SI9800030A - Jeklo za hladno oblikovanje - Google Patents
Jeklo za hladno oblikovanje Download PDFInfo
- Publication number
- SI9800030A SI9800030A SI9800030A SI9800030A SI9800030A SI 9800030 A SI9800030 A SI 9800030A SI 9800030 A SI9800030 A SI 9800030A SI 9800030 A SI9800030 A SI 9800030A SI 9800030 A SI9800030 A SI 9800030A
- Authority
- SI
- Slovenia
- Prior art keywords
- ppm
- preferential
- range
- wide range
- less
- Prior art date
Abstract
Predloženi izum se nanaša na jeklo za hladno oblikovanje, ki daje odlično odpornost proti obrabi z abrazijo. To jeklo dobimo s fuzijo in rafinacijo jekla in je označeno s tem, da ima zlitina naslednjo masno sestavo: ogljik - prednostno območje 1 - 1,20%, široko območje 0,80 - 1,50%; mangan - prednostno območje 0,30 -0,50%, široko območje manjše od 1%; silicij - prednostno območje 0,80 - 1%, široko območje manjše od 1%; fosfor - prednostno območje manjše ali enako 0,020%, široko območje manjše ali enako 0,030%; žveplo - prednostno območje manjše ali enako 0,005%, široko območje je manjše ali enako 0,005%; krom - prednostno območje 8 - 8,50%, široko območje 6,25 - 9%; nikelj je manjše od 0,30%, široko območje manjše od 0,50%; molibden - prednostno območje 2 - 2,30%, široko območje 1,80 - 3%; aluminij - prednostno območje je manjše od 200 ppm, široko območje manjše od 0,15%; vanadij - prednostno območje 0,20 - 0,40%, široko območje 0,20 - 0,40%; niobij - prednostno območje 0,60 - 0,90%, široko območje 0,60 - 1,5%; dušik - prednostno območje manjše od 130 ppm, široko območje manjše od 150 ppm, kisik - prednostno območje manjše od 30 ppm, široko območje manjše od 50 ppm; titan ali cirkonij - prednostno območje 500 - 1000 ppm, široko območje 500 - 1500 ppm.ŕ
Description
THYSSEN FRANCE SA
Jeklo za hladno oblikovanje
Predloženi izum se nanaša na jeklo za hladno oblikovanje, ki daje odlično odpornost proti obrabi z abrazijo.
To jeklo dobimo s fuzijo in rafinacijo jekla in je označeno s tem, da ima zlitina naslednjo masno sestavo:
| Prednostno območje | Široko območje | |
| ogljik | 1 - 1,20% | 0,80 - 1,50% |
| mangan | 0,30 - 0,50% | < 1% |
| silicij | 0,80 - 1% | < 1% |
| fosfor | £ 0,020% | s 0,030% |
| žveplo | s 0,005% | s 0,005% |
| krom | 8 - 8,50% | 6,25 - 9% |
| ni kelj | < 0,30% | < 0,50% |
| molibden | 2 - 2,30% | 1,80 - 3% |
| aluminij | < 200 ppm | < 0,15% |
| vanadij | 0,20 - 0,40% | 0,20 - 0,40% |
| niobij | 0,60 - 0,90% | 0,60 - 1,5% |
| dušik | < 130 ppm | <150 ppm |
| kisik | < 30 ppm | < 50 ppm |
| titan ali | ||
| cirkonij | 500-1000 ppm | 500-1500 ppm |
Ostalo je železo in nečistoče, značilne pri proizvodnji kovin.
To jeklo obdelamo z električno fuzijo in nato z rafiniranjem v grelni ponvi, razplojevanjem v vakuumu in ponovnim pretaljevanjem.
V navedenem jeklu ogljik in niobij tvorita niobijev karbid, titan ali cirkonij pa dajeta prednost tvorbi idiomorfnega niobijevega karbida. Stehiometrično razmerje za tvorbo niobijevega karbida je približno 1% niobija za 0,12% ogljika. Prebitek ogljika uravnotežimo z vsebnostjo kroma, molibdena in vanadija v jeklu.
Jeklo v smislu izuma ima trdoto večjo od 60 HRc. Ima naslednje kvalitete: odpornost proti abrazivni obrabi, obdelovalnost in žilavost, ki do sedaj še niso bile dosežene.
Zilavost določimo z meritvijo v skladu s preiskusom po Charpy-ju. Referenčni preizkušanec 7x10x55 mm obdelamo pri 1050°C, ugasimo v olju, nato pa popuščamo 2 uri pri 560°C. Za trdoto, ki je večja ali enaka 60 HRc, ima utržno energijo enako ali večjo od 40 J.
Hladno oblikovno jeklo v smislu izuma izboljša odpornost proti obrabi, ki je v naslednjih treh oblikah:
- abrazivna obraba, očitno izboljšana
- obraba z luščenjem, očitno izboljšana na osnovi odlične žilavosti jekla
- obraba z adherenco, tudi odlično izboljšana.
Predloženi izum ni omejen le z opisano in prikazano izvedbo, temveč pokriva tudi vse možne variante.
Za
THYSSEN FRANCE SA:
Claims (2)
- PATENTNI ZAHTEVKI1. Jeklo za hladno oblikovanje, dobljeno s fuzijo in rafinacijo zlitine, označeno s tem, da ima zlitina naslednjo masno sestavo:
ogljik 0,80 -1,50% mangan < 1% silicij < 1% fosfor < 0,030% žveplo < 0,005% krom 6,25 - 9% nikelj < 0,50% molibden 1,80-3% aluminij < 0,15% vanadij 0,20 - 0,40% niobij 0,60 -1,5% dušik < 150 ppm kisik < 50 ppm titan ali cirkonij 500-1500 ppm pri čemer je ostalo železo in nečistoče, značilne pri proizvodnji kovin. - 2. Jeklo po zahtevku 1, označeno s tem, da ima zlitina naslednjo masno sestavo:
ogljik 1 -1,20% mangan 0,30 - 0,50% silicij 0,80 -1% fosfor < 0,020% žveplo < 0,005% krom 8 - 8,50% nikelj < 0,30% molibden 2 - 2,30% aluminij < 200 ppm vanadij 0,20 - 0,40% niobij 0,60 - 0,90% dušik < 130 ppm kisik < 30 ppm titan ali cirkonij 500-1000 ppm pri čemer je ostalo železo in nečistoče, značilne pri proizvodnji kovin.