RU2481956C2 - Rubber-cord composite - Google Patents

Abstract

FIELD: chemistry.

SUBSTANCE: invention relates to rubber-cord composites and can be used in the tyre and industrial rubber industry. The rubber-cord composite consists of a layer of textile cord which is saturated with a latex-resorcinol-formaldehyde composition based on latex DBA-1 - a copolymer of butadiene, butyl acrylate, methacrylic acid amide or based on latex with vinyl pyridine links, optionally with another latex and optionally containing blocked E-caprolactam polyisocyanate, and a rubber layer. The rubber layer is made from a composition based on unsaturated rubber, with the following ratio of components of the rubber layer, pts.wt: unsaturated rubber - 100; ground technical sulphur - 0.5-0.8; polymeric sulphur - 1.0-1.5; sulphamide TS 0.2-0.4; altax - 0.4-0.7; technical carbon N 550 - 50-55; stearic acid - 1-2; oil-softener - 7-16; resin Pikar - 0.5-2.0; diaphene FP-1-2.5; pine rosin -1-3; zinc oxide - 5-6; modifier RU-D - 1-4 or resin modifier R-17-34 -0.8-1.5; white soot - 5-10; kaolin KR-1- 1-4.

EFFECT: invention increases strength of the textile cord-rubber bond.

2 tbl, 12 ex

Description

Изобретение относится к резинокордным композитам и может быть использовано в шинной и резинотехнической промышленности.The invention relates to rubber-cord composites and can be used in the tire and rubber industry.

Известен резинокордный композит (патент 2305037RU, МПК В32В 25/10, опубл. 27.08.07, Бюл. №24), состоящий из слоя текстильного корда, слоя адгезива, включающего латекс ДБА-1, и резинового слоя, включающего ненасыщенный каучук, технический углерод П-245, модификатор РУ-Д и белую сажу или модификатор РУ-Д и гексахлорпараксилол.Known rubber-cord composite (patent 2305037RU, IPC B32V 25/10, publ. 08/27/07, Bull. No. 24), consisting of a layer of textile cord, a layer of adhesive, including DBA-1 latex, and a rubber layer, including unsaturated rubber, carbon black P-245, RU-D modifier and white soot or RU-D modifier and hexachloroparaxylene.

Недостатком известного технического решения является недостаточно высокая прочность связи в резинокордном композите со слоем анидного текстильного корда.A disadvantage of the known technical solution is the insufficiently high bond strength in the rubber-cord composite with a layer of anide textile cord.

Наиболее близким к предлагаемому техническому решению является резинокордный композит (патент 2021148 RU, МПК В32В 25/10, опубл. 15.10.94, Бюл. №19), состоящий из слоя текстильного корда, слоя адгезива, включающего латекс со звеньями винилпиридина, и резинового слоя, включающего ненасыщенный каучук, гексахлорпараксилол, дифенилгуанидин или алкилфеноламинную смолу.Closest to the proposed technical solution is a rubber-cord composite (patent 2021148 RU, IPC B32V 25/10, publ. 10/15/94, Bull. No. 19), consisting of a layer of textile cord, an adhesive layer including latex with vinyl pyridine links, and a rubber layer including unsaturated rubber, hexachloroparaxylene, diphenylguanidine or alkylphenolamine resin.

Недостатком известного технического решения (прототипа) также является недостаточный уровень прочности связи в резинокордном композите, в состав которого входит текстильный анидный корд.A disadvantage of the known technical solution (prototype) is also an insufficient level of bond strength in the rubber-cord composite, which includes textile anide cord.

Техническим результатом предлагаемого технического решения является повышение прочности связи в системе текстильный корд-резина. Технический результат достигается тем, что в резинокордном композите текстильный корд пропитан составом на основе латекса ДБА-1 - сополимера бутадиена, бутилакрилата и амида метакриловой кислоты или составом, включающим латекс со звеньями винилпиридина, а резиновый слой выполнен из смеси на основе ненасыщенного каучука 100 мас.ч., включающий модификатор РУ-Д-1-4 мас.ч. или модификатор Resine R-17-34 - 0,8-1,5 мас.ч., белую сажу - 5-10 мас.ч., смолу Пикар - 0,5-2,0 мас.ч., канифоль сосновую - 1-3 мас.ч., технический углерод N 550-50-55 мас.ч., масло-мягчитель «Норман-583» или ПН-6ш-7-16 мас.ч., серу полимерную Polsinex-33 - 1,0-1,5 мас.ч., серу молотую техническую - 0,5-0,8 мас.ч., вулканокс 4010 NA/LG (импортный аналог диафена ФП) - 1,0-2,5 мас.ч., белила цинковые - 2,5-6,0 мас.ч., стеариновую кислоту-1-2 мас.ч., вулкацит CZ/EG-С(импортный аналог сульфенамида Ц)-0,2-0,4 мас.ч., каолин КР-1 - 1-4 мас.ч., диспрактол К-16 (отечественный аналог альтакса) - 0,4-0,7 мас.ч.The technical result of the proposed technical solution is to increase the bond strength in the textile cord-rubber system. The technical result is achieved in that in a rubber-cord composite, the textile cord is impregnated with a composition based on DBA-1 latex - a copolymer of butadiene, butyl acrylate and methacrylic acid amide, or a composition comprising latex with vinylpyridine units, and the rubber layer is made of a mixture based on unsaturated rubber of 100 wt. h., including the modifier RU-D-1-4 wt.h. or Resine R-17-34 modifier - 0.8-1.5 parts by weight, white soot - 5-10 parts by weight, Picard resin - 0.5-2.0 parts by weight, pine rosin - 1-3 parts by weight, carbon black N 550-50-55 parts by weight, oil softener Norman-583 or PN-6sh-7-16 parts by weight, polymer sulfur Polsinex-33 - 1, 0-1.5 parts by weight, technical ground sulfur - 0.5-0.8 parts by weight, volcanox 4010 NA / LG (imported analogue of FP diaphene) - 1.0-2.5 parts by weight, zinc white - 2.5-6.0 parts by weight, stearic acid-1-2 parts by weight, vulcanizite CZ / EG-C (imported analogue of sulfenamide C) -0.2-0.4 parts by weight , kaolin KR-1 - 1-4 parts by weight, dyspractol K-16 (domestic analogue of altax) - 0.4-0.7 parts by weight

