RU2183516C1 - Method for preparing hot rolled steel strips to etching - Google Patents
Method for preparing hot rolled steel strips to etching Download PDFInfo
- Publication number
- RU2183516C1 RU2183516C1 RU2001117596/02A RU2001117596A RU2183516C1 RU 2183516 C1 RU2183516 C1 RU 2183516C1 RU 2001117596/02 A RU2001117596/02 A RU 2001117596/02A RU 2001117596 A RU2001117596 A RU 2001117596A RU 2183516 C1 RU2183516 C1 RU 2183516C1
- Authority
- RU
- Russia
- Prior art keywords
- rolls
- etching
- tonnage
- strip
- rolled
- Prior art date
Abstract
Description
Изобретение относится к обработке металлов давлением и может быть использовано в производстве холоднокатаной полосовой стали при подготовке подката к травлению. The invention relates to the processing of metals by pressure and can be used in the production of cold-rolled strip steel in the preparation of rolled for pickling.
Подкатом (заготовкой) для производства холоднокатаной стали служат горячекатаные полосы. Необходимой операцией перед холодной прокаткой таких полос является удаление с их поверхности окалины, как правило, путем травления в серно- или соляно-кислотных растворах на специализированных непрерывных травильных агрегатах (НТА). Для ускорения процесса травления широко используется предварительное разрушение окалины, например, за счет обжатия небольшой величины валками дрессировочной клети, установленной на входе в НТА (см. , например, справочник под ред. В.И.Зюзина и А.В.Третьякова "Технология прокатного производства", кн.2. М.: Металлургия, 1991, с. 636), в результате чего слой окалины дробится и частично осыпается с движущейся полосы до входа в ванны, что увеличивает скорость травления в 1,5-2 раза. Hot rolled strips serve as a tack (blank) for the production of cold rolled steel. A necessary operation before the cold rolling of such strips is the removal of scale from their surface, as a rule, by etching in sulfuric or hydrochloric acid solutions on specialized continuous etching units (NTA). To accelerate the etching process, preliminary destruction of scale is widely used, for example, by compressing a small size with rolls of a training stand installed at the entrance to the NTA (see, for example, the manual edited by V.I. Zyuzin and A.V. Tretyakov "Rolling technology production ", book 2. M .: Metallurgy, 1991, p. 636), as a result, the scale layer is crushed and partially crumbles from the moving strip to the entrance to the bathtubs, which increases the etching rate by 1.5-2 times.
Дрессировка, т.е. холодная прокатка с относительным обжатием до 5...8%, осуществляется в насеченных валках с развитой микрогеометрией (см. книгу В. К. Белосевича и Н.П.Нетесова "Совершенствование процесса холодной прокатки", М. : "Металлургия", 1971, с. 218). При этом микрогеометрия поверхности характеризуется параметрами шероховатости Rz (средняя высота неровностей профиля по десяти точкам) и S (шаг местных выступов). Указанные параметры шероховатости определяются в пределах базовой длины l (обычно принимают l= 0,8 мм) в соответствие с ГОСТ 2789-73. Кроме того, бочки валков имеют определенную твердость (обычно - в единицах по Шору).Training, i.e. cold rolling with a relative compression of up to 5 ... 8% is carried out in notched rolls with developed microgeometry (see the book “Improving the Cold Rolling Process” by V. K. Belosevich and N. P. Netesov, M.: Metallurgy, 1971 , p. 218). In this case, surface microgeometry is characterized by roughness parameters R z (average height of profile irregularities at ten points) and S (step of local protrusions). The indicated roughness parameters are determined within the base length l (usually take l = 0.8 mm) in accordance with GOST 2789-73. In addition, roll barrels have a certain hardness (usually in Shore units).
Известен процесс удаления окалины с непрерывно движущейся полосы путем перегиба ее с помощью специального устройства с электроприводом (см. пат. США 3393434, кл. 29-81 от 23.07.68). Известен также способ удаления окалины с металлических листов рабочими роликами, на которых укреплены абразивные пластины, совершающими касательное движение (см. пат. США 3888048, кл. В 23 В 7/12 от 10.06.75). Недостатком известных способов удаления окалины является невозможность их применения для быстро движущейся широкой (до 2 м) полосы относительно большой (до 4 мм) толщины, а также при наличии у горячекатаной полосы дефекта "вкатанная окалина", который может привести описанные устройства к поломке. The known process of removing scale from a continuously moving strip by bending it using a special device with an electric drive (see US Pat. US 3393434, CL 29-81 from 07.23.68). There is also a known method of removing scale from metal sheets by working rollers on which abrasive plates are mounted that perform tangential movement (see US Pat. US 3888048, class B 23 V 7/12 of 06/10/75). A disadvantage of the known methods of descaling is the impossibility of their use for a rapidly moving wide (up to 2 m) strip of relatively large (up to 4 mm) thickness, as well as in the case of a hot rolled strip defect "rolled scale", which can lead to the described devices to breakage.
