RU2353637C1 - Roadway marking paint - Google Patents

Abstract

FIELD: chemistry.

SUBSTANCE: invention relates to paint and varnish industry, in particular to production of paints for carriageway of automobile roads and aerodromes with asphalt, concrete or asphalt-concrete covering. Roadway marking paint contains copolymer of methyl methacrylate and H-butylmethacrylate - resin "Degalan LP 64/12" as acryl film-forming agent, contains as calcite filler finely-crashed white marble Omicarb and micronised kalidit filler MK and additionally contains fractioned microbarite Mirabi, plasticiser- clorparaffin "ХП"-470, organic solvent - toluol and ethyl acetate, pigment - titanium dioxide, thickener - organic derivative of montmorillonite Bentone SD-2, dispersant - mixture of natural phospholipids Soya lecithin, anti-sedimentation preparation - 20% solution of organic compound in xylol "М-П-А-2000Х" with claimed component ratio.

EFFECT: obtaining paint for roadway marking with white colour brightness coefficient 80-85% preserving values of other characteristics at the same level.

2 tbl, 11 ex

Description

Изобретение относится к лакокрасочной промышленности, в частности к производству красок для проезжей части автомобильных дорог и аэродромов с асфальтовым, бетонным или асфальтобетонным покрытием.The invention relates to the paint and varnish industry, in particular to the production of paints for the carriageway of roads and airfields with asphalt, concrete or asphalt concrete pavement.

Наиболее близким техническим решением по совокупности существенных признаков и достигаемому результату к изобретению является «Краска дорожная разметочная» по патенту РФ №2267507, МПК C09D 133/04, содержащая, мас.ч.:The closest technical solution for the combination of essential features and the achieved result for the invention is "Road marking paint" according to the patent of the Russian Federation No. 2267507, IPC C09D 133/04, containing, by weight:

Акриловый пленкообразователь:Acrylic film former:   48-52%-ный раствор сополимера стирола и бутилакрилата в смеси толуола и бутилацетата «Акролен-2»48-52% solution of styrene-butyl acrylate copolymer in a mixture of toluene and Acrolene-2 butyl acetate 22-2822-28 Наполнитель:Filler:   Микромрамор фракционированныйFractionated micromarble 36-4336-43 Оксигидроксид алюминия «Прокаль»Aluminum oxyhydroxide "Procal" 10-1410-14 Пластификатор:Softener:   Хлорпарафин ХП - 470Chloroparaffin HP - 470 1-31-3 Органический растворитель:Organic solvent:   Смесь толуола и этилацетата в отношении 2,4:1A mixture of toluene and ethyl acetate in the ratio of 2.4: 1 7-167-16 Пигмент:Pigment:   Диоксид титанаTitanium dioxide 7-137-13 Загуститель:Thickener:   Органическое производное монтмориллонита «Бентоне SD-2»Bentone SD-2 Organic Montmorillonite Derivative 0,2-0,80.2-0.8 Диспергатор:Dispersant:   Смесь натуральных фосфолипидов «Соя лецитин «Nalec 10-F»A mixture of natural phospholipids "Soya lecithin" Nalec 10-F " 0,2-0,50.2-0.5 Противоседиментационное средство:Anti-sedimentation agent:   20%-ный раствор органического соединения в ксилоле «М-П-А 2000Х»20% solution of the organic compound in xylene "M-P-A 2000X" 0,1-0,30.1-0.3

Краска может дополнительно содержать модифицирующую добавку 45-60%-ный раствор линейного термопластичного полиуретана на основе политетраметиленгликоля и толуилендиизоционата в бутилацетате до 5 мас.ч.The paint may additionally contain a modifying additive 45-60% solution of linear thermoplastic polyurethane based on polytetramethylene glycol and toluene diisocyanate in butyl acetate up to 5 parts by weight

Недостатком известной краски является низкий коэффициент яркости покрытия краски белого цвета 60%.A disadvantage of the known paint is the low brightness coefficient of the coating of white paint 60%.

Задачей изобретения является создание краски дорожной разметочной с повышенным коэффициентом яркости покрытия краски белого цвета при сохранении значений остальных показателей на том же уровне.The objective of the invention is the creation of road marking paint with a high brightness coefficient of the coating of white paint while maintaining the values of the remaining indicators at the same level.

