RU2414527C1 - Procedure for cutting tool multi-layer coating - Google Patents

Abstract

FIELD: machine building. ^ SUBSTANCE: two-layer coating is applied on working surfaces of cutting tool by vacuum-plasma procedure. As a lower layer there is applied titanium and silicon nitride or titanium and chromium nitride, or titanium and niobium nitride, or titanium and aluminium nitride, or titanium and iron nitride, or titanium and zirconium nitride. As an upper layer there is applied the same nitride alloyed with molybdenum. Also, at application of layers temperature of condensation and pressure of nitrogen are different in each layer. ^ EFFECT: increased functionality of tool and upgraded quality of processing. ^ 2 cl, 1 tbl, 1 ex

Description

Изобретение относится к способам нанесения износостойких покрытий на режущий инструмент и может быть использовано в металлообработке.The invention relates to methods for applying wear-resistant coatings to a cutting tool and can be used in metalworking.

Известен способ получения износостойкого покрытия для режущего инструмента (РИ), при котором на его поверхность вакуумно-дуговым методом наносят покрытие из нитрида титана (TiN) или карбонитрида титана (TiCN) (см. Табаков В.П. Работоспособность режущего инструмента с износостойкими покрытиями на основе сложных нитридов и карбонитридов титана. Ульяновск: УлГТУ, 1998. 122 с.). К причинам, препятствующим достижению указанного ниже технического результата при использовании известного способа, относится то, что в известном способе покрытия, обладающие хорошей адгезией к инструментальному материалу, имеют относительно низкую твердость и уровень сжимающих напряжений либо имеют высокую микротвердость, но недостаточную прочность сцепления с инструментальной основой. В результате этого покрытие легко подвергается абразивному износу, в нем быстро зарождаются и распространяются трещины, приводящие к разрушению покрытия, что снижает стойкость РИ с покрытием.There is a method of obtaining a wear-resistant coating for a cutting tool (RI), in which a titanium nitride (TiN) or titanium carbonitride (TiCN) coating is applied on its surface by a vacuum-arc method (see Tabakov V.P. Performance of a cutting tool with wear-resistant coatings on based on complex nitrides and titanium carbonitrides. Ulyanovsk: UlSTU, 1998. 122 p.). The reasons that impede the achievement of the following technical result when using the known method include the fact that in the known method, coatings having good adhesion to the tool material have relatively low hardness and level of compressive stresses or have high microhardness, but insufficient adhesion to the tool base . As a result of this, the coating easily undergoes abrasive wear, cracks quickly nucleate and propagate in it, leading to the destruction of the coating, which reduces the resistance of the RI with the coating.

Наиболее близким способом того же назначения к заявленному изобретению по совокупности признаков является способ, включающий вакуумно-плазменное нанесение многослойного покрытия, состоящего из нижнего слоя нитрида титана и алюминия TiAlN и верхнего слоя нитрида титана, алюминия и циркония TiAlZrN (см. патент на изобретение RU 2293794 C1, C23C 14/24, C23C 14/06. - 20.02.2007. - Бюл. №5), принятый за прототип.The closest method of the same purpose to the claimed invention in terms of features is a method comprising vacuum-plasma deposition of a multilayer coating consisting of a lower layer of titanium nitride and aluminum TiAlN and an upper layer of titanium nitride, aluminum and zirconium TiAlZrN (see patent for the invention RU 2293794 C1, C23C 14/24, C23C 14/06. - 02.20.2007. - Bull. No. 5), adopted as a prototype.

К причинам, препятствующим достижению указанного ниже технического результата при использовании известного способа, принятого за прототип, относится то, что в известном способе многослойное покрытие содержит слои, имеющие низкие остаточные напряжения и высокую теплопроводность. В результате покрытие плохо сопротивляется процессам трещинообразования и практически не препятствует проникновению тепла вглубь инструмента.For reasons that impede the achievement of the technical result indicated below when using the known method adopted as a prototype, the multilayer coating in the known method contains layers having low residual stresses and high thermal conductivity. As a result, the coating poorly resists cracking processes and practically does not prevent the penetration of heat into the instrument.

