Abstract

FIELD: oil and gas well drilling.

SUBSTANCE: invention is related to water-based drilling fluids. The lubricating additive for drilling fluids contains, wt%: synthetic hydrocarbon fluid 65-89.5; ester 10-34.5; nonionic or zwitterionic surfactant 0.5-2. As an ester, the reaction product of a polyhydric alcohol and at least one of the higher fatty acids of tall oils or the reaction product of a polyhydric alcohol and distilled tall oil or crude tall oil obtained as a result of an acid-catalytic esterification reaction is used.

EFFECT: preservation of high lubricating properties, as well as an increase in anti-sticking properties at the "metal-clay cake" and "metal-metal" boundaries in fresh and mineralized drilling fluids at low temperatures.

5 cl, 1 dwg, 4 tbl

Description

Область техники, к которой относится изобретениеThe field of technology to which the invention belongs

Изобретение относится к области бурения нефтяных и газовых скважин, в частности к буровым растворам на водной основе.The invention relates to the field of oil and gas well drilling, in particular to water-based drilling fluids.

Уровень техникиState of the art

Известен смазочный реагент к буровым растворам на основе отработанного подсолнечного масла с модифицирующими добавками (Патент RU2105783C1, опубл. 1998.02.27), характеризующийся тем, что в качестве модифицирующих добавок он содержит отработанную смазочно-охлаждающую жидкость и легкое талловое масло при следующем соотношении компонентов, мас. %:Known lubricant for drilling fluids based on used sunflower oil with modifying additives (Patent RU2105783C1, publ. 1998.02.27), characterized in that as modifying additives it contains used cutting fluid and light tall oil in the following ratio, wt . %:

Отработанное подсолнечное масло - 45-60;Waste sunflower oil - 45-60;

Легкое талловое масло - 10-20;Light tall oil - 10-20;

Отработанная смазочно-охлаждающая жидкость - 20-45.Waste coolant - 20-45.

Недостатками указанной смазочной добавки являются температура замерзания, непригодная для использования в северных регионах; низкая противоприхватная способность, нестабильность фильтрационной корки ввиду использования чистых талловых масел.The disadvantages of this lubricant additive are the freezing point, unsuitable for use in the northern regions; low anti-seize ability, filter cake instability due to the use of pure tall oils.

Известна смазывающая добавка к буровым растворам (патент RU2163616C2, опубл. 2001.02.27), включающая синтетическую жидкость, нейтрализующий агент и воду, которая содержит в качестве синтетической жидкости ацетали, или альфаолефины, или полиальфаолефины, жирные кислоты высшего ряда с C9 и выше, а в качестве нейтрализующего реагента - гидроокиси щелочных металлов при следующем соотношении компонентов, мас. %:Known lubricating additive to drilling fluids (patent RU2163616C2, publ. 2001.02.27), including a synthetic fluid, a neutralizing agent and water, which contains as a synthetic fluid acetals, or alpha-olefins, or polyalphaolefins, fatty acids of the highest series with C9 and above, and as a neutralizing agent - hydroxides of alkali metals in the following ratio of components, wt. %:

синтетическая жидкость 10-35,synthetic fluid 10-35,

жирные кислоты 60-80,fatty acids 60-80,

нейтрализующий агент 0-3,neutralizing agent 0-3,

вода - остальное.water is the rest.

Недостатками указанной смазочной добавки являются температура замерзания, непригодная для использования в северных регионах; низкая противоприхватная способность.The disadvantages of this lubricant additive are the freezing point, unsuitable for use in the northern regions; low anti-seize ability.

Известна смазочная добавка к буровым растворам (RU2197511C2, опубл. 2003.01.27), содержащая легкое талловое масло, триэтаноламин, дополнительно содержащая оксиэтилированный алкифенол, пентамер пропилена при следующем соотношении ингредиентов, мас. %:Known lubricating additive for drilling fluids (RU2197511C2, publ. 2003.01.27), containing light tall oil, triethanolamine, additionally containing ethoxylated alkylphenol, propylene pentamer in the following ratio of ingredients, wt. %:

легкое талловое масло 35-55,light tall oil 35-55,

оксиэтилированный алкилфенол 5-10,ethoxylated alkylphenol 5-10,

триэтаноламин 5-10,triethanolamine 5-10,

пентамер пропилена 35-55.propylene pentamer 35-55.