Поставленная задача решается за счет того, что краска дорожная разметочная, включающая акриловый пленкообразователь, кальцитовый наполнитель, пластификатор - хлорпарафин ХП - 470, органический растворитель - толуол и этилацетат, пигмент - диоксид титана, загуститель - органическое производное монтмориллонита «Бентоне SD-2», диспергатор - смесь натуральных фосфолипидов "Соя лецитин, противоседиментационное средство - 20%-ный раствор органического соединения в ксилоле «М-П-А 2000Х», в качестве акрилового пленкообразователя она содержит сополимер метилметакрилата И-бутилметакрилата смола «Дегалан LP 64/12», а в качестве кальцитового наполнителя содержит тонкоизмельченный белый мрамор «Омикарб» и микронизированный кальцитовый наполнитель «МК» и дополнительно содержит микробарит фракционированный «Мираби», при следующем соотношении компонентов, мас.ч.:The problem is solved due to the fact that the road marking paint, including an acrylic film former, a calcite filler, a plasticizer is chloroparaffin XP-470, an organic solvent is toluene and ethyl acetate, a pigment is titanium dioxide, a thickener is an organic derivative of Bentone SD-2 montmorillonite, dispersant - a mixture of natural phospholipids "Soya lecithin, anti-sedimentation agent - 20% solution of the organic compound in xylene" M-P-A 2000X ", it contains a copolymer as an acrylic film former methyl methacrylate I-butyl methacrylate resin "Degalan LP 64/12", and as a calcite filler contains finely ground white marble "Omicarb" and micronized calcite filler "MK" and additionally contains fractionated microbarite "Mirabi", in the following ratio, wt.h. :

Сополимер метилметакрилата и Н-бутилметакрилата
смола «Дегалан LP 64/12»A copolymer of methyl methacrylate and N-butyl methacrylate
resin "Degalan LP 64/12" 12-1512-15 Указанный кальцитовый наполнительSpecified Calcite Filler 35-5035-50 Микробарит фракционированный «Мираби»Fractionated microbarite "Mirabi" 10-1510-15 Хлорпарафин ХП-470Chloroparaffin HP-470 2,0-3,52.0-3.5 ТолуолToluene 20-2520-25 ЭтилацетатEthyl acetate 3-53-5 Диоксид титанаTitanium dioxide 10-1310-13 Органическое производное монтмориллонита «Бентоне SD-2»Bentone SD-2 Organic Montmorillonite Derivative 0,1-0,20.1-0.2 Смесь натуральных фосфолипидов «Соя лецитин»A mixture of natural phospholipids "Soya lecithin" 0,2-0,50.2-0.5 20%-ный раствор органического соединения в ксилоле «М-П-А 2000Х»20% solution of the organic compound in xylene "M-P-A 2000X" 0,1-0,30.1-0.3

В краске дорожной разметочной в качестве акрилового пленкообразователя используется сополимер метилметакрилата и Н-бутилметакрилата - смола «Дегалан LP 64/12» (лист спецификации фирмы Degussa, Германия).In the road marking paint, a copolymer of methyl methacrylate and N-butyl methacrylate - Degalan LP 64/12 resin (specification sheet from Degussa, Germany) is used as an acrylic film former.

Физико-механические характеристикиPhysical and mechanical characteristics

Внешний видAppearance ГранулыGranules   белого цветаwhite color Молекулярный весMolecular weight 60000 г/мол60,000 g / mol Кислотное числоAcid number 8 мгКОН/г8 mgKOH / g Динамическая вязкость (40%-ного раствора в метилэтилкетоне)Dynamic viscosity (40% solution in methyl ethyl ketone) 180 МПас180 MPas ПлотностьDensity 1,08 г/см³ 1.08 g / cm ³ Насыпная плотностьBulk density 650 г/л650 g / l

В качестве кальцитового наполнителя используются:As calcite filler are used:

