RU2664340C1 - Absorbing infrared radiation homogeneous composition for textile product treatment - Google Patents

Abstract

FIELD: physics.

SUBSTANCE: invention relates to the development of concealment means, to compositions absorbing electromagnetic radiation in the near infrared wavelength range used for applying to the textile base products, used to mask servicemen for the purpose of their electromagnetic camouflage in the spectrum of the near infrared wavelength range. Composition absorbing infrared radiation for applying to the surface of textile products consists of the following components (in vol. %): or liquid mineral, semi-synthetic, synthetic hydrocarbons of technical purpose in the form of multi-grade engine oil, or liquid hydrocarbons of plant origin of food purpose in the form of edible vegetable oil, or a combination of the above liquid hydrocarbons in an arbitrary ratio of 90–91 %; pigment "soot", in the form of monochrome, black, magnetic or non-magnetic mechanical toner or in the form of carbon black in the native state or in an arbitrarily taken ratio of the above substances in an amount of 3–4 %; paraffin – 5–6 %.

EFFECT: increase the strength of the coating while increasing the thermal insulation properties, ease of use and economy.

1 cl, 4 dwg

Description

Изобретение относится к сфере разработок средств маскировки, к составам, поглощающим электромагнитное излучение в спектре ближнего инфракрасного диапазона длин волн, используемым для нанесения на текстильную основу изделий, применяемых для маскирования военнослужащих с целью их электромагнитного камуфляжа в спектре ближнего инфракрасного диапазона длин волн.The invention relates to the field of development of camouflage means, to compositions that absorb electromagnetic radiation in the near infrared range of wavelengths used for applying to the textile base products used to mask military personnel with the aim of their electromagnetic camouflage in the near infrared range of wavelengths.

Область техники, к которой относится изобретение.The technical field to which the invention relates.

Изобретение относится к сфере разработок средств маскировки, составам для обработки текстильных материалов, предназначенных для поглощения инфракрасного излучения генерируемого внешними источниками электромагнитных волн инфракрасного спектра с целью маскировки военнослужащих и объектов военного назначения, обеспечения инфракрасного электромагнитного камуфляжа в полевых условиях в сумеречное и темное время суток.The invention relates to the development of masking agents, compositions for processing textile materials designed to absorb infrared radiation generated by external sources of electromagnetic waves in the infrared spectrum in order to mask military personnel and military objects, to provide infrared electromagnetic camouflage in the field at dusk and night.

Уровень техники.The level of technology.

Сведений об известных заявителю аналогах изобретения с выделением из них аналога наиболее близкого к изобретению (прототипа) по сфере его применения, заявителем в открытых источниках выявлено не было.Information about analogues of the invention known to the applicant with the isolation from them of an analogue closest to the invention (prototype) in the field of its application was not revealed by the applicant in open sources.

Известны приборы ночного видения (далее - «ПНВ»), работающие в ближнем инфракрасном диапазоне длин волн (0,78-1 мкм) [1].Known night vision devices (hereinafter - "NVD"), operating in the near infrared wavelength range (0.78-1 μm) [1].

Работа ПНВ основана на основе фотонного эффекта, обеспечиваемого электронно-оптическим преобразователем (ЭОП), изготовленного на основе фоточувствительных элементов. В отличие от приборов теплового видения ЭОП работает на основе внешнего фотоэффекта. Электронно-оптические преобразователи (ЭОП) - оптические приборы с высоким коэффициентом усиления. В отличие от приборов теплового видения, для работы приборов на основе ЭОП требуется хотя бы незначительная подсветка.The work of NVD is based on the basis of the photon effect provided by an electron-optical converter (EOP) made on the basis of photosensitive elements. Unlike thermal vision devices, the image intensifier tube operates on the basis of an external photoelectric effect. Electron-optical converters (EOCs) are optical devices with a high gain. Unlike thermal vision devices, the operation of devices based on the image intensifier tube requires at least slight illumination.

ПНВ могут работать как в пассивном, так и в активном режиме. Пассивный режим применяется при наличии собственного излучения объекта наблюдения и в условиях слабого рассеянного излучения случайных искусственных или естественных источников, уровень которого превышает 10^-5 лк. Активный режим используется в условиях полного отсутствия освещения для облучения исследуемого объекта и получения отраженного от него инфракрасного света. Он сопровождается применением источника подсветки объекта наблюдения. Им может быть лазерный светодиод или специальный ИК-прожектор, как правило, работающий в диапазоне длин волн 0,82-0,98 мкм.NVDs can work both in passive and in active mode. The passive mode is applied in the presence of intrinsic radiation of the object under observation and in conditions of weak scattered radiation from random artificial or natural sources, the level of which exceeds 10 ^-5 lux. The active mode is used in conditions of complete absence of lighting to irradiate the studied object and to receive infrared light reflected from it. It is accompanied by the use of the illumination source of the observation object. It can be a laser LED or a special IR illuminator, as a rule, operating in the wavelength range of 0.82-0.98 microns.

На изображениях, полученных с помощью ПНВ, объекты с высокой отражательной способностью выглядят в виде ярких силуэтов. Этот эффект обусловлен отраженным от поверхности объекта инфракрасным излучением, исходящим от внешнего источника (например, подсветка ПНВ).In images obtained using NVD, objects with high reflectivity look like bright silhouettes. This effect is due to infrared radiation reflected from the surface of the object coming from an external source (for example, NVD illumination).

Способ и эффективность блокирования процессов, как отражения падающего на объект ИК-излучения, так и температурного равновесия, определяет качество инфракрасного электромагнитного камуфляжа.The method and effectiveness of blocking processes, both the reflection of infrared radiation incident on an object and temperature equilibrium, determines the quality of infrared electromagnetic camouflage.

Известные подходы маскировки объектов от обнаружения их детекторами инфракрасного излучения основаны на методе теплоотражения через технологии теплоизоляции маскируемого объекта с целью замедления выравнивания контраста отражения инфракрасного излучения между объектом и окружающей средой.Known approaches to masking objects from being detected by infrared radiation detectors are based on the heat reflection method through the thermal insulation technology of a masked object in order to slow down the alignment of the infrared reflection contrast between the object and the environment.

Например, в патенте США 5281460 [2] предлагается рисунок из полос, наложенный на пористую нейлоновую сетку. Полосы покрываются серебром, медью или пигментом.For example, US Pat. No. 5,282,460 [2] proposes a strip pattern overlaid on a porous nylon mesh. The bands are coated with silver, copper or pigment.

В патенте США 4495239 [3] применяется слой-основание из текстильной ткани, на который методом осаждения из газовой фазы наносится металлический отражающий слой, а затем производится камуфляжная раскраска.US Pat. No. 4,495,239 [3] uses a textile fabric base layer onto which a metal reflective layer is deposited by vapor deposition and then camouflaged.

В патенте США 4659602 [4] используется тканый материал, на котором располагаются металлическая фольга и полиэтиленовая пленка, содержащая проводящие частицы.US Pat. No. 4,659,602 [4] uses a woven material on which metal foil and a polyethylene film containing conductive particles are arranged.

В патенте США 4621012 [5] текстильный материал покрыт термопластом, содержащим внутри выбранный дипольный материал и имеющим металлический слой, который отражает инфракрасное излучение.In US Pat. No. 4,621,012 [5], the textile material is coated with a thermoplastic material containing inside a selected dipole material and having a metal layer that reflects infrared radiation.

В патенте США 4064305 [6] предлагается трикотаж из нитей, выполненных из резаных полимерных волокон и резаных металлических волокон, которые отражают волны радара.US Pat. No. 4,064,305 [6] proposes knitwear made of cut polymer fibers and cut metal fibers that reflect radar waves.

В патенте США 4529633 [7] описывается электромагнитный отражающий материал, состоящий из слоя полиэтилена, слоя металлического покрытия, клеящего вещества и ткани.US Pat. No. 4,529,633 [7] describes an electromagnetic reflective material consisting of a layer of polyethylene, a layer of a metal coating, an adhesive and a fabric.

В патенте США 4533591 [8] предлагается термопластичная смола с рассеянными в ней дискретными электромагнитными частицами.US Pat. No. 4,533,591 [8] proposes a thermoplastic resin with discrete electromagnetic particles scattered therein.

В патенте США 4467005 [9] используется опорная сетка, на обеих сторонах которой имеется несущее полотно с металлическим покрытием, отражающим ИК излучение.US Pat. No. 4,467,005 [9] uses a support net, on both sides of which there is a carrier web with a metal coating reflecting IR radiation.