Углеводородная смола Пикар (ТУ 2451-010-54861661-2003) по внешнему виду представляет собой чешуйки темно-коричневого цвета, является продуктом модификации полиизопреноидов ангидридом малеиновой кислоты, повыситель клейкости резиновых смесей.Picard hydrocarbon resin (TU 2451-010-54861661-2003) in appearance is a dark brown flake, a product of the modification of polyisoprenoids with maleic anhydride, an increase in the stickiness of rubber compounds.

Модификатор РУ-Д (ТУ 2494-011-00149452-99) по внешнему виду представляет собой порошок белого цвета с желтоватым оттенком. Является продуктом взаимодействия резорцина и уротропина с добавлением борной кислоты и масла ПН-6, повышает упруго-прочностные, адгезионные свойства резиновых смесей.The RU-D modifier (TU 2494-011-00149452-99) in appearance is a white powder with a yellowish tint. It is a product of the interaction of resorcinol and urotropin with the addition of boric acid and PN-6 oil, it increases the elastic-strength, adhesive properties of rubber compounds.

Модификатор Resine (смола) R-17-3 4 по внешнему виду представляет собой мелкодисперсный порошок белого цвета, гекса (метоксиметил)меламиновая смола, нанесенная на оксид кремния, повышает адгезионные свойства резиновых смесей.Resine modifier (resin) R-17-3 4 in appearance is a fine powder of white color, hexa (methoxymethyl) melamine resin deposited on silicon oxide, increases the adhesion properties of rubber compounds.

Сульфенамид Ц (ТУ 2491-055-05761637-2005) - N-циклогексил-2-бензтиазолилсульфенамид, по внешнему виду представляет собой порошок или цилиндрические гранулы от светло-кремового до светло-зеленого цвета. Является эффективным ускорителем с замедленным действием в начальной стадии вулканизации, уменьшает опасность подвулканизации резиновых смесей.Sulfenamide C (TU 2491-055-05761637-2005) - N-cyclohexyl-2-benzthiazolylsulfenamide, in appearance it is a powder or cylindrical granules from light cream to light green in color. It is an effective accelerator with a delayed action in the initial stage of vulcanization, reduces the risk of vulcanization of rubber compounds.

Альтакс (ТУ 6-14-851-8б)-ди-(2-бензтиазолил)-дисульфид представляет собой цилиндрические гранулы желтовато-серого цвета. Является ускорителем средней активности, обеспечивает широкое плато вулканизации.Altax (TU 6-14-851-8b) -di- (2-benzthiazolyl) disulfide is a yellowish-gray cylindrical granule. It is an accelerator of medium activity, provides a wide plateau of vulcanization.

Диафен ФП (ТУ 2492-057-05761637-2005) - N-фенил-N-изопропил-п-фенилендиамин по внешнему виду представляет собой чешуйки от серовато-розового до темно-коричневого цвета. Является эффективным противостарителем, защищает резины от теплового старения.Diafen FP (TU 2492-057-05761637-2005) - N-phenyl-N-isopropyl-p-phenylenediamine in appearance is a grayish pink to dark brown flake. It is an effective antioxidant, protects rubber from heat aging.

Масло-мягчитель ПН-6ш (СТО 84035624-024-2009) - по внешнему виду представляет собой вязкую жидкость темно-коричневого цвета, экстракт фенольной очистки остаточных масел. Используется в качестве пластификатора в резиновых смесях шинного производства.Softener oil PN-6sh (STO 84035624-024-2009) - in appearance it is a dark brown viscous liquid, an extract of phenolic purification of residual oils. It is used as a plasticizer in rubber compounds of tire production.

Масло-мягчитель «Норман-583» (ТУ 0258-047-58604719-2004) - по внешнему виду представляет собой вязкую жидкость светло-коричневого цвета, является очищенным остаточным ароматическим экстрактом. Масло нормализовано по содержанию полициклических ароматических углеводородов. Используется в качестве пластификатора резиновых смесей.Softener oil "Norman-583" (TU 0258-047-58604719-2004) - in appearance it is a viscous liquid of light brown color, it is a purified residual aromatic extract. The oil is normalized by the content of polycyclic aromatic hydrocarbons. Used as a plasticizer for rubber compounds.

