SE508696C2 - Pulled gunpipe and method of making such pipe - Google Patents
Pulled gunpipe and method of making such pipeInfo
- Publication number
- SE508696C2 SE508696C2 SE9602736A SE9602736A SE508696C2 SE 508696 C2 SE508696 C2 SE 508696C2 SE 9602736 A SE9602736 A SE 9602736A SE 9602736 A SE9602736 A SE 9602736A SE 508696 C2 SE508696 C2 SE 508696C2
- Authority
- SE
- Sweden
- Prior art keywords
- weapon
- hardened
- tube
- barrel
- gun barrel
- Prior art date
Abstract
Description
10 15 20 NW (j 30 35 508 696 2 klarläggs i underpatentkraven. 10 15 20 NW (j 30 35 508 696 2 clarified in the sub-patent claims.
Till grund för uppfinningen ligger i huvudsak den tanken att bommarna i vapenröret åtminstone vid området intill mynningen skall vara ythärdade, nämligen företrädesvis till ett djup av mellan 0,3 och 0,5 mm.The basis of the invention is mainly the idea that the barriers in the weapon tube shall be surface hardened at least at the area adjacent to the mouth, namely preferably to a depth of between 0.3 and 0.5 mm.
Härdningen av de ythärdade rörpartierna skall ge en hårdhet av åtminstone 650 HV.The hardening of the surface-hardened pipe sections shall give a hardness of at least 650 HV.
Lämpligen bör de ythärdade rörpartierna sträcka sig över åtminstone hälften av vapenrörets längd. l det fall att varje vapenrör inom området för laddningsrummet ytterligare förses med ett hårdmetallskikt för att minska den på grund av drivladdningsgaserna förorsakade rörerosionen så ythärdas endast bommarna i vapenröret inom ett område mellan mynningen och det med hårdmetall belagda rörpartiet för att minska bomytförslitningen.Preferably, the surface hardened pipe sections should extend over at least half the length of the barrel. In the case of each barrel within the area of the hold further provided with a cemented carbide layer to reduce it due to the propellant gases caused the pipe erosion, so only the booms are surface hardened in the barrel within a range between the muzzle and the cemented carbide coated pipe section to reduce boom wear.
Vid vapenrör, där laddningsavgasningen vid avskjutning sker vid relativt ringa tryck och ringa temperatur kan man vanligen utesluta den ytterligare hårdmetallbeskiktning, eftersom bomförslitningen vid mynningssidan på grund av friktionen mellan projektilen och röret är betydligt större än erosionen i det område som gränsar till laddningsrummet. Vid sådana rör har det visat sig fördelaktigt att man ythärdar inte endast området intill mynningen på vapenröret utan att man eventuellt innefattar även laddningsrummet för att minska rörerosionen i hela vapenröret.In the case of weapon pipes, where the charge degassing during firing takes place at relative low pressure and low temperature, it can usually be ruled out further cemented carbide coating, as the boom wear at the mouth side is due of the friction between the projectile and the tube is significantly greater than the erosion in it area adjacent to the cargo space. In such pipes it has been shown It is advantageous to surface harden not only the area next to the mouth the weapon tube without possibly also including the cargo space to reduce pipe erosion throughout the gun barrel.
För härdning av bomytorna intill mynningen på rörpartiet har det visat sig speciellt lämpligt att utföra härdningen med hjälp av laserstrålar emedan den förslitningszon som skall härdas kan måttas in och värmebehandlas kortvarigt, så att man slipper genomföra en separat avkylningsprocess, och därvid arbetsstyckets behandlingstid blir mycket kort. Svårtillgängliga avsnitt kan vid dessa förfarande nås på ett enkelt sätt med hjälp av speglar.For hardening of the boom surfaces next to the mouth on the pipe section, it has been shown it is particularly convenient to carry out the curing by means of laser beams since the wear zone to be cured can be measured in and heat treated short-term, so as not to carry out a separate cooling process, and thereby the processing time of the workpiece becomes very short. Hard to access sections can be achieved in these procedures in a simple way with the help of mirrors.
Ytterligare detaljer och fördelar med uppfinningen kommer att framgå av den följande beskrivningen i anslutning till bifogade ritningar som visar utföringsexempel på uppfinningen. På ritningarna visar: figur 1 ett första utföringsexempel av ett vapenrör enligt uppfinningen, vilket är ythärdat endast på ett delområde; figur 2 området intill mynningen på det i figur 1 visade vapenröret vid härdning med hjälp av laserstrålar; och figur 3 ett andra utföringsexempel av ett vapenrör enligt uppfinningen, vilket ythärdats fullständigt. 10 15 20 30 35 3 sus 696 l figur 1 betecknas ett vapenrör med siffran 1, vilket rör är försett med räfflor 2 och bommar 3, och vilket i bakänden har ett laddningsrum 4.Further details and advantages of the invention will become apparent of the following description in connection with the accompanying drawings which show embodiments of the invention. The drawings show: Figure 1 shows a first embodiment of a weapon barrel according to the invention, which is surface hardened in only one sub-area; Figure 2 shows the area next to the mouth of the weapon barrel shown in Figure 1 at curing using laser beams; and Figure 3 shows a second embodiment of a weapon barrel according to the invention, which has been surface hardened completely. 10 15 20 30 35 3 sus 696 In Figure 1, a weapon barrel is denoted by the number 1, which barrel is provided with grooves 2 and bars 3, and which at the rear end has a cargo space 4.