В патенте США 97118428/12 (Пат. RU 2127194) [10] материал с покрытием, отражающим инфракрасное излучение, содержит, по меньшей мере, одну металлизированную микропористую мембрану, дублированную, по меньшей мере, с еще одним слоем текстильного материала. В материале металлизированная мембрана выполнена из микропористого вспененного политетрафторэтилена, текстильная основа представляет собой шелк, а металл - алюминий.In US patent 97118428/12 (Pat. RU 2127194) [10] the material with a coating that reflects infrared radiation, contains at least one metallized microporous membrane, duplicated, at least one more layer of textile material. In the material, the metallized membrane is made of microporous foamed polytetrafluoroethylene, the textile base is silk, and the metal is aluminum.

В патенте РФ 2403328 [11] описывается материал с покрытием, отражающим инфракрасное излучение, содержащий текстильную основу в виде полиэфирного текстильного материала с водоотталкивающей пропиткой, металлизированный слой в виде нитрида титана, нанесенного на микропористый мембранный слой на атомарно-молекулярном уровне, и микропористый мембранный слой, выполненный из термопластичной полиуретановой смолы, который размещен между текстильной основой и металлизированным слоем. В диссертации на соискание ученой степени кандидата технических наук по теме "Разработка технологии производства экранирующих швейных изделий" Специальность 05.19.04 - «Технология швейных изделий» (ИГТА, Иваново, 2007 г.) [12], непосредственно связанной с патентом РФ 2403328 [11], решены задачи по разработке и маскировочной одежды для военнослужащих, где впервые использовалось металлизированное покрытие, применение которого значительно повышает маскировочные свойства изделий аналогичного назначения. Теоретически доказано и практически подтверждено, что применение металлизированного покрытия позволит повысить экранирующие свойства изделия [13]. Для снижения теплового излучения от тела человека выбирались пакеты материалов с применением технологии металлизации покрытия внутренней поверхности костюма, которая позволяет повысить экранирующие свойства изделия в 14,5 раз при использовании алюминия, а при использовании титана и нитрида титана - в 23 и 36,5 раза соответственно.In the patent of the Russian Federation 2403328 [11] describes a material with a coating that reflects infrared radiation, containing a textile base in the form of a polyester textile material with water-repellent impregnation, a metallized layer in the form of titanium nitride deposited on a microporous membrane layer at the atomic-molecular level, and a microporous membrane layer made of thermoplastic polyurethane resin, which is placed between the textile base and the metallized layer. In the dissertation for the degree of candidate of technical sciences on the topic "Development of technology for the production of shielding garments" Specialty 05.19.04 - "Technology of garments" (IGTA, Ivanovo, 2007) [12], which is directly related to RF patent 2403328 [11 ], the tasks of designing and camouflage clothing for military personnel were solved, where for the first time a metallized coating was used, the use of which significantly increases the camouflage properties of products of similar purpose. It has been theoretically proved and practically confirmed that the use of a metallized coating will improve the shielding properties of the product [13]. To reduce thermal radiation from the human body, packages of materials were selected using the metallization technology of coating the inner surface of the suit, which allows to increase the shielding properties of the product by 14.5 times when using aluminum, and when using titanium and titanium nitride - by 23 and 36.5 times, respectively .

Недостатками вышеперечисленных изобретений являются:The disadvantages of the above inventions are:

- ограниченный методологический подход к созданию свойств электромагнитного камуфляжа, избирательно основанный на методе отражения инфракрасного биологического аутоизлучения посредством увеличения изолирующих инфракрасное излучение характеристик камуфлирующих материалов без учета необходимости их комплексного сочетания со свойствами теплопроводности используемых материалов, возможностью используемых материалов обеспечивать поглощение внешнего инфракрасного облучения, направленного на биологический объект;- a limited methodological approach to creating the properties of electromagnetic camouflage, selectively based on the method of reflecting infrared biological autoradiation by increasing the infrared radiation-insulating characteristics of camouflage materials without taking into account the need for their complex combination with the thermal conductivity of the materials used, the ability of the materials used to absorb external infrared radiation aimed at biological an object;

- материалы по уровню их изготовления являются продуктами высокотехнологичного и ресурсоемкого промышленного производства в частности, использующего технологии газового напыления или методов прессования, что очевидно показывает невозможность их оперативного создания в полевых условиях из доступных и подручных компонентов или восстановления подобных тканей в полевых условиях при наличии обширных повреждений;- materials at the level of their manufacture are products of high-tech and resource-intensive industrial production, in particular, using gas spraying technologies or pressing methods, which obviously shows the impossibility of their prompt creation in the field from available and available components or restoration of such fabrics in the field in the presence of extensive damage ;

- отсутствие в приведенных выше изобретениях данных об эффективном временном периоде обеспечения изотермического баланса между собственным инфракрасным излучением биологического объекта (внутренняя среда) и внешней средой, где границей раздела сред является теплоизолирующее покрытие объекта наблюдения, использующего известный тип электромагнитного камуфляжа, представляются важным практическим недостатком описанных выше изобретений.- the absence in the above inventions of data on the effective time period for ensuring an isothermal balance between the intrinsic infrared radiation of a biological object (internal environment) and the external environment, where the interface is a heat-insulating coating of an observation object using a known type of electromagnetic camouflage, are an important practical drawback of the above inventions.

Однако, существует еще одна характеристика теплового излучения - поглощательная способность тела, определяемая через коэффициент поглощения тела, рассчитываемого как отношение поглощенного потока лучистой энергии, падающей на элементарную площадку тела к потоку лучистой энергии, падающему на эту площадку, обусловленного электромагнитными волнами, длина которых заключена в заданном интервале.However, there is another characteristic of thermal radiation - the absorption capacity of the body, determined through the absorption coefficient of the body, calculated as the ratio of the absorbed flux of radiant energy incident on the elementary area of the body to the flux of radiant energy incident on this area, due to electromagnetic waves, the length of which is enclosed in given interval.

Коэффициент поглощения тела зависит от длины волны падающего излучения, от температуры тела, его химического состава и состояния поверхности. По определению коэффициент поглощения не может быть больше 1. Тело, поглощающее все падающее на него излучение независимо от направления падения излучения и его спектрального состава, называется абсолютно черным телом. Для такого тела коэффициент поглощения равен единице для всех длин волн и температур.The absorption coefficient of the body depends on the wavelength of the incident radiation, on the temperature of the body, its chemical composition and surface condition. By definition, the absorption coefficient cannot be greater than 1. A body that absorbs all the radiation incident on it, regardless of the direction of incidence of the radiation and its spectral composition, is called a completely black body . For such a body, the absorption coefficient is equal to unity for all wavelengths and temperatures.

Тела, для которых коэффициент поглощения в широком интервале длин волн остается постоянным, но меньше единицы, называются серыми телами. У серых тел коэффициент поглощения зависит только от температуры, материала и состояния поверхности. Между спектральной плотностью энергетической светимости и коэффициентом поглощения любого тела существует прямая связь - такая система через некоторое время придет в состояние теплового равновесия - все тела примут одну и ту же температуру, равную температуре оболочки. В таком состоянии тело, обладающее большей спектральной плотностью энергетической светимости, теряет в единицу времени с единицы поверхности больше энергии, чем тело, обладающее меньшей. Поскольку температура (а следовательно и энергия) тел не меняется, то тело, излучающее больше энергии, должно и больше поглощать, т.е. обладать большей спектральной плотностью энергетической светимости. Таким образом, чем больше спектральная плотность энергетической светимости тела, тем больше и его коэффициент поглощения потока лучистой энергии, падающей на элементарную площадку, обусловленного электромагнитными волнами, длины которых заключены в заданном интервале.Bodies for which the absorption coefficient in a wide range of wavelengths remains constant, but less than unity, are called gray bodies . In gray bodies, the absorption coefficient depends only on temperature, material and surface condition. There is a direct connection between the spectral density of energy luminosity and the absorption coefficient of any body - such a system will come to a state of thermal equilibrium after some time - all bodies will take the same temperature equal to the shell temperature. In this state, a body with a higher spectral density of energy luminosity loses more energy per unit time per unit surface than a body that has a smaller one. Since the temperature (and hence the energy) of bodies does not change, the body radiating more energy must absorb more, i.e. have a higher spectral density of energy luminosity. Thus, the greater the spectral density of the energy luminosity of a body, the greater is its absorption coefficient for the flux of radiant energy incident on an elementary site due to electromagnetic waves whose lengths are in a given interval.