В качестве слоя текстильного корда может быть использован корд капроновый (найлон-6), анидный (найлон-6,6), арамидный, полиэфирный или корд арамидный с капроновой нитью, полиэфирный с капроновой нитью, вискозный, пропиточный состав - латексно-резорцинформальдегидный, включающий латекс - сополимер бутадиена, бутилакрилата, амида метилакриловой кислоты или латекс со звеньями винилпиридина, который может применяться в сочетании с другими латексами, например бутадиеновым карбоксилсодержащим, бутадиенстирольным или натуральным и необязательно с водной дисперсией блокированного изоцианата. Резиновый слой на основе ненасыщенного каучука может включать серную вулканизующую группу с сульфенамидом Ц (импортный аналог вулкацит CZ/EG-C), сульфенамидом М (импортный аналог вулкацит MOZ/LG), альтаксом (отечественный аналог диспрактол К-16), каптаксом и другими ускорителями вулканизации, полимерную серу, например Polsinex-33 или CRYSTEX OT-33, масла-мягчители ПН-6ш или «Норман-583», «Норман-346», традиционные ингредиенты резиновой смеси: технический углерод, мягчители, например, стирольно-инденовую смолу и рубракс, олеиновую кислоту, антискорчинги, например, сантогард PVI, фталевый ангидрид и бензойную кислоту, антиоксиданты, например, диафен ФП с ацетонанилом Н и защитным воском. В качестве ненасыщенного каучука могут использоваться синтетический изопреновый (СКИ), натуральный (НК), бутадиеновый (СКД), бутадиенстирольный (БСК), бутадиенметилстирольный или их комбинация.As a textile cord layer, kapron (nylon-6), anide (nylon-6,6), aramid, polyester or aramid cord with kapron thread, polyester with kapron thread, viscose, impregnating composition - latex-resorcin formaldehyde, including latex is a copolymer of butadiene, butyl acrylate, methyl acrylic acid amide or latex with vinyl pyridine units, which can be used in combination with other latexes, for example, butadiene carboxyl-containing, styrene butadiene or natural and optional o with an aqueous dispersion of blocked isocyanate. The unsaturated rubber-based rubber layer may include a sulfuric vulcanizing group with sulfenamide C (an imported analog of CZ / EG-C vulcacite), sulfenamide M (an imported analog of MOZ / LG vulcacite), altax (a domestic analog of K-16 duractol), captax and other accelerators vulcanization, polymer sulfur, for example Polsinex-33 or CRYSTEX OT-33, softener oils PN-6sh or Norman-583, Norman-346, traditional rubber compounds: carbon black, softeners, for example styrene-indene resin and rubrax, oleic acid, anti-scorchings, for example p santogard PVI, phthalic anhydride and benzoic acid, antioxidants such as AF diafen with atsetonanilom H and a protective wax. As unsaturated rubber, synthetic isoprene (SKI), natural (NK), butadiene (SKD), styrene butadiene (BSK), butadiene methyl styrene or a combination thereof can be used.

Пример 1 (прототип).Example 1 (prototype).

В качестве слоя текстильного корда используется анидный корд марки 55 АДУ (ТУ 6-00206-2007). Ткань пропитана составом латексно-резорцинформальдегидным на основе бутадиенового карбоксилсодержащего латекса СКД-1C с латексом «Ярлаткорд ВП-15» (ОАО НИИ «Ярсинтез», без технических условий) со звеньями винилпиридина в массовом соотношении 50:50. В пропиточный состав, кроме того, входят, мас.ч. на 100 мас.ч. латексов (считая на сухое вещество): 16,5 новолачной резорцинформальдегидной смолы СФ-282; 6,6 формальдегида и 1,24 едкого натра. Резиновый слой содержит ингредиенты, мас.ч. на 100 мас.ч. каучука: комбинацию каучуков НК+СКД+БСК - 100; серу - 2,2; вулкацит CZ/EG-C (импортный аналог сульфенамида Ц) - 1,4; диспрактол К-16 (отечественный аналог альтакса) - 0,2; гексахлорпараксилол - 0,8; оксид цинка - 5,0; алкилфеноламинную смолу - 3,0; стеариновую кислоту - 2,0; масло-мягчитель «Норман-583» (отечественный экологически чистый аналог масла ПН-6ш, ТУ 0258-047-58604719-2004) - 5,0; стирольно-инденовую смолу - 3,0; рубракс - 5,0; вулканокс 4010 NA/LG (импортный аналог диафена ФП) - 1,0; техуглерод N 550 (аналог техуглерода П-514) - 40,0; техуглерод N 330 (аналог техуглерода П-234) - 15,0.As an textile cord layer, an anide cord of grade 55 ADU (TU 6-00206-2007) is used. The fabric is impregnated with a latex-resorcinol formaldehyde composition based on a SKD-1C butadiene carboxyl-containing latex with a Yarlatkord VP-15 latex (OAO Yarsintez Scientific Research Institute, without specifications) with vinylpyridine units in a mass ratio of 50:50. The impregnating composition, in addition, includes, by weight.h. per 100 parts by weight latexes (counting on dry matter): 16.5 novolac resorcinol formaldehyde resin SF-282; 6.6 formaldehyde and 1.24 sodium hydroxide. The rubber layer contains ingredients, parts by weight per 100 parts by weight rubber: a combination of rubber NK + SKD + BSK - 100; sulfur - 2.2; vulcanizite CZ / EG-C (imported analogue of sulfenamide C) - 1.4; Dispractol K-16 (domestic analogue of Altax) - 0.2; hexachloroparaxylene - 0.8; zinc oxide - 5.0; alkyl phenolamine resin 3.0; stearic acid - 2.0; softener oil "Norman-583" (domestic environmentally friendly analogue of oil PN-6sh, TU 0258-047-58604719-2004) - 5.0; styrene-indene resin - 3.0; rubrax - 5.0; Vulkanoks 4010 NA / LG (imported analogue of diafen FP) - 1.0; carbon black N 550 (analog of carbon black P-514) - 40.0; carbon black N 330 (analogue of carbon black P-234) - 15.0.

