SU396368A1 - METHOD OF OBTAINING METALLIZED WELLS - Google Patents
METHOD OF OBTAINING METALLIZED WELLSInfo
- Publication number
- SU396368A1 SU396368A1 SU1472771A SU1472771A SU396368A1 SU 396368 A1 SU396368 A1 SU 396368A1 SU 1472771 A SU1472771 A SU 1472771A SU 1472771 A SU1472771 A SU 1472771A SU 396368 A1 SU396368 A1 SU 396368A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- pellets
- metal
- slag
- reducing agent
- pellet
- Prior art date
Description
1one
Изобретение относитс к области пр мого получени железа.The invention relates to the field of direct iron production.
Известен способ получени металлизованных окатышей, приготовл емых из смеси руды с восстановителем и флюсом, с коагул цией металла в процессе обжига, при котором восстановленное металлическое железо коагулирует , создава наружную металлическую оболочку, а окислы пустой породы составл ют внутреннее дро.A known method for producing metallized pellets prepared from a mixture of ore with a reducing agent and a flux, with metal coagulation during the burning process, in which the reduced metallic iron coagulates, creating an outer metallic shell, and the oxides of the empty rock constitute an internal core.
Однако при такой структуре металлических окатышей затруднительно хорошее отделение железа от шлака магнитной сепарацией, поскольку при низкой степени науглераживани металла окатыши плохо измельчаютс (ковкое железо), а при значительном науглераживании неизбежно сильное развитие жидкой фазы и сплавление гранул в сплошной конгломерат .However, with such a structure of metal pellets, it is difficult to separate iron from slag by magnetic separation, because with a low degree of metal carbonization, the pellets are poorly crushed (ductile iron), and with significant carbonizing, inevitably strong development of the liquid phase and fusion of granules into a solid conglomerate.
Цель изобретени - улучшение условий последуюшего разделени металла и шлака, нолученне двухслойных окатышей с металлическим дром и шлаковой оболочкой.The purpose of the invention is to improve the conditions for the subsequent separation of metal and slag, but not obtained double-layer pellets with a metal core and a slag shell.
Дл этого окатыши или гранулы крупностью 3-20 мм, приготовленные из руды или концентрата с добавкой в качестве св зующего и восстановител до 10% мазута и в случае необходимости флюса, обжигают в слое ме.лкого (О-3 мм) твердого восстановител (коксик, полукокс, бурый или каменный For this, pellets or granules with a particle size of 3-20 mm, prepared from ore or concentrate with an additive as a binder and a reducing agent up to 10% of mazut and, if necessary, flux, are burned in a layer of solid (O-3 mm) solid reducing agent (coking , semi-coke, brown or stone
уголь) так, чтобы каждый окатыш был окружен восстановителем, сначала при 1100- 1250°С до степени восстановлени железа 85-100%, а затем при 1300-1500°С до коагул дии металла внутри окатыша.coal) so that each pellet is surrounded by a reducing agent, first at 1100–1250 ° C to an iron reduction level of 85–100% and then at 1300–1500 ° C until the metal coagulates inside the pellet.
Слой восстановител может быть накатан на окатыши. Коагул ци металла внутри окатыша обеспечиваетс за счет снл поверхностного нат жени . Сохранение формы окатыша при разм гчении шлаковой составл ющей шихты обеспечиваетс также силами поверхностного нат жени , действующими в услови х , когда окатыш окружен смачиваемой средой (углеродистый восстановитель).A layer of reducing agent can be rolled on the pellets. Coagulation of the metal inside the pellet is ensured by the removal of surface tension. The preservation of the shape of the pellet during the softening of the slag component of the charge is also provided by surface tension forces operating under conditions when the pellet is surrounded by a wettable medium (carbonaceous reducing agent).