Наиболее близким аналогом к заявляемому объекту является технология подготовки к травлению горячекатаной полосовой стали, описанная в книге П.И. Полухина и др. "Прокатное производство", М.: "Металлургия", 1982, с. 485-487. The closest analogue to the claimed object is the technology of preparation for pickling hot rolled strip steel, described in the book P.I. Polukhina and others. "Rolling production", M .: "Metallurgy", 1982, p. 485-487.
Эта технология включает пропускание полосы перед травильными ваннами через роликовый окалиноломатель и дрессировочную клеть и характеризуется обжатием полосы в этой клети, лежащим в пределах 3...8%, что не только дополнительно разрушает окалину, но и устраняет изломы полосы после ее разматывания. Недостатком такой технологии является большой верхний предел относительного обжатия, что приводит к ускоренному износу валков (сглаживанию микронеровностей) и, как следствие, замедлению процесса травления и возможности появления при этом неисправимого и недопустимого при холодной прокатке дефекта "недотрав". This technology involves passing the strip in front of the pickling baths through a roller descaler and a training stand, and is characterized by squeezing the strip in this stand lying within 3 ... 8%, which not only destroys the scale, but also eliminates the breaks in the strip after it is unwound. The disadvantage of this technology is the large upper limit of the relative compression, which leads to accelerated wear of the rolls (smoothing of microroughnesses) and, as a result, to a slowdown of the etching process and the possibility of the occurrence of a defect "undergrav" which is unrecoverable and unacceptable during cold rolling.
Технической задачей изобретения является повышение качества холоднокатаной полосовой стали за счет уменьшения дефектов в процессе травления подката. An object of the invention is to improve the quality of cold-rolled strip steel by reducing defects during pickling etching.
Для решения этой задачи в способе подготовки к травлению горячекатаной полосовой стали, включающем предварительное обжатие заданной величины движущейся полосы в дрессировочной клети с валками, имеющими заданные твердость и шероховатость поверхности, величину обжатия ε меняют в зависимости от планируемого тоннажа Т полосы, подвергаемой дрессировке за время рабочей кампании валков, причем при тоннаже менее или равном 0,3 Т-2% ≤ ε ≤ 2,5%; более 0,3 Т и менее или равном 0,6 Т-2,5% < ε ≤ 3%; более 0,6 Т-3% < ε ≤ 4% и используют валки с твердостью бочки 94-96 ед. по Шору; при этом задают параметры шероховатости поверхности валков Rz=15-35 мкм и S не более 35 мкм на базовой длине l=0,8 мм.To solve this problem, in a method for preparing hot-rolled strip steel for pickling, including preliminary compression of a given value of a moving strip in a training stand with rolls having a given hardness and surface roughness, the compression value ε is changed depending on the planned tonnage T of the strip subjected to tempering during the working campaign rolls, and with tonnage less than or equal to 0.3 T-2% ≤ ε ≤ 2.5%; more than 0.3 T and less than or equal to 0.6 T-2.5% <ε ≤ 3%; more than 0.6 T-3% <ε ≤ 4% and use rolls with a barrel hardness of 94-96 units. along shore; in this case, the parameters of the surface roughness of the rolls R z = 15-35 μm and S no more than 35 μm on the base length l = 0.8 mm are set.
Приведенные величины отдельных параметров получены в результате обработки экспериментальных данных. The given values of individual parameters were obtained as a result of processing experimental data.
Сущность найденного технического решения заключается в оптимизации величины обжатия ε (2-4%) движущейся горячекатаной полосы валками дрессировочной клети, установленной на входе НТА, причем начинают рабочую кампанию валков (т. е. после их непосредственной установки в клеть) с минимальной величины обжатия (2%) и меняют в зависимости от планируемого тоннажа Т полосы, подвергаемой дрессировке за время рабочей кампании валков, причем при тоннаже менее или равном 0,3 Т величину обжатия устанавливают в пределах 2% ≤ ε ≤ 2,5%; более 0,3 Т и менее или равном 0,6 Т-2,5% < ε ≤ 3%; более 0,6 Т-3% < ε ≤ 4%. Кроме того, валки должны иметь определенную твердость, а их поверхность - заданную микрогеометрию (величину Rz и величину шага местных выступов S).The essence of the technical solution found is to optimize the amount of compression ε (2-4%) of the moving hot-rolled strip by the rolls of the training stand installed at the inlet of the NTA, and the work campaign of the rolls (i.e., after their direct installation in the stand) begins with a minimum amount of compression ( 2%) and change depending on the planned tonnage T of the strip subjected to training during the working campaign of the rolls, and with a tonnage less than or equal to 0.3 T, the compression value is set within 2% ≤ ε ≤ 2.5%; more than 0.3 T and less than or equal to 0.6 T-2.5% <ε ≤ 3%; more than 0.6 T-3% <ε ≤ 4%. In addition, the rolls must have a certain hardness, and their surface must have a given microgeometry (R z value and the step size of the local protrusions S).