Повышение в последнее время стоимости металлорежущего инструмента и ужесточение требований к точности обрабатываемых деталей сделало еще более актуальной проблему повышения стойкости РИ. Основной причиной износа РИ является возникновение трещин в его режущей части, являющихся причиной появления сколов и выкрашиваний, связанных с усталостным разрушением и явлением ползучести режущего клина РИ. Ползучесть, в свою очередь, вызвана проникновением тепла, образующегося при резании и трении стружки о поверхности инструмента, вглубь инструмента. Одним из путей повышения стойкости и работоспособности РИ с покрытием является нанесение покрытий многослойного типа. Наличие в покрытии слоев с определенными теплофизическими и механическими свойствами способно тормозить процессы образования и распространения трещин без снижения микротвердости, улучшить термонапряженное состояние РИ с покрытием и повысить стойкость РИ.Recently, the increase in the cost of metal-cutting tools and the tightening of requirements for precision machined parts made the problem of increasing the resistance of radiation sources even more urgent. The main cause of RI wear is the occurrence of cracks in its cutting part, which are the cause of chips and chipping associated with fatigue failure and the creep phenomenon of the RI cutting wedge. Creep, in turn, is caused by the penetration of heat generated during cutting and friction of the chips on the surface of the tool into the instrument. One of the ways to increase the durability and performance of coated RIs is by applying multilayer coatings. The presence in the coating of layers with certain thermophysical and mechanical properties can inhibit the processes of formation and propagation of cracks without reducing microhardness, improve the thermally stressed state of RS with a coating and increase the resistance of RS.

Технический результат - повышение работоспособности РИ и качества обработки.The technical result is an increase in the health of the Republic of Ingushetia and the quality of processing.

Указанный технический результат при осуществлении изобретения достигается тем, что в известном способе на рабочие поверхности РИ вакуумно-дуговым методом наносится двухслойное покрытие. Особенность заявляемого способа заключается в том, что в качестве нижнего слоя при давлении азота в камере установки 7,5·10^-4 Па и температуре 600°C наносят нитрид титана и кремния, или нитрид титана и хрома, или нитрид титана и ниобия, или нитрид титана и алюминия, или нитрид титана и железа, или нитрид титана и циркония, а в качестве верхнего слоя при давлении азота в камере установки 4,3·10^-3 Па и температуре 500°C наносят такой же нитрид, легированный молибденом. Осаждение нижнего слоя покрытия при пониженном давлении газа и повышенной температуре позволяет получить более высокую прочность сцепления покрытия с инструментальной основой, а снижение температуры и увеличение давления газа при осаждении верхнего слоя позволяет увеличить его микротвердость и остаточные сжимающие напряжения. Компоновка установки для нанесения покрытия включает один составной катод с корпусом из титанового сплава ВТ1-0 и вставкой из молибдена и два составных катода с корпусом из титанового сплава ВТ1-0 и вставкой из хрома, или ниобия, или железа, или циркония, или составной катод с алюминиевым корпусом и вставкой из ВТ1-0, или катод из сплава титана и кремния. При осаждении верхнего слоя используются все три катода с целью получения слоя TiCrMoN, или TiNbMoN, или TiFeMoN, или TiZrMoN, или TiAlMoN, или TiSiMoN, а при осаждении нижнего слоя катод, содержащий молибден отключают. Использование в качестве материалов слоев сложных нитридов (TiCrMoN, или TiNbMoN, или TiFeMoN, или TiZrMoN, или TiAlMoN, или TiSiMoN) с высокими остаточными сжимающими напряжениями способствует повышению трещиностойкости покрытия, кроме того, такие материалы имеют более низкую теплопроводность по сравнению с покрытиями типа TiN, TiCN, TiAlN. При этом в зависимости от области использования инструмента с покрытием, его общая толщина может колебаться в пределах от 5 до 8 мкм, а доля нижнего слоя составлять 40-50% от общей толщины покрытия.The specified technical result in the implementation of the invention is achieved by the fact that in the known method on the working surfaces of the RI by a vacuum-arc method, a two-layer coating is applied. A feature of the proposed method lies in the fact that titanium and silicon nitride, or titanium and chromium nitride, or titanium and niobium nitride, are applied as a lower layer at a nitrogen pressure in the installation chamber of 7.5 · 10 ^-4 Pa and a temperature of 600 ° C, or titanium and aluminum nitride, or titanium and iron nitride, or titanium and zirconium nitride, and the same layer is applied with molybdenum doped nitride in the chamber of the apparatus 4.3 · 10 ^-3 Pa and a temperature of 500 ° C as the upper layer. The deposition of the lower coating layer under reduced gas pressure and elevated temperature makes it possible to obtain a higher adhesion strength of the coating to the tool base, and lowering the temperature and increasing gas pressure during deposition of the upper layer can increase its microhardness and residual compressive stresses. The layout of the coating installation includes one composite cathode with a VT1-0 titanium alloy housing and a molybdenum insert and two composite cathodes with a VT1-0 titanium alloy housing and a chromium or niobium or iron or zirconium insert or composite cathode with an aluminum case and an insert made of VT1-0, or a cathode made of an alloy of titanium and silicon. In the deposition of the upper layer, all three cathodes are used to obtain a TiCrMoN, or TiNbMoN, or TiFeMoN, or TiZrMoN, or TiAlMoN, or TiSiMoN layer, and when the lower layer is deposited, the cathode containing molybdenum is turned off. The use of complex nitride layers as materials (TiCrMoN, or TiNbMoN, or TiFeMoN, or TiZrMoN, or TiAlMoN, or TiSiMoN) with high residual compressive stresses increases the crack resistance of the coating, in addition, such materials have lower thermal conductivity compared to TiN coatings TiCN, TiAlN. Moreover, depending on the area of use of the coated tool, its total thickness can range from 5 to 8 microns, and the proportion of the lower layer can be 40-50% of the total coating thickness.