Пример 2. Отличается от примера 1 тем, что в резиновом слое отсутствует гексахлорпараксилол (ГХПК), рубракс, алкилфеноламинная смола (АФАС), стирольно-инденовая смола, техуглерод N 330, при этом содержание ингредиентов, мас.ч: серы - 0,5; вулкацита CZ/EG-C - 0,2; масла-мягчителя «Норман-583» - 7,0; вулканокса 4010 NA/LG - 1,0; стеариновой кислоты - 1,0; диспрактола К-16 - 0,4; техуглерода N 550 - 50,0; оксида цинка - 5,0; присутствует белая сажа БС-120 - 5,0; модификатор РУ-Д - 1,0; полимерная сера Polsinex - 33 - 1,0; смола «Пикар» - 0,5; канифоль сосновая - 1,0; каолин КР-1 - 1,0.Example 2. It differs from example 1 in that the rubber layer does not contain hexachloroparaxylene (GHPC), rubrax, alkyl phenolamine resin (AFAS), styrene-indene resin, carbon black N 330, while the content of ingredients, parts by weight: sulfur — 0.5 ; Vulcacite CZ / EG-C 0.2; softener oil "Norman-583" - 7.0; Vulcanox 4010 NA / LG - 1.0; stearic acid - 1.0; dyspractol K-16 - 0.4; carbon black N 550 - 50.0; zinc oxide - 5.0; there is white soot BS-120 - 5.0; RU-D modifier - 1.0; Polsinex polymer sulfur - 33 - 1.0; resin "Picard" - 0.5; pine rosin - 1.0; kaolin KR-1 - 1.0.

Пример 3. Отличается от примера 1 тем, что в резиновом слое отсутствует гексахлорпараксилол (ГХПК), рубракс, алкилфеноламинная смола (АФАС), стирольно-инденовая смола, техуглерод N 330, при этом содержание ингредиентов, мас.ч: серы - 0,8; вулкацита CZ/EG-C - 0,4; масла-мягчителя «Норман-583» - 16,0; вулканокса 4010 NA/LG - 2,5; стеариновой кислоты - 2,0; диспрактола К-16 - 0,7; техуглерода N 550 - 55,0; оксида цинка - 6,0; присутствует белая сажа БС-120 - 10,0; модификатор РУ-Д - 4,0; полимерная сера Polsinex-33 - 1,5; смола «Пикар» - 2,0; канифоль сосновая - 3,0; каолин КР-1 - 4,0.Example 3. It differs from example 1 in that the rubber layer does not contain hexachloroparaxylene (GHPC), rubrax, alkyl phenolamine resin (AFAS), styrene-indene resin, carbon black N 330, while the content of ingredients, wt.h: sulfur - 0.8 ; vulvacite CZ / EG-C - 0.4; softener oil "Norman-583" - 16.0; Vulcanox 4010 NA / LG - 2.5; stearic acid - 2.0; dyspractol K-16 - 0.7; carbon black N 550 - 55.0; zinc oxide - 6.0; there is white soot BS-120 - 10.0; RU-D modifier - 4.0; polymer sulfur Polsinex-33 - 1.5; resin "Picard" - 2.0; pine rosin - 3.0; kaolin KR-1 - 4.0.

Пример 4. Отличается от примера 1 тем, что в резиновом слое отсутствует гексахлорпараксилол (ГХПК), рубракс, алкилфеноламинная смола (АФАС), стирольно-инденовая смола, техуглерод N 330, при этом содержание ингредиентов, мас.ч: серы - 0,8; вулкацита CZ/EG-C - 0,4; масла-мягчителя «Норман-583» - 16,0; вулканокса 4010 NA/LG - 2,5; стеариновой кислоты - 2,0; диспрактола К-16 - 0,7; техуглерода N 550 - 55,0; оксида цинка - 6,0; присутствует белая сажа БС-120 - 10,0; модификатор РУ-Д - 4,0; полимерная сера Polsinex-33 - 1,5; смола «Пикар» - 2,0; канифоль сосновая - 3,0; каолин КР-1 - 4,0; а в пропиточном составе вместо латекса «Ярлаткорд ВП-15» используется латекс ДБА-1.Example 4. It differs from example 1 in that the rubber layer does not contain hexachloroparaxylene (GHPC), rubrax, alkyl phenolamine resin (AFAS), styrene-indene resin, carbon black N 330, while the content of ingredients, wt.h: sulfur - 0.8 ; vulvacite CZ / EG-C - 0.4; softener oil "Norman-583" - 16.0; Vulcanox 4010 NA / LG - 2.5; stearic acid - 2.0; dyspractol K-16 - 0.7; carbon black N 550 - 55.0; zinc oxide - 6.0; there is white soot BS-120 - 10.0; RU-D modifier - 4.0; polymer sulfur Polsinex-33 - 1.5; resin "Picard" - 2.0; pine rosin - 3.0; kaolin KR-1 - 4.0; and in the impregnating composition, instead of the Yarlatkord VP-15 latex, DBA-1 latex is used.