Однако недостатками указанной смазочной добавки являются температура замерзания, непригодная для использования в северных регионах; низкая противоприхватная способность; нестабильность фильтрационной корки ввиду использования чистых талловых масел.However, the disadvantages of this lubricant additive are the freezing point, unsuitable for use in the northern regions; low anti-seize ability; filter cake instability due to the use of pure tall oils.

Наиболее близким решением является смазочная добавка к буровым растворам (RU2684657C1, опубл. 2019.04.11), содержащая растительное масло и углеводородную синтетическую жидкость, отличающаяся тем, что дополнительно содержит сложный эфир жирных кислот растительных масел и поверхностно-активное вещество, в качестве которого используют неионогенное или цвиттерионное поверхностно-активное вещество, при следующем соотношении компонентов, мас. %:The closest solution is a lubricant additive for drilling fluids (RU2684657C1, publ. 2019.04.11) containing vegetable oil and hydrocarbon synthetic fluid, characterized in that it additionally contains a fatty acid ester of vegetable oils and a surfactant, which is a nonionic or zwitterionic surfactant, in the following ratio, wt. %:

Растительное масло 40-80;Vegetable oil 40-80;

Углеводородная синтетическая жидкость 10-40;Hydrocarbon synthetic fluid 10-40;

Сложный эфир жирных кислот растительных масел 5-20;Esters of fatty acids of vegetable oils 5-20;

Неионогенное или цвиттерионное поверхностно-активное вещество 0,5-2.Nonionic or zwitterionic surfactant 0.5-2.

Существенным отличием заявляемой смазочной добавки от прототипа является использование в составе продукта взаимодействия многоатомных спиртов и талловых масел или чистых жирных кислот, другой массовый состав компонентов, что в совокупности обеспечивает синергетический эффект, проявляющийся в повышении устойчивости как в пресных, так и в минерализованных буровых растворах, а также в повышении смазочных и противоприхватных свойств добавки.The essential difference of the claimed lubricant additive from the prototype is the use of polyhydric alcohols and tall oils or pure fatty acids in the composition of the product of the interaction, a different mass composition of the components, which together provides a synergistic effect, manifested in increasing stability in both fresh and mineralized drilling fluids, as well as in increasing the lubricating and anti-seize properties of the additive.

Раскрытие изобретенияDisclosure of invention

В одном аспекте изобретения раскрыта смазочная добавка к буровым растворам, содержащая углеводородную синтетическую жидкость, поверхностно-активное вещество (ПАВ), сложный эфир, причем в качестве сложного эфира используют полученный в результате кислотно-каталитической реакции этерификации продукт взаимодействия многоатомного спирта и по меньшей мере одной из высших жирных кислот талловых масел или продукт взаимодействия многоатомного спирта и дистиллированного таллового масла или сырого таллового масла, при следующем соотношении компонентов, мас. %:In one aspect of the invention, a lubricating additive for drilling fluids is disclosed, containing a hydrocarbon synthetic fluid, a surfactant, an ester, wherein the ester is an acid catalytic esterification reaction product of a reaction between a polyhydric alcohol and at least one from higher fatty acids of tall oils or the product of the interaction of a polyhydric alcohol and distilled tall oil or crude tall oil, in the following ratio, wt. %:

углеводородная синтетическая жидкость: 65-89,5%;hydrocarbon synthetic fluid: 65-89.5%;

продукт взаимодействия многоатомных спиртов и жирных кислот:the product of the interaction of polyhydric alcohols and fatty acids:

10-34,5,10-34.5,

неионогенное или цвиттерионное поверхностно-активное вещество: 0,5-2.nonionic or zwitterionic surfactant: 0.5-2.

