SU1073617A1 - Method of increasing wear-resistance of paper-cutting machine blades - Google Patents

Abstract

СПОСОБ ПОВЫШЕНИЯ ИЗНОСОСТОЙКОСТИ НОЖЕЙ БУМАГОРЕЗАТЕЛЬНЫХ МАШИН, заключающийс  в том, что на рабочую крюмку ножей нанос т слой материала, отличающийс  тем, что, с целью повышени  эффективности и достоверности резу;7ьтатов, во врем  работы в зону контакта ножей ввод т металлоплакирующую смазку, содержащую , мас.%: Окись кадми 10-12 Железный сурик 15-18 Ароматический амин О,0-0,12 Смазывающа  основа 74,9-69,88A METHOD FOR IMPROVING WEAR WEIGHTNESS OF KNIVES OF PAPER AND CUTTING MACHINES, which consists in that a layer of material is applied to the working blade of knives, characterized in that, in order to increase the efficiency and reliability of cuts; wt.%: Cadmium oxide 10-12 Iron oxide 15-18 Aromatic amine O, 0-0.12 Lubricating base 74.9-69.88

Description

Изобретение относитс  к контактн химическим способам восстановлени  рабочих кромок ножей и повышени  износостойкости ножей бумагорезател ных машин. Известен способ повьошени  износостойкости ножей бумагорезательных машин, заключающийс  ,в том, что на рабочую кромку ножей нанос т слой материала l . Однако данный способ характеризу с  недостаточной эффективностью .и достоверностью результатов, что обусловлено необходимостью предвари тельного сн ти  ножей со станка, использовани  сложного оборудовани  возможностью восстановлени  одного ножа. Цель изобретени  - повышение эффективности и достоверности результ тов, Указанна  цель достигаетс  тем, что согласно способу повышени  износостойкости ножей бумагорезательн машин, заключающемус  в том, что на рабочую кромку ножей нанос т слой материала, во врем  работы в зону контакта ножей ввод т металлоплакирующую смазку, содержащую, мас.1: Окись кадми 10-12 Железный сурик15-18 А)эоматический амин 0,10-0,12 Смазывающа  основа 74,9-69,88. Предлагаемый способ реализуетс  следующим образом. Удельное давление между ножами выбирают 10-30 МПа, а скорость их вращени  600-2500 об/мин. Во врем  работы ножейв зону их контакта ввод т металлоплакирующую смазку, содержащую, мас.%; окись кадми  12; железный сурик 18; ароматический амин 0,12; смазывающа  основа 69,88. В результате контакта этой смазки с изношенной поверхностью рабочих кромок ножей при давлении 30 МПа и скорости 600 м/мин образуетс  тонкий слой пленки композиционного износостойкого покрыти . При уменьшении концентрации наполнителей за указанные пределы происходит износ основного материала ножей , а при увеличении скорость образовани  пленки превышает скорость износа, что приводит к изменению геометрии ножей. Подобный эффект наблюдаетс  при давлении выше 30 МПа. При скорости меньше 600 м/мин не происходит образовани  сло  с достаточной износостойкостью. Предлагаемый способ повышает эффективность и достоверность результатов .This invention relates to chemical contact methods for restoring the working edges of knives and improving the wear resistance of knives of paper-cutting machines. A known method of improving the wear resistance of knives of shredders, which consists in applying a layer of material l to the working edge of the knives. However, this method is characterized with insufficient efficiency and reliability of the results, which is caused by the need to preliminarily remove the knives from the machine, to use complex equipment with the ability to restore one knife. The purpose of the invention is to increase the efficiency and reliability of the results. This goal is achieved in that according to the method of improving the durability of knives with a paper cutter machines, which implies that a layer of material is applied to the working edge of the knives, metal cladding grease is introduced into the blade contact area, containing, wt.1: cadmium oxide 10-12 iron oxide 15-18 A) eomatic amine 0.10-0.12 Lubricating base 74.9-69.88. The proposed method is implemented as follows. The specific pressure between the blades is chosen 10-30 MPa, and their rotational speed is 600-2500 rpm. During the operation of the blades, a metalplating grease containing, in wt.%, Is introduced into the zone of their contact; cadmium oxide 12; iron oxide 18; aromatic amine 0.12; lubricating base 69,88. By contacting this lubricant with the worn surface of the working edges of the knives at a pressure of 30 MPa and a speed of 600 m / min, a thin film of a composite wear-resistant coating is formed. When the concentration of fillers decreases beyond the specified limits, the base material of the knives deteriorates, and with an increase in the rate of film formation exceeds the rate of wear, which leads to a change in the geometry of the knives. A similar effect is observed at pressures above 30 MPa. At speeds of less than 600 m / min, no layer is formed with sufficient wear resistance. The proposed method improves the efficiency and reliability of the results.

Claims (1)

СПОСОБ ПОВЫШЕНИЯ ИЗНОСОСТОЙКОСТИ НОЖЕЙ БУМАГОРЕЗАТЕЛЬНЫХ МАШИН, заключающийся в том, что на рабочую кромку ножей наносят слой материала, отличающийся тем, что, с целью повышения эффективности и достоверности результатов, во время работы в зону контакта ножей вводят металлоплакирующую смазку, содержа-METHOD FOR INCREASING THE WEAR RESISTANCE OF PAPER CUTTER KNIVES, which consists in applying a layer of material to the working edge of the knives, characterized in that, in order to increase the efficiency and reliability of the results, a metal-clad lubricant is introduced into the contact zone of the knives, containing щую, мас.%: total, wt.%: Окись кадмия Cadmium oxide 10-12 10-12 Железный сурик Iron Meerk 15-18 15-18 Ароматический амин Aromatic amine 0,10-0,12 0.10-0.12 Смазывающая основа Grease base 74,9-69,88 74.9-69.88 >>