Пример 5. Отличается от примера 1 тем, что в резиновом слое отсутствует гексахлорпараксилол (ГХПК), рубракс, алкилфеноламинная смола (АФАС), стирольно-инденовая смола, техуглерод N 330, при этом содержание ингредиентов, мас.ч: серы - 0,8; вулкацита CZ/EG-C - 0,4; масла-мягчителя «Норман-583» - 16,0; вулканокса 4010 NA/LG - 2,5; стеариновой кислоты - 2,0; диспрактола К-16 - 0,7; техуглерода N 550 - 55,0; оксида цинка - 6,0; присутствует белая сажа БС-120 - 10,0; модификатор РУ-Д - 4,0; полимерная сера Polsinex-33 - 1,5; смола «Пикар» - 2,0; канифоль сосновая - 3,0; каолин КР-1 - 4,0, а в пропиточном составе содержится блокированный Е-капролактамом полиизоцианат МК-1 (ТУ 2433-001-03045658-2003) - 24,5 мас.ч.Example 5. It differs from example 1 in that the rubber layer does not contain hexachloroparaxylene (GHPC), rubrax, alkylphenolamine resin (AFAS), styrene-indene resin, carbon black N 330, while the content of ingredients, parts by weight of sulfur: 0.8 ; vulvacite CZ / EG-C - 0.4; softener oil "Norman-583" - 16.0; Vulcanox 4010 NA / LG - 2.5; stearic acid - 2.0; dyspractol K-16 - 0.7; carbon black N 550 - 55.0; zinc oxide - 6.0; there is white soot BS-120 - 10.0; RU-D modifier - 4.0; polymer sulfur Polsinex-33 - 1.5; resin "Picard" - 2.0; pine rosin - 3.0; kaolin KR-1 - 4.0, and the impregnating composition contains MK-1 polyisocyanate blocked by E-caprolactam (TU 2433-001-03045658-2003) - 24.5 parts by weight

Пример 6. Отличается от примера 1 тем, что в резиновом слое отсутствует гексахлорпараксилол (ГХПК), рубракс, алкилфеноламинная смола (АФАС), стирольно-инденовая смола, техуглерод N 330, при этом содержание ингредиентов, мас.ч: серы - 0,8; вулкацита CZ/EG-C - 0,4; масла-мягчителя «Норман-583» - 16,0; вулканокса 4010 NA/LG - 2,5; стеариновой кислоты - 2,0; диспрактола К-16 - 0,7; техуглерода N 550 - 55,0; оксида цинка - 6,0; присутствует белая сажа БС-120 - 10,0; модификатор Resine R-17-34 - 0,8; полимерная сера Polsinex-33 - 1,5; смола «Пикар» - 2,0; канифоль сосновая - 3,0; каолин КР-1 - 4,0.Example 6. It differs from example 1 in that the rubber layer does not contain hexachloroparaxylene (GHPC), rubrax, alkyl phenolamine resin (AFAS), styrene-indene resin, carbon black N 330, while the content of ingredients, parts by weight of sulfur: 0.8 ; vulvacite CZ / EG-C - 0.4; softener oil "Norman-583" - 16.0; Vulcanox 4010 NA / LG - 2.5; stearic acid - 2.0; dyspractol K-16 - 0.7; carbon black N 550 - 55.0; zinc oxide - 6.0; there is white soot BS-120 - 10.0; modifier Resine R-17-34 - 0.8; polymer sulfur Polsinex-33 - 1.5; resin "Picard" - 2.0; pine rosin - 3.0; kaolin KR-1 - 4.0.

Пример 7. Отличается от примера 1 тем, что в резиновом слое отсутствует гексахлорпараксилол (ГХПК), рубракс, алкилфеноламинная смола (АФАС), стирольноинденовая смола, техуглерод N 330, при этом содержание ингредиентов, мас.ч: серы - 0,8; вулкацита CZ/EG-C - 0,4; масла-мягчителя «Норман-583» - 16,0; вулканокса 4010 NA/LG - 2,5; стеариновой кислоты - 2,0; диспрактола К-16 - 0,7; техуглерода N 550 - 55,0; оксида цинка - 6,0; присутствует белая сажа БС-120 - 10,0; модификатор Resine R-17-34 - 1,5; полимерная сера Polsinex-33 - 1,5; смола «Пикар» - 2,0; канифоль сосновая - 3,0; каолин КР-1-4,0.Example 7. It differs from example 1 in that the rubber layer lacks hexachloroparaxylene (GHPC), rubrax, alkyl phenolamine resin (AFAS), styrene-indene resin, carbon black N 330, while the content of ingredients, wt.h: sulfur - 0.8; vulvacite CZ / EG-C - 0.4; softener oil "Norman-583" - 16.0; Vulcanox 4010 NA / LG - 2.5; stearic acid - 2.0; dyspractol K-16 - 0.7; carbon black N 550 - 55.0; zinc oxide - 6.0; there is white soot BS-120 - 10.0; Resine R-17-34 modifier - 1.5; polymer sulfur Polsinex-33 - 1.5; resin "Picard" - 2.0; pine rosin - 3.0; kaolin KR-1-4.0.