В дополнительных аспектах раскрыто, что в качестве жирных кислот используют высшие жирные кислоты; в качестве многоатомного спирта используют одно из следующего: этиленгликоль, пропиленгликоль, бутандиол, глицерин, эритрит, пентаэритрит; в качестве жирных кислот используют, одно из следующего: жирные кислоты растительного масла, жирные кислоты талловых масел, дистиллированное талловое масло, сырое талловое масло, олеиновую кислоту, пальметиновую кислоту, линолевую кислоту; в качестве углеводородной синтетической жидкости используют по меньшей мере одно из следующего: дистиллятные нефтяные масла малой и средней вязкости, экстракты от селективной очистки остаточных нефтяных масел, углеводородные компоненты полученные гидрокрекингом и гидроизомеризацией, высокомолекулярные углеводороды, полиальфаолефины; в качестве неионогенных ПАВ используют одно из следующего: глицерил лаурат, оксиэтилированные спирты, оксиэтилированный моноалкилфенол; в качестве в качестве цвиттерионных ПАВ используют одно из следующего: лецитин, аминокислоты, производные бетаина, кокаминопропил бетаин, имидазолин.In additional aspects, it is disclosed that higher fatty acids are used as fatty acids; as the polyol, one of the following is used: ethylene glycol, propylene glycol, butanediol, glycerin, erythritol, pentaerythritol; as fatty acids, one of the following is used: vegetable oil fatty acids, tall oil fatty acids, distilled tall oil, crude tall oil, oleic acid, palmetic acid, linoleic acid; as a hydrocarbon synthetic fluid, at least one of the following is used: distillate petroleum oils of low and medium viscosity, extracts from the selective purification of residual petroleum oils, hydrocarbon components obtained by hydrocracking and hydroisomerization, high molecular weight hydrocarbons, polyalphaolefins; as nonionic surfactants use one of the following: glyceryl laurate, ethoxylated alcohols, ethoxylated monoalkylphenol; as zwitterionic surfactants use one of the following: lecithin, amino acids, betaine derivatives, cocaminopropyl betaine, imidazoline.

Основными задачами, решаемыми заявленным изобретением, являются сохранение высоких показателей смазочных свойств, таких как снижение коэффициента трения бурильного инструмента о стенки скважины и обсадную колонну, а также повышение противоприхватных свойств, таких как снижение коэффициента потенциального прихвата на границе «металл - глинистая корка» и «метал-металл» в пресных и минерализованных буровых растворах.The main tasks solved by the claimed invention are the preservation of high lubricating properties, such as a decrease in the coefficient of friction of the drilling tool against the borehole walls and the casing, as well as an increase in anti-stick properties, such as a decrease in the coefficient of potential sticking at the interface "metal - clay cake" and " metal-metal” in fresh and mineralized drilling fluids.

Сущность изобретения заключается в том, что использование в составе продукта взаимодействия многоатомных спиртов и талловых масел в совокупности с углеводородной синтетической жидкостью и поверхностно-активным веществом обеспечивает синергетический эффект, проявляющийся в повышении устойчивости как в пресных, так и в минерализованных буровых растворах, а также в повышении смазочных и противоприхватных свойств добавки.The essence of the invention lies in the fact that the use of polyhydric alcohols and tall oils in the composition of the product of interaction in combination with a hydrocarbon synthetic fluid and a surfactant provides a synergistic effect, which is manifested in an increase in stability both in fresh and mineralized drilling fluids, as well as in increasing the lubricating and anti-seize properties of the additive.

Технический результат, достигаемый при осуществлении заявленного изобретения, заключается в повышении смазочных свойств и снижении коэффициента потенциального прихвата на границе «металл - глинистая корка» и «метал-металл» в пресных и минерализованных буровых растворах при низких температурах.The technical result achieved in the implementation of the claimed invention is to increase the lubricating properties and reduce the coefficient of potential sticking at the border "metal-clay cake" and "metal-metal" in fresh and mineralized drilling fluids at low temperatures.

Краткое описание чертежейBrief description of the drawings

Фиг. 1 показывает схему реакции взаимодействия высших жирных кислот и многоатомных спиртов.Fig. 1 shows a reaction scheme for the interaction of higher fatty acids and polyhydric alcohols.

Осуществление изобретенияImplementation of the invention

Поставленная задача решается тем, что получают смазочную добавку, содержащую углеводородную синтетическую жидкость, сложный эфир жирных кислот растительных масел и поверхностно-активное вещество при следующем соотношении компонентов, мас. %:The problem is solved by obtaining a lubricant additive containing a hydrocarbon synthetic fluid, an ester of fatty acids of vegetable oils and a surfactant in the following ratio, wt. %:

жирных кислот растительных масел и поверхностно-активное вещество при следующем соотношении компонентов, мас.%:fatty acids of vegetable oils and a surfactant in the following ratio of components, wt.%:

углеводородная синтетическая жидкостьhydrocarbon synthetic fluid 65-89,5 65-89.5 продукт взаимодействия многоатомных спиртов и жирных кислотreaction product of polyhydric alcohols and fatty acids 10-34,510-34.5 неионогенное или цвиттерионное поверхностно-активное веществоnonionic or zwitterionic surfactant 0,5-20.5-2

Процесс получения смазочной добавки осуществляется в две стадии.The process of obtaining a lubricant additive is carried out in two stages.