Металлизованные окатыши после обжига имеют структуру типа ореха с металлом во внутренней полости. Отделение металлизованных окатышей от восстановител достигаетс путем грохочени или отмагничпвани . Охлаждение окатышей возможно на воздухе в св зи с тем, что оплавленна шлакова оболочка предохран ет металл от окислени . При дроблении охлажденных окатышей шлакова оболочка легко растрескнваетс и отдел етс от металла, который отмапшчиваетс . Структура таких двухслойных лгеталлизованных окатышей дает возможность легче и полнее осуществить отделение металла от шлака. Пример. В качестве исхйдНйго материала используют бурохромистую руду Серовского месторождени (39-44% Fe общ. 0,3- 0,4% Ni). Шихта дл окатывани содержит 10% мазута. Окомкование производитс в барабанном окомкователе. В опытах используютс окатыши диаметром 8-20 мм. Восстаповление осуществл ют в печи сопротивлени с графитовым нагревателем. Сырые окатыши, погруженные в слой дробленого коксика крупностью 2-3 мм, помещаютс в предварительно нагретую до 1100-1150°С печь п выдерживают при этой температуре в течение 1 час. Затем температура в ней повышаетс до 1500°С. Охлаждение окатышей производитс на воздухе. Отделение их от коксика производитс путем грохочени , причем прилипани кусочков коксика .к поверхности окатышей не происходит. При дроблении окаты5 10 15 20 шлаковой шей происходит легкое отделение оболочки от металлического дра. Состав металлической фазы, %: С 0,93; Ni 0,89. Состав щлаковой фазы, %: FeO 3,5; Ni 0,057. Предмет изобретени Снособ получени металлизовзпных окатышей , приготовл емых из смеси руды или коицентрата с мазутом и флюсом, с коагул цией металла в процессе обжига, отличающийс тем, что, с целью улучшени условий последующего разделени металла и шлака, получени двухслойных окатышей с металлическим дром и шлаковой оболочкой, их обжигают в услови х окружени каждого окатыша твердым восстановителем при 1100-1250°С до степепи восстановлени железа 85-100%, а затем при 1300-1500°С до коагул ции Д1еталла .внутри окатыша.After calcination, the metallized pellets have a nut-like structure with a metal in the inner cavity. The separation of the metallized pellets from the reducing agent is achieved by screening or magnetisation. The pellets may be cooled in air due to the fact that the molten slag shell prevents the metal from oxidizing. When crushing cooled pellets, the slag shell is easily cracked and separated from the metal, which is otmashshchivatsya. The structure of such double-layered metallised pellets makes it possible to more easily and more completely separate the metal from the slag. Example. The raw material from the Serovskoye deposit (39–44% Fe total 0.3–0.4% Ni) is used as the source material. The coating mixture contains 10% fuel oil. Palletizing is done in a drum pelletizer. Pellets with a diameter of 8-20 mm are used in the experiments. Restoration is carried out in a resistance furnace with a graphite heater. Raw pellets, immersed in a layer of crushed coke with a size of 2-3 mm, are placed in a furnace preheated to 1100-1150 ° C and kept at this temperature for 1 hour. Then the temperature in it rises to 1500 ° C. The pellets are cooled in air. Separating them from the coke is done by screening, and no sticking of the coke pieces to the surface of the pellets occurs. When crushing the okat5 10 15 20 slag necks, the shell easily separates from the metal core. The composition of the metal phase,%: C 0.93; Ni 0.89. The composition of the slag phase,%: FeO 3,5; Ni 0.057. The subject of the invention is a method for producing metallized pellets prepared from a mixture of ore or co-concentrate with black oil and flux, with metal coagulation in the firing process, characterized in that, in order to improve the conditions for the subsequent separation of metal and slag, to obtain two-layer pellets with a metal core and slag shell, they are calcined under the conditions of each pellet with a solid reducing agent at 1100–1250 ° C until iron reduction is 85–100%, and then at 1300–1500 ° C until D1 metal coagulates inside the pellet.