Это соотношение выражает закон, установленный Кирхгофом (1859): Отношение спектральной плотности энергетической светимости к коэффициенту поглощения не зависит от природы тел, является для всех тел одной и той же (универсальной) функцией длины волны (частоты) и температуры и равно спектральной плотности энергетической светимости абсолютно черного тела.This relation expresses the law established by Kirchhoff (1859): The ratio of the spectral density of energy luminosity to the absorption coefficient does not depend on the nature of the bodies, is for all bodies the same (universal) function of wavelength (frequency) and temperature and is equal to the spectral density of energy luminosity absolutely black body.

Важное значение применительно к предмету изобретения приобретает следствие, вытекающее из закона Кирхгофа:With respect to the subject of the invention, the consequence arising from Kirchhoff’s law is of great importance:

1. Всякое тело при данной температуре излучает электромагнитные волны той частоты, которые оно поглощает при той же температуре.1. Every body at a given temperature emits electromagnetic waves of that frequency, which it absorbs at the same temperature.

Законом Стефана-Больцмана определено, что энергетическая светимость абсолютно черного тела пропорциональна четвертой степени температуры, и в соответствии с I законом Вина (законом смещения) длина волны, на которую приходится максимальная спектральная плотность энергетической светимости абсолютно черного тела, обратно пропорциональна температуре Т., т.е. из термодинамических соображений следует, что равновесная плотность энергии излучения зависит только от температуры и не зависит от свойств стенок полости.The Stefan-Boltzmann law determines that the energy luminosity of an absolutely black body is proportional to the fourth power of the temperature, and in accordance with Wien's law (the law of displacement), the wavelength at which the maximum spectral density of the energy luminosity of an absolutely black body is inversely proportional to the temperature T., t .e. from thermodynamic considerations it follows that the equilibrium radiation energy density depends only on temperature and does not depend on the properties of the cavity walls.

Следовательно, из высказанных выше утверждений применительно предмета изобретения вытекает принципиально важный вывод:Therefore, from the statements made above regarding the subject of the invention, a fundamentally important conclusion follows:

- независимо от известных видов материалов, их структурного построения с течением времени отражающие инфракрасное излучение объекта свойства таких материалов вследствие влияния термодинамических закономерностей будут снижаться;- regardless of the known types of materials, their structural construction over time, the properties of such materials reflecting the infrared radiation of an object will decrease due to the influence of thermodynamic laws;

Тем самым, применение свойств материалов, поглощающих электромагнитное излучение инфракрасного спектра длин волн, поступающих как в режиме облучения объекта из внешней среды, так и в режиме инфракрасного аутоизлучения объекта, приобретает уровень альтернативного направления развития методов электромагнитного камуфляжа.Thus, the application of the properties of materials that absorb electromagnetic radiation from the infrared wavelength spectrum, both in the mode of irradiating the object from the external environment and in the infrared mode of the object, acquires the level of an alternative direction in the development of electromagnetic camouflage methods.

Известны сведения о материалах, способных поглощать и отражать инфракрасное излучение, которые представляют определенную (методологическую) связь с предметом настоящего изобретения:Information is known about materials capable of absorbing and reflecting infrared radiation, which represent a certain (methodological) connection with the subject of the present invention:

В патенте РФ 2197041 [14] описан способ получения многослойных нетканых материалов из смески диэлектрических и электропроводящих волокон, обладающих радиопоглощающими свойствами в широком диапазоне электромагнитного излучения (ЭМИ) путем предварительного формования холстов из синтетических волокон, диспергирования углеродного волокна в жидкой или газообразной среде, фильтрования дисперсии сквозь холст из синтетических волокон или укладки ленты электропроводящих материалов на холст из синтетических волокон, сборки многослойного пакета из, по крайней мере, двух нетканых синтетических холстов, на один из которых наносят слой углеродных волокон или лент электропроводящих материалов так, чтобы слой углеродных волокон или лент электропроводящих материалов чередовался со слоем холстов из синтетических волокон, с последующим прокалыванием собранного многослойного пакета иглами. Изобретение относится к поглотителям электромагнитных волн и средствам маскировки, а более конкретно к способам получения многослойных нетканых материалов из смеси диэлектрических и электропроводящих волокон, обладающих радиопоглощающими свойствами в широком диапазоне электромагнитного излучения (ЭМИ).RF patent 2197041 [14] describes a method for producing multilayer nonwoven materials from a mixture of dielectric and electrically conductive fibers having radio-absorbing properties in a wide range of electromagnetic radiation (EMR) by pre-forming canvases from synthetic fibers, dispersing carbon fibers in a liquid or gaseous medium, and filtering the dispersion through a canvas of synthetic fibers or laying a tape of electrically conductive materials on a canvas of synthetic fibers, assembly of a multilayer package from at least two synthetic non-woven webs, one of which is applied a layer of carbon fibers or ribbons of conductive material so that a layer of carbon fibers or ribbons of conductive material alternated with fiber batts of synthetic fibers, followed by piercing of needles assembled multilayer package. The invention relates to absorbers of electromagnetic waves and means of camouflage, and more particularly to methods for producing multilayer nonwoven materials from a mixture of dielectric and conductive fibers having radio-absorbing properties in a wide range of electromagnetic radiation (EMR).

В патенте РФ №2343547 [15]описывается способ защиты от подделки ценных изделий и контроля их подлинности, при котором на ценном изделии формируют пассивное защитное средство заданной структуры, обеспечивают возможность контроля его наличия и подлинности, в качестве материала защитного средства используют островковые пленки Со наноразмерного уровня, а также мультислои, в которых островковые пленки Со отделены наноразмерными слоями SiO₂, при этом для определения информативных признаков используют аномальное поглощение зондирующего электромагнитного излучения оптического диапазона, в качестве которого используют лазерное излучение в инфракрасном оптическом диапазоне длин волн, а возможность контроля наличия и подлинности защитного средства обеспечивают методом анализа по оптическим эффектам в процессе внешнего воздействия на него указанного излучения и детектирования информативных признаков в оптическом отклике защитного средства на упомянутое внешнее воздействие, заключающемся в снижении интенсивности отраженного излучения, с последующим сопоставлением зарегистрированных параметров информативных признаков с информативными признаками, содержащимися в базе данных средства детектирования.RF patent No. 2343547 [15] describes a method of protecting against counterfeiting of valuable products and controlling their authenticity, in which a passive protective agent of a given structure is formed on a valuable product, it is possible to control its presence and authenticity, island material Co nanoscale is used as a protective agent material level, as well as multilayers in which the island Co films are separated by nanosized layers of SiO ₂ , while anomalous absorption of the probing electrodes is used to determine informative features magnetic radiation of the optical range, which is used as laser radiation in the infrared optical wavelength range, and the ability to control the presence and authenticity of a protective agent is provided by an analysis of the optical effects during the external action of said radiation and detecting informative signs in the optical response of the protective agent to the mentioned external effect, which consists in reducing the intensity of the reflected radiation, followed by a comparison of zaregis tripled parameters of informative features with informative features contained in the database of the detection tool.

В патенте РФ 2456558 [16] описывается устройство для определения альбедо деятельной поверхности материала, состоящее из двух идентичных тепловоспринимающих элементов, приемные поверхности которых разнонаправлено обращены в сторону источника инфракрасного излучения и к поверхности исследуемого материала для поглощения лучистых потоков, и термопар, отличающееся тем, что приемные поверхности и боковые грани металлических пластин тепловоспринимающих элементов покрыты черной влагонепроницаемой краской, поверхности пластин, противоположные приемным поверхностям, закрыты слоем теплогидроизоляции со светоотражательной пленкой, термопары регистрируют нагрев пластин во времени, по которому математически рассчитывают альбедо деятельной поверхности материала.RF patent 2456558 [16] describes a device for determining the albedo of the active surface of a material, consisting of two identical heat-receiving elements, the receiving surfaces of which are multidirectional facing the source of infrared radiation and the surface of the material under study for absorption of radiant fluxes, and thermocouples, characterized in that the receiving surfaces and the side faces of the metal plates of the heat-absorbing elements are coated with black waterproof paint, the surfaces of the plates are opposite e receiving surfaces, closed with a layer of thermal insulation with a reflective film, thermocouples record the heating of the plates in time, according to which the albedo of the active surface of the material is mathematically calculated.