I стадия:I stage:

Кислотно-каталитическая реакция этерификации - получение сложных эфиров в результате взаимодействия высших жирных кислот и многоатомных спиртов. Схема химической реакции показана на фиг. 1Acid-catalytic esterification reaction - obtaining esters as a result of the interaction of higher fatty acids and polyhydric alcohols. The scheme of the chemical reaction is shown in Fig. 1

Реакцию проводят в интервале температур от 140 до 200°С в течение 2-6 часов в присутствии кислотного катализатора. Контроль протекания реакции ведется по кислотному числу.The reaction is carried out in the temperature range from 140 to 200°C for 2-6 hours in the presence of an acid catalyst. The reaction progress is monitored by acid number.

II стадия:II stage:

Смешение продукта синтеза с другими компонентами смазки. Для этого полученную активную основу охлаждают и производят смешение с остальными компонентами смазки с помощью мешалки не менее 30 минут до получения однородной массы.Mixing the synthesis product with other lubricant components. To do this, the resulting active base is cooled and mixed with the rest of the lubricant components using a stirrer for at least 30 minutes until a homogeneous mass is obtained.

Подробные варианты осуществленияDetailed Embodiments

В качестве многоатомного спирта используют, например, этиленгликоль, пропиленгликоль, бутандиол, глицерин, эритрит, пентаэритрит.As the polyhydric alcohol, for example, ethylene glycol, propylene glycol, butanediol, glycerol, erythritol, pentaerythritol are used.

В качестве источника жирных кислот используют, например, жирные кислоты растительного масла, жирные кислоты талловых масел, дистиллированное талловое масло, сырое талловое масло, олеиновую, пальметиновую или линолевую кислоту.As a source of fatty acids, for example, vegetable oil fatty acids, tall oil fatty acids, distilled tall oil, crude tall oil, oleic, palmetic or linoleic acid are used.

В качестве синтетической жидкости используют, например, дистиллятные нефтяные масла малой и средней вязкости, экстракты от селективной очистки остаточных нефтяных масел, дистиллятные и остаточные компоненты различной вязкости (углеводороды), углеводородные компоненты полученные гидрокрекингом и гидроизомеризацией, а также синтетические продукты (высокомолекулярные углеводороды, полиальфаолефины и другие) и их смеси.As a synthetic fluid, for example, distillate petroleum oils of low and medium viscosity, extracts from the selective purification of residual petroleum oils, distillate and residual components of various viscosities (hydrocarbons), hydrocarbon components obtained by hydrocracking and hydroisomerization, as well as synthetic products (high molecular weight hydrocarbons, polyalphaolefins and others) and mixtures thereof.

В качестве поверхностно-активного вещества (далее по тексту - ПАВ) используют неионогенные ПАВ или цвиттерионнные ПАВ. В качестве неионогенных ПАВ используют, например, глицерил лаурат, оксиэтилированные спирты, например, оксиэтилированный моноалкилфенол. В качестве цвиттерионных используют, например, лецитин, аминокислоты, производные бетаина, например, кокаминопропил бетаин и имидазолин.Non-ionic surfactants or zwitterionic surfactants are used as a surfactant (hereinafter referred to as surfactant). As nonionic surfactants, for example, glyceryl laurate, ethoxylated alcohols, for example, ethoxylated monoalkylphenol are used. As zwitterionics, for example, lecithin, amino acids, betaine derivatives, such as cocaminopropyl betaine and imidazoline are used.

Концентрация активной основы (продукта взаимодействия жирных кислот и многоатомных спиртов) 10-34,5% является оптимальной, так как при концентрации ниже 10% все преимущества смазки проявляются слабо, а при увеличение активной основы свыше 34,5% роста полезных свойств не наблюдается.The concentration of the active base (the product of the interaction of fatty acids and polyhydric alcohols) of 10-34.5% is optimal, since at a concentration below 10%, all the benefits of the lubricant are weak, and with an increase in the active base over 34.5%, no growth in useful properties is observed.