Сущность изобретения заключается в следующем. В процессе резания РИ работает в условиях трещинообразования, а также воздействия высоких температур. Для снижения интенсивности процессов износа и разрушения покрытия и самого инструмента наиболее эффективны покрытия сложного состава, а в условиях трещинообразования еще большую эффективность показывают многослойные покрытия со слоями сложного состава. При этом увеличение количества легирующих элементов в составе покрытия приводит к росту его твердости и износостойкости, а также трещиностойкости. Однако при этом часто снижается прочность сцепления покрытия с инструментальной основой. В то же время повысить прочность сцепления покрытия с основой можно путем снижения давления реакционного газа при его конденсации и увеличения температуры конденсации, правда при этом снижаются другие его эксплуатационные свойства (износостойкость и др.). Поэтому целесообразно применение двухслойного покрытия, в котором верхний слой должен обладать наивысшими износо- и трещиностойкостью, а нижний в первую очередь должен обеспечивать высокую прочность сцепления с инструментальной основой. В зависимости от условий резания толщина покрытия меняется от 5 до 8 мкм (меньшие значения - при прерывистом резании). При этом при уменьшении толщины покрытия доля нижнего слоя возрастает до 50%, чтобы обеспечить возможность получения сплошного слоя, способного полноценно выполнять свои функции (слои толщиной менее 1 мкм нефункциональны). Пластины с покрытиями, полученные с отклонениями от указанных в формуле изобретения толщин слоев, показали более низкие результаты.The invention consists in the following. In the process of cutting, RI works in conditions of crack formation, as well as exposure to high temperatures. To reduce the intensity of the processes of wear and destruction of the coating and the tool itself, coatings of complex composition are most effective, and in conditions of crack formation, multilayer coatings with layers of complex composition show even greater efficiency. Moreover, an increase in the number of alloying elements in the composition of the coating leads to an increase in its hardness and wear resistance, as well as crack resistance. However, this often reduces the adhesion strength of the coating to the tool base. At the same time, it is possible to increase the adhesion strength of the coating to the base by reducing the pressure of the reaction gas during its condensation and increasing the condensation temperature, although at the same time its other operational properties (wear resistance, etc.) are reduced. Therefore, it is advisable to use a two-layer coating, in which the upper layer should have the highest wear and crack resistance, and the lower one should first provide high adhesion to the tool base. Depending on the cutting conditions, the coating thickness varies from 5 to 8 μm (lower values with interrupted cutting). In this case, with a decrease in the coating thickness, the fraction of the lower layer increases to 50% in order to ensure the possibility of obtaining a continuous layer capable of fully performing its functions (layers with a thickness of less than 1 μm are non-functional). Coated plates obtained with deviations from the layer thicknesses indicated in the claims showed lower results.

