SU536145A1 - Piezoceramic material - Google Patents

Piezoceramic material

Info

Publication number
SU536145A1
SU536145A1 SU2004545A SU2004545A SU536145A1 SU 536145 A1 SU536145 A1 SU 536145A1 SU 2004545 A SU2004545 A SU 2004545A SU 2004545 A SU2004545 A SU 2004545A SU 536145 A1 SU536145 A1 SU 536145A1
Authority
SU
USSR - Soviet Union
Prior art keywords
woj
published
class
properties
metal fluoride
Prior art date
Application number
SU2004545A
Other languages
Russian (ru)
Inventor
Галина Ефимовна Савенкова
Всеволод Валентинович Климов
Original Assignee
Предприятие П/Я А-3481
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Предприятие П/Я А-3481 filed Critical Предприятие П/Я А-3481
Priority to SU2004545A priority Critical patent/SU536145A1/en
Application granted granted Critical
Publication of SU536145A1 publication Critical patent/SU536145A1/en

Description

(54) ПЬЕЗОКЕРАМИЧЕСКИЙ МАТЕРИАЛ(54) PIEZOCERAMIC MATERIAL

1one

Изобретение относит- ч к материалам, примен емым в радиоэлектронике.The invention relates to materials used in radio electronics.

Известен пьезокерамическиЗ материал на основе твердого раствора Vb2f Ti 0 (где ,4-0,6), в котором свинец частично замещен на стронций, барий, кальций с добавками , Еll Материал обладает недостаточно высокими значени ми пьезомодулей 3 и cljj.Piezoceramic3 material is known on the basis of the Vb2fTi0 solid solution (where, 4-0.6), in which lead is partially replaced by strontium, barium, calcium with additives, Еll The material has insufficiently high values of piezomodules 3 and cljj.

Наиболее близким по технической сущ- кости и достигаемому результату  вл етс  пьезокерамический материал на основе цирконата-титаната свинца с частичным замещением свинца на стронций и добавками и N1)0 Г2. Недостатком данного мате риала  вл ютс  сравнительно невысокие значени  пьезомодулей д,. и особенно .The closest in technical essence and the achieved result is a piezoceramic material based on lead zirconate titanate with partial replacement of lead by strontium and additives and N1) 0 Г2. The disadvantage of this material is the relatively low values of the piezomodules d ,. and especially .

Цель изобретени  - повышение пьезоэлектрических модулей d, и dThe purpose of the invention is to increase the piezoelectric modules d, and d

5Это достигаетс  тем, что материал, вклю- 5This is achieved by the fact that the material, including

чающий PI)О, S hО , I г O.J, Т1 О.., и добавкиB-ijOg NbjOj; дополнительно содержит PI PI) O, S hO, I g O.J, T1 O., and additives B-ijOg NbjOj; additionally contains

S.SS.S

фторид металла: Noi , К , О( или ъг- , при metal fluoride: Noi, K, O (or fg-, with

CdCd

Zr следующем соотношении компонентов, вес.%:Zr is the following ratio of components, wt.%:

ТЧэО63,34-69,22ТЧэО63,34-69,22

16,44-23,31 9,75-15,54 0,32- 3,36 0,251 ,50 0,251 ,50 О,101 ,00 О,251 ,5О 1,ОО 0,10х добавок приводит к с высокой диэлектри (до 315О), коэс|х})Иической св зи Кр16.44-23.31 9.75-15.54 0.32-3.36 0.251, 50 0.251, 50 O, 101, 00 O, 251, 5O 1, OO 0.10 x additives result in a high dielectric ( up to 315O), coees | x}) of the Iic connection

.-12.-12

лем т (до 265-Ю lem t (up to 265

г 12 djj (до 73О-10 g 12 djj (up to 73O-10

Материал получают следующим образом.The material is obtained as follows.

После помола исходных веществ из полученной щихты изготовл ют брикеты. Брикеты подвергают синтезу при 850°С в течение 2 час, затем тщательно измельчают в порощок с размером частиц 3-5 мкм, после чего добавл ют раствор поливинилового спирта в качестве св зки и прессуют издели  заданной формы и величины. Спреесованные издели  спекают при 1220-1230°С в атмосфере окиси свинца.After grinding the starting materials, briquettes are made from the resultant solid. Briquettes are synthesized at 850 ° C for 2 hours, then thoroughly crushed into powders with a particle size of 3-5 µm, after which a solution of polyvinyl alcohol is added as a binder and pressed into articles of a given shape and size. The packed products are sintered at 1220-1230 ° C in an atmosphere of lead oxide.

После спекани  образцы ишифуют. Электроды нанос т вжиганием при 700°С в течение 20 мин.After sintering, the samples are encrypted. Electrodes are applied by firing at 700 ° C for 20 minutes.

Пол ризацию изделий осуществл ют в полисилоксановой жидкости при 100°С в теСостав , вес.лThe polarization of the products is carried out in a polysiloxane fluid at 100 ° C in the composition, weight l

Claims (2)

Формула изобретени  Пьезокерамический материал на основе твердого раствора Pt)(,4-O,6), включающий PljO , Z.h 0 , Ti 0, и добавки B-t,jOj и NUjOj., отличающийс  тем, что, с целью повышени  пьезоэлектрических модулей (. и d, он дополнительно содержит WOj . и фторид металла: Noi, К , Со или Xf при следующем соотнощении компонентов, вес,%:Claims Piezoceramic material based on Pt solid solution (, 4-O, 6), including PljO, Zh 0, Ti 0, and additives Bt, jOj and NUjOj., Characterized in that, in order to increase the piezoelectric modules (. And d, it additionally contains WOj. and metal fluoride: Noi, K, Co or Xf with the following ratio of components, weight,%: Т ЪО63,34-69,22T b63,34-69,22 IhOa16,44-23,31IhOa16,44-23,31 чение 1,0-1,5 час в посто нном поле с напр женностью 3-4 кв/мм.1.0-1.5 hours in a constant field with a strength of 3-4 kV / mm. Благодар  сочетанию высоких значений пьезомодулей dj и c3jj коэффициента электромеханической св зи Кр, диэлектрической проницаемостью 6 , данный материал может с успехом примен тьс  в гидроакустике. В таблице приведены свойства предлагаемого материала.Due to the combination of high values of the piezomodules dj and c3jj of the electromechanical coupling coefficient Kp, dielectric constant 6, this material can be successfully used in hydroacoustics. The table shows the properties of the proposed material. СвойстваProperties , , 9,75-15,54 0,32- 3,36 SrO Bi,0 0,25- 1,50 9.75-15.54 0.32- 3.36 SrO Bi, 0 0.25- 1.50 Nt,,0 0,25- 1,50 WOj Nt ,, 0 0,25-1,50 WOj 0,10- 1,00 5b,0,0.10-1.00 5b, 0, 0,25- 1,50 0,25-1,50 фторид металла 0,10- 1,00metal fluoride 0.10-1.00 Источники информации, прин тые во вниание при экспертизе:Sources of information taken into consideration in the examination: 1,Патент Японии № 43-10713, класс 6 С 23, опубликовано 1968.1, Japan Patent No. 43-10713, class 6 C 23, published 1968. 2.Патент США № 3.580.846, класс 52-62.9, опубликовано 1971.2. US Patent No. 3,580,846, class 52-62.9, published 1971.
SU2004545A 1974-03-14 1974-03-14 Piezoceramic material SU536145A1 (en)