SU454240A1 - Method for producing green pigments - Google Patents
Method for producing green pigmentsInfo
- Publication number
- SU454240A1 SU454240A1 SU1801518A SU1801518A SU454240A1 SU 454240 A1 SU454240 A1 SU 454240A1 SU 1801518 A SU1801518 A SU 1801518A SU 1801518 A SU1801518 A SU 1801518A SU 454240 A1 SU454240 A1 SU 454240A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- iron blue
- green pigments
- producing green
- water
- suspension
- Prior art date
Description
1one
Изобретение относитс к способу получени зеленых пигментов на базе лимонного свинцового крона и железной лазури, примен емых в производстве красок и эмалей, в полиграфической промышленности, дл окраски полимерных материалов и т. п.The invention relates to a method for producing green pigments based on lemon lead crown and iron blue used in the manufacture of paints and enamels, in the printing industry, for dyeing polymeric materials, etc.
Известный способ получени зеленых пигментов заключаетс во взаимодействии соли свинца с предварительно промытой железной лазурью с последующим введением в реакционный объем хромовой смеси и отделением осадка.A known method of producing green pigments involves the interaction of lead salts with pre-washed iron blue, followed by introducing chromium mixture into the reaction volume and separating the precipitate.
Однако качество таких пигментов невысокое: интенсивность 104%, кроюща способность 8,5 г/м, маслоемкость 26 г на 100 г пигмента , миграционна устойчивость - неудовлетворительна .However, the quality of such pigments is low: the intensity is 104%, the covering power is 8.5 g / m, the oil absorption is 26 g per 100 g of pigment, the migration stability is unsatisfactory.
Предложенный способ отличаетс тем, что железную лазурь ввод т предварительно в хромовую смесь.The proposed method is characterized in that iron blue is pre-introduced into the chromium mixture.
Это повыщает качество пигмента: интенсивность возрастает до 125%, кроюща способность снижаетс до 7 г/м, маслоемкость - до 22 г на 100 г пигмента.This increases the quality of the pigment: the intensity increases to 125%, the covering power decreases to 7 g / m, the oil absorption increases to 22 g per 100 g of pigment.
Согласно предложенному способу железную лазурь ввод т в виде суспензии в маточном растворе.According to the proposed method, iron blue is introduced as a suspension in the mother liquor.
осадителей, состо щую из 27,5 г ЫазСгоОт, растворенного в 300-509 мл воды, п 520 мл суспензии железной лазури в маточном растворе (концентраци л елезной лазури 50 г/л). Перед сливом смесь осадителей нейтрализуют до значени рП 6,5-7,5. Суспензию полученной зелени перед фпльтрацией также нейтрализуют до значени рН 5-6. Пигмент промывают , фильтруют п сушат.precipitating agents, consisting of 27.5 g of NazSgoOt dissolved in 300-509 ml of water, and 520 ml of a suspension of iron blue in the mother liquor (concentration of iron blue 50 g / l). Before draining, the mixture of precipitants is neutralized to a value of RP 6.5-7.5. The suspension of the greens obtained is also neutralized to pH 5-6 before filtration. The pigment is washed, filtered and dried.
, .Пример 2. К 81,0 г РЬ(МОз)2, растворенного в 300-500 мл воды, добавл ют смесь осадителей, состо щую из 27,5 г ЫааСгаОт и 11,0 г NaaSOi, растворенных в 300-500 мл воды, и 60,5 г водной пасты (условна влажность 60%) предварительно промытой лселезной лазури, суспендированной в 500 мл воды. Далее процесс ведут аналогично примеру 1.Example 2. To a mixture of precipitants consisting of 27.5 g of Na-CoGo and 11.0 g of NaaSOi dissolved in 300-500 ml is added to 81.0 g of Pb (MOZ) 2 dissolved in 300-500 ml of water. water, and 60.5 g of water paste (relative humidity of 60%) of previously washed blue azure, suspended in 500 ml of water. Next, the process is carried out analogously to example 1.
Пример 3. К 51,0 г РЬ(ОН)2-РЬ(МОз)2, суспендированного в 300-503 мл воды, добавл ют смесь осадителей, состо щую из 27,5 г NaaCraOy, растворенного в 300-500 мл воды, и 520 мл суспензпп железной лазури в маточном растворе (концентраци железной лазури 50 г/л). Перед сливом смесь осадителей подкисл ют азотной кислотой до рН 1,0. Далее процесс ведут аналогично примеру 1 с равной скоростью раствор 27,5 г Na2Cr2O7 в 500 мл воды, доведенный до рН 9,0 и 520 мл суспензии железной лазури в маточном растворе (концентраци железной лазури 50г/л). Суспензию полученной зелени перед фильтра- 5 цией нейтрализуют до значени рН 5-6. Пигмент нромывают, фильтруют и сушат. Сравнительные характеристики иигментов, полученных ио предложенному и известному способам, приведены в таблице.Example 3. A precipitant mixture consisting of 27.5 g of NaaCraOy dissolved in 300-500 ml of water was added to 51.0 g of Pb (OH) 2-Pb (MOZ) 2 suspended in 300-503 ml of water. and 520 ml suspension of iron blue in the mother liquor (concentration of iron blue 50 g / l). Before draining, the precipitant mixture is acidified with nitric acid to a pH of 1.0. Next, the process is carried out analogously to example 1 with an equal speed of a solution of 27.5 g of Na2Cr2O7 in 500 ml of water, adjusted to pH 9.0 and 520 ml of a suspension of iron blue in the mother liquor (concentration of iron blue 50 g / l). The suspension of the obtained green is neutralized before filtration to a pH of 5-6. Pigment nromyvayut, filtered and dried. Comparative characteristics of the pigments obtained by the proposed and known methods are shown in the table.
Предмет изобретени Subject invention
1. Способ получени зеленых пигментов путем взаимодействи соли свинца и хромовой смеси, включающий обработку железной лазурью, отличающийс тем, что, с целью повыщени качества пигмента, железную лазурь ввод т предварительно в хромовую смесь.1. A method of producing green pigments by reacting a lead salt and a chromium mixture, which includes treatment with iron blue, characterized in that, in order to improve the quality of the pigment, iron blue is introduced into the chrome mixture beforehand.
2. Способ ио н. 1, отличающийс тем, что железную лазурь ввод т в виде суспензии в маточном растворе.2. The way io n. 1, characterized in that iron blue is introduced as a suspension in the mother liquor.