Тонкоизмельченный белый мрамор высокой чистоты «Омикарб» марок: «Омикарб 2-GU, 5-GU, 5-UR, 15-GU» (Приложение: лист спецификации) со следующими физико-механическими характеристиками:Finely ground white high-purity marble “Omicarb” grades: “Omicarb 2-GU, 5-GU, 5-UR, 15-GU” (Appendix: specification sheet) with the following physical and mechanical characteristics:

Физико-механические характеристики Physical and mechanical characteristics

Химический состав СаСо₃ The chemical composition of CaCO ₃ >98%> 98% Fe₂O₃ Fe ₂ O ₃ <0,15%<0.15% Остаток, не растворимый в HClHCl Insoluble Residue <2,0%<2.0% ПлотностьDensity 2,7 г/см³ 2.7 g / cm ³ Показатель преломленияRefractive index 1,591,59 Твердость по МоосуMohs hardness 33 Средний размер частицAverage particle size 2,5-27 мкм2.5-27 microns БелизнаWhite 94,5-96,5%94.5-96.5% Показатель рНPH value 99 МаслоемкостьOil consumption 13-19 г/100 г13-19 g / 100 g

Микронизированный кальцитовый наполнитель МК-10 и МК-40:Micronized calcite filler MK-10 and MK-40:

Физико-механические характеристикиPhysical and mechanical characteristics МК-10MK-10 МК-40MK-40 Химический состав, % Chemical composition, % СаСо₃, не менееCaCO ₃ , not less 9797 9797   MgO, не болееMgO, no more 0,150.15 0,150.15   SiO₂, не болееSiO ₂ , no more 0,150.15 0,150.15   Fe₂О₃+Al₂О₃, не болееFe ₂ About ₃ + Al ₂ About ₃ , no more 0,120.12 0,120.12 Массовая доля летучих веществ, % не болееMass fraction of volatiles,% no more 0,20.2 0,20.2 Показатель рНPH value 8-98-9 8-98-9 Количество частиц размером не менее 5 мкмNumber of particles no less than 5 microns in size 7070 2525 Показатель белизны, условных единицIndicator of whiteness, conventional units 9494 9494

Микробарит фракционированный «Мибари» марок «Мибари» 15-96, 10-96, 05-96, 01-96, 15-98, 10-98, 05-98, 03-98 по ТУ 1769-002-40705684-2001 со следующими физико-механическими характеристиками (приложение: лист спецификации):Microbarite fractionated "Mibari" of the Mibari grades 15-96, 10-96, 05-96, 01-96, 15-98, 10-98, 05-98, 03-98 according to TU 1769-002-40705684-2001 with the following physical and mechanical characteristics (Appendix: specification sheet):

Химический составChemical composition

BaSO₄ Baso ₄ 97-99%97-99% СаСо₃ CaCO ₃ 0.2-0.5%0.2-0.5% Fe₂О₃ Fe ₂ About ₃ 0.04-0.1%0.04-0.1% SiO₂ SiO ₂ 0.5-2.0%0.5-2.0% ПлотностьDensity 4,3 г/см³ 4.3 g / cm ³ Твердость по МоосуMohs hardness 33 Показатель рНPH value 8-98-9 БелизнаWhite 97,5-98%97.5-98% Средний размер частицAverage particle size 3-15 мкм3-15 microns МаслоемкостьOil consumption 7-15 г/100 г7-15 g / 100 g Количество частиц менее 2 мкмNumber of particles less than 2 microns 30%thirty% Насыпная плотностьBulk density 1,2 г/л1.2 g / l ЯркостьBrightness 96%96%

В качестве пигмента в краске дорожной разметочной используется: диоксид титана CR-02 по ТУ 6-10-01650-92; диоксид титана «Кронос 2190» и «Кронос 2310» (приложение: лист спецификации).The following is used as a pigment in road marking paint: titanium dioxide CR-02 according to TU 6-10-01650-92; titanium dioxide "Kronos 2190" and "Kronos 2310" (Appendix: specification sheet).