Vapenröret är i ett första rörparti 5, vilket omfattar laddningsrummet 4, försett med ett hårdmetallskikt 6, t ex bestående av en kromlegering. Vid det andra rörpartiet 8, vilket sträcker sig till mynningen 7, är vapenröret ythärdat till ett djup från ytan av mellan 0,3 och 0,5 mm.The weapon tube is in a first tube portion 5, which comprises the cargo space 4, provided with a cemented carbide layer 6, for example consisting of a chromium alloy. At that second tube portion 8, which extends to the mouth 7, the weapon tube is surface hardened to a depth from the surface of between 0.3 and 0.5 mm.
Härdningen av röravsnittet 8 sker med hjälp av laserstrålar och skall i det följande beskrivas närmare i anslutning till figur 2. Med siffran 10 betecknas en 5 kW COQ-laser, vars strålar 11 vid mynningssidan skickas axiellt in i vapenröret 1. Med hjälp av en i vapenröret 1 lagrad spegel 12 omlänkas Iaserstrålarna 1 1, så att de i rät vinkel träffar bomytan som skall härdas. Bomytorna är företrädesvis svärtade för att minska reflektionen från Iaserstrålarna 1 1 vid dessa rörytor.The curing of the pipe section 8 takes place by means of laser beams and shall in the following is described in more detail in connection with figure 2. With the number 10 is a 5 kW COQ laser, whose beams 11 are sent at the mouth side axially into the weapon tube 1. By means of a mirror 12 stored in the weapon tube 1 redirect the laser beams 1 1, so that they strike the boom surface at the right angle hardened. The boom surfaces are preferably blackened to reduce the reflection from The laser beams 1 1 at these pipe surfaces.
Mellan vapenröret 1 och spegeln 12 skapas en axiell och en radiell relativrörelse (i figur 2 antydd med pilarna 13 och 14), så att brännpunkten för laserljuset följer bom-räffelbanan. Genom parametrarna lasereffekt, brännpunktsstorlek och framföringshastighet styrs effekttjockleken (103 till 105 W/cm3l och inverkansvaraktigheten och därmed den i ytskiktet på vapenröret införda energin per ytenhet.Between the weapon tube 1 and the mirror 12 an axial and a radial are created relative motion (in Figure 2 indicated by arrows 13 and 14), so that the focal point for the laser light follows the boom-groove path. Through the parameters laser power, focal length and feed rate control the power thickness (103 to 105 W / cm3l and the duration of impact and thus that in the surface layer of the weapon tube introduced the energy per unit area.
Figur 3 visar ett ytterligare utföringsexempel på ett vapenrör enligt uppfinningen, vid vilket man avstått från att applicera ett hårdmetallskikt. l stället är vapenröret ythärdat över hela sin längd 15, så att man erhållit ett genomgående härdat område 16 (för samma delar har använts samma hänvisningsbeteckningar som i figur 1).Figure 3 shows a further embodiment of a weapon barrel according to the invention, in which one has refrained from applying a cemented carbide layer. l instead, the weapon tube is surface hardened over its entire length 15, so that one has obtained one through hardened area 16 (for the same parts the same has been used reference numerals as in Figure 1).
HÄNv|sN|NGss|FFnoR 1 vapenrör 1 1 laserståle 2 räffla 12 spegel 3 bom 13 pil för att ange en axiell relativ- 4 laddningsrum förskjutning mellan vapenröret 1 5 första röravsnitt och spegeln 12 6 hårdmetallskikt 14 pil för att ange en radiell relativ- 7 mynning förskjutning mellan vapenröret 1 8 andra röravsnitt och spegeln 12 9 tjocklek 15 vapenrörets längd, röravsnitt 10 laser 16 ythärdat områdeHÄNv | sN | NGss | FFnoR 1 weapon tube 1 1 laser steel 2 groove 12 mirrors 3 boom 13 arrow to indicate an axial relative 4 payload displacement between the weapon barrel 1 5 first pipe section and the mirror 12 6 carbide layer 14 arrow to indicate a radial relative 7 muzzle displacement between the gun barrel 1 8 second pipe sections and the mirror 12 9 thickness 15 length of weapon barrel, barrel section Laser 16 surface hardened area
Claims (5)