Заявляемая смазочная добавка обладает следующим преимуществами по сравнению с прототипом:The inventive lubricant additive has the following advantages compared to the prototype:

1) Образование более прочной смазочной пленки на поверхности металла.1) Formation of a stronger lubricating film on the metal surface.

2) более низкая температуры застывания (ниже минус 35°С), что позволяет эффективно применять заявленную смазку в северных регионах проведения работ. При температуре ниже - 35°С смазка по прототипу застывает и перестает работать.2) lower pour point (below minus 35°C), which allows the effective application of the claimed lubricant in the northern regions of the work. At temperatures below - 35°C grease prototype hardens and stops working.

Эффективность смазочной добавки оценивали по стандарту Американского нефтяного института на приборе Lubricity Tester фирмы OFITE путем определения коэффициента трения пары "металл-металл" (Ктр в паре «М-М»). Для измерения коэффициента трения в паре «металл-фильтрационная корка» (Ктр в паре «М-ФК») использовали прибор ФСК-4Э.The effectiveness of the lubricant additive was evaluated according to the American Petroleum Institute standard on the OFITE Lubricity Tester by determining the coefficient of friction of the metal-to-metal pair (Ktr in the M-M pair). The FSK-4E device was used to measure the friction coefficient in the “metal-filter cake” pair (Ktr in the “M-FK” pair).

Результаты исследования смазочного состава показаны в таблице ниже:The results of the study of the lubricant composition are shown in the table below:

МАССОВОЕ СОДЕРЖАНИЕMASS CONTENT СОСТАВCOMPOUND Состав 1Composition 1 Состав 2Composition 2 Состав 3Composition 3 Состав 4Composition 4 Состав 5Composition 5 Состав 6Composition 6 углеводородная синтетическая жидкостьhydrocarbon synthetic fluid дистиллятные нефтяные масла малой и средней вязкостиdistillate petroleum oils of low and medium viscosity 6565 9090   экстракты от селективной очистки остаточных нефтяных маселextracts from selective purification of residual petroleum oils   7070       7575 углеводородные компоненты полученные гидрокрекингом и гидроизомеризациейhydrocarbon components obtained by hydrocracking and hydroisomerization   8080 полиальфаолефиныpolyalphaolefins 9090     поверхностно-активное веществоsurface-active substance глиерил лауратglieryl laurate 0,50.5 22   оксиэтилированные спиртыethoxylated alcohols 11 лецитинlecithin 1,51.5 0,50.5 имидазолинimidazoline 22     продукт взаимодействия спиртов и жирных кислот reaction product of alcohols and fatty acids 34,534.5 8,08.0   пропиленгликоль и жирные кислоты талловых маселpropylene glycol and tall oil fatty acids 29,029.0 бутандиол и дистиллированное талловое маслоbutanediol and distilled tall oil 8,08.0     эритрит и сырое талловое маслоerythritol and crude tall oil 18,518.5 пентаэритрит и дистиллированное талловое маслоpentaerythritol and distilled tall oil 24,524.5 коэффициент трения М-М, при температуре -35°Сcoefficient of friction M-M, at a temperature of -35°C 0,310.31 0,280.28 0,270.27 0,270.27 0,270.27 0,320.32 коэффициент трения М-ФК, при температуре -35°Сcoefficient of friction M-FK, at a temperature of -35°C 0,340.34 0,320.32 0,350.35 0,320.32 0,330.33 0,340.34

Как видно из таблицы, заявленная смазка обеспечивает сохранение высоких показателей смазочных свойств на границе «металл - глинистая корка» и «металл - металл» при низких температурах.As can be seen from the table, the claimed lubricant ensures the preservation of high lubricating properties at the interface "metal - clay cake" and "metal - metal" at low temperatures.

Варианты осуществления не ограничиваются описанными здесь вариантами осуществления, специалисту в области техники на основе информации, изложенной в описании, и знаний уровня техники станут очевидны и другие варианты осуществления изобретения, не выходящие за пределы сущности и объема данного изобретения.Embodiments are not limited to the embodiments described herein, other embodiments of the invention will become apparent to those skilled in the art based on the information set forth in the description and knowledge of the prior art without going beyond the spirit and scope of the present invention.