Для экспериментальной проверки заявленного способа было нанесено покрытие-прототип с соотношением слоев, соответствующим оптимальному значению, указанному в известном способе, а также двухслойное покрытие по предлагаемому способу. Покрытия наносили на твердосплавные пластины в вакуумной камере установки «Булат-6», снабженной тремя вакуумно-дуговыми испарителями, расположенными горизонтально в одной плоскости. В качестве катодов испаряемого металла при нанесении нижнего слоя (TiCrN, или TiNbN, или TiFeN, или TiZrN, или TiAlN, или TiSiN) использовали два составных катода с корпусом из титанового сплава ВТ1-0 со вставкой из хрома, или ниобия, или железа, или циркония, или составной катод с алюминиевым корпусом и вставкой из ВТ1-0, или катод из сплава титана и кремния. При нанесении верхнего слоя (TiCrMoN, или TiNbMoN, или TiFeMoN, или TiZrMoN, или TiAlMoN, или TiSiMoN) используют указанные два катода плюс катод, содержащий корпус из титанового сплава ВТ1-0 со вставкой из молибдена и расположенный между первыми катодами. Покрытия наносили после предварительной ионной очистки.For experimental verification of the claimed method, a prototype coating was applied with a layer ratio corresponding to the optimal value specified in the known method, as well as a two-layer coating according to the proposed method. The coatings were applied to carbide plates in the vacuum chamber of the Bulat-6 installation, equipped with three vacuum arc evaporators located horizontally in the same plane. As the cathodes of the evaporated metal when applying the lower layer (TiCrN, or TiNbN, or TiFeN, or TiZrN, or TiAlN, or TiSiN), two composite cathodes with a housing made of titanium alloy VT1-0 with an insert of chromium, or niobium, or iron, were used or zirconium, or a composite cathode with an aluminum casing and an insert of VT1-0, or a cathode of an alloy of titanium and silicon. When applying the upper layer (TiCrMoN, or TiNbMoN, or TiFeMoN, or TiZrMoN, or TiAlMoN, or TiSiMoN), the two cathodes are used plus the cathode containing a VT1-0 titanium alloy housing with a molybdenum insert and located between the first cathodes. The coatings were applied after preliminary ion cleaning.

Ниже приведен конкретный пример осуществления предлагаемого способа (покрытие TiCrN-TiCrMoN толщиной 6 мкм).The following is a specific example of the proposed method (coating TiCrN-TiCrMoN with a thickness of 6 μm).

Твердосплавные пластины МК8 (размером 4,7×12×12 мм) промывают в ультразвуковой ванне, протирают ацетоном, спиртом и устанавливают на поворотном устройстве в вакуумной камере установки «Булат-6», снабженной тремя испарителями, расположенными горизонтально в одной плоскости. Камеру откачивают до давления 6,65-10^-3 Па, включают поворотное устройство, подают на него отрицательное напряжение 1,1 кВ, включают один испаритель и при токе дуги 100 А производят ионную очистку и нагрев пластин до температуры 560-580°C. Ток фокусирующей катушки 0,4 А. Затем снижают отрицательное напряжение до 150 В, ток катушек до 0,35 А, включают два противоположных испарителя (катода) - составных (с хромовой вставкой), подают в камеру реакционный газ - азот, и осаждают покрытие толщиной 3,0 мкм (слой TiCrN) в течение 18 мин при давлении газа 7,5·10^-4 Па. Температура конденсации при этом 600°C. Затем при напряжении до 120 В, токе фокусирующих катушек до 0,25 А включают третий катод (содержащий молибден). В камеру подается реакционный газ (давление 4,3·10^-3 Па) - азот, и осаждают второй слой покрытия (TiCrMoN) толщиной 3,0 мкм в течение 18 мин. Температура конденсации при этом 500°C. Затем отключают испарители, подачу реакционного газа, напряжение и вращение приспособления. Через 15-20 мин камеру открывают и извлекают инструмент с покрытием.MK8 carbide inserts (4.7 × 12 × 12 mm in size) are washed in an ultrasonic bath, wiped with acetone, alcohol and mounted on a rotary device in the vacuum chamber of the Bulat-6 installation equipped with three evaporators located horizontally in the same plane. The chamber is pumped out to a pressure of 6.65-10 ^-3 Pa, the rotator is turned on, a negative voltage of 1.1 kV is applied to it, one evaporator is turned on, and at an arc current of 100 A, the plates are cleaned and heated to a temperature of 560-580 ° C. The focusing coil current is 0.4 A. Then the negative voltage is reduced to 150 V, the coil current to 0.35 A, include two opposite evaporators (cathodes) - composite (with a chrome insert), the reaction gas - nitrogen is fed into the chamber, and the coating is deposited 3.0 μm thick (TiCrN layer) for 18 min at a gas pressure of 7.5 · 10 ^-4 Pa. The condensation temperature is 600 ° C. Then, at voltages up to 120 V, current focusing coils up to 0.25 A, a third cathode (containing molybdenum) is turned on. The reaction gas (pressure 4.3 · 10 ^-3 Pa) - nitrogen is fed into the chamber, and a second coating layer (TiCrMoN) 3.0 μm thick is deposited for 18 minutes. The condensation temperature is 500 ° C. Then shut off the evaporators, the supply of reaction gas, voltage and rotation of the device. After 15-20 minutes, the chamber is opened and the coated tool is removed.

