace. Glass volatility at 1400 is 29 mg / cm h; the region of p © surface crystallization of glass TOO-BSO S. The glass practically does not crystallize in the working zone of temperatures with continuous or periodic melting. The described glass will allow to improve the technology of the new glass, especially its transfer to a continuous method of melting in order to ensure

в стекле снижено содержание лету чих компонентов дополнительно введены нелетучие компоненты Мдои СаО, что в сочетании с новым соотношением компонентов позвол ет получить оптическое стекло с п 1,516,У2)64 меньшей летучести и кристаллизации при высоких температурах.In the glass, the content of volatile components is reduced; non-volatile components of Mdoi CaO are additionally introduced, which, in combination with the new ratio of components, makes it possible to obtain optical glass with n 1.516, U2) 64 less volatility and crystallization at high temperatures.

Claims (2)

В таблице даны примеры составов, оптических свойств и качестве стекла . печить резкий рост производительности труда-, выход годного, снижение потерь и отходов, повышение качества стекла, Ьсобённо по однородности , в том числе загртово к большого размера , волоконно-оптических элементов, включа  сверхчистыедл  линий св зи. Формула изобретени  Оптическое стекло, включающее SiOt, , БаО/ KjO, , АЗ Озили 3eOj ,отличающеес   тем, что, с целью снижени  летучести компонейтов при варке и температурного интервала кристаллизации, оно дополнительно содержит MgO и СаО при следующем соотношении ингредиентов,, вес.%: 66-68 8,5-9,5 2,5-5 А8гО4ИЛИ GeOa 0,2-2 MgO 2-4 CaO 0,5-2 Источники информации, прин тые во внимание при экспертизе 1. Авторское свидетельство СССР 185468, кл. С 03 С 3/08, 1965. The table gives examples of the composition, optical properties and quality of glass. to bake a sharp increase in labor productivity, yield, reduction of losses and waste, improving the quality of glass, especially for uniformity, including loading to large size, fiber-optic elements, including ultra-pure communication lines. Optical glass including SiOt, BaO / KjO, AZ Ozili 3eOj, characterized in that, in order to reduce the volatility of the components during cooking and the crystallization temperature range, it additionally contains MgO and CaO in the following ratio of ingredients, wt.% : 66-68 8.5-9.5 2.5-5 A8gO4IL or GeOa 0.2-2 MgO 2-4 CaO 0.5-2 Sources of information taken into account during the examination 1. USSR author's certificate 185468, cl . From 03 On 3/08, 1965. 2. Технологи  стекла под ред. И. И. Китайгородского, М, Гиэлегпром, 1939, т. 2, с, 374.2. Glass technology ed. I. I. Kitaygorodskogo, M, Gielegprom, 1939, v. 2, p. 374.
SU782605317A 1978-04-17 1978-04-17 Optical glass SU691423A1 (en)