Пример 8. Отличается от примера 1 тем, что в резиновом слое отсутствует гексахлорпараксилол (ГХПК), рубракс, алкилфеноламинная смола (АФАС), стирольноинденовая смола, техуглерод N 330, при этом содержание ингредиентов, мас.ч: серы - 0,8; вулкацита CZ/EG-C - 0,4; масла-мягчителя «Норман-583» - 16,0; вулканокса 4010 NA/LG - 2,5; стеариновой кислоты - 2,0; диспрактола К-16 - 0,7; техуглерода N 550 - 55,0; оксида цинка - 6,0; присутствует белая сажа БС-120 - 10,0; модификатор РУ-Д - 2,0; полимерная сера Polsinex-33 - 1,5; смола «Пикар» - 2,0; канифоль сосновая - 3,0; каолин КР-1 - 4,0; а в пропиточном составе вместо комбинации латексов «Ярлаткорд ВП-15» и СКД-1c используется латекс ДБА-1.Example 8. It differs from example 1 in that the rubber layer does not contain hexachloroparaxylene (GHPC), rubrax, alkyl phenolamine resin (AFAS), styrene-indene resin, carbon black N 330, while the content of ingredients, parts by weight: sulfur — 0.8; vulvacite CZ / EG-C - 0.4; softener oil "Norman-583" - 16.0; Vulcanox 4010 NA / LG - 2.5; stearic acid - 2.0; dyspractol K-16 - 0.7; carbon black N 550 - 55.0; zinc oxide - 6.0; there is white soot BS-120 - 10.0; RU-D modifier - 2.0; polymer sulfur Polsinex-33 - 1.5; resin "Picard" - 2.0; pine rosin - 3.0; kaolin KR-1 - 4.0; and in the impregnating composition, instead of the combination of Yarlatkord VP-15 latexes and SKD-1c latexes, DBA-1 latex is used.

Пример 9. Отличается от примера 1 тем, что в резиновом слое отсутствует гексахлорпараксилол (ГХПК), рубракс, алкилфеноламинная смола (АФАС), стирольноинденовая смола, техуглерод N 330, при этом содержание ингредиентов, мас.ч: серы - 0,8; вулкацита CZ/EG-C - 0,4; масла-мягчителя «Норман-583» - 16,0; вулканокса 4010 NA/LG - 2,5; стеариновой кислоты -2,0; диспрактола К-16 - 0,7; техуглерода N 550 - 55,0; оксида цинка - 6,0; присутствует белая сажа БС-120 - 10,0; модификатор РУ-Д - 2,0; полимерная сера Polsinex-33 - 1,5; смола «Пикар» - 2,0; канифоль сосновая - 3,0; каолин КР-1 - 4,0; а в пропиточном составе вместо комбинации латексов «Ярлаткорд ВП-15» и СКД-1c используется латекс «Ярлаткорд ВП-15».Example 9. It differs from example 1 in that the rubber layer does not contain hexachloroparaxylene (GHPC), rubrax, alkyl phenolamine resin (AFAS), styrene-indene resin, carbon black N 330, while the content of ingredients, parts by weight: sulfur — 0.8; vulvacite CZ / EG-C - 0.4; softener oil "Norman-583" - 16.0; Vulcanox 4010 NA / LG - 2.5; stearic acid -2.0; dyspractol K-16 - 0.7; carbon black N 550 - 55.0; zinc oxide - 6.0; there is white soot BS-120 - 10.0; RU-D modifier - 2.0; polymer sulfur Polsinex-33 - 1.5; resin "Picard" - 2.0; pine rosin - 3.0; kaolin KR-1 - 4.0; and in the impregnating composition, instead of the combination of Yarlatkord VP-15 latexes and SKD-1c latexes, Yarlatkord VP-15 latex is used.

Пример 10. Отличается от примера 1 тем, что в резиновом слое отсутствует гексахлорпараксилол (ГХПК), рубракс, алкилфеноламинная смола (АФАС), стирольноинденовая смола, техуглерод N 330, при этом содержание ингредиентов, мас.ч: серы - 0,8; вулкацита CZ/EG-C - 0,4; масла-мягчителя «Норман-583» - 16,0; вулканокса 4010 NA/LG - 2,5; стеариновой кислоты - 2,0; диспрактола К-16 - 0,7; техуглерода N 550 - 55,0; оксида цинка - 6,0; присутствует белая сажа БС-120 - 10,0; модификатор РУ-Д - 2,0; полимерная сера Polsinex-33 - 1,5; смола «Пикар» - 2,0; канифоль сосновая - 3,0; каолин КР-1 - 4,0; а в качестве слоя текстильного корда используется арамидный корд марки Русар 75 (ТУ 8378-041-05138230-2006).Example 10. It differs from example 1 in that the rubber layer does not contain hexachloroparaxylene (GHPC), rubrax, alkyl phenolamine resin (AFAS), styrene-indene resin, carbon black N 330, while the content of ingredients, parts by weight: sulfur — 0.8; vulvacite CZ / EG-C - 0.4; softener oil "Norman-583" - 16.0; Vulcanox 4010 NA / LG - 2.5; stearic acid - 2.0; dyspractol K-16 - 0.7; carbon black N 550 - 55.0; zinc oxide - 6.0; there is white soot BS-120 - 10.0; RU-D modifier - 2.0; polymer sulfur Polsinex-33 - 1.5; resin "Picard" - 2.0; pine rosin - 3.0; kaolin KR-1 - 4.0; and the Rusar 75 brand aramid cord (TU 8378-041-05138230-2006) is used as a textile cord layer.