Физико-механические характеристикиPhysical and mechanical characteristics

Физико-механические характеристикиPhysical and mechanical characteristics КроносKronos КроносKronos   21902190 23102310 Яркость белого лака, %The brightness of white varnish,% 97,397.3 98,298.2 Дисперсность по гриндометру, мкмGrindometer dispersion, microns 6,86.8 6,86.8 Показатель рНPH value 7,87.8 7,97.9 Содержание рутильной формы, %The content of the rutile form,% 98,998.9 99,999.9

Диоксид титана, обработанный смесью диоксида циркония и оксида алюминия «Тронокс 828» (приложение: лист спецификации)Titanium dioxide treated with a mixture of zirconia and alumina "Tronox 828" (Appendix: specification sheet)

Физико-механические характеристикиPhysical and mechanical characteristics

Содержание TiO₂ TiO ₂ Content 95%95% ПлотностьDensity 4.1 г/см³ 4.1 g / cm ³ МаслоемкостьOil consumption 18 г/100 г18 g / 100 g Показатель рНPH value 7,57.5 Средний размер частицAverage particle size 0,19 мкм0.19 μm

В качестве пластификатора используется хлорпарафин ХП-470 по ТУ 6-01-16-90.Chloroparaffin HP-470 according to TU 6-01-16-90 is used as a plasticizer.

В качестве органических растворителей используется толуол по ГОСТ 5789-78, этилацетат по ГОСТ 8981-78.Toluene according to GOST 5789-78, ethyl acetate according to GOST 8981-78 are used as organic solvents.

В качестве загустителя используется органическое производное монтмориллонита «Бентоне SD-2», представляющего собой реологическую присадку на основе органических модификаций слоистых силикатов (приложение: лист спецификации фирмы «Реокс», «ИНК» Германия).As a thickener, the Bentone SD-2 organic montmorillonite derivative is used, which is a rheological additive based on organic modifications of layered silicates (Appendix: Reox, INK Germany specification sheet).

СоставStructure Органическое производное монтмориллонитаMontmorillonite Organic Derivative ЦветColor Слабая кремовая окраскаLight cream color Внешний видAppearance Тонкодисперсный порошокFine powder Размер частиц (в дисперсном виде)Particle size (dispersed) >1 мкм> 1 μm ПлотностьDensity 1,62 г/см³ 1.62 g / cm ³

В качестве диспергатора краска содержит смесь натуральных фосфолипидов «Соя лецитин».As a dispersant, the paint contains a mixture of natural soya lecithin phospholipids.

Соя лецитин «Nalec 10-F» (приложение: лист спецификации фирмы BYK - CHEMIE, Германия)Soya Lecithin “Nalec 10-F” (Appendix: BYK Specification Sheet - CHEMIE, Germany)

Физико-механические характеристики:Physico-mechanical characteristics:

СоставStructure Смесь натуральных фосфолипидовA mixture of natural phospholipids Содержание маслаOil content 38%38% ВязкостьViscosity 125 с125 s Кислотное числоAcid number 30 мгКОН/г30 mgKOH / g Общее бактериальное числоTotal bacterial number 5000 гр5000 gr Содержание нерастворимых вInsoluble in 62%62% ацетоне веществacetone substances  

Соя лецитин «АДЛЕК» (приложение: информационный листок)Soya lecithin "ADLEK" (Appendix: information leaflet)

Физико-механические характеристики:Physico-mechanical characteristics:

СоставStructure Смесь натуральных фосфолипидовA mixture of natural phospholipids Вязкость при 25°СViscosity at 25 ° C 10 Пас10 Pass Кислотное числоAcid number 28 мг КОН/г28 mg KOH / g Пероксидное числоPeroxide number 1one Общее число микроорганизмовTotal number of microorganisms 5000 гр5000 gr

В качестве противоседиментационного средства используется 20%-ный раствор эмульсионной полиэтиленовой смолы в ксилоле «М-П-А 2000Х» (приложение: лист спецификации фирмы «RHEOX Europe NV» Бельгия и патент №4975119, США).As an anti-sedimentation agent, a 20% solution of emulsion polyethylene resin in xylene "M-P-A 2000X" is used (Appendix: RHEOX Europe NV Belgium specification sheet and patent No. 4975119, USA).