Последняя величина характеризует "плотность" распределения пиков микронеровностей и, как подтвердили опыты (см. ниже), является одним из показателей работоспособности валков и степени предварительного разрушения окалины. Рекомендуемый диапазон Rz также является оптимальным с точки зрения продолжительности рабочей кампании валков и эффективности их работы. Найденная же величина твердости бочек валков не только увеличивает длительность их кампании, но и обеспечивает вышеприведенные параметры микрогеометрии бочек. Предлагаемые пределы величины обжатия в зависимости от планируемого тоннажа полосы, подвергаемой дрессировке за время рабочей кампании валков являются оптимальными с точки зрения качественного удаления окалины. Это объясняется тем, что после завалки валков в клеть микрорельеф их поверхности достаточно развит, и для качественного удаления окалины в начале рабочей кампании валков требуется небольшое изменение обжатия; по мере увеличения тоннажа подвергнутой дрессировке полосы (в конце рабочей кампании валков), микровыступы сглаживаются, и для наилучшего удаления окалины необходимо большее изменение обжатия.The latter value characterizes the "density" of the distribution of the peaks of microroughness and, as experiments have confirmed (see below), is one of the indicators of the rolls working capacity and the degree of preliminary scale destruction. The recommended range of R z is also optimal in terms of the duration of the working campaign of the rolls and their efficiency. The found value of the hardness of the roll barrels not only increases the duration of their campaign, but also provides the above microgeometry parameters of the barrels. The proposed limits for the amount of compression, depending on the planned tonnage of the strip subjected to training during the working campaign of the rolls, are optimal from the point of view of high-quality descaling. This is explained by the fact that after filling the rolls into the cage, the microrelief of their surface is sufficiently developed, and for a high-quality removal of scale at the beginning of the working campaign of the rolls, a small change in compression is required; as the tonnage of the strip subjected to training increases (at the end of the working campaign of the rolls), the microprotrusions are smoothed out, and a better change in compression is necessary for the best removal of scale.
Совокупность всех этих факторов способствует интенсивному разрушению окалины на поверхности стальной горячекатаной полосы, гарантируя отсутствие после травления с максимальной скоростью таких дефектов как недотрав и вкатанная окалина. The combination of all these factors contributes to the intensive destruction of scale on the surface of a hot-rolled steel strip, guaranteeing the absence of defects such as undergravity and rolled mill scale after etching at maximum speed.
При реализации предлагаемого способа предварительно осуществляют термообработку бочек валков с целью достижения необходимой их твердости, а затем осуществляют нанесение микрорельефа с требуемыми параметрами (например, дробеструйной обработкой поверхности бочек валков). When implementing the proposed method, heat treatment of roll barrels is preliminarily carried out in order to achieve their necessary hardness, and then microrelief is applied with the required parameters (for example, by shot peening the surface of roll barrels).
Опытную проверку заявляемого способа осуществляли на непрерывном травильном агрегате для травления полосовой стали различного сортамента. С этой целью при травлении горячекатаной полосы использовали для дрессировки металла валки с различной твердостью и микрогеометрией, варьируя величину обжатия при прохождении полос через дрессировочную клеть НТА. Результаты опытов оценивали по наличию дефектов после травления, а также по выходу холоднокатаной стали пониженного качества: Ш группы отделки поверхности полос (по ГОСТ 16523) и второго сорта. Experimental verification of the proposed method was carried out on a continuous pickling unit for pickling strip steel of various grades. For this purpose, when etching a hot-rolled strip, rolls with different hardness and microgeometry were used to train metal, varying the amount of compression when the strips passed through the NTA training stand. The results of the experiments were assessed by the presence of defects after etching, as well as by the yield of low-quality cold-rolled steel: Ш groups of surface finish of strips (according to GOST 16523) and second grade.