Пример 11. Отличается от примера 1 тем, что в резиновом слое отсутствует гексахлорпараксилол (ГХПК), рубракс, алкилфеноламинная смола (АФАС), стирольноинденовая смола, техуглерод N 330, при этом содержание ингредиентов, мас.ч: серы - 0,8; вулкацита CZ/EG-C - 0,4; масла-мягчителя «Норман-583» - 16,0; вулканокса 4010 NA/LG - 2,5; стеариновой кислоты - 2,0; диспрактола К-16 - 0,7; техуглерода N 550 - 55,0; оксида цинка - 6,0; присутствует белая сажа БС-120 - 10,0; модификатор РУ-Д - 2,0; полимерная сера Polsinex-33 - 1,5; смола «Пикар» - 2,0; канифоль сосновая - 3,0; каолин КР-1 - 4,0; а в качестве слоя текстильного корда используется полиэфирный корд марки 14 ЛДУ (ТУ 6-00-211-2000).Example 11. It differs from example 1 in that the rubber layer does not contain hexachloroparaxylene (GHPC), rubrax, alkyl phenolamine resin (AFAS), styrene-indene resin, carbon black N 330, while the content of ingredients, parts by weight: sulfur — 0.8; vulvacite CZ / EG-C - 0.4; softener oil "Norman-583" - 16.0; Vulcanox 4010 NA / LG - 2.5; stearic acid - 2.0; dyspractol K-16 - 0.7; carbon black N 550 - 55.0; zinc oxide - 6.0; there is white soot BS-120 - 10.0; RU-D modifier - 2.0; polymer sulfur Polsinex-33 - 1.5; resin "Picard" - 2.0; pine rosin - 3.0; kaolin KR-1 - 4.0; and as a layer of textile cord used polyester cord brand 14 LDU (TU 6-00-211-2000).

Пример 12. Отличается от примера 1 тем, что в резиновом слое отсутствует гексахлорпараксилол (ГХПК), рубракс, алкилфеноламинная смола (АФАС), стирольноинденовая смола, техуглерод N 330, при этом содержание ингредиентов, мас.ч: серы - 0,8; вулкацита CZ/EG-C - 0,4; масла-мягчителя «Норман-583» - 16,0; вулканокса 4010 NA/LG - 2,5; стеариновой кислоты - 2,0; диспрактола К-16 - 0,7; техуглерода N 550 - 55,0; оксида цинка - 6,0; присутствует белая сажа БС-120 - 10,0; модификатор РУ-Д - 2,0; полимерная сера Polsinex-33 - 1,5; смола «Пикар» - 2,0; канифоль сосновая - 3,0; каолин КР-1 - 4,0; а в качестве слоя текстильного корда используется капроновый корд марки 23 КНТС (ГОСТ 24221-94).Example 12. It differs from example 1 in that the rubber layer does not contain hexachloroparaxylene (GHPC), rubrax, alkyl phenolamine resin (AFAS), styrene-indene resin, carbon black N 330, while the content of ingredients, parts by weight: sulfur — 0.8; vulvacite CZ / EG-C - 0.4; softener oil "Norman-583" - 16.0; Vulcanox 4010 NA / LG - 2.5; stearic acid - 2.0; dyspractol K-16 - 0.7; carbon black N 550 - 55.0; zinc oxide - 6.0; there is white soot BS-120 - 10.0; RU-D modifier - 2.0; polymer sulfur Polsinex-33 - 1.5; resin "Picard" - 2.0; pine rosin - 3.0; kaolin KR-1 - 4.0; and as a layer of textile cord kapron cord of brand 23 KNTS is used (GOST 24221-94).

Изготовление резины по приведенным примерам 1-12 осуществляется известными способами.The manufacture of rubber according to examples 1-12 is carried out by known methods.

Сопоставительная прочность связи между текстильным кордом и резиной различных резинокордных композитов в сравнении с предлагаемым резинокордным композитом, а также основные физико-механические свойства резины приведены в таблицах 1 и 2.The comparative strength of the bond between the textile cord and rubber of various rubber-cord composites in comparison with the proposed rubber-cord composite, as well as the main physical and mechanical properties of the rubber are shown in tables 1 and 2.