Стойкостные испытания проводили на токарно-винторезном станке 16К20 при обработке конструкционной стали 5ХНМ. Испытывали твердосплавные пластины марки МК8, обработанные по известному и предлагаемому способам. Критерием износа служила фаска износа по задней поверхности шириной 0,4 мм.Durability tests were carried out on a screw-cutting machine 16K20 when machining structural steel 5XHM. Tested carbide inserts grade MK8, processed according to the known and proposed methods. The wear criterion was a chamfer of wear along the back surface with a width of 0.4 mm.

Таблица Table Результаты испытаний РИ с покрытиемCoated RI Test Results № ппNo pp Материал покрытияCoating material Толщина слоев покрытия (нижний-верхний), мкмThe thickness of the coating layers (lower-upper), microns H_µ, ГПаH _µ , GPa К₀ K ₀ Стойкость, минResistance, min ПримечаниеNote 1one 22 33 4four 55 66 77 Обрабатываемый материал - 5ХНМ, V=157 м/мин, S=0,25 мм/об, t=1 ммThe processed material - 5XNM, V = 157 m / min, S = 0.25 mm / rev, t = 1 mm 1one TiNTiN 66 21,221,2 0,700.70 3838 АналогAnalogue 22 TiAlN - TiAlZrNTiAlN - TiAlZrN 2-42-4 36,136.1 0,330.33 117117 ПрототипPrototype 33 TiCrN - TiCrMoNTiCrN - TiCrMoN 3-33-3 37,037.0 0,310.31 127127 В соответствии с формулойAccording to the formula 4four TiZrN - TiZrMoNTiZrN - TiZrMoN 3-33-3 36,936.9 0,320.32 138138 55 TiNbN - TiNbMoNTiNbN - TiNbMoN 3-33-3 36,536.5 0,320.32 131131 66 TiAlN - TiAlMoNTiAlN - TiAlMoN 3-33-3 37,037.0 0,300.30 136136 77 TiSiN - TiSiMoNTiSiN - TiSiMoN 3-33-3 36,936.9 0,310.31 137137 88 TiFeN - TiFeMoNTiFeN - TiFeMoN 3-33-3 36,336.3 0,290.29 125125

Продолжение табл.Continuation of the table. 1one 22 33 4four 55 66 77 99 TiCrN - TiCrMoNTiCrN - TiCrMoN 4-24-2 35,635.6 0,350.35 110110 Получены с отклонениями толщиныReceived with thickness deviations 1010 TiZrN - TiZrMoNTiZrN - TiZrMoN 4-24-2 36,036.0 0,370.37 112112 11eleven TiNbN - TiNbMoNTiNbN - TiNbMoN 4-24-2 34,334.3 0,400.40 102102 1212 TiAlN - TiAlMoNTiAlN - TiAlMoN 4-24-2 35,635.6 0,350.35 115115 1313 TiSiN - TiSiMoNTiSiN - TiSiMoN 4-24-2 36,036.0 0,370.37 114114 14fourteen TiFeN - TiFeMoNTiFeN - TiFeMoN 4-24-2 34,334.3 0,400.40 113113 15fifteen TiCrN - TiCrMoNTiCrN - TiCrMoN 3-33-3 36,236,2 0,380.38 118118 При одинаковом давленииAt the same pressure 1616 TiZrN - TiZrMoNTiZrN - TiZrMoN 3-33-3 35,835.8 0,360.36 120120 1717 TiNbN - TiNbMoNTiNbN - TiNbMoN 3-33-3 36,236,2 0,370.37 118118 18eighteen TiAlN - TiAlMoNTiAlN - TiAlMoN 3-33-3 36,236,2 0,380.38 118118 1919 TiSiN - TiSiMoNTiSiN - TiSiMoN 3-33-3 35,835.8 0,360.36 120120 20twenty TiFeN - TiFeMoNTiFeN - TiFeMoN 3-33-3 36,236,2 0,370.37 118118 2121 TiCrN - TiCrMoNTiCrN - TiCrMoN 3-33-3 36,036.0 0,410.41 110110 При одинаковой температуреAt the same temperature 2222 TiZrN - TiZrMoNTiZrN - TiZrMoN 3-33-3 36,036.0 0,420.42 113113 2323 TiNbN - TiNbMoNTiNbN - TiNbMoN 3-33-3 35,935.9 0,450.45 120120 2424 TiAlN - TiAlMoNTiAlN - TiAlMoN 3-33-3 36,036.0 0,410.41 110110 2525 TiSiN - TiSiMoNTiSiN - TiSiMoN 3-33-3 36,036.0 0,420.42 113113 2626 TiFeN - TiFeMoNTiFeN - TiFeMoN 3-33-3 35,935.9 0,450.45 120120