В патенте РФ 2385895 [17] описывается агросадоводческая почвопокровная пленка, включающая слой, отражающий белый свет и содержащий материал, отражающий белый свет, и слой, поглощающий инфракрасное излучение и содержащий наночастицы материала, поглощающего инфракрасное излучение. Материалом, поглощающим инфракрасное излучение, является, по меньшей мере, одни из наночастиц оксида вольфрама и наночастиц сложного оксида вольфрама, которые, в свою очередь, покрыты оксидом, содержащим, по меньшей мере, один элемент, выбранный из Si, Ti, Zr и Al.RF patent 2385895 [17] describes an agro-horticultural ground cover film comprising a layer reflecting white light and containing a material reflecting white light, and a layer absorbing infrared radiation and containing nanoparticles of a material that absorbs infrared radiation. The infrared absorbing material is at least one of the tungsten oxide nanoparticles and the tungsten composite nanoparticles, which, in turn, are coated with an oxide containing at least one element selected from Si, Ti, Zr and Al .

В патенте РФ 2294944 [18] описывается поглощающая инфракрасное излучение поливинилбутиральная композиция, изготовленный из нее слой и содержащее его многослойное стекло. Указанная композиция содержит перерабатываемую в расплаве поливинилбутиральную смолу и диспергированные в указанной поливинилбутиральной смоле гексаборид лантана, и, по меньшей мере, один компонент, выбранный из смешанного оксида индия и олова и смешанного оксида сурьмы и олова. Поливинилбутиральный листовой слой используют для остекления автомобилей и архитектурного остекления, смотрового покрытия и защитного стекла для картин, документов и т.д., также поглощает энергию и предупреждает разрушение.RF patent 2294944 [18] describes an infrared-absorbing polyvinyl butyral composition, a layer made of it, and laminated glass containing it. Said composition comprises a melt-processable polyvinyl butyral resin and lanthanum hexaboride dispersed in said polyvinyl butyral resin, and at least one component selected from mixed indium and tin oxide and mixed antimony and tin oxide. The polyvinyl butyral sheet layer is used for car glazing and architectural glazing, a viewing cover and protective glass for paintings, documents, etc., also absorbs energy and prevents destruction.

В патенте РФ 2325631 [19] описывается способ определения концентрации компонентов в потоке водно-нефтяной смеси. В основе способа определения компонент в водно-нефтяной смеси лежат спектральные зависимости коэффициентов поглощения нефти и воды в ближней инфракрасной области, где для технической реализации способа существуют недорогие и компактные оптические излучатели типа инжекционных полупроводниковых лазеров и мощных светодиодов, а также существуют недорогие, долговечные, быстродействующие фотоприемники - фотодиоды на основе германия и тройных соединений InGaAs.In the patent of the Russian Federation 2325631 [19] describes a method for determining the concentration of components in the flow of a water-oil mixture. The method for determining the components in a water-oil mixture is based on the spectral dependences of the absorption coefficients of oil and water in the near infrared region, where for the technical implementation of the method there are inexpensive and compact optical emitters such as injection semiconductor lasers and high-power LEDs, and there are also inexpensive, durable, high-speed photodetectors - photodiodes based on germanium and InGaAs ternary compounds.

В патенте РФ 2342415 [20] описывается относимое к сфере строительства жидкое керамическое изоляционное покрытие, имеющее способность образования пленки на поверхностях различных форм и материалов, представляющее собой водно-суспензионную композицию, включающую смесь заполненных воздухом полых керамических и кремниевых микросфер, полимерное связующее, содержит фрактальные агрегаты - сильно разрыхленные пористые структуры в виде аэрогеля, вермикулита вспученного и перлита вспученного, загустители и иные дополнительные компоненты, обеспечивающие стабильность термоизолирующего покрытия в эксплуатации.In the patent of the Russian Federation 2342415 [20] describes a liquid ceramic insulating coating related to the field of construction, having the ability to form films on surfaces of various shapes and materials, which is a water-suspension composition comprising a mixture of hollow ceramic and silicon microspheres filled with air, a polymer binder, contains fractal aggregates - highly loosened porous structures in the form of airgel, expanded vermiculite and expanded perlite, thickeners and other additional components, ensuring ivayuschie stability of the insulating coating operation.

В патенте РФ №2206550 [21] приведены сведения об относимом к сфере строительства жидком теплоизоляционном керамическом покрытии, имеющем способность образования пленки, и представляющем собой композицию, включающую равномерно распределенную в ней заполненных воздухом керамических и кремниевых микробусин и углеродистых микроволокон с фибриллами, а также смесь бутадиен-стирольного каучука и акрилового полимера и, по крайней мере, одного пигмента.RF patent No. 2206550 [21] provides information on a liquid heat-insulating ceramic coating related to the construction industry, having a film-forming ability and representing a composition comprising ceramic and silicon microbeads and carbon microfibers with fibrils evenly distributed therein, as well as a mixture styrene butadiene rubber and acrylic polymer and at least one pigment.

Техническим результатом изобретения является повышение прочности покрытия при одновременном повышении теплоизоляционных свойств, удобства пользования и экономичности.The technical result of the invention is to increase the strength of the coating while improving thermal insulation properties, ease of use and economy.

Пленка покрытия после высыхания обладает повышенной прочностью, долговечна и имеет повышенные теплоизоляционные свойства.After drying, the coating film has increased strength, is durable and has improved thermal insulation properties.

В патенте РФ на полезную модель №: 5 3667 [22] описывается высокотемпературное теплоизоляционное покрытие. Техническим результатом предлагаемой полезной модели является расширение ассортимента составов теплозащитных покрытий, повышение теплоизоляционных, теплофизических характеристик покрытия (снижение его теплопроводности, тепловосприятия и теплоотдачи), расширение области рабочих температур от минус 60 до плюс 260°С. Технический результат достигается тем, что теплозащитное покрытие, представляющее собой, по крайней мере, один слой, адгезионно связанный с основой покрываемого материала и состоящий из полимерного связующего, в котором равномерно распределен наполнитель из полых керамических микросфер с заданной дисперсностью, удельной массой, твердостью и распределением частиц микросфер, по размерам распределенных в полимерном связующем составе.In the patent of the Russian Federation for utility model No: 5 3667 [22] describes a high-temperature heat-insulating coating. The technical result of the proposed utility model is to expand the assortment of compositions of thermal protective coatings, increase the thermal insulation, thermal properties of the coating (decrease its thermal conductivity, heat perception and heat transfer), expand the range of operating temperatures from minus 60 to plus 260 ° С. The technical result is achieved by the fact that the heat-shielding coating, which is at least one layer, adhesive bonded to the base of the material to be coated and consisting of a polymer binder, in which the filler is made of hollow ceramic microspheres with a given dispersion, specific gravity, hardness and distribution particles of microspheres distributed by size in a polymer binder composition.

В предлагаемой полезной модели в качестве наполнителя используют полые керамические микросферы из золы уноса ТЭС в заявляемых пределах соотношений и дисперсности. Выбор наполнителя произведен на основе экспериментальных данных, показывающих оптимальное содержание его, достаточное для обеспечения требуемых теплозащитных свойств покрытия и его прочности.In the proposed utility model, hollow ceramic microspheres from fly ash of TPPs are used as filler within the claimed limits of proportions and dispersion. The choice of filler was made on the basis of experimental data showing its optimum content sufficient to provide the required heat-shielding properties of the coating and its strength.

В патенте РФ №2473751 [23] описано теплоизоляционное покрытие, представляющее собой смесь из металлизированных и неметаллизированных керамических микросфер, при этом в качестве связующего вещества используется смесь стирол-акрилового латекса, натриевого жидкого, низкомолекулярного силиконового каучука. Металлизация керамических микросфер выполнена из магнитомягкого металла железа и в процессе нанесения покрытия на них воздействуют магнитные силовые линии, для создания которых на обратной стороне поверхности изделия сложной конфигурации по отношению к стороне, на которую наносится покрытие, имеется стальной сердечник, индукционная обмотка, провода для подвода электрического тока и напряжения.In RF patent No. 2473751 [23] a heat-insulating coating is described, which is a mixture of metallized and non-metallized ceramic microspheres, and a mixture of styrene-acrylic latex, sodium liquid, and low molecular weight silicone rubber is used as a binder. The metallization of ceramic microspheres is made of soft magnetic iron metal and in the process of coating they are affected by magnetic lines of force, to create which on the reverse side of the surface of the product a complex configuration with respect to the side on which the coating is applied, there is a steel core, induction winding, wires for supply electric current and voltage.