Физико-механические характеристики:Physico-mechanical characteristics:

СоставStructure 20%-ный раствор эмульсионной полиэтиленовой смолы в ксилоле20% solution of emulsion polyethylene resin in xylene ФормаThe form жидкостьliquid ЦветColor белыйwhite Плотность при 20°СDensity at 20 ° C 0,88 г/см³ 0.88 g / cm ³ Температура кипенияBoiling temperature 137°С137 ° C Растворимость в водеSolubility in water не растворяетсяnot soluble Давление пара при 20°СSteam pressure at 20 ° C 5 мбар5 mbar

Краска дорожная разметочная готовится по следующей технологии.Road marking paint is prepared according to the following technology.

В диссольвер без обогрева загружают органический растворитель, пластификатор, загуститель, диспергатор, акриловый пленкообразователь, пигменты, наполнитель, противоседиментационное средство и перемешивают 1,5-2,0 часа. Полученную композицию диспергируют в бисерной мельнице.An organic solvent, plasticizer, thickener, dispersant, acrylic film former, pigments, filler, anti-sedimentation agent are loaded into a dissolver without heating and mixed for 1.5-2.0 hours. The resulting composition is dispersed in a bead mill.

Готовая краска наносится машинами для разметки дорог или краскораспылителем, валиком или кистью.Ready-made paint is applied by road marking machines or by a spray gun, roller or brush.

В таблице 1 приведены примеры выполнения компонентного состава краски дорожной разметочной.Table 1 shows examples of the implementation of the component composition of road marking paint.

Испытания свойств краски и покрытий из нее проводятся по стандартным методикам.Tests of the properties of paint and coatings from it are carried out according to standard methods.

Коэффициент яркости покрытия краски белого цвета по прототипу определен дополнительно по ГОСТ Р51256-99.The brightness coefficient of the coating of white paint according to the prototype is additionally determined according to GOST R51256-99.

Полученные результаты испытаний предлагаемой краски и покрытий в сравнении с прототипом приведены в таблице 2.The obtained test results of the proposed paint and coatings in comparison with the prototype are shown in table 2.

Из таблицы 2 видно, что краска дорожная разметочная по изобретению имеет коэффициент яркости белого цвета 80-85% при сохранении значений остальных показателей на том же уровне.From table 2 it is seen that the road marking paint according to the invention has a white brightness factor of 80-85% while maintaining the values of the remaining indicators at the same level.

