RU2337970C1 - Method of strengthening of leather fabric of fur half-finished product - Google Patents

Abstract

FIELD: items of personal use, clothes.

SUBSTANCE: invention concerns the fur industry and can be used in furriery-tailoring manufacture at manufacturing and repair of fur products. The method of strengthening of fur fabric leathers of a half-finished product is carried out by application and drying of a collagen-containing composition containing moist collagenic aggregation, a softener and a hardening agent. Thus the collagen-containing composition additionally contains cod-liver oil and castor oil. The composition is applied in two stages. The first stage of treatment is performed with a compound, in recalculation on a solid: collagenic aggregation 2%, glycerin 2.6-4%, oak extract 0.1%, cod-liver oil 0.2%, castor oil 0.2%, water - the rest. The second stage of treatment is performed with a compound, in recalculation on a solid: collagenic weight 6%, glycerin 7.8-12%, oak extract 0.3%, cod-liver oil 0.6%, castor oil of 0.6%, water - the rest. Drying of a fur half-finished product is performed after the first and the second application. The way allows to raise adhesion strength of body hair coat with a leather fabric, to increase useful area of a fur half-finished product due restoration of defective sites of leather fabrics and simultaneously to receive a detail with the zones differing by properties.

EFFECT: increase of adhesion strength of body hair coat with leather fabric, increase in useful area of a fur half-finished product.

2 cl, 1 dwg, 1 tbl, 2 ex

Description

Изобретение относится к меховой промышленности и может быть использовано в скорняжно-пошивочном производстве при изготовлении и ремонте меховых изделий.The invention relates to the fur industry and can be used in furrier-sewing production in the manufacture and repair of fur products.

Известен способ облагораживания кожевой ткани меховых изделий из низкозачетных шкур, при котором швы, полученные при сшивании деталей и ушивке дефектных мест кожевой ткани, прессуют, после чего наклеивают на них полоски ткани и прессуют швы вторично, а затем на кожевую ткань наносят пленкообразующие вещества, например поливинилхлоридную пленку (Патент СССР 147290, С14В 15/04).A known method of refinement of leather fabric of fur products from low-grade hides, in which the seams obtained by stitching parts and suturing of the defective places of the leather fabric are pressed, then strips of fabric are glued to them and the seams are pressed again, and then film-forming substances are applied to the leather fabric, for example polyvinyl chloride film (USSR Patent 147290, С14В 15/04).

Недостатками способа являются уменьшение полезной площади мехового полуфабриката и использование химических материалов, ухудшающих гигиенические свойства меха.The disadvantages of the method are the reduction of the useful area of the semi-finished fur product and the use of chemical materials that degrade the hygienic properties of the fur.

Известен способ изготовления объемных декоративных элементов в меховых изделиях нанесением коллагенсодержащей композиции на кожевую ткань меха и последующей сушкой (Патент РФ №2283350 от 18 сентября 2006 г.).A known method of manufacturing volumetric decorative elements in fur products by applying a collagen-containing composition to a leather fabric of fur and subsequent drying (RF Patent No. 2283350 of September 18, 2006).

Недостатком данного способа является то, что при нанесении коллагенсодержащей композиции на кожевую ткань меха не обеспечивается адгезионная прочность связи между слоями полученного комплексного материала, необходимая для устранения дефектов кожевой ткани, что приводит к сужению области применения коллагенсодержащей композиции.The disadvantage of this method is that when applying the collagen-containing composition to the skin fabric of the fur, the adhesive strength of the bonds between the layers of the obtained complex material is not provided, which is necessary to eliminate defects in the skin tissue, which leads to a narrowing of the scope of application of the collagen-containing composition.

Ближайшим аналогом предлагаемого способа (Патент РФ №2151534, А42С 1/00) является способ изготовления формованных изделий путем нанесения волокнистого материала на формозадающую поверхность и последующей сушки. В качестве волокнистого материала используют коллагенсодержащую композицию, включающую коллагеновую массу в пересчете на сухое вещество 3-8%, пластификатор 2,4-12%, дубовый экстракт 0,1-0,33% и воду.The closest analogue of the proposed method (RF Patent No. 2151534, A42C 1/00) is a method of manufacturing molded products by applying a fibrous material to a molding surface and subsequent drying. As a fibrous material, a collagen-containing composition is used, including the collagen mass in terms of dry matter 3-8%, plasticizer 2.4-12%, oak extract 0.1-0.33% and water.

Недостатки данного способа заключаются в следующем:The disadvantages of this method are as follows:

- недостаточная прочность связи волосяного покрова с кожевой тканью;- insufficient bond strength of the hairline with skin tissue;

- невозможность обеспечения нескольких зон с различными заданными свойствами в одном полуфабрикате или детали.- the impossibility of providing multiple zones with different desired properties in one semi-finished product or part.

Техническим результатом заявляемого изобретения является повышение прочности связи волосяного покрова с кожевой тканью, увеличение полезной площади мехового полуфабриката за счет восстановления дефектных участков кожевой ткани и возможность одновременного получения деталей с зонами, отличающимися по свойствам.The technical result of the claimed invention is to increase the bond strength of the hairline with the skin tissue, increase the useful area of the fur semi-finished product by restoring the defective areas of the skin tissue and the possibility of simultaneously obtaining parts with zones that differ in properties.