В патенте РФ на полезную модель №118654 [24], относимую к области строительства, в частности к слоистым теплоизоляционным изделиям, определено, что покрытие содержит, по крайней мере, один слой, включающий полимерное связующее в виде модифицированного акрилацетатного латекса и полые керамические микросферы, при этом оно дополнительно содержит основу из гибкого материала для нанесения слоев. Гибкий материал выполнен в виде ткани или нетканого полотна. Термоизоляционное покрытие может использоваться при температуре эксплуатации от -60°С до +260°С.In the patent of the Russian Federation for utility model No. 118654 [24], relating to the field of construction, in particular to layered heat-insulating products, it is determined that the coating contains at least one layer comprising a polymer binder in the form of a modified acrylate acetate latex and hollow ceramic microspheres, however, it further comprises a base of flexible material for applying layers. The flexible material is in the form of a fabric or non-woven fabric. Thermal insulation coating can be used at operating temperatures from -60 ° C to + 260 ° C.

Недостатком вышеперечисленных изобретений и промышленных моделей применительно предмета настоящего изобретения определяется следующее:The disadvantage of the above inventions and industrial models with respect to the subject of the present invention is determined by the following:

- материалы по уровню их изготовления являются продуктами высокотехнологичного и ресурсоемкого промышленного производства, что очевидно показывает невозможность их оперативного создания в полевых условиях из доступных и/или подручных компонентов или восстановления поверхностей, обработанных подобными материалами в полевых условиях при наличии обширных повреждений;- materials at the level of their manufacture are products of high-tech and resource-intensive industrial production, which obviously shows the impossibility of their prompt creation in the field of available and / or improvised components or the restoration of surfaces treated with similar materials in the field in the presence of extensive damage;

- материалы не предназначены для использования в динамических условиях, имеют жесткую пленочную структуру, обеспечивающую длительное статическое применение на неподвижных поверхностях, не содержат пластификатора, позволяющего применять их в качестве составной части одежды или изделий на текстильной основе технического назначения, а именно мобильных укрытий (палаток, тентов).- the materials are not intended for use in dynamic conditions, have a rigid film structure that provides long-term static use on fixed surfaces, do not contain a plasticizer that allows them to be used as an integral part of clothing or textile-based products for technical purposes, namely mobile shelters (tents, tents).

- материалы не обладают поглощающими свойствами серых тел, достаточными для обеспечения поглощения внешнего инфракрасного излучения с целью электромагнитного камуфляжа в инфракрасном спектре.- materials do not have the absorbing properties of gray bodies, sufficient to ensure absorption of external infrared radiation with the aim of electromagnetic camouflage in the infrared spectrum.

Техническим результатом заявляемого изобретения является обеспечение электромагнитного камуфляжа объекта за счет состава, наносимого на поверхность текстильной основы изделий, применяемых для маскирования военнослужащих, способных стойко поглощать инфракрасное излучение при внешнем облучении объекта электромагнитными волнами инфракрасного спектра. Технический результат достигается путем способности состава нанесенного на наружную сторону текстильной основы изделий обмундирования военнослужащих.The technical result of the claimed invention is the provision of electromagnetic camouflage of the object due to the composition applied to the surface of the textile base of the products used to mask military personnel capable of absorbing infrared radiation with external irradiation of the object with electromagnetic waves of the infrared spectrum. The technical result is achieved by the ability of the composition applied to the outer side of the textile base of military uniforms.

В целях эффективного камуфлирования военнослужащего за базовое текстильное изделие, обрабатываемое комплексом составов принимается накидка, выполненная в виде плащ-палатки с несъемным капюшоном и лицевой маской, изготовленная промышленным или индивидуальным способом (далее - «накидка»).For the purpose of effective camouflage of a military man, a cloak made in the form of a raincoat with fixed hood and face mask made by an industrial or individual method (hereinafter referred to as “the cloak”) is taken as a basic textile product processed by a complex of compounds.

На поверхность текстильной основы накидки равномерным слоем или фрагментарно (пикселизированно) наносится состав, поглощающий направленное на объект инфракрасное излучение, генерируемое внешними источниками, включающий в себя жидкий углеводород растительного, минерального, полусинтетического или синтетического происхождения технического или пищевого назначения с гомогенно распределенными в нем пигментом «сажа» и выполняющим функцию пластификатора парафином (далее - состав, поглощающий ИКИ).A composition absorbing the infrared radiation directed at the object by external sources, including liquid hydrocarbon of vegetable, mineral, semisynthetic or synthetic origin of technical or food purpose with a pigment homogeneously distributed in it, is applied to the surface of the textile base of the cape evenly or fragmentally (pixelated). soot ”and performing the function of a plasticizer with paraffin (hereinafter referred to as the composition absorbing IKI).

На лицевые маски выполненные в виде мелкоячеистой сетки с целью обеспечения электромагнитного камуфляжа лица поглощающий ИКР! состав наносится на наружную ее поверхность и поверхность головных фиксаторов (при их наличии). За достаточную толщину слоя принимается слой состава до 1 мм. Сетчатая структура подкладочной ткани, обработанной составом поглощающим ИКИ, позволяет сохранить полноценный обзор, одновременно блокировать конвективный теплообмен обусловленный дыханием и механизм теплообмена посредством теплового излучения между поверхностью лица и средой, находящейся за наружной поверхностью сетки.On face masks made in the form of a fine mesh to ensure electromagnetic camouflage of the face, absorbing RBI! the composition is applied to its outer surface and the surface of the head retainers (if any). For a sufficient layer thickness, a composition layer of up to 1 mm is taken. The mesh structure of the lining fabric treated with an absorbing IKI composition allows you to maintain a full view, while blocking convective heat transfer due to respiration and the heat transfer mechanism through thermal radiation between the face surface and the medium located outside the mesh surface.

Состав, поглощающий ИКИ, состоит, по меньшей мере, из одного жидкого углеводорода минерального, полусинтетического или растительного происхождения, обладающего низкой теплопроводностью (интервал λ 0,1-0,13 Вт/Мк [25]) и сохраняющего свои характеристики вязкости в широком диапазоне температур (от +30°С до -15°C), независимо от родового признака, а так же равномерно распределенных в нем пигмента «сажа», по своей поглощающей способности относящегося к категории серых тел с коэффициентом поглощения близким к коэффициенту поглощения абсолютно черного тела [26] и пластификатора в виде парафина, который при сохранении поглощающих свойств состава позволяет перевести без потери основных свойств жидкую форму состава в пластичную гомогенную консистенцию, благодаря которой, состав может наноситься на поверхность текстильного изделия путем наружной промазки. Состав дополнительно увеличивает теплоизоляционные свойства за счет низкой теплопроводности и высокой теплоемкости парафина.The IRI absorbing composition consists of at least one liquid hydrocarbon of mineral, semisynthetic, or vegetable origin, having low thermal conductivity (range λ 0.1-0.13 W / Mk [25]) and retaining its viscosity characteristics in a wide range temperatures (from + 30 ° C to -15 ° C), regardless of the generic characteristic, as well as the soot pigment evenly distributed in it, in terms of its absorption capacity belonging to the category of gray bodies with an absorption coefficient close to the absorption coefficient of absolutely black about the body [26] and a plasticizer in the form of paraffin, which, while maintaining the absorbing properties of the composition, allows the liquid form of the composition to be transferred without loss of basic properties to a plastic homogeneous consistency, due to which the composition can be applied to the surface of a textile product by external lubrication. The composition further increases the thermal insulation properties due to the low thermal conductivity and high heat capacity of paraffin.

Согласно изобретению в качестве жидкого углеводорода используются:According to the invention, the following are used as liquid hydrocarbon:

- или жидкие минеральные, полусинтетические, синтетические углеводороды технического назначения в виде всесезонного моторного масла,- or liquid mineral, semi-synthetic, synthetic technical hydrocarbons in the form of multigrade engine oil,

- или жидкие углеводороды растительного происхождения пищевого назначения в виде пищевого растительные масла,- or liquid hydrocarbons of vegetable origin for food purposes in the form of edible vegetable oils,

- или сочетание указанных выше жидких углеводородов в произвольном соотношении в количестве - 90-91% (здесь и далее при указании процентов понимаются объемные %);- or a combination of the above liquid hydrocarbons in an arbitrary ratio in the amount of 90-91% (hereinafter, when percent is indicated, volume% is understood);

- пигмент «сажа», в виде монохромного, черного, магнитного или немагнитного механического тонера или в виде сажи в нативном состоянии или в произвольно взятом соотношении указанных выше веществ в количестве - 3-4%.- the pigment "soot", in the form of monochrome, black, magnetic or non-magnetic mechanical toner or in the form of soot in the native state or in an arbitrary ratio of the above substances in an amount of 3-4%.