Таблица 1Table 1 Наименование компонентовName of components По прототипу, мас.ч.According to the prototype, parts by weight По примерам, мас.ч.By examples, parts by weight 1one 22 33 4four 55 66 77 88 99 1010 11eleven Акриловый пленкообразовательAcrylic film former                         48-52%-ный раствор сополимера стирола и бутилакрилата в смеси толуола и бутилацетата «Акролен-2»48-52% solution of styrene-butyl acrylate copolymer in a mixture of toluene and Acrolene-2 butyl acetate 22-2822-28 -- -- -- -- -- -- -- -- -- -- -- Сополимер метилметакрилата и Н-бутилметакрилата смола «дегалан LP64/12»The copolymer of methyl methacrylate and N-butyl methacrylate resin "degalan LP64 / 12" -- 1212 1212 1313 14fourteen 15fifteen 15fifteen 1313 1313 1212 14fourteen 15fifteen Наполнитель:Filler:                         Микромрамор фракционированныйFractionated micromarble 36-4336-43 -- -- -- -- -- -- -- -- -- -- -- Оксигидроксид алюминия «Прокаль»Aluminum oxyhydroxide "Procal" 10-1410-14 -- -- -- -- -- -- -- -- -- -- -- Тонкоизмельченный белый мрамор «Омикарб»Fine White Omicarb Marble -- 20twenty 20twenty 2121 2222 2323 2323 2424 2323 2323 2424 2525 Микробарит фракционированный «Мибари»Fractionated microbarite "Mibari" -- 1010 11eleven 1212 1313 14fourteen 14fourteen 1313 1212 14fourteen 15fifteen 15fifteen Микронизированный кальцитовый наполнитель «МК»Micronized Calcite Filler "MK" -- 15fifteen 1616 18eighteen 20twenty 2121 2222 2323 2424 2424 2525 2525 Пластификатор:Softener:                         Хлорпарафин ХП-470Chloroparaffin HP-470 1-31-3 2,02.0 2,22.2 2,52.5 2,72.7 3,03.0 3,13,1 3,33.3 3,43.4 3,53,5 3,53,5 3,53,5 Органический растворитель:Organic solvent:                         Смесь толуола и этилацетата в отношении 2,4:1A mixture of toluene and ethyl acetate in the ratio of 2.4: 1 7-167-16 -- -- -- -- -- -- -- -- -- -- -- ЭтилацетатEthyl acetate -- 3,03.0 3,33.3 3,53,5 3,73,7 3,73,7 3,73,7 4,04.0 4,54,5 5,05,0 5,05,0 5,05,0 ТолуолToluene -- 20twenty 20twenty 2121 2525 2525 2222 2323 2424 2525 2525 2525 Пигмент:Pigment:                         Диоксид титанаTitanium dioxide 7-137-13 1010 1010 11eleven 1212 1212 1313 1313 1212 11eleven 1010 1313 Загуститель:Thickener:                         Органическое производное монтмориллонита «Бентоне SD-2»Bentone SD-2 Organic Montmorillonite Derivative 0,2-0,80.2-0.8 0,100.10 0,110.11 0,120.12 0,140.14 0,150.15 0,160.16 0,170.17 0,180.18 0,190.19 0,190.19 0,200.20 Диспергатор:Dispersant:                         Смесь натуральных фосфолипидов «Соя лецитин»A mixture of natural phospholipids "Soya lecithin" 0,2-0,50.2-0.5 0,20.2 0,20.2 0,30.3 0,50.5 0,50.5 0,40.4 0,40.4 0,30.3 0,40.4 0,50.5 0,50.5 Противоседиментационное средство:Anti-sedimentation agent:                         20%-ный раствор эмульсионной полиэтиленовой смолы в ксилоле «М-П-А-2000Х»20% solution of emulsion polyethylene resin in xylene "M-P-A-2000X" 0,1-0,30.1-0.3 0,10.1 0,10.1 0,20.2 0,30.3 0,30.3 0,20.2 0,20.2 0,30.3 0,30.3 0,30.3 0,30.3

Таблица 2table 2 Наименование компонентовName of components По прототипуAccording to the prototype По примерамBy examples 1one 22 33 4four 55 66 77 88 99 1010 11eleven Цвет пленки краскиPaint film color белыйwhite белыйwhite белыйwhite белыйwhite белыйwhite белыйwhite белыйwhite белыйwhite белыйwhite белыйwhite белыйwhite белыйwhite Массовая доля нелетучих веществ, %Mass fraction of nonvolatile substances,% 68-7068-70 7070 7070 7070 7070 7070 7070 7070 7070 7070 7070 7070 Время высыхания до степени 3 при температуре 20±2°С, часDrying time to degree 3 at a temperature of 20 ± 2 ° C, hour 0,3-0,40.3-0.4 0,30.3 0,30.3 0,40.4 0,40.4 0,40.4 0,30.3 0,40.4 0,40.4 0,40.4 0,40.4 0,40.4 Условная вязкость по В3-246 при температуре 20±5°С при диаметре сопла 6 мм, сConditional viscosity according to B3-246 at a temperature of 20 ± 5 ° C with a nozzle diameter of 6 mm, s 57-7057-70 6060 6060 6565 6060 6565 6060 6565 6060 6565 6565 6565 Укрывистость высушенной пленки, г/см² Spreading rate of the dried film, g / cm ² 179-220179-220 180180 180180 185185 180180 185185 180180 180180 185185 190190 190190 185185 Адгезия пленки, баллыFilm adhesion, points 1one 1one 1one 1one 1one 1one 1one 1one 1one 1one 1one 1one Стойкость пленки к статическому воздействию жидкостей, час: водыResistance to static action of liquids, hour: water 184-210184-210 210210 210210 205205 205205 210210 205205 210210 210210 205205 210210 210210 3%-ного раствора хлористого натрия3% sodium chloride solution 184-210184-210 210210 205205 205205 205205 210210 205205 210210 210210 210210 205205 210210 Прочность пленки к абразивному износу (истирание песком), кг/мкмFilm abrasion resistance (abrasion by sand), kg / μm 2,2-3,02.2-3.0 2,52.5 2,72.7 2,62.6 2,82,8 2,92.9 2,52.5 2,62.6 2,52.5 2,52.5 2,72.7 2,72.7 Белизна, %White,% 91-9491-94 9191 9191 9191 9393 9393 9292 9191 9191 9393 9494 9494 Условная светостойкость покрытия, часConditional light fastness of the coating, hour 70-7270-72 7171 7171 7171 7171 7272 7272 7272 7171 7272 7272 7272 Прочность пленки при ударе, смFilm strength upon impact, cm 100one hundred 100one hundred 100one hundred 100one hundred 100one hundred 100one hundred 100one hundred 100one hundred 100one hundred 100one hundred 100one hundred 100one hundred Твердость пленки по маятниковому прибору типа М-3, усл. ед.The hardness of the film according to the pendulum device type M-3, conv. units 0,70-0,800.70-0.80 0,750.75 0,750.75 0,760.76 0,760.76 0,770.77 0,800.80 0,800.80 0,790.79 0,790.79 0,800.80 0,800.80 Коэффициент яркости покрытия краски белого цвета, %The brightness coefficient of the coating of white paint,% 6060 8080 8383 8282 8282 8383 8484 8484 8585 8585 8585 8585