Предлагаемый состав резинового слоя резинокордного композита на основе текстильного корда марки 55 АДУ обеспечивает повышение прочности связи в системе с 141 Н (прототип) до (241-190) Н (примеры 2-6). Примеры 3-6 и 8, 9 показывают, что предлагаемое техническое решение позволяет обеспечить высокую прочность связи при заявленном изменении пропиточного состава резинокордного композита следующим образом: на основе латекса ДБА-1 (комбинация ДБА-1+СКД-1С) прочность связи составляет 218 Н (пример 4); на основе латекса со звеньями винилпиридина (комбинация Ярлаткорд ВП-15+СКД-1С) прочность связи составляет 236-190 Н (примеры-3 и 6); максимальная прочность связи 241 Н для комбинации латексов наблюдается в композите (пример 5), содержащем в пропиточном составе дополнительно блокированный Е-капролактамом полиизоцинат (Ярлаткорд ВП-15+СКД-1С + блокированный Е-капролактамом полиизоцианат). Исключение из пропиточного состава латекса СКД-1С приводит к повышению прочности связи анидного корда для латекса ДБА-1 до 257 Н (пример 8) и для латекса Ярлаткорд ВП-15 до 286 Н (пример 9).The proposed composition of the rubber layer of rubber-cord composite based on textile cord grade 55 ADU provides increased bond strength in the system from 141 N (prototype) to (241-190) N (examples 2-6). Examples 3-6 and 8, 9 show that the proposed technical solution allows for high bond strength with the declared change in the impregnation composition of the rubber cord composite as follows: based on the DBA-1 latex (combination DBA-1 + SKD-1C), the bond strength is 218 N (example 4); based on latex with vinylpyridine units (Yarlatkord VP-15 + SKD-1S combination), bond strength is 236-190 N (examples 3 and 6); the maximum bond strength of 241 N for the combination of latexes is observed in the composite (example 5) containing in the impregnating composition an additional polyisocinate blocked by E-caprolactam (Yarlatkord VP-15 + SKD-1C + blocked by E-caprolactam polyisocyanate). The exclusion of SKD-1C latex from the impregnation composition leads to an increase in the bond strength of the anide cord for DBA-1 latex to 257 N (example 8) and for Yarlatkord VP-15 latex to 286 N (example 9).

При заявленном изменении типа корда в резинокордном композите (примеры 10-12) обеспечивается также высокая прочность связи текстильного корда с резиной, однако для полиэфирного и арамидного кордов прочность связи с резиной ниже прототипа, что объясняется известным фактом зависимости адгезионных свойств корда от его химической структуры.With the stated change in the type of cord in the rubber-cord composite (examples 10-12), the high bond strength of the textile cord with rubber is also provided, however, for polyester and aramid cords, the bond strength with rubber is lower than the prototype, which is explained by the known fact that the adhesive properties of the cord depend on its chemical structure.

Использование по предлагаемому изобретению резинокордного композита в многослойных резинокордных изделиях позволяет значительно увеличить прочность связи текстильного корда с резиной и в результате этого повысить работоспособность изделий.The use of the rubber-cord composite according to the invention in multilayer rubber-cord products can significantly increase the bond strength of the textile cord with rubber and, as a result, increase the performance of the products.

Claims (1)

Резинокордный композит, состоящий из слоя текстильного корда, пропитанного латексно-резорцинформальдегидным составом, и резинового слоя, выполненного на основе ненасыщенного каучука, включающего техническую молотую серу, сульфенамид Ц, альтакс, технический углерод, стеариновую кислоту, масло-мягчитель, диафен ФП, оксид цинка, отличающийся тем, что слой текстильного корда пропитан составом, содержащим латекс ДБА-1 - сополимер бутадиена, бутилакрилата и амида метакриловой кислоты или латекс со звеньями винилпиридина необязательно с другим латексом и необязательно блокированный Е-капролактамом полиизоцианат, при этом резиновый слой дополнительно содержит полимерную серу, смолу «Пикар», сосновую канифоль, каолин, модификатор РУ-Д или модификатор смолу R-17-34 и белую сажу при следующем соотношении ингредиентов резинового слоя, мас.ч:
ненасыщенный каучук 100 сера молотая техническая 0,5-0,8 сера полимерная 1,0-1,5 сульфенамид Ц 0,2-0,4 альтакс 0,4-0,7 технический углерод 50,0-55,0 стеариновая кислота 1,0-2,0 масло-мягчитель 7,0-16,0 смола «Пикар» 0,5-2,0 канифоль сосновая 1,0-3,0 диафенФП 1,0-2,5 оксид цинка 5,0-6,0 модификатор РУ-Д 1,0-4,0 или модификатор смола R-17-34 0,8-1,5 белая сажа 5,0-10,0 каолин 1,0-4,0 Rubber-cord composite consisting of a layer of textile cord impregnated with a latex-resorcinol formaldehyde composition and a rubber layer made on the basis of unsaturated rubber, including technical ground sulfur, sulfenamide C, altax, carbon black, stearic acid, softener oil, diphene phenol, zinc oxide characterized in that the textile cord layer is impregnated with a composition containing DBA-1 latex - a copolymer of butadiene, butyl acrylate and methacrylic acid amide or latex with vinyl pyridine units optionally with each other m latex and optionally blocked by E-caprolactam polyisocyanate, the rubber layer additionally contains polymer sulfur, Picard resin, pine rosin, kaolin, RU-D modifier or R-17-34 resin modifier and white soot in the following ratio of rubber layer ingredients wt.h:
unsaturated rubber one hundred technical ground sulfur 0.5-0.8 polymer sulfur 1.0-1.5 sulfenamide C 0.2-0.4 altax 0.4-0.7 carbon black 50.0-55.0 stearic acid 1.0-2.0 softener oil 7.0-16.0 resin "Picard" 0.5-2.0 pine rosin 1.0-3.0 diaphen 1.0-2.5 zinc oxide 5.0-6.0 modifier RU-D 1.0-4.0 or resin modifier R-17-34 0.8-1.5 white soot 5.0-10.0 kaolin 1.0-4.0