- парафин - 5-6%- paraffin - 5-6%

Пигмент «сажа» и парафин равномерно распределены в среде указанных выше жидких углеводородов путем механического перемешивания при нагреве состава на водяной бане до температуры достаточной для расплавления парафина в жидких углеводородах с последующим охлаждением полученного гомогенного состава до пластифицированного состояния в условиях комнатной температуры.The soot pigment and paraffin are evenly distributed in the medium of the above liquid hydrocarbons by mechanical stirring while heating the composition in a water bath to a temperature sufficient to melt the paraffin in liquid hydrocarbons, followed by cooling the resulting homogeneous composition to a plasticized state at room temperature.

Состав обладает хорошими адгезивными свойствами. Достаточная толщина слоя до 1 мм. Состав наносится на ткань методом промазывания или фрагментарного (по пиксельному типу) промакивания.The composition has good adhesive properties. Sufficient layer thickness up to 1 mm. The composition is applied to the fabric by smearing or fragmentary (pixel type) blotting.

Техническим результатом от применения состава, поглощающего ИКИ, является обеспечение электромагнитного камуфляжа объекта за счет обработки внешней поверхности текстильной основы составом, способным поглощать внешнее инфракрасное излучение. Технический результат достигается путем потенцирования способности компонентов состава поглощать инфракрасное излучение.The technical result from the use of a composition absorbing IKI is the provision of electromagnetic camouflage of an object by treating the outer surface of the textile base with a composition capable of absorbing external infrared radiation. The technical result is achieved by potentiating the ability of the components of the composition to absorb infrared radiation.

Для случаев индивидуального пошива накидок, на которые наносится комплекс составов, представляется целесообразным использовать льняные ленточные пакли - утеплители, текстильная основа которых выступает в качестве элемента каркаса за счет высокой степени устойчивости к разрыву и низкой теплопроводности. Ее показатель удельной разрывной нагрузки для волокна - 54-72 сН/текс (для сравнения, хлопковое волокно - 19-36 сН/текс) [27], обусловлен высокой степенью полимеризации волокон целлюлозы образующих полимеры (25000-30000, для сравнения - аналогичный показатель для хлопкового волокна - 5000-6000), а коэффициент теплопроводности льняного утеплителя 0,034-0,04 Вт/(м⋅∈С) [28].For cases of individual tailoring of wraps, on which a complex of compositions is applied, it seems appropriate to use linen tape tows - heaters, the textile base of which acts as an element of the frame due to the high degree of resistance to tearing and low thermal conductivity. Its specific breaking load for fiber is 54-72 cN / tex (for comparison, cotton fiber is 19-36 cN / tex) [27], due to the high degree of polymerization of cellulose fibers forming polymers (25000-30000, for comparison - a similar indicator for cotton fiber - 5000-6000), and the coefficient of thermal conductivity of flax insulation is 0.034-0.04 W / (m⋅∈C) [28].

Общий вид текстильной основы в режиме индивидуального пошива накидки с нанесенным на нее поглощающим ИКИ составом приведен на фотографиях 1 и 2 (Фот.1, 2, соответственно).A general view of the textile base in the mode of individual sewing of the cape with the absorbing IKI composition applied to it is shown in photographs 1 and 2 (Photo 1, 2, respectively).

Как уже было сказано выше электромагнитный камуфляж лица обеспечивается за счет маски, выполненной их синтетической мелкоячеистой подкладочной ткани, наружная поверхность которой обрабатывается заявленным в изобретении составом методом промазывания или промакивания с толщиной его слоя до 1 мм.As already mentioned above, electromagnetic face camouflage is provided by a mask made of their synthetic fine-mesh lining fabric, the outer surface of which is treated with the claimed composition by the method of smearing or blotting with a layer thickness of up to 1 mm.

Обработанная комплексом составов маска в случае пошива накидки индивидуальным способом, закрепляется на регулируемом головном креплении. Мелкоячеистая структура подкладочной ткани, обработанной составом, позволяет сохранить полноценный обзор.The mask processed by the complex of compounds in case of tailoring the cape in an individual way is fixed on an adjustable head mount. The fine-meshed structure of the lining fabric treated with the composition allows you to maintain a full view.

Аналогичная обработка проводится и с поверхностью головного крепления маски. Размер ткани должен быть достаточным для полного покрытия лица, шеи и грудной клетки на уровне границы верхней и средней третей грудины. Общий вид маски, выполненной индивидуальным способом, обработанной составом, представлен на фотографиях 3 и 4 (Фот. 3, 4, соответственно).Similar processing is carried out with the surface of the head mount of the mask. The size of the tissue should be sufficient to completely cover the face, neck and chest at the level of the border of the upper and middle third of the sternum. A general view of the mask, made in an individual way, processed by the composition, is presented in photographs 3 and 4 (Phot. 3, 4, respectively).

Поглощающий ИКИ состав имеет прикладную многовариантную технологию изготовления, легко реализуемую в полевых условиях, низкие производственные издержки, применим в широком температурном диапазоне. Исходя из заявленных свойств вытекают определенные недостатки комплекса: непроницаемость для водяных паров, субъективный дискомфорт от контакта с маслянистой поверхностью.The IKI absorbing composition has an applied multivariate manufacturing technology that is easily implemented in the field, low production costs, and is applicable in a wide temperature range. Based on the declared properties, certain disadvantages of the complex follow: impermeability to water vapor, subjective discomfort from contact with an oily surface.

Для испытания свойств состава применялась комбинированная система ночного видения, а именно монокуляр ночного видения YukonNV Exelon 4×50 (24102), с фотокамерой Samsung ES28, с помощью которой велась видеосъемка изображения, полученного посредством указанного монокуляра ночного видения.To test the properties of the composition, a combined night vision system was used, namely, the YukonNV Exelon 4 × 50 (24102) night vision monocular with the Samsung ES28 camera, with which video was captured using the image obtained using the specified night vision monocular.

Исследовались:Researched:

- поглощающие ИКИ свойства объекта (человек) экипированного в плащ-палатку с лицевой маской, на поверхность которой был нанесен заявленный состав (далее - объект «Камуфляж»)- IKI-absorbing properties of an object (person) equipped in a raincoat with a face mask on the surface of which the claimed composition was applied (hereinafter - the Camouflage object)

- поглощающие ИКИ свойства объекта (человека), экипированного в стандартное обмундирование - костюм «Горка» и лицевую маску (далее - объект «Контроль»);- IKI-absorbing properties of an object (person) equipped in standard uniforms - a Gorka suit and a face mask (hereinafter referred to as the “Control” object);

- поглощающие ИКИ свойства окружающего фона.- IR absorbing properties of the surrounding background.

За базовый фон внешней среды, определяющий эффективность заявленного в изобретении комплекса, был принят фон, создаваемый плотными зарослями лиственного кустарника и лиственных деревьев, отражающие ИКИ свойства которых индицировались посредством монокуляра ночного видения параллельно с данными, получаемыми от объектов заявленного в изобретении состава.The background created by the dense thickets of deciduous shrubs and deciduous trees, reflecting the IRI properties of which were indicated by the night vision monocular in parallel with the data obtained from the objects of the composition claimed in the invention, was taken as the basic environmental background that determines the effectiveness of the complex claimed in the invention.

С целью определения свойств состава, заявленного в изобретении, была выбрана совокупность природных факторов, имеющих заведомо четкие отражающие ИКИ контрасты. Наблюдение велось в ночное время суток на открытом пространстве на песчаном пляже, расположенном на берегу водоема, окаймленном плотными зарослями лиственного кустарника и лиственных деревьев.In order to determine the properties of the composition claimed in the invention, a combination of natural factors having obviously clear contrasting IRI contrasts was chosen. Observation was carried out at night in open space on a sandy beach located on the shore of a reservoir bordered by dense thickets of deciduous shrubs and deciduous trees.

Метеоусловия при проведении наблюдения: Температура +14С*, ветер западный 2 м/сек. Ясно, полная луна. Полнолуние в ясную погоду позволяло достичь максимально возможной внешней подсветки заявленного в изобретении состава сочетанным светом астрономических тел и активной подсветки ПНВ с целью исследования его поглощающих инфракрасное излучение свойств в темное время суток в условиях наличия существенных демаскирующих исследуемый объект факторов.Weather conditions during observation: Temperature + 14C *, west wind 2 m / s. Clear, full moon. The full moon in clear weather made it possible to achieve the maximum possible external illumination of the composition claimed in the invention by the combined light of astronomical bodies and active NVD illumination in order to study its properties absorbing infrared radiation in the dark during the presence of significant factors unmasking the object under study.

