SU1049591A1 - Method of making textile material shape-retaining - Google Patents
Method of making textile material shape-retaining Download PDFInfo
- Publication number
- SU1049591A1 SU1049591A1 SU752194827A SU2194827A SU1049591A1 SU 1049591 A1 SU1049591 A1 SU 1049591A1 SU 752194827 A SU752194827 A SU 752194827A SU 2194827 A SU2194827 A SU 2194827A SU 1049591 A1 SU1049591 A1 SU 1049591A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- polyvinyl butyral
- solution
- rectangles
- textile material
- applying
- Prior art date
Abstract
СПОСОБ ПРИДАНИЯ ФОРМОУСТОЙЧИВОСТИ ТЕКСТИЛЬНОМУ МАТЕРИАЛУ нанесением раствора поливинилбутирал в органическом растворителе с последующей термообработкой, отличающийс тем, что, с целью повышени формоустойчивости, используют раствор поливинилбутирал в диоксане и нанесение его осуществл ют посредством шаблона с раппортом из направленных под углом 45° к нит м основы взаимно-перпендикул рных пр моугольников размером 0,8-1,2x3,8-4,2 мм с рассто нием между центрами пр моугольников 4,8-5,2 мм. (ЛA method for imparting dimensional stability of textile materials by applying a solution of polyvinyl butyral in an organic solvent with subsequent heat treatment, characterized in that, in order to increase dimensional stability, use polyvinyl butyral solution in dioxane and applying it carried out by a template directed rapport of 45 ° to the base threads of mutually perpendicular rectangles of 0.8-1.2 x3.8-4.2 mm in size with a distance between the centers of the rectangles of 4.8-5.2 mm. (L
Description
Распер чеакиRasper Cheaks
fXltnHfXltnH
Основа Изобретение относи7-с к способам придани формоустойчивости текстиль ным материалам и может быть использовано на предпри ти х легкой промышленности . Известен способ придани формоустойчивости текстильному материалу нанесением на него сло полимерного материала с последующим расплавлением полимера под воздействием ультразвукового излучени 1 , : Однако этот способ недостаточно эффективен из-за высокой условной жесткости обработанного материала и потребности специального сложного оборудовани . Наиболее близким к изобретению вл етс способ придани формоустойчивости текстильному материалу, заключающийс в том, что на материал нанос т, например напылением, раствор поливинилбутирал (ПВБ) в органи ческом растворителе с последующей термообработкой .2 , Однако материал, обработанный по Данному способу имеет повышенные жесткость и сминаемость, вследствии чего не обладает высокой формоустой чивостью. Кроме того, ухудшаютс гигиенические свойства материала путем уменьшени воздухопроницаемое ти и по вл етс ломкость.ткани. Цель изобретени - повышение формоустойчивости текстильного материала, Поставленна цель достигаетс тем, что согласно способу придани формоустойчивости текстильному материалу нанесением раствора поливинилбутирал в органическом растворителе с последующей термообработкой, используют раствор поливинилбутирал в диоксане и нанесение его осуществл ют посредством шаблона с раппортом из направленных под углом 45 к нит м основы взаимно-перпендикул рных пр моугольников размером 0,81 ,2x3,8-4,2 мм с рассто нием между центрами пр моугольников 4,8-5,2 им. Пример. На костюмную ткань из смеси шерст ных и лавсановых волокон , вз тых в весовом соотношении 45.: 55, нанос т на изнаночную сторону 12%-ный раствор поливинилбутирал в диоксане методом печати по шаблону с раппортом из направленных под углом 45 к нит м основы взаимноперпендикул рных пр моугольников размером 1x4 мм с рассто нием между центрами пр моугольников 5 мм (фиг. 1). Параллельно провод т обработку изнанки ткани путем напылени 12%-ного раствора поливинилбутирал в диоксане , Свой.ства обработанных тканей приведены в таблице, Как следует из представленных данных,предлагаемый способ позвол ет повысить формоустойчивость текстильного материала.Basis The invention relates to methods of shaping textile materials for dimensional stability and can be used in light industry enterprises. There is a known method of imparting a form-stability to a textile material by applying a layer of a polymeric material onto it with subsequent melting of the polymer under the influence of ultrasonic radiation 1: The closest to the invention is a method of imparting a form-stability to a textile material, which consists in applying a material, for example by spraying, a solution of polyvinyl butyral (PVB) in an organic solvent followed by heat treatment. However, the material treated by this method has an increased rigidity and crushability, as a result of which it does not have a high formoustychivosti. In addition, the hygienic properties of the material are impaired by reducing air-permeable tees and brittleness appears. The purpose of the invention is to increase the dimensional stability of a textile material. The aim is achieved by applying a solution of polyvinyl butyral in an organic solvent followed by heat treatment, using a polyvinyl butyral in dioxane solution, and applying it by means of a template with an angle of 45 ° directed by Base threads of mutually perpendicular rectangles of size 0.81, 2x3.8-4.2 mm with a distance between the centers of the rectangle s 4.8-5.2 them. Example. A 12% polyvinyl butyral in dioxane solution was applied to the costume fabric from a mixture of wool and polyester fibers, taken in a weight ratio of 45 .: 55, on the wrong side of the fabric using a pattern printed with a pattern of 45 perpendicular directed at 45 to the yarn of the base There are 1x4 mm rectangular rectangles with a distance of 5 mm between the centers of the rectangles (Fig. 1). In parallel, the processing of the inside of the fabric is carried out by spraying a 12% solution of polyvinylbutyral in dioxane. The properties of the treated fabrics are given in the table. As follows from the presented data, the proposed method allows increasing the dimensional stability of the textile material.
232 0,78 0,26 55 42,6232 0.78 0.26 55 42.6
Исходна тканьOriginal fabric
154154
43,843.8
149149
Claims (1)