Claims (1)

Краска дорожная разметочная, включающая акриловый пленкообразователь, кальцитовый наполнитель, пластификатор хлорпарафин ХП-470, органический растворитель - толуол и этилацетат, пигмент - диоксид титана, загуститель - органическое производное монтмориллонита «Бентоне SD-2», диспергатор - смесь натуральных фосфолипидов «Соя лецитин», противоседиментационное средство - 20%-ный раствор органического соединения в ксилоле «М-П-А-2000Х», отличающаяся тем, что в качестве акрилового пленкообразователя она содержит сополимер метилметакрилата и Н-бутилметакрилата смола «Дегалан LP 64/12», а в качестве кальцитового наполнителя содержит тонкоизмельченный белый мрамор «Омикарб» и микронизированный кальцитовый наполнитель «МК» и дополнительно содержит микробарит фракционированный «Мираби» при следующем соотношении компонентов, мас.ч:
Сополимер метилметакрилата и Н-бутилметакрилата   смола «Дегалан LP 64/12» 12-15 Указанный кальцитовый наполнитель 35-50 Микробарит фракционированный «Мираби» 10-15 Хлорпарафин ХП-470 2,0-3,5 Толуол 20-25 Этилацетат 3-5 Диоксид титана 10-13 Органическое производное монтмориллонита «Бентоне   SD-2» 0,1-0,2 Смесь натуральных фосфолипидов «Соя лецитин» 0,2-0,5 20%-ный раствор органического соединения в ксилоле   «М-П-А2000Х» 0,1-0,3 Road marking paint, which includes an acrylic film former, a calcite filler, a plasticizer, chlorine paraffin ХП-470, an organic solvent - toluene and ethyl acetate, a pigment - titanium dioxide, a thickener - an organic derivative of montmorillonite "Bentone SD-2", a dispersant - a mixture of natural phospholipids "Soy Leci , anti-sedimentation agent - a 20% solution of the organic compound in xylene "M-P-A-2000X", characterized in that it contains a copolymer of methyl methacrylate and H-butyl as an acrylic film former Ilgalacrylate resin Degalan LP 64/12, and as a calcite filler it contains finely ground white Omicarb marble and micronized calcite filler MK and additionally contains fractionated Mirabi microbarite in the following ratio, wt.h:
A copolymer of methyl methacrylate and N-butyl methacrylate resin "Degalan LP 64/12" 12-15 Specified Calcite Filler 35-50 Fractionated microbarite "Mirabi" 10-15 Chloroparaffin HP-470 2.0-3.5 Toluene 20-25 Ethyl acetate 3-5 Titanium dioxide 10-13 Bentone Organic Montmorillonite Derivative SD-2 " 0.1-0.2 A mixture of natural phospholipids "Soya lecithin" 0.2-0.5 20% solution of the organic compound in xylene M-P-A2000X 0.1-0.3