Съемка данных с ПНВ осуществлялась через каждых 5 метров до достижения наблюдаемыми объектами 50 метров удаления от оператора, осуществляющего съемку. Такой же режим съемки сохранялся при обратном движении объектов наблюдения.The data were collected from the NVD every 5 meters until the observed objects reached 50 meters of distance from the operator performing the survey. The same shooting mode was maintained during the reverse movement of objects of observation.

Как уже было сказано выше одновременно и параллельно двигались два объекта наблюдения, один из которых был экипирован в накидку по типу плащ-палатки, обработанной заявленным в изобретении составом, объект Камуфляж, а другой - объект Контроль, обмундирован в костюм «Горка» и лицевую маску, выполненные из 100% хлопчатобумажного текстиля.As it was said above, two objects of observation simultaneously and simultaneously moved, one of which was equipped with a cloak like a cloak-tent, processed by the composition claimed in the invention, the Camouflage object, and the other - the Control object, was dressed in a Gorka suit and a face mask made from 100% cotton textile.

При наблюдении в ПНВ с активной подсветкой объект Камуфляж на расстоянии 15-20 метров от оператора приобрел достоверный визуальный камуфлирующий эффект, а с 25-30 метров стал практически невидим, в тоже время объект Контроль перестал достоверно идентифицироваться на расстоянии 40 и свыше метров.When observing in NVD with active illumination, the Camouflage object at a distance of 15-20 meters from the operator acquired a reliable visual camouflage effect, and from 25-30 meters became practically invisible, at the same time, the Control object ceased to be reliably identified at a distance of 40 meters or more.

Привязка расстояния между исследуемыми объектами Камуфляж, Контроль и оператором осуществлялась посредством радиосвязи.The distance between the studied objects Camouflage, Control and the operator was carried out by means of radio communication.

Элемент «лицевая маска», обработанный составом, поглощающим ИКИ, обеспечил надлежащую маскировку лица человека, позволил существенно деформировать силуэтные очертания верхней половины наблюдаемого объекта, что наглядно определяется на видеоизображении возврата объекта Камуфляж к оператору.The “face mask” element, processed by the IR absorbing compound, ensured proper camouflage of the person’s face, allowed to significantly deform the silhouette outline of the upper half of the observed object, which is visually determined on the video image of the Camouflage returning to the operator.

Данные исследования подтверждают, что заявляемый в изобретении состав обладает поглощающими, изолирующими и отражающими инфракрасное излучение свойствами.These studies confirm that the composition claimed in the invention has absorbing, insulating and reflecting infrared radiation properties.

Многообразие примеров, основанных на отличиях построения структуры заявленного в изобретении состава, обусловленной потенциалом количественной и качественной многовариантности жидких углеводородов пищевого или технического назначения минерального, полусинтетического, синтетического или растительного происхождения, обладающих низкой теплопроводностью и сохраняющих свои характеристики вязкости независимо от родового признака в широком диапазоне температур, которые могут быть использованы в заявляемом изобретении приводиться не будет в связи с их практической неограниченностью.A variety of examples based on differences in the structure of the composition claimed in the invention, due to the potential of quantitative and qualitative multivariance of liquid hydrocarbons of food or technical purpose of mineral, semi-synthetic, synthetic or plant origin, having low thermal conductivity and retaining their viscosity characteristics regardless of the generic characteristic in a wide temperature range that can be used in the claimed invention are given on It is due to their almost unlimited.

Краткое описание фотографий.A brief description of the photos.

А. Обзорные фотографии накидки и маски, выполненных способом индивидуального пошива, обработанных составом.A. Overview photographs of cloaks and masks made by individual tailoring, processed by the composition.

Фиг. 1 - Накидка, обработанная составом. Вид спереди.FIG. 1 - Cape treated with the composition. Front view.

Фиг. 2 - Накидка, обработанная составом. Вид слева.FIG. 2 - Cape treated with the composition. Left view.

Фиг. 3 - Маска, обработанная составом. Вид спереди-слева.FIG. 3 - Mask treated with the composition. Front-left view.

Фиг. 4 - Маска, обработанная составом. Вид сзади-слева.FIG. 4 - Mask treated with the composition. Rear view, left.

Библиография.Bibliography.

1. Криксунов Л.З. Приборы ночного видения Киев: «Техника» 1975 г., стр. 216, табл. 9, илл. 117, библ. 138 http://www.twirpx.com/file/17055211. Kriksunov L.Z. Night vision devices Kiev: “Technique” 1975, p. 216, table. 9, ill. 117, bibl. 138 http://www.twirpx.com/file/1705521

2. Пат. US 5281460: http://www.archpatent.com/patents/5281460/, МПК F41H 3/02. Опубл. 25.01.1994;2. Pat. US 5281460: http://www.archpatent.com/patents/5281460/, IPC F41H 3/02. Publ. 01/25/1994;

3. Пат. US 4495239: http://www.archpatent.com/patents/4495239?cds=8/МПК F41H 3/02. Опубл. 22.01.1985;3. Pat. US 4495239: http://www.archpatent.com/patents/4495239?cds=8/ IPC F41H 3/02. Publ. 01/22/1985;

4. Пат. US 4659602: http://www.***.ru/patents/US 4659602 МПК F41H 3/02. Опубл. 21.04.19874. Pat. US 4659602: http://www.***.com/patents/US 4659602 IPC F41H 3/02. Publ. 04/21/1987

5. Пат. US 4621012: http://www.***.ru/patents/US 4621012 МПК F41H 3/02. Опубл. 04.11.19865. Pat. US 4621012: http://www.***.com/patents/US 4621012 IPC F41H 3/02. Publ. 11/04/1986

6. Пат. US 4064305: http://www.***.ru/patents/US 4064305?dq=US+4064305&hl=ru&sa=X&ei=8o2HUaObA8am4gSknIDYDg&ved=0CDcQ6wEwAA МПК F41H 3/00 Опубл. 20.12.1977.6. Pat. US 4064305: http://www.***.com/patents/US 4064305? Dq = US + 4064305 & hl = ru & sa = X & ei = 8o2HUaObA8am4gSknIDYDg & ved = 0CDcQ6wEwAA IPC F41H 3/00 Publ. 12/20/1977.

7. Пат. US 4529633: https://docs.***.com/viewer?url=www.***.com/patents/US 4529633.pdf МПК F41H 3/00. Опубл. 16.07.19857. Pat. US 4529633: https://docs.***.com/viewer?url=www.***.com/patents/US 4529633.pdf IPC F41H 3/00. Publ. 07/16/1985

8. Пат. US 4533591: http://www.***.ru/patents/WO 1996032252A1?cl=en&dq=US+4533591&hl=ru&sa=Х&ei=PZCHUYTCKOjP4QSFqIDIBg&ved=0CDwQ6AEwAQ МПК F41H 3/00 Опубл. 17.10.1996.8. Pat. US 4533591: http://www.***.com/patents/WO 1996032252A1? Cl = en & dq = US + 4533591 & hl = ru & sa = X & ei = PZCHUYTCKOjP4QSFqIDIBg & ved = 0CDwQ6AEwAQ IPC F41H 3/00 Publ. 10/17/1996.

9. Пат. US 4467005: http://ww.***.ru/patents/US 4467005?pg=PAl&dq=US+4467005&hl=ru&sa=X&ei=BJKHUZHQO4LJ4ATHnIHoDQ&sqi=2&pjf=1&ved=0CDwQ6AEwAg МПК D06Q 1/04 Опубл. 21.08.84.9. Pat. US 4467005: http://ww.***.com/patents/US 4467005? Pg = PAl & dq = US + 4467005 & hl = ru & sa = X & ei = BJKHUZHQO4LJ4ATHnIHoDQ & sqi = 2 & pjf = 1 & ved = 0CDwQ6AE06A04 Mp. 08.21.84.

10. Пат. US 97118428/12 (Пат. РФ 2127194): http://www.freepatent.ru/patents/2127194 МПК В32В 5/00 Опубл. 10.03.199910. Pat. US 97118428/12 (Pat. RF 2127194): http://www.freepatent.ru/patents/2127194 IPC В32В 5/00 Publ. 03/10/1999

11. Пат. РФ 2403328: http://www.freepatent.ru/patents/2403328 МПК D03D 11/00 Опубл. 10.11.2010.11. Pat. RF 2403328: http://www.freepatent.ru/patents/2403328 IPC D03D 11/00 Publ. 11/10/2010.