Данный результат достигается следующим образом. Укрепление кожевой ткани мехового полуфабриката путем нанесения и сушки коллагенсодержащей (КС) композиции, содержащей обводненную коллагеновую массу, пластификатор, дубитель, отличается тем, что коллагенсодержащая композиция дополнительно содержит рыбий жир и касторовое масло, которую наносят в две стадии, причем первую стадию обработки осуществляют составом, в пересчете на сухое вещество: коллагеновая масса 2%, глицерин 2,6-4%, дубовый экстракт 0,1%, рыбий жир 0,2%, касторовое масло 0,2%, вода - остальное; вторую стадию обработки осуществляют составом, в пересчете на сухое вещество: коллагеновая масса 6%, глицерин 7,8-12%, дубовый экстракт 0,3%, рыбий жир 0,6%, касторовое масло 0,6%, вода - остальное, а сушку проводят после первого и второго нанесения.This result is achieved as follows. Strengthening the skin tissue of a semi-finished fur product by applying and drying a collagen-containing (KS) composition containing an irrigated collagen mass, a plasticizer, a tanning agent, is characterized in that the collagen-containing composition additionally contains fish oil and castor oil, which is applied in two stages, the first stage of processing being carried out by the composition , in terms of dry matter: collagen mass 2%, glycerol 2.6-4%, oak extract 0.1%, fish oil 0.2%, castor oil 0.2%, water - the rest; the second stage of processing is carried out with the composition, in terms of dry matter: collagen mass 6%, glycerol 7.8-12%, oak extract 0.3%, fish oil 0.6%, castor oil 0.6%, water - the rest, and drying is carried out after the first and second application.

Вторую стадию обработки кожевой ткани мехового полуфабриката осуществляют фрагментарным нанесением композиции для получения полужестких и жестких зон в изделии (см. чертеж).The second stage of processing the leather fabric of the fur semi-finished product is carried out by fragmentary application of the composition to obtain semi-rigid and hard zones in the product (see drawing).

Способ осуществляют следующим образом.The method is as follows.

Пример 1. Кожевую ткань мехового полуфабриката ондатры увлажняют смесью воды с глицерином в пропорции 5:1. После увлажнения полуфабрикат складывают кожевой тканью внутрь для пролежки на 30 минут. Далее увлажненный полуфабрикат или детали скроя правят и закрепляют на деревянных рамах. На первой стадии обработки на кожевую ткань наносят коллагенсодержащую композицию состава, в пересчете на сухое вещество:Example 1. The skin tissue of a furry semi-finished muskrat is moistened with a mixture of water with glycerin in a ratio of 5: 1. After moisturizing, the semi-finished product is folded with leather cloth inward for sinking for 30 minutes. Next, the moistened semi-finished product or the details of the cut are corrected and fixed on wooden frames. At the first stage of processing, a collagen-containing composition is applied to the skin tissue, in terms of dry substance:

коллагеновая массаcollagen mass 2%2% глицеринglycerol 3,2%3.2% дубовый экстрактoak extract 0,1%0.1% рыбий жирfish fat 0,2%0.2% касторовое маслоCastor oil 0,2%0.2% водаwater остальноеrest

Наносят композицию равномерно по всей площади заданного участка с помощью специального устройства ракельного типа. В результате нанесения композиции с низким содержанием коллагеновой массы обеспечивается лучшая смачиваемость и проникновение субстрата. Первую стадию обработки мехового полуфабриката выполняют с целью упрочнения кожевой ткани меха и обеспечения адгезионной прочности полученного материала. Количество наносимой композиции равно 0,14 г/см². После нанесения композиции меховой полуфабрикат подвергают сушке. Сушка производится в сушильных камерах при температуре 50-55°С или при нормальной температуре. На второй стадии обработки композицию наносят для обеспечения большей толщины и прочности полученного комплексного материала следующим составом, в пересчете на сухое вещество:The composition is applied uniformly over the entire area of a given area using a special doctor blade type device. The application of a composition with a low content of collagen mass provides better wettability and penetration of the substrate. The first stage of processing the semi-finished fur product is performed with the aim of hardening the leather fabric of the fur and ensuring the adhesive strength of the obtained material. The amount of applied composition is 0.14 g / cm ² . After applying the composition, the semi-finished fur product is dried. Drying is carried out in drying chambers at a temperature of 50-55 ° C or at normal temperature. In the second stage of processing, the composition is applied to provide greater thickness and strength of the obtained complex material with the following composition, in terms of dry matter:

коллагеновая массаcollagen mass 6%6% глицеринglycerol 9,6%9.6% дубовый экстрактoak extract 0,3%0.3% рыбий жирfish fat 0,6%0.6% касторовое маслоCastor oil 0,6%0.6% водаwater остальноеrest

Для обеспечения одинакового количества коллагена на единицу площади композицию с величиной сухого остатка коллагена 6% наносят в количестве 0,12 г/см². Далее выполняют вторичную сушку для удаления дисперсионной среды. Вторую стадию обработки осуществляют для придания меховым полуфабрикатам требуемых физико-механических свойств. Результаты испытания представлены в таблице.To ensure the same amount of collagen per unit area, a composition with a dry collagen residue of 6% is applied in an amount of 0.12 g / cm ² . Next, secondary drying is performed to remove the dispersion medium. The second stage of processing is carried out to give the fur semi-finished products the required physical and mechanical properties. The test results are presented in the table.

Результаты испытания прочности связи волосяного покрова с кожевой тканью меха ондатрыTest results of the bond strength of the hairline with the skin tissue of the muskrat fur Вид материлаType of material Номер образцаSample Number Усилие при выдергивании волосяного покрова, Н/мм² The force when pulling the hairline, N / mm ² до нанесенияbefore application после нанесенияafter application 1one 22 33 4four меховой полуфабрикат + КСкомпозиция (2% с.о.к.) + КСкомпозиция (6% с.о.к.)semi-finished fur product + KS composition (2% s.o.s.) + KS composition (6% s.o.s.) 1one 4,14.1 8,18.1 22 2,42,4 6,86.8 33 3,23.2 5,55.5 СреднееAverage   3,23.2 6,86.8

Результаты испытания показали, что при нанесении коллагенсодержащей композиции по предлагаемому способу наблюдается повышение прочности связи волосяного покрова с кожевой тканью в два раза относительно образца до нанесения композиции.The test results showed that when applying a collagen-containing composition according to the proposed method, there is an increase in the bond strength of the hairline with skin tissue twice as much as the sample before applying the composition.

Пример 2. Вторую стадию обработки кожевой ткани мехового полуфабриката осуществляют нанесением композиции фрагментарно для получения зон с различными свойствами, в соответствии с предъявляемыми требованиями к изделию, например головной убор типа «кепи» (см. чертеж). Для получения жестких зон используют состав, в пересчете на сухое вещество: коллагеновая масса 6%, глицерин 7,8%, дубовый экстракт 0,3%, рыбий жир 0,6%, касторовое масло 0,6%, вода - остальное, а для получения полужестких зон используют состав, в пересчете на сухое вещество: коллагеновая масса 6%, глицерин 9,6%, дубовый экстракт 0,06%, рыбий жир 0,6%, касторовое масло 0,6%, вода - остальное, при этом количество наносимой композиции составляет от 0,16 г/см² до 0,24 г/см².Example 2. The second stage of processing leather fabric of a semi-finished fur product is carried out by applying the composition fragmentarily to obtain zones with different properties, in accordance with the requirements for the product, for example, a hat of the "cap" type (see drawing). To obtain hard zones, the composition is used, calculated on the dry matter: collagen mass 6%, glycerol 7.8%, oak extract 0.3%, fish oil 0.6%, castor oil 0.6%, water - the rest, and to obtain semi-rigid zones use the composition, in terms of dry matter: collagen mass 6%, glycerol 9.6%, oak extract 0.06%, fish oil 0.6%, castor oil 0.6%, water - the rest, with this amount of applied composition is from 0.16 g / cm ² to 0.24 g / cm ² .

Claims (2)

1. Способ укрепления кожевой ткани мехового полуфабриката путем нанесения и сушки коллагенсодержащей композиции, содержащей обводненную коллагеновую массу, пластификатор, дубитель, отличающийся тем, что коллагенсодержащая композиция дополнительно содержит рыбий жир и касторовое масло, которую наносят в две стадии, причем первую стадию обработки осуществляют составом, в пересчете на сухое вещество: коллагеновая масса 2%, глицерин 2,6-4%, дубовый экстракт 0,1%, рыбий жир 0,2%, касторовое масло 0,2%, вода - остальное; вторую стадию обработки осуществляют составом, в пересчете на сухое вещество: коллагеновая масса 6%, глицерин 7,8-12%, дубовый экстракт 0,3%, рыбий жир 0,6%, касторовое масло 0,6%, вода - остальное, а сушку проводят после первого и второго нанесений.1. A method of strengthening leather fabric of a semi-finished fur product by applying and drying a collagen-containing composition containing an irrigated collagen mass, a plasticizer, tanning agent, characterized in that the collagen-containing composition additionally contains fish oil and castor oil, which is applied in two stages, the first stage of processing being carried out by the composition , in terms of dry matter: collagen mass 2%, glycerol 2.6-4%, oak extract 0.1%, fish oil 0.2%, castor oil 0.2%, water - the rest; the second stage of processing is carried out with the composition, in terms of dry matter: collagen mass 6%, glycerol 7.8-12%, oak extract 0.3%, fish oil 0.6%, castor oil 0.6%, water - the rest, and drying is carried out after the first and second application. 2. Способ по п.1, отличающийся тем, что вторую стадию обработки кожевой ткани мехового полуфабриката осуществляют нанесением композиции фрагментарно для получения в изделии жестких и полужестких зон.2. The method according to claim 1, characterized in that the second stage of processing the leather fabric of the fur semi-finished product is carried out by applying the composition fragmentarily to obtain hard and semi-rigid zones in the product.