RU2505845C2

RU2505845C2 - Method of making lenses for dental glasses

Info

Publication number: RU2505845C2
Application number: RU2012100816/28A
Authority: RU
Inventors: Тагир Абдурашидович Исмаилов; Айшат Расуловна Шахмаева; Патимат Расуловна Захарова
Priority date: 2012-01-11
Filing date: 2012-01-11
Publication date: 2014-01-27
Also published as: RU2012100816A

Abstract

FIELD: physics.

SUBSTANCE: method involves layer-by-layer sputtering of metals on lenses. Successive magnetron sputtering of Ti and Cu metal is carried without temperature action, wherein composition of said metals enables to obtain an effect of colour change under the action of UV radiation from transparent to orange in order to protect the eyeball from burns.

EFFECT: combining the functions of protection from mechanical damages and UV radiation during treatment, which increases efficiency of the dentist.

1 dwg

Description

Изобретение относится к медицинской технике. В настоящий момент при лечении пациента в стоматологии используются два вида пластиковых очков: медицинские прозрачные стоматологические очки, служащие для защиты глазного яблока от механических и химических повреждений, и стоматологические очки с оранжевым покрытием для предотвращения от ожогов при попадании ультрафиолетовых лучей во время использования гелиевой лампы в процессе пломбирования зуба. И тот, и другой вид стоматологических очков широко распространены на рынке стоматологической техники (фирмы «» - Китай, фирма «» - Украина).The invention relates to medical equipment. Currently, two types of plastic glasses are used in the treatment of a patient in dentistry: medical transparent dental glasses, which protect the eyeball from mechanical and chemical damage, and orange-coated dental glasses to prevent burns from ultraviolet rays when using a helium lamp in tooth filling process. Both types of dental glasses are widely distributed in the market of dental equipment (firms "" - China, firms "" - Ukraine).

Недостатком при лечении в стоматологии является дискомфорт, связанный со сменой одного вида очков на другой при работе с одним и тем же пациентом во время лечения.A disadvantage in treatment in dentistry is the discomfort associated with the change of one type of glasses to another when working with the same patient during treatment.

Целью изобретения является получение такого вида стоматологических очков, объединяющего функции защиты от механических повреждений и от ультрафиолетовых излучений во время лечения, позволяющего повысить производительность врача-стоматолога.The aim of the invention is to obtain this type of dental glasses, combining the functions of protection against mechanical damage and ultraviolet radiation during treatment, which improves the performance of the dentist.

Поставленная цель достигается заменой пластиковых линз на линзы из стекла с напыленным защитным покрытием, обеспечивающим одновременную защиту от механических и ультрафиолетовых воздействий. Эффект напыления защитного покрытия дает оранжевый цвет при попадании ультрафиолетовых лучей, тем самым защищая глазное яблоко от ожога. Сущность способа заключается в том, что на поверхности стекла формируется 2-слойная металлизация методом магнетронного напыления определенной толщины (Фиг.1). Напыление проводится на установке магнетронного напыления «Leybold-Z600» при комнатной температуре при следующих режимах: первый слой металла - титан (Ti), время напыления - 5 мин, толщина напыленного слоя равна 30±2 нм; второй слой металла - медь (Сu), время напыления 3 мин и толщина 75±5 нм.The goal is achieved by replacing plastic lenses with glass lenses with a sprayed protective coating, which provides simultaneous protection against mechanical and ultraviolet influences. The effect of spraying a protective coating gives an orange color when exposed to ultraviolet rays, thereby protecting the eyeball from burns. The essence of the method lies in the fact that on the surface of the glass a 2-layer metallization is formed by the method of magnetron sputtering of a certain thickness (Figure 1). Spraying is carried out on a Leybold-Z600 magnetron sputtering device at room temperature under the following conditions: the first metal layer is titanium (Ti), the sputtering time is 5 minutes, the thickness of the deposited layer is 30 ± 2 nm; the second layer of metal is copper (Cu), the deposition time is 3 min and the thickness is 75 ± 5 nm.

Предлагаемый способ позволяет получить защитный слой линзы, который способен отразить ультрафиолетовый свет, тем самым защищая глазное яблоко от ожога.The proposed method allows to obtain a protective layer of the lens, which is able to reflect ultraviolet light, thereby protecting the eyeball from burns.

Сущность изобретения подтверждается следующими примерами.The invention is confirmed by the following examples.

Пример 1. Процесс проводят на установке магнетронного распыления в среде аргона с расходом 150 л/ч. Первый слой металла - титан (Ti), время напыления 10 мин, толщина напыления 67 нм; второй слой металла - медь (Сu), время напыления 5 мин, толщина напыления 120 нм.Example 1. The process is carried out on the installation of magnetron sputtering in an argon medium with a flow rate of 150 l / h The first metal layer is titanium (Ti), spraying time 10 min, spraying thickness 67 nm; the second layer of metal is copper (Cu), the deposition time is 5 min, and the deposition thickness is 120 nm.

Пример 2. Процесс проводят на установке магнетронного распыления в среде аргона с расходом 150 л/ч. Первый слой металла - титан (Ti), время напыления 5 мин, толщина напыления 30 нм; второй слой металла - медь (Сu), время напыления 3 мин, толщина напыления 75 нм.Example 2. The process is carried out on the installation of magnetron sputtering in an argon medium with a flow rate of 150 l / h The first metal layer is titanium (Ti), the deposition time is 5 min, the deposition thickness is 30 nm; the second layer of metal is copper (Cu), the deposition time is 3 min, and the deposition thickness is 75 nm.

Пример 3. Процесс проводят на установке магнетронного распыления в среде аргона с расходом 150 л/ч. Первый слой металла - титан (Ti), время напыления 3 мин, толщина напыления 20 нм; второй слой металла - медь (Сu), время напыления 2 мин, толщина напыления 50 нм. ЛитератураExample 3. The process is carried out on the installation of magnetron sputtering in an argon medium with a flow rate of 150 l / h The first metal layer is titanium (Ti), sputtering time 3 min, sputtering thickness 20 nm; the second metal layer is copper (Cu), the deposition time is 2 min, and the deposition thickness is 50 nm. Literature

1. http://www.hivcc.com1.http: //www.hivcc.com

2. http://www.mirou.ua2. http://www.mirou.ua

Claims

Способ изготовления линз для стоматологических очков, включающий послойное напыление на линзы металлов, отличающийся тем, что проводят последовательное магнетронное напыление металлов Ti и Сu без температурного воздействия, композиция которых позволяет получить эффект изменения цвета под ультрафиолетовым излучением от прозрачного до оранжевого для защиты глазного яблока от ожога. A method of manufacturing lenses for dental glasses, including layer-by-layer spraying on metal lenses, characterized in that they conduct sequential magnetron sputtering of Ti and Cu metals without temperature exposure, the composition of which allows to obtain the effect of color change under ultraviolet radiation from transparent to orange to protect the eyeball from burns .