1. H_µ - микротвердость, ГПа (по Виккерсу).1. H _µ - microhardness, GPa (according to Vickers).

2. K₀ - коэффициент отслоения, уменьшение величины которого свидетельствует о росте прочности сцепления с инструментальной основой.2. K ₀ - peeling coefficient, a decrease in the value of which indicates an increase in adhesion to the tool base.

Как видно из приведенных в табл. данных, стойкость пластин, обработанных по предлагаемому способу, выше стойкости пластин, обработанных по способу-прототипу, на 7-18%. При этом пп.9-14 иллюстрируют, что при нарушении требований по назначению толщин слоев стойкость пластин снижается. В пп.15-20 показано, что в случае применения покрытий со слоями, осажденными при одинаковом давлении газа, стойкость также снижается. В пп.21-26 показано, что в случае применения покрытий со слоями, осажденными при одинаковой температуре конденсации, стойкость также снижается.As can be seen from the table. data, the resistance of the plates processed by the proposed method is higher than the resistance of the plates processed by the prototype method by 7-18%. Moreover, paragraphs 9-14 illustrate that in case of violation of the requirements for the appointment of layer thicknesses, the resistance of the plates decreases. In paragraphs 15-20 it is shown that in the case of coatings with layers deposited at the same gas pressure, the resistance also decreases. In paragraphs.21-26 it is shown that in the case of coatings with layers deposited at the same condensation temperature, the resistance also decreases.

Claims (2)

1. Способ получения многослойного покрытия для режущего инструмента, включающий вакуумно-плазменное нанесение двухслойного покрытия, отличающийся тем, что в качестве нижнего слоя при давлении азота в камере установки 7,5·10^-4 Па и температуре 600°С наносят нитрид титана и кремния или нитрид титана и хрома, или нитрид титана и ниобия, или нитрид титана и алюминия, или нитрид титана и железа, или нитрид титана и циркония, а в качестве верхнего слоя при давлении азота в камере установки 4,3·10^-3 Па и температуре 500°С наносят такой же нитрид, легированный молибденом.1. A method of obtaining a multilayer coating for a cutting tool, including vacuum-plasma deposition of a two-layer coating, characterized in that titanium and silicon nitride are applied as a lower layer at a nitrogen pressure in the chamber of the apparatus 7.5 · 10 ^-4 Pa and a temperature of 600 ° C. or titanium and chromium nitride, or titanium and niobium nitride, or titanium and aluminum nitride, or titanium and iron nitride, or titanium and zirconium nitride, and as the upper layer at a nitrogen pressure in the installation chamber of 4.3 · 10 ^-3 Pa and at a temperature of 500 ° C the same nitride is applied, alloyed first molybdenum. 2. Способ по п.1, отличающийся тем, что в двухслойном покрытии наносят нижний слой толщиной 40-50% от общей толщины покрытия, а общая толщина покрытия составляет 5-8 мкм. 2. The method according to claim 1, characterized in that in the two-layer coating, a lower layer is applied with a thickness of 40-50% of the total coating thickness, and the total coating thickness is 5-8 microns.