Способы, раскрытые здесь, содержат один или несколько этапов или действий для достижения описанного способа. Этапы и/или действия способа могут заменять друг друга, не выходя за пределы объема формулы изобретения. Другими словами, если не определен конкретный порядок этапов или действий, порядок и/или использование конкретных этапов и/или действий может изменяться, не выходя за пределы объема формулы изобретения.The methods disclosed herein contain one or more steps or actions to achieve the described method. The steps and/or steps of the method may replace one another without departing from the scope of the claims. In other words, if no specific order of steps or actions is specified, the order and/or use of specific steps and/or actions may be varied without departing from the scope of the claims.

Несмотря на то, что примерные варианты осуществления были подробно описаны и показаны на сопроводительных чертежах, следует понимать, что такие варианты осуществления являются лишь иллюстративными и не предназначены ограничивать более широкое изобретение, и что данное изобретение не должно ограничиваться конкретными показанными и описанными компоновками и конструкциями, поскольку различные другие модификации могут быть очевидны специалистам в соответствующей области.While the exemplary embodiments have been described in detail and shown in the accompanying drawings, it should be understood that such embodiments are illustrative only and are not intended to limit the wider invention, and that the invention is not to be limited to the particular arrangements and structures shown and described. as various other modifications may be apparent to those skilled in the art.

Признаки, упомянутые в различных зависимых пунктах формулы, а также реализации раскрытые в различных частях описания могут быть скомбинированы с достижением полезных эффектов, даже если возможность такого комбинирования не раскрыта явно.Features mentioned in various dependent claims, as well as implementations disclosed in various parts of the description, can be combined to achieve beneficial effects, even if the possibility of such a combination is not explicitly disclosed.

Claims (6)

1. Смазочная добавка к буровым растворам, содержащая углеводородную синтетическую жидкость, поверхностно-активное вещество ПАВ, сложный эфир, отличающаяся тем, что в качестве сложного эфира используют полученный в результате кислотно-каталитической реакции этерификации продукт взаимодействия многоатомного спирта и по меньшей мере одной из высших жирных кислот талловых масел или продукт взаимодействия многоатомного спирта и дистиллированного таллового масла или сырого таллового масла, при следующем соотношении компонентов, мас.%:1. A lubricating additive for drilling fluids containing a hydrocarbon synthetic fluid, a surfactant, an ester, characterized in that the ester is the product of the interaction of a polyhydric alcohol and at least one of the higher fatty acids of tall oils or the product of the interaction of a polyhydric alcohol and distilled tall oil or crude tall oil, in the following ratio, wt.%: углеводородная синтетическая жидкостьhydrocarbon synthetic fluid 65-89,5 65-89.5 указанный продукт взаимодействияspecified interaction product многоатомного спирта и жирных кислотpolyhydric alcohol and fatty acids 10-34,5 10-34.5 неионогенное или цвиттерионное ПАВnonionic or zwitterionic surfactant 0,5-2 0.5-2 2. Добавка по п. 1, в которой в качестве многоатомного спирта используют одно из следующего: пропиленгликоль, бутандиол, эритрит, пентаэритрит.2. The additive of claim 1 wherein the polyhydric alcohol is one of the following: propylene glycol, butanediol, erythritol, pentaerythritol. 3. Добавка по п. 1, в которой в качестве углеводородной синтетической жидкости используют по меньшей мере одно из следующего: дистиллятные нефтяные масла малой и средней вязкости, экстракты от селективной очистки остаточных нефтяных масел, углеводородные компоненты, полученные гидрокрекингом и гидроизомеризацией, высокомолекулярные углеводороды, полиальфаолефины.3. The additive according to claim 1, wherein at least one of the following is used as the hydrocarbon synthetic fluid: distillate petroleum oils of low and medium viscosity, extracts from the selective refining of residual petroleum oils, hydrocarbon components obtained by hydrocracking and hydroisomerization, high molecular weight hydrocarbons, polyalphaolefins. 4. Добавка по п. 1, в которой в качестве неионогенных ПАВ используют одно из следующего: глицерил лаурат, оксиэтилированные спирты, оксиэтилированный моноалкилфенол.4. The additive of claim 1 wherein the nonionic surfactants are one of the following: glyceryl laurate, ethoxylated alcohols, ethoxylated monoalkylphenol. 5. Добавка по п. 1, в которой в качестве цвиттерионных ПАВ используют одно из следующего: лецитин, аминокислоты, производные бетаина, кокаминопропил бетаин, имидазолин.5. An additive according to claim 1, wherein the zwitterionic surfactants are one of the following: lecithin, amino acids, betaine derivatives, cocaminopropyl betaine, imidazoline.

Images