Description

Изобретение относитс  к области произ- водства катализаторов, примен емых в химической промышленности дл  гидрировани  например, жиров, Сахаров.The invention relates to the manufacture of catalysts used in the chemical industry for the hydrogenation of, for example, fats, sugars.

Известен способ повышени  активности сплавного катализатора, например никельалюминиевого , путем закалки сплава в воде с последующим-выщелачиванием.There is a method of increasing the activity of an alloy catalyst, for example, nickel-aluminum, by quenching the alloy in water, followed by leaching.

Однако такой катализатор про$шл ет невысокую активность в реакци х гидрирова - However, such a catalyst exhibits low activity in the hydrogenation – hydrogen reaction.

НИН.Nin

Цель изобретени  - повышение активности сплавного ката1шзатора.The purpose of the invention is to increase the activity of the alloy catcher.

Это достигаетс  тем, что исходный сплав предварительно до закалки подверга- ют термической обработке при 750-950°С не менее 1 часа.This is achieved by preheating the initial alloy to heat treatment at 750–950 ° C for at least 1 hour.

Это позвол ет повысить активность сплавного катализатора на 5О-6О% по сравнению с катализаторами, не подвергнутыми термической обработке.This makes it possible to increase the activity of the alloy catalyst by 5% –6% compared with catalysts that have not been heat treated.

Сплав катализатора готов т следующим образом.The catalyst alloy is prepared as follows.

Алюминий помещают в кварцевый тигел кусочками 3-5 мм, затем тигель нагревают в высокочастотной печи до расплавлени  алюмини , после чего ввод т никель. Перемещивание сплава производ т индукционным током после алюмотермической реакции в течение 2 мин при 17ОО18ОО°С . Далее сплав охлаждают.The aluminum is placed in a quartz crucible with pieces of 3-5 mm, then the crucible is heated in a high-frequency furnace until the aluminum melts, after which nickel is introduced. The displacement of the alloy was made by induction current after the aluminothermic reaction for 2 minutes at 17OO18OO ° C. Next, the alloy is cooled.

Охлаждение сплава провод т при 2О С в чугунной изложнице и в воде.The cooling of the alloy is carried out at 2 ° C in a cast-iron mold and in water.

Сплав, охлажденный в чугунной изложнице , подвергают термической обработке при 75О-95О°С в зависимости от состава никель-алюминиевого сплава.An alloy cooled in a cast-iron mold is subjected to heat treatment at 75 ° -95 ° C, depending on the composition of the nickel-aluminum alloy.

Выбор температуры в этом интервале обуславливаетс  химическим составом сплава и микроструктурой, получающейс  после указанной термической обработки в результате фазовых превращений.The choice of temperature in this range is determined by the chemical composition of the alloy and the microstructure resulting from this heat treatment as a result of phase transformations.

Роль термической обработки заключаетс  в том, что сплав при нагреве выше критических точек (75О и 95О С) претерпевает фазовые превращени  и при последующем охлаждении в воде (при 20°С) кристаллизуетс  со структурой, позвол ю - щей получать высокую активность катализатора . При охлаждении же жидкого расплава в воде аналогичные фазовые превра щени  происход т не полностью или совсем не происход т. Температурную обработку провод т в муфельной печи. Образцы катализатора (куски 2О-30 мм) загружают в печь при . После выравнивани  температуры по объему печи образцы выдержи вают в ней в течение 1 часа, а затем охлаждают в воде (при 20 С) и дроб т фракции 0,25 мм. Ката1шзаторы активируют путем выщеThe role of heat treatment is that the alloy under heating above critical points (75 ° C and 95 ° C) undergoes phase transformations and, upon subsequent cooling in water (at 20 ° C), crystallizes with a structure that allows for high catalyst activity. When cooling a liquid melt in water, similar phase transformations do not fully or completely do not occur. The heat treatment is carried out in a muffle furnace. Samples of the catalyst (pieces O-30 mm) are loaded into the furnace at. After the temperature was equalized over the furnace volume, the samples were kept in it for 1 hour, and then cooled in water (at 20 ° C) and fractions were divided into 0.25 mm. Kata1zzator activate by

Исходное состо ние образцовInitial state of samples

Состав сплава, вес. %The composition of the alloy, weight. %

Охлажденные в изложнице Chilled Mold

50,0 (при 20°С) SO.O50.0 (at 20 ° С) SO.O

Охлажденные в воде (при 20 С)Chilled in water (at 20 С)

о жеabout the same

Охлажденные в чугункой изложнице и термообработанные при 90О°С, выдержка 1 час, охлаждение в воде/Cooled in a cast iron mold and heat-treated at 90 ° C, holding for 1 hour, cooling in water /

50,0 50.0

Охлажденные в чугунной изложнице (при ) 49,0Chilled in a cast-iron mold (upon) 49.0

1 «0 ten

о же about the same

Охлажденные в воде (при 20 С)Chilled in water (at 20 С)

((

Охлажденные в чугунной изложнице и термообработанные при 90ООС, выдержка 1 час, охлаждение в воде (при )Cooled in a cast-iron mold and heat-treated at 90 ° C, holding for 1 hour, cooling in water (at)

Активность МП/минMP activity / min

10,310.3

13,313.3

15,415.4

11,011.0

11,3. 17,0 чивани  сплавов 2О%-ным водным раствором едкого натра при кип чении на вод ной . бане в течение 2 час. После этого катализатор тщательно отмывают водой до нейтральной реакции. Активность полученных катализатордв испытывают в процессе гидрировани  малеиново-кислого натри . Изучают активность сплавных никель-алюминиевых катализаторов следующего соста- ва, вес. %: А1 - 5О, NL-50; А1 - 5О, N1- 49, Nb - 1. Данные по активности никель-алюминие-, вых катализаторов представлены в таблице..11.3. 17.0% of alloys with a 2O% aqueous solution of caustic soda when boiling on water. bath for 2 hours. After that, the catalyst is thoroughly washed with water until neutral. The activity of the resulting catalysts is tested in the process of hydrogenation of maleic acid sodium. The activity of alloyed nickel-aluminum catalysts of the following composition is studied, weight. %: A1 - 5O, NL-50; A1 - 5O, N1- 49, Nb - 1. Data on the activity of nickel-aluminum catalysts are presented in the table ..

Предмет изобретени последующим выщелачиванием, о т л и ч а.The subject matter of the invention is subsequent leaching, a tl and h.

Способ повышени  активности сплавного 40- активности катализатора, сплав до закалки катализатора, например никель-алюминиевого,: . подвергают термообработке при 750-950°СThe method of increasing the activity of the alloyed 40-catalyst activity, an alloy before quenching the catalyst, for example, nickel-aluminum,:. heat treated at 750-950 ° C

путем закалки исходного сплава в воде сby quenching the original alloy in water with

ю щ и и с   тем, что, с целью повышени u u and with the fact that, in order to increase

не менее 1 часа.not less than 1 hour.