12. Разработка технологии производства экранирующих швейных изделий: http://tekhnosfera.com/razrabotka-tehnologii-proizvodstva-ekraniruyuschih-shveynyh-izdeliy. Автореферат диссертации по технологии материалов и изделия текстильной и легкой промышленности, 05.19.04, диссертация на тему Разработка технологии производства экранирующих швейных изделий. ИТГА. Иваново-200712. Development of the technology for the production of shielding garments: http://tekhnosfera.com/razrabotka-tehnologii-proizvodstva-ekraniruyuschih-shveynyh-izdeliy. Abstract of the dissertation on the technology of materials and products of the textile and light industry, 05.19.04, the dissertation on the theme: Development of the production technology of shielding garments. ITGA. Ivanovo-2007

13. Собственно диссертация: «Разработка технологии производства экранирующих швейных изделий» савторефератом: http://yadi.sk/d/JxRZiYpiKAy8U13. Actually the dissertation: “Development of the technology for the production of shielding garments”, abstract: http://yadi.sk/d/JxRZiYpiKAy8U

14. Пат. РФ 2197041: http://www.findpatent.ru/patent/219/2197041.html МПК H01Q17/00 Опубл. 20.01.2003.14. Pat. RF 2197041: http://www.findpatent.ru/patent/219/2197041.html IPC H01Q17 / 00 Publ. 01/20/2003.

15. Пат. РФ 2343547: http://www.findpatent.ru/patent/234/2343547.html МПК G07D 7/06 (2006.01)В82В 3/00 (2006.01) Опубл. 27.04.2007.15. Pat. RF 2343547: http://www.findpatent.ru/patent/234/2343547.html IPC G07D 7/06 (2006.01) B82B 3/00 (2006.01) Publ. 04/27/2007.

16. Пат. РФ 2456558: http://www.freepatent.ru/images/patents/5/2456558/patent-2456558.pdf МПК G01J 5/12. (2006.01) Опубл.20.07.201216. Pat. RF 2456558: http://www.freepatent.ru/images/patents/5/2456558/patent-2456558.pdf IPC G01J 5/12. (2006.01) Publish. 20.07.2012

17. Пат. РФ 2385895: http://bd.patent.su/2385000-2385999/pat/servl/servlet30be.html МПК С09К 9/00 (2006.01) Опубл. 10.04.201017. Pat. RF 2385895: http://bd.patent.su/2385000-2385999/pat/servl/servlet30be.html IPC S09K 9/00 (2006.01) Publ. 04/10/2010

18. Пат. РФ 2294944: http://bd.patent.su/2294000-2294999/pat/servl/servletd47b.html МПК C08L 29/14 (2006.01) С08К 3/38 (2006.01) В32В 17/10 (2006.01) Опубл. 10.03.2007.18. Pat. RF 2294944: http://bd.patent.su/2294000-2294999/pat/servl/servletd47b.html IPC C08L 29/14 (2006.01) С08К 3/38 (2006.01) В32В 17/10 (2006.01) Publ. 03/10/2007.

19. Пат. РФ 2325631: http://www.findpatent.ru/patent/232/2325631.html МПК G01N 21/35 (2006.01) Опубл. 14.12.2006.19. Pat. RF 2325631: http://www.findpatent.ru/patent/232/2325631.html IPC G01N 21/35 (2006.01) Publ. 12/14/2006.

20. Пат. РФ 2342415:http://www.freepatent.ru/patents/2342415 МПК C09D 183/00, C09D 5/02 Опубл. 27.12.200820. Pat. RF 2342415: http: //www.freepatent.ru/patents/2342415 IPC C09D 183/00, C09D 5/02 Publ. 12/27/2008

21. Пат. РФ 2206550: http://www.findpatent.ru/patent/220/2206550.html МПК E04B 1/76, C09D 109, C04B 41/48 Опубл. 20.06.200321. Pat. RF 2206550: http://www.findpatent.ru/patent/220/2206550.html IPC E04B 1/76, C09D 109, C04B 41/48 Publ. 06/20/2003

22. Пат. РФ на полезную модель 53667: http://bankpatentov.ru/node/456850 МПК: С04В Опубл: 27.05.200622. Pat. RF on utility model 53667: http://bankpatentov.ru/node/456850 IPC: С04В Publisher: 05/27/2006

23. Пат. РФ 2473751: http://www.findpatent.ru/patent/247/2473751.html МПК Е04В 1/74, C09D 5/02 Опубл. 27.01.201323. Pat. RF 2473751: http://www.findpatent.ru/patent/247/2473751.html IPC Е04В 1/74, C09D 5/02 Publ. 01/27/2013

24. Пат. РФ 118654 на полезную модель: http.//poleznayamodel.ru/model/11/118654.html МПК: Е04В 1/7624. Pat. RF 118654 for utility model: http.//poleznayamodel.ru/model/11/118654.html IPC: Е04В 1/76

25. Бухмиров В.В., Ракутина Д.В., Солнышкова Ю.С. Справочные материалы для решения задач по курсу «Теплообъемнообмен» стр. 54 таб. 1.63. / ГОУ ВПО «Ивановский государственный энергетический университет имени В.И. Ленина». Иваново, 2009. http://ispu.ru/files/u2/Spravochnye_materialy_ТМО_104_v1.pdf25. Bukhmirov V.V., Rakutina D.V., Solnyshkova Yu.S. Reference materials for solving problems on the course “Heat and Volume Exchange” p. 54 tab. 1.63. / GOU VPO "Ivanovo State Power Engineering University named after V.I. Lenin. " Ivanovo, 2009. http://ispu.ru/files/u2/Spravochnye_materialy_ТМО_104_v1.pdf

26. С.Я. Задера, П.П. Першенков «Волновая и квантовая оптика» Конспект лекций по курсу общей физики. Стр. 76-8126. S.Ya. Zadera, P.P. Pershenkov “Wave and quantum optics” Lecture notes on the course of general physics. Page 76-81

Государственное образовательное учреждение высшего профессионального образования «Пензенский государственный университет» Пенза 2006 http://window.edu.ru/resource/857/36857/files/stup083.pdfPenza State University State Educational Institution of Higher Professional Education Penza 2006 http://window.edu.ru/resource/857/36857/files/stup083.pdf

27. И.А. Шеромова «Текстильные материалы: получение, строение, свойства». Учебное пособие. Рекомендовано Дальневосточным региональным учебно-методическим центром (ДВ РУМЦ) в качестве учебного пособия для студентов специальностей 260901 «Технология швейных изделий», 260902 «Конструирование швейных изделий», 071501 «Художественное проектирование костюма», 070601 «Дизайн» стр. 12, 19.27. I.A. Sheromova "Textile materials: production, structure, properties." Tutorial. Recommended by the Far Eastern Regional Educational and Methodological Center (DV RMTS) as a textbook for students of specialties 260901 "Technology of garments", 260902 "Design of garments", 071501 "Artistic design of a costume", 070601 "Design" p. 12, 19.

28. Теплопроводность пакли. http://remstd.ru/archives/mezhventsovyie-utepliteli-uplotniteli-dlya-derevyannyih-domov-kakoy-luchshe/28. Thermal conductivity tow. http://remstd.ru/archives/mezhventsovyie-utepliteli-uplotniteli-dlya-derevyannyih-domov-kakoy-luchshe/

Claims (6)

Состав, поглощающий инфракрасное излучение, для нанесения на поверхность текстильных изделий, состоящий из следующих компонентов (в объемных %):Composition that absorbs infrared radiation, for applying to the surface of textile products, consisting of the following components (in volume%): - или жидкие минеральные, полусинтетические, синтетические углеводороды технического назначения в виде всесезонного моторного масла,- or liquid mineral, semi-synthetic, synthetic technical hydrocarbons in the form of multigrade engine oil, - или жидкие углеводороды растительного происхождения пищевого назначения в виде пищевого растительного масла,- or liquid vegetable hydrocarbons of edible purpose in the form of edible vegetable oil, - или сочетание указанных выше жидких углеводородов в произвольном соотношении в количестве - 90-91%;- or a combination of the above liquid hydrocarbons in an arbitrary ratio in an amount of 90-91%; - пигмент «сажа», в виде монохромного, черного, магнитного или немагнитного механического тонера или в виде сажи в нативном состоянии или в произвольно взятом соотношении указанных выше веществ в количестве - 3-4%;- the soot pigment, in the form of monochrome, black, magnetic or non-magnetic mechanical toner, or in the form of soot in the native state or in an arbitrary ratio of the above substances in an amount of 3-4%; - парафин - 5-6%.- paraffin - 5-6%.