Наилучшие результаты (отсутствие вышеупомянутых дефектов при травлении с принятой на НТА скоростью движения полос, а также отсортировка холоднокатаного металла в пределах до 0,5%) получены при использовании заявляемого способа. При твердости бочек валков дрессировочной клети менее 94 ед. по Шору длительность их рабочей кампании уменьшалась, а при твердости более 96 ед. - не удавалось получить требуемую микрогеометрию поверхности бочек. В свою очередь при Rz<15 мкм и S>35 мкм происходило менее интенсивнее разрушение окалины, что ухудшало качество травления (и холоднокатаных полос), вынуждая увеличивать длительность травления, т.е. снижать скорость и производительность. При Rz >35 мкм возрастала интенсивность износа микрогеометрии поверхности бочек, что сокращало рабочую кампанию валков. Параметры микрорельефа определяли с помощью профилографа модели 201 путем снятия профилограмм на базовой длине l=0,8 мм.The best results (the absence of the aforementioned defects during etching with the strip speed adopted by the NTA, as well as the sorting of cold-rolled metal in the range up to 0.5%) were obtained using the proposed method. When the hardness of the barrels of rolls of the training stand is less than 94 units. according to Shore, the duration of their working campaign decreased, and with a hardness of more than 96 units. - it was not possible to obtain the required microgeometry of the barrel surface. In turn, at R z <15 μm and S> 35 μm, scale destruction was less intense, which impaired the quality of etching (and cold-rolled strips), forcing to increase the etching duration, i.e. reduce speed and performance. At R z > 35 μm, the wear rate of the microgeometry of the barrel surface increased, which reduced the working campaign of the rolls. The microrelief parameters were determined using a model 201 profilograph by taking profilograms at a base length l = 0.8 mm.
"Контрольное" травление с применением при дрессировке валков с оптимальными (см. выше) параметрами микрорельефа поверхности и с рекомендуемой твердостью, но с величиной обжатия более 4% (т.е. согласно известной технологии) сократило длительность кампании валков в 1,5...2 раза при соответствующем увеличении трудозатрат, а после травления наблюдался дефект "вкатанная окалина", в результате чего отсортировка холоднокатаного металла возросла до 3...5%. Увеличение обжатия в ходе рабочей кампании валков, отличное от найденных пределов, ухудшало удаление окалины к концу рабочей кампании валков, что приводило к возрастанию отсортировки холоднокатаной полосы до 1,2%. The “control” etching using roll training with optimal (see above) surface microrelief parameters and recommended hardness, but with a compression ratio of more than 4% (that is, according to known technology) reduced the duration of the roll campaign by 1.5 .. .2 times with a corresponding increase in labor costs, and after pickling there was a defect "rolled mill scale", as a result of which the sorting of cold-rolled metal increased to 3 ... 5%. An increase in the reduction during the work roll campaign other than the limits found worsened the descaling by the end of the work roll campaign, which led to an increase in sorting of the cold-rolled strip to 1.2%.
Таким образом, опыты подтвердили приемлемость найденного технического решения для выполнения поставленной задачи и его преимущества перед известным объектом. Thus, the experiments confirmed the acceptability of the technical solution found to fulfill the task and its advantages over the known object.
Пример конкретного выполнения
Горячекатаная полосовая сталь 08пс с сечением 1600 х 2,5 мм перед травлением подвергается дрессировке с использованием валков, твердость бочки которых - 95 ед. по Шору, а параметры микрогеометрии поверхности (замеренные на базовой длине l= 0,8 мм) составляют Rz=25 мкм и S=30 мкм. Планируемая продолжительность рабочей кампании валков составляет 800 т. Непосредственно после завалки валков в клеть величину обжатия принимают 2%; после дрессировки 240 т полосы обжатие увеличивают до 2,5%; подвергнув дрессировке 400 т металла, устанавливают обжатие 3%; после дрессировки 550 т обжатие увеличивают до 4%. Последнюю величину обжатия сохраняют до перевалки валков.Concrete example
08ps hot-rolled strip steel with a cross section of 1600 x 2.5 mm is subjected to training before etching using rolls, the barrel hardness of which is 95 units. according to Shore, and the parameters of surface microgeometry (measured at a base length l = 0.8 mm) are R z = 25 μm and S = 30 μm. The planned duration of the working campaign of the rolls is 800 tons. Immediately after filling the rolls in the stand, the compression ratio is 2%; after training 240 tons of strip compression is increased to 2.5%; having trained 400 tons of metal, set compression of 3%; after training 550 tons, the compression is increased to 4%. The last compression value is stored until the rolls are